JPH0732471A - Epoxy resin composition packaging film - Google Patents
Epoxy resin composition packaging filmInfo
- Publication number
- JPH0732471A JPH0732471A JP18100193A JP18100193A JPH0732471A JP H0732471 A JPH0732471 A JP H0732471A JP 18100193 A JP18100193 A JP 18100193A JP 18100193 A JP18100193 A JP 18100193A JP H0732471 A JPH0732471 A JP H0732471A
- Authority
- JP
- Japan
- Prior art keywords
- film
- resin composition
- epoxy resin
- density
- polybutylene terephthalate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、注型用、埋込み用、封
入用、シーリング用、或は、含浸用等のエポキシ樹脂組
成物の包装用フィルムに関するものである。更に具体的
には、段ボール箱の中に装着された袋の中に、各種添加
剤を混合させた直後でまだ高温状態のエポキシ樹脂組成
物を流し込む際の袋に用いるフィルムに関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a packaging film of an epoxy resin composition for casting, embedding, encapsulation, sealing or impregnation. More specifically, the present invention relates to a film used for a bag when a high temperature epoxy resin composition is poured into a bag mounted in a cardboard box immediately after mixing various additives.
【０００２】[0002]
【従来技術】従来、エポキシ樹脂に希釈剤、充填剤、可
塑性付与剤、或は、難燃剤等の各種添加剤は、各ユーザ
ーでそれぞれ用途に応じて添加混合されていた。しか
し、これらの添加剤の混合は非常に難しく高度の技術を
必要とするものであった。そこで、最近では、それぞれ
の用途に応じるように各種添加剤を予め混合させたエポ
キシ樹脂組成物がメーカーから発売されるようになっ
た。2. Description of the Related Art Conventionally, various additives such as a diluent, a filler, a plasticizer, a flame retardant and the like have been added to an epoxy resin and mixed by each user according to their use. However, the mixing of these additives was very difficult and required a high degree of skill. Therefore, recently, manufacturers have begun to sell epoxy resin compositions in which various additives are premixed so as to meet their respective uses.
【０００３】このようなエポキシ樹脂組成物のメーカー
からユーザーへ輸送するための包装は、各種添加剤を混
合させた直後で、高温、粘調な状態の樹脂組成物を容器
に流し込み、冷却固化させる方法が行われている。そし
て、その容器としては金属性の缶が用いられていたが、
コストが高くついていた。又、金属製の缶は使用後に廃
棄することにおいても多大な問題を有していた。そこ
で、箱の内面にポリエチレンテレフタレートフィルムを
貼り合わせた段ボール箱が用いられるようになった。し
かし、該方法でもコストが高くつき、しかも、表面層の
ポリエチレンテレフタレートフィルムとエポキシ樹脂組
成物との剥離性が悪いので、該樹脂組成物に移行しない
ような特殊な離型剤を該フィルム表面に塗布する必要が
あった。Packaging for transporting such an epoxy resin composition from a manufacturer to a user is carried out by pouring the resin composition in a high temperature and viscous state into a container immediately after mixing various additives and cooling and solidifying the resin composition. The way is done. And a metal can was used as the container,
The cost was high. Further, the metal can has a great problem in discarding it after use. Therefore, a corrugated box in which a polyethylene terephthalate film is attached to the inner surface of the box has come to be used. However, even with this method, the cost is high, and since the peelability between the polyethylene terephthalate film of the surface layer and the epoxy resin composition is poor, a special release agent that does not migrate to the resin composition is applied to the film surface. It had to be applied.
【０００４】尚、各種添加剤を混合させた直後の温度は
一般に１６０℃以上であるので、該包装に用いるフィル
ムは、少なくともそれ以上の温度に耐えるものでなけれ
ばならない。又、ポリエチレンテレフタレートフィルム
は、ヒートシール性が悪くて袋状にすることが困難なた
め、段ボール箱の中に入れる角底袋を製袋することがで
きなかったので、段ボール箱の内面に貼り合されてい
た。Since the temperature immediately after mixing the various additives is generally 160 ° C. or higher, the film used for the packaging must be able to withstand at least that temperature. Also, since polyethylene terephthalate film has poor heat-sealing properties and it is difficult to make it into a bag, it was not possible to make a square bottom bag into a cardboard box. It had been.
