JPH0215657B2 - - Google Patents
Info
- Publication number
- JPH0215657B2 JPH0215657B2 JP56051906A JP5190681A JPH0215657B2 JP H0215657 B2 JPH0215657 B2 JP H0215657B2 JP 56051906 A JP56051906 A JP 56051906A JP 5190681 A JP5190681 A JP 5190681A JP H0215657 B2 JPH0215657 B2 JP H0215657B2
- Authority
- JP
- Japan
- Prior art keywords
- polymer
- molten
- blowing
- molten thermoplastic
- nozzle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
この発明は、熱可塑性ポリマーから非織成又は
不織布マツト製造に於ける溶融熱可塑性ポリマー
の吹込法とその装置に関する。 より詳細に言えば、熱可塑性樹脂を加熱ノズル
のオリフイスから熱気体流に溶融状態で押出し、
溶融樹脂を繊維として微細化する。これら繊維は
繊維流路の受台に集められ非織成又は不織布マツ
トが形成される。 従来の熱可塑性ポリマーの溶融吹込法につい
て、フアン A.ヴエンテの論文(“Industrial
and Engineering Chemistry”Vol.48,No.8
(1956)……米国の刊行物)、米国特許第3849241
号、3379811号、3634573号等において詳しく説明
されている。 例えば前記米国特許第3379811号等の方法では、
高溶融粘度で吹込まれ、1秒間に100m以下の繊
維速度を実現する。 米国特許第3849241号では、低溶融粘度(50〜
300ポアズ)で吹込まれ最適紡糸条件を実現する
ためポリマーの苛酷な分解を必要とする。そして
高質の溶融吹込みウエブの生産は繊維形成ポリマ
ーの先行分解を必要とする。分解したポリマーが
ウエブ/繊維の引張強さの点で劣り利用上不利で
あることはよく知られている。従来技術の不利益
に着目してこの発明は成就されたのである。 この発明の主たる目的は、高温で溶融した低粘
度の熱可塑性ポリマーをノズル内のオリフイスか
ら押出し、押出された溶融繊維が上記オリフイス
から同時に流れる気体により略音波速度で吹込ま
れる非織成マツト製造に於ける溶融熱可塑性ポリ
マーの吹込法とその装置を提供することにある。 押出された溶融ポリマーは低い温度上昇にある
第一加熱ゾーンを通つてノズルに進み、次に高い
温度上昇の前記ノズルを急速に通過する。これは
過剰なポリマー分解を軽減又は阻止するため短い
残留時間で繊維の加速に必要な低溶融粘度を達成
するためである。 この発明の一つの特徴として、微細な繊維はユ
ニークな熱伝達パターンを適用することによつて
ほとんど熱分解の影響を受けずに生成されるとい
うことである。これは各ポリマー押出ノズル周辺
に極めて小径の気体(空気)通過オリフイスを形
成することにより1ポンド当り非常に低い空気消
費により実現される。各ポリマー(樹脂)押出ノ
ズルに於ける空気オリフイス面積を縮少すること
により、空気の高速流が得られるのである。 溶融ポリマー吹込法により微細な繊維を製造す
るため、ノズルの樹脂押出を減少させることが必
要である。これは下記により証明される。繊維の
最大速度が音波速度である(それを越える実際の
速度設計はない)と仮定すれば、最大繊維直径は
次の方程式により樹脂押出率に関係する。 D2=4Q/πV ……(1) D=繊維直径 Q=樹脂フロー率(cm3/秒) V=繊維速度 一秒あたり550メートルの速度で直径1ミクロ
ン繊維を製造するためには、オリフイスからの樹
脂押出率は1秒間に0.023cm3を越えてはならない。
音波速度は温度で上昇するので、空気温度が高く
なればなるほど繊維の直径は短かくなる。上述か
ら明かな通り微細な繊維を経済的に製造するため
には、多数のオリフイスが必要となることがわか
るであろう。従来の吹込法のシステムでは、ダイ
の幅に沿つて1インチに約20個のオリフイスが存
在している。樹脂フロー率を上記レベルに減少さ
せるため、押出しダイの樹脂は少く、樹脂滞留時
間も長くそれにより樹脂の分解をまねいている。 円筒管内の熱伝達はフオリエル基本方程式
(Fourier equation)により表わされる。 d2T/dr2=l・dT/adt ……(2) T=温度(℃) r=半径(cm) t=時間(秒) a=温度拡散率 温度拡散率は次の式より計算される。 a=h/cd(cm2/秒) h=温度拡散率(cal/℃秒cm2/cm) c=熱量(cal/グラム℃) d=密度(グラム/cm3) 第1図から説明すると、ダイは厚板2に接続し
たチヤンバーを有する長径の管1(管状ダイを意
味する)から成り、ノズル3が厚板2の孔に挿入
されており、スリツプと漏洩を防止するため銀は
