JPH06300085A - Conveyor belt - Google Patents
Conveyor beltInfo
- Publication number
- JPH06300085A JPH06300085A JP5086493A JP8649393A JPH06300085A JP H06300085 A JPH06300085 A JP H06300085A JP 5086493 A JP5086493 A JP 5086493A JP 8649393 A JP8649393 A JP 8649393A JP H06300085 A JPH06300085 A JP H06300085A
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- conveyor belt
- cord
- twisted
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、補強体を備えたコンベ
アベルトに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a conveyor belt provided with a reinforcing member.
【０００２】[0002]
【従来の技術】最近のコンベアベルトの高強力分野は、
主に、その補強体にスチールコードが用いられている
が、近年、省エネルギー、地球環境問題等からコンベア
ベルトの軽量化、易廃棄性が求められているため、スチ
ールコードに代わり有機繊維材料を用いることも必要に
なってきた。2. Description of the Related Art Recently, high strength fields of conveyor belts are
Steel cords are mainly used for the reinforcements, but in recent years, since energy saving, global environmental issues, and the like, weight reduction of conveyor belts and easy disposal are required, organic fiber materials are used instead of steel cords. Things have become necessary.
【０００３】また、コンベアベルトは、運搬する輸送物
や周辺環境の影響、例えば、地下坑内などで水分下で使
用されることも多く、水分によるスチールコードのサビ
が強度低下や耐久性の低下、並ぶに接着力の低下に結び
つく例もあり、信頼性向上、メインテナンスフリー化の
ためスチールコードの有機繊維材料化のニーズも高い。Further, the conveyor belt is often used under the influence of the transported goods to be conveyed or the surrounding environment, for example, in the underground mine under the moisture, and the rust of the steel cord due to the moisture lowers the strength and the durability. In addition, there are cases where it leads to a decrease in adhesive strength, and there is a great need for steel cords to be made of organic fiber materials to improve reliability and make them maintenance-free.
【０００４】スチールコードベルトの代替としてアラミ
ド繊維（商品名「ケブラー」、「トワロン」、「テクノ
ーラ」など）で補強したコンベアベルトが近年作製され
るようになってきている。アラミド繊維製の補強体を備
えたコンベアベルトは、その補強層が一層構造のものが
知られているが、現在コマーシャルベースで作られてい
るのは一層構造のみであり、そのＭＡＸ強力は、アラミ
ド繊維の強度及び補強体を作る撚り・織り設備等の制約
により２５００〜３０００Ｋｇ／ｃｍが限界である。As a substitute for steel cord belts, conveyor belts reinforced with aramid fibers (trade names "Kevlar", "Twaron", "Technora", etc.) have been recently produced. Conveyor belts provided with a reinforcement made of aramid fiber are known to have a one-layer reinforcement layer, but at present, only a one-layer structure is made on a commercial base, and its MAX strength is aramid. The limit is 2500 to 3000 Kg / cm due to the fiber strength and the twisting and weaving equipment for making the reinforcement.
【０００５】また、アラミド製コンベアベルトは、アラ
ミド繊維の弱点である屈曲疲労性の悪さを補強層の一層
化というベルト構造面でカバーしているので、補強体の
多層化ができず、補強体の限界強力がそのままベルト強
力の限界になっている。現在、国内外で稼働しているス
チールベルトの大半は８００〜５０００Ｋｇ／ｃｍのク
ラスである。従って、特に、２５００〜５０００Ｋｇ／
ｃｍクラスの有機繊維からなる補強体を備えたコンベア
ベルトを作製することが望まれている。Further, since the aramid conveyor belt covers the weakness of bending fatigue, which is a weak point of the aramid fiber, with a belt structure of a single reinforcing layer, the reinforcing body cannot be multilayered and the reinforcing body cannot be formed. The limit strength of the belt is the limit of belt strength. Currently, most of the steel belts operating in Japan and overseas are in the class of 800 to 5000 kg / cm. Therefore, in particular, 2500 to 5000 kg /
It is desired to make a conveyor belt with a reinforcement made of cm-class organic fibers.
【０００６】一方、汎用のナイロンやポリエステル繊維
製の補強体によっても多層化により３０００〜３５００
Ｋｇ／ｃｍのコンベアベルトを作製することができる
が、この場合は、スチールに較べ伸びが大きすぎるため
機体のストローク（テークアップ機構）で吸収しきれな
いという問題点がある。[0006] On the other hand, a general-purpose nylon or polyester fiber reinforcement is also used to form a multi-layer structure, and the number of layers is 3000 to 3500.
A conveyor belt of Kg / cm can be manufactured, but in this case, there is a problem that it cannot be absorbed by the stroke (take-up mechanism) of the machine body because the elongation is too large compared with steel.
