JPH02269872A - Planar structure of water absorbing fiber without imparting wet feeling and production thereof - Google Patents
Planar structure of water absorbing fiber without imparting wet feeling and production thereofInfo
- Publication number
- JPH02269872A JPH02269872A JP9156989A JP9156989A JPH02269872A JP H02269872 A JPH02269872 A JP H02269872A JP 9156989 A JP9156989 A JP 9156989A JP 9156989 A JP9156989 A JP 9156989A JP H02269872 A JPH02269872 A JP H02269872A
- Authority
- JP
- Japan
- Prior art keywords
- water
- repellent
- planar structure
- absorbing
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
（′産業上の利用分野）
この発明は、湿濡感を与えない吸水性繊維の平面状構造
物に関するものである。平たく云えば、この発明は、吸
水性を持った繊維から成る編織布又は不織布であって、
吸水しても濡れた感じを与えない編織布又は不織布を提
供するものである。DETAILED DESCRIPTION OF THE INVENTION ('Industrial Application Field) This invention relates to a planar structure of water-absorbing fibers that does not give a wet feeling. Simply put, the present invention is a woven or nonwoven fabric made of water-absorbing fibers,
To provide a woven fabric or a nonwoven fabric that does not give a wet feeling even when it absorbs water.
また、この発明は、そのような平面状構造物の製造方法
を提供するものである。The present invention also provides a method for manufacturing such a planar structure.
（従来の技術）
吸水性を持った繊維から成る編織布又は不織布（以下、
これを吸水性布帛という）は、既に知られている。それ
は、例えば、オムツ、シーツなどとして、既に使用され
ている。(Prior art) Woven fabrics or non-woven fabrics (hereinafter referred to as
This is called a water-absorbent fabric) is already known. It is already used, for example, as diapers, sheets, etc.
吸水性布帛は、僅かに吸水した程度では濡れた感じを与
えないが、成る程度以上吸水すると、濡れた感じを与え
るものとなる。濡れた感じを与えるようになった布帛を
そのまま着用するときは、不快な感じを与えるだけでな
く、病原菌も繁殖させる源となり、引いては皮膚炎など
を惹き起こすことにもつながる。そこで、多量の水を吸
収したあとも、湿潤感を与えないような吸水性布帛を作
ろうとの試みがなされた。A water-absorbent fabric does not give a wet feeling when it absorbs a small amount of water, but when it absorbs more than a certain amount of water, it gives a wet feeling. If you wear a fabric that has become wet, it not only makes you feel uncomfortable, but also becomes a breeding ground for pathogens, which can lead to dermatitis. Therefore, attempts were made to create water-absorbing fabrics that do not give a wet feeling even after absorbing large amounts of water.
そのような試みは、二、三の公報に記載されている。例
えば、実公昭５８−３７８８８号公報、実願昭５９−１
９８８．３２号の出願（実開昭６ｌ−１１１３７４）、
実願昭６０−７２８１５号の出願（実開昭６ｌ−１８７
５６０） 、な□どに記載されている。これらの試みを
総合すると、今まで湿潤感を与えないようにして来た手
段は、吸水性布帛の表面又は裏面に撥水性の層を設ける
ということであった。Such attempts are described in a few publications. For example, Utility Model Publication No. 58-37888, Utility Model Application No. 59-1
Application No. 988.32 (Utility Model Publication No. 6l-111374),
Application for Utility Application No. 60-72815 (Utility Application No. 61-187)
560), □, etc. Summarizing these attempts, the method that has been used so far to prevent the feeling of moisture is to provide a water-repellent layer on the front or back surface of a water-absorbing fabric.
公報は、吸水性布帛の表面に付設する撥水性の層につい
て、その実体を詳しく説明していない。The publication does not explain in detail the substance of the water-repellent layer attached to the surface of the water-absorbing fabric.
しかし、今まで撥水性を持った編織物の実体を考えると
、撥水性の層は、編織物の表面全体が一様に撥水性を持
ったものだと考えられる。それは、今まで、表面上で一
部が撥水性を持つだけで、一部に吸水性部分が存在する
ような編織物は、見当らなかったからである。However, considering the reality of knitted fabrics that have been water-repellent up until now, the water-repellent layer is considered to be one in which the entire surface of the knitted fabric is uniformly water-repellent. This is because until now, no knitted fabric has been found that has only a portion of its surface that is water-repellent and a portion of its surface that is water-absorbing.