んだ付けされている。ノズル3は、空気キヤビテ
イ4を通つて第2図に示すようなパターンのプレ
ートの正方形の孔へ延びている。ノズル3周辺の
正方形6の4つの隅部はオリフイスでそのオリフ
イスを通つて空気が繊維出口の管3とほぼ平行に
吹込まれる。プレート2,5およびノズル3から
なるノズル構造は、例えば第3図に例示するよう
に、異なつた径のノズルと形状の孔の組合わせか
らなるものに適宜交換することができる。 空気キヤビテイ4は空気圧力ゲージ8、サーモ
カツプル9及び熱風ヒーター12の前の空気流量
計を具えた空気供給管10を具備する。熱風ヒー
ター12は移転ゾーンの金属を空気温度に予熱す
るためジヤケツト取囲みの管1に貫通している。
押出機13から管状ダイ1に熱ポリマーが送給さ
れる。この管状ダイ1は図に示す通り等間隔に3
個のサーモカツプル14,15,16を具えてい
る。これらのサーモカツプルはジヤケツトされて
おりスチールの温度よりむしろポリマーの溶融温
度を測定する。 ポリマー溶融圧力を測定する圧力変換器17は
スピニングノズル入口近くのキヤビテイ18に位
置している。樹脂を押出機からバイパスするため
樹脂放出管19とバルブ20があり、これにより
ノズルを介して樹脂フロー率を減少させる。放出
バルブ20を調整することによつて、異つた温
度/熱変換パターンを管部及びノズルゾーンで確
立することができる。 第4図乃至第7図について説明する。ダイは覆
い板22と底板23からなり、この底板には半円
溝が第5図に示す通り円形樹脂変換溝を形成する
よう配設されている。押出機から流れる樹脂は流
路24に流れ、流路25で2つの流れに区分され
る。そして樹脂は更に区分された流路26と再び
流路27に流れる。 孔28はノズルプレート31に配設されている
ノズル30へポリマーを送給するキヤビテイ29
に導く。ノズル30は入口パイプ33によつて送
給される空気キヤビテイ32に導く。ノズル30
はスクリーン板34に配設したスクリーン34の
網状孔部35に出させている。 空気キヤビテイ32の両側は側板36により密
閉されている。この装置はボルト(図示せず)3
7により保持されている。 第7図はノズルとスクリーン(孔)との関係を
示す、本発明装置ノズル部分の底面図であり、第
8図は、その8−8における断面図であり、樹脂
と空気のフローの関係を示している。本発明のノ
ズル部分の構造によれば、加熱気体は各々のノズ
ル端の周囲の気体オリフイスから、各々のノズル
より吐出されるポリマー(繊維)に沿つて乱れな
くほぼ平行に噴出される。また、本発明の吹込ノ
ズル装置においては、ノズルを複数列に配列させ
ることにより、より均斉な非織成マツトを製造す
ることが可能であり、このような配列のノズルの
製作は容易である。 第9図は本発明の吹込装置の全体斜視図であ
る。 第10図は、空間の平均温度Tmとr2に於ける
フオリエル数(Fourier Number)の関係を示す
グラフである。一定半径(r)に於いて、外部か
ら温度T2と接触すると、開始温度T1から時間付
きシリンダーの温度増加を示す。基本熱伝達方程
式(2)は理想モデルのみ対称としかつ混合温度変
化、境界条件と樹脂フローの流路断面変化の影響
を考慮していないけれども、それは有用と判断
し、プロセス変数と設計特徴を記載するため良好
な推定である。固定された又は静止システムに適
用される無次元式at/r2は、ダイ流路を介してポ
リマーフローのようなフローシステムに適用させ
るように変更できる。これは次の式により明かと
なる。 Vp=l/t ……(4) A=Q/Vp ……(5) A=πr2 ……(6) Vp=長さlの流路に於けるポリマーのフロー
速度 t=長さlの流路に於ける滞留時間 A=流路断面積 Q=Aを通過する樹脂のフロー率(量/時間) at/r2=πal/Q ……(7) 非円筒状樹脂フローのチヤンネルにとつて、r
=2A/pが利用され、pは湿性のペリメーター
である。 実施例の説明 第1実施例から第8実施例までに共通して言え
ることは、第1図装置が利用されこれは放出管1
9と放出バルブ20を具えている。これにより放
出バルブ20の調整と、異つた温度/熱伝達パタ
ーンは、種々の空気量と圧力に於けるスピニング
性能で測定された影響で管断面とノズルゾーンで
確立できる。 ダイ1は0.3175cmの内径を有する縦12cmの管
で、0.1588cmの厚板2に接続している。 尚、以下の実施例は最も好ましい例について説
明するもので、具体的構成はこの発明の精神と範
囲に反することなく種々変更できるものである。 実施例 1 この実施例では、ノズル3の長さは1.27cmであ
る。各ノズル周囲の空気オリフイス開口部6は
0.086mm2の面積である。プレート5に突出するノ
ズル7の長さは0.2mmである。 実験は溶融粘度78ポアズで生じる溶融フロー率
10分間につき35グラムのポリプロピレンを使用す
る低温でスタートする。この条件で空気は繊維を
秒速45mに増加した。空気温度は700〓から750〓
に増加し高温分布と苛酷なポリマーの分解(0.3
