JPH0140751B2 - - Google Patents
Info
- Publication number
- JPH0140751B2 JPH0140751B2 JP16842280A JP16842280A JPH0140751B2 JP H0140751 B2 JPH0140751 B2 JP H0140751B2 JP 16842280 A JP16842280 A JP 16842280A JP 16842280 A JP16842280 A JP 16842280A JP H0140751 B2 JPH0140751 B2 JP H0140751B2
- Authority
- JP
- Japan
- Prior art keywords
- synthetic resin
- wall covering
- resin layer
- covering material
- fibrous material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は、壁紙等として使用される呼吸性を有
する壁装材に係り、より詳しくは高湿度下では急
速に水分を吸収でき、また低湿度下では水分を放
出できる呼吸性を有する壁装材に関するものであ
る。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a breathable wall covering material used as wallpaper, etc., and more specifically, it can rapidly absorb moisture under high humidity and release moisture under low humidity. This invention relates to a wall covering material that is breathable.
壁紙、天井表装材などの内装用壁装材は、多く
は紙、布等の基材に樹脂加工したものや、プラス
チツクシートそのものを加工したものなどが用い
られている。例えば、紙又は布に樹脂加工してな
る壁紙は、引張り、引裂等の強度も強くまた耐水
性などもあり汚れを容易に払き落せるなどの利点
を有することから、現在では居間などのほかに台
所、トイレなどにも使用されているが、通気性、
吸湿性に乏しいことから室温の急変や湿度の変化
によつて、壁紙の表面に水分が結路し、水滴とな
つてあらわれるという現象がしばしば起つてい
る。このように水分が表面に結路すると、その部
分が伸びて折角きれいに貼つた壁紙面にたるみや
しわが出来たり、また長い間にはシミとして残つ
たり、黴が生えるという問題を生じている。 Interior wall covering materials such as wallpaper and ceiling covering materials are often made of base materials such as paper or cloth processed with resin, or processed plastic sheets themselves. For example, wallpaper made of paper or cloth treated with resin has advantages such as strong tensile and tear strength, water resistance, and the ability to easily remove dirt, so it is now used in living rooms and other places. It is also used in kitchens, toilets, etc., but it has good breathability,
Due to its poor hygroscopicity, sudden changes in room temperature or humidity often cause moisture to form on the surface of wallpaper and appear as water droplets. When moisture connects to the surface in this way, the area stretches, causing sagging and wrinkles on the wallpaper surface that has been applied neatly, and over a long period of time, leaving stains and mold. .
特に、この種の壁装材を、風呂場の天井が台
所、洗面所の壁面に用いたときに上記問題の発生
が著しい。 Particularly, when this type of wall covering material is used for the ceiling of a bathroom, the wall of a kitchen, or a washroom, the above-mentioned problem occurs significantly.
また、この種の壁装材では、樹脂の絶縁性にも
とずく静電気の発生により、表面にごみ等が付着
する汚れなども起きている。 In addition, with this type of wall covering material, the generation of static electricity due to the insulating properties of the resin causes stains such as dust and the like to adhere to the surface.
本発明は、上記の問題を解決するためのもの
で、結露による水滴発生の防止と、防黴、防汚性
を有する壁装材を提供するものである。 The present invention is intended to solve the above-mentioned problems, and provides a wall covering material that prevents the generation of water droplets due to dew condensation and has anti-mold and antifouling properties.
本発明の壁装材は、吸湿性樹脂と繊維状物とを
含有する合成樹脂層からなり、該繊維状物の少な
くとも一部が合成樹脂層面に露出していることを
特徴とする。更に詳しくは、吸湿性合成樹脂と繊
維状物、例えば糸、布等を含有する合成樹脂シー
トからなるか、または前記合成樹脂層を紙、布等
の基材上に形成してなるものである。 The wall covering material of the present invention is characterized in that it consists of a synthetic resin layer containing a hygroscopic resin and a fibrous material, and that at least a portion of the fibrous material is exposed on the surface of the synthetic resin layer. More specifically, it is made of a synthetic resin sheet containing a hygroscopic synthetic resin and a fibrous material such as thread or cloth, or it is made by forming the synthetic resin layer on a base material such as paper or cloth. .