ところが、撥水性を持った表面が全体にわたる吸水性布
帛は、表面の吸水性が悪くなるために、吸水性が劣るこ
とになった。このことは、撥水性編織物の表面に水を滴
下すると、水滴が生じて表面上を移動し、容易に吸収さ
れないことから明らかである。このように吸水性を低下
させたのでは、折角の吸水性布帛も価値がなくなる。そ
こで、吸水性を低下させないで、湿潤感を与えなくなる
ような、吸水性布帛の出現が要求された。However, water-absorbing fabrics having a water-repellent surface over the entire surface have poor water-absorbing properties because the surface has poor water-absorbing properties. This is evident from the fact that when water is dropped on the surface of a water-repellent knitted fabric, water droplets form, move on the surface, and are not easily absorbed. If the water absorbency is reduced in this way, the water absorbent fabric will become worthless. Therefore, there has been a demand for a water-absorbing fabric that does not give a wet feeling without reducing its water-absorbing properties.
（発明が解決しようとする課題）
この発明は、上述のような要求に応じようとして生れた
ものである。すなわち、この発明は、吸水性を大きく低
下させないで、しかも湿潤感を与えないような吸水性布
帛の提供を目的としてなされたち、のである。(Problems to be Solved by the Invention) This invention was created in an attempt to meet the above-mentioned demands. That is, the present invention was made with the object of providing a water-absorbing fabric that does not significantly reduce its water-absorbing properties and does not give a wet feeling.
（課題解決のための手段）
この発明者は、撥水性の表面層を設けるにあたり、表面
に撥水剤を部分的に塗布し、表面上には撥水剤の塗布さ
れていない部分がところどころに残っているものを作っ
た。その結果、吸水性部分と撥水性部分とが入りまじっ
て表面に現われ、内部がすべて吸水性のままに残ってい
る吸水性布帛を作ると、吸水性はさほど低下しないでそ
のまま保持され、湿潤感が少なくなることを見出した。(Means for Solving the Problem) In providing a water-repellent surface layer, the inventor partially applied a water-repellent agent to the surface, and there were some areas on the surface where the water-repellent agent was not applied. I made what was left. As a result, if we create a water-absorbent fabric in which a mixture of water-absorbent and water-repellent parts appears on the surface, and the interior remains entirely water-absorbent, the water absorption remains as it is without significantly decreasing, resulting in a moist feeling. It was found that the
さらに、表面に現われる吸水性部分の幅を５囮以下の小
さなものとして、これを５ ５０ｍ＋の幅を持った撥水
性部分の間に散在させると、吸水性布帛は吸水しても、
−層確実にａｍ感を与えなくなることを見出した。この
発明は、このような知見に基づいてなされたものである
。Furthermore, if the width of the water-absorbing parts that appear on the surface is as small as 5 decoys or less, and these are scattered between water-repellent parts with a width of 5 to 50 m+, the water-absorbing fabric will absorb water, but
- It has been found that the layer reliably does not give an am feeling. This invention was made based on such knowledge.
この発明は、吸水性繊維を含んだ平面状構造物から成り
、表面だけが部分的に撥水剤を付与されて、表面上では
撥水剤の付与された撥水性部分と、撥水・剤の付与され
ていない吸水性部分とが入りまじって存在していること
を特徴とする、湿潤感を与えない吸水性繊維の平面状構
造物を要旨とするものである。This invention consists of a planar structure containing water-absorbing fibers, and only the surface is partially coated with a water-repellent, and the surface has a water-repellent portion coated with a water-repellent and a water-repellent agent. The gist of the present invention is a planar structure of water-absorbing fibers that does not give a wet feeling, and is characterized by the presence of water-absorbing portions that are not provided with water-absorbing portions.