【０００７】[0007]
【発明が解決しようとする課題】本発明の目的は、上記
従来の問題点を解決するものであり、屈曲疲労性及び接
着性の向上が図られ、２５００〜５０００Ｋｇ／ｃｍク
ラスの繊維からなる補強体を備えたコンベアベルトを提
供することを目的とするものであり、更に、耐熱性、難
燃性の向上を発揮することができるコンベアベルトを提
供することにある。SUMMARY OF THE INVENTION The object of the present invention is to solve the above-mentioned problems of the prior art, to improve the bending fatigue property and the adhesive property, and to reinforce the fibers of 2500 to 5000 Kg / cm class. It is an object of the present invention to provide a conveyor belt including a body, and further to provide a conveyor belt that can exhibit improved heat resistance and flame retardancy.
【０００８】[0008]
【課題を解決するための手段】本発明者らは、上記従来
の課題を解決するために鋭意検討した結果、コンベアベ
ルトに使用される補強体を特定の繊維から構成される補
強体とすることにより上記目的のコンベアベルトを得る
ことに成功し、本発明を完成するに至ったのである。DISCLOSURE OF THE INVENTION As a result of intensive studies to solve the above-mentioned conventional problems, the present inventors have decided that the reinforcing body used in a conveyor belt is a reinforcing body made of specific fibers. As a result, the above-mentioned objective conveyor belt was successfully obtained, and the present invention was completed.
【０００９】すなわち、本発明は、 (1) ヘテロ環含有芳香族ポリマーからなる繊維と、他の
材料からなる繊維との混撚りコードから構成される補強
体を備えてなるコンベアベルトである。 (2) ヘテロ環含有芳香族ポリマーからなる繊維と、他の
材料からなる繊維とのデニール比が１：４〜４：１であ
る上記(1)記載のコンベアベルトである。 (3) ヘテロ環含有芳香族ポリマーからなる繊維がポリパ
ラフェニレンベンゾビスオキサゾール繊維又はポリパラ
フェニレンベンゾビスチアゾール繊維である上記(1)又
は(2)記載のコンベアベルトである。 (4) 混撚りコードは、諸撚り構造であり、下記式（Ｉ）
で表される上撚りの撚り係数Ｋが、少なくとも１１００
以上である上記(1)〜(3)の何れか一つに記載のコンベア
ベルトである。 Ｋ＝Ｔ×（Ｄｅ）1/2 ………（Ｉ） 〔なお、Ｔは、Ｔ（回／１０cm）＝上撚り数であり、Ｄ
ｅは、上撚りコードのデニール数である。〕That is, the present invention is (1) a conveyor belt provided with a reinforcing member composed of a mixed twist cord of a fiber made of a heterocycle-containing aromatic polymer and a fiber made of another material. (2) The conveyor belt according to (1) above, wherein the fiber made of the heterocycle-containing aromatic polymer and the fiber made of another material have a denier ratio of 1: 4 to 4: 1. (3) The conveyor belt according to the above (1) or (2), wherein the fiber made of a heterocycle-containing aromatic polymer is a polyparaphenylenebenzobisoxazole fiber or a polyparaphenylenebenzobisthiazole fiber. (4) A mixed twist cord has a ply twist structure and has the following formula (I).
The twist coefficient K of the upper twist represented by is at least 1100.
The conveyor belt according to any one of the above (1) to (3). K = T × (De) 1/2 (I) [where T is T (turns / 10 cm) = number of twists, D
e is the denier number of the twisted cord. ]
【００１０】以下、本発明の内容を説明する。本発明の
コンベアベルトは、ヘテロ環含有芳香族ポリマーからな
る繊維と、他の材料からなる繊維との混撚りコードから
構成される補強体を備えてなるものである。ヘテロ環含
有芳香族ポリマーからなる繊維としては、例えば、ポリ
パラフェニレンベンゾビスオキサゾール繊維（以下、Ｐ
ＢＯ繊維という）又はポリパラフェニレンベンゾビスチ
アゾール繊維（以下、ＰＢＴ繊維という）が挙げられ
る。これらの繊維は、炭素繊維の弾性率とアラミド繊維
の強度およびハンドリングの容易さを合わせもつ繊維で
あり、上記従来の炭素繊維、アラミド繊維などの有機繊
維よりも、さらに、高強度、低伸度、耐熱性、難燃性に
優れた繊維である。すなわち、これらの繊維は、強度が
２５ｇ／Ｄ以上であり、伸度が６．０％以下であり、分
解温度が６００℃以上であり、弾性率が１０００ｇ／Ｄ
以上であり、酸素指数（JIS K 7201により定義され、測
定されるものであり、Ｌ．Ｏ．Ｉ．とも称される）は４
０以上である。本発明は、上記の特性を有する繊維を用
いるものであるが、これらの繊維のうちＰＢＯ繊維を用
いることが好ましく、さらに、下記一般式（II）The contents of the present invention will be described below. The conveyor belt of the present invention comprises a reinforcing member composed of a mixed twisted cord of a fiber made of a heterocycle-containing aromatic polymer and a fiber made of another material. As the fiber made of a heterocycle-containing aromatic polymer, for example, polyparaphenylene benzobisoxazole fiber (hereinafter, referred to as P
Examples thereof include BO fibers) and polyparaphenylene benzobisthiazole fibers (hereinafter referred to as PBT fibers). These fibers are fibers having both the elastic modulus of carbon fibers, the strength of aramid fibers, and the ease of handling, and further higher strength and lower elongation than organic fibers such as the above conventional carbon fibers and aramid fibers. It is a fiber with excellent heat resistance and flame retardancy. That is, these fibers have a strength of 25 g / D or more, an elongation of 6.0% or less, a decomposition temperature of 600 ° C. or more, and an elastic modulus of 1000 g / D.
