JPH0425317Y2 - - Google Patents
Info
- Publication number
- JPH0425317Y2 JPH0425317Y2 JP12182186U JP12182186U JPH0425317Y2 JP H0425317 Y2 JPH0425317 Y2 JP H0425317Y2 JP 12182186 U JP12182186 U JP 12182186U JP 12182186 U JP12182186 U JP 12182186U JP H0425317 Y2 JPH0425317 Y2 JP H0425317Y2
- Authority
- JP
- Japan
- Prior art keywords
- innermost layer
- packaging material
- layer
- sealing
- packaging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
〔産業上の利用分野〕
本考案はフレーバー保持包装材に関し、詳しく
はフレーバーを含有する内容物を収納する包装袋
を製造するに用いる包装材に関する。
〔従来の技術及び考案の解決するための問題点〕
果汁、化粧品等のフレーバーを含有する物品を
収納するため、例えば軟包装袋が使用されてい
る。この種軟包装袋を製袋するに用いられる包装
材は、該包装材を製袋のため重ね合わせた際に内
側になる層、即ち、最内層が主にポリエチレン系
樹脂、ポリプロピレン系樹脂等の樹脂フイルムか
ら形成されている。
上記構成からなる包装材を用いて製袋した包装
袋にフレーバーを含有する物品を収納した場合、
最内層の上記樹脂のフイルムにフレーバーが吸着
してしまい、その結果、香りが悪くなつたり。ま
た少なくなつたりするという不具合が生じる。そ
のため、フレーバーの吸着を防止するため上記最
内層として溶解性パラメーターが9.5以上の樹脂
フイルム、例えばポリエチレンテレフタレート、
ポリカーボネート等を使用すれば良いことが知ら
れている。
しかしながら、最内層を上記溶解性パラメータ
ーを有する樹脂フイルムにて形成した包装材は、
包装材の製袋時のヒートシールに高熱が必要とな
り、また上記樹脂フイルムは強度の点で弱く伸び
も少ないため衝撃に対して耐えにくいという問題
点を有する。
本考案は上記の点に鑑みなされたもので、フレ
ーバーの吸着が少なく、製袋のためのシール性も
良好なフレーバー保持包装材を提供することを目
的とする。
〔問題点を解決するための手段〕
即ち、本考案のフレーバー保持包装材は基材上
に、ポリオフイン系樹脂からなるシール層及び溶
解性パラメーターが9.5以上の合成樹脂からなる
最内層を順次積層してなり、且つ上記最内層の製
袋時におけるシール部に相当する箇所がレーザー
光線により少なくとも一部消除されてなることを
特徴とするものである。
〔実施例〕
以下、本考案の実施例を図面に基づいて説明す
る。
第１図及び第２図は本考案の一実施例を示すも
ので、本考案フレーバー保持包装材１は基材２上
に、ポリオレフイン系樹脂からなるシール層３及
び溶解性パラメーターが9.5以上の合成樹脂から
なる最内層４を順次積層してなり、また上記最内
層４の製袋時におけるシール部に相当する箇所が
レーザー光線により少なくとも一部消除された構
成からなるものである。
上記基材２の材質としては合成樹脂、金属箔、
紙類等を用いることができ、特に限定されるもの
ではなく、また該基材２はこれらの樹脂を用いた
単層、多層、複層のいずれの構成からなるもので
あつてもよい。
シール層３はポリオレフイン系樹脂からなるも
のであり、該樹脂としては低密度ポリエチレン、
中密度ポリエチレン、高密度ポリエチレン、直鎖
−高密度ポリエチレン、ポリプロピレン等が挙げ
られ、またそれらのいずれのものを50重量％以上
含む共重合体或いは混合樹脂等でもよく、例えば
アイオノマー、エチレン酢酸ビニル共重合体、酸
変性樹脂等が挙げられる。上記層３の厚さは15〜
200μが好ましく、更に好ましくは40〜100μであ
る。
最内層４における”最内層”とは、本考案包装
材１を用いて製袋を行つた場合、包装袋における
内表面となる層のことをいい、本考案における最
内層４は溶解性パラメーターが9.5以上の合成樹
脂からなのものである。上記樹脂の具体例として
はポリエチレンテレフタレート（溶解性パラメー
ター：sp＝10.7）、ポリアミド（sp＝12.7〜13.5）、
エチレン−ビニルアルコール共重合体（sp＝
11.0）、ポリカーボネート（sp＝12.5）等が挙げ
られる。上記樹脂を用いることによりフレーバー
の吸着を防止することができる。上記層４の厚さ
５〜50μが好ましい。
本考案包装材１は、上記基材２上に、シール層
３及び最内層４をこの順に積層したものであり、
その積層方法としてはドライラミネート法、エキ
ストルージヨンラミネート法、共押出法等の従来
既知の方法を用いることができる。
本考案包装材１は、上記構成からなる積層体の
なかで、最内層４の製袋時におけるシール部に相
当する箇所を少なくとも一部除去したものであ
り、例えば、最内層４のシール部に相当する箇所
を貫通孔時を穿設する等により一部除去したり、
或いは上記シール部に相当する箇所全部を除去す
るというように最内層４のみ一部加工を施するも
のである。
本考案は従来、積層体の最上層（表面層）の所
定箇所のみを自在に取り除くという加工技術がな
かつてという点を、レーザー光線を用いることに
よりその加工を初めて可能ならしめたもので、本
考案に用いるレーザーとしては炭酸ガスレーザー
が最適である。炭酸ガスレーザーは波長が10.6μ
であり、プラスチツクへの吸収効率が良好なレー
ザーである。尚、レーザーに各種波長を有するも
のであるが、例えばYACレーザーを本考案にお
いて用した場合、貫通孔等を穿設しにくく、例え
穿設しても整然とした貫通孔が得られなかつた
り、またHeNeレーザーを同様に用いた場合、レ
ーザー出力が低いため貫通孔の穿設が難しいとい
う問題点がある。また、本考案において最内層の
所定箇所に貫通孔等を機械的に設けることは、理
論上、可能であるが、微細で所望箇所に整然と貫
通孔を設けることは、実用上、不可能である。
上記炭酸ガスレーザーを用いて、第１図に示す
ように最内層４の製袋時におけるシール部に相当
する箇所５のみに貫通孔６を穿設したり、第２図
に示すように連続して境界線７の如くに除去した
り（同図ａ）、または製袋時におけるシール部に
相当する箇所５の最内層全部を除去する（同図
ｂ）。本考案包装材１は、上記の如く最内層４の
製袋時におけるシール部に相当する箇所が少なく
とも一部除去されることにより、最内層４の下方
に位置するシール層３が最内層４の除去部分から
露出するため、該包装材１を用いて製袋を行うに
当たり、最内層４同志の接合によるヒートシール
ではなく、シール層３を利用した確実なコートシ
ールを行うことが可能になる。
上記構成からなる本考案フレーバー保持包装材
１を実際に用いて製袋するに当たつては、通常の
ヒートシール、インパルスシール、超音波シール
等により製袋することができ、また包装材１は３