の減少極限粘度数)が生じた。繊維の加速は秒当
り510mであつたが、1分間当り8cm3から16cm3及
び20cm3まで増加した。これは管1に於いてal/Q
要素と滞留時間を減少させた、試験(f)は第1表及
び第2表から明かな通りわづかな熱ポリマー分解
で最低の溶融粘度と最高の繊維粘度をもつた。
(表はこの説明の最後に記載) 実施例 2 この実施例では、押出機からの樹脂フロー率は
管1内で0.06のal/Q要素を与えるようセツトさ
れ、わづか2.85秒の滞留時間で低温分布が生じ
た。そこでは、熱可塑性樹脂の分解をほとんど生
じさせなかつた。放出バルブ20はその時ノズル
内の樹脂フロー率を減少させ滞留時間を増加させ
るため開放された。2.6秒のノズル滞留時間で熱
分解は0.3減少極限粘度で苛酷で、ウエブはかな
りの量のシヨツトをもつた。空気圧力はゲージ8
で17平方インチポンド(以下“平方インチポン
ド”はPsiと称す)であつた。 実施例 3 この実験シリーズでは、管1は大径の管に取替
えられた。これは温度分布を変更しなかつたが、
一定の樹脂フロー率で滞留時間を増加させた。ノ
ズル内の滞留時間は分解を回避するため短く保た
れた。管1内で45秒の滞留時間、樹脂分解は苛酷
で(0.4の減少極限粘度数)、樹脂は管の加熱部で
長く滞留した。空気圧はゲージ8で17Psiであつ
た。 実施例 4 この実施例は、実施例1及び2に用いたダイよ
りも長径のダイを使用した。 管1の内径は0.3167cmであつた。ノズルは内径
が0.0584cm外径が0.0889cmで全長1.27cmであつた。
プレート5内の孔は第3図に示す通り三角形で、
1つのノズルに対し0.4mm2の空気オリフイス開口
部であつた。 このシリーズでは、樹脂のフロー率はノズル内
のal/Qを減少させるように増加された。0.1及
びそれ以下のal/Qで、正常空気率(17Psi)で
の溶融粘度と繊維径は著しく増大し、ノズル内の
温度は空気温度と均衡する十分な時間はなかつ
た。 実施例 5 第4実施例のダイは同じ空気フロー条件で使用
されている。放出バルブ20はal/Q要素とノズ
ル中の滞留時間を増加するように開放された。
al/Q−0.1で繊維形成は良好であつた。樹脂分
解は1.36秒以上の滞留時間で苛酷であつた。 実施例 6 この実施例では、小ノズルを有する管ダイは高
分子量の小繊維を作る条件の下で使用された。実
施例1の管1は次の寸法のノズル装置に適合す
る。外径0.0508cm、内径0.0254cm、長さ0.7cm。 プレートの孔は0.508cmの正方形で、1つのノ
ズルにつき0.055mm2の空気オリフイス開口部に生
じる。その結果は第3表に記載されている。 試験(a)は高樹脂率で低い温度分布を有し、ノズ
ル中の滞留時間は短かつた。それにより高溶融粘
度が生じ比較的遅い繊維速度で粗い繊維が生じ
た。1分間10cm3とal/Q0.12の試験は、著しい樹
脂分解(減少した極限粘度数)とウエブ中の望ま
しくないシヨツトを生じる管内の温度分布を有し
た、試験(c)は最適な繊維質をもちほとんど樹脂分
解はなかつた。試験(d),(e)及び(f)では、放出バル
ブ20は16個のノズルを通過するフローを減少さ
せるため、また比較的高分子量の小繊維を製造す
るため開放された。 実施例 7 この実施例では、第1実施例に記載されたダイ
が利用された。樹脂はメルトインデツクス12.0の
一般用ポリスチレンが使用された。ポリエステル
(ポリエチレン テレフタレート)は相対粘度40
の繊維銘柄であつた。相対粘度とはフエノール10
重量部と2.4.6−トリクロロフエノール7重量部
の混合物中に於けるポリエチレン テレフタレー
トの10%溶液(20mlの溶剤中2.15gのポリマー)
の粘度率とフエノール−トリクロロフエノール混
合物の粘度との関係を示す。この結果は第4表に
示されている。 ポリスチレンとポリエステルとの間の温度拡散
率の相違の効果は、試験(b)と(d)の比較により明か
となる。繊維形成とその速度はこの試験では類似
しており、溶融粘度もほぼ同じであつた(それぞ
れ22と18ポアズ)。しかしながら、ポリエステル
は事実上高い樹脂フロー率をもつた。 実施例 8 この実施例は、変換ゾーンに於ける温度分布の
重要性を示している。実施例1の(d)の樹脂フロー
率は6つの試験全てに使用された。試験(a),(b)及
び(c)では、押出温度は620〓から680〓に上昇し、
試験(c)では樹脂分解は増大し苛酷なシヨツトであ
つた。試験(d),(e),(f)では、押出温度は温度を40
〓に保持しながら下降した。これは樹脂分解を減
少させたが、溶融粘度を増加させ、粗い繊維とな
り繊維速度は落ちた。樹脂の低い熱分解と高い繊
維速度(最低の繊維直径)との最適バランスを得
るため、溶融吹込法は約40ポアズ以下の溶融粘度
とノズル温度(空気)と押出温度(樹脂)との間
の40〓以上の温度差となつて吹込まれることは明
かとなる。 次の実施例では、第4図に示す通り4″のダイが
使用されている。第4図に於ける樹脂の流路24