Above, the oxygen index (as defined and measured by JIS K 7201 and also referred to as LOI) is 4
It is 0 or more. The present invention uses fibers having the above-mentioned characteristics, and it is preferable to use PBO fibers among these fibers, and further, the following general formula (II)
【化１】 で表されるシス構造のＰＢＯ繊維を用いることが好まし
い。シス構造のＰＢＯ繊維は、強度が３８ｇ／Ｄであ
り、伸度が１．８％であり、分解温度が６３０℃であ
り、弾性率が２１００ｇ／Ｄであり、酸素指数は５５で
ある。[Chemical 1] It is preferable to use a PBO fiber having a cis structure represented by The cis-structured PBO fiber has a strength of 38 g / D, an elongation of 1.8%, a decomposition temperature of 630 ° C., an elastic modulus of 2100 g / D, and an oxygen index of 55.
【００１１】他の材料からなる繊維としては、コンベア
ベルトの補強体に汎用されている繊維が用いられ、例え
ば、ポリフェニレンサルファイド（ＰＰＳ）繊維、ポリ
エーテルイミド（ＰＥＩ）繊維、ポリエーテルエテール
ケトン（ＰＥＥＫ）繊維、ナイロン繊維（例えば、６ナ
イロン，６６ナイロン，４６ナイロン繊維）、芳香族ポ
リエステル繊維、芳香族ポリアミド繊維（例えば、アラ
ミド繊維）、炭素繊維、天然繊維、ビニロン、レーヨ
ン、ポリエステル繊維（例えば、ＰＥＴ，ＰＢＴ，ＰＥ
Ｎ繊維）、ポリエチレン繊維、ポリプロピレン繊維等を
単用又は併用することができる。As the fiber made of another material, a fiber generally used for a reinforcing member of a conveyor belt is used. For example, polyphenylene sulfide (PPS) fiber, polyether imide (PEI) fiber, polyether ether ketone ( PEEK fiber, nylon fiber (for example, 6 nylon, 66 nylon, 46 nylon fiber), aromatic polyester fiber, aromatic polyamide fiber (for example, aramid fiber), carbon fiber, natural fiber, vinylon, rayon, polyester fiber (for example, , PET, PBT, PE
N fibers), polyethylene fibers, polypropylene fibers and the like can be used alone or in combination.
【００１２】異種繊維を組み合わせて混撚りしたコード
（ハイブリッドコード）は、その組み合わせる素材、デ
ニール比（太さの比）、撚り数等の選択により目的とし
た特性（強力、伸び、弾性率、クリープ、熱収縮率、耐
久性、耐熱性、接着性、難燃性など）を得ることができ
る。混撚りコードの特性は、その組合せる素材の特性に
依存するためＰＢＯ繊維又はＰＢＴ繊維の原糸強度が２
５ｇ／Ｄ以上、好ましくは、３５ｇ／Ｄ以上でないとＰ
ＢＯ又はＰＢＴ混撚りコードの強度は、アラミド繊維単
独コード以上の強度を得ることができず、その結果アラ
ミド繊維を越えてスチールベルトに匹敵する（３０００
ｋｇ／ｃｍ以上の）高強力コンベアベルトを得ることは
できず適当でない。同様に，ＰＢＯ繊維又はＰＢＴ繊維
の伸度が６％未満、好ましくは４．５％未満でないとＰ
ＢＯ混撚りコードの伸度が１０％以上になり、その場合
ベルトの伸びがスチールベルトより大きくなってしまい
適当でない。ＰＢＯ又はＰＢＴの混撚りコードの強度
は、２０ｇ／Ｄ以上も可能であり、アラミド繊維単独コ
ード以上の強度を得ることができる。A cord (hybrid cord) obtained by mixing and twisting different kinds of fibers is a desired characteristic (strength, elongation, elastic modulus, creep) depending on selection of materials to be combined, denier ratio (ratio of thickness), number of twists and the like. , Heat shrinkage, durability, heat resistance, adhesiveness, flame retardancy, etc.) can be obtained. Since the characteristics of the mixed twisted cord depend on the characteristics of the materials to be combined, the strength of the PBO fiber or PBT fiber is 2 or less.
P of 5 g / D or more, preferably 35 g / D or more
The strength of the BO or PBT mixed twisted cord cannot be higher than that of the aramid fiber alone cord, and as a result, it exceeds that of the aramid fiber and is comparable to a steel belt (3000).
A high strength conveyor belt (kg / cm or more) cannot be obtained and is not suitable. Similarly, if the elongation of PBO fiber or PBT fiber is less than 6%, preferably less than 4.5%, P
The BO mixed twist cord has an elongation of 10% or more, and in that case, the elongation of the belt becomes larger than that of the steel belt, which is not suitable. The strength of the mixed twisted cord of PBO or PBT can be 20 g / D or more, and the strength equal to or higher than the cord of the aramid fiber alone can be obtained.
【００１３】ＰＢＯ繊維又はＰＢＴ繊維をナイロン、ポ
リエステル等の汎用繊維と組み合わせ混撚りコードにす
ると、ＰＢＯ等の屈曲疲労性や擦れ摩耗性及び接着性が
大幅に改善される（この点に関しては、更に後述する実
施例で詳しく説明する）。ＰＢＯ繊維等を混撚り化する
ことで、その屈曲疲労性が大幅に改善されるため補強層
に負荷される屈曲条件が一層構造よりはるかに厳しくな
る二層構造のコンベアベルトの補強体として屈曲疲労を
考慮せずに使用可能となる。ＰＢＯ繊維等の混撚りコー
ドを使用した補強層（体）は、一層当りのＭＡＸ強力が
アラミド繊維並の２５００〜３０００Ｋｇ／ｃｍが可能
となり、しかも、二層構造にしてもコンベアベルトの疲
労性は問題とならないため、アラミド繊維の約２倍の５
０００〜５５００Ｋｇ／ｃｍのコンベアベルトを作製す
ることができる。When a PBO fiber or PBT fiber is combined with a general-purpose fiber such as nylon or polyester to form a mixed twist cord, bending fatigue, abrasion resistance and adhesiveness of PBO or the like are significantly improved. This will be described in detail in Examples described later). By bending PBO fibers etc. into a twisted mixture, the bending fatigue property is greatly improved, and the bending conditions applied to the reinforcing layer become much more severe than in the single layer structure. It can be used without considering. The reinforcing layer (body) using the mixed twisted cord such as PBO fiber can have the MAX strength per layer of 2500 to 3000 kg / cm, which is comparable to that of aramid fiber. 5 times that of aramid fiber
A conveyor belt of 000 to 5500 Kg / cm can be produced.
【００１４】本発明において、混撚りコードは、諸撚り
構造であり、下記式（Ｉ）で表される上撚りの撚り係数
Ｋが、少なくとも１１００以上であることが好ましい。 Ｋ＝Ｔ×（Ｄｅ）1/2 ………（Ｉ） 〔なお、Ｔは、Ｔ（回／１０cm）＝上撚り数であり、Ｄ
ｅは、上撚りコードのデニール数である。〕 混撚りコードは、異なった素材のＡ繊維とＢ繊維を始め
各々別々に所定の撚り数で撚ったコード（下撚りコー
ド）を、次の撚りステップでＡ繊維とＢ繊維を所定の撚
り数で撚り合せて複合化し混撚りコード（上撚りコー
ド）とするのが一般的である。混撚りに限らず、上記の
下撚り・上撚りのように２ステップ以上で撚り加工した
撚りコードの撚り構造を諸撚り構造と呼ぶ。諸撚り構造
には、上記以外に下撚り・中撚り・上撚りの３ステップ
で撚り加工したもの、あるいは４ステップ以上で撚り加
工したものがある。In the present invention, the mixed twist cord has a ply twist structure, and the twist coefficient K of the upper twist represented by the following formula (I) is preferably at least 1100 or more. K = T × (De) 1/2 (I) [where T is T (turns / 10 cm) = number of twists, D
e is the denier number of the twisted cord. The mixed twisted cord is a cord (lower twisted cord) obtained by separately twisting the A fiber and the B fiber of different materials with a predetermined twist number, and then twisting the A fiber and the B fiber with a predetermined twist in the next twisting step. It is common to twist the fibers in some numbers to form a composite and to make a mixed twisted cord (twisted cord). Not only the mixed twisting, the twisting structure of a twisted cord that is twisted in two or more steps like the above-mentioned lower twisting and upper twisting is called a ply twisting structure. In addition to the above, the ply-twisted structure includes a ply-twisted, middle-twisted, and upper-twisted three-step twisted structure or a four-step or more twisted-twisted structure.