辺シール袋、４辺シール袋、ピロー、ガセツト
袋、自立型袋、パウチ等の各種形状の包装袋を製
袋するために使用することができる。
次に、具体的実施例を挙げて本考案を更に詳細
に説明する。
実施例 １
紙（80g／m2）とアルミニウム（9μ厚）からな
る基材上に、酸変性ポリエチレン樹脂とポリエチ
レンテレフタレート（溶解性パラメーター：sp＝
10.7，20μ厚）からなる共押出フイルムをドライ
ラミネート法いて積層を行つて積層体を形成し、
次いで該積層体において、第１図に示されるよう
に最内層の製袋時におけるシール部に相当する箇
所に炭酸ガスレーザーを用いて直径１mmの貫通孔
を0.5mm間隔で穿設して最内層の一部を除去し、
本考案包装袋を得た。
上記包装材を用いて150mm×200mm（シール部の
幅10mm）の４辺シール包装袋を、100％オレンジ
果汁を充填しながらヒートシール（200℃の熱板
を用いて３Kg／m2の圧力で１秒間プレスを行う）
により製袋した。
上記包装袋を37℃で１ヶ月間放置させた後、フ
レーバーの成分であるリモネンの保持率の測定
（ガスクロマトグラフ法にて測定）及びシール強
度の測定（東洋ゴールドウイン社製：テンシロン
Ｔ型剥離、引張りスピード300m／min）を行い、
また落下試験（1mの高さからコンクリート面に
自然落下させた）を行つた。結果を第１表に示
す。表中において、○及び×の記号の意味は以下
の通りである。
○：落下による破損はなかつた。
×：落下により破損した。
実施例 ２
実施例１で得られた同様の包装材を用い、該包
装材において、最内層のシール部の境界に相当す
る箇所に第３図ａに示すように１mm幅の境界線と
なるよう炭酸ガスレーザーにて除去を行つた。以
下、実施例１と同様に包装袋を製袋し、同様の測
定、試験を行つた。結果を第１表に示す。
実施例 ３
実施例１と同様の積層体を用いて、該積層体に
おいて第３図ｂに示すように最内層におけるシー
ル部に相当する箇所を全面に亘つて除去して包装
材を得た。
上記包装材を用いて実施例１と同様に包装袋を
製袋し、同様の測定、試験を行つた。結果を第１
表に示す。
実施例 ４
延伸ナイロン（15μ厚）／アルミニウム箔（9μ
厚）の被層からなる基材を用い、該基材のアルミ
ニウム箔側上に酸変性ポリエチレン樹脂とエチレ
ンビニルアルコール共重合体（sp＝11.0，20μ厚）
よりなる共押出フイルムをドライラミネート法に
て積層を行つて積層体を形成し、該積層体の最内
層を実施例３と同様に除去して包装材を得た。
上記包装材を用いて実施例１と同様に包装袋を
製袋し、同様の測定、試験を行つた。結果を第１
表に示す。
比較例 １
ポリエチレンテレフタレートからなる基材
（15μ厚）上に、エチレン酢酸ビニル共重合体か
らなるシール層（60μ厚）を積層した包装材を用
いて、実施例１と同様に包装袋を製袋し、同様の
測定、試験を行つた。結果を第１表に示す。
比較例 ２
ポリエチレンテレフタレート（15μ厚）／ポリ
エチレン（50μ厚）の被層からなる基材を用い
て、該基材のポリエチレン層側上に酸変性ポリエ
チレン樹脂からなるシール層（20μ厚）及びポリ
エチレンテレフタレートからなる最内層（5μ厚）
をドライラミネート法にて積層して包装材を得
た。
上記包装材を用いて、実施例１と同様に包装袋
を製袋し、同様の測定、試験を行つた。結果を第
１表に示す。
[Industrial Application Field] The present invention relates to a flavor-retaining packaging material, and more particularly to a packaging material used for manufacturing a packaging bag for storing flavor-containing contents. [Problems to be solved by conventional techniques and ideas] For example, flexible packaging bags are used to store articles containing flavors such as fruit juices and cosmetics. The packaging material used to make this type of flexible packaging bag has a layer that becomes the inner layer when the packaging materials are stacked together for bag making, that is, the innermost layer is mainly made of polyethylene resin, polypropylene resin, etc. It is made of resin film. When an article containing flavor is stored in a packaging bag made using the packaging material having the above structure,
Flavors are adsorbed to the innermost layer of the resin film, resulting in a bad scent. There is also the problem that the amount decreases. Therefore, in order to prevent flavor adsorption, the innermost layer is a resin film with a solubility parameter of 9.5 or more, such as polyethylene terephthalate.
It is known that polycarbonate or the like can be used. However, packaging materials in which the innermost layer is made of a resin film having the above-mentioned solubility parameters,
There is a problem in that high heat is required for heat sealing during bag making of packaging materials, and the resin film is weak in strength and has little elongation, making it difficult to withstand impact. The present invention was devised in view of the above points, and it is an object of the present invention to provide a flavor-retaining packaging material that exhibits less adsorption of flavor and good sealing properties for bag making. [Means for solving the problem] That is, the flavor-retaining packaging material of the present invention has a sealing layer made of a polyoffine resin and an innermost layer made of a synthetic resin with a solubility parameter of 9.5 or more laminated in sequence on a base material. and is characterized in that a portion of the innermost layer corresponding to a seal portion during bag making is at least partially removed by a laser beam. [Example] Hereinafter, an example of the present invention will be described based on the drawings. Figures 1 and 2 show an embodiment of the present invention, in which the flavor retaining packaging material 1 of the present invention has a base material 2, a sealing layer 3 made of a polyolefin resin, and a synthetic resin having a solubility parameter of 9.5 or more. The innermost layer 4 made of resin is successively laminated, and the portion of the innermost layer 4 corresponding to the seal portion during bag making is at least partially removed by a laser beam. The material of the base material 2 is synthetic resin, metal foil,
Paper or the like can be used, and is not particularly limited, and the base material 2 may have a single layer, multilayer, or multilayer structure using these resins. The sealing layer 3 is made of polyolefin resin, and the resin includes low density polyethylene,
Examples include medium-density polyethylene, high-density polyethylene, linear high-density polyethylene, polypropylene, etc. Copolymers or mixed resins containing 50% by weight or more of any of these may also be used, such as ionomers, ethylene-vinyl acetate, etc. Examples include polymers and acid-modified resins. The thickness of the above layer 3 is 15~
The thickness is preferably 200μ, more preferably 40 to 100μ. The "innermost layer" in the innermost layer 4 refers to the layer that becomes the inner surface of the packaging bag when the packaging material 1 of the present invention is used to make bags, and the innermost layer 4 in the present invention has a solubility parameter. It is made of synthetic resin with a rating of 9.5 or higher. Specific examples of the above resins include polyethylene terephthalate (solubility parameter: sp = 10.7), polyamide (sp = 12.7 to 13.5),
Ethylene-vinyl alcohol copolymer (sp=
11.0), polycarbonate (sp=12.5), etc. By using the above resin, flavor adsorption can be prevented. The thickness of the layer 4 is preferably 5 to 50 microns. The packaging material 1 of the present invention has a sealing layer 3 and an innermost layer 4 laminated in this order on the base material 2,
As the lamination method, conventionally known methods such as dry lamination, extrusion lamination, coextrusion, etc. can be used. The packaging material 1 of the present invention is obtained by removing at least a portion of the innermost layer 4 from the laminate having the above-mentioned structure, which corresponds to the seal portion during bag manufacturing. Part of the corresponding part is removed by drilling a through hole, etc.
