JPH0446615A - Device and method for repairing surface of dull roll for rolling - Google Patents
Device and method for repairing surface of dull roll for rollingInfo
- Publication number
- JPH0446615A JPH0446615A JP2155081A JP15508190A JPH0446615A JP H0446615 A JPH0446615 A JP H0446615A JP 2155081 A JP2155081 A JP 2155081A JP 15508190 A JP15508190 A JP 15508190A JP H0446615 A JPH0446615 A JP H0446615A
- Authority
- JP
- Japan
- Prior art keywords
- doctor blade
- roll
- rolling
- dull
- dull roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〈産業上の利用分野〉
本発明は、銅帯等を圧延する、表面粗さが中心線表面相
さＲａ−１〜３Ｐの圧延用ダルロールの表面に付着した
異物を除去するドクターブレード式ロール表面の手入れ
装置及びその使用方法に関するものである。Detailed Description of the Invention <Industrial Application Field> The present invention is a method for removing foreign matter attached to the surface of a dull roll for rolling a copper strip or the like and having a centerline surface roughness of Ra-1 to 3P. The present invention relates to a doctor blade type roll surface care device for removing and a method for using the same.
〈従来の技術〉
調帯やステンレス鋼帯を圧延する際に、ワークロールの
表面に異物が付着していると、銅帯の表面が凹み状に形
成されて、いわゆる押込圧が発生する。そこで、−ａに
ワークロールには、表面の異物を除去するロール手入れ
装置が使用される。<Prior Art> When rolling a toning strip or stainless steel strip, if foreign matter adheres to the surface of the work roll, the surface of the copper strip is formed in a concave shape, and so-called indentation pressure is generated. Therefore, in -a, a roll care device is used for the work roll to remove foreign matter from the surface.
ロール手入れ装置としては、実公昭５６−２６８８１号
公報や実公昭６３μｍ５０００５号公報、あるいは実開
平２２８３０４号公報のように、第４図に示すような金
属製のドクターブレード５を直接ワークロール２に押し
当てる方法が知られている。As a roll care device, a metal doctor blade 5 as shown in FIG. There are known ways to apply it.
〈発明が解決しようとする課題〉
しかし、上記の従来の方法では、表面粗さが中心線表面
粗さＲａ＝ １．０〜３．Ｏｎのダルロールの場合、ド
クターブレードのダルロールへの押付力が大であると、
短期間にダルロールの表面粗度が低下するという問題が
ある。<Problems to be Solved by the Invention> However, in the above conventional method, the surface roughness is within the range of centerline surface roughness Ra=1.0 to 3. In the case of a dull roll that is ON, if the pressing force of the doctor blade to the dull roll is large,
There is a problem that the surface roughness of the dull roll decreases in a short period of time.
なお、この対策として、押付力を軽減すると、粗度低下
は緩和されるが、いずれにしてもロール寿命の低下は避
けられない。Note that as a countermeasure to this problem, if the pressing force is reduced, the decrease in roughness is alleviated, but in any case, a decrease in the life of the roll is unavoidable.
本発明は、このような問題を解決するだけでなく、積極
的にロール粗度を上昇させてロール寿命延長をはかる圧
延用ダルロール表面の手入れ装置及びその使用方法を提
供することを目的とする。An object of the present invention is not only to solve such problems but also to provide a rolling dull roll surface care device and a method for using the same, which proactively increases the roll roughness and extends the life of the roll.
〈課題を解決するための手段〉
本発明の圧延用ダルロール表面の手入れ装置は、表面粗
さが中心線平均粗さＲａ＝１〜３μｍの圧延用ダルロー
ルの表面に付着した異物を除去するドクターブレード式
ロール表面の手入れ装置において、前記ドクターブレー
ドとして先端がノコギリ刃状の金属製ドクターブレード
を用いることを特徴とするものであり、前記ドクターブ
レードをロール胴長方向に往復摺動させる摺動機構を設
けるのが好ましい、また、前記ドクターブレードの厚み
を０．１〜０．４ ｍの範囲とするのが好ましい。<Means for Solving the Problems> The rolling dull roll surface care device of the present invention includes a doctor blade for removing foreign matter attached to the surface of a rolling dull roll having a center line average roughness Ra of 1 to 3 μm. The roll surface care device is characterized in that a metal doctor blade with a sawtooth tip is used as the doctor blade, and a sliding mechanism is provided for reciprocating the doctor blade in the longitudinal direction of the roll body. Preferably, the doctor blade has a thickness of 0.1 to 0.4 m.