【００１５】Ａ繊維とＢ繊維を各々別々に撚る場合（上
記の下撚りなど）、Ａ繊維の撚り係数ＫAとＢ繊維の撚
り係数ＫBは必ずしも同一にする必要はなく、目的に応
じて変えて良い。撚り係数ＫA及び撚り係数ＫBは、下記
式で表される。 ＫA＝ＴA×（ＤｅA）1/2 ＴA（回／１０ｃｍ）＝Ａ繊維の撚り数 ＤｅA＝Ａ繊維のデニール数 ＫB＝ＴB×（ＤｅB）1/2 ＴB（回／１０ｃｍ）＝Ｂ繊維の撚り数 ＤｅB＝Ｂ繊維のデニール数 また、本発明では、３種以上の異なった繊維材料を用い
て混撚りすることもできる。When the A fiber and the B fiber are separately twisted (for example, the above-mentioned twisting), the twisting coefficient K A of the A fiber and the twisting coefficient K B of the B fiber do not necessarily have to be the same. You can change it. The twist coefficient K A and the twist coefficient K B are represented by the following equations. K A = T A × (De A) 1/2 T A ( times / 10 cm) = A twist number of the fibers De A = A fiber denier K B = T B × (De B) 1/2 T B ( (Number of turns / 10 cm) = number of twists of B fiber De B = number of denier of B fiber In the present invention, three or more different fiber materials can be used for twisting.
【００１６】ＰＢＯ繊維等と他の繊維とを混撚り加工す
る場合、ＰＢＯ繊維等と他の繊維（ポリアミド、ポリエ
ステルなど）との混撚り（異種繊維の撚り合せ）は、下
撚り、上撚り等どの撚りステップで行っても良いが、好
ましくは２ステップ目である。最終的に仕上がった混撚
りコードの撚り構造は、少なくとも２ステップ以上で撚
り加工した撚り構造、即ち、諸撚り構造になってないと
ＰＢＯ繊維等と他の繊維との複合化が充分になされず実
用に耐えないこととなる。また、混撚りコードの上撚り
（最終ステップの撚り）の撚り係数（Ｋ）が少なくとも
１１００以上、好ましくは１４００以上でないと、ＰＢ
Ｏ繊維等と他の繊維との複合化が充分でなく目的とする
特性値が得られない（具体的には、後述する実施例にお
いて説明する失敗例のように引張りテストでＰＢＯ繊維
と他の繊維が同時に破断しない）こととなる。When the PBO fiber or the like and the other fiber are mixed and twisted, the PBO fiber or the like and the other fiber (polyamide, polyester, etc.) are mixed and twisted together. Although any twisting step may be performed, it is preferably the second step. If the final twisted structure of the mixed twisted cord is a twisted structure that is twisted in at least two steps or more, that is, a twisted structure, the PBO fiber and other fibers cannot be sufficiently combined. It will not be practical. Further, the twisting coefficient (K) of the twisting (twisting in the final step) of the mixed twisted cord is not at least 1100 or more, preferably 1400 or more, the PB
The desired characteristic value cannot be obtained because the O fiber or the like and other fibers are not sufficiently compounded (specifically, the PBO fiber and other fibers are not tested by the tensile test as in the failure example described in Examples described later). The fibers do not break at the same time).
【００１７】混撚りコードのヘテロ環含有芳香族ポリマ
ーからなる繊維、例えば、ＰＢＯ繊維と他の繊維とのデ
ニール比は、１：４〜４：１、好ましくは１：２．５〜
２．５：１とすることが望ましく、この範囲を外れる
と、例えば、ＰＢＯ繊維：６６ナイロン繊維が１０：１
のデニール比になると混撚りコードの特性は、ほとんど
ＰＢＯ単独コードと変わらなくなってしまい混撚り化す
る意味がなくなってしまうからである。The denier ratio of the fiber made of the heterocycle-containing aromatic polymer of the mixed twist cord, for example, the PBO fiber and the other fiber is 1: 4 to 4: 1, preferably 1: 2.5 to.
It is desirable to set the ratio to 2.5: 1. When the ratio is out of this range, for example, PBO fiber: 66 nylon fiber is 10: 1.
This is because the characteristics of the mixed twisted cord are almost the same as those of the PBO single cord at the denier ratio of 1, and there is no point in making the mixed twisted cord.
【００１８】本発明においてコンベアベルトに埋設され
る補強体は、上記の特性を有する混撚りコードを使用し
て作製するものであり、補強体の構造例としては、ロー
プ（ケーブル）構造、平織構造、斜紋織構造、バスケッ
ト織構造、レノー織構造、簾コード織構造、ソリッドウ
ーブン織構造、ストレートワープ織構造等が挙げられる
が、これらに限定されるものではない。In the present invention, the reinforcing member embedded in the conveyor belt is manufactured by using the twisted cord having the above-mentioned characteristics. Examples of the reinforcing member structure include a rope (cable) structure and a plain weave structure. Examples include, but are not limited to, a diagonal weave structure, a basket weave structure, a Renault weave structure, a cord cord weave structure, a solid woven weave structure, and a straight warp weave structure.
