JPH0476061A - イミドシリコン系重合体組成物 - Google Patents
イミドシリコン系重合体組成物Info
- Publication number
- JPH0476061A JPH0476061A JP19018090A JP19018090A JPH0476061A JP H0476061 A JPH0476061 A JP H0476061A JP 19018090 A JP19018090 A JP 19018090A JP 19018090 A JP19018090 A JP 19018090A JP H0476061 A JPH0476061 A JP H0476061A
- Authority
- JP
- Japan
- Prior art keywords
- oxide
- polymer
- imidesilicone
- flame
- metal oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、電気、電子機器配線に用いられるイミドシリ
コン系重合体組成物に関する。
コン系重合体組成物に関する。
最近開発されたイミドノリコン系重合体は、たとえばイ
ミドとシリコン系モノマーを共重合することによって得
られ、一般に耐熱性、電気特性等に優れており、電気や
電子機器用配電線の絶縁層構成材料として有望視されて
いる。しかし難燃性が充分でなく、また−・度燃焼する
と黒煙を多量に放出する問題もある。
ミドとシリコン系モノマーを共重合することによって得
られ、一般に耐熱性、電気特性等に優れており、電気や
電子機器用配電線の絶縁層構成材料として有望視されて
いる。しかし難燃性が充分でなく、また−・度燃焼する
と黒煙を多量に放出する問題もある。
而して本発明は、イミドシリコン系重合体をヘースとし
、その優れた耐熱性、電気特性等を生かしつつ高難燃性
にして且つたとえ燃焼しても黒煙発生量の少ない組成物
を開発することにある。
、その優れた耐熱性、電気特性等を生かしつつ高難燃性
にして且つたとえ燃焼しても黒煙発生量の少ない組成物
を開発することにある。
本発明の上記課題は、イミドシリコン系重合体１００重
量部に対し、金属酸化物またはヂノ化ホウ素を１種以上
１〜５０重量部配合してなることを特徴とする難燃樹脂
組成物によって解決される。
量部に対し、金属酸化物またはヂノ化ホウ素を１種以上
１〜５０重量部配合してなることを特徴とする難燃樹脂
組成物によって解決される。
本発明者らのイミドシリコン系重合体の難燃化に関する
検討から、金属酸化物やヂッ化ホウ素などを添加すると
、イミドシリコン系重合体をその固有の特性をさほど損
なうことなく燃焼中のススの発生量が減少し、同時に自
己消火時間が短く難燃度が高まる。
検討から、金属酸化物やヂッ化ホウ素などを添加すると
、イミドシリコン系重合体をその固有の特性をさほど損
なうことなく燃焼中のススの発生量が減少し、同時に自
己消火時間が短く難燃度が高まる。
本発明において用いられるイミドソリコン系重合体は、
メチル基等のアルキル基、フェニル’ＪＬ等のアリール
基を有するシリコンモノマーとイミドとのブロンク共重
合体やランダム共重合、イミドにシロキシンを共重合し
た共重合体等が例示される。これらの１種または２種以
上が用いられる。
メチル基等のアルキル基、フェニル’ＪＬ等のアリール
基を有するシリコンモノマーとイミドとのブロンク共重
合体やランダム共重合、イミドにシロキシンを共重合し
た共重合体等が例示される。これらの１種または２種以
上が用いられる。
イミドシリコン系重合体の市販品としては、ＧＥ社のＳ
ＩＬＴＥＭ ＳＴＭ−１５００、ＳＩＬＴＥＭ−０９０
０１，５ＩＬＴＥ閃０９０００等のＳＩｌ、ＴＥＨの９
０００シリーズが例示される。
ＩＬＴＥＭ ＳＴＭ−１５００、ＳＩＬＴＥＭ−０９０
０１，５ＩＬＴＥ閃０９０００等のＳＩｌ、ＴＥＨの９
０００シリーズが例示される。
イミドシリコン系重合体にエーテルイミド重合体たとえ
ばＧＥネ１の商品名１１ＬＴＥＭ 、をイミドシリコン
系重合体１００重量部あたり１０〜５０重量部混合滑部
ものをイミドシリコン系重合体として用いてもよい。
ばＧＥネ１の商品名１１ＬＴＥＭ 、をイミドシリコン
系重合体１００重量部あたり１０〜５０重量部混合滑部
ものをイミドシリコン系重合体として用いてもよい。
本発明に用いる金属酸化物としては、二酸化アンチモン
、二酸化アンチモン等の酸化アンチモン、酸化チタン、
酸化セリウム、酸化モリブデン、酸化タングステン、酸
化ホウ素、酸化ジルコニウム、酸化ビスマス、酸化鉄、
酸化ネオジウム、酸化サマリウム、酸化ジスプロシウム
、酸化マグネシウム、酸化亜鉛、酸化イツトリウム、酸
化アルミニウム、酸化テルル、酸化リチウム、酸化ルビ
ジウム、酸化セシウム、酸化へリリウム、酸化ストロン
チウム、酸化バリウム、酸化スカンジウム、酸化ランタ
