JPH04323318A - Production of square tube reduced in yield ratio - Google Patents

Abstract

PURPOSE:To inexpensively produce a square tube reduced in yield ratio and having strength as high as >=50kgf/mm<2> without using expensive alloying elements in particular. CONSTITUTION:The corner part of a square tube made of low carbon steel or low carbon low alloy steel is heated to a temp. not lower than the Ac3 point, air-cooled and cooled from the temp. between (Ar3-20 deg.C) and (Ar3-250 deg.C) at >=15 deg.C/sec cooling rate, and subjected, if necessary, to tempering at 200-600 deg.C, by which the square tube reduced in yield ratio can be obtained.

Description

[Detailed description of the invention]

0001

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing square tubes with a low yield ratio.

0002

[Prior art] In recent years, across various fields that handle steel materials,
There are increasing demands for improvements in usage characteristics and reductions in manufacturing costs in order to improve competitiveness.

Among these, in the field of construction, it is desired to lower the yield ratio in order to improve the safety of structures, particularly in order to improve their seismic resistance. Until now, this requirement has been strong mainly in the thick plate field, but recently it has become stronger in the steel pipe field. Various methods are being considered for manufacturing thick steel plates with low yield ratios, but unfortunately, in the field of steel pipes,
At present, there are almost no examples of this being considered for architectural use. For example, electric resistance welded steel pipes are manufactured by forming hot coils, but since the yield ratio increases due to work hardening during forming, this manufacturing method is considered disadvantageous for manufacturing steel pipes with a low yield ratio. For example, Japanese Patent Application Laid-Open No. 57-16118 discloses a method for manufacturing ERW steel pipes for oil wells with a low yield ratio, but in order to obtain a low yield ratio, the amount of C is considerably increased (the amount of C:
0.26 to 0.48%), it cannot be applied to architectural structures specified by Ceq from the viewpoint of weldability. Similarly, there is Japanese Patent Application Laid-Open No. 57-16119 as a manufacturing method for low yield ratio, high tensile resistance welded steel pipes, but this method involves manufacturing extremely low YR steel at the hot coil stage, and In order to suppress work hardening, the amount of strain is considerably limited, but this is quite difficult in actual operation.

Furthermore, when considering square steel pipes, there are those that are formed from a round tube into a square tube by so-called roll forming, and those that are formed from a plate into a square tube without going through a round tube. For all of these square tubes, material deterioration occurs, and material deterioration is particularly severe at the corner portions of the square tubes, with some reports reporting that YR is close to 100% and elongation is almost 1%. In such a cold-formed square tube, the yield ratio of the entire tube becomes 80% or more due to material deterioration at the corner portions, so it is impossible to manufacture a low yield ratio square tube with a yield ratio of 80% or less.

[0005]

Problem to be Solved by the Invention: As a low yield ratio angle pipe for construction, a yield ratio of 80% with a tensile strength of 40 to 60 kg level.
Although there are the following requirements, it is impossible to manufacture them using the current manufacturing method. In other words, in the roll-forming method in which a hot coil is formed into a round shape and then formed into a square tube, and in the so-called as-roll type, which is a non-temperature type in which a plate is formed into a square tube without going through the round tube, material deterioration at the corners causes Furthermore, in the tempered type so-called QT type, the structure becomes tempered martensite, so a yield ratio of 80% or less is not achieved.

[0006]

[Means for Solving the Problems] The present inventors conducted numerous experiments and detailed studies in order to reduce the yield ratio. The necessity of creating a two-phase structure consisting of ferrite and a second phase of carbide was confirmed. Furthermore, it was confirmed that in order to lower the yield ratio, it is important to lower the yield point and increase the tensile strength.

Furthermore, in the case of cold-formed square tubes, it has been confirmed that the yield ratio of the entire square tube can be lowered to 80% or less by improving only the material of the corner portions.

Based on this knowledge, the present invention has made it possible to manufacture square tubes with a low yield ratio. The corner part of
This is a method for manufacturing a rectangular tube with a low yield ratio, which is characterized by tempering in a temperature range of 00°C.

[0009]

[Function] In the present invention, the heating temperature of the corner portion of the square tube is set to the Ac3 transformation point or higher to form a complete austenite phase, thereby completely eliminating the influence of work hardening of the corner portion during pipe forming and subsequent square tube forming. By combining this process with subsequent air cooling to below the Ar3 transformation point to precipitate ferrite, and subsequent water cooling, they have succeeded in creating a dual-phase steel.