【００１９】本発明のコンベアベルトのベルト自体は、
コンベアベルトに汎用されているゴム又は樹脂を使用す
ることができ、コンベアベルトの使用目的、態様に応じ
て、天然ゴム、合成ゴムなどの公知のゴム配合物、塩化
ビニル樹脂、フッ素樹脂、シリコーン樹脂、ウレタン樹
脂等の公知の樹脂配合物を用いることができる。また、
コンベアベルトの耐熱性、難燃性を向上させるために、
上記ゴム配合物又は樹脂配合物に、耐熱性、難燃性等を
有するゴム又は樹脂、及び／又は難燃性付与剤などの種
々の添加剤を配合することができる。The belt itself of the conveyor belt of the present invention is
It is possible to use a commonly used rubber or resin for the conveyor belt, depending on the purpose of use of the conveyor belt, the mode, known rubber compounds such as natural rubber and synthetic rubber, vinyl chloride resin, fluororesin, silicone resin. Known resin compounds such as urethane resin can be used. Also,
To improve the heat resistance and flame retardancy of the conveyor belt,
Various additives such as a rubber or resin having heat resistance and flame retardancy, and / or a flame retardancy-imparting agent can be added to the above rubber compound or resin compound.
【００２０】本発明の補強体を備えたコンベアベルトで
あれば、コンベアベルトの形状、構造等は特に限定され
るものではなく、使用目的、態様に応じて、コンベアベ
ルトの形状、構造等を、例えば、帆布コンベアベルト、
パイプコンベアベルト、ヒレ付きコンベアベルト、中寄
棧付きコンベアベルトにすることができ、また、コンベ
アベルトの表面形状を、Ｍ型形状、凹凸布目形状、凹凸
網目形状等にすることができる。The shape and structure of the conveyor belt is not particularly limited as long as it is a conveyor belt provided with the reinforcing member of the present invention, and the shape, structure, etc. of the conveyor belt may be changed according to the purpose and mode of use. For example, a canvas conveyor belt,
It can be a pipe conveyor belt, a fin conveyor belt, or a middle conveyor belt conveyor surface, and the surface shape of the conveyor belt can be an M shape, an uneven cloth shape, an uneven mesh shape, or the like.
【００２１】[0021]
【実施例】次に、実施例、比較例により本発明を更に具
体的にかつ詳細に説明するが、本発明はこれらの実施例
に限定されるものではない。 （実施例１〜４、比較例１〜８）下記表１に、各種の混
撚りコード（本発明の実施例１〜４）、混撚りコードの
上撚りの撚り係数が本発明の範囲外となる場合（比較例
１，２）、ＰＢＯ繊維単独（比較例３）、アラミド繊維
単独（比較例４）、汎用繊維（アラミド繊維＋６６ナイ
ロン繊維）の混撚りコード（比較例５）、スチールワイ
ヤー単独（比較例６）、６６ナイロン繊維単独（比較例
７）、ＰＥＴ繊維単独（比較例８）からなるディップ処
理後のサンプルコードの特性及びこのサンプルコードを
用いたサンプルベルトの疲労性モデルテストについて測
定した結果を示す。撚りコードのディップ処理方法、サ
ンプルベルトの作製、疲労性モデルテスト及びディップ
コードのテスト法は、下記のとおりである。EXAMPLES Next, the present invention will be described more specifically and in detail with reference to Examples and Comparative Examples, but the present invention is not limited to these Examples. (Examples 1 to 4 and Comparative Examples 1 to 8) In Table 1 below, various twisted cords (Examples 1 to 4 of the present invention) and twist factors of the top twist of the mixed twisted cords are out of the range of the present invention. (Comparative Examples 1 and 2), PBO fiber alone (Comparative Example 3), aramid fiber alone (Comparative Example 4), general-purpose fiber (aramid fiber + 66 nylon fiber) mixed twist cord (Comparative Example 5), steel wire alone (Comparative Example 6), 66 nylon fiber alone (Comparative Example 7), PET fiber alone (Comparative Example 8) The characteristics of the sample cord after the dip treatment and the fatigue model test of the sample belt using this sample cord were measured. The result is shown. The twisted cord dip treatment method, sample belt production, fatigue model test, and dip cord test method are as follows.