そして、本発明の圧延用ダルロール表面の手入れ装置の
使用方法は、前記装置を使用するに際し、ドクターブレ
ードの押付力を線圧０．５ｋｇ／ｍ以上、１０ｋｇ／ｍ
未満とすることを特徴とするものである。The method for using the rolling dull roll surface care device of the present invention is that when using the device, the pressing force of the doctor blade is set at a linear pressure of 0.5 kg/m or more to 10 kg/m.
It is characterized by being less than or equal to
く作 用〉
本発明によれば、第５図に示したように（詳細は後記の
第５図の説明を参照）、ダルロールの表面粗度低下によ
るロール寿命短縮の問題が生じない。Effects> According to the present invention, as shown in FIG. 5 (for details, refer to the description of FIG. 5 below), the problem of shortening the life of the roll due to a decrease in the surface roughness of the dull roll does not occur.
この理由は、本発明では先端がノコギリ刃状の金属製ド
クターブレードを用いて、積極的にダルロールの表面粗
度を上昇させるからである。This is because the present invention uses a metal doctor blade with a sawtooth tip to actively increase the surface roughness of the dull roll.
〈実施例〉 本発明の実施例を図面に基づいて説明する。<Example> Embodiments of the present invention will be described based on the drawings.
第１図は、本発明の装置の一実施例を示し、装置の片側
の説明図である。第２図は第１図のｌＩ線断面図である
。FIG. 1 shows an embodiment of the apparatus of the present invention, and is an explanatory view of one side of the apparatus. FIG. 2 is a sectional view taken along the line II in FIG. 1.
第１．２図において、ドクターブレード５は、ブレード
ホルダー３に、ブレード押え６で固定され、軸４と軸受
８により回転自在に支持されている。ドクターブレード
５のダルロール２例の先端は、第３図のように、ノコギ
リ刃状に加工されている。ドクターブレード５のダルロ
ール２への押付力Ｆは、自重Ｗで与えられるが、カウン
ターウェイト７により、押付力Ｆの調整を可能としであ
る。In FIG. 1.2, a doctor blade 5 is fixed to a blade holder 3 with a blade presser 6, and is rotatably supported by a shaft 4 and a bearing 8. The tips of the two dull rolls of the doctor blade 5 are machined into a sawtooth shape, as shown in FIG. The pressing force F of the doctor blade 5 against the dull roll 2 is given by its own weight W, but the pressing force F can be adjusted by the counterweight 7.
また、軸受８の下部には、スライドライナー９とアクチ
ュエータ１０があり、電磁切換弁１３、スピードコント
ローラ１２の操作により、ドクターブレード５はダルロ
ール２の胴長方向に往復摺動可能としである。A slide liner 9 and an actuator 10 are provided at the bottom of the bearing 8, and the doctor blade 5 can be slid back and forth in the lengthwise direction of the dull roll 2 by operating an electromagnetic switching valve 13 and a speed controller 12.
１１は、スライドライナー９及びアクチエエータｌＯを
支持するブラケットである。また、１は綱帯である。11 is a bracket that supports the slide liner 9 and the actuator IO. Also, 1 is a rope belt.
なお、本実施例にドクターブレード５の往復摺動機構を
設けたのは、ドクターブレード５の摺動がないと、ロー
ルスジ状疵を発生させることがあるためであり、設置し
ておくことが望ましい。The reason why a reciprocating sliding mechanism for the doctor blade 5 is provided in this embodiment is because roll line-like flaws may occur if the doctor blade 5 does not slide, so it is desirable to provide the mechanism. .
次に、具体的実施例について説明する。Next, specific examples will be described.