Furthermore, by lowering the tempering temperature, the second phase portion is not softened more than necessary, which has a synergistic effect, making it possible to manufacture a rectangular tube with a low yield ratio.

Next, the steel pipe manufacturing, square pipe forming, heating,
Cooling and tempering conditions will be described.

First, there are no particular regulations regarding the manufacture of the steel pipe and the subsequent forming of the square tube, and any form of forming is acceptable. For example, steel pipes can be classified into seamless steel pipes, electric resistance welded steel pipes, UO steel pipes, spiral steel pipes, forge-welded pipes, etc. according to their manufacturing methods, and the present invention allows any of these manufacturing methods. Of course, it is also acceptable to directly form a square tube from a plate such as a hot coil and weld it. This is to set the heating temperature in the subsequent heat treatment of the corner portion to a temperature at which processing strain is removed. Next, the heating temperature after molding is set to A
The reason for setting it to c3 or more is to completely eliminate molding strain as a complete austenite single-phase structure.

The purpose of performing air cooling after heating is to precipitate an appropriate amount of ferrite before cooling, with the aim of creating a complete duplex steel.

The reason why the upper limit of the cooling start temperature is set to Ar3-20°C is to lower the yield point, and the lower limit is set to Ar3-20°C.
The reason for setting the temperature to 50°C is that when cooling from a low temperature below this temperature, the effect of accelerated cooling becomes weak and the tensile strength decreases, making it difficult to secure strength, and as a result, it becomes impossible to secure a low yield ratio.

[0015] Cooling after air cooling to Ar3-20 to Ar3-250 is performed to austenitize during reheating and harden the C-enriched part to a quenched structure, thereby increasing tensile strength and achieving a low yield ratio. It's to get it. If cooling is insufficient,
Since the quenched structure was not sufficiently hardened and a low yield ratio could not be obtained as a result, the cooling rate was specified to be 15° C./sec or more. As for the cooling method, water cooling is usually used, but any method may be used as long as the cooling rate is secured.

As for the heating method, for example, by heating a square steel pipe with an induction heating device having a round cross section, only the corners of the square pipe near the induction coil are heated, the flat part is not heated, and then the pipe is cooled. , the above heat treatment can be applied only to the corner portions.

Regarding the cooling method, a water-cooled ring nozzle is most desirable.

By the way, depending on the type of steel, there are some steels that do not have good toughness when water-cooled only after heating, and a tempering treatment after water-cooling may be necessary to improve the toughness. At this time, the tempering temperature should be determined for the two-phase structure of ferrite and second phase carbide. If the second phase part, which has been sufficiently hardened by previous water cooling, is tempered at too high a temperature, it will become too soft, resulting in a decrease in tensile strength. Since this causes an increase in yield ratio, the upper limit was set at 600°C. However, if the tempering temperature is too low to be less than 200°C, the tempering effect will be almost gone and the toughness may not be improved, so the lower limit was set at 200°C.

The method of the present invention can be applied to low carbon steel or low carbon low alloy steel to which special elements are added with good results. A preferable component composition is C: 0.05~
0.30% Si: 0.02-0.50% Mn: 0.50-2.00% Al: 0.001-0.100% N: 0.0005-0.0100% Depending on the required characteristics of carbon steel or strength steel in addition to the above basic components, Cu: 2.0% or less Ni: 9.5% or less Cr: 5.5% or less Mo: 2.0% or less Nb: 0.15 % or less V: 0.3% or less Ti: 0.15% or less B: 0.0003 to 0.0030% Ca: 0.0080% or less One or more of the following may be added.

C has the effect of increasing the strength of steel, and 0.
However, if it exceeds 0.30%, the toughness will be significantly deteriorated, so the content should be reduced to 0.05%.
~0.30%.

[0021]Si has a solid solution strengthening effect and has the effect of improving the strength and ductility of steel materials, and is added in an amount of 0.02% or more, but if added in excess of 0.50%, it deteriorates the toughness of steel materials. Therefore, its content was set to 0.02 to 0.50%.

Like C, Mn also has the effect of increasing the strength of steel materials, and is added in an amount of 0.50% or more.
．． If it exceeds 0%, not only will steel making work be difficult;
Since it is not economical, the content should be reduced from 0.50 to 2.0.
%.

[0023] Al is necessary for deoxidation in the steel manufacturing stage, and its lower limit was set at 0.001%. Furthermore, if it is added in excess of 0.100%, the amount of inclusions will increase and the cleanliness of the steel will be lost, and this will interfere with steelmaking operations, so the range has been reduced to 0.001 to 0.100%. And so.

[0024]N is generally contained in steel as an unavoidable impurity, but if a too low N content is aimed at, the cost of steel manufacturing will increase significantly, so the lower limit was set at 0.0005%. In addition, when the amount of N increases, the weldability of steel materials deteriorates,
Furthermore, in order to promote the occurrence of surface scratches on the continuously cast slab, the upper limit was set at 0.0100%.

[0025] Cu is added because it is useful for increasing strength and improving corrosion resistance, but even if it is added in an amount exceeding 2.0%, there is almost no increase in strength, so the upper limit of the content is set at 2.0%.

Ni is useful for improving low-temperature toughness and is added, but since it is an expensive element, the upper limit of its content is 9.5%.

[0027] Cr is added because it is useful for increasing strength and improving corrosion resistance, but since too much Cr impedes low temperature toughness and weldability, the upper limit of the content is 5.5%.

[0028] Mo is useful for increasing strength, but if too much it impedes weldability, so the upper limit of the content is 2.0%.

[0029] Nb is added because it is useful for refining austenite grains and increasing strength, but if the amount is too large, it impedes weldability, so the upper limit of the content is set to 0.15%.

[0030] V is useful for precipitation strengthening, but if too much V impedes weldability, so the upper limit of the content is 0.3%.

[0031] Ti is useful for refining austenite grains and is added, but if it increases, it impedes weldability, so the upper limit of the content is 0.3%.

B has the effect of significantly increasing the hardenability of steel when added in a small amount. In order to effectively obtain this effect, it is necessary to add at least 0.0003%. However, if added in excess, B compounds are generated and the toughness is deteriorated, so the upper limit is set to 0.0030%.

[0033] Ca is added because it is useful for controlling the morphology of sulfide-based inclusions, but if too much Ca forms inclusions in the steel and deteriorates the properties of the steel, the upper limit of the content is set at 0.006%.

[0034]

[Example] Table 1 shows the chemical composition of the test materials, and Table 2 shows the size of the square tube, heat treatment conditions, and mechanical properties of the obtained square tube.

Steel pipes NoA1, B1, C1, shown in Table 2
D1, E1, F1, G1, H1, I1, J1, K1, L
1, M1, N1, O1, P1, Q1, R1, S1, T1
, U1, and V1 are steels according to the present invention, which have achieved the low yield ratio (yield ratio of 80% or less) targeted by the present invention.

On the other hand, A2 has a high yield ratio because the heating temperature is too high. A3 has a high yield ratio because the heating temperature is too low. A4 has a high yield ratio because the cooling rate after heating is insufficient. A5 has a high yield ratio because the tempering temperature is too high.

Further, B2 has a high yield ratio because the tempering temperature is too high. C2 has a high yield ratio due to insufficient cooling rate. D2 has a high yield ratio because the heating temperature is too low.

[0038]

[Table 1]

[0039]

[Table 2]

[0040]

[Table 3]

[0041]

Effects of the Invention As explained in detail above, the present invention can achieve 50kgf/m without using any particularly expensive alloying elements.
This makes it possible to manufacture low yield ratio angle tubes with high strength of m2 or more at low cost, and this has great industrial effects.

Claims (2)

[Claims] Claim 1: A corner part of a low carbon steel square tube or a low carbon low alloy steel square tube is heated to Ac3 or higher, and then air cooled to heat the corner at 15℃/se from Ar3-20℃ to Ar3-250℃.
A method for manufacturing a rectangular tube with a low yield ratio, characterized by cooling at a cooling rate of c or more. [Claim 2] The corner part of a low carbon steel square tube or a low carbon low alloy steel square tube is heated to Ac3 or higher, and then air cooled at 15℃/se from Ar3-20℃ to Ar3-250℃.
A method for manufacturing a rectangular tube with a low yield ratio, characterized by cooling at a cooling rate of c or higher and then tempering at a temperature range of 200 to 600°C.