本発明で使用する吸湿性樹脂とは、例えばアク
リルグラフトポリマーで親水性基等を有する合成
樹脂で、高湿度下で水分を多量に吸収することが
でき、例えば樹脂自体の重量に対し300倍程度の
水分を吸収でき、また低湿度となつたとき吸収し
た水分を放出することができる性質を有し、吸水
時加圧しても水分が表面に滲出してくることはな
く、また50％吸湿させたときでも、外観、形状は
ほとんど変化しない性質を有するものである。具
体的には、例えば、三洋化成(株)のサンウエツト
IM−300（商品名）があげられる。 The hygroscopic resin used in the present invention is, for example, an acrylic graft polymer, a synthetic resin having hydrophilic groups, etc., and can absorb a large amount of moisture under high humidity, for example, about 300 times the weight of the resin itself. It has the property of being able to absorb moisture and releasing the absorbed moisture when the humidity becomes low, so that even if pressure is applied when absorbing water, the moisture will not seep out to the surface, and it will absorb 50% of moisture. Its appearance and shape remain almost unchanged even when Specifically, for example, Sanyo Chemical Co., Ltd.'s Sunwet
One example is IM-300 (product name).
本発明では、この吸湿性樹脂を繊維状物ととも
に合成樹脂中に含有させて使用するが、吸湿性樹
脂の使用量としては、合成樹脂100部に対して５
部（5PHR）ないし50部（50PHR）の間で混入
される。吸湿性樹脂の混入量が少いと吸湿性が少
いため、結露現象を充分に防止することができ
ず、また多すぎると壁装材としての強度に欠け
る。そのため前記範囲で使用されるが、好ましく
は10〜30PHRで用いられる。 In the present invention, this hygroscopic resin is used by being contained in a synthetic resin together with a fibrous material, and the amount of hygroscopic resin used is 5 parts per 100 parts of synthetic resin.
(5PHR) to 50 parts (50PHR). If the amount of the hygroscopic resin mixed in is small, the hygroscopicity will be low, so that dew condensation cannot be sufficiently prevented, and if it is too large, the strength as a wall covering material will be lacking. Therefore, it is used within the above range, preferably 10 to 30 PHR.
本発明で使用される繊維状物としては、木綿ス
フ、合成樹脂、混紡繊維などからなる糸、布など
があげられるが、これらは場合によつては合成樹
脂コンパウンドに混入できるように短く切断した
ものであつてもよい。これら繊維状物は、そのま
ま使用されるか、または予じめ吸湿性樹脂を含浸
させたのち合成樹脂中に混入される。 The fibrous materials used in the present invention include yarns and cloth made of cotton cloth, synthetic resins, blended fibers, etc. In some cases, these may be cut short so that they can be mixed into the synthetic resin compound. It may be something. These fibrous materials are used as they are, or are mixed into a synthetic resin after being impregnated with a hygroscopic resin in advance.
繊維状物は、補強材としても用いられるが、そ
の毛細管現象による吸水性を利用するために用い
られる。そのため、使用量及び合成樹脂への混入
はこれらの性質が失われない範囲内で、使用され
混入される。 Fibrous materials are also used as reinforcing materials, and are used to take advantage of their water absorbing properties due to capillary action. Therefore, the amount used and the amount mixed into the synthetic resin should be within a range that does not cause loss of these properties.
吸湿性樹脂及び繊維状物を混入する基材として
の合成樹脂には、通常壁装材に使用される樹脂が
使用でき、例えば、ポリ塩化ビニルなどをあげる
ことができる。 As the synthetic resin as the base material into which the hygroscopic resin and the fibrous material are mixed, resins commonly used for wall covering materials can be used, such as polyvinyl chloride.
