JPH0324180A - 防汚用組成物 - Google Patents
防汚用組成物Info
- Publication number
- JPH0324180A JPH0324180A JP15851389A JP15851389A JPH0324180A JP H0324180 A JPH0324180 A JP H0324180A JP 15851389 A JP15851389 A JP 15851389A JP 15851389 A JP15851389 A JP 15851389A JP H0324180 A JPH0324180 A JP H0324180A
- Authority
- JP
- Japan
- Prior art keywords
- rosin
- citrate
- antifouling
- metallic copper
- adhesion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明は海棲生物及び海藻類の付着防止用組成物に関す
るものである。
るものである。
〔従来の技術１
船底、海中構造物、各穏浮子類，各種魚網及びその他海
中に長期間浸漬する各種器具類には海棲生物の付看及び
それによる腐蝕を防止するため、これら器具類の表面に
海棲生物の付着防止用組成物を塗布している． しかしながら、従来この種の目的に使用されていた組成
物の多くは、毒物を常に僅かずつ海中に溶出させること
によって海棲生物の付着や成長を防止するものであるた
め効果の持続期間が短く、しがち海洋汚染の原因にもな
るという欠点があった． ［発明が解決しようとする課題］ このような欠点を解消するため、先に本発明者らは微粒
子状金属鋼とロジン系樹脂又はクマロン系樹脂の混合物
をセルローズ系高分子からなるＲ着剤中に分散してなる
組成物を提案し、特許出願（特公昭５３−６６６１号公
報）した。このものは上記欠点は有しないが、使用する
海域によって防汚効果が低下する事が判明したので調査
した結果、奥深い湾内での停滞水域では現地でヌタと呼
ばれているスライム（粘着性微生物群）が付着し、この
上に多毛類、ワレカラ類が付着し防汚効果が３〜４ケ月
後あたりから減少するという問題が生じていることがわ
かった。
中に長期間浸漬する各種器具類には海棲生物の付看及び
それによる腐蝕を防止するため、これら器具類の表面に
海棲生物の付着防止用組成物を塗布している． しかしながら、従来この種の目的に使用されていた組成
物の多くは、毒物を常に僅かずつ海中に溶出させること
によって海棲生物の付着や成長を防止するものであるた
め効果の持続期間が短く、しがち海洋汚染の原因にもな
るという欠点があった． ［発明が解決しようとする課題］ このような欠点を解消するため、先に本発明者らは微粒
子状金属鋼とロジン系樹脂又はクマロン系樹脂の混合物
をセルローズ系高分子からなるＲ着剤中に分散してなる
組成物を提案し、特許出願（特公昭５３−６６６１号公
報）した。このものは上記欠点は有しないが、使用する
海域によって防汚効果が低下する事が判明したので調査
した結果、奥深い湾内での停滞水域では現地でヌタと呼
ばれているスライム（粘着性微生物群）が付着し、この
上に多毛類、ワレカラ類が付着し防汚効果が３〜４ケ月
後あたりから減少するという問題が生じていることがわ
かった。
本発明はこのような従来の問題点を解決した海棲生物の
付着防止用組成物を提供しようとするものであり、先に
本発明者らが提案し、特許出願した防汚組成物にクエン
酸塩を添加することによって組成物の防汚性が抜群に改
善されることを知見し、本発明に到達した． 本発明で使用する微粒子状金属銅とは２００メシュ以下
の粉末状あるいは燐片状のもので、特に表面の酸化され
