JPH06130659A - Photosensitive microcapsules - Google Patents
Photosensitive microcapsulesInfo
- Publication number
- JPH06130659A JPH06130659A JP28154792A JP28154792A JPH06130659A JP H06130659 A JPH06130659 A JP H06130659A JP 28154792 A JP28154792 A JP 28154792A JP 28154792 A JP28154792 A JP 28154792A JP H06130659 A JPH06130659 A JP H06130659A
- Authority
- JP
- Japan
- Prior art keywords
- color
- photosensitive
- microcapsules
- cyan
- image
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【目的】 シート上に塗布されているか、トナーの状態
であるかに関わらず、且つ変換露光、直接露光等の何れ
の露光方法を用いても、不要な感度をなくし、原稿画像
の色彩を忠実に再現した画像を得ることができる感光性
マイクロカプセルを提供すること。
【構成】 本発明の感光性マイクロカプセルは、受像紙
上にカラー画像を形成する際に用いるものであり、シア
ンを発色する色材の濃度を通常濃度よりも高くすること
により、シアンを発色する不要な波長における余分な感
度を補正することができる。
(57) [Abstract] [Purpose] Irrespective of whether it is coated on the sheet or in the state of toner, no matter which exposure method such as conversion exposure or direct exposure is used, unnecessary sensitivity is eliminated. To provide a photosensitive microcapsule capable of obtaining an image that faithfully reproduces the color of an original image. [Structure] The photosensitive microcapsules of the present invention are used when forming a color image on an image receiving paper, and it is not necessary to develop cyan by increasing the density of a coloring material that develops cyan to be higher than the normal density. Extra sensitivity at different wavelengths can be corrected.
Description
【０００１】[0001]
【産業上の利用分野】本発明は、カラー複写機、カラー
プリンタなどに用いられ、特定の波長の光に露光される
ことで物性が変化する感光性マイクロカプセルに関する
ものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a photosensitive microcapsule which is used in a color copying machine, a color printer or the like and which changes its physical properties when exposed to light of a specific wavelength.
【０００２】[0002]
【従来の技術】従来、感光性マイクロカプセルを用いた
画像形成方法については、特開昭５７−１２４３４３号
公報に感光性組成物を含有するものが開示されている。
また、特開昭５７−１７９８３６号公報には感光性組成
物と染料前駆体を含有した感光性マイクロカプセルとそ
の画像形成方法が開示されている。2. Description of the Related Art Conventionally, as an image forming method using a photosensitive microcapsule, Japanese Patent Application Laid-Open No. 57-124343 discloses that containing a photosensitive composition.
Further, JP-A-57-179836 discloses a photosensitive microcapsule containing a photosensitive composition and a dye precursor, and an image forming method thereof.
【０００３】一方、感光性組成物と染料前駆体を含有し
た感光性マイクロカプセルに波長選択性を持たせてカラ
ー画像を得る方法が特開昭５９−３０５３７号公報に開
示されている。これは例えば、画像をレッド、グリー
ン、ブルーに分解し、それぞれの色をＵＶ−１、ＵＶ−
２、ＵＶ−３に変換して、それぞれの光で、ＵＶ−１に
感光する組成物とシアンの染料前駆体、ＵＶ−２に感光
する組成物とマゼンタの染料前駆体、ＵＶ−３に感光す
る組成物とイエローの染料前駆体を含有する３種類の感
光性マイクロカプセルを混合して均一に塗布したシート
を露光するものである。すなわち、画像のレッド部分が
ＵＶ−１に変換されて露光されると、シート上のシアン
の染料前駆体を含有する感光性マイクロカプセルが硬化
し、同様に、画像のグリーン部分に対応してマゼンタの
染料前駆体含有マイクロカプセルが、ブルー部分に対応
してイエローの染料前駆体含有マイクロカプセルが硬化
する。On the other hand, JP-A-59-30537 discloses a method for obtaining a color image by imparting wavelength selectivity to photosensitive microcapsules containing a photosensitive composition and a dye precursor. For example, the image is decomposed into red, green, and blue, and each color is UV-1, UV-.
2, converted into UV-3 and exposed to respective light, UV-1 sensitive composition and cyan dye precursor, UV-2 sensitive composition and magenta dye precursor, UV-3 The composition and three types of photosensitive microcapsules containing a yellow dye precursor are mixed and uniformly coated on a sheet to be exposed. That is, when the red portion of the image is converted into UV-1 and exposed, the photosensitive microcapsules containing the cyan dye precursor on the sheet are cured, and similarly, the magenta corresponding to the green portion of the image is obtained. The dye precursor-containing microcapsules of No. 2 are cured corresponding to the blue portion, and the yellow dye precursor-containing microcapsules are cured.
【０００４】そして、画像の潜像が得られたシートのカ
プセル面と顕色剤が塗布されたシートの顕色剤層面を圧
接し、未硬化マイクロカプセルを破壊し、カプセル内包
物を顕色剤と接触させ、顕色剤が塗布されたシート上に
画像が形成される。Then, the capsule surface of the sheet on which the latent image of the image is obtained and the surface of the developer layer of the sheet coated with the developer are pressed to destroy the uncured microcapsules, and the encapsulated material is developed by the developer. And an image is formed on the sheet coated with the color developer.
【０００５】また、特開昭６２−１４３０４４号公報に
は、可視光で感度の良好な感光性マイクロカプセルを用
いたカラー画像形成についての記載がみられる。これに
よれば、上記のように原稿画像を色分解せずに直接露光
することが可能である。Further, JP-A-62-143044 discloses a color image formation using a photosensitive microcapsule having good sensitivity to visible light. According to this, it is possible to directly expose the original image without color separation as described above.
【０００６】[0006]
【発明が解決しようとする課題】しかしながら、上述し
たような従来の感光性マイクロカプセルの分光感度特性
はきわめて不完全であり、マゼンタに発色する感光性マ
イクロカプセルは画像のブルー部分に対応した光にも若
干の感度を有し、シアンに発色する感光性マイクロカプ
セルは画像のレッド部分に対応した光以外の光にも若干
の感度を有している。そして、特に、後者に起因するシ
アン発色不良はおおきな問題となっている。However, the spectral sensitivity characteristics of the conventional photosensitive microcapsules as described above are extremely imperfect, and the photosensitive microcapsules that develop magenta emit light corresponding to the blue portion of the image. Also has some sensitivity, and the photosensitive microcapsule that develops cyan has some sensitivity to light other than light corresponding to the red portion of the image. In particular, the cyan color defect due to the latter is a big problem.
【０００７】そこで、感光性マイクロカプセル内部に色
相を持たないような紫外線吸収剤を含有させることによ
り、不用な感度を打ち消すようにする方法が特開昭６１
−２４４９５号公報に開示されている。また、同様の効
果を得るために、カプセル層以外に紫外線吸収層を設け
る方法が特開平３−８７８２７号公報に開示されてい
る。Therefore, there is a method of canceling unnecessary sensitivity by incorporating an ultraviolet absorber having no hue inside the photosensitive microcapsules.
No. 24495. Further, in order to obtain the same effect, a method of providing an ultraviolet absorbing layer in addition to the capsule layer is disclosed in JP-A-3-87827.
【０００８】一方、特開平３−２９４８５９号公報に
は、紫外線吸収特性の異なる壁剤を用いた感光性マイク
ロカプセルについて記述されており、これは、例えば、
尿素−ホルマリン−ジヒドロキシナフタリンの３元系を
壁剤に用いるものである。On the other hand, Japanese Patent Laid-Open No. 3-294859 describes a photosensitive microcapsule using a wall material having different ultraviolet absorption characteristics.
A ternary system of urea-formalin-dihydroxynaphthalene is used as a wall agent.
【０００９】しかしながら、これらのものは感光性マイ
クロカプセルがシート上に担持されていなければならな
かったり、原稿画像を色分解して３つの異なる紫外光域
に変換して露光させなければならなかった。However, in these products, the photosensitive microcapsules had to be carried on the sheet, or the original image had to be color-separated and converted into three different ultraviolet light regions for exposure. .
【００１０】そこで、直接露光に対応できる感光性マイ
クロカプセルの不要感光防止方法として、特開平２−２
９４６５２号公報には複数の色の波長に対して感度を有
する感光性マイクロカプセルを用いて色補正を行う方法
が提案されている。Therefore, as a method for preventing unnecessary exposure of a photosensitive microcapsule which can be directly exposed, Japanese Patent Laid-Open No. 2-2 is known.
Japanese Patent No. 94652 proposes a method of performing color correction using photosensitive microcapsules having sensitivity to wavelengths of a plurality of colors.
【００１１】これはカプセルの外表面に光半導体物質及
び金属塩と感光性色素との金属錯体を含む染料脱色層を
設けることにより、光半導体表面に金属錯体化して共吸
着された感光色素が選択的色光を吸収して光半導体を励
起し、この励起半導体から電荷の注入が起こり光脱色が
開始されるものである。This is because a photosensitive decolorizing layer containing a photo-semiconductor substance and a metal complex of a metal salt and a photosensitive dye is provided on the outer surface of the capsule so that the photosensitive dye co-adsorbed by forming a metal complex on the photo-semiconductor surface is selected. The photo-semiconductor is excited by absorbing specific colored light, and charges are injected from the excited semiconductor to start photobleaching.
【００１２】また、特開平３−１３４６６７号公報に
は、例えば、マゼンタの発色がイエローがかっていたり
した場合には、イエローに発色するマイクロカプセルに
レッド光でも感光するようにして、イエローとマゼンタ
の混色時にはイエローの発色を抑えることによりイエロ
ーがかったレッドの色補正を行い、シアンの発色がマゼ
ンタがかっている場合には、シアンに発色するマイクロ
カプセルにグリーン光でも感光するようにして、シアン
とマゼンタの混色時にはマゼンタがかった色を抑え補正
する方法が開示されている。Further, in Japanese Laid-Open Patent Publication No. 3-134667, for example, when the color of magenta is yellow, the microcapsules that develop yellow are exposed to red light so that the color of yellow and magenta is increased. When mixing colors, the yellowish red color is corrected by suppressing the yellow coloration.If the cyan coloration is magenta, the microcapsules that develop cyan are exposed to green light so that cyan and magenta are exposed. There is disclosed a method of suppressing and correcting a magenta color when the colors are mixed.
【００１３】しかしながら、これらの方法が用いられる
のは、マゼンタがイエローがかっていたり、シアンがマ
ゼンタがかっていたりする場合であり、感光性マイクロ
カプセルが染顔料を含んでいて、色補正の必要がない場
合にはむしろ用いない方がよいぐらいである。However, these methods are used when magenta is yellowish or cyan is magenta, and since the photosensitive microcapsules contain dyes and pigments, color correction is not necessary. In some cases, it is better not to use it.
【００１４】このように、感光性マイクロカプセルの不
要な感度部分の減感方法には完全な方法がなく、特にシ
アンの発色不良は大きな問題であり、よって原稿画像の
色再現性も完全なものとは言えない状態であった。As described above, there is no perfect method for desensitizing the unnecessary sensitive portions of the photosensitive microcapsules. In particular, cyan color development is a serious problem, and therefore the color reproducibility of the original image is also perfect. It could not be said that.
【００１５】本発明は、上述した問題点を解決するため
になされたものであり、シート上に塗布されているか、
トナーの状態であるかに関わらず、且つ変換露光、直接
露光等の何れの露光方法を用いても、不要な感度をなく
し、原稿画像の色彩を忠実に再現した画像を得ることが
できる感光性マイクロカプセルを提供することを目的と
している。The present invention has been made to solve the above-mentioned problems, and whether it is applied on a sheet,
Irrespective of the toner state, even if any exposure method such as conversion exposure or direct exposure is used, unnecessary sensitivity is eliminated and an image faithfully reproducing the color of the original image can be obtained. The purpose is to provide microcapsules.
【００１６】[0016]
【課題を解決するための手段】この目的を達成するため
に本発明の感光性マイクロカプセルは、受像紙上にカラ
ー画像を形成する際に用いられ、シアン、マゼンタ、イ
エロ−にそれぞれ発色する色材を備えた複数種の感光性
マイクロカプセルであり、更には前記シアンに発色する
色材の濃度を通常濃度の１．１倍以上にしたことを特徴
としている。In order to achieve this object, the photosensitive microcapsules of the present invention are used in forming a color image on an image-receiving paper, and are coloring materials capable of coloring cyan, magenta and yellow, respectively. Is a plurality of types of photosensitive microcapsules, and is characterized in that the density of the coloring material that develops cyan is 1.1 times or more the normal density.
【００１７】[0017]
【作用】上記の構成を有する本発明の感光性マイクロカ
プセルは、シアンに発色する色材の濃度が通常濃度の
１．１倍以上になっている。ここで、通常濃度とは、感
光性マイクロカプセルに不要な感度がないと仮定したと
きに、最も忠実な色再現を可能とする色材濃度のことで
ある。感光性マイクロカプセル中には、基本的に重合す
ることによって硬化するモノマ−と、重合を開始させる
ための重合開始剤と、感光する光の波長領域を制御する
増感色素と、実際に色を出すための色材とが含まれてお
り、必要に応じて吸収した光に対する反応感度を高める
感度増感剤が加えられる。In the photosensitive microcapsule of the present invention having the above structure, the density of the coloring material that develops cyan is 1.1 times or more the normal density. Here, the normal density is a color material density that enables the most faithful color reproduction, assuming that the photosensitive microcapsules do not have unnecessary sensitivity. In the photosensitive microcapsules, a monomer that is basically cured by polymerization, a polymerization initiator for initiating the polymerization, a sensitizing dye that controls the wavelength region of light to be exposed, and an actual color are formed. A coloring material for emitting the light is included, and if necessary, a sensitivity sensitizer for increasing the reaction sensitivity to the absorbed light is added.
【００１８】そして、感光性マイクロカプセルの感光硬
化は以下のように行われる。すなわち、６５０nm付近
（レッド）の波長の露光によって、シアンの増感色素を
内包したマイクロカプセルが固まり、５５０nm付近（グ
リーン）の波長の露光によって、マゼンタの増感色素を
内包したマイクロカプセルが固まり、４５０nm付近（ブ
ルー）の波長の露光によって、イエローの増感色素を内
包したマイクロカプセルが固まる。Photosensitive curing of the photosensitive microcapsules is performed as follows. That is, microcapsules encapsulating a cyan sensitizing dye are solidified by exposure with a wavelength of around 650 nm (red), and microcapsules encapsulating a magenta sensitizing dye are solidified with exposure of a wavelength of around 550 nm (green). Upon exposure to light having a wavelength near 450 nm (blue), the microcapsules containing the yellow sensitizing dye solidify.
【００１９】この時、それぞれの感光性マイクロカプセ
ルの色材濃度が通常濃度で、均一に混合されて塗布され
ていると、図２に示すように、シアンのマイクロカプセ
ルの感度とイエローやマゼンタのマイクロカプセルの感
度との間に重なる部分ができるので、原稿の画像の色が
忠実に再現されなくなるのである。At this time, if the coloring material concentration of each photosensitive microcapsule is a normal concentration and is uniformly mixed and applied, as shown in FIG. 2, the sensitivity of the cyan microcapsule and that of yellow or magenta are shown. Since there is a portion that overlaps with the sensitivity of the microcapsule, the color of the original image cannot be faithfully reproduced.
【００２０】しかし、本発明は、図１に示すように、マ
ゼンタ発色感光性マイクロカプセル２、イエロー発色感
光性マイクロカプセル３の色材濃度が通常濃度であるの
に対し、シアン発色感光性マイクロカプセル１の色材濃
度は通常濃度よりも高い。すなわち、該シアン発色感光
性マイクロカプセル１の破壊によって発色するシアン色
濃度は、他の２色のカプセル崩壊によるマゼンタ、イエ
ロー発色濃度よりも高い。従って、該シアン発色感光性
マイクロカプセル１の本来感度を持たない方がよい波長
での硬化に伴うシアン色濃度低下がなくなり、発色不良
が改善される。However, according to the present invention, as shown in FIG. 1, the coloring material density of the magenta coloring photosensitive microcapsules 2 and the yellow coloring photosensitive microcapsules 3 is normal, whereas the cyan coloring photosensitive microcapsules are normal. The colorant density of 1 is higher than the normal density. That is, the cyan color density developed by the destruction of the cyan color-sensitive photosensitive microcapsules 1 is higher than the magenta and yellow color densities caused by the capsule collapse of the other two colors. Therefore, the cyan color density of the microcolor-sensitive photosensitive microcapsules 1 should not have the inherent sensitivity.
【００２１】[0021]
【実施例】以下、本発明の感光性マイクロカプセルを具
体化した一実施例を図面を参照して説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the photosensitive microcapsule of the present invention will be described below with reference to the drawings.
【００２２】まず第１に本発明の感光性マイクロカプセ
ルの調製方法を説明する。First, the method for preparing the photosensitive microcapsules of the present invention will be described.
【００２３】イエローマイクロカプセルの調製 まず始めに、モノマ−としてのポリエチレングリコール
ジアクリレート（東亜合成社製アロニックスＭ２４０）
とジペンタエリスリトールヘキサアクリレート（東亜合
成社製アロニックスＭ４００）を３：４に配合したもの
を１００重量部と、重合開始剤としての２，２−ジメチ
ル−２−モルフォリノ−４´−メチルチオアセトフェノ
ン（チバガイギー製イルガキュア９０７）を３．５重量
部と、感度増感剤としての２，４−ジエチルチオキサン
トン（日本化薬製カヤキュアＤＥＴＸ）を３．５重量部
と、増感色素としての３−テノイル−７−ジメチルアミ
ノクマリンを０．５重量部と、色材としてのジスアゾ系
イエロー顔料を１重量部を混合した物を５分間超音波分
散し、１００℃で１０分間加熱することにより感光性組
成物を得る。Preparation of Yellow Microcapsules First, polyethylene glycol diacrylate as a monomer (Aronix M240 manufactured by Toagosei Co., Ltd.)
And 100 parts by weight of dipentaerythritol hexaacrylate (Aronix M400 manufactured by Toagosei Co., Ltd.) in a ratio of 3: 4, and 2,2-dimethyl-2-morpholino-4′-methylthioacetophenone (Ciba Geigy) as a polymerization initiator. Irgacure 907), 3.5 parts by weight, 2,4-diethylthioxanthone (Kayacure DETX manufactured by Nippon Kayaku) as a sensitivity sensitizer, and 3-thenoyl-7 as a sensitizing dye. A mixture of 0.5 part by weight of dimethylaminocoumarin and 1 part by weight of a disazo yellow pigment as a coloring material is ultrasonically dispersed for 5 minutes, and heated at 100 ° C. for 10 minutes to form a photosensitive composition. obtain.
【００２４】次にこの感光性組成物をＰＶＡ１０％水溶
液に乳化する。そして、この乳化液に塩化アンモニウム
水溶液を混入し、さらに、メラミンプレポリマー水溶液
を加える。このメラミンプレポリマーはＰＨ８のアルカ
リ水溶液にメラミンとホルマリンを１：３の割合で溶解
し１５分間８０℃で加熱して得られるものである。そし
て、その後、先の乳化溶液を８０℃で４時間攪はんしな
がら反応させてイエローの感光性マイクロカプセルを得
た。Next, the photosensitive composition is emulsified in a 10% PVA aqueous solution. Then, an ammonium chloride aqueous solution is mixed with this emulsion, and a melamine prepolymer aqueous solution is further added. This melamine prepolymer is obtained by dissolving melamine and formalin in a ratio of 1: 3 in an alkaline aqueous solution of PH8 and heating at 80 ° C. for 15 minutes. Then, the above emulsified solution was reacted at 80 ° C. for 4 hours with stirring to obtain yellow photosensitive microcapsules.
【００２５】マゼンタマイクロカプセルの調製 まず始めにモノマ−としてのポリエチレングリコールジ
アクリレート（東亜合成社製アロニックスＭ２４０）と
ジペンタエリスリトールヘキサアクリレート（東亜合成
社製アロニックスＭ４００）を３：４に配合したものを
１００重量部と、重合開始剤としての［（η5 −２，４
−シクロペンタジエン−１−イル）［（１，２，３，
４，５，６−η）−（１−メチルエチル）ベンゼン］鉄
（１＋）ヘキサフルオロホスフェート（１−）］（チバ
ガイギー製イルガキュア２６１）を１０重量部と、増感
色素としてのエオシンＹを０．５重量部と、色材として
のキナクリドン系マゼンタ顔料を１重量部を混合した物
を５分間超音波分散し、１００℃で１０分間加熱するこ
とにより感光性組成物を得る。Preparation of magenta microcapsule First, a mixture of polyethylene glycol diacrylate (Aronix M240 manufactured by Toagosei Co., Ltd.) and dipentaerythritol hexaacrylate (Aronix M400 manufactured by Toagosei Co., Ltd.) as a monomer in a ratio of 3: 4 was prepared. 100 parts by weight and [(η 5 -2,4 as a polymerization initiator
-Cyclopentadiene-1-yl) [(1,2,3,
4,5,6- (η)-(1-methylethyl) benzene] iron (1+) hexafluorophosphate (1-)] (Ciba Geigy Irgacure 261) and 10 parts by weight of Eosin Y as a sensitizing dye. A mixture of 0.5 parts by weight and 1 part by weight of a quinacridone-based magenta pigment as a coloring material is ultrasonically dispersed for 5 minutes, and heated at 100 ° C. for 10 minutes to obtain a photosensitive composition.