６１ＯＩＷｌφの３％Ｃｒ鋼製で、粗度Ｒａ＝ ２．５
，１１１１１のダルロール２に対して、ドクタープレー
Ｆ５の厚み及び押付力Ｆを変えて、実験を行った。Made of 61OIWlφ 3% Cr steel, roughness Ra = 2.5
, 11111, an experiment was conducted by changing the thickness of the doctor plate F5 and the pressing force F.
なお、ドクターブレード５の先端加工は、第４図に示す
ように、あらかじめ操業には使用しないオフラインのダ
ルロール１４をロール回転台１５にのせ、ドクターブレ
ード５に線圧１０ｋｇ／ｍの圧下刃を加えてダルロール
１４を回転すると、先端部が第３図に示す寸法１．ｍが
それぞれ０．１〜１．０−程度のノコギリ刃状を形成で
きるので、それを使用した。勿論、別の手段でノコギリ
刃を加工してもよい。As shown in FIG. 4, the tip of the doctor blade 5 is machined by placing the off-line dull roll 14, which is not used in the operation, on the roll rotating table 15 in advance, and applying a reduction blade with a linear pressure of 10 kg/m to the doctor blade 5. When the dull roll 14 is rotated, the tip end has the size 1. shown in FIG. This was used because it can form a sawtooth shape with m of approximately 0.1 to 1.0. Of course, the saw blade may be processed by other means.
実験結果を第５図に示す。The experimental results are shown in Figure 5.
押付力Ｆが線圧２ ｋｇ ／ ｍでは従来とほぼ変化な
いが、押付力Ｆを線圧５ｋｇ／ｍとすると、綱帯１によ
るダルロール２の粗度低下とドクターブレード５による
粗度上昇が釣り合い、はぼ同粗度で推移する。なお、そ
の後減少に転じるのは、ドクターブレード５の摩耗でド
クターブレード５がフラットになり、粗度を上昇させる
効果が無くなるためである。When the pressing force F is a linear pressure of 2 kg/m, there is almost no change from the conventional method, but when the pressing force F is set to a linear pressure of 5 kg/m, the roughness reduction of the dull roll 2 due to the rope belt 1 and the roughness increase due to the doctor blade 5 are balanced. , the roughness changes at the same level. Note that the reason why it starts to decrease after that is because the doctor blade 5 becomes flat due to wear and the effect of increasing the roughness is lost.
押付力Ｆを線圧１０ｋｇ／ｍにすると、−時粗度は上昇
した後、短期間でドクターブレード５がフラットに摩耗
するので、逆にロール寿命が短くなる。When the pressing force F is set to a linear pressure of 10 kg/m, the doctor blade 5 wears flat in a short period of time after the negative roughness increases, and the life of the roll is conversely shortened.
したがって、押付力Ｆは線圧１０ｋｇ／ｍ未満の必要が
あり、この時、ドクターブレード５の厚みを、通常のロ
ールクラウン凸０．１−になじむドクターブレードの厚
みである０、４閤以下とする必要がある。Therefore, the pressing force F needs to be less than 10 kg/m in line pressure, and at this time, the thickness of the doctor blade 5 should be 0.4 mm or less, which is the thickness of the doctor blade that fits the normal roll crown convexity of 0.1 mm. There is a need to.
また、１ ｋｇ ／ ｍ以下の軽圧下でも使用可能であ
るが、０．５ｋｇ／ｍ以下では振動等でブレードホルダ
ー３が反転することがある。また、ドクターブレード５
の厚みをあまり薄くすると、０．５ｋｇ／ｍの軽圧下で
もすぐ摩耗してフラーットになるので、０．１ｍ以上の
厚みが望ましい。Further, it can be used under light pressure of 1 kg/m or less, but if the pressure is 0.5 kg/m or less, the blade holder 3 may be reversed due to vibration or the like. Also, Doctor Blade 5
If the thickness is made too thin, it will quickly wear out and become flat even under a light pressure of 0.5 kg/m, so a thickness of 0.1 m or more is desirable.
