JPH0471043B2 - - Google Patents
Info
- Publication number
- JPH0471043B2 JPH0471043B2 JP56211693A JP21169381A JPH0471043B2 JP H0471043 B2 JPH0471043 B2 JP H0471043B2 JP 56211693 A JP56211693 A JP 56211693A JP 21169381 A JP21169381 A JP 21169381A JP H0471043 B2 JPH0471043 B2 JP H0471043B2
- Authority
- JP
- Japan
- Prior art keywords
- wood
- parts
- ebip
- tbp
- nch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本発明は、３−エトキシカルボニルオキシ−１
−ブロモ−１，２−ジヨード−１−プロペン（以
下EBIPと略す）に、トリブロモフエノール（以
下TBPと略す）、Ｎ−ニトロソ−Ｎ−シクロヘキ
シルヒドロキシルアミンのアルミニウム塩（以下
NCHと略す）及びビストリブチル錫オキシド
（以下TBTOと略す）より選ばれた１種または２
種を配合してなる木材用防腐組成物に関する。 種々の木材腐朽菌による腐朽を防ぐため従来よ
り種々の無機あるいは有機化合物が木材防腐剤と
して広く用いられている。しかし、従来の薬剤は
毒性が高く、人体への悪影響や環境汚染などの欠
点が指摘され、より低毒性で有効な防腐剤の出現
が強く要望されている。 本発明者等は、よりすぐれた木材防腐剤につい
て鋭意検討を重ねて来た結果、EBIPにTBP、
NCHまたはTBTOを配合することにより、相剰
的にすぐれた防腐効果を示すことを見出し、本発
明を完成した。 これら組成物を使用する際の混合比は広い範囲
に亘つて変化させることができ、特にEBIP：
TBP、NCHまたはTBTO＝４：１から１：４の
場合に優れた効果が達成される。 本発明の組成物は、担体および必要に応じて他
の補助剤と混合して、木材防腐剤として通常用い
られる製剤形態、例えば油溶性剤、乳剤、ペース
ト剤の他に、粉剤、エアゾール剤、塗料等に調製
されて、公知の木材防腐処理法により使用され
る。 適当な担体としてはクレー、タルク、ベントナ
イト、カオリン、無水硅酸、炭酸カルシウム、木
粉等の不活性固体；ケロシン、リグロイン、キシ
レン、メチルナフタリン、ジメチルホルムアミド
等の液体担体；窒素ガス、ジメチルエーテル、フ
ロンガス、塩化ビニル単量体等の気体担体があげ
られる。製剤の性状を改善し、防腐効果を高める
ため適宜使用される補助剤としては例えば、陰イ
オン性、陽イオン性、非イオン性の界面活性剤や
メチルセルロース、酢酸ビニル樹脂、アルギン酸
ソーダ等の種々の高分子化合物等があげられる。
もちろん、他の木材防腐剤やパーメスリン等のピ
レスロイド系、ホキシム等の有機燐系、クロルデ
ン等の有機塩素系等の木材防虫剤と併用出来、そ
れにより一層の防腐、防虫の効果向上をはかるこ
とも可能である。 実際の使用に際して本発明組成物の含量は製剤
の形態に従い広い範囲にわたつて変化させ得る
が、一般には0.1〜95重量％、好ましくは0.2〜60
重量％の範囲が適当である。 次に本発明の防腐組成物の効力を試験例によつ
て説明する。 試験例 寒天希釈法により所定濃度に薬剤に調製した各
滅菌培地（マルトエキス２％、グルコース１％、
ペプトン0.5％、寒天２％）上に、木材腐朽菌カ
ワラタケおよびオオウズラタケの菌系を接触し、
25℃で７日間培養したのちの菌系の生育状況より
発育阻止最低濃度（MIC）を求めた。 この結果を表１に示す。
−ブロモ−１，２−ジヨード−１−プロペン（以
下EBIPと略す）に、トリブロモフエノール（以
下TBPと略す）、Ｎ−ニトロソ−Ｎ−シクロヘキ
シルヒドロキシルアミンのアルミニウム塩（以下
NCHと略す）及びビストリブチル錫オキシド
（以下TBTOと略す）より選ばれた１種または２
種を配合してなる木材用防腐組成物に関する。 種々の木材腐朽菌による腐朽を防ぐため従来よ
り種々の無機あるいは有機化合物が木材防腐剤と