Alternatively, only a portion of the innermost layer 4 is processed, such as removing the entire portion corresponding to the seal portion. The present invention is the first to make it possible by using a laser beam to remove only a predetermined part of the top layer (surface layer) of a laminate. The most suitable laser for this purpose is a carbon dioxide laser. The wavelength of carbon dioxide laser is 10.6μ
This laser has good absorption efficiency into plastics. Although lasers have various wavelengths, for example, when a YAC laser is used in the present invention, it is difficult to drill through holes, and even if holes are drilled, it may not be possible to obtain well-ordered through holes. When a HeNe laser is similarly used, there is a problem in that it is difficult to drill through holes due to the low laser output. Furthermore, although it is theoretically possible to mechanically provide through holes etc. at predetermined locations in the innermost layer in the present invention, it is practically impossible to provide minute through holes in desired locations in an orderly manner. . Using the carbon dioxide laser, as shown in FIG. 1, the through holes 6 are drilled only in the portions 5 of the innermost layer 4 that correspond to the sealing part during bag manufacturing, or in a continuous manner as shown in FIG. or remove the entire innermost layer at the portion 5 corresponding to the seal portion during bag making (see figure b). In the packaging material 1 of the present invention, at least a portion of the innermost layer 4 corresponding to the seal portion during bag manufacturing is removed, so that the sealing layer 3 located below the innermost layer 4 is removed from the innermost layer 4. Since it is exposed from the removed portion, when making bags using the packaging material 1, it is possible to perform reliable coat sealing using the sealing layer 3 instead of heat sealing by bonding the innermost layers 4 together. When actually using the flavor-retaining packaging material 1 of the present invention having the above-mentioned configuration to make bags, the packaging material 1 can be made by ordinary heat sealing, impulse sealing, ultrasonic sealing, etc. 3
It can be used to make packaging bags of various shapes such as side-sealed bags, four-sided sealed bags, pillows, gusset bags, free-standing bags, and pouches. Next, the present invention will be explained in more detail with reference to specific examples. Example 1 Acid-modified polyethylene resin and polyethylene terephthalate (solubility parameter: sp=
10.7, 20μ thick) was laminated using the dry lamination method to form a laminate.