なお、ドクターブレード５の先端の隙間から異物が逃げ
出し、押し込み疵が多発することが心配されたが、最大
１．０閣程度の隙間では、圧延油の粘性で異物はドクタ
ーブレード５上にかきあげられており、特に問題はなか
った。There was a concern that foreign matter would escape from the gap at the tip of the doctor blade 5, resulting in frequent push-in flaws, but in a gap of about 1.0 mm at most, the viscosity of the rolling oil would scrape up the foreign matter onto the doctor blade 5. There were no particular problems.
〈発明の効果〉
以上説明したように、本発明により、押し込み疵を防止
しながらダルロールの寿命を延長することができ、生産
性を向上することができる。また、製品の品質を向上す
ることが可能となる。<Effects of the Invention> As explained above, according to the present invention, the life of the dull roll can be extended while preventing indentation flaws, and productivity can be improved. Moreover, it becomes possible to improve the quality of the product.
第１図は本発明の装置の一実施例を示し、装置の片側の
説明図である。第２図は第１図のＩ−１線断面図である
。第３図は本発明のドクターブレードの平面図である。
第４図は本発明のドクターブレードの先端を加工する装
置の一例を示す側面図である。第５図は押付力を変えた
ときの通板距離と粗度との関係を示したグラフである。
１・・・銅帯、
２・・・ダルロール、
３・・・ブレードホルダー
４・・・軸、
５・・・ドクターブレード、
６・・・ブレード押え、
７・・・カウンターウェイト、
８・・・軸受、
９・・・スライドライナー
ＩＯ・・・アクチュエータ、
１１・・・ブラケット、
１２・・・スピードコントローラ、
１３・・・電磁切換弁、
１４・・・ダルロール、
１５・・・ロール回転台。
第１図
ｒ＋１
第２図
第
図
第
図
通板距離（ｋｌ）FIG. 1 shows an embodiment of the apparatus of the present invention, and is an explanatory view of one side of the apparatus. FIG. 2 is a sectional view taken along line I-1 in FIG. 1. FIG. 3 is a plan view of the doctor blade of the present invention. FIG. 4 is a side view showing an example of an apparatus for processing the tip of a doctor blade according to the present invention. FIG. 5 is a graph showing the relationship between the threading distance and the roughness when the pressing force is changed. 1... Copper band, 2... Dull roll, 3... Blade holder 4... Shaft, 5... Doctor blade, 6... Blade holder, 7... Counter weight, 8... Bearing, 9... Slide liner IO... Actuator, 11... Bracket, 12... Speed controller, 13... Solenoid switching valve, 14... Dull roll, 15... Roll rotation table. Fig. 1 r+1 Fig. 2 Fig. Fig. Threading distance (kl)
Claims (4)
延用ダルロールの表面に付着した異物を除去するドクタ
ーブレード式ロール表面の手入れ装置において、前記ド
クターブレードとして先端がノコギリ刃状の金属製ドク
ターブレードを用いることを特徴とする圧延用ダルロー
ル表面の手入れ装置。(1) In a doctor blade type roll surface care device for removing foreign matter attached to the surface of a dull roll for rolling having a center line average roughness Ra of 1 to 3 μm, the doctor blade has a sawtooth tip. A rolling dull roll surface care device characterized by using a metal doctor blade.
せる摺動機構を設けたことを特徴とする請求項１の圧延
用ダルロール表面の手入れ装置。(2) The rolling dull roll surface care device according to claim 1, further comprising a sliding mechanism for reciprocating the doctor blade in the longitudinal direction of the roll body.
ある請求項１又は２の圧延用ダルロール表面の手入れ装
置。(3) The rolling dull roll surface care device according to claim 1 or 2, wherein the doctor blade has a thickness of 0.1 to 0.4 mm.
ードの押付力を線圧０．５ｋｇ／ｍ以上、１０ｋｇ／ｍ
未満とすることを特徴とする圧延用ダルロール表面の手
入れ装置の使用方法。(4) When using the device according to claim 3, the pressing force of the doctor blade should be set to a linear pressure of 0.5 kg/m or more and 10 kg/m.
A method of using a rolling dull roll surface care device characterized in that: