JPH0720575A - Reflection type screen material for projection - Google Patents
Reflection type screen material for projectionInfo
- Publication number
- JPH0720575A JPH0720575A JP31794593A JP31794593A JPH0720575A JP H0720575 A JPH0720575 A JP H0720575A JP 31794593 A JP31794593 A JP 31794593A JP 31794593 A JP31794593 A JP 31794593A JP H0720575 A JPH0720575 A JP H0720575A
- Authority
- JP
- Japan
- Prior art keywords
- beads
- binder
- bead layer
- sheet
- screen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、映写用反射型スクリー
ン材（スクリーンフィルム）、特に、液晶プロジェクタ
ー等の映写用反射型スクリーン材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a reflective screen material for projection (screen film), and more particularly to a reflective screen material for projection such as a liquid crystal projector.
【０００２】[0002]
【従来の技術および発明が解決しようとする課題】従来
より、紙、布、ガラス繊維などから構成されたシート基
材の表面に、ガラスビーズ等を塗設したシート材が、液
晶プロジェクター等を用いて画像を投影するためのシー
ト材として汎用されていた。 しかしながら、これら従
来のシート材によると、スクリーン輝度が低く、特に、
室内が明るい場合には、スクリーン上の画像がほとんど
見えず、従って、投影操作の他に、室内の明るさをやや
暗くするなどの調光操作を必要とするものであった。2. Description of the Related Art Conventionally, a sheet material having glass beads coated on the surface of a sheet base material made of paper, cloth, glass fiber or the like has been used in a liquid crystal projector or the like. Was widely used as a sheet material for projecting images. However, according to these conventional sheet materials, the screen brightness is low, and in particular,
When the room is bright, the image on the screen is hardly visible, and therefore, in addition to the projection operation, a light control operation such as making the room slightly darker is required.
【０００３】[0003]
【課題を解決するための手段】本発明は、上述した従来
のスクリーン材において指摘されていた問題点に鑑み
て、反射効率を高めることによりスクリーン輝度を改善
して、明るい部屋においても投映画像が鑑賞できるよう
な反射型スクリーン材を提供する目的で発明されたもの
であり、その要旨とするところは、光透過性もしくは光
非透過性の基材シートと、該基材シート上面に塗設され
たバインダーならびにビーズを含むビーズ層から構成さ
れた映写用反射型スクリーン材である。In view of the problems pointed out in the above-mentioned conventional screen materials, the present invention improves the screen brightness by increasing the reflection efficiency so that a projected image can be displayed even in a bright room. The invention was invented for the purpose of providing a reflection-type screen material that can be viewed, and the gist of the invention is that a light-transmitting or light-impermeable base sheet and a coating on the top surface of the base sheet are provided. A reflective screen material for projection comprising a bead layer containing a binder and beads.
【０００４】すなわち、本発明のビーズ層の構成には、
以下の二態様が含まれる。That is, in the constitution of the bead layer of the present invention,
The following two aspects are included.
【０００５】 透明ビーズとバインダーからなるビー
ズ層（図１(a))。A bead layer composed of transparent beads and a binder (FIG. 1 (a)).
【０００６】 着色ビーズとバインダーからなるビー
ズ層（図１(b))。A bead layer composed of colored beads and a binder (FIG. 1 (b)).
【０００７】 透明ビーズ、着色ビーズおよびバイン
ダーからなるビーズ層（図１(c))。A bead layer composed of transparent beads, colored beads and a binder (FIG. 1 (c)).
【０００８】そして、本発明における光透過性基材シー
トとしては、プラスチックフィルム、例えば、ポリエチ
レンテレフタレート(PET) 、ポリカーボネート(PC)等の
透明、乳白色透明のプラスチックフィルム、あるいはガ
ラス繊維からなる布、合成紙等の優れた光透過性を有す
るものが使用され、また光非透過性基材シートとして
は、前述した光透過性基材シートの構成材料に、無機
物、例えば、二酸化チタン(TiO2)を混合して非透過性を
付与したものが使用される。The light-transmitting substrate sheet in the present invention is a plastic film, for example, a transparent, milky-white transparent plastic film such as polyethylene terephthalate (PET) or polycarbonate (PC), or a cloth made of glass fiber, synthetic. A material having excellent light transmissivity such as paper is used, and as the light non-transmissive base material sheet, an inorganic material, for example, titanium dioxide (TiO 2 ) is used as the constituent material of the light transmissive base material sheet described above. Those which are mixed with each other to make them impermeable are used.