ていないものを使用するのが好ましい．又該金属銅と混
合するロジン系樹脂、クマロン系樹脂の例としては、水
素化ロジン、重合ロジン、脱水素ロジン、ロジンエステ
ル、マロン樹脂、クマロンインデン樹脂等が挙げられる
．本発明におけるセルローズ系高分子物質とは、例えば
メチルセルローズ、エチルセルローズ、ニトロセルロー
ズ、アセチルセルローズ等である． 本発明の組成物はクエン酸塩を含有する必要があるが、
クエン酸塩を含有させることによって海棲生物の付着防
止効果を更に増強し、長期間安定して使用することがで
きる．ここでクエン酸塩としては広く使用されている、
一Ｍ式Ｍ （Ｃ．Ｈ．０，） ・ＸＩ｛．０ （Ｍ！−
［、鉄、亜鉛、マクネシウム等の金属、Ｘは水の分子量
に対する係数）で表わされるクエン酸の金属塩を用いる
ことができ、好ましくは例えばクエン酸鉄をあげること
ができる． 本発明組成物は、必要に応じ上記のもののばか従来この
種の組成物に加えられている充填剤、着色材、安定剤等
の助剤を加えることができる． 本発明の使用に当っては、まず微粒子状金属銅とクエン
酸塩を混合し、さらにロジン系樹脂又はクマロン系樹脂
を添加混合し、これに公知の安定剤、可塑剤等を添加し
、このものをセルローズ系高分子物質よりなる展看剤中
に分散せしめ、更にジクロロフエン及び希釈剤のトルエ
ンを加え、あるいは、また必要に応じてペンガラ、充填
剤等を加えて混合撹拌し防汚用組成物となすちのである
． 本発明の防汚用組成物の各構成成分の量は、防汚する被
塗布物の種類に応じて変化させることができるが、一般
には固形分に対して、微粒子状金属銅５〜３０重量％，
クエン酸塩１０〜２０重量％とすることが好ましい． 本発明の組成物には海棲生物の付着防止効果を更に高め
るため、水に対する溶解度の極めて小さい他の防虫防藻
剤、例えばＤＣＭＵ，チアベンダゾール、ＴＰＮ，シマ
ジン、プロメトリン、ＡＣＮ，等を含有させることもで
きる．防虫防藻剤の添加量は、固形物１００重量部に対
して５〜ｉｏｚ量部使用するのが好ましい．このような
防虫防藻剤を混入させてもこのものは溶解度が非常に小
さく、しかもセルローズ系高分子物質を使用しているた
め、該セルローズ系高分子物質中に銅と共に溶解分散し
ているロジン系樹脂又はクロマン系樹脂に包含されるた
め、この防虫防藻剤の海中への溶出は極度に抑制される
． 本発明の組成物は、船底、漁網、港湾関係海中構造物、
各種浮子類、養殖用いかだ及びその他海中に長期間浸漬
する各種器具類等のような海棲生物の付着防止が要求さ
れるあらゆるちのの海棲生物付着防止に使用することが
できる．［実施例１ 次ぎに実施例を挙げて本発明を更に説明するが、本発明
はこれら実施例に限定されない。
付着防止用組成物を提供しようとするものであり、先に
本発明者らが提案し、特許出願した防汚組成物にクエン
酸塩を添加することによって組成物の防汚性が抜群に改
善されることを知見し、本発明に到達した． 本発明で使用する微粒子状金属銅とは２００メシュ以下
の粉末状あるいは燐片状のもので、特に表面の酸化され
ていないものを使用するのが好ましい．又該金属銅と混
合するロジン系樹脂、クマロン系樹脂の例としては、水
素化ロジン、重合ロジン、脱水素ロジン、ロジンエステ
ル、マロン樹脂、クマロンインデン樹脂等が挙げられる
．本発明におけるセルローズ系高分子物質とは、例えば
メチルセルローズ、エチルセルローズ、ニトロセルロー
ズ、アセチルセルローズ等である． 本発明の組成物はクエン酸塩を含有する必要があるが、
クエン酸塩を含有させることによって海棲生物の付着防
止効果を更に増強し、長期間安定して使用することがで
きる．ここでクエン酸塩としては広く使用されている、
一Ｍ式Ｍ （Ｃ．Ｈ．０，） ・ＸＩ｛．０ （Ｍ！−
