JPH0219358B2 - - Google Patents
Info
- Publication number
- JPH0219358B2 JPH0219358B2 JP60116151A JP11615185A JPH0219358B2 JP H0219358 B2 JPH0219358 B2 JP H0219358B2 JP 60116151 A JP60116151 A JP 60116151A JP 11615185 A JP11615185 A JP 11615185A JP H0219358 B2 JPH0219358 B2 JP H0219358B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- tape
- asphalt
- adhesive
- connection part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、建築工事、土木工事、空調工事等に
おいて管体の接続部を粘着テープ又はシートで接
続する方法に関する。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to a method for connecting the joints of pipe bodies with adhesive tapes or sheets in construction work, civil engineering work, air conditioning work, etc.
従来、建築工事等の各種工事において、管体の
接続にアスフアルト・コンパウンドによる粘着テ
ープ或いはシートが多く利用されている。例え
ば、土木工事において、ヒユーム管等の接続部に
漏水防止のためアスフアルト・コンパウンドを主
体とした粘着テープが利用され、更に空調工事に
おいては、風管等の金属管の接続部に同様なアス
フアルト・コンパウンドによる粘着テープやシー
トが利用されている。
BACKGROUND ART Conventionally, adhesive tapes or sheets made of asphalt compound have been widely used to connect pipe bodies in various construction works such as construction work. For example, in civil engineering work, adhesive tape mainly made of asphalt compound is used to prevent water leakage at the joints of humid pipes, etc., and in air conditioning work, similar asphalt compound is used at the joints of metal pipes such as wind pipes. Adhesive tapes and sheets made from compounds are used.
しかしながら、これらの工事に用いる従来のア
スフアルト・コンパウンドによるテープやシート
は、アスフアルト・コンパウンドの単層か或いは
芯部に織布、不織布、プラスチツクフイルムを用
い、これにアスフアルト・コンパウンド層を成層
したものであるため、伸縮性に乏しく、シール
性、水密性に劣り、特に前記の諸工事において、
曲面や凹凸面などに用いる場合、これらの面に追
随し難いので、この部分における防水性が悪く、
漏水が生じる等の問題があつた。
However, the conventional tapes and sheets made of asphalt compound used in these construction works are either a single layer of asphalt compound, or a core made of woven fabric, non-woven fabric, or plastic film, and a layer of asphalt compound is layered on top of this. Therefore, it has poor elasticity, poor sealing performance, and watertightness, especially in the above-mentioned construction works.
When used on curved or uneven surfaces, it is difficult to follow these surfaces, so the waterproof properties in these areas are poor.
There were problems such as water leakage.
本発明は、上記事情に鑑みなされたもので、優
れたシール性をもつて管体を接続でき、特に曲面
や凹凸面などに確実に追随し、このため各種工事
において曲面や凹凸面を有する接続部などに使用
した場合、これに追随して〓間や空〓等を生じさ
せることがなく、この接続部を確実に防水し得る
管体の接続方法を提供することを目的とする。 The present invention has been developed in view of the above circumstances, and can connect pipe bodies with excellent sealing properties, and in particular, can reliably follow curved surfaces and uneven surfaces. To provide a method for connecting pipe bodies that can reliably waterproof the connection part without creating gaps or voids when used in a joint or the like.
即ち、本発明は上記目的を達成するため、管体
の接続部に、伸長度200％以上の伸縮性を有する
テープ状もしくはシート状のポリウレタン系弾性
繊維の不織布からなる基材の少なくとも片面にブ
チルゴムとアスフアルトが重量比として１：２〜
５の割合のゴム化アスフアルトからなる粘着剤層
を成層してなる粘着テープ又はシートを100％以
上伸長して巻き付け、貼着し、次いで該テープ又
はシートの復元力により収縮させて、上記接続部
を締め付けると共に、液密状態にシールするよう
にしたものである。
That is, in order to achieve the above-mentioned object, the present invention includes butyl rubber on at least one side of a base material made of a tape-like or sheet-like nonwoven fabric of polyurethane elastic fibers having elasticity with a degree of elongation of 200% or more. and asphalt in a weight ratio of 1:2~
An adhesive tape or sheet formed by laminating an adhesive layer made of rubberized asphalt at a ratio of 5% or more is stretched by 100% or more, wrapped and pasted, and then contracted by the restoring force of the tape or sheet to form the above-mentioned connection part. It is designed to tighten and seal in a liquid-tight state.