【０００９】また、シート厚みは特に限定されるもので
はないが、スクリーン材としての使用形態を考慮すれ
ば、10〜5000μｍ程度が好ましい。Although the sheet thickness is not particularly limited, it is preferably about 10 to 5000 μm in consideration of the usage as a screen material.
【００１０】また、本発明に使用可能なビーズとして
は、プラスチックビーズ（例、アクリル乳白色ビー
ズ）、着色ビーズ（例、白色プラスチックビーズ、白色
ガラスビーズ）等があり、ビーズの粒径は、特に限定さ
れるものではないが、光の反射効率などを考慮すれば、
１〜 100μm 程度のものを、好ましくは、粒度の異なる
ビーズを混在させて用いる。 なお、ビーズに付与すべ
き色としては、反射効率の観点からして白色が好まし
く、この場合の着色材としては、白色無機顔料、例え
ば、酸化チタン、タルク、酸化亜鉛等が使用できるが、
最終調製品の反射効率を考慮すれば、二酸化チタンが特
に好ましい。 なお、透明ビーズと着色ビーズを混合し
て使用する場合（図１(c))、両者の混合比は、光線の反
射効果を考慮すれば、１：99重量％〜99：１重量％の範
囲が好ましい。The beads that can be used in the present invention include plastic beads (eg, acrylic milk white beads), colored beads (eg, white plastic beads, white glass beads), and the particle size of the beads is particularly limited. However, considering the light reflection efficiency,
Those having a size of about 1 to 100 μm are preferably used by mixing beads having different particle sizes. The color to be imparted to the beads is preferably white from the viewpoint of reflection efficiency, and as the coloring material in this case, a white inorganic pigment, for example, titanium oxide, talc, zinc oxide or the like can be used.
Considering the reflection efficiency of the final preparation, titanium dioxide is particularly preferable. When the transparent beads and the colored beads are mixed and used (Fig. 1 (c)), the mixing ratio of the two is in the range of 1: 99% by weight to 99: 1% by weight in consideration of the light reflection effect. Is preferred.
【００１１】さらに、バインダーとしては、合成樹脂
（例えば、アクリルコポリマー樹脂あるいはウレタン樹
脂）が、本発明において使用できる。 なお、ビーズと
バインダーとの配合比は、光反射効果などを考慮して、
バインダー 100重量部に対して、ビーズ５〜95重量部の
範囲が好ましい。Further, as the binder, synthetic resin (for example, acrylic copolymer resin or urethane resin) can be used in the present invention. In addition, the blending ratio of the beads and the binder, considering the light reflection effect and the like,
The range of 5 to 95 parts by weight of beads is preferable with respect to 100 parts by weight of the binder.
【００１２】なお、本発明のスクリーン材を構成する、
基材シート、バインダーおよびビーズに、難燃化性能を
付与する目的で、難燃剤、例えば、トリフェニルホスフ
ェート、ポリクレジルホスフェートなどをさらに配合す
ることも可能である。The screen material of the present invention is constituted,
A flame retardant such as triphenyl phosphate or polycresyl phosphate may be further added to the base sheet, binder and beads for the purpose of imparting flame retardancy.
