JPH03217300A - 汚泥用脱臭固化剤 - Google Patents
汚泥用脱臭固化剤Info
- Publication number
- JPH03217300A JPH03217300A JP1208090A JP1208090A JPH03217300A JP H03217300 A JPH03217300 A JP H03217300A JP 1208090 A JP1208090 A JP 1208090A JP 1208090 A JP1208090 A JP 1208090A JP H03217300 A JPH03217300 A JP H03217300A
- Authority
- JP
- Japan
- Prior art keywords
- sludge
- deodorizing
- calcium oxide
- fly ash
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は、海域、湖沼、河川、下水及び生活排水から発
生するしゅんせつされた汚泥の脱臭固化処理させるため
の脱臭固化剤に関する。
生するしゅんせつされた汚泥の脱臭固化処理させるため
の脱臭固化剤に関する。
（従来の技術及び解決するための課題）生活排水、産業
排水等から発生する汚泥は河川、湖沼、港湾などの水域
に堆積し、流路や航路の閉塞を起こすばかりでなく、魚
介類をはじめとする生物の棲息を阻害するばかりでなく
、環境汚染による社会的問題を引き起こしている。汚泥
の処理方法として主に行われている海洋投棄は禁止され
る方向にあり、このため汚泥は埋め立て等で処理しなけ
ればならなくなる。従来埋め立て処理する場合、土壌固
化材を用いて汚泥の固化処理を行うが、処理時及び処理
後の汚泥から発生する悪臭を除去することが出来ない。
排水等から発生する汚泥は河川、湖沼、港湾などの水域
に堆積し、流路や航路の閉塞を起こすばかりでなく、魚
介類をはじめとする生物の棲息を阻害するばかりでなく
、環境汚染による社会的問題を引き起こしている。汚泥
の処理方法として主に行われている海洋投棄は禁止され
る方向にあり、このため汚泥は埋め立て等で処理しなけ
ればならなくなる。従来埋め立て処理する場合、土壌固
化材を用いて汚泥の固化処理を行うが、処理時及び処理
後の汚泥から発生する悪臭を除去することが出来ない。
また、汚泥の悪臭処理材としては植物精油を主体とした
もの（特開昭６３−１９７５７０）、活性炭等を用いら
れているが必ずしも充分な効果を得ることが出来ない。
もの（特開昭６３−１９７５７０）、活性炭等を用いら
れているが必ずしも充分な効果を得ることが出来ない。
このため、脱臭固化を同時に行える脱臭固化剤の開発が
望まれていた。
望まれていた。
（課題を解決するための手段）
本発明者は、汚泥の脱臭固化を同時に行うことのできる
脱臭固化剤を鋭意検討した結果、少なくともアルカリ金
属又はアルカリ土類金属を除く金属の強酸塩とフライア
ッシュ及び酸化カルシウムを主成分とする混合物が汚泥
の脱臭固化剤として有効であることを見いだし本課題を
解決することが出来た。
脱臭固化剤を鋭意検討した結果、少なくともアルカリ金
属又はアルカリ土類金属を除く金属の強酸塩とフライア
ッシュ及び酸化カルシウムを主成分とする混合物が汚泥
の脱臭固化剤として有効であることを見いだし本課題を
解決することが出来た。
本発明に用いられる金属の強酸塩はアルカリ金属又はア
ルカリ土類金属の強酸塩であれば如何なるものでもよい
。一例を挙げるとすればアルミニウム、亜鉛、鉄、銅、
、マンガン、コバルト、ニッケルなどの硫酸塩、硝酸塩
、塩化物を挙げることが出来る。好ましくは、硫酸アル
ミニウム、硫酸亜鉛、硫酸第一鉄を挙げることが出来る
。本発明に用いるフライアツシュはＪＩＳに定義されて
いるものか又はそれ相当品であればよい。その組成の一
例を挙げるとＳｉ０２が４５〜５５重量％、Ａ１２０３
が２２〜２７重量％で残りが鉄、カルシウム、カリウム
等の酸化物である。粒度は３２〜２００メッシュが好ま
しいが、必ずしもこの数値に限定されるものではない。
ルカリ土類金属の強酸塩であれば如何なるものでもよい
。一例を挙げるとすればアルミニウム、亜鉛、鉄、銅、
、マンガン、コバルト、ニッケルなどの硫酸塩、硝酸塩
、塩化物を挙げることが出来る。好ましくは、硫酸アル
ミニウム、硫酸亜鉛、硫酸第一鉄を挙げることが出来る
。本発明に用いるフライアツシュはＪＩＳに定義されて
いるものか又はそれ相当品であればよい。その組成の一
例を挙げるとＳｉ０２が４５〜５５重量％、Ａ１２０３
が２２〜２７重量％で残りが鉄、カルシウム、カリウム
等の酸化物である。粒度は３２〜２００メッシュが好ま
しいが、必ずしもこの数値に限定されるものではない。
この範囲の粒度のものは粉塵発生によるトラブルも少な
く脱臭固化効率もよい。
