JPH0417557Y2 - - Google Patents
Info
- Publication number
- JPH0417557Y2 JPH0417557Y2 JP1986041079U JP4107986U JPH0417557Y2 JP H0417557 Y2 JPH0417557 Y2 JP H0417557Y2 JP 1986041079 U JP1986041079 U JP 1986041079U JP 4107986 U JP4107986 U JP 4107986U JP H0417557 Y2 JPH0417557 Y2 JP H0417557Y2
- Authority
- JP
- Japan
- Prior art keywords
- film
- hot melt
- adhesive layer
- melt adhesive
- coating agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【考案の詳細な説明】
〔産業上の利用分野〕
この考案は、食品などの包装に用いる合成樹脂
や紙の容器を封緘する蓋材に関する。[Detailed description of the invention] [Industrial application field] This invention relates to a lidding material for sealing synthetic resin or paper containers used for packaging foods, etc.
一般に、紙を基材とする熱封緘蓋材としては、
紙に介在層を設けてポリエチレンフイルムを積層
し、そのフイルムの外面にホツトメルト接着剤を
塗布したものが用いられている。
In general, paper-based heat-sealing lid materials include:
The paper used is one in which an intervening layer is provided on paper, a polyethylene film is laminated thereon, and a hot melt adhesive is applied to the outer surface of the film.
このような蓋材は、開封時に、容器とホツトメ
ルト接着剤層の界面で剥離し易く、そのため、抵
抗感があつて滑らかな剥離感が得られない問題が
ある。 Such a lid material tends to peel off at the interface between the container and the hot melt adhesive layer when the lid is opened, and as a result, there is a problem in that it feels resistant and does not provide a smooth peeling feeling.
この対策として、容器と上記ホツトメルト接着
剤層との接着力を単に弱くするだけでは、蓋材の
密封性が低下するという新たな問題が生じる。 As a countermeasure to this problem, simply weakening the adhesive force between the container and the hot melt adhesive layer causes a new problem in that the sealing performance of the lid material deteriorates.
そこで、この考案の目的は、上記の問題を解決
し、良好な密封性を維持しながら、滑らかで安定
した剥離感が得られる蓋材を提供することにあ
る。 Therefore, the purpose of this invention is to solve the above problems and provide a lid material that provides a smooth and stable feeling of peeling while maintaining good sealing performance.
上記の目的を達成するため、この考案において
は、紙を含む基材にポリエステル又はポリプロピ
レンフイルムを積層し、そのフイルムの外面に、
前記ポリエステル又はポリプロピレンフイルムに
対応する特定のアンカーコート剤を介してホツト
メルト接着剤層を設け、この接着剤層のアンカー
コート剤に対する接着力を、容器に対する接着力
よりも弱くなるよう制御して、アンカーコート剤
とホツトメルト接着剤層の界面で剥離が生じるよ
うにしたのである。
In order to achieve the above object, in this invention, a polyester or polypropylene film is laminated on a base material including paper, and on the outer surface of the film,
A hot melt adhesive layer is provided via a specific anchor coating agent corresponding to the polyester or polypropylene film, and the adhesive force of this adhesive layer to the anchor coating agent is controlled to be weaker than the adhesive force to the container. The design was such that peeling occurred at the interface between the coating agent and the hot melt adhesive layer.
図示のように、蓋材１は、基材２に、接着剤３
を介して合成樹脂フイルム４を積層し、さらにそ
の外面に、アンカーコート剤５を介してホツトメ
ルト接着剤層６を設けたものである。
As shown in the figure, a lid material 1 is attached to a base material 2 with an adhesive 3.
A synthetic resin film 4 is laminated thereon, and a hot melt adhesive layer 6 is further provided on its outer surface with an anchor coating agent 5 interposed therebetween.
前記基材２は、紙単体のほか、金属箔や合成樹
脂フイルムとの積層体であつてもよく、さらに、
印刷層や表面保護層などを設けることができる。 The base material 2 may be a single paper or a laminate with metal foil or synthetic resin film, and further,
A printed layer, a surface protective layer, etc. can be provided.
前記合成樹脂フイルム４は、薄くて容易に破断
せず、伸びにくいものを用いる必要があり、例え
ば、ポリエチレンテレフタレートやポリブチレン
テレフタレートのようなポリエステルの延伸フイ
ルム（例えばユニチカ社のエンブレツト、エンブ
レツトDC、ICI社のメルネツクス）、が好適であ
る。また、その厚みは、５〜40μ程度が良く、5μ
未満は薄過ぎて実用的でなく、40μを越えると、
熱封緘の際の熱伝導が不十分になる恐れがある。 The synthetic resin film 4 needs to be thin, not easily broken, and difficult to stretch. For example, a stretched polyester film such as polyethylene terephthalate or polybutylene terephthalate (for example, Unitika's Emblem, Emblem DC, ICI) is used as the synthetic resin film 4. Melnetx, Inc.) is preferred. In addition, its thickness is preferably about 5 to 40μ, and 5μ
Anything less than 40μ is too thin to be practical;
Heat conduction during heat sealing may be insufficient.