［、鉄、亜鉛、マクネシウム等の金属、Ｘは水の分子量
に対する係数）で表わされるクエン酸の金属塩を用いる
ことができ、好ましくは例えばクエン酸鉄をあげること
ができる． 本発明組成物は、必要に応じ上記のもののばか従来この
種の組成物に加えられている充填剤、着色材、安定剤等
の助剤を加えることができる． 本発明の使用に当っては、まず微粒子状金属銅とクエン
酸塩を混合し、さらにロジン系樹脂又はクマロン系樹脂
を添加混合し、これに公知の安定剤、可塑剤等を添加し
、このものをセルローズ系高分子物質よりなる展看剤中
に分散せしめ、更にジクロロフエン及び希釈剤のトルエ
ンを加え、あるいは、また必要に応じてペンガラ、充填
剤等を加えて混合撹拌し防汚用組成物となすちのである
． 本発明の防汚用組成物の各構成成分の量は、防汚する被
塗布物の種類に応じて変化させることができるが、一般
には固形分に対して、微粒子状金属銅５〜３０重量％，
クエン酸塩１０〜２０重量％とすることが好ましい． 本発明の組成物には海棲生物の付着防止効果を更に高め
るため、水に対する溶解度の極めて小さい他の防虫防藻
剤、例えばＤＣＭＵ，チアベンダゾール、ＴＰＮ，シマ
ジン、プロメトリン、ＡＣＮ，等を含有させることもで
きる．防虫防藻剤の添加量は、固形物１００重量部に対
して５〜ｉｏｚ量部使用するのが好ましい．このような
防虫防藻剤を混入させてもこのものは溶解度が非常に小
さく、しかもセルローズ系高分子物質を使用しているた
め、該セルローズ系高分子物質中に銅と共に溶解分散し
ているロジン系樹脂又はクロマン系樹脂に包含されるた
め、この防虫防藻剤の海中への溶出は極度に抑制される
． 本発明の組成物は、船底、漁網、港湾関係海中構造物、
各種浮子類、養殖用いかだ及びその他海中に長期間浸漬
する各種器具類等のような海棲生物の付着防止が要求さ
れるあらゆるちのの海棲生物付着防止に使用することが
できる．［実施例１ 次ぎに実施例を挙げて本発明を更に説明するが、本発明
はこれら実施例に限定されない。
以下に実施例並びに実験結果を示す。
次ぎの３種類の防汚用組成物を調製した．なお、％は重
量％を示す． Ｎｏ． １ 金属銅粉末 ５％ク
エン酸鉄 １０％ ジ才クチルフクレート ３％ ベンガラ ３％ジクロロフエン
２％ 水素化ロジン １０％ ２０％エチルセルローズ アルコール溶液 ３０％ トルエン ３７％ Ｎｏ． ２ 金属銅粉末 クエン酸鉄 クロマン樹脂 ジオクチルフクレ−１・ ジクロロフエン ２０％エチルセルローズ アルコール溶液 トルエン １ ０ ％ １ ５ ％ １ ０％ ５％ ２ ％ ３ ０％ ２ ８％ Ｎｏ、４ 金膚銅粉末 水素化口ジン ジ才クチルフタレーｌ・ ベンガラ ジク・ロロフエン ２０％エチルセルローズ アルコール溶液 トルエン ３％ １ ０％ ３ ％ ３％ ２ ％ ３ ０％ ４ ９ ％ Ｎｏ． ３ 金属銅粉末 クエン酸銅 水素化ロジン ジオクチルフタレート ジクロロフエン ２０％エチルセル口ーズ アルコール溶液 トルエン １ ５％ 】 ５％ ８ ％ ５％ ３％ ２ ５％ Ｎｏ． ５ 金属銅粉末 クロマン樹脂 ジオクチルフタレート ジク口ロフエン ２０％エチルセルローズ アルコール溶液 トルエン １ ５ ％ １０ ％ ５ ％ ２ ％ ３ ０％ ３ ８％ ２ ９％ なお比較例として次ぎの防汚組成物を調製した． 更に市販の防汚剤Ａ，Ｂ，二社のものを同時に実験に供
した． 上記の各防汚用組成物中にポリエチレン無結節網（６０
本より、６節のものを使用．大きさは４０ロｍｆｆｌＸ
４００ｍｍ）をｌＯ分間浸漬後風乾する．そして処
理した漁網を経８ｍ＋Ｉ１の曲加工した６００ｍｍＸ
６００ｍｍの鉄製外枠の四隅に銅線で取り付け、静岡
県沼津市静浦沖５００Ｍの海面下水深１．５−２，ＯＭ
の所に懸垂して１２ケ月間浸漬し、各月の海棲生物及び