【００２６】次に、この感光性組成物をＰＶＡ１０％水
溶液に乳化する。そして、この乳化液に塩化アンモニウ
ム水溶液を混入し、さらに、メラミンプレポリマー水溶
液を加える。その後、この乳化溶液を８０℃で４時間攪
はんしながら反応させてマゼンタの感光性マイクロカプ
セルを得た。Next, this photosensitive composition is emulsified in a 10% PVA aqueous solution. Then, an ammonium chloride aqueous solution is mixed with this emulsion, and a melamine prepolymer aqueous solution is further added. Then, the emulsified solution was reacted at 80 ° C. for 4 hours while stirring to obtain magenta photosensitive microcapsules.
【００２７】シアンマイクロカプセルの調製 まず始めに、モノマ−としてのポリエチレングリコール
ジアクリレート（東亜合成社製アロニックスＭ２４０）
とジペンタエリスリトールヘキサアクリレート（東亜合
成社製アロニックスＭ４００）を３：４に配合したもの
を１００重量部と、重合開始剤としての［（η5 −２，
４−シクロペンタジエン−１−イル）［（１，２，３，
４，５，６−η）−（１−メチルエチル）ベンゼン］鉄
（１＋）ヘキサフルオロホスフェート（１−）］（チバ
ガイギー製イルガキュア２６１）を１０重量部と、増感
色素としてのメチレンブルーを０．５重量部と、色材と
してのフタロシアニン系シアン顔料を１．５重量部を混
合した物を５分間超音波分散し、１００℃で１０分間加
熱することにより感光性組成物を得る。Preparation of cyan microcapsules First, polyethylene glycol diacrylate as a monomer (Aronix M240 manufactured by Toagosei Co., Ltd.)
Dipentaerythritol hexaacrylate (manufactured by Toagosei Co., Ltd. Aronix M400) 3: 100 parts by weight of a material obtained by blending to 4, as a polymerization initiator [(eta 5 -2,
4-cyclopentadiene-1-yl) [(1,2,3,
4,5,6- (η)-(1-methylethyl) benzene] iron (1+) hexafluorophosphate (1-)] (Ciba Geigy Irgacure 261) and 10 parts by weight of methylene blue as a sensitizing dye. A mixture of 5 parts by weight and 1.5 parts by weight of a phthalocyanine-based cyan pigment as a coloring material is ultrasonically dispersed for 5 minutes and heated at 100 ° C. for 10 minutes to obtain a photosensitive composition.
【００２８】次に、この感光性組成物をＰＶＡ１０％水
溶液に乳化する。この乳化液に塩化アンモニウム水溶液
を混入し、さらに、メラミンプレポリマー水溶液を加え
る。その後、この乳化溶液を８０℃で４時間攪はんしな
がら反応させてシアンの感光性マイクロカプセルを得
た。Next, this photosensitive composition is emulsified in a 10% PVA aqueous solution. An ammonium chloride aqueous solution is mixed with this emulsion, and a melamine prepolymer aqueous solution is further added. Then, this emulsified solution was reacted at 80 ° C. for 4 hours with stirring to obtain cyan photosensitive microcapsules.
【００２９】感光性マイクロカプセルシートの製作とそ
の評価 ポリエチレンテレフタレート（ＰＥＴ）フィルムシート
上に、前述したように調製されたシアン発色感光性マイ
クロカプセル１、マゼンタ発色感光性マイクロカプセル
２、イエロー発色感光性マイクロカプセル３の混合物を
均一の厚みに塗布する。このシートを８０度の乾燥炉に
いれて１０分間乾燥させる。Production of photosensitive microcapsule sheet and its evaluation On a polyethylene terephthalate (PET) film sheet, cyan color-developing light-sensitive microcapsules 1, magenta color-sensing light-sensitive microcapsules 2 and yellow-coloring-sensitivity prepared as described above. The mixture of microcapsules 3 is applied to a uniform thickness. The sheet is placed in a drying oven at 80 ° C. and dried for 10 minutes.