ン、酸化プラセオジム、酸化ユウロピウム、酸化ガドリ
ニウム、酸化テルビウム、酸化ホルミウム、酸化エルビ
ウム、酸化ツリウム、酸化イッテルビウム、酸化ルテチ
ウム、酸化ハフニウム、酸化バナジウム、酸化ニオブ、
酸化タンタル、酸化クロム、酸化マンガン、酸化レニウ
ム、酸化ルテニウム、酸化オスミウム、酸化コハルＩ−
１酸化ロジウノ１、酸化イリジウム、酸化ニンケル、酸
化パラジウム、酸化白金、酸化ガリウム、酸化インジウ
ム、酸化タウリウム、酸化ゲルマニウム、酸化セ１／ン
などが挙げられる。難燃効果は夫々若干の差があるが、
特に性能面からは三酸化アンチモン、五酸化アンチモン
、二酸化チタン、酸化セリウム、三酸化タングステン、
二酸化モリブデン、酸化ホウ素、酸化ジルコニウム、酸
化ビスマス、酸化ネオジウム、酸化サマリウムなどが効
果的である。粒子径は１〜］、Ｏｌｔ ｍ程度が機械特
性、成形性の優れた組成物を調製する」−で好ましい。
、二酸化アンチモン等の酸化アンチモン、酸化チタン、
酸化セリウム、酸化モリブデン、酸化タングステン、酸
化ホウ素、酸化ジルコニウム、酸化ビスマス、酸化鉄、
酸化ネオジウム、酸化サマリウム、酸化ジスプロシウム
、酸化マグネシウム、酸化亜鉛、酸化イツトリウム、酸
化アルミニウム、酸化テルル、酸化リチウム、酸化ルビ
ジウム、酸化セシウム、酸化へリリウム、酸化ストロン
チウム、酸化バリウム、酸化スカンジウム、酸化ランタ
ン、酸化プラセオジム、酸化ユウロピウム、酸化ガドリ
ニウム、酸化テルビウム、酸化ホルミウム、酸化エルビ
ウム、酸化ツリウム、酸化イッテルビウム、酸化ルテチ
ウム、酸化ハフニウム、酸化バナジウム、酸化ニオブ、
酸化タンタル、酸化クロム、酸化マンガン、酸化レニウ
ム、酸化ルテニウム、酸化オスミウム、酸化コハルＩ−
１酸化ロジウノ１、酸化イリジウム、酸化ニンケル、酸
化パラジウム、酸化白金、酸化ガリウム、酸化インジウ
ム、酸化タウリウム、酸化ゲルマニウム、酸化セ１／ン
などが挙げられる。難燃効果は夫々若干の差があるが、
特に性能面からは三酸化アンチモン、五酸化アンチモン
、二酸化チタン、酸化セリウム、三酸化タングステン、
二酸化モリブデン、酸化ホウ素、酸化ジルコニウム、酸
化ビスマス、酸化ネオジウム、酸化サマリウムなどが効
果的である。粒子径は１〜］、Ｏｌｔ ｍ程度が機械特
性、成形性の優れた組成物を調製する」−で好ましい。
金属酸化物または千ノ化ホウ素の使用は、（両者を併用
する場合はそれらの合計量で）イミドう／リヨン系重合
体１００重量部に対し１〜５０重量部、好ましくは５〜
１５重量部である。１重量部未満では使用効果が少なく
、５０重量部より多量ではイミドシリコン系重合体の引
張特性が低下する。
する場合はそれらの合計量で）イミドう／リヨン系重合
体１００重量部に対し１〜５０重量部、好ましくは５〜
１５重量部である。１重量部未満では使用効果が少なく
、５０重量部より多量ではイミドシリコン系重合体の引
張特性が低下する。
実施例
以下実施例及び比較例により本発明を一層詳細に説明す
る。
る。
実施例１〜１０、比較例１〜２
第１表に示す組成物をブラベンダープラストミル（東洋
精機社）を用いて２７０〜２８０°Ｃで混練し、ついで
プＩ／ス成形して０．６ ｍｍ厚のシートを作成した。
精機社）を用いて２７０〜２８０°Ｃで混練し、ついで
プＩ／ス成形して０．６ ｍｍ厚のシートを作成した。
ついで電子線をシート両面から１５Ｍｒａｄずつ照射し
て架橋した。
て架橋した。
実施例１〜１０、比較例１〜２で得た各架橋シートにつ
き、第１表に示す各種特性を試験した。弓張特性はＡＳ
ＴＭ Ｄ ６３８、脆化温度はＡＳＴＭ Ｄ７４６ 、
体積抵抗率はＡＳＴＭ Ｄ２５７ 、難燃性はＵＬ ５
ｕｂｊｅｃｔ ７５８に準じてそれぞれ評価した。
き、第１表に示す各種特性を試験した。弓張特性はＡＳ
ＴＭ Ｄ ６３８、脆化温度はＡＳＴＭ Ｄ７４６ 、
体積抵抗率はＡＳＴＭ Ｄ２５７ 、難燃性はＵＬ ５
ｕｂｊｅｃｔ ７５８に準じてそれぞれ評価した。
燃焼用ンー１−は幅６ｍｍのもので、着火から１５秒内
には消えるものとし、その時のスス発生量は目視によっ
た。スス発生量が少ないか、自己消火時間が短いものは
良とした。
には消えるものとし、その時のスス発生量は目視によっ
た。スス発生量が少ないか、自己消火時間が短いものは
良とした。
実施例はこの難燃性がずべて良好であることを示す。ま
た引張強さは少なくとも１．０ ｋｇ ／ （１１ｍ２
伸びは少なくとも５０χあれば電線被覆材料として適用
可能と考えられ、これらの基準には合格している。
た引張強さは少なくとも１．０ ｋｇ ／ （１１ｍ２
伸びは少なくとも５０χあれば電線被覆材料として適用
可能と考えられ、これらの基準には合格している。
［以Ｆ、余白］
Claims (1)
- （１）イミドシリコン系重合体１００重量部に対し金属
酸化物またはチッ化ホウ素を１種以上１〜５０重量部配
合してなることを特徴とする難燃樹脂組成物。