海藻類の付着程度を調べた結果を第ｌ図に示す．又付看
生物の種類については第１表に示す． ｌ）防汚効果の判定は、網を覆った付着生物の付着面積
（対照区を１とする）によって判定する． Ｏ＝付着なし ○＝付着が対照区の１／３以内 ●；付着が対照区の２７３以内 ×＝付着が対照区の２／３以上 ２）試験網の湿重量の測定 懸垂ローブより枠を取り外し、枠と網を一緒に測定し、
この測定重量より原重量を差し引き、付着物の重量を算
出する． 第１表 ｉ２ケ月目における生物種と付着量 第１表の結果より明らかなように、比較例ではスライム
、ワレカラ、カサネカンザシ等の付着がみられたが、実
施例ではこれら生物の付着がなく、しかち第１図に示す
ごとく他の海棲生物や海藻類等の付着も少なく、本発明
による防汚用組成物は、長期にわたって海棲付着生物の
付着を防止しつる利点を有するものである．
量％を示す． Ｎｏ． １ 金属銅粉末 ５％ク
エン酸鉄 １０％ ジ才クチルフクレート ３％ ベンガラ ３％ジクロロフエン
２％ 水素化ロジン １０％ ２０％エチルセルローズ アルコール溶液 ３０％ トルエン ３７％ Ｎｏ． ２ 金属銅粉末 クエン酸鉄 クロマン樹脂 ジオクチルフクレ−１・ ジクロロフエン ２０％エチルセルローズ アルコール溶液 トルエン １ ０ ％ １ ５ ％ １ ０％ ５％ ２ ％ ３ ０％ ２ ８％ Ｎｏ、４ 金膚銅粉末 水素化口ジン ジ才クチルフタレーｌ・ ベンガラ ジク・ロロフエン ２０％エチルセルローズ アルコール溶液 トルエン ３％ １ ０％ ３ ％ ３％ ２ ％ ３ ０％ ４ ９ ％ Ｎｏ． ３ 金属銅粉末 クエン酸銅 水素化ロジン ジオクチルフタレート ジクロロフエン ２０％エチルセル口ーズ アルコール溶液 トルエン １ ５％ 】 ５％ ８ ％ ５％ ３％ ２ ５％ Ｎｏ． ５ 金属銅粉末 クロマン樹脂 ジオクチルフタレート ジク口ロフエン ２０％エチルセルローズ アルコール溶液 トルエン １ ５ ％ １０ ％ ５ ％ ２ ％ ３ ０％ ３ ８％ ２ ９％ なお比較例として次ぎの防汚組成物を調製した． 更に市販の防汚剤Ａ，Ｂ，二社のものを同時に実験に供
した． 上記の各防汚用組成物中にポリエチレン無結節網（６０
本より、６節のものを使用．大きさは４０ロｍｆｆｌＸ
４００ｍｍ）をｌＯ分間浸漬後風乾する．そして処
理した漁網を経８ｍ＋Ｉ１の曲加工した６００ｍｍＸ
６００ｍｍの鉄製外枠の四隅に銅線で取り付け、静岡
県沼津市静浦沖５００Ｍの海面下水深１．５−２，ＯＭ
の所に懸垂して１２ケ月間浸漬し、各月の海棲生物及び
海藻類の付着程度を調べた結果を第ｌ図に示す．又付看
生物の種類については第１表に示す． ｌ）防汚効果の判定は、網を覆った付着生物の付着面積
（対照区を１とする）によって判定する． Ｏ＝付着なし ○＝付着が対照区の１／３以内 ●；付着が対照区の２７３以内 ×＝付着が対照区の２／３以上 ２）試験網の湿重量の測定 懸垂ローブより枠を取り外し、枠と網を一緒に測定し、
この測定重量より原重量を差し引き、付着物の重量を算
出する． 第１表 ｉ２ケ月目における生物種と付着量 第１表の結果より明らかなように、比較例ではスライム
、ワレカラ、カサネカンザシ等の付着がみられたが、実
施例ではこれら生物の付着がなく、しかち第１図に示す
ごとく他の海棲生物や海藻類等の付着も少なく、本発明
による防汚用組成物は、長期にわたって海棲付着生物の
付着を防止しつる利点を有するものである．
第１図は、各漁網の海中における海棲物に対する防汚効
果を示すグラフである．
果を示すグラフである．
Claims (1)
- （１）微粒子状金属銅とクエン酸塩及びロジン系樹脂又
はクロマン系樹脂の混合物をセルローズ系高分子物質よ
りなる展着剤中に分散してなることを特徴とする防汚用
組成物。