JPH07100524A - Extrusion method - Google Patents
Extrusion methodInfo
- Publication number
- JPH07100524A JPH07100524A JP24415793A JP24415793A JPH07100524A JP H07100524 A JPH07100524 A JP H07100524A JP 24415793 A JP24415793 A JP 24415793A JP 24415793 A JP24415793 A JP 24415793A JP H07100524 A JPH07100524 A JP H07100524A
- Authority
- JP
- Japan
- Prior art keywords
- billet
- die
- container
- extrusion
- extruded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【構成】 ビレット用の長尺なアルミニウム原材からビ
レットを所定長さ単位に切断していくことによって生じ
る余剰ビレットＢn を、内部に空間部１ａを有する未使
用ダイス１を用いたビレット１本目Ｂ1 の押出におい
て、同ダイス内の空間部１ａの充填に用いる。
【効果】 未使用ダイス１を用いた１本目のビレットＢ
1 の押出による押出材の長さが、ダイス内空間部１ａの
充填のために短くなってしまうのが防がれ、製造歩留ま
りよく押出品を製造することができ、しかも、余剰ビレ
ットＢn をダイス内空間部１ａの充填に有効に利用する
ことができる。
(57) [Summary] [Structure] The surplus billet B n generated by cutting the billet from a long aluminum raw material for billet into predetermined length units is an unused die 1 having a space portion 1a inside. It is used to fill the space 1a in the die in the extrusion of the first billet B 1 using. [Effect] The first billet B using the unused die 1.
It is possible to prevent the length of the extruded material due to the extrusion of 1 from being shortened due to the filling of the space 1a in the die, and it is possible to manufacture the extruded product with a good manufacturing yield, and to eliminate the surplus billet B n . It can be effectively used for filling the space 1a in the die.
Description
【０００１】[0001]
【産業上の利用分野】この発明は、アルミニウム等の金
属の押出加工方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for extruding a metal such as aluminum.
【０００２】[0002]
【従来の技術】例えばアルミニウムの押出加工は、コン
テナにアルミニウムビレットを装填し、ステムを前進さ
せてこのビレット金属をダイスの成形隙間に通してい
き、一定量のディスカード部を残した状態でステムの前
進を停止し、コンテナとステムとを後退させ、ダイスの
後端部に突出する上記ディスカード部をダイス後端面位
置においてシャーにて切除すると共に、押出された押出
材をプラテンカッターにて切断する。そして、次のビレ
ットをコンテナに装填し、同じようにステムを前進させ
てダイス内金属と押継ぎ状態に押出を繰返すというよう
にして行われる。2. Description of the Related Art For extruding aluminum, for example, an aluminum billet is loaded into a container, the stem is moved forward and the billet metal is passed through a molding gap of a die, and a stem with a certain amount of discard part left. Stop the advance of the container, retract the container and stem, cut off the above-mentioned discard portion protruding to the rear end of the die with a shear at the rear end face position of the die, and cut the extruded extruded material with a platen cutter. To do. Then, the next billet is loaded into the container, the stem is advanced in the same manner, and the extrusion is repeated in a state of being pushed together with the metal in the die.
【０００３】そして、押出品の製造、例えば押出品の小
ロット生産などにおいては、押出品の製造歩留まりを高
いものにすべく、１つの押出品に使用するアルミニウム
の量、１本の押出材から切り出す押出品の数、切除すべ
きディスカード部の量などを考慮することによって、ビ
レット１本当たりのアルミニウム量を算出し、このアル
ミニウム量に相当する長さのビレットを、ビレット用の
長尺なアルミニウム原材から切り出していき、このよう
に切り出されたビレットをコンテナに装填して押出を繰
返し、各押出材から押出品を切り出していくというよう
にして、押出品の製造が行われる。In the production of extruded products, for example, small-lot production of extruded products, the amount of aluminum used in one extruded product and one extruded material are increased in order to increase the production yield of the extruded product. The amount of aluminum per billet is calculated by taking into consideration the number of extruded products to be cut out, the amount of discard part to be cut, and the like. Extruded products are manufactured by cutting out aluminum raw materials, loading the billet thus cut into a container, repeating extrusion, and cutting out extruded products from each extruded material.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、押出品
の製造において、ダイスとして、ポートホールダイスや
プレート付き平ダイス等のように、内部にビレット金属
の充填される空間部を有するダイスを用いた場合、１本
目のビレットの押出において、このビレット金属のうち
の一部がダイス内の空間部の充填に用いられることとな
り、そのため、この１本目のビレットから得られる押出
材の全長長さが、ダイス内充填量分に相当する長さだけ
短いものになってしまい、１本目の押出材から得られる
押出品の数が減少されると共に、１本目の押出材から製
品長さに満たない余剰品を生じて押出品の製造歩留まり
を悪くしてしまうという問題を生じることがある。ま
た、このように１本目の押出材の長さが２本目以降の押
出材の長さよりも短いものになると、押出材のストレッ
チング作業の作業性が悪くなるという問題も生じる。However, in the production of extruded products, when a die having a space filled with billet metal such as a porthole die or a flat die with a plate is used as a die. In extruding the first billet, a part of the billet metal is used for filling the space in the die, and therefore, the total length of the extruded material obtained from the first billet is The length is reduced by a length corresponding to the internal filling amount, the number of extruded products obtained from the first extruded material is reduced, and the surplus product that is less than the product length is extruded from the first extruded material. This may cause a problem that the production yield of the extruded product is deteriorated. Further, when the length of the first extruded material is shorter than the length of the second extruded material and thereafter, the workability of the stretching operation of the extruded material deteriorates.