Next, in the laminate, as shown in Fig. 1, through-holes with a diameter of 1 mm are bored at 0.5 mm intervals using a carbon dioxide laser at locations corresponding to the sealing portions of the innermost layer during bag manufacturing. remove part of
A packaging bag according to the present invention was obtained. Using the above packaging material, heat-seal a 150mm x 200mm (width of the sealed part 10mm) four-sided sealed packaging bag while filling it with 100% orange juice (using a 200℃ hot plate at a pressure of 3Kg/m2 ). (press for 1 second)
Bags were made by After leaving the above packaging bag at 37°C for one month, the retention rate of limonene, which is a flavor component, was measured (measured by gas chromatography) and the seal strength was measured (manufactured by Toyo Goldwin Co., Ltd.: Tensilon T-type peeling. , tensile speed 300m/min),
We also conducted a drop test (dropping the product naturally onto a concrete surface from a height of 1m). The results are shown in Table 1. In the table, the meanings of the symbols ○ and × are as follows. ○: No damage caused by falling. ×: Damaged by falling. Example 2 A similar packaging material obtained in Example 1 was used, and in the packaging material, a border line with a width of 1 mm was formed at a location corresponding to the boundary of the innermost seal portion as shown in Figure 3a. Removal was performed using a carbon dioxide laser. Thereafter, packaging bags were made in the same manner as in Example 1, and the same measurements and tests were performed. The results are shown in Table 1. Example 3 Using the same laminate as in Example 1, a packaging material was obtained by removing the entire surface of the innermost layer of the laminate, which corresponds to the seal portion, as shown in FIG. 3b. A packaging bag was made using the above packaging material in the same manner as in Example 1, and the same measurements and tests were performed. Results first
Shown in the table. Example 4 Stretched nylon (15μ thick)/aluminum foil (9μ
Acid-modified polyethylene resin and ethylene vinyl alcohol copolymer (sp = 11.0, 20μ thickness) are used on the aluminum foil side of the base material.
A laminate was formed by laminating the coextruded films consisting of the following by a dry lamination method, and the innermost layer of the laminate was removed in the same manner as in Example 3 to obtain a packaging material. A packaging bag was made using the above packaging material in the same manner as in Example 1, and the same measurements and tests were performed. Results first
Shown in the table. Comparative Example 1 A packaging bag was produced in the same manner as in Example 1 using a packaging material in which a sealing layer (60 μm thick) made of ethylene vinyl acetate copolymer was laminated on a base material (15 μm thick) made of polyethylene terephthalate. Similar measurements and tests were conducted. The results are shown in Table 1. Comparative Example 2 Using a base material consisting of a coating layer of polyethylene terephthalate (15μ thickness)/polyethylene (50μ thickness), a sealing layer (20μ thickness) made of acid-modified polyethylene resin and polyethylene terephthalate was placed on the polyethylene layer side of the base material. Innermost layer (5μ thickness) consisting of
were laminated using a dry lamination method to obtain a packaging material. Using the above packaging material, a packaging bag was made in the same manner as in Example 1, and the same measurements and tests were performed. The results are shown in Table 1.
以上説明したように、本考案フレーバー保持包
装材は溶解性パラメーター9.5以上の合成樹脂か
らなる最内層を設けてなり、且つ最内層の製袋時
におけるシール部に相当する箇所を少なくとも一
部除去して、該最内層の下方に位置するシール層
を露出してなるため、本考案包装材を用いて包装
袋を製袋し、該包装袋にフレーバーを含有する物
品を収納した場合、フレーバーが最内層に吸着す
ることがなく、収納物の香りを充分に保持するこ
とができ、また製袋におけるシール性が良好で且
つシール強度に優れたものである。
As explained above, the flavor-retaining packaging material of the present invention has an innermost layer made of a synthetic resin with a solubility parameter of 9.5 or more, and at least a portion of the innermost layer that corresponds to the seal portion during bag manufacturing is removed. Since the sealing layer located below the innermost layer is exposed, when a packaging bag is made using the packaging material of the present invention and an article containing flavor is stored in the packaging bag, the flavor is It is not adsorbed to the inner layer, can sufficiently retain the fragrance of stored items, and has good sealing properties and excellent sealing strength during bag making.
第１図は本考案フレーバー保持包装材の一実施
例を示す平面図、第２図は第１図の−線に沿
う縦断面図、第３図は本考案の他の実施例を示す
平面図である。
１……フレーバー保持包装材、２……基材、３
……シール層、４……最内層。
Fig. 1 is a plan view showing one embodiment of the flavor-retaining packaging material of the present invention, Fig. 2 is a longitudinal sectional view taken along the - line in Fig. 1, and Fig. 3 is a plan view showing another embodiment of the present invention. It is. 1... Flavor retention packaging material, 2... Base material, 3
... Seal layer, 4 ... Innermost layer.
Claims (1)
ル層及び溶解性パラメーターが9.5以上の合成樹
脂からなる最内層を順次積層してなり、且つ上記
最内層の製袋時におけるシール部に相当する箇所
がレーザー光線により少なくとも一部削除されて
なることを特徴とするフレーバー保持包装材。 A sealing layer made of a polyolefin resin and an innermost layer made of a synthetic resin with a solubility parameter of 9.5 or more are laminated in sequence on a base material, and the part of the innermost layer corresponding to the sealing part during bag making is exposed to laser beams. A flavor-retaining packaging material characterized by being at least partially removed by.