して広く用いられている。しかし、従来の薬剤は
毒性が高く、人体への悪影響や環境汚染などの欠
点が指摘され、より低毒性で有効な防腐剤の出現
が強く要望されている。 本発明者等は、よりすぐれた木材防腐剤につい
て鋭意検討を重ねて来た結果、EBIPにTBP、
NCHまたはTBTOを配合することにより、相剰
的にすぐれた防腐効果を示すことを見出し、本発
明を完成した。 これら組成物を使用する際の混合比は広い範囲
に亘つて変化させることができ、特にEBIP：
TBP、NCHまたはTBTO＝４：１から１：４の
場合に優れた効果が達成される。 本発明の組成物は、担体および必要に応じて他
の補助剤と混合して、木材防腐剤として通常用い
られる製剤形態、例えば油溶性剤、乳剤、ペース
ト剤の他に、粉剤、エアゾール剤、塗料等に調製
されて、公知の木材防腐処理法により使用され
る。 適当な担体としてはクレー、タルク、ベントナ
イト、カオリン、無水硅酸、炭酸カルシウム、木
粉等の不活性固体；ケロシン、リグロイン、キシ
レン、メチルナフタリン、ジメチルホルムアミド
等の液体担体；窒素ガス、ジメチルエーテル、フ
ロンガス、塩化ビニル単量体等の気体担体があげ
られる。製剤の性状を改善し、防腐効果を高める
ため適宜使用される補助剤としては例えば、陰イ
オン性、陽イオン性、非イオン性の界面活性剤や
メチルセルロース、酢酸ビニル樹脂、アルギン酸
ソーダ等の種々の高分子化合物等があげられる。
もちろん、他の木材防腐剤やパーメスリン等のピ
レスロイド系、ホキシム等の有機燐系、クロルデ
ン等の有機塩素系等の木材防虫剤と併用出来、そ
れにより一層の防腐、防虫の効果向上をはかるこ
とも可能である。 実際の使用に際して本発明組成物の含量は製剤
の形態に従い広い範囲にわたつて変化させ得る
が、一般には0.1〜95重量％、好ましくは0.2〜60
重量％の範囲が適当である。 次に本発明の防腐組成物の効力を試験例によつ
て説明する。 試験例 寒天希釈法により所定濃度に薬剤に調製した各
滅菌培地（マルトエキス２％、グルコース１％、
ペプトン0.5％、寒天２％）上に、木材腐朽菌カ
ワラタケおよびオオウズラタケの菌系を接触し、
25℃で７日間培養したのちの菌系の生育状況より
発育阻止最低濃度（MIC）を求めた。 この結果を表１に示す。
【表】
【表】
次に本発明組成物の若干の製剤例をあげるが、
配合量、補助剤の種類等は大幅に変更し得るもの
であることは云うまでもない。 製剤例 １ 乳 剤 EBIP10部およびTBP40部をジメチルホルムア
ミド10部およびキシレン30部に溶解させ、ポリオ
キシエチレンノニルフエニルエーテル10部を加え
て十分に混合し、乳剤を得た。 この乳剤は用時適量の水で希釈して処理すべき
木質材料に塗布、浸漬もしくはスプレー等の方法
で使用される他に、合板、パーテイクルボード、
ハードボード等の接着剤混入処理に適用出来る。 製剤例 ２ 油 剤 EBIP2部およびTBTO1部をキシレン97部に溶
解し油剤を得た。 製剤例 ３ 粉 剤 EBIP30部、NCH30部、メツシユ100以上の木
粉40部を混合機中で均一に混合し、ハンマーミル
で粉砕して粉剤を得た。
配合量、補助剤の種類等は大幅に変更し得るもの
であることは云うまでもない。 製剤例 １ 乳 剤 EBIP10部およびTBP40部をジメチルホルムア
ミド10部およびキシレン30部に溶解させ、ポリオ
キシエチレンノニルフエニルエーテル10部を加え
て十分に混合し、乳剤を得た。 この乳剤は用時適量の水で希釈して処理すべき
木質材料に塗布、浸漬もしくはスプレー等の方法
で使用される他に、合板、パーテイクルボード、
ハードボード等の接着剤混入処理に適用出来る。 製剤例 ２ 油 剤 EBIP2部およびTBTO1部をキシレン97部に溶
解し油剤を得た。 製剤例 ３ 粉 剤 EBIP30部、NCH30部、メツシユ100以上の木
粉40部を混合機中で均一に混合し、ハンマーミル
で粉砕して粉剤を得た。
Claims (1)
- １ ３−エトキシカルボニルオキシ−１−ブロモ
−１，２−ジヨード−１−プロペンに、トリブロ
モフエノール、Ｎ−ニトロソ−Ｎ−シクロヘキシ
ルヒドロキシルアミンのアルミニウム塩及びビス
トリブチル錫オキシドより選ばれた１種または２
種以上を配合してなる木材用防腐組成物。