この発明では、吸水性繊維として合成繊維と天然繊維と
の何れも使用することができる。天然繊維としては、木
綿、羊毛、絹などの本来吸水性を持った繊維などを用い
ることができる。そのほか、レーヨンを用いることもで
きる。また、□合成繊維としては、ぎリエステル、ざリ
アクリロニトリル、ポリアミド等の本来吸水性を持たな
いものの表面を化学剤で処理して、吸水性を持たせたも
のを用いることができる。In this invention, both synthetic fibers and natural fibers can be used as the water absorbent fibers. As natural fibers, fibers that inherently have water absorption properties such as cotton, wool, and silk can be used. In addition, rayon can also be used. □As the synthetic fiber, it is possible to use materials such as Giriester, Zaryacrylonitrile, polyamide, etc., which do not inherently have water absorbency, but whose surfaces are treated with a chemical agent to make them water absorbent.
吸水性繊維を含んだ平面状構造物は、上述のような吸水
性繊維だけから成るものであってもよく、また一部が吸
水性繊維であって、非吸水性繊維との混合物であっても
よい。混合物の場合には、吸水性繊維が５０重量％以上
を占めることが望ましい。混合の形態は、混紡であって
も混署織であってもよい。平面状構造物の形態は、織布
であっても編物であっても不織布であってもよい。織布
もその織った態様はどのようであってもよい。平面状構
造物の中で、とくに好ましいのはタオル生地とパイルニ
ット生地とである。The planar structure containing water-absorbing fibers may be composed only of water-absorbing fibers as described above, or may be partially composed of water-absorbing fibers and a mixture with non-water-absorbing fibers. Good too. In the case of a mixture, it is desirable that the water-absorbing fibers account for 50% by weight or more. The form of the mixture may be a blended yarn or a mixed weave. The form of the planar structure may be woven fabric, knitted fabric, or nonwoven fabric. The woven fabric may be woven in any manner. Among the planar structures, towel fabrics and pile knit fabrics are particularly preferred.
木綿繊維を含んだタオル生地とパイルニット生地とは、
充分精練することにより、吸水性の太きい布帛とするこ
とができる。例えば、界−活性剤を含んだ糊抜剤水溶液
に浸漬し、次いで綿蝋除去剤を含んだ水溶液に浸漬し、
続いて金属封鎖剤や過酸化水素のような漂白剤を含んだ
水溶液中に浸漬し、その後吸水性ウレタン樹脂で処理す
ると、非常に吸水性の大きい布帛が得られる。この発明
では、このようなものを用いるのが最も適している。What are towel fabrics and pile knit fabrics that contain cotton fibers?
By sufficiently refining, a fabric with high water absorption can be obtained. For example, immersing in an aqueous desizing agent solution containing a surfactant, then immersing in an aqueous solution containing a cotton wax remover,
Subsequent immersion in an aqueous solution containing a sequestering agent and a bleaching agent such as hydrogen peroxide, followed by treatment with a water-absorbing urethane resin, results in a highly water-absorbing fabric. In this invention, it is most suitable to use such a material.
撥水剤としては、今まで用いられて来た各種のものを用
いることができる。例えば、シリコン樹脂、高融点ワッ
クス、弗素樹脂等を用いることができる。撥水剤は、平
面状構造物の表面だけに、部分的に付与さｎていること
が必要とされる。As the water repellent, various types of water repellents that have been used up to now can be used. For example, silicone resin, high melting point wax, fluororesin, etc. can be used. The water repellent agent is required to be partially applied only to the surface of the planar structure.
これまでは、布帛に均一な撥水性を与えることを目的と
して来たから、布帛用の撥水剤は低粘度のものが多かっ
た。すなわち、布帛の撥水処理は、撥水剤の溶液に布帛
を浸漬したり、撥水剤の溶液を布帛の全面に塗布したり
する方法が専ら採用されたので、撥水剤は、布帛への浸
透をよ′くするために、粘度の低い溶液として用いられ
て来た。また実際の撥水処理にあたっては、布帛の平面
方向にも厚み方向にも、撥水剤をよく浸透させるように
配慮して来た。Up until now, the aim has been to impart uniform water repellency to fabrics, so most water repellents for fabrics have low viscosity. In other words, water repellent treatment for fabrics has been carried out exclusively by immersing the fabric in a water repellent solution or applying a water repellent solution to the entire surface of the fabric. It has been used as a low viscosity solution to improve penetration. Furthermore, in the actual water repellent treatment, care has been taken to ensure that the water repellent agent penetrates well both in the planar direction and the thickness direction of the fabric.