【０００５】一方、長尺アルミニウム原材から上記のよ
うに所定長さ単位にビレットを切り出していく場合、最
終的に、必要なビレット長さに満たない余剰ビレットを
生じ、この余剰ビレットは押出品長さとの関係で使える
ものは使うこともあるが、多くの場合廃棄しており、余
剰ビレットを無駄にしている場合が多いという問題もあ
った。On the other hand, when a billet is cut out from a long aluminum raw material in a unit of a predetermined length as described above, a surplus billet less than the required billet length is finally produced, and this surplus billet is an extruded product. There is also a problem in that in many cases, what can be used in relation to the length is used, but in many cases, it is discarded and the surplus billet is wasted.
【０００６】この発明は、上記のような従来の問題点に
鑑み、ビレット金属充填空間部を有する未使用ダイスを
用いた１本目のビレットの押出により得られる押出材の
長さが上記ダイス内空間部の充填のために短くなってし
まうことがないようにして１本目の押出材から製造歩留
まり良く押出品を得ることができ、同時に、余剰ビレッ
トの有効利用も図ることができる押出加工方法を提供す
ることを目的とする。In view of the above-mentioned conventional problems, the present invention is such that the length of the extruded material obtained by extruding the first billet using an unused die having a billet metal-filled space portion has a length within the die space. Provided is an extrusion processing method capable of obtaining an extruded product from a first extruded material with a good production yield without being shortened due to filling of a portion, and at the same time, capable of effectively utilizing an excess billet. The purpose is to do.
【０００７】[0007]
【課題を解決するための手段】上記目的において、この
発明は、ビレット用の長尺な金属原材からのビレットの
切出しによって生じる余剰ビレットを、内部にビレット
金属充填空間部を有する未使用ダイスを用いたビレット
１本目の押出において、同ダイス内空間部の充填に用い
ることを特徴とする押出加工方法を要旨とする。In order to achieve the above object, the present invention provides an extra billet produced by cutting out a billet from a long metal raw material for billet, and an unused die having a billet metal filling space inside. In the extrusion of the first billet used, the gist is an extrusion processing method characterized by being used for filling the space inside the die.
【０００８】なお、本発明方法を実施するに当たって
は、ダイス内空間部の容量に相当するビレット孔を有す
るミニコンテナを用い、先行押出における最終の余剰ビ
レットを用いた押出に際して、このミニコンテナをダイ
スとコンテナとの間に配置し、この余剰ビレットをコン
テナに装填し、押出を行い、この余剰ビレットの後端面
がミニコンテナよりも所定距離後方に位置したところで
押出を停止し、補助コンテナとダイスとの間でビレット
金属を切断すると共に、ミニコンテナから後方に突出す
るディスカード部を切除し、しかるのち、新たなダイス
をセットすると共に、コンテナに１本目のビレットを装
填し、該ビレットをミニコンテナ内のビレット金属とと
もに押出すようにするのが好ましい。In carrying out the method of the present invention, a mini-container having a billet hole corresponding to the capacity of the space inside the die is used, and this mini-container is diced at the time of extrusion using the final surplus billet in the preceding extrusion. It is placed between the container and the container, the surplus billet is loaded into the container and extruded, and when the rear end surface of this surplus billet is located a predetermined distance behind the mini-container, the extrusion is stopped, and the auxiliary container and die are While cutting the billet metal between them, cut out the discard part protruding rearward from the mini container, and then setting a new die, loading the first billet into the container, and loading the billet into the mini container. It is preferred to extrude with the billet metal inside.
【０００９】[0009]
【作用】上記方法では、未使用ダイスを用いたビレット
１本目の押出において、通常のビレットの外、ダイス内
充填用のビレットをも用いて押出を行うものとしている
ことにより、この充填用ビレットの金属分でダイス内空
間部が充填される。従って、１本目のビレットの押出に
て得られる押出材の長さが、このダイス内空間部の充填
により短くなるということがなくなり、１本目の押出材
から押出品が余剰品少なく製造歩留まり良く得られる。In the above method, in the extrusion of the first billet using an unused die, not only the ordinary billet but also the billet for filling the inside of the die is used to extrude the billet. The space inside the die is filled with metal. Therefore, the length of the extruded material obtained by extruding the first billet is not shortened due to the filling of the space in the die, and the extruded material from the first extruded material is small and the production yield is good. To be
【００１０】しかも、上記充填用ビレットとして、ビレ
ット用の長尺な金属原材からのビレットの切出しによっ
て生じる余剰ビレットを使用することとしていることに
より、この余剰ビレットが無駄に廃棄等されることなく
上記１本目の押出材の長さ確保のために有効に利用され
る。Moreover, since the surplus billet generated by cutting out the billet from the long metal raw material for the billet is used as the filling billet, the surplus billet is not wastefully discarded. It is effectively used to secure the length of the first extruded material.
【００１１】[0011]
【実施例】次に、本発明方法の実施例について説明す
る。EXAMPLES Next, examples of the method of the present invention will be described.
【００１２】本押出加工方法に使用する押出加工装置を
示す図１において、（１）はダイス、（４）はコンテ
ナ、（５）はステム、（６）はダミー、（７）はミニコ
ンテナである。In FIG. 1 showing an extrusion processing apparatus used in the present extrusion processing method, (1) is a die, (4) is a container, (5) is a stem, (6) is a dummy, and (7) is a mini container. is there.
【００１３】ダイス（１）は、雄型（２）と雌型（３）
とからなるポートホールダイスで、雄型（２）のポート
孔（2a）と、雌型（３）の溶着室（3a）とにより、内部
にビレット金属充填空間部（1a）を有する。The die (1) comprises a male die (2) and a female die (3).
The port hole die comprises a male mold (2) port hole (2a) and a female mold (3) welding chamber (3a) having a billet metal filling space (1a) inside.
【００１４】ミニコンテナ（７）は、そのビレット孔
（7a）が、ダイス（１）のビレット金属充填空間部（1
a）の容積に相当する容積を有するものに形成されてい
る。そして、このミニコンテナ（７）は、側方に移動可
能に備えられており、必要に応じてダイス（１）とコン
テナ（４）との間に介在配置することができると共に、
また、その位置から側方に除けることができるようにさ
れている。また、このミニコンテナ（７）は、ダイス
（１）とコンテナ（４）とに介在配置された状態で、前
後方向に変位動しうるようになされている。The mini-container (7) has a billet hole (7a) whose billet metal filling space (1) of the die (1).
It is formed to have a volume corresponding to that of a). The mini-container (7) is provided so as to be movable laterally, and can be arranged between the die (1) and the container (4) if necessary, and
In addition, it can be removed laterally from that position. The mini-container (7) can be displaced in the front-rear direction while being interposed between the die (1) and the container (4).
【００１５】なお、（８）はシャーで、ダイス（１）の
後部に突出されるディスカード部を切除するものであ
る。また、（11）もシャーで、これは、後述するよう
に、ミニコンテナ（７）の後部に突出されるディスカー
ド部を切除するものである。（９）は切断機で、これも
後述するように、ダイス（１）とミニコンテナ（７）と
の間でビレット金属を切断するものである。Reference numeral (8) is a shear for cutting off the discard portion protruding to the rear portion of the die (1). Further, (11) is also a shear, which cuts out a discard part protruding to the rear part of the mini-container (7), as described later. A cutting machine (9) cuts billet metal between the die (1) and the mini-container (7) as will be described later.
【００１６】押出に使用するビレットは、長尺なアルミ
ニウム原材を所定長さ単位に切断していくことによって
得られる。このビレットの長さは、１つのビレットから
製造歩留まり良く押出品が得られるように、１つの押出
品に使用されるアルミニウムの量、一本の押出材から切
り出す押出品の数、押出において切除すべきディスカー
ド部の量等を考慮して、計算によって求められたもので
ある。アルミニウム原材からのこのようなビレットの切
出しによって、余剰のビレットを生じる。The billet used for extrusion can be obtained by cutting a long aluminum raw material into predetermined length units. The length of this billet is cut so that the amount of aluminum used in one extruded product, the number of extruded products cut out from one extruded product, and the number of extruded products cut out from one extruded product, so that the extruded product can be obtained from one billet with good production yield It is obtained by calculation in consideration of the amount of discard section that should be used. Excision of such billets from aluminum stock results in excess billets.
【００１７】実施例にかかる押出加工法は、上記押出加
工装置とビレットを用いて、次のように実施される。The extrusion processing method according to the embodiment is carried out as follows using the above-mentioned extrusion processing apparatus and billet.
【００１８】この方法を、先行押出における最終から一
つ前の押出段階から説明すると、図２（イ）に示される
ように、先行ダイス（１´）を用いた先行押出におい
て、最終ビレットから一つ前のビレット（Ｂn-1 ）を
コンテナ（４）のビレット孔（4a）に装填する。この場
合、ミニコンテナ（７）は側方に除けられている。そし
て、図２（ロ）に示されるように、ステム（５）を前進
させて押出を行い、ディスカード部（Ｄ）を残して押出
を終了後、図２（ハ）に示されるように、コンテナ
（４）とステム（５）を後退させ、シャー（８）にてデ
ィスカード部（Ｄ）を切除する。また、プラテンカッタ
ー（10）にて押出材（ｅn-1 ）を切り離す。This method will be described from the extrusion step immediately before the last in the preceding extrusion. As shown in FIG. 2 (a), in the preceding extrusion using the preceding die (1 '), the first billet is removed. The preceding billet (B n-1 ) is loaded into the billet hole (4a) of the container (4). In this case, the mini-container (7) is removed laterally. Then, as shown in FIG. 2 (B), the stem (5) is advanced to perform extrusion, and after the extrusion is completed while leaving the discard portion (D), as shown in FIG. The container (4) and stem (5) are retracted, and the discard part (D) is cut off by the shear (8). Further, the extruded material (en -1 ) is cut off by the platen cutter (10).
【００１９】そして、図２（ニ）に示されるように、最
終ビレットである余剰ビレット（Ｂn ）を用いた先行の
最終押出において、ダイス（１´）とコンテナ（４）と
の間にミニコンテナ（７）を介在配置し、このミニコン
テナ（７）とコンテナ（４）のビレット孔（7a）（4a）
に上記余剰ビレット（Ｂn ）を装填し、ステム（５）を
前進させて押出を行う。そして、図３（ホ）に示される
ように、余剰ビレット（Ｂn ）の後端面位置が、ミニコ
ンテナ（７）よりも所定距離後方の位置に位置するまで
押出を進めた時点で、ステム（５）の前進を止める。そ
して、図３（ヘ）に示されるように、コンテナ（４）、
ミニコンテナ（７）、ステム（５）を同調して後退さ
せ、ビレット金属（Ｂn ）をミニコンテナ（７）の前端
面位置において切断機（９）にて切断すると共に、図３
（ト）に示されるように、コンテナ（４）をミニコンテ
ナ（７）から後退させ、ミニコンテナ（７）の後方に突
出するディスカード部（Ｄ）をシャー（11）にて切除す
る。これにより、ミニコンテナ（４）のビレット孔（4
a）に、次の押出に用いられるダイス（１）のビレット
金属充填空間部（1a）の容積に相当する量のビレット
（Ｂn ）が装填状態にされる。なお、図３（ヘ）に示さ
れるように、最終ビレット（Ｂn ）にて押出された押出
材（ｅn ）はプラテンカッター（10）にて切り離してお
く。Then, as shown in FIG. 2D, in the preceding final extrusion using the surplus billet (B n ) which is the final billet, the mini-between the die (1 ') and the container (4). The container (7) is arranged in between, and the billet holes (7a) (4a) of this mini container (7) and container (4)
The surplus billet (B n ) is loaded into the above, and the stem (5) is advanced to perform extrusion. Then, as shown in FIG. 3 (e), when the extrusion is advanced until the position of the rear end face of the surplus billet (B n ) is located a predetermined distance behind the mini-container (7), the stem ( Stop the advance of 5). Then, as shown in FIG. 3 (f), the container (4),
The mini-container (7) and the stem (5) are retracted in synchronization with each other, and the billet metal (B n ) is cut by the cutting machine (9) at the front end face position of the mini-container (7), and as shown in FIG.