【００１３】また、本発明のビーズ層の厚みは特に限定
されるものではないが、周知のロールコート方式による
基材シートへの塗設の難易性、強度および光線の遮蔽効
果などを考慮して、10〜 500μm 程度が好ましい。 さ
らに、ビーズ層内におけるビーズの配置態様としては、
光拡散効果などを考慮すれば、バインダーに埋設された
ビーズとバインダーに部分的に埋設されたビーズを混在
させて用いること、ならびに、ビーズを基材シート表面
に分散あるいは基材シート表面をほぼ被うように分布さ
せる態様が好ましい。The thickness of the bead layer of the present invention is not particularly limited, but in consideration of the difficulty of applying it to the base sheet by the well-known roll coating method, the strength, the light shielding effect and the like. , 10 to 500 μm is preferable. Furthermore, as the arrangement mode of the beads in the bead layer,
Considering the light diffusion effect, etc., the beads embedded in the binder and the beads partially embedded in the binder are used in a mixed manner, and the beads are dispersed on the surface of the base sheet or the surface of the base sheet is almost covered. The preferred embodiment is such a distribution.
【００１４】さらに、本発明のスクリーン材の反射効率
を補足する目的で、基材シートの他方の面、すなわち、
ビーズ層から基材シートを介して、反射層を形成するこ
とができる。 この反射層としては、光の反射効率を向
上させる物質であれば、基本的には適用可能であり、例
えば、アルミニウム、銀などの金属を蒸着させて反射層
を形成する方法、あるいはこの金属蒸着反射層にさらに
着色ビーズを配合してその反射効率を高めることなどが
できる。Further, for the purpose of supplementing the reflection efficiency of the screen material of the present invention, the other surface of the base sheet, that is,
The reflective layer can be formed from the bead layer via the substrate sheet. The reflective layer is basically applicable as long as it is a substance that improves the light reflection efficiency. For example, a method of depositing a metal such as aluminum or silver to form the reflective layer, or this metal deposition Colored beads may be further added to the reflective layer to improve the reflection efficiency.
【００１５】また、本発明により得られたスクリーン材
の使用態様としては、周知の態様、例えば、ローラース
クリーン（図３(a))またはパネルスタンド型スクリーン
（図３(b))などのスクリーン形態に適用できる。The screen material obtained by the present invention may be used in a well-known manner, for example, a screen form such as a roller screen (FIG. 3 (a)) or a panel stand type screen (FIG. 3 (b)). Applicable to
【００１６】[0016]
【実施例】以下、本発明のスクリーン用シート材の実施
例につき説明する。EXAMPLES Examples of the screen sheet material of the present invention will be described below.
【００１７】図１の各態様を参照すると、光透過性の基
材シートを用いた場合、本発明の構成によれば、投影機
から放たれた光線７は、スクリーン用シート材１の基材
シート２を透過して、ビーズ層３のバインダー６中に分
散された着色ビーズ４および／または透明ビーズ５との
接触・屈折・反射を幾度となく繰り返した末に、ビーズ
層３を通過する。 また、光非透過性の基材シートを用
いた場合には、前記したビーズ層での接触・屈折・反射
作用に加えて、基材シートによる反射作用がさらに付加
されるのである。 これらいずれの態様においても、ビ
ーズ層３から反射してきた光は均質に拡散し、比較的明
るい室内においても鑑賞するに足りる輝度で、映写画像
をスクリーン上に提供するのである。With reference to each embodiment of FIG. 1, when a light-transmissive base sheet is used, according to the constitution of the present invention, the light beam 7 emitted from the projector is the base material of the screen sheet material 1. After passing through the sheet 2 and repeatedly contacting, refracting and reflecting the colored beads 4 and / or the transparent beads 5 dispersed in the binder 6 of the bead layer 3, the beads layer 3 is passed. When a light-impermeable base sheet is used, in addition to the contact, refraction, and reflection actions of the bead layer described above, the reflection action of the base sheet is further added. In any of these modes, the light reflected from the bead layer 3 is uniformly diffused and provides a projected image on the screen with a brightness sufficient for viewing even in a relatively bright room.
【００１８】また、図１(c) に示したように、着色ビー
ズ４と透明ビーズ５を併用することにより、光の拡散の
程度を加減することができ、さらに、使用する着色ビー
ズ４と透明ビーズ５の混合比ならびに粒径を調整するこ
とで、スクリーン輝度の加減も可能となるのである。Further, as shown in FIG. 1 (c), by using the colored beads 4 and the transparent beads 5 together, the degree of light diffusion can be adjusted, and the colored beads 4 to be used and the transparent beads 5 are transparent. By adjusting the mixing ratio and the particle size of the beads 5, the screen brightness can be adjusted.
【００１９】以下、実施例１〜６に、本願発明の映写用
反射型スクリーン材の調製方法について説明する。Hereinafter, Examples 1 to 6 will be used to explain the method for preparing the reflective screen material for projection of the present invention.
【００２０】実施例１ 厚さ 100μm のポリエチレンテレフタレートシート
（「PET 100 」；ダイヤホイル株式会社製）を基材シー
トとして用い、その上面に、周知のロールコート方式
で、下記表１に示した組成の塗工液を厚さ50μm となる
ように塗設して、図１(b) に示した構造を有する本発明
の映写用反射型スクリーン材を調製した。 Example 1 A polyethylene terephthalate sheet ("PET 100"; manufactured by Dia foil Co., Ltd.) having a thickness of 100 μm was used as a substrate sheet, and the composition shown in Table 1 below was applied on the upper surface thereof by a well-known roll coating method. This coating solution was applied to a thickness of 50 μm to prepare a projection type reflective screen material of the present invention having the structure shown in FIG. 1 (b).
【００２１】[0021]
【表１】 [Table 1]
【００２２】実施例２ 実施例１と同じポリエチレンテレフタレートシートを基
材シートとして用い、その上面に、周知のロールコート
方式で、下記表２に示した組成の塗工液を厚さ45μm と
なるように塗設して、図１(c) に示した構造を有する本
発明の映写用反射型スクリーン材を調製した。 Example 2 The same polyethylene terephthalate sheet as in Example 1 was used as a substrate sheet, and a coating solution having the composition shown in Table 2 below was formed to a thickness of 45 μm on the upper surface thereof by a well-known roll coating method. Then, the reflective screen material for projection of the present invention having the structure shown in FIG. 1 (c) was prepared.
【００２３】[0023]
【表２】 [Table 2]
【００２４】実施例３ 二酸化チタンを８％含有した 100μm 厚さの光非透過性
ポリエチレンテレフタレートシートを基材シートとして
用い、その上面に、周知のロールコート方式で、下記表
３に示した組成の塗工液を厚さ50μm となるように塗設
して、光非透過性シートを基材シートとして用いた図１
(a) に示した構造を有する映写用反射型スクリーン材を
調製した。 Example 3 A light-transmissive polyethylene terephthalate sheet having a thickness of 100 μm and containing 8% of titanium dioxide was used as a base sheet, and the upper surface thereof was coated by a well-known roll coating method with the composition shown in Table 3 below. The coating solution was applied to a thickness of 50 μm, and the light-impermeable sheet was used as the base sheet.
A reflective screen material for projection having the structure shown in (a) was prepared.
【００２５】[0025]
【表３】 [Table 3]
【００２６】実施例４ 実施例１に記載の厚さ 100μm のポリエチレンテレフタ
レートシート（基材シート）の上面に、表１に示した組
成の塗工液を厚さ50μm となるように塗設し、一方で、
該基材シートの下面（前記塗設面の裏面）に、周知の金
属蒸着装置(EBH-6：日本真空技術株式会社製）を用い
て、厚さ約 400nmのアルミニウム蒸着反射層を設けて、
図２(a) に示した構造を有する光反射層を備えた本発明
の映写用反射型スクリーン材を調製した。 Example 4 A coating solution having the composition shown in Table 1 was coated on the upper surface of a polyethylene terephthalate sheet (base sheet) having a thickness of 100 μm described in Example 1 so as to have a thickness of 50 μm. On the other hand,
On the lower surface of the substrate sheet (the back surface of the coating surface), using a well-known metal vapor deposition device (EBH-6: manufactured by Nippon Vacuum Technology Co., Ltd.), an aluminum vapor deposition reflective layer having a thickness of about 400 nm is provided,
A reflective screen material for projection of the present invention having a light reflecting layer having the structure shown in FIG. 2 (a) was prepared.