ところが、この発明に係る平面状構造物は、表面方向に
おいて撥水剤の付与された部分と、撥水剤の付与されて
いない部分とを交互に含む必要があるので、従来の撥水
剤付与方法をそのまま適用することができない。そこで
、撥水処理にあたっては、捺染の手段を応用する。すな
わち、撥水剤を捺染糊と混合して粘稠なものとし、この
粘稠物を吸水性布帛の上に部分的に塗布し、撥水剤の塗
布された部分と、撥水剤の塗布されていない部分とを入
りまじって存在させ、その後これを熱処理又は自然乾燥
によって固定化するのである。However, the planar structure according to the present invention needs to alternately include portions to which a water repellent is applied and areas to which no water repellent is applied in the surface direction. The method cannot be applied as is. Therefore, for water-repellent treatment, we apply the method of textile printing. That is, a water repellent agent is mixed with printing paste to make it viscous, and this viscous material is partially applied onto a water-absorbing fabric, and the area coated with the water repellent agent and the area where the water repellent agent is applied are separated. It is made to exist mixed with the untreated parts, and then fixed by heat treatment or natural drying.
布帛を処理するための撥水剤は、通常水を媒体とするエ
マルジョンとされている。しかし、この状態では粘度が
不足している。そこで、水を媒体とした撥水側エマルジ
ョンに、さらに大量の油を加えて粘稠なエマルジョンと
する１例えば、弗素樹脂を撥水剤として使用する場合に
は、弗素樹脂の水性エマルシロン８部に、白灯油エマル
ジョン９２部を加えてよく混合し、粘度７０００センチ
ポイズと言うような高粘性物として、吸水性布帛に塗布
することとする。Water repellents for treating fabrics are generally emulsions containing water as a medium. However, in this state, the viscosity is insufficient. Therefore, a large amount of oil is added to the water-repellent emulsion using water as a medium to make a viscous emulsion.1For example, when using a fluororesin as a water repellent, add 8 parts of the water-based emulsion of the fluororesin to 8 parts of the water-based emulsion. , 92 parts of white kerosene emulsion were added, mixed well, and applied to a water-absorbing fabric as a highly viscous product with a viscosity of 7000 centipoise.
吸水性布帛上に撥水剤を部分的に塗布するには捺染機を
使用することができる。捺染機としては、ロー′う捺染
機、スクリーン捺染機、ロータ１７スクリーン捺染機、
走行式捺染機など各種の捺染機を用いることができる。A printing machine can be used to partially apply the water repellent onto the absorbent fabric. The printing machines include row printing machines, screen printing machines, rotor 17 screen printing machines,
Various textile printing machines such as a traveling textile printing machine can be used.
これらの捺染機を用いて撥水剤を塗布するには、従来の
捺染の技術がそのまま適用できるので、ここでは詳細な
説明を省略する。To apply the water repellent agent using these textile printing machines, conventional textile printing techniques can be applied as they are, so detailed explanation will be omitted here.
この発明では、吸水性布帛の表面上に撥水性部分と吸水
性部分とが交互に存在することが必要である、交互に存
在するＵＳは、第１図に示すように、一方向にだけ交互
になる縞状であってもよく、または二方向に交互となる
格子状であってもよい。In this invention, it is necessary that water-repellent parts and water-absorbing parts exist alternately on the surface of the water-absorbent fabric. It may be in the form of stripes, or it may be in the form of a grid alternating in two directions.
また、第２図に示すように撥水性部分が全表面に広がる
中に、吸水性部分が方形、円形、その信子規則な形状と
なって分散している状態であってもよい。Alternatively, as shown in FIG. 2, the water-repellent portion may be spread over the entire surface, and the water-absorbing portion may be dispersed in a regular shape such as a square or a circle.