As shown in (g), the container (4) is retracted from the mini-container (7), and the discard part (D) protruding rearward of the mini-container (7) is cut off by the shear (11). As a result, the billet holes (4
In a), a billet ( Bn ) of an amount corresponding to the volume of the billet metal-filled space (1a) of the die (1) used for the next extrusion is loaded. Incidentally, as shown in FIG. 3 (f), the final billet extruded extrudate at (B n) (e n) is kept disconnected with the platen cutter (10).
【００２０】しかるのち、図３（チ）に示されるよう
に、先行押出において使用したダイス（１´）を取り外
して、未使用の次のポートホールダイス（１）をセッテ
ィングし、コンテナ（４）に１本目のビレット（Ｂ1 ）
を装填して押出を行う。この押出において、ミニコンテ
ナ（７）内の余剰ビレット（Ｂn ）の容積に相当する量
のアルミニウム金属にてポートホールダイス（１）のビ
レット金属充填空間部（1a）が充填され、この結果、１
本目のビレット（Ｂ1 ）の押出によって、ディスカード
部として除去される分を除く一本目のビレット（Ｂ1 ）
の量に相当する所望長さの押出材（ｅ1 ）が得られる。After that, as shown in FIG. 3 (h), the die (1 ') used in the preceding extrusion is removed, the unused next port hole die (1) is set, and the container (4) is set. First billet (B 1 )
Is charged and extrusion is performed. In this extrusion, the billet metal filling space (1a) of the porthole die (1) is filled with an amount of aluminum metal corresponding to the volume of the surplus billet ( Bn ) in the mini container (7), and as a result, 1
The first billet (B 1 ) excluding the part removed as the discard part by extruding the first billet (B 1 )
A desired length of extruded material (e 1 ) corresponding to the amount of
【００２１】なお、１本目のビレット（Ｂ1 ）の押出
は、図４（リ）に示されるように、ディスカード部
（Ｄ）を残して終了し、図４（ヌ）に示されるように、
ミニコンテナ（７）、コンテナ（４）、ステム（５）を
後退させて、ディスカード部（Ｄ）をシャー（８）にて
切除する。そして、図４（ル）に示されるように、ミニ
コンテナ（７）を、ダイス（１）とコンテナ（４）との
間から側方に除け、図４（ヲ）に示されるように、ミニ
コンテナ（７）なしで、通常どおりコンテナ（４）に２
本目のビレット（Ｂ2 ）を装填して、上記先行押出の場
合と同様に押出を繰返していく。Extrusion of the first billet (B 1 ) is completed with the discard portion (D) left as shown in FIG. 4 (i), and as shown in FIG. 4 (n). ,
The mini-container (7), the container (4) and the stem (5) are retracted, and the discard part (D) is cut off by the shear (8). Then, as shown in FIG. 4 (l), the mini container (7) is removed laterally from between the die (1) and the container (4), and as shown in FIG. 2 in container (4) as usual, without container (7)
A second billet (B 2 ) is loaded and the extrusion is repeated in the same manner as in the preceding extrusion.
【００２２】以上の説明のように、上記の押出加工方法
は、１本目のビレット（Ｂ1 ）の押出において、先行押
出における最終のビレット（Ｂn ）、即ち余剰のビレッ
トを用い、これを新たなポートホールダイス（１）のビ
レット充填空間部（1a）の充填分に当てて、押出を行う
ものとしているから、１本目の押出材（ｅ1 ）の長さ
が、ダイス（１）内の空間部（1a）のアルミニウム充填
のために、短くなってしまうということがなく、１本目
の押出材から製造歩留まり良く押出品を切り出していく
ことができ、押出品を製造歩留まりよく製造することが
でき、同時に、このようにして余剰ビレット（Ｂn ）の
有効利用を図ることができる。As described above, in the extrusion method described above, when the first billet (B 1 ) is extruded, the final billet (B n ) in the preceding extrusion, that is, the surplus billet, is used. Since the extruding is performed by hitting the filled portion of the billet filling space (1a) of the port hole die (1), the length of the first extruded material (e 1 ) is within the die (1). Since the space (1a) is filled with aluminum, it does not become short, and the extruded product can be cut out from the first extruded material with good production yield, and the extruded product can be produced with good production yield. At the same time, the surplus billet (B n ) can be effectively used in this way.