【００２２】(1) 撚りコードのディップ処理方法、サン
プルベルトの作製 各種混撚りコード及びアラミド（商品名、「ケブラ
ー」）、ＰＢＯ、ＰＥＴの撚りコードは、１浴目にエポ
キシ水溶液に浸漬後、温度２４０℃、時間６０秒、張力
０.５ｇ／Ｄで熱処理し，次いで、２浴目としてＲＦＬ
液（レゾルシン・ホルマリン・ラテックス水溶液）に浸
漬後、１浴目と同様の温度・時間・張力で熱処理したデ
ィップ処理コードをサンプルコードとした。また、６６
ナイロンの撚りコードは、１浴目にＲＦＬ液に浸漬後、
温度２３０℃、時間６０秒、張力０.５ｇ／Ｄで熱処理
したディップ処理コードをサンプルコードとした。上記
のサンプルコードを等間隔に並べてゴム（ＮＲ／ＳＢＲ
ブレンドゴム）中に埋設し，図１の(a)及び(b)に示すよ
うに一層のサンプルベルトＳ1（30cm×1m）、二層のサ
ンプルベルトＳ2（30cm×1m）を作製した。(1) Method for dipping twisted cord, preparation of sample belt Various mixed twisted cords and aramid (trade name, "Kevlar"), PBO, and PET twisted cords are immersed in an epoxy aqueous solution in the first bath, Heat treatment at a temperature of 240 ° C, time of 60 seconds, tension of 0.5 g / D, then RFL for the second bath
After dipping in a liquid (resorcin / formalin / latex aqueous solution), heat treatment was performed at the same temperature, time, and tension as in the first bath, and a dip treatment code was used as a sample code. Also, 66
After twisting the nylon twisted cord in the RFL solution in the first bath,
A sample code was a dip-treated cord which was heat-treated at a temperature of 230 ° C. for 60 seconds and a tension of 0.5 g / D. Rubber (NR / SBR) by arranging the above sample codes at equal intervals
Embedded in a blend rubber), as shown in FIGS. 1A and 1B, a one-layer sample belt S 1 (30 cm × 1 m) and a two-layer sample belt S 2 (30 cm × 1 m) were prepared.
【００２３】(2) 疲労性モデルテスト（屈曲テスト） 図１の(c)に示すベルト屈曲試験機Ｋにより、下記条件
で行った。 プーリー径 ７５φMM 屈曲回数 ２０万回 荷重（Ｗ） １．５ｇ／Ｄ（１デニール当り１．５ｇの
荷重） 上記条件の屈曲テスト後、強力保持率で評価した。(2) Fatigue Model Test (Bending Test) A belt bending tester K shown in FIG. 1C was used under the following conditions. Pulley diameter 75φ MM Number of times of bending 200,000 times Load (W) 1.5 g / D (load of 1.5 g per 1 denier) After the bending test under the above conditions, the strength retention was evaluated.
【００２４】(3) ディップコードのテスト法 引張強さ、伸び率、撚り数は、JIS L 1017により測定し
た。(3) Dip cord test method Tensile strength, elongation and twist number were measured according to JIS L 1017.
【００２５】[0025]
【表１】 [Table 1]
【００２６】表１の結果から明らかなように、本発明の
実施例１〜４は、特に、比較例４のアラミド繊維単独に
較べ二層構造のベルトにしてもベルトの疲労性は大幅に
改善されることが判明し、強度、強力、伸度も良好であ
ることが判明した。これに対して、比較例１，２は、混
撚りコードの上撚りの撚り係数が本発明の範囲外となる
場合は、ＰＢＯだけが切れ、６６Ｎ，ＰＥＴが残り複合
化ができなかった。比較例３のＰＢＯ繊維単独では、二
層構造のベルトにした場合、比較例４と同様であった。
比較例５の汎用繊維（アラミド繊維＋６６ナイロン繊
維）の混撚りコード、比較例７の６６ナイロン繊維単独
及び比較例８のＰＥＴ繊維単独では、実施例１〜４に較
べ強度、強力は低く、また、伸度は大きいものであっ
た。As is clear from the results shown in Table 1, in Examples 1 to 4 of the present invention, compared with the aramid fiber of Comparative Example 4 alone, even if the belt has a two-layer structure, the fatigue property of the belt is significantly improved. It was found that the strength, strength, and elongation were also good. On the other hand, in Comparative Examples 1 and 2, when the twisting coefficient of the twist of the mixed twisted cord was out of the range of the present invention, only PBO was cut off and 66N, PET remained, and composite formation was not possible. The PBO fiber of Comparative Example 3 alone was similar to that of Comparative Example 4 when a belt having a two-layer structure was formed.
The mixed twisted cord of the general-purpose fiber (aramid fiber + 66 nylon fiber) of Comparative Example 5, the 66 nylon fiber alone of Comparative Example 7 and the PET fiber alone of Comparative Example 8 had lower strength and strength than Examples 1 to 4, and The elongation was large.