吸水性布帛の表面では、少なくとも１つの方向において
、吸水性部分が５−以下の幅を持ち、撥水性部分が５−
５０■の幅を持つことが望ましい。On the surface of the water-absorbing fabric, the water-absorbing portion has a width of 5- or less in at least one direction, and the water-repellent portion has a width of 5- or less.
It is desirable to have a width of 50 cm.
少なくとも１つの方向というのは、幅の最も狭いような
方向を捉えた場合の表現であって、縞状の場合には、縞
幅の方向を基準として、上述のような寸法関係になって
いるという意味である。At least one direction refers to the direction in which the width is the narrowest, and in the case of stripes, the dimensional relationship as described above is based on the direction of the stripe width. That is what it means.
上述の寸法関係は、実験の結果によって得られたもので
ある。一般的にいえば、吸水性部分が比較的小さな幅を
持って、比較的大きな幅のｍ水性部分中に散在している
ときは、吸水性部分が存在しても、全体としては湿潤感
を与えるに至らない、という事実に由来している。具体
的に検討すると、吸水性部分は約５腫が大きさの上限で
あり、撥水性部分は約５閤が大きさの下限であり、５０
閣が大きさの上限であると認められた。The above-mentioned dimensional relationships were obtained from experimental results. Generally speaking, if the water-absorbing areas have a relatively small width and are scattered within a relatively large-width aqueous area, even if the water-absorbing areas are present, the overall feeling of moisture will not be felt. This stems from the fact that it is not enough to give. Specifically, the upper limit of the size of the water-absorbing part is about 5 cm, the lower limit of the water-repellent part is about 5 cm, and the lower limit of the water-repellent part is about 5 cm.
The cabinet was recognized as the upper limit of size.
以上を主として、平面状構造物を表面方向に沿って検討
した場合の説明である。平面状構造物の厚みが小さい場
合には、表面方向の検討だけで足りる０例えば、平面状
構造物として薄い布帛を用い、中に厚い吸水性の不織布
を挿入した場合の薄い布帛は、表面方向の検討だけで足
りる。The above is an explanation mainly based on the case where a planar structure is examined along the surface direction. If the thickness of the planar structure is small, it is sufficient to consider the surface direction. It is sufficient to consider.
ところが、厚みの大きい平面状構造物の場合には、厚み
方向の検討も必要となる。厚み方向では、ｍ水性部分が
表面にだけ存在し、芯部は吸水性部 −分のままで
とどめることが必要である。吸水性の芯部は、平面状構
造物全体の厚みの半分以上の厚みを持って、表面方向に
連続して存在するようにすることが望ましい、とくに、
ｍ水性部分が、平面状構造物全体の表面にだけ部分的に
存在し、表面から少し内部へ入れると、そこではすべて
吸水性繊維のままであることが望ましい、これによって
、平面状構造物は、大きな吸水性をそのまま保持するこ
とになる。However, in the case of a planar structure with a large thickness, consideration in the thickness direction is also required. In the thickness direction, it is necessary that the aqueous portion exists only on the surface and the core portion remains as the water-absorbing portion. It is desirable that the water-absorbing core has a thickness that is at least half the thickness of the entire planar structure and that it exists continuously in the surface direction.
It is desirable that the aqueous portion exists only partially on the entire surface of the planar structure, and once it enters a little inside from the surface, it remains entirely water-absorbing fibers, thereby making the planar structure , it will maintain its high water absorbency.
（発明の効果）
この発明によれば、吸水性繊維を含んだ平面状構造物か
ら成り、表面だけが部分的に撥水剤を付与されたものと
したので、平面状構造物の芯部は吸水性をそのまま保持
していることとなり、従って平面状構造物はもとの吸水
性を大きく失わない。(Effects of the Invention) According to the present invention, since the planar structure is made of a planar structure containing water-absorbing fibers and only the surface is partially coated with a water repellent, the core of the planar structure is This means that the water absorbency is maintained as is, and therefore, the planar structure does not lose its original water absorbency to a large extent.