【００２３】しかも、このように１本目のビレットの押
出によって得られた押出材が、短くなることなく、２本
目以降の押出材の長さと合うようになることで、押出後
のストレッチング作業の作業性向上を図ることもでき
る。In addition, the extruded material obtained by extruding the first billet in this way matches the length of the extruded material of the second and subsequent ones without shortening, so that the stretching work after extrusion can be performed. Workability can also be improved.
【００２４】また、上記実施例方法では、ポートホール
ダイス（１）の内部空間部（1a）の容積に相当する容積
のビレット孔（7a）を有するミニコンテナ（７）を用
い、先行押出における最終余剰ビレット（Ｂn ）による
押出において、このミニコンテナ（７）をダイス（１）
とコンテナ（４）との間に配置し、このビレット
（Ｂn）をミニコンテナ（７）の所定距離後方の位置ま
で押出に用い、ミニコンテナ（７）の前端面位置におい
て切断機（９）にてこのビレット（Ｂn ）を切断すると
共に、このビレット（Ｂn ）のディスカード部（Ｄ）を
ミニコンテナ（７）の後端面位置においてシャー（11）
にて切除することによって、ミニコンテナ（７）のビレ
ット孔（7a）に必要な量の余剰ビレット金属（Ｂn ）を
充填状態となし、そして、次の新たなポートホールダイ
ス（１）をセッティングすると共に、コンテナ（７）に
は１本目のビレット（Ｂ1 ）を装填して、補助コナテナ
（７）内のビレット（Ｂn ）とともに１本目のビレット
（Ｂ1 ）の押出を行うようにしている。Further, in the method of the above-mentioned embodiment, the mini-container (7) having the billet hole (7a) having a volume corresponding to the volume of the internal space (1a) of the porthole die (1) is used, and the final container in the preceding extrusion is used. In extrusion by the surplus billet (B n ), this mini container (7) is used for the die (1)
And the container (4), and this billet (B n ) is used for extrusion up to a position behind the mini container (7) by a predetermined distance, and the cutting machine (9) is placed at the front end face position of the mini container (7). The billet (B n ) is cut by the shearing part (D) of the billet (B n ) at the rear end face position of the mini container (7) at the shear (11).
The billet hole (7a) of the mini-container (7) is filled with the required amount of excess billet metal (B n ) by cutting it off, and the next new porthole die (1) is set. while, in the container (7) is loaded first run of billet (B 1), so as to perform the extrusion of the first run of the billet (B 1) with the billet in the auxiliary Konatena (7) (B n) There is.
【００２５】このように、先行押出における最終余剰ビ
レット（Ｂn ）について、新たなポートホールダイス
（１）内の空間部（1a）の充填に必要な量の長さ分を残
して、あとは、先行押出における押出材の押出に用いる
ようにしているから、先行押出においてこの余剰ビレッ
ト（Ｂn ）の押出による押出材からも押出品が得られて
押出品を製造歩留まりよく製造することができる。しか
も同時に、ミニコンテナ（７）によってダイス充填用の
ビレット金属の量も必要量に制限されるようになされて
いるから、後行押出におけるビレット（Ｂ1 ）１本目の
押出において得られる押出材が無駄に長くなって余剰品
を多く出してしまうことも防がれ、この１本目の押出材
から歩留まり良く押出品を得ることができる。In this way, with respect to the final surplus billet (B n ) in the preceding extrusion, leaving the length of the amount necessary for filling the space (1a) in the new porthole die (1), Since the extruded material is used for extruding the extruded material in the preceding extrusion, the extruded material can be obtained from the extruded material obtained by extruding the surplus billet ( Bn ) in the preceding extrusion, and the extruded material can be manufactured with a high production yield. . At the same time, the mini-container (7) limits the amount of billet metal for die filling to the required amount, so that the extruded material obtained in the first extrusion of the billet (B1) in the subsequent extrusion is wasted. It is also possible to prevent the excessive production of a large amount of surplus product, and it is possible to obtain an extruded product from this first extruded material with a good yield.