次に、前記アンカーコート剤５は、フイルム４
の材質に応じて種々選択する必要があり、例えば
ポリエステルフイルムの場合は、飽和或は不飽和
線状ポリエステル樹脂又はポリウレタン樹脂、ポ
リプロピレンフイルムには、塩素化カルボキシル
化ポリプロピレン樹脂をそれぞれ主成分とするも
のがよく、厚みは0.1〜2μ程度、塗布するのが好
ましい。0.1μ未満であると、均一に塗布するのが
困難でかつ効果も少なく、2μ以上塗布しても無
駄であるからである。 Next, the anchor coating agent 5 is applied to the film 4.
It is necessary to select various materials depending on the material, for example, for polyester film, saturated or unsaturated linear polyester resin or polyurethane resin, and for polypropylene film, the main component is chlorinated carboxylated polypropylene resin. It is preferable to apply the coating to a thickness of about 0.1 to 2 μm. This is because if it is less than 0.1 μm, it is difficult to apply it uniformly and the effect is low, and even if it is applied more than 2 μm, it is useless.
このようにアンカーコート剤を選択することに
よつて、アンカーコート剤５とホツトメルト接着
剤層６との界面の接着性を制御し、ホツトメルト
接着剤層６と容器との間の接着力よりも適度に弱
くすることによつて、蓋材１の開封時、アンカー
コート剤５と接着剤層６との界面での剥離を可能
にし、滑らかで安定した剥離感が得られる。 By selecting the anchor coating agent in this manner, the adhesion at the interface between the anchor coating agent 5 and the hot melt adhesive layer 6 can be controlled to be more moderate than the adhesive force between the hot melt adhesive layer 6 and the container. By weakening the adhesive layer, when the lid material 1 is opened, the anchor coating agent 5 and the adhesive layer 6 can be peeled off at the interface, and a smooth and stable feeling of peeling can be obtained.
なお、ホツトメルト接着剤層６としては、通常
用いられるものでよいが、特にエチレン−酢酸ビ
ニル共重合体系樹脂にワツクスを混合したものが
好ましい。 The hot melt adhesive layer 6 may be of any commonly used adhesive, but is particularly preferably a mixture of ethylene-vinyl acetate copolymer resin and wax.
次に、さらに詳細な実施例を挙げる。 Next, more detailed examples will be given.
〔実施例 １〕
厚み12μの延伸ポリエステルフイルムの一面に
アンカーコート剤として、飽和線状ポリエステル
樹脂を1μの厚みで塗布し、さらにエチレン−酢
酸ビニル共重合体系のホツトメルト接着剤を25
ｇ／m2塗布し、前記ポリエステルフイルムの他面
に、接着剤を介して、79.1ｇ／m2の片アート紙を
積層した。なお、片アート紙の外面には、印刷及
びオーバーコートを施した厚み7μのアルミニウ
ム箔を接着剤で予め積層しておいた。このような
積層体で蓋を形成し、ポリプロピレンの成形容器
の開口部フランジに、ホツトメルト接着剤を内面
にしてヒートシールし、密封容器を形成した。[Example 1] A saturated linear polyester resin was applied to a thickness of 1 μm as an anchor coating agent on one side of a stretched polyester film with a thickness of 12 μm, and a hot melt adhesive based on ethylene-vinyl acetate copolymer was further coated with 25 μm of ethylene-vinyl acetate copolymer-based hot melt adhesive.
g/m 2 , and a piece of art paper weighing 79.1 g/m 2 was laminated on the other side of the polyester film via an adhesive. Note that on the outer surface of the piece of art paper, a printed and overcoated aluminum foil with a thickness of 7 μm was laminated in advance with an adhesive. A lid was formed from such a laminate, and the lid was heat-sealed to the opening flange of a polypropylene molded container with hot melt adhesive applied to the inner surface to form a sealed container.
この密封容器の蓋を手で剥離したところ、アン
カーコート剤とホツトメルト接着剤の界面で剥離
し、均一で滑らかな剥離感が得られた。また、ホ
ツトメルト接着剤の層は、容器開口部のフランジ
内周縁できれいに破断し、フイルム残りはなかつ
た。 When the lid of this sealed container was peeled off by hand, it peeled off at the interface between the anchor coating agent and the hot melt adhesive, and a uniform and smooth feeling of peeling was obtained. Further, the hot melt adhesive layer was cleanly broken at the inner peripheral edge of the flange at the opening of the container, and no film remained.