また、表面状では、搗水剤の付与された撥水性部分と、
撥水剤の付与されていない吸水性部分とが、交互に存在
することにしたので、表面に存在する水分は吸水性部分
を通して芯部に吸収されるので、表面に水分が水滴とな
って溜まるに至らないし、また布帛が吸水しても湿潤感
を与えるに至らない。In addition, on the surface, a water-repellent part with a water-repellent added,
Since the water-absorbing parts to which no water-repellent agent has been applied are arranged alternately, the water present on the surface is absorbed into the core through the water-absorbing parts, and the water collects on the surface in the form of water droplets. Even if the fabric absorbs water, it does not give a moist feeling.
とくに、吸水性部分が少なくとも１つの方向において、
５１以下の幅を持ワて、５−５０ｍあ幅を持ったｍ水性
部分中に介在していることとすれば、吸水性部分が大量
の水分を吸収して湿った状態にあっても、吸水性部分が
大きな集塊となって存在しないため、撥水性部分の乾い
た状態に圧倒されて、全く湿潤感を与えないものとなる
。このため、この平面状構造物は、自体に直接接触して
よく水分を吸収し、吸収したあとも湿潤感を与えないも
のとなる。従って、この平面状構造物は肌着、オムツ、
オネシヲマット等に好適なものとなる。In particular, the water-absorbing portion in at least one direction,
If the water-absorbing part has a width of 51 m or less and is interposed in an aqueous part with a width of 5-50 m, even if the water-absorbing part absorbs a large amount of water and is in a wet state, Since the water-absorbing portion does not exist as a large agglomerate, the water-repellent portion is overwhelmed by the dry state and does not give a wet feeling at all. Therefore, this planar structure absorbs moisture well by directly contacting itself, and does not give a wet feeling even after absorbing moisture. Therefore, this planar structure can be used for underwear, diapers,
It is suitable for one-sided mats, etc.
なお、オムツ又はオネシッマットに使用するときは、平
面状構造物の片面だけに撥水剤を付与し、他の面上には
不透水性の樹脂シートを貼りつける。When used in diapers or one-sided mats, a water repellent is applied to only one side of the planar structure, and a water-impermeable resin sheet is pasted on the other side.
不透水性の樹脂シートは、ウレタン樹脂、アクリル樹脂
又は軟質塩化ビニル樹脂を材料として、平面状構造物の
延びとおなじような延び杢持ったものとする。The water-impermeable resin sheet is made of urethane resin, acrylic resin, or soft vinyl chloride resin and has the same elongation as the planar structure.
次に、実施例を挙げて、この発明に係る平面状構造物を
具体的に説明する。Next, the planar structure according to the present invention will be specifically explained with reference to Examples.
実施例１
まず、綿１００％のタオル生機を糊抜、精練、晒、吸水
加工の処理をして、吸水性の布帛を作った。その詳細は
次のとおりである。タオル生機を糊抜剤（洛東化成社製
、ラクトーゼＡＣＲ）０．５％、界面活性剤（里田化工
社製、ニスノンＨ）０．５％の水溶液中に、９５〜１０
０℃で、１時間浸漬し、水洗する０次に、乳化剤（日本
東北社製、センカノール１２）０．５％、苛性ソーダ１
％、炭酸ソーダ２％の水溶液に、９５〜１００℃で、１
時間浸漬し、綿蝋を除去した。続いて、３５％の過酸化
水素の水溶液８％、珪酸ナトリウム１％、エチレンジア
ミンテトラアセチックアシド０．５％の水溶液に、９５
〜９８℃で１時間浸漬し、その後水洗し脱水乾燥した。Example 1 First, a 100% cotton greige towel was subjected to desizing, scouring, bleaching, and water-absorbing processing to produce a water-absorbent fabric. The details are as follows. A rag towel was placed in an aqueous solution of 0.5% desizing agent (Lactose ACR, manufactured by Rakuto Kasei Co., Ltd.) and 0.5% surfactant (Nisnon H, manufactured by Satoda Kako Co., Ltd.) at 95 to 10%.
Soak for 1 hour at 0°C and wash with water. Next, add 0.5% emulsifier (Senkanol 12, manufactured by Nippon Tohoku Co., Ltd.) and 1% caustic soda.