〜30を第5表に示す。 変換ゾーンは放出システムを利用せずに特別の
樹脂フロー率のための最適al/Q要素を提供する
ように設計されている。放出システムの代りに、
生産性を上げるための樹脂配分システムがある。 実施例 9 この実施例は、384個のノズルダイに於けるポ
リプロピレンの熱分解に於ける熱伝達パターンの
影響を示している。溶融フロー率35と平均分子量
225.000のポリプロピレンが使用されている。押
出機の出口温度は600〓、ダイと空気の温度は750
〓である。この試験の結果は第7表に示されてい
る。試験(a)では、溶融吹込は高い樹脂フロー率と
最適熱伝達パターン、すなわち、移転ゾーンに於
ける低いΣal/Q、ダイとノズルの短い滞留時間
をもたらした。試験(b)と(c)では樹脂フロー率が減
少したので、ポリマー分解は増大した。試験(c)で
はal/Qは移転ゾーンで0.171に達し、ウエブの
質は不良となつた。 実施例 10 この実施例では、最適熱伝達パターンに於ける
樹脂フロー率に関する異つたポリマーの熱伝達率
の効果が示されている。ここではナイロン66とポ
リスチレンが使用された。この結果は第8表に示
されている。試験(a)及び(c)は高樹脂フロー率で行
なわれ、その結果、ノズルゾーン中に於ける一個
のal/Q要素は高繊維粘度ではあまりにも低すぎ
るとが判明した。これらの繊維は粗いものであつ
た。試験(b)及び(d)の条件は、微細な繊維のウエブ
質に最適だつた。上記2つのポリマーの伝熱率
(温度拡散率“a”)の差異に基づき、この状態で
はナイロン66に対してよりもポリスチレンで高い
樹脂フロー率に達した。 尚、見掛溶融粘度はポアゼイユ(Poisseille)
の方程式から計算される。 Q=πPr4/8lη ……(8) すなわち Q=単一ノズルを通過するポリマーフロー
(cm3./sec.) P=ポリマー圧力(ダインズ/cm2) r=内側ノズル半径(cm.) l=ノズルの長さ(cm.)、及び η=見掛溶融粘度(ポアズ);及び 上記押出ノズル上のポリマーの溶融圧力を測定
することにより、次式が与えられる。 η=2747 P A2/Ql ……(9) P=Psiに於けるポリマー圧力 A=クロスセクシヨン地域の押出ノズル(cm2) ここで使用されている極限粘度数〔η〕はサー
ジエント粘度計#50で135℃のデカリン中で測定
されている。溶融フロー率はテイニウム オスレ
ンのメルトインデツクス測定装置でASTM方法
#D 1238 65Tに従つて測定された。
不織布マツト製造に於ける溶融熱可塑性ポリマー
の吹込法とその装置に関する。 より詳細に言えば、熱可塑性樹脂を加熱ノズル
のオリフイスから熱気体流に溶融状態で押出し、
溶融樹脂を繊維として微細化する。これら繊維は
繊維流路の受台に集められ非織成又は不織布マツ
トが形成される。 従来の熱可塑性ポリマーの溶融吹込法につい
て、フアン A.ヴエンテの論文(“Industrial
and Engineering Chemistry”Vol.48,No.8
(1956)……米国の刊行物)、米国特許第3849241
号、3379811号、3634573号等において詳しく説明
されている。 例えば前記米国特許第3379811号等の方法では、
高溶融粘度で吹込まれ、1秒間に100m以下の繊
維速度を実現する。 米国特許第3849241号では、低溶融粘度(50〜
300ポアズ)で吹込まれ最適紡糸条件を実現する
ためポリマーの苛酷な分解を必要とする。そして
高質の溶融吹込みウエブの生産は繊維形成ポリマ
ーの先行分解を必要とする。分解したポリマーが
ウエブ/繊維の引張強さの点で劣り利用上不利で
あることはよく知られている。従来技術の不利益
に着目してこの発明は成就されたのである。 この発明の主たる目的は、高温で溶融した低粘
度の熱可塑性ポリマーをノズル内のオリフイスか
ら押出し、押出された溶融繊維が上記オリフイス
から同時に流れる気体により略音波速度で吹込ま
れる非織成マツト製造に於ける溶融熱可塑性ポリ
マーの吹込法とその装置を提供することにある。 押出された溶融ポリマーは低い温度上昇にある
第一加熱ゾーンを通つてノズルに進み、次に高い
温度上昇の前記ノズルを急速に通過する。これは
過剰なポリマー分解を軽減又は阻止するため短い
残留時間で繊維の加速に必要な低溶融粘度を達成
するためである。 この発明の一つの特徴として、微細な繊維はユ
ニークな熱伝達パターンを適用することによつて
ほとんど熱分解の影響を受けずに生成されるとい
うことである。これは各ポリマー押出ノズル周辺
に極めて小径の気体(空気)通過オリフイスを形
成することにより1ポンド当り非常に低い空気消
費により実現される。各ポリマー(樹脂)押出ノ
ズルに於ける空気オリフイス面積を縮少すること
により、空気の高速流が得られるのである。 溶融ポリマー吹込法により微細な繊維を製造す
るため、ノズルの樹脂押出を減少させることが必
要である。これは下記により証明される。繊維の
最大速度が音波速度である(それを越える実際の
速度設計はない)と仮定すれば、最大繊維直径は
次の方程式により樹脂押出率に関係する。 D2=4Q/πV ……(1) D=繊維直径 Q=樹脂フロー率(cm3/秒) V=繊維速度 一秒あたり550メートルの速度で直径1ミクロ
ン繊維を製造するためには、オリフイスからの樹
脂押出率は1秒間に0.023cm3を越えてはならない。
音波速度は温度で上昇するので、空気温度が高く
なればなるほど繊維の直径は短かくなる。上述か
ら明かな通り微細な繊維を経済的に製造するため
には、多数のオリフイスが必要となることがわか
るであろう。従来の吹込法のシステムでは、ダイ
の幅に沿つて1インチに約20個のオリフイスが存
在している。樹脂フロー率を上記レベルに減少さ
せるため、押出しダイの樹脂は少く、樹脂滞留時
間も長くそれにより樹脂の分解をまねいている。 円筒管内の熱伝達はフオリエル基本方程式
(Fourier equation)により表わされる。 d2T/dr2=l・dT/adt ……(2) T=温度(℃) r=半径(cm) t=時間(秒) a=温度拡散率 温度拡散率は次の式より計算される。 a=h/cd(cm2/秒) h=温度拡散率(cal/℃秒cm2/cm) c=熱量(cal/グラム℃) d=密度(グラム/cm3) 第1図から説明すると、ダイは厚板2に接続し
たチヤンバーを有する長径の管1(管状ダイを意
味する)から成り、ノズル3が厚板2の孔に挿入
されており、スリツプと漏洩を防止するため銀は
んだ付けされている。ノズル3は、空気キヤビテ
イ4を通つて第2図に示すようなパターンのプレ
ートの正方形の孔へ延びている。ノズル3周辺の
正方形6の4つの隅部はオリフイスでそのオリフ
イスを通つて空気が繊維出口の管3とほぼ平行に
吹込まれる。プレート2,5およびノズル3から
なるノズル構造は、例えば第3図に例示するよう
に、異なつた径のノズルと形状の孔の組合わせか
らなるものに適宜交換することができる。 空気キヤビテイ4は空気圧力ゲージ8、サーモ
カツプル9及び熱風ヒーター12の前の空気流量
計を具えた空気供給管10を具備する。熱風ヒー
ター12は移転ゾーンの金属を空気温度に予熱す
るためジヤケツト取囲みの管1に貫通している。
押出機13から管状ダイ1に熱ポリマーが送給さ
れる。この管状ダイ1は図に示す通り等間隔に3
個のサーモカツプル14,15,16を具えてい
る。これらのサーモカツプルはジヤケツトされて
おりスチールの温度よりむしろポリマーの溶融温
度を測定する。 ポリマー溶融圧力を測定する圧力変換器17は
スピニングノズル入口近くのキヤビテイ18に位
置している。樹脂を押出機からバイパスするため
樹脂放出管19とバルブ20があり、これにより
ノズルを介して樹脂フロー率を減少させる。放出
バルブ20を調整することによつて、異つた温
度/熱変換パターンを管部及びノズルゾーンで確
立することができる。 第4図乃至第7図について説明する。ダイは覆
い板22と底板23からなり、この底板には半円
溝が第5図に示す通り円形樹脂変換溝を形成する
よう配設されている。押出機から流れる樹脂は流
路24に流れ、流路25で2つの流れに区分され
る。そして樹脂は更に区分された流路26と再び
流路27に流れる。 孔28はノズルプレート31に配設されている
ノズル30へポリマーを送給するキヤビテイ29
に導く。ノズル30は入口パイプ33によつて送
給される空気キヤビテイ32に導く。ノズル30
はスクリーン板34に配設したスクリーン34の
網状孔部35に出させている。 空気キヤビテイ32の両側は側板36により密
閉されている。この装置はボルト(図示せず)3
7により保持されている。 第7図はノズルとスクリーン(孔)との関係を
示す、本発明装置ノズル部分の底面図であり、第
8図は、その8−8における断面図であり、樹脂
と空気のフローの関係を示している。本発明のノ
ズル部分の構造によれば、加熱気体は各々のノズ
ル端の周囲の気体オリフイスから、各々のノズル
より吐出されるポリマー(繊維)に沿つて乱れな
くほぼ平行に噴出される。また、本発明の吹込ノ
ズル装置においては、ノズルを複数列に配列させ
ることにより、より均斉な非織成マツトを製造す
ることが可能であり、このような配列のノズルの
製作は容易である。 第9図は本発明の吹込装置の全体斜視図であ
る。 第10図は、空間の平均温度Tmとr2に於ける
フオリエル数(Fourier Number)の関係を示す
グラフである。一定半径(r)に於いて、外部か
ら温度T2と接触すると、開始温度T1から時間付
きシリンダーの温度増加を示す。基本熱伝達方程
式(2)は理想モデルのみ対称としかつ混合温度変
化、境界条件と樹脂フローの流路断面変化の影響
を考慮していないけれども、それは有用と判断
し、プロセス変数と設計特徴を記載するため良好
な推定である。固定された又は静止システムに適
用される無次元式at/r2は、ダイ流路を介してポ
リマーフローのようなフローシステムに適用させ
るように変更できる。これは次の式により明かと
なる。 Vp=l/t ……(4) A=Q/Vp ……(5) A=πr2 ……(6) Vp=長さlの流路に於けるポリマーのフロー
速度 t=長さlの流路に於ける滞留時間 A=流路断面積 Q=Aを通過する樹脂のフロー率(量/時間) at/r2=πal/Q ……(7) 非円筒状樹脂フローのチヤンネルにとつて、r
=2A/pが利用され、pは湿性のペリメーター
である。 実施例の説明 第1実施例から第8実施例までに共通して言え
ることは、第1図装置が利用されこれは放出管1
9と放出バルブ20を具えている。これにより放
出バルブ20の調整と、異つた温度/熱伝達パタ
ーンは、種々の空気量と圧力に於けるスピニング
性能で測定された影響で管断面とノズルゾーンで
確立できる。 ダイ1は0.3175cmの内径を有する縦12cmの管
で、0.1588cmの厚板2に接続している。 尚、以下の実施例は最も好ましい例について説
明するもので、具体的構成はこの発明の精神と範
囲に反することなく種々変更できるものである。 実施例 1 この実施例では、ノズル3の長さは1.27cmであ
る。各ノズル周囲の空気オリフイス開口部6は
0.086mm2の面積である。プレート5に突出するノ
ズル7の長さは0.2mmである。 実験は溶融粘度78ポアズで生じる溶融フロー率
10分間につき35グラムのポリプロピレンを使用す
る低温でスタートする。この条件で空気は繊維を
秒速45mに増加した。空気温度は700〓から750〓
に増加し高温分布と苛酷なポリマーの分解(0.3
の減少極限粘度数)が生じた。繊維の加速は秒当
り510mであつたが、1分間当り8cm3から16cm3及
び20cm3まで増加した。これは管1に於いてal/Q
要素と滞留時間を減少させた、試験(f)は第1表及
び第2表から明かな通りわづかな熱ポリマー分解
で最低の溶融粘度と最高の繊維粘度をもつた。
(表はこの説明の最後に記載) 実施例 2 この実施例では、押出機からの樹脂フロー率は
管1内で0.06のal/Q要素を与えるようセツトさ
れ、わづか2.85秒の滞留時間で低温分布が生じ
た。そこでは、熱可塑性樹脂の分解をほとんど生
じさせなかつた。放出バルブ20はその時ノズル
内の樹脂フロー率を減少させ滞留時間を増加させ
るため開放された。2.6秒のノズル滞留時間で熱
分解は0.3減少極限粘度で苛酷で、ウエブはかな
りの量のシヨツトをもつた。空気圧力はゲージ8
で17平方インチポンド(以下“平方インチポン
ド”はPsiと称す)であつた。 実施例 3 この実験シリーズでは、管1は大径の管に取替
えられた。これは温度分布を変更しなかつたが、
一定の樹脂フロー率で滞留時間を増加させた。ノ
ズル内の滞留時間は分解を回避するため短く保た
れた。管1内で45秒の滞留時間、樹脂分解は苛酷
で(0.4の減少極限粘度数)、樹脂は管の加熱部で
長く滞留した。空気圧はゲージ8で17Psiであつ
た。 実施例 4 この実施例は、実施例1及び2に用いたダイよ
りも長径のダイを使用した。 管1の内径は0.3167cmであつた。ノズルは内径
が0.0584cm外径が0.0889cmで全長1.27cmであつた。
プレート5内の孔は第3図に示す通り三角形で、
1つのノズルに対し0.4mm2の空気オリフイス開口
部であつた。 このシリーズでは、樹脂のフロー率はノズル内
のal/Qを減少させるように増加された。0.1及
びそれ以下のal/Qで、正常空気率(17Psi)で
の溶融粘度と繊維径は著しく増大し、ノズル内の
温度は空気温度と均衡する十分な時間はなかつ
た。 実施例 5 第4実施例のダイは同じ空気フロー条件で使用
されている。放出バルブ20はal/Q要素とノズ
ル中の滞留時間を増加するように開放された。
al/Q−0.1で繊維形成は良好であつた。樹脂分
解は1.36秒以上の滞留時間で苛酷であつた。 実施例 6 この実施例では、小ノズルを有する管ダイは高
分子量の小繊維を作る条件の下で使用された。実
施例1の管1は次の寸法のノズル装置に適合す
る。外径0.0508cm、内径0.0254cm、長さ0.7cm。 プレートの孔は0.508cmの正方形で、1つのノ
ズルにつき0.055mm2の空気オリフイス開口部に生
じる。その結果は第3表に記載されている。 試験(a)は高樹脂率で低い温度分布を有し、ノズ
ル中の滞留時間は短かつた。それにより高溶融粘
度が生じ比較的遅い繊維速度で粗い繊維が生じ
た。1分間10cm3とal/Q0.12の試験は、著しい樹
脂分解(減少した極限粘度数)とウエブ中の望ま
しくないシヨツトを生じる管内の温度分布を有し
た、試験(c)は最適な繊維質をもちほとんど樹脂分
解はなかつた。試験(d),(e)及び(f)では、放出バル
ブ20は16個のノズルを通過するフローを減少さ
せるため、また比較的高分子量の小繊維を製造す
るため開放された。 実施例 7 この実施例では、第1実施例に記載されたダイ
が利用された。樹脂はメルトインデツクス12.0の
一般用ポリスチレンが使用された。ポリエステル
(ポリエチレン テレフタレート)は相対粘度40
の繊維銘柄であつた。相対粘度とはフエノール10