く脱臭固化効率もよい。
該金属塩とフライアッシュとの比率は如何なる割合でも
よいが、好ましくは、金属塩２〜４０重量％、フライア
ッシュ６０〜９８％程度がよい。金属塩を多量に用いる
と例えば６０重量％以上になると汚泥の固化強度に悪影
響を及ぼす恐れがある。
よいが、好ましくは、金属塩２〜４０重量％、フライア
ッシュ６０〜９８％程度がよい。金属塩を多量に用いる
と例えば６０重量％以上になると汚泥の固化強度に悪影
響を及ぼす恐れがある。
本発明に使用される酸化カルシウムは単独か又は例えば
二酸化ケイ素、酸化アルミニウム、酸化第二鉄等の様な
酸化物との混合物でもよい。混合物の場合、酸化カルシ
ウムは５０〜７０重量％程度含有することが好ましい。
二酸化ケイ素、酸化アルミニウム、酸化第二鉄等の様な
酸化物との混合物でもよい。混合物の場合、酸化カルシ
ウムは５０〜７０重量％程度含有することが好ましい。
又、最も好ましいのは該混合物中に二酸化ケイ素が１５
〜２５重量％、酸化カルシウムが５５〜６０重量％の割
合で配合されている混合物である。該混合物としてはセ
メント系固化材、土壌改良固化材として市販されている
ものを用いることも出来る。例示すれば商品名ダイセル
化学工業株式会社製セルベース［相］ハードを挙げるこ
とが出来る。
〜２５重量％、酸化カルシウムが５５〜６０重量％の割
合で配合されている混合物である。該混合物としてはセ
メント系固化材、土壌改良固化材として市販されている
ものを用いることも出来る。例示すれば商品名ダイセル
化学工業株式会社製セルベース［相］ハードを挙げるこ
とが出来る。
本発明に使用する脱臭固化剤は汚泥の臭気の程度、含水
比土質によって異なるが、通常汚泥に対し該金属塩とフ
ライアッシュとの混合物は２０重量％以下、好ましくは
５重量％以下で該酸化カルシウム又は該混合物は２０重
量％以下で、好ましくは１０重量％以下がよい。
比土質によって異なるが、通常汚泥に対し該金属塩とフ
ライアッシュとの混合物は２０重量％以下、好ましくは
５重量％以下で該酸化カルシウム又は該混合物は２０重
量％以下で、好ましくは１０重量％以下がよい。
以下、実施例を挙げて本発明を詳細に説明する。
（実施例）
実施例エ
硫酸第一鉄の１水塩１０重量部、フライアツシュ９０重
量部との混合物Ａを調製した。
量部との混合物Ａを調製した。
兵庫県姫路市の河川よりヘドロを採取し、ＪＩＳＡ１２
０３による含水率５９．３％のヘドロ１０００ｇを３ｌ
のステンレス製バットに入れ、１１．５ｌのデシケータ
ー中に入れた。
０３による含水率５９．３％のヘドロ１０００ｇを３ｌ
のステンレス製バットに入れ、１１．５ｌのデシケータ
ー中に入れた。
一方ヘトロ１０００ｇに酸化カルシウム混合物Ｂ（酸化
カルシウム６０％、二酸化ケイ素２０％、酸アルミニウ
ム１０％、酸化第二鉄２％、酸化マグネシウム１％、三
酸化イオウ８％、その他１％）１００ｇ ，２００ｇと
混合物Ａ Ｏｇ ， ５０ｇ ， １００ｇ ， ２０
０ｇとの組合せ混練りし、試料を調整したものを各々１
１．５ｊのデシケーター中に入れた。
カルシウム６０％、二酸化ケイ素２０％、酸アルミニウ
ム１０％、酸化第二鉄２％、酸化マグネシウム１％、三
酸化イオウ８％、その他１％）１００ｇ ，２００ｇと
混合物Ａ Ｏｇ ， ５０ｇ ， １００ｇ ， ２０
０ｇとの組合せ混練りし、試料を調整したものを各々１
１．５ｊのデシケーター中に入れた。
各々のデシケーター中のアンモニア、硫化水素を測定し
、更に官能法による脱臭評価試験を行った。
、更に官能法による脱臭評価試験を行った。
官能試験の評価基準は６段階臭気強度表示法を用い、６
人のパネラーの平均値とした。
人のパネラーの平均値とした。
試料調製後、材令３日の一軸圧縮試験をＪＩＳＡ１２１
６の方法により強度を測定した。
６の方法により強度を測定した。
測定結果を表−１に示す。
実施例２
硫酸アルミニウムの１８水塩１ｏ重量部、フライアッシ
ュ９０重量部との混合物Ａを調製した。
ュ９０重量部との混合物Ａを調製した。
以下、実施例１と同様の試験を行い結果を表一２に示す
。
。
（発明の効果）
本発明の脱臭固化剤は脱臭効果が大きいばかりでなく、
固化物の強度も酸化カルシウム混合物単独処理よりも大
きく、良好な効果を得ることができた。又、本脱臭固化
剤はしゅんせつヘドロばかりでなく湖沼等で発生するア
オコ、藻類等を回収し、脱臭固化して埋立て処理に使用
することも出来る。
固化物の強度も酸化カルシウム混合物単独処理よりも大
きく、良好な効果を得ることができた。又、本脱臭固化
剤はしゅんせつヘドロばかりでなく湖沼等で発生するア
オコ、藻類等を回収し、脱臭固化して埋立て処理に使用
することも出来る。
Claims (1)
- 少なくともアルカリ金属又はアルカリ土類金属を除く金
属の強酸塩とフライアッシュ及び酸化カルシウムを主成
分とする汚泥用脱臭固化剤。