%, 1% in an aqueous solution of 2% soda carbonate at 95-100°C.
The cotton wax was removed by soaking for an hour. Subsequently, 95% of an aqueous solution of 35% hydrogen peroxide, 1% sodium silicate, and 0.5% ethylenediaminetetraacetic acid was added.
It was immersed at ~98°C for 1 hour, then washed with water and dehydrated and dried.
さらに、ウレタン処理剤（日華化学社製、エバハノール
Ｎ７）３％水溶液で処理し、１５０℃で３分間熱処理し
て、吸水性布帛を得た。Furthermore, it was treated with a 3% aqueous solution of a urethane treatment agent (manufactured by Nicca Chemical Co., Ltd., Evahanol N7) and heat-treated at 150° C. for 3 minutes to obtain a water-absorbent fabric.
上記の吸水性布帛を次のようにして撥水剤処理した。撥
水剤としては、弗素樹脂を用いた。具体的には、弗素樹
脂の水性エマルジョン（敷島紡績社製、エクスト）８部
、白灯油エマルジョン９２部を混合して、粘度７０００
センチボイズの粘稠な撥水糊を作った。The above water absorbent fabric was treated with a water repellent agent as follows. A fluororesin was used as the water repellent. Specifically, 8 parts of aqueous fluororesin emulsion (manufactured by Shikishimabo Co., Ltd., Ext) and 92 parts of white kerosene emulsion were mixed to obtain a viscosity of 7000.
I made Centiboise's viscous water-repellent glue.
ロータリースクリーン捺染機を使用して、この撥水糊を
布帛の片面だけに縞状に塗布した。具体的には、第１図
に示したように、溌水糊の塗布部分１が５閣の幅を持ち
、０．４ ｔｍの未塗布部分２をあけて配置されている
ようにした。その後、１２０℃で５分間乾燥し、続いて
１５０°Ｃで３分間熱処理により固定化して、この発明
に係る布帛を得た。This water-repellent paste was applied in stripes on only one side of the fabric using a rotary screen printing machine. Specifically, as shown in FIG. 1, the areas 1 coated with water-repellent glue had a width of 5 squares, and were arranged with an unapplied area 2 of 0.4 tm open. Thereafter, it was dried at 120°C for 5 minutes, and then fixed by heat treatment at 150°C for 3 minutes to obtain a fabric according to the present invention.
この布帛は、充分な吸水性を持ち、吸水量１３０％にな
っても、なお湿濡感を与えなかった。従って、この布帛
は吸水性肌着として好適なものであヮた。This fabric had sufficient water absorption and did not give a wet feeling even when the water absorption amount was 130%. Therefore, this fabric was suitable as a water absorbent underwear.
さらに、この布帛の他面全体にウレタンフィルムを貼り
合わせた。このものは、水を外へもらさないので、オム
ツ又はオネジぢマットとして好適であった。Furthermore, a urethane film was attached to the entire other side of this fabric. This product was suitable for use as a diaper or male screw mat because it did not allow water to leak out.
実施例２
綿５０％、ポリエステル５０％のパイルニット生地を実
施例１と同様にして糊抜、精練、晒、吸水加工を行って
、吸水性布帛を得た。Example 2 A pile knit fabric of 50% cotton and 50% polyester was subjected to desizing, scouring, bleaching, and water absorption processing in the same manner as in Example 1 to obtain a water absorbent fabric.
撥水剤としてシリコン樹脂を用いて、以下に述べるよう
にして撥水剤を塗布した。まず、シリコン樹脂（明成化
学社製、アサヒシリコンリベラント７０２）１０部、白
灯油９０部を混合し、粘度７０００センチポイズの粘稠
な撥水糊を作り、これをオートスクリーン捺染機により
布帛の片面だけに塗布した。塗布した状態は、第２図に
示したように、塗布部分ｌが全体に広がる中に、未塗布
部分２が５ｍＸ２−の矩形となって分散されているよう
にした。その後１２０℃で５分間乾趨し、次いで１５０
℃で３分間熱処理により固定化して、この発明に係る布
帛を得た。A silicone resin was used as a water repellent, and the water repellent was applied as described below. First, 10 parts of silicone resin (Asahi Silicon Liberant 702 manufactured by Meisei Kagaku Co., Ltd.) and 90 parts of white kerosene were mixed to make a viscous water-repellent glue with a viscosity of 7000 centipoise, and this was applied to one side of the fabric using an autoscreen printing machine. It was applied only to The applied state was such that, as shown in FIG. 2, the uncoated area 2 was dispersed in a rectangular shape of 5 m x 2 - while the applied area 1 was spread over the entire area. It was then dried at 120°C for 5 minutes, and then dried at 150°C.