重量部と2.4.6−トリクロロフエノール7重量部
の混合物中に於けるポリエチレン テレフタレー
トの10%溶液(20mlの溶剤中2.15gのポリマー)
の粘度率とフエノール−トリクロロフエノール混
合物の粘度との関係を示す。この結果は第4表に
示されている。 ポリスチレンとポリエステルとの間の温度拡散
率の相違の効果は、試験(b)と(d)の比較により明か
となる。繊維形成とその速度はこの試験では類似
しており、溶融粘度もほぼ同じであつた(それぞ
れ22と18ポアズ)。しかしながら、ポリエステル
は事実上高い樹脂フロー率をもつた。 実施例 8 この実施例は、変換ゾーンに於ける温度分布の
重要性を示している。実施例1の(d)の樹脂フロー
率は6つの試験全てに使用された。試験(a),(b)及
び(c)では、押出温度は620〓から680〓に上昇し、
試験(c)では樹脂分解は増大し苛酷なシヨツトであ
つた。試験(d),(e),(f)では、押出温度は温度を40
〓に保持しながら下降した。これは樹脂分解を減
少させたが、溶融粘度を増加させ、粗い繊維とな
り繊維速度は落ちた。樹脂の低い熱分解と高い繊
維速度(最低の繊維直径)との最適バランスを得
るため、溶融吹込法は約40ポアズ以下の溶融粘度
とノズル温度(空気)と押出温度(樹脂)との間
の40〓以上の温度差となつて吹込まれることは明
かとなる。 次の実施例では、第4図に示す通り4″のダイが
使用されている。第4図に於ける樹脂の流路24
〜30を第5表に示す。 変換ゾーンは放出システムを利用せずに特別の
樹脂フロー率のための最適al/Q要素を提供する
ように設計されている。放出システムの代りに、
生産性を上げるための樹脂配分システムがある。 実施例 9 この実施例は、384個のノズルダイに於けるポ
リプロピレンの熱分解に於ける熱伝達パターンの
影響を示している。溶融フロー率35と平均分子量
225.000のポリプロピレンが使用されている。押
出機の出口温度は600〓、ダイと空気の温度は750
〓である。この試験の結果は第7表に示されてい
る。試験(a)では、溶融吹込は高い樹脂フロー率と
最適熱伝達パターン、すなわち、移転ゾーンに於
ける低いΣal/Q、ダイとノズルの短い滞留時間
をもたらした。試験(b)と(c)では樹脂フロー率が減
少したので、ポリマー分解は増大した。試験(c)で
はal/Qは移転ゾーンで0.171に達し、ウエブの
質は不良となつた。 実施例 10 この実施例では、最適熱伝達パターンに於ける
樹脂フロー率に関する異つたポリマーの熱伝達率
の効果が示されている。ここではナイロン66とポ
リスチレンが使用された。この結果は第8表に示
されている。試験(a)及び(c)は高樹脂フロー率で行
なわれ、その結果、ノズルゾーン中に於ける一個
のal/Q要素は高繊維粘度ではあまりにも低すぎ
るとが判明した。これらの繊維は粗いものであつ
た。試験(b)及び(d)の条件は、微細な繊維のウエブ
質に最適だつた。上記2つのポリマーの伝熱率
(温度拡散率“a”)の差異に基づき、この状態で
はナイロン66に対してよりもポリスチレンで高い
樹脂フロー率に達した。 尚、見掛溶融粘度はポアゼイユ(Poisseille)
の方程式から計算される。 Q=πPr4/8lη ……(8) すなわち Q=単一ノズルを通過するポリマーフロー
(cm3./sec.) P=ポリマー圧力(ダインズ/cm2) r=内側ノズル半径(cm.) l=ノズルの長さ(cm.)、及び η=見掛溶融粘度(ポアズ);及び 上記押出ノズル上のポリマーの溶融圧力を測定
することにより、次式が与えられる。 η=2747 P A2/Ql ……(9) P=Psiに於けるポリマー圧力 A=クロスセクシヨン地域の押出ノズル(cm2) ここで使用されている極限粘度数〔η〕はサー
ジエント粘度計#50で135℃のデカリン中で測定
されている。溶融フロー率はテイニウム オスレ
ンのメルトインデツクス測定装置でASTM方法
#D 1238 65Tに従つて測定された。
【表】
【表】
【表】
【表】
【表】
【表】
【表】
【表】
【表】
第1図は、この発明に係る溶融熱可塑性ポリマ
ーの吹込装置のダイの一部切欠縦断面図、第2図
は第1図2−2線ノズル部の拡大断面図、第3図
は同上ノズル部の他の実施例の拡大断面図、第4
図はノズル部の分解斜視図、第5図は第4図ノズ
ル部の側面図、第6図は第5図6−6線断面図、
第7図は第4図ノズル部の一部底面図、第8図は
第7図ノズル部の側面断面図、第9図はこの発明
に係る溶融熱可塑性ポリマーの吹込装置の全体を
示す斜視図、第10図は空間の平均温度とフオリ
エル数の関係を示すグラフである。
ーの吹込装置のダイの一部切欠縦断面図、第2図
は第1図2−2線ノズル部の拡大断面図、第3図
は同上ノズル部の他の実施例の拡大断面図、第4
図はノズル部の分解斜視図、第5図は第4図ノズ
ル部の側面図、第6図は第5図6−6線断面図、
第7図は第4図ノズル部の一部底面図、第8図は
第7図ノズル部の側面断面図、第9図はこの発明
に係る溶融熱可塑性ポリマーの吹込装置の全体を