【００２６】加えて、ミニコンテナ（７）の採用におい
てシャー（11）が採用されているから、余剰ビレット
（Ｂn ）の一部を先行押出に使用することによってこの
ビレット（Ｂn ）の後部に集中する不純物をディスカー
ド部（Ｄ）として切除することができ、後行押出におけ
る１本目の押出材を材質的に問題のないものとして押出
加工することができる。In addition, since the shear (11) is adopted in the adoption of the mini-container (7), a part of the surplus billet (B n ) is used for the preceding extrusion, so that the rear part of this billet (B n ) is used. The impurities concentrated in the can be removed as the discard part (D), and the first extruded material in the subsequent extrusion can be extruded as a material having no problem.
【００２７】[0027]
【発明の効果】上述の次第で、この発明の押出加工方法
は、未使用ダイスを用いたビレット１本目の押出におい
て、通常のビレットの外、ダイス内充填用のビレットを
も用いて押出を行うものとしているから、この充填用ビ
レットの金属分でダイス内空間部が充填される。従っ
て、１本目のビレットによる押出にて得られる押出材の
長さが、このダイス内空間部の充填のために短くなって
しまうということがなくなり、１本目の押出材から押出
品を余剰品少なく製造歩留まり良く得ることができ、押
出品の製造歩留まりの向上を図ることができる。As described above, according to the extrusion processing method of the present invention, in the extrusion of the first billet using the unused die, the extrusion is performed using not only the ordinary billet but also the billet for filling the die. Therefore, the space inside the die is filled with the metal component of the filling billet. Therefore, the length of the extruded material obtained by extruding with the first billet does not become short due to the filling of the space in the die, and the surplus extruded material is reduced from the first extruded material. It is possible to obtain a good production yield and improve the production yield of extruded products.
【００２８】しかも、上記充填用ビレットとして、長尺
金属原材からのビレットの切出しによって生じる余剰ビ
レットを使用することとしているから、この余剰ビレッ
トを上記１本目の押出材の長さ確保のために有効に利用
することができて、無駄に廃棄等せずにすむようにな
り、ひいては押出品の製品歩留まりの更なる向上を図る
ことができる。Moreover, since the surplus billet generated by cutting out the billet from the long metal raw material is used as the filling billet, this surplus billet is used to secure the length of the first extruded material. It can be effectively used, and it is possible to avoid wasteful disposal, and further improve the product yield of extruded products.
【図１】本発明方法の実施に用いられる押出加工装置の
断面図である。FIG. 1 is a sectional view of an extrusion processing apparatus used for carrying out the method of the present invention.
【図２】図（イ）ないし図（ニ）はそれぞれ、先行押出
における最終のビレットの一つ前のビレットをコンテナ
に装填してから、その押出を終え、ミニコンテナを用い
て最終余剰ビレットをコンテナに装填するまでの過程を
示す断面図である。FIGS. 2 (a) to 2 (d) respectively show that the billet preceding the final billet in the preceding extrusion is loaded into the container, the extrusion is completed, and the final surplus billet is removed using a mini container. It is sectional drawing which shows the process until it loads in a container.
【図３】図（ホ）ないし図（チ）はそれぞれ、最終余剰
ビレットの押出から、新たなポートホールダイスをセッ
ティングして１本目のビレットの押出を開始するまでの
過程を示す断面図である。3 (e) to 3 (h) are cross-sectional views showing the process from the extrusion of the final surplus billet to the setting of a new porthole die and the extrusion of the first billet. .
【図４】図（リ）ないし図（ヲ）はそれぞれ、新たなダ
イスを用いて１本目のビレットの押出を行い、２本目の
ビレットのコンテナに装填するのでの押出過程を示す断
面図である。4A to 4C are cross-sectional views showing an extrusion process for extruding a first billet using a new die and loading it into a container for a second billet. .
１…ダイス １ａ…空間部 Ｂn …余剰ビレット Ｂ1 …１本目のビレット1 ... die 1a ... space B n ... surplus billet B 1 ... 1 -th billet
Claims (1)
ットの切出しによって生じる余剰ビレットを、内部にビ
レット金属充填空間部を有する未使用ダイスを用いたビ
レット１本目の押出において、同ダイス内空間部の充填
に用いることを特徴とする押出加工方法。1. Extruded billet produced by cutting out a billet from a long metal raw material for billet is extruded in a first billet using an unused die having a billet metal filling space inside. An extrusion method characterized by being used for filling a space.