本発明壁装材を得るには、例えばポリ塩化ビニ
ル（PVC）コンパウンド中に前記吸湿性樹脂と
繊維状物を混入し、このコンパウンドをシート状
に成形するか、または紙等の裏打材上にこのコン
パウンド層を形成する。この場合、繊維状物とし
ての長尺の糸、又は布を使用し、これら繊維状物
の一部が合成樹脂層中に埋入されるようにして合
成樹脂層上に繊維状物を積層してもよい。 In order to obtain the wall covering material of the present invention, for example, the hygroscopic resin and the fibrous material are mixed into a polyvinyl chloride (PVC) compound, and the compound is formed into a sheet, or the compound is formed on a backing material such as paper. This compound layer is formed. In this case, a long thread or cloth is used as the fibrous material, and the fibrous material is laminated on the synthetic resin layer so that a part of the fibrous material is embedded in the synthetic resin layer. It's okay.
次に、本発明壁装材の獄成例のいくつかを第１
図〜第８図に示す。 Next, some examples of the wall covering material of the present invention will be described in the first section.
It is shown in FIGS.
第１図は、吸湿性樹脂と短糸状繊維状物２を合
成樹脂中に混入し、シート状物１とした例であ
る。 FIG. 1 shows an example in which a hygroscopic resin and a short thread-like fibrous material 2 are mixed into a synthetic resin to form a sheet-like material 1.
第２図は、吸湿性樹脂を混入した合成樹脂シー
ト１上に、一部がシート１中に埋入されるように
して布等の繊維状物２を積層した例であり第３図
は吸湿性樹脂と繊維状物２を混入した合成樹脂層
１を裏打材３上に形成した例である。 Figure 2 shows an example in which a fibrous material 2 such as cloth is layered on a synthetic resin sheet 1 mixed with a hygroscopic resin, with a part of the material being embedded in the sheet 1. This is an example in which a synthetic resin layer 1 containing a synthetic resin and a fibrous material 2 is formed on a backing material 3.
第４図及び第５図は、合成樹脂シート１及び合
成樹脂層１の表面にエンボス加工による凹凸模様
を附した例である。この場合繊維状物２として
は、短繊維、ガーゼのような目の粗い布、糸など
が適する。第４図及び第５図は、糸を用いた例を
示す。 4 and 5 show examples in which the surfaces of the synthetic resin sheet 1 and the synthetic resin layer 1 are provided with an uneven pattern by embossing. In this case, as the fibrous material 2, short fibers, coarse cloth such as gauze, thread, etc. are suitable. FIGS. 4 and 5 show an example using thread.
第６図は、吸湿性樹脂を含有する合成樹脂層１
を紙、布、プラスチツクシート等の基材３上に斑
点状または線条状に形成した例を示し、第７図及
び第８図はその斜視図を示す。第７図及び第８図
は繊維状物２として目の粗い布を使用した例であ
る。 FIG. 6 shows a synthetic resin layer 1 containing a hygroscopic resin.
7 and 8 show perspective views thereof. 7 and 8 are examples in which a coarse cloth is used as the fibrous material 2. FIG.
本発明壁装材は、上記の如く吸湿性樹脂と繊維
状物を含む合成樹脂層のみか、裏打材を付して構
成されるが、必要に応じ更に補強材等を積層して
もよい。 The wall covering material of the present invention is constructed with only a synthetic resin layer containing a hygroscopic resin and a fibrous material as described above, or with a backing material, but it may be further laminated with a reinforcing material, etc., if necessary.