【００２７】実施例５ 実施例１に記載の厚さ 100μm のポリエチレンテレフタ
レートシート（基材シート）の上面に、表１に示した組
成の塗工液を厚さ50μm となるように塗設し、一方で、
該基材シートの下面（前記塗設面の裏面）に、下記表４
に記載の組成の塗工液を厚さ20μm となるように塗設し
た。 Example 5 A coating solution having the composition shown in Table 1 was coated on the upper surface of a polyethylene terephthalate sheet (base sheet) having a thickness of 100 μm described in Example 1 so as to have a thickness of 50 μm, On the other hand,
On the lower surface of the substrate sheet (the back surface of the coating surface), the following Table 4
The coating solution having the composition described in 1 above was applied to a thickness of 20 μm.
【００２８】[0028]
【表４】 [Table 4]
【００２９】次に、この20μm 厚みの塗工層上に、実施
例４に記載の方法に従って、厚さ約400nmのアルミニウ
ム蒸着反射層を設けて、図２(b) に示した構造を有する
本発明の映写用反射型スクリーン材を調製した。Then, an aluminum vapor-deposited reflective layer having a thickness of about 400 nm was provided on the coating layer having a thickness of 20 μm according to the method described in Example 4 to obtain a book having the structure shown in FIG. 2 (b). A reflective screen material for projection of the invention was prepared.
【００３０】実施例６ 実施例１に記載の厚さ 100μm のポリエチレンテレフタ
レートシート（基材シート）の上面に、難燃剤を含む下
記表５に示した組成の塗工液を厚さ30μm となるように
塗設して、難燃剤を利用した態様の映写用反射型スクリ
ーン材を調製した。 Example 6 A coating liquid having a composition shown in Table 5 below containing a flame retardant was applied to the upper surface of a polyethylene terephthalate sheet (base material sheet) having a thickness of 100 μm as described in Example 1 to a thickness of 30 μm. A reflective screen material for projection was prepared by applying the flame retardant.
【００３１】[0031]
【表５】 [Table 5]
【００３２】得られたシート材に関して、基材シートを
水平に保ち、ガスバーナーの炎を２cmの距離を開けて、
シート端部および中央部に設定し、５〜10秒間燃焼を継
続して、シートの燃焼状態を目視で観察し、評価した。
その結果、10秒間の燃焼でも、シートは着火し、やや
黒ずむものの、延焼することなく自然消火し、本実施例
のシート材の難燃性が良好であることが確認できた。With respect to the obtained sheet material, the substrate sheet was kept horizontal, the flame of the gas burner was opened at a distance of 2 cm,
The combustion state of the sheet was visually observed and evaluated by setting the sheet at the end and the center and continuing the combustion for 5 to 10 seconds.
As a result, even after burning for 10 seconds, the sheet ignited and darkened slightly, but spontaneously extinguished without spreading fire, and it was confirmed that the sheet material of this example had good flame retardancy.
【００３３】実施例７：性能試験 実施例１〜６で得られた各シート材に関して、SG（スク
リーンゲイン）値の測定、すなわち、白色板にプロジェ
クターの光を照射した際に輝度計を用いて計った際の白
色板の輝度を１とした時の、試料シートの相対的な輝度
を測定した。 Example 7: Performance test With respect to each sheet material obtained in Examples 1 to 6, SG (screen gain) value was measured, that is, using a luminance meter when a white plate was irradiated with light from a projector. The relative brightness of the sample sheet was measured, where the measured brightness of the white plate was 1.
【００３４】さらに、液晶プロジェクター（シャープ株
式会社製）を用いて、実施例１〜６で得られた各シート
材からなるスクリーンフィルムに画像を投映し、その画
像効果を評価した。Further, using a liquid crystal projector (manufactured by Sharp Corporation), an image was projected on the screen film made of each sheet material obtained in Examples 1 to 6, and the image effect was evaluated.
【００３５】これらの試験結果を下記表６に示した。The results of these tests are shown in Table 6 below.