【００２７】[0027]
【発明の効果】本発明のコンベアベルトは、ポリパラフ
ェニレンベンゾビスオキサゾール（ＰＢＯ）繊維、ポリ
パラフェニレンベンゾビスチアゾール（ＰＢＴ）繊維等
のヘテロ環含有芳香族ポリマーからなる繊維をナイロ
ン、ポリエステル等の汎用繊維と組み合わせてなる混撚
りコードからなる補強体を備えているので、ＰＢＯ等の
屈曲疲労性が大幅に改善されるため、補強体に負荷され
る屈曲条件が一層構造よりはるかに厳しくなる二層構造
にしてもコンベアベルトの疲労性は問題とならないた
め、アラミド繊維の約２倍の５０００〜５５００Ｋｇ／
ｃｍのコンベアベルトを作製することができる。また、
補強体に用いる混撚りされるＰＢＯ繊維、ＰＢＴ繊維等
のヘテロ環含有芳香族ポリマーからなる繊維は、従来の
炭素繊維、アラミド繊維などの有機繊維よりも、さら
に、高強度、低伸度、耐熱性、難燃性に優れた繊維であ
るので、ベルトの軽量化及びその結果による消費電力の
低減化を図ることができ、また、ベルト機械本体の単純
化を図ることができ、更に、ベルトの耐熱性の向上及び
難燃性の向上を図ることができる。INDUSTRIAL APPLICABILITY The conveyor belt of the present invention comprises fibers made of a heterocyclic ring-containing aromatic polymer such as polyparaphenylene benzobisoxazole (PBO) fibers and polyparaphenylene benzobisthiazole (PBT) fibers such as nylon and polyester. Since the reinforcing body made of the mixed twisted cord combined with the general-purpose fiber is provided, the bending fatigue property of PBO or the like is significantly improved, so that the bending condition applied to the reinforcing body becomes much more severe than the structure. Even if it has a layered structure, the fatigue property of the conveyor belt does not become a problem, so it is about twice that of aramid fiber, that is, 5000 to 5500 kg /
cm conveyor belts can be made. Also,
Fibers made of heterocyclic ring-containing aromatic polymers such as PBO fibers and PBT fibers to be mixed and twisted used for the reinforcing body have higher strength, lower elongation and heat resistance than conventional carbon fibers and organic fibers such as aramid fibers. Since it is a fiber with excellent heat resistance and flame retardancy, it is possible to reduce the weight of the belt and the resulting reduction in power consumption, and to simplify the belt machine body. It is possible to improve heat resistance and flame retardancy.
【図１】(a)及び(b)は、サンプルベルトを示す断面図、
(c)は、ベルト屈曲試験機を示す断面図である。1A and 1B are cross-sectional views showing a sample belt,
(c) is a sectional view showing a belt bending tester.
Ｓ1 サンプルベルト（一層構造） Ｓ2 サンプルベルト（二層構造） Ｋ ベルト屈曲試験機S 1 sample belt ( single layer structure) S 2 sample belt (double layer structure) K Belt bending tester
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 // Ｂ２９Ｄ 29/00 2126−4Ｆ Ｃ０８Ｊ 5/04 7310−4Ｆ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Office reference number FI technical display location // B29D 29/00 2126-4F C08J 5/04 7310-4F
Claims (4)
維と、他の材料からなる繊維との混撚りコードから構成
される補強体を備えてなるコンベアベルト。1. A conveyor belt comprising a reinforcing member composed of a mixed twist cord of a fiber made of a heterocycle-containing aromatic polymer and a fiber made of another material.
維と、他の材料からなる繊維とのデニール比が１：４〜
４：１である請求項１記載のコンベアベルト。2. A denier ratio of fibers made of a heterocyclic ring-containing aromatic polymer to fibers made of another material is 1: 4 to.
4. The conveyor belt according to claim 1, which is 4: 1.
維がポリパラフェニレンベンゾビスオキサゾール繊維又
はポリパラフェニレンベンゾビスチアゾール繊維である
請求項１又は２記載のコンベアベルト。3. The conveyor belt according to claim 1, wherein the fiber made of a heterocycle-containing aromatic polymer is a polyparaphenylenebenzobisoxazole fiber or a polyparaphenylenebenzobisthiazole fiber.
記式（Ｉ）で表される上撚りの撚り係数Ｋが、少なくと
も１１００以上である請求項１〜３の何れか一つに記載
のコンベアベルト。 Ｋ＝Ｔ×（Ｄｅ）1/2 ………（Ｉ） 〔なお、Ｔは、Ｔ（回／１０cm）＝上撚り数であり、Ｄ
ｅは、上撚りコードのデニール数である。〕4. The mixed twisted cord has a ply twisted structure, and the twist coefficient K of the upper twist represented by the following formula (I) is at least 1100 or more. Conveyor belt. K = T × (De) 1/2 (I) [where T is T (turns / 10 cm) = number of twists, D
e is the denier number of the twisted cord. ]