〔実施例 ２〕
厚み20μの２軸延伸ポリプロピレンフイルムの
一面にアンカーコート剤として、塩素化カルボキ
シル化ポリプロピレン樹脂を1μの厚みで塗布し、
さらにエチレン−酢酸ビニル共重合体系のホツト
メルト接着剤を25ｇ／m2塗布し、前記ポリプロピ
レンフイルムの他面に、接着剤を介して、79.1
ｇ／m2の片アート紙を積層した。なお、片アート
紙の外面には、印刷及びオーバーコートを施した
厚み7μのアルミニウム箔を接着剤で予め積層し
ておいた。このような積層体で蓋を形成し、ポリ
プロピレンの成形容器の開口部フランジに、ホツ
トメルト接着材を内面にしてヒートシールし、密
封容器を形成した。[Example 2] A chlorinated carboxylated polypropylene resin was applied as an anchor coating agent to a thickness of 1 μm on one side of a biaxially stretched polypropylene film with a thickness of 20 μm,
Furthermore, 25 g/m 2 of a hot melt adhesive based on ethylene-vinyl acetate copolymer was applied to the other surface of the polypropylene film via the adhesive.
g/m 2 pieces of art paper were laminated. Note that on the outer surface of the piece of art paper, a printed and overcoated aluminum foil with a thickness of 7 μm was laminated in advance with an adhesive. A lid was formed from such a laminate, and the lid was heat-sealed to the opening flange of a molded polypropylene container with a hot melt adhesive on the inner surface to form a sealed container.
この密封容器の蓋を手で剥離したところ、アン
カーコート剤とホツトメルト接着剤の界面で剥離
し、均一で滑らかな剥離感が得られた。また、ホ
ツトメルト接着剤の層は、容器開口部のフランジ
内周縁できれいに破断し、フイルム残りはなかつ
た。 When the lid of this sealed container was peeled off by hand, it peeled off at the interface between the anchor coating agent and the hot melt adhesive, and a uniform and smooth feeling of peeling was obtained. Further, the hot melt adhesive layer was cleanly broken at the inner peripheral edge of the flange at the opening of the container, and no film remained.
以上のような蓋材１によつて密封する容器は、
その開口部に蓋材１を熱封緘可能であればよく、
その他、材質、形状、用途などは、任意である。 The container sealed with the lid material 1 as described above is
It is sufficient if the lid material 1 can be heat-sealed to the opening,
In addition, the material, shape, purpose, etc. are arbitrary.
この考案によれば、以上のように、蓋材のポリ
エステル又はポリプロピレンフイルムとホツトメ
ルト接着剤層との間に特定のアンカーコート剤を
介在せしめて、ホツトメルト接着剤層の容器に対
する接着力よりも、適度に弱くなるよう制御し、
蓋材の開封時にアンカーコート剤とホツトメルト
接着剤層との間の界面剥離を可能とすることによ
つて、滑らかで安定した剥離感が得られる一方、
ホツトメルト接着剤層の容器に対する接着力は、
いくら強くしても蓋材の剥離には関係がなくなる
ので、密封性を充分向上させることができる効果
がある。
According to this invention, as described above, by interposing a specific anchor coating agent between the polyester or polypropylene film of the lid material and the hot melt adhesive layer, the adhesive force of the hot melt adhesive layer to the container is moderately improved. control so that it becomes weaker,
By enabling interfacial peeling between the anchor coating agent and the hot melt adhesive layer when the lid material is opened, a smooth and stable peeling feeling can be obtained, while
The adhesive strength of the hot melt adhesive layer to the container is
No matter how strong it is, it has no effect on the peeling of the lid material, so it has the effect of sufficiently improving the sealing performance.
図はこの考案の実施例を示す蓋材の断面図であ
る。
図中、１は蓋材、２は基材、３は接着剤、４は
合成樹脂フイルム、５はアンカーコート剤、６は
ホツトメルト接着剤層である。
The figure is a sectional view of a lid material showing an embodiment of this invention. In the figure, 1 is a lid material, 2 is a base material, 3 is an adhesive, 4 is a synthetic resin film, 5 is an anchor coating agent, and 6 is a hot melt adhesive layer.
Claims (1)
ポリプロピレンフイルムを積層し、そのフイルム
の外面に、アンカーコート剤として、前記ポリエ
ステルフイルムの場合は線状ポリエステル樹脂又
はポリウレタン樹脂、ポリプロピレンフイルムの
場合は塩素化カルボキシル化ポリプロピレン樹脂
を介して、ホツトメルト接着剤層を設け、この接
着剤層のアンカーコート剤に対する接着力を、容
器に対する接着力よりも弱くなるようにした容器
の蓋材。 A stretched polyester or biaxially stretched polypropylene film is laminated on a base material including paper, and an anchor coating agent is applied to the outer surface of the film, in the case of the polyester film, a linear polyester resin or polyurethane resin, and in the case of the polypropylene film, a chlorinated film is applied. A lid material for a container in which a hot melt adhesive layer is provided via a carboxylated polypropylene resin, and the adhesive force of this adhesive layer to an anchor coating agent is weaker than the adhesive force to the container.