The fabric was fixed by heat treatment at ℃ for 3 minutes to obtain a fabric according to the present invention.
この布帛は、充分な吸水性を持ち、吸水量１００％でも
、なお湿濡感を与えなかった。従って、この布帛は吸水
性肌着として好適なものであった。This fabric had sufficient water absorption and did not give a wet feeling even when the water absorption amount was 100%. Therefore, this fabric was suitable as a water absorbent underwear.
さらに、この布帛の他面全体にアクリル樹脂フィルムを
貼り合わせた。このものは、水を外へ漏らさないので、
オムツ又はオネジ！マットとして好適であった。Furthermore, an acrylic resin film was attached to the entire other side of this fabric. This item does not leak water, so
Diaper or male screw! It was suitable as a mat.
第１図及び第２図は、この発明に係る平面状構造物の平
面図であって、撥水剤の塗布部分と非塗布部分との配置
関係を示している。
図において、ｌは塗布部分（出水性部分）であり、２は
非塗布部分（Ｗ＆水性部分）である。FIGS. 1 and 2 are plan views of a planar structure according to the present invention, showing the arrangement relationship between a portion coated with a water repellent and a portion not coated with a water repellent. In the figure, 1 is a coated part (water-generating part), and 2 is a non-coating part (W&aqueous part).
Claims (1)
けが部分的に撥水剤を付与されて、表面上では撥水剤の
付与された撥水性部分と、撥水剤の付与されてない吸水
性部分とが入りまじつて存在していることを特徴とする
、湿濡感を与えない吸水性繊維の平面状構造物。 ２、吸水性繊維を含んだ平面状構造物から成り、表面だ
けが部分的に撥水剤を付与されて、表面上では撥水剤の
付与された撥水性部分と、撥水剤の付与されていない吸
水性部分とが入りまじつて存在し、吸水性部分が少なく
とも１つの方向において、５ｍｍ以下の幅を持つて、５
−５０ｍｍの幅を持つた撥水性部分中に介在しているこ
とを特徴とする、湿濡感を与えない吸水性繊維の平面状
構造物。 ３、撥水剤の水性エマルジョンに捺染糊を加えて粘稠な
エマルジョンとし、この粘稠物を吸水性繊維の含まれた
平面状構造物の表面に部分的に塗布し、塗布部分と非塗
布部分とを表面上に入りまじつて存在させ、これを固定
化することを特徴とする、湿濡感を与えない吸水性繊維
の平面状構造物を製造する方法。[Scope of Claims] 1. Consisting of a planar structure containing water-absorbing fibers, only the surface of which is partially coated with a water-repellent agent; A planar structure of water-absorbing fibers that does not give a wet feeling and is characterized by the presence of water-absorbing portions to which no water repellent has been applied. 2. It consists of a planar structure containing water-absorbing fibers, and only the surface is partially coated with a water-repellent, and on the surface there are water-repellent parts coated with the water-repellent and areas where the water-repellent is coated with the water-repellent. 5 mm or less, and the water absorbing portion has a width of 5 mm or less in at least one direction.
- A planar structure of water-absorbing fibers that does not give a wet feeling and is characterized by being interposed in a water-repellent portion having a width of 50 mm. 3. Add printing paste to the water-based emulsion of the water repellent agent to make a viscous emulsion, and partially apply this viscous substance to the surface of the planar structure containing water-absorbing fibers, separating the coated and uncoated areas. 1. A method for manufacturing a planar structure of water-absorbing fibers that does not give a wet feeling, the method comprising making a part intermixed with a surface and fixing the part.