【００３０】このシートの感光性マイクロカプセル塗工
面に画像電子学会カラーテストチャートＮｏ．２１の焼
付け露光を施し、感光性マイクロカプセル塗工面を普通
受像紙に接触させて加圧し、該普通受像紙に印画された
イエロー、マゼンタ、シアン、ブルー、グリーン、レッ
ドの各チャート色を分光測色計ＭＳＣ−２（スガ試験
機）にてＤ65２°視野の条件で反射測色を行った。図３
ａは、測色の結果得られたＬ＊ａ＊ｂ＊表色系の色度図
を示している。ここで、Ｌ＊ａ＊ｂ＊表色系とは、ＣＩ
Ｅ（国際照明委員会）にて定められた表色系のひとつ
で、Ｌ＊は明度を表し、ａ＊及びｂ＊は彩度を表してい
る。また、Ｌ＊ａ＊ｂ＊表色系の色度図とは、ａ＊、ｂ
＊をそれぞれ横軸、縦軸にとった座標グラフのことで、
おおよそ色度図の左方向は緑、右方向は赤、上方向は
黄、下方向は青に対応している。この色度図において
は、外側に行けば行くほど色の鮮明さは増していく。On the coated surface of the photosensitive microcapsule of this sheet, the color test chart No. 21 printing exposure is performed, the photosensitive microcapsule coated surface is brought into contact with the ordinary image-receiving paper and pressure is applied, and each chart color of yellow, magenta, cyan, blue, green and red printed on the ordinary image-receiving paper is spectroscopically measured. Reflection colorimetry was performed with a colorimeter MSC-2 (Suga Test Instruments) under the condition of D 65 2 ° visual field. Figure 3
a shows a chromaticity diagram of the L * a * b * color system obtained as a result of color measurement. Here, the L * a * b * color system is CI
It is one of the color systems defined by E (International Commission on Illumination), L * represents lightness, and a * and b * represent saturation. The chromaticity diagram of the L * a * b * color system is a *, b
A coordinate graph with * on the horizontal axis and on the vertical axis.
In the chromaticity diagram, the left direction corresponds to green, the right direction corresponds to red, the upper direction corresponds to yellow, and the lower direction corresponds to blue. In this chromaticity diagram, the sharpness of the color increases as it goes outward.
【００３１】比較例 前述とは別にフタロシアニン系顔料を１重量部とした比
較用シアン発色感光性マイクロカプセルを調製し、該比
較用シアン発色感光性マイクロカプセルと、先に調製し
たイエロー、マゼンタの感光性マイクロカプセルを均一
に混合し、この混合物をＰＥＴシートに実施例と同じ厚
みに成るように塗布し、乾燥した。このシート上に、実
施例と同じテストチャートＮｏ．２１を焼付け露光し、
感光性マイクロカプセル塗工面を普通受像紙に接触させ
て加圧し、該ＭＳＣ−２にて該普通受像紙のチャート色
の反射測色を行った。その結果、図３ｂに示す色度図が
得られた。Comparative Example Separately from the above, comparative cyan color-developing photosensitive microcapsules containing 1 part by weight of a phthalocyanine pigment were prepared. The comparative cyan color-developing photosensitive microcapsules and the previously prepared yellow and magenta photosensitive pigments were prepared. Microcapsules were uniformly mixed, and this mixture was applied to a PET sheet so as to have the same thickness as in the example, and dried. On this sheet, the same test chart No. 21 is exposed by exposure,
The coated surface of the photosensitive microcapsules was brought into contact with the ordinary image-receiving paper and pressed, and the chart color of the ordinary image-receiving paper was measured by reflection with the MSC-2. As a result, the chromaticity diagram shown in FIG. 3b was obtained.
【００３２】また、図３ｃは該画像電子学会カラーテス
トチャートＮｏ．２１を直接、該ＭＳＣ−２にて反射測
色を行った結果を示している。尚、図３ａ、ｂ中の点線
は、図３ｃの測色結果を重ね書きしたものである。Further, FIG. 3c shows the color test chart No. 21 shows the result of directly performing reflection colorimetry on the MSC-2. The dotted lines in FIGS. 3a and 3b are the colorimetric results of FIG. 3c overwritten.
【００３３】図３ａと図３ｂを比べてわかるように、図
３ｂの比較例において特にグリーンがイエローよりの色
になっているのに対して、本実施例の場合、図３ａのよ
うにグリーン色が原稿となっているテストチャートのグ
リーンに非常に近づき、原稿の色を忠実に再現している
様子がわかる。As can be seen by comparing FIGS. 3a and 3b, in the comparative example of FIG. 3b, the green color is particularly different from the yellow color, whereas in the case of this embodiment, the green color is as shown in FIG. 3a. It is very close to the green of the test chart where is the manuscript, and you can see that the color of the manuscript is faithfully reproduced.