本発明は、上記の如く構成されているため、吸
湿性樹脂による吸湿性と繊維状物の毛細管現象に
よる吸水性との組合せによる相乗作用で、高湿度
下では急速に水分を吸収でき、また低湿度下では
水分を放出できる呼吸性を有する壁装材とするこ
とができる。したがつて、雨季などの湿度が多い
時でも、表面に水滴が現われることがなく完全に
水分の結露が防止される。この結露防止効果は、
吸湿性樹脂の使用量使用繊維状物の材質や量によ
つて調節することができるが、更に第４図及び第
５図に示す如く表面をエンボス加工して表面積を
大きくするとかまたは水分を吸収しやすい形状に
することによつて結露現象を更に有効に防止でき
る。このように結露した水分は合成樹脂層中に吸
収され表面に残らないため、この水によつて生じ
ていた黴も生える余地がなくなり、その結果防黴
効果も示す。本発明壁装材は、高湿度下では急速
に水分を吸収でき、また低湿度下では水分を放出
できる。いわゆる呼吸性を有するので、小さな部
屋などでは湿度調節の目的で使用することもでき
る。また、壁装材は適度の水分を常に保持するた
め、特に帯電防止剤を使用しななくても、帯電す
ることがなく、静電気による汚れも発生しないと
いう利点を有する。更にまた、低湿度状態になる
と吸収していた水分を急速に放出する性質を有す
るため、難燃効果をも有する。 Since the present invention is configured as described above, it is possible to rapidly absorb moisture under high humidity and to reduce It can be a breathable wall covering that can release moisture under humid conditions. Therefore, even in times of high humidity such as during the rainy season, no water droplets appear on the surface, completely preventing moisture condensation. This dew condensation prevention effect is
The amount of hygroscopic resin used can be adjusted depending on the material and amount of the fibrous material used, but the surface can be embossed to increase the surface area or absorb moisture as shown in Figures 4 and 5. By creating a shape that is easy to absorb, dew condensation can be more effectively prevented. Since the water condensed in this way is absorbed into the synthetic resin layer and does not remain on the surface, there is no room for mold to grow due to this water, and as a result, it also exhibits an anti-mold effect. The wall covering of the present invention can rapidly absorb moisture under high humidity conditions and release moisture under low humidity conditions. Since it has so-called breathability, it can also be used for the purpose of controlling humidity in small rooms. Furthermore, since the wall covering material always retains a suitable amount of moisture, it has the advantage that it does not become charged or stain due to static electricity, even without the use of an antistatic agent. Furthermore, since it has the property of rapidly releasing absorbed moisture when the humidity becomes low, it also has a flame retardant effect.
以下本発明を実施例と従来例との試験例により
説明する。実施例１として、裏打基材として紙を
使用し、該裏打基材上にアクリルグラフトポリマ
ーよりなる吸湿性樹脂を5PHR混入したポリ塩化
ビニルコンパウンドを間隔をおいて筋状に塗布
し、前記コンパウンドに片麻平織布（縦糸：１イ
ンチ間にスフ40番手23本、横糸；１インチ間に麻
30番手21本）を一部露出して埋設し、その表面に
凹凸エンボスを打つた壁装材を製作した。 The present invention will be explained below with reference to examples and test examples of conventional examples. As Example 1, paper was used as the backing base material, and on the backing base material, a polyvinyl chloride compound mixed with 5 PHR of a hygroscopic resin made of an acrylic graft polymer was applied in stripes at intervals. Single hemp plain woven fabric (warp: 23 pieces of 40 thread count per inch, weft: linen per inch)
A wall covering material was created by partially exposing and burying 21 pieces of No. 30 wood and embossed the surface with unevenness.
実施例２として、裏打基材として紙を使用し該
裏打基材上にアクリルグラフトポリマーよりなる
吸湿性樹脂を5PHR混入したポリ塩化ビニルコン
パウンドをベタ塗りし、前記コンパウンドに片麻
平織布（上記実施例１のものと同じ）を一部露出
して埋設し、その表面に凹凸エンボスを行つた壁
装材を製作した。 As Example 2, paper was used as a backing base material, a polyvinyl chloride compound mixed with 5 PHR of a hygroscopic resin made of an acrylic graft polymer was applied solidly onto the backing base material, and a hemp plain woven fabric (as described above) was applied to the compound. A wall covering material (same as that in Example 1) was partially exposed and buried, and the surface was embossed with irregularities to produce a wall covering material.