本発明の管体の接続方法によれば、粘着テープ
もしくはシートがこのように基材として伸長度
200％以上の伸縮性を有するテープ状もしくはシ
ート状のポリウレタン系弾性繊維の不織布を使用
し、粘着剤としてブチルゴムとアスフアルトが重
量比１：２〜５の伸縮性を有するゴム化アスフア
ルトを使用して構成されているので、容易に100
％以上伸長することができ、管体の接続に際し、
100％以上伸長させた状態でその接続部に巻き付
け粘着した後、前記基材の復元力で接続部を締め
付けるため、粘着テープもしくはシートを貼着し
た際に接続部に〓間や空〓などが生じても粘着テ
ープもしくはシートが収縮してこれを埋めるよう
に作用するので、シール性に優れ、接続部の水密
化が確実に達成され、該接続部における漏水が防
止されると共に、曲面や凹凸面に良好に追随する
ため、各種工事において管体の接続に有効に使用
される。 According to the pipe connection method of the present invention, the adhesive tape or sheet is used as a base material to
A tape-like or sheet-like polyurethane elastic fiber non-woven fabric with a stretchability of 200% or more is used, and rubberized asphalt with a stretchability of butyl rubber and asphalt in a weight ratio of 1:2 to 5 is used as the adhesive. It is configured so that 100
% or more, and when connecting the tube,
After it is stretched over 100% and attached to the joint, the restoring force of the base material tightens the joint, so there will be no gaps or voids in the joint when the adhesive tape or sheet is attached. Even if this occurs, the adhesive tape or sheet will shrink and act to fill it, so it has excellent sealing properties, ensures that the connection is watertight, prevents water leakage at the connection, and prevents curved or uneven surfaces. Because it follows the surface well, it is effectively used for connecting pipes in various construction works.
以下、本発明につき図面を参照して更に詳しく
説明する。 Hereinafter, the present invention will be explained in more detail with reference to the drawings.
本発明に係る管体の接続方法は、管体の接続部
に粘着テープ又はシートを巻き付けるものである
が、粘着テープもしくはシートは、伸長度200％
以上、好ましくは400％以上の伸縮性を有するテ
ープ状もしくはシート状基材の片面又は両面の粘
着剤層を成層し、更に必要により粘着剤層上の剥
離性フイルムを積層したものである。 The pipe connection method according to the present invention involves wrapping an adhesive tape or sheet around the joint of the pipe.
As described above, an adhesive layer is laminated on one or both sides of a tape-like or sheet-like base material preferably having a stretchability of 400% or more, and a releasable film is further laminated on the adhesive layer if necessary.
ここで、伸縮性の基材としては、厚さ0.5〜３
mm、特に0.8〜1.5mmであり、重量25〜200Kg／m2、
特に30〜120ｇ／m2のポリウレタン系の弾性繊維
からなる不織布が用いられる。また、粘着剤とし
ては、ブチルゴムとアスフアルトからなるゴム化
アスフアルトが用いられるが、かかるゴム化アス
フアルトとしては、とりわけ環球法による軟化点
が65〜150℃であり、針入度が130〜250程度のも
のが好ましい。この場合、ブチルゴムとアスフア
ルトとの配合比は、重量比としてブチルゴム１に
対してアスフアルトを２〜５程度とするものであ
り、また可塑剤としてテルペン樹脂等の石油系樹
脂などを配合することができる。更に、このよう
なゴム化アスフアルトを粘着剤として使用する場
合、必要によりこのゴム化アスフアルト粘着剤層
の表面に初期接着を確保するためゴム系粘着剤の
薄膜層を形成することができる。 Here, the elastic base material has a thickness of 0.5 to 3
mm, especially 0.8~1.5mm, weight 25~200Kg/ m2 ,
In particular, a nonwoven fabric made of polyurethane elastic fibers of 30 to 120 g/m 2 is used. In addition, rubberized asphalt made of butyl rubber and asphalt is used as the adhesive, and such rubberized asphalt has a softening point of 65 to 150°C by the ring and ball method and a penetration of about 130 to 250. Preferably. In this case, the blending ratio of butyl rubber and asphalt is approximately 2 to 5 asphalt to 1 part of butyl rubber by weight, and a petroleum resin such as terpene resin may be blended as a plasticizer. . Furthermore, when such rubberized asphalt is used as an adhesive, a thin film layer of a rubber adhesive may be formed on the surface of the rubberized asphalt adhesive layer to ensure initial adhesion, if necessary.
このように、伸縮性基材として上記不織布を使
用し、これにゴム化アスフアルトの粘着剤層を成
層する場合は、第１図に示すように基材１にゴム
化アスフアルト粘着剤層２を成層する際に基材１
中にゴム化アスフアルト粘着剤が浸透し、基材１
と粘着剤層２とが一体化した粘着テープ又はシー
ト３が得られる。 In this way, when using the above-mentioned nonwoven fabric as a stretchable base material and layering a rubberized asphalt adhesive layer thereon, a rubberized asphalt adhesive layer 2 is layered on a base material 1 as shown in FIG. Base material 1
The rubberized asphalt adhesive penetrates into the base material 1.
An adhesive tape or sheet 3 is obtained in which the adhesive layer 2 and the adhesive layer 2 are integrated.
本発明の接続方法は、例えば管体相互を接続す
る場合、第２図に示したように、管体４，４′の
接続部に粘着テープ又はシート３を100％以上伸
長して巻き付け、貼着するもので、巻き付け、伸
長後、該テープ又はシート３の復元力により該テ
ープ又はシート３が収縮し、これによりテープ又
はシート３が接続部を締め付けるものである。 In the connection method of the present invention, for example, when connecting tube bodies to each other, as shown in FIG. After being wrapped and stretched, the tape or sheet 3 contracts due to its restoring force, and as a result, the tape or sheet 3 tightens the joint.
このため、該接続部が〓間や空〓などが生じる
ことなく、液密にシールされ、接続部からの漏水
が防止される。 Therefore, the connection part is sealed liquid-tight without any gaps or voids, and water leakage from the connection part is prevented.
本発明の管体の接続方法は、建築工事、土木工
事、空調工事等の工事において管体を接合した場
合の接続部の防水などのために有効に使用される
もので、管体を接続するに際し、粘着テープ又は
シートを100％以上伸長した状態に接続部に巻き
付け、貼着する。これにより、貼着後、粘着テー
プ又はシートはその復元力により収縮するように
作用し、接続部を締め付け、液密状態にシールす
るものであつて、前記接続部が曲面や凹凸面があ
つてもこれに確実に追随し、粘着テープ又はシー
トの貼着時に〓間や空〓などが生じてもこれを埋
めるようにするので、極めてシール性がよく、接
続部を確実に防水する。
The method for connecting pipes of the present invention is effectively used for waterproofing joints when pipes are joined in construction work, civil engineering work, air conditioning work, etc., and is used to connect pipes. When doing so, wrap the adhesive tape or sheet around the connection part in a state where it is stretched more than 100% and attach it. As a result, after pasting, the adhesive tape or sheet acts to contract due to its restoring force, tightens the connection part, and seals the connection part in a liquid-tight state. The adhesive tape or sheet also follows this pattern and fills any gaps or voids that may occur when applying the adhesive tape or sheet, resulting in extremely good sealing properties and ensuring that the joint is waterproof.
以下、実施例を示す。 Examples are shown below.
重量50ｇ／m2のポリウレタン系の弾性繊維不織
布（伸長度約500％）を基材とし、その両面にそ
れぞれ軟化点77℃、針入度175のブチルゴムとア
スフアルトを１：４（重量比）で配合したゴム化
アスフアルトを厚さ0.5mmとなるように成層し、
幅10cmの粘着テープを作成した。
The base material is a polyurethane elastic fiber non-woven fabric (elongation degree of about 500%) weighing 50g/ m2 , and butyl rubber and asphalt with a softening point of 77℃ and a penetration rate of 175 are coated on both sides at a ratio of 1:4 (weight ratio). The compounded rubberized asphalt is layered to a thickness of 0.5 mm,
I made an adhesive tape with a width of 10cm.
これに３Kg／10cmの力を加えて伸長度100％以
上に伸長し、これを直径300mmのコンクリートヒ
ユーム管の接合部に２回巻き付け、貼着した。そ
の結果、この粘着テープは貼着後収縮を開始し、
前記接合部に対する密着性が向上して良好な水密
構造が得られた。 A force of 3 kg/10 cm was applied to this to elongate it to a degree of elongation of more than 100%, and this was wrapped twice around the joint of a concrete fume pipe with a diameter of 300 mm and pasted. As a result, this adhesive tape starts to shrink after being applied,
Adhesion to the joint portion was improved and a good watertight structure was obtained.
以上説明したように、本発明は伸長度200％以
上の伸縮性を有するテープ状もしくはシート状の
ポリウレタン系弾性繊維の不織布からなる基材の
少なくとも片面にブチルゴムとアスフアルトが重
量比として１：２〜５の割合のゴム化アスフアル
トからなる粘着剤層を成層した粘着テープ又はシ
ートを100％以上伸長して管体の接続部に巻き付
けた後、収縮させることにより、接続部の曲面や
凹凸部にも追随し、管体の接続部を締め付け、確
実にシールし、その適用箇所に良好な水密構造を
形成することができる。
As explained above, the present invention is characterized in that butyl rubber and asphalt are coated on at least one side of a base material made of a tape-like or sheet-like nonwoven fabric of polyurethane elastic fibers having an elongation of 200% or more, in a weight ratio of 1:2 to 1:2. By stretching an adhesive tape or sheet laminated with an adhesive layer made of rubberized asphalt at a ratio of 5% to 100% or more, wrapping it around the connection part of the pipe body, and then shrinking it, it can be applied to curved surfaces and uneven parts of the connection part. Following this, it is possible to tighten the connection part of the pipe body, reliably seal it, and form a good watertight structure at the place where it is applied.
第１図は本発明の実施に用いる粘着テープ又は
シートの一例を示す断面図、第２図は本発明の管
体接続方法の一実施例を示す断面図である。
１……基材、２……粘着剤層、３……粘着テー
プ又はシート、４，４′……管体。
FIG. 1 is a cross-sectional view showing an example of an adhesive tape or sheet used in the practice of the present invention, and FIG. 2 is a cross-sectional view showing an example of the pipe connection method of the present invention. 1... Base material, 2... Adhesive layer, 3... Adhesive tape or sheet, 4, 4'... Tube body.
Claims (1)
を有するテープ状もしくはシート状のポリウレタ
ン系弾性繊維の不織布からなる基材の少なくとも
片面にブチルゴムとアスフアルトが重量比として
１：２〜５の割合のゴム化アスフアルトからなる
粘着剤層を成層してなる粘着テープ又はシートを
100％以上伸長して巻き付け、貼着し、次いで該
テープ又はシートの復元力により収縮させて、上
記接続部を締め付けると共に、液密状態にシール
することを特徴とする管体の接続方法。1 At the connection part of the pipe body, at least one side of a base material made of a tape-like or sheet-like nonwoven fabric of polyurethane elastic fibers having an elasticity of 200% or more is coated with butyl rubber and asphalt in a weight ratio of 1:2 to 5. An adhesive tape or sheet formed by laminating an adhesive layer made of rubberized asphalt in a proportion of
A method for connecting pipes, which comprises stretching the tape or sheet by 100% or more, wrapping it, pasting it, and then contracting it by the restoring force of the tape or sheet to tighten the connection part and seal it in a liquid-tight state.