【００３４】また、本発明のシアン発色感光性マイクロ
カプセル中の色材濃度（量）は、通常加えられる色材濃
度（量）に対して１．１〜５．０倍であることが好まし
い。もし、シアンカプセルの色材濃度が１．１倍よりも
小さいと、本発明の効果がほとんど確認できなくなって
しまい、５．０倍よりも大きいとシアン自体の色濃度が
濃くなりすぎて黒ずんでしまうという問題が発生する。
さらに、本発明の効果を発揮するために、シアンカプセ
ルの色材濃度は１．１〜３．０倍であることがさらに好
ましく、１．５〜２．０倍であることが最も好ましい。The color material concentration (amount) in the cyan color-sensitive photosensitive microcapsules of the present invention is preferably 1.1 to 5.0 times the color material concentration (amount) normally added. If the color material density of the cyan capsule is less than 1.1 times, the effect of the present invention can hardly be confirmed, and if it is more than 5.0 times, the color density of cyan itself becomes too dark and becomes dark. There is a problem that it will end up.
Further, in order to exert the effect of the present invention, the color material concentration of the cyan capsule is more preferably 1.1 to 3.0 times, and most preferably 1.5 to 2.0 times.
【００３５】尚、本発明は、上述した実施例に限定され
るものではなく、その趣旨を逸脱しない限りにおいて、
種々の変更を加えることができる。It should be noted that the present invention is not limited to the above-mentioned embodiments, and within the scope of the spirit of the present invention,
Various changes can be made.
【００３６】例えば、上述の実施例において、露光面の
最上層に紫外線吸収層が設けられていてもよい。また、
ブラックの感光性マイクロカプセルを用いてもよい。さ
らに、色補正のためなどに、他の色の感光性マイクロカ
プセルを用いてもよい。For example, in the above-mentioned embodiment, an ultraviolet absorbing layer may be provided on the uppermost layer of the exposed surface. Also,
Black photosensitive microcapsules may be used. Furthermore, photosensitive microcapsules of other colors may be used for color correction.
【００３７】また、感光性マイクロカプセルはトナー状
のものでもよい。その場合、塗布方法は静電式でも粘着
式でもよい。支持体は、紙でも、金属でも、セラミック
であってもよい。支持体はドラム状であってもよい。The photosensitive microcapsules may be in the form of toner. In that case, the application method may be electrostatic or adhesive. The support may be paper, metal or ceramic. The support may be drum-shaped.
【００３８】[0038]
【発明の効果】以上説明したことから明かなように、本
発明の感光性マイクロカプセルは、シアンに発色する色
材の濃度を通常濃度の１．１倍以上にしたことにより、
シート上に塗布されているか、トナーの状態であるかに
関わらず、且つ変換露光、直接露光等の何れの露光方法
を用いても、不要な感度に基づくシアン発色不良を生じ
ることなく、原稿画像の色彩を忠実に再現した画像を得
ることができる。As is apparent from the above description, in the photosensitive microcapsule of the present invention, the density of the coloring material that develops cyan is 1.1 times or more the normal density,
Regardless of whether it is coated on the sheet or in the toner state, and regardless of which exposure method such as conversion exposure or direct exposure is used, the original image does not cause cyan color defect due to unnecessary sensitivity and does not occur. An image that faithfully reproduces the color of can be obtained.
【図１】本発明の感光性マイクロカプセルの構成を具体
化した一実施例を示す概略断面図である。FIG. 1 is a schematic cross-sectional view showing an embodiment embodying the constitution of a photosensitive microcapsule of the present invention.
【図２】従来の感光性マイクロカプセルの感度の説明に
供する図である。FIG. 2 is a diagram for explaining the sensitivity of a conventional photosensitive microcapsule.
【図３】本発明の感光性マイクロカプセルと比較例の色
再現を表す図である。FIG. 3 is a diagram showing color reproduction of a photosensitive microcapsule of the present invention and a comparative example.
１ シアンのマイクロカプセル ２ マゼンタのマイクロカプセル ３ イエローのマイクロカプセル 1 cyan microcapsule 2 magenta microcapsule 3 yellow microcapsule
Claims (1)
いられ、シアン、マゼンタ、イエロ−にそれぞれ発色す
る色材を備えた複数種の感光性マイクロカプセルにおい
て、 前記シアンに発色する色材の濃度を通常濃度の１．１倍
以上にしたことを特徴とする感光性マイクロカプセル。1. A plurality of types of photosensitive microcapsules which are used when forming a color image on an image receiving paper and are provided with coloring materials that respectively develop cyan, magenta and yellow. A photosensitive microcapsule characterized in that the concentration is 1.1 times or more the normal concentration.