従来例１として、裏打基材として紙を使用し該
裏打基材上にポリ塩化ビニルコンパウンドをベタ
塗りし、前記コンパウンドに片麻平織布（上記実
施例１のものと同じ）を一部露出して埋設し、そ
の表面に凹凸エンボスを行つた壁装材を製作し
た。 As Conventional Example 1, paper was used as a backing base material, a polyvinyl chloride compound was applied solidly on the backing base material, and a part of hemp plain woven cloth (same as that of Example 1 above) was exposed to the compound. Then, we created a wall covering material with embossed unevenness on its surface.
従来例２として、裏打基材として紙を使用し該
裏打基材上にポリ塩化ビニルコンパウンドをベタ
塗りし、その表面に凹凸エンボスを行つた壁装材
を製作した。 As Conventional Example 2, a wall covering material was produced in which paper was used as a backing base material, a polyvinyl chloride compound was applied solidly onto the backing base material, and unevenness was embossed on the surface.
試験例
室温（温度21℃、湿度67％）において、上記実
施例１乃至従来例２の各試験片を30分間常温水に
浸水し、その後30分間乾燥して乾燥前後の水分放
出割合を測定したところ、実施例１で98.57％、
実施例２で57.99％、従来例１で47.76％、従来例
２で43.20％の結果を得た。上記試験結果より、
本実施例１及び実施例２は従来例１及び従来例２
に比較し、水分放出割合において、大きな改善が
なされたことが分るものである。Test example At room temperature (temperature 21°C, humidity 67%), each test piece of Example 1 to Conventional Example 2 was immersed in room temperature water for 30 minutes, then dried for 30 minutes, and the moisture release rate before and after drying was measured. However, in Example 1, 98.57%,
The results were 57.99% in Example 2, 47.76% in Conventional Example 1, and 43.20% in Conventional Example 2. From the above test results,
Embodiment 1 and Embodiment 2 are conventional example 1 and conventional example 2.
It can be seen that there was a significant improvement in the water release rate compared to the above.
第１図ないし第６図は本発明の各実施例を示す
拡大断面図、第７図及び第８図は本発明の他の実
施例を示す拡大斜視図である。
図中、１……合成樹脂層、２……繊維状物、３
……裏打基材。
1 to 6 are enlarged sectional views showing each embodiment of the invention, and FIGS. 7 and 8 are enlarged perspective views showing other embodiments of the invention. In the figure, 1... synthetic resin layer, 2... fibrous material, 3
...backing base material.
Claims (1)
含有する合成樹脂層からなり、該繊維状物の少な
くとも一部が合成樹脂層面に露出していることを
特徴とする呼吸性を有する壁装材。 ２ 合成樹脂層がシートであることを特徴とする
特許請求の範囲第１項記載の呼吸性を有する壁装
材。 ３ 合成樹脂層が裏打基材上に設けられているこ
とを特徴とする特許請求の範囲第１項記載の呼吸
性を有する壁装材。 ４ 裏打基材上の合成樹脂層がシート状である特
許請求の範囲第３項記載の呼吸性を有する壁装
材。 ５ 合成樹脂層が表面にエンボス加工されている
ことを特徴とする特許請求の範囲第１〜４項のい
ずれか１項に記載の呼吸性を有する壁装材。 ６ 合成樹脂層が基材上に斑点状又は線条状に設
けられていることを特徴とする特許請求の範囲第
３項記載の呼吸性を有する壁装材。[Scope of Claims] 1. Consisting of a synthetic resin layer containing a hygroscopic resin and a fibrous material made of natural fiber, at least a part of the fibrous material is exposed on the surface of the synthetic resin layer. Breathable wall covering. 2. The breathable wall covering material according to claim 1, wherein the synthetic resin layer is a sheet. 3. The breathable wall covering material according to claim 1, wherein the synthetic resin layer is provided on a backing base material. 4. The breathable wall covering material according to claim 3, wherein the synthetic resin layer on the backing base material is in the form of a sheet. 5. The breathable wall covering material according to any one of claims 1 to 4, characterized in that the synthetic resin layer is embossed on the surface. 6. The breathable wall covering material according to claim 3, wherein the synthetic resin layer is provided on the base material in the form of spots or lines.