【００３６】[0036]
【表６】 [Table 6]
【００３７】表６の結果から明らかな通り、本発明によ
るシート材によると、いずれの実施例のシート材におい
ても輝度が改善されるのみならず、スクリーン上に鮮明
な画質の映像が、明るい室内でも充分に得られるなど、
その画像効果も良好であることが確認された。As is clear from the results of Table 6, the sheet materials according to the present invention not only improve the brightness in any of the sheet materials of the examples, but also provide a clear image on the screen in a bright room. But you can get enough,
It was confirmed that the image effect was also good.
【００３８】[0038]
【発明の効果】本発明のスクリーン材によると、投影機
から放たれた光線の反射効率が改善され、その結果、ス
クリーン面の輝度が向上すると共に、画質が鮮明にな
り、比較的明るい場所においても映像を鑑賞することが
可能となり、さらには調光操作に関する負担も解消され
るなどの優れた効果を奏するのである。According to the screen material of the present invention, the reflection efficiency of the light rays emitted from the projector is improved, and as a result, the brightness of the screen surface is improved and the image quality becomes clear, and in a relatively bright place. This makes it possible to view images, and also has the excellent effect of eliminating the burden of dimming operations.
【図１】(a) 、(b) および(c) は、本発明の一実施例を
示す一部断面図である。FIG. 1 (a), (b) and (c) are partial cross-sectional views showing an embodiment of the present invention.
【図２】(a) および(b) は、本発明の他の実施例を示す
一部断面図である。2A and 2B are partial cross-sectional views showing another embodiment of the present invention.
【図３】(a) および(b) は、本発明の使用態様を示す図
である。FIG. 3 (a) and (b) are diagrams showing a use mode of the present invention.
１…スクリーン材 ２…基材シート ３…ビーズ層 ４…着色ビーズ ５…透明ビーズ ６…バインダー ７…光線 ８…反射層 ９…着色ビーズ DESCRIPTION OF SYMBOLS 1 ... Screen material 2 ... Substrate sheet 3 ... Bead layer 4 ... Colored beads 5 ... Transparent beads 6 ... Binder 7 ... Rays 8 ... Reflective layer 9 ... Colored beads
Claims (8)
トと、前記基材シートの一方の面に塗設されたビーズ層
から構成された、反射型スクリーンに用いられるスクリ
ーン材であって、 前記ビーズ層が、バインダーおよびビーズから構成され
ていることを特徴とする映写用反射型スクリーン材。1. A screen material used for a reflective screen, comprising a light-transmitting or light-impermeable substrate sheet and a bead layer coated on one surface of the substrate sheet. A reflective screen material for projection, wherein the bead layer is composed of a binder and beads.
する反射層がさらに形成されていることを特徴とする請
求項１に記載の映写用反射型スクリーン材。2. The reflective screen material for projection according to claim 1, further comprising a reflective layer that reflects light on the other surface of the base sheet.
ている請求項２に記載の映写用反射型スクリーン材。3. The reflective screen material for projection according to claim 2, wherein the reflective layer is formed by vapor deposition of metal.
請求項３に記載の映写用反射型スクリーン材。4. The reflective screen material for projection according to claim 3, wherein the reflective layer further contains colored beads.
ズ、あるいはこれらの混合物を含む請求項１ないし４の
いずれかに記載の映写用反射型スクリーン材。5. The reflection type screen material for projection according to claim 1, wherein the bead layer contains transparent beads, colored beads, or a mixture thereof.
ら構成されている請求項１ないし５のいずれかに記載の
映写用反射型スクリーン材。6. The reflective screen material for projection according to claim 1, wherein the bead layer is composed of beads having various particle sizes.
求項１ないし６のいずれかに記載の映写用反射型スクリ
ーン材。7. The reflective screen material for projection according to claim 1, wherein the bead layer further contains a flame retardant.
されたビーズと、前記バインダーに部分的に埋設された
ビーズから構成されている請求項１ないし７のいずれか
に記載の映写用反射型スクリーン材。8. The reflective screen for projection according to claim 1, wherein the bead layer includes beads embedded in the binder and beads partially embedded in the binder. Material.