示す斜視図、第10図は空間の平均温度とフオリ
エル数の関係を示すグラフである。
Claims (1)
- 【特許請求の範囲】 1 溶融熱可塑性ポリマーを微細な繊維の流れに
するため前記熱可塑性ポリマーを加熱ノズルのオ
リフイスから熱気体流の中に溶融状に押出し、前
記繊維の流れを受台に集合するようにした非織成
マツト製造に於ける溶融熱可塑性ポリマーの吹込
法に於いて、 (a) 前記溶融熱可塑性ポリマーを流路を介して送
給室に送り、前記溶融ポリマーの前記流路に於
ける滞留時間は30秒以下とすることと、 (b) 前記流路を通過する溶融ポリマーをaΣl/Q
>0.1の数式を満足させる条件で一定の温度に
加熱し、前記数式に於いて、aは溶融ポリマー
の温度拡散率、lは各ポリマー流路の長さ、Q
は各ポリマー流路のフロー率であることと、 (c) 前記溶融ポリマーを前記送給室から多数の加
熱ノズルに通過させ、前記溶融ポリマーは前記
加熱ノズル内で2秒以下の滞留時間を有するこ
とと、及び (d) 更に前記ノズルを通過する溶融ポリマーを
aΣl/Q<0.07の数式を満足させる条件で一定
の温度に加熱し、前記数式に於いてaは溶融ポ
リマーの温度拡散率、lは各ポリマー流路の長
さ、Qは各ポリマー流路のフロー率であり、 前記溶融ポリマーは45ポアズ以下の見掛溶融粘
度を有する溶融吹込繊維を形成しかつ前記流路に
導入された前記溶融ポリマーは、前記溶融吹込繊
維の温度より少なくとも40〓低い温度であること
を特徴とする非織成マツト製造に於ける溶融熱可
塑性ポリマーの吹込法。 2 前記熱気体の流れは前記溶融ポリマーの各オ
リフイスの周囲の気体オリフイスから吹込まれ、
前記気体オリフイスは0.5m2以下の面積の各溶融
ポリマーオリフイスに隣接して組み合わされてい
ることを特徴とする特許請求の範囲第1項記載の
非織成マツト製造に於ける溶融熱可塑性ポリマー
の吹込法。 3 前記非織成マツトを形成する一繊維の平均直
径は、前記溶融ポリマーオリフイスのフロー率7
〜15倍の平方根であり、また前記繊維の平均分子
量は前記溶融熱可塑性ポリマーの平均分子量の少
なくとも0.4倍であることを特徴とする特許請求
の範囲第1項記載の非織成マツト製造に於ける溶
融熱可塑性ポリマーの吹込法。 4 前記一繊維の平均直径は2ミクロン以下であ
ることを特徴とする特許請求の範囲第3項記載非
織成マツト製造に於ける溶融熱可塑性ポリマーの
吹込法。 5 前記非織成マツトは多数の列に配設した多数
の溶融ポリマーオリフイスから生成されることを
特徴とする特許請求の範囲第1項記載の非織成マ
ツト製造に於ける溶融熱可塑性ポリマーの吹込
法。 6 前記溶融熱可塑性ポリマーの吹込により非織
成マツトを製造したことを特徴とする特許請求の
範囲第1項乃至第5項いづれか記載の非織成マツ
ト製造に於ける溶融熱可塑性ポリマーの吹込法。 7 溶融熱可塑性ポリマーを微細な繊維の流れに
するため前記熱可塑性ポリマーを加熱ノズルから
熱気体流の中に溶融状に押出し、前記繊維の流れ
を受台に集合するようにした非織成マツト製造に
於ける溶融熱可塑性ポリマーの吹込装置に於い
て、前記溶融ポリマーを通過させるための流路
と、前記流路通過中に前記溶融ポリマーをaΣl/
Q>0.1の数式を満足させる条件で加熱させる加
熱機構と、該流路から溶融ポリマーを加熱ノズル
に導く送給室と、前記溶融ポリマーを微細な繊維
に形成するため前記溶融ポリマーを受入れるため
の多数の加熱ノズル機構と、前記多数の加熱ノズ
ル機構の各々の周囲に略音波速度で加熱気体を通
過させる気体オリフイス機構と、前記ノズルを通
過する溶融ポリマーをaΣl/Q<0.07の数式を満
足させる条件で加熱させるために前記加熱気体を
加熱させる加熱機構とを具備し、前記数式に於い
てaは溶融ポリマーの温度拡散率、lは各ポリマ
ー流路の長さ、Qは各ポリマー流路のフロー率で
あることを特徴とした非織成マツト製造に於ける
溶融熱可塑性ポリマーの吹込装置。 8 前記オリフイス機構はスクリーン上の孔部に
突出していることを特徴とする特許請求の範囲第
7項記載の非織成マツト製造に於ける溶融熱可塑
性ポリマーの吹込装置。 9 前記オリフイス機構は断面正方形状であるこ
とを特徴とする特許請求の範囲第7項記載の非織
成マツト製造に於ける溶融熱可塑性ポリマーの吹
込装置。 10 溶融熱可塑性ポリマーを微細な繊維の流れ
にするため熱可塑性ポリマーを加熱ノズルから熱
気体流の中に溶融状に押出する溶融熱加熱性ポリ
マーの吹込装置であつて、多数の管状ノズルを固
定したノズルプレートと、該ノズル端に対応して
設けられた多数の孔を有する下方プレートとを備
え、両プレート間に加熱気体が供給されるキヤビ
テイが形成され、各々のノズルが空気キヤビテイ
を通つて下方プレートのそれぞれの孔に突出し、
該ノズルの各々の周囲に加熱気体を通過させる気
体オリフイスを形成したことを特徴とする溶融熱
可塑性ポリマーの吹込装置。 11 多数の管状ノズルが複数列に配列されたこ
とを特徴とする特許請求の範囲第10項記載の溶
融熱可塑性ポリマーの吹込装置。