【０００５】[0005]
【発明が解決しようとする課題】本発明は、高温のエポ
キシ樹脂組成物が流し込めるように高温時でのフィルム
の強度が強く、又、取り出しが容易なような該樹脂組成
物との剥離性を有し、しかも、ヒートシール法により容
易に製袋することができる安価なエポキシ樹脂組成物の
包装用フィルムを提供しようとするものである。DISCLOSURE OF THE INVENTION According to the present invention, the strength of the film at high temperature is high so that the high temperature epoxy resin composition can be poured, and the releasability from the resin composition is such that the film can be easily taken out. Further, it is an object of the present invention to provide an inexpensive epoxy resin composition packaging film that has the above-mentioned properties and can be easily bag-formed by the heat-sealing method.
【０００６】[0006]
【課題を解決するための手段】本発明は、上記課題を解
決するために次のような手段を講じた。即ち、１．３０
ｇ／ｃｍ3 以上の密度を有するポリブチレンテレフタレ
ートフィルムからなる。又、好ましくは、密度１．３０
ｇ／ｃｍ3 以上のポリブチレンテレフタテートフィルム
は、インフレーション法によりにより得られる。又、好
ましくは、密度１．３０ｇ／ｃｍ3 以上のポリブチレン
テレフタレートフィルムは、二軸延伸法により製膜され
た後に熱処理されて得られる。The present invention has taken the following means in order to solve the above problems. That is, 1.30
It is made of a polybutylene terephthalate film having a density of g / cm 3 or more. Also, preferably, the density is 1.30.
A polybutylene terephthalate film having a g / cm 3 or more is obtained by an inflation method. Further, preferably, a polybutylene terephthalate film having a density of 1.30 g / cm 3 or more is obtained by heat treatment after being formed by a biaxial stretching method.
【０００７】本発明に用いられるポリブチレンテレフタ
レート樹脂としては、特に限定されるものではないが、
固有粘度が０．９以上のものが好ましい。固有粘度が
０．９未満の場合には、押出成形時の溶融粘度が低くて
形状を保持することが困難である。尚、本発明に於て、
固有粘度とは２５℃のオルソクロルフェノール中で測定
された値である。The polybutylene terephthalate resin used in the present invention is not particularly limited,
It is preferable that the intrinsic viscosity is 0.9 or more. If the intrinsic viscosity is less than 0.9, the melt viscosity during extrusion molding is low and it is difficult to maintain the shape. In the present invention,
Intrinsic viscosity is a value measured in orthochlorophenol at 25 ° C.
【０００８】又、上記ポリブチレンテレフタレート樹脂
からなるフィルムの密度としては、１．３０ｇ／ｃｍ3
以上であることが必要である。 密度が１．３０ｇ／ｃ
ｍ3未満であると、エポキシ樹脂組成物との剥離性が悪
くなる。又、高温のエポキシ樹脂組成物を充填させる際
に、フィルムの腰が弱くてフィルムに皺を生じ易くな
る。尚、フィルムに皺が生じると、該皺の溝の中にエポ
キシ樹脂組成物が入り込み、取り出し作業が困難にな
る。The density of the film made of the polybutylene terephthalate resin is 1.30 g / cm 3.
It is necessary to be above. Density 1.30g / c
When it is less than m 3 , the releasability from the epoxy resin composition deteriorates. In addition, when the high temperature epoxy resin composition is filled, the film has a weak stiffness and is easily wrinkled. When the film has wrinkles, the epoxy resin composition enters the groove of the wrinkles, and it becomes difficult to take out the epoxy resin composition.
【０００９】ポリブチレンテレフタレートフィルムの密
度を１．３０ｇ／ｃｍ3 以上に高めるには、押し出され
た樹脂を徐冷させる方法がある。そこで、該方法として
は、インフレーション方式により製膜するのが好まし
い。Ｔダイ方式による製膜されたフィルムは、押し出さ
れた樹脂が急冷されるために密度が低下し、エポキシ樹
脂組成物との剥離性が悪くなり、しかも、高温時でのフ
ィルムの腰が弱くなるので、エポキシ樹脂組成物包装用
フィルムとしては好ましくない。In order to increase the density of the polybutylene terephthalate film to 1.30 g / cm 3 or more, there is a method of gradually cooling the extruded resin. Therefore, as the method, it is preferable to form a film by an inflation method. The film formed by the T-die method has a low density because the extruded resin is rapidly cooled, the releasability from the epoxy resin composition deteriorates, and the film becomes less stiff at high temperature. Therefore, it is not preferable as a film for packaging an epoxy resin composition.
【００１０】又、熱処理によって密度を高める方法もあ
る。該方法としては、急冷させたフィルムを延伸加工さ
せた後、熱処理加工させて寸法安定性を付与させると共
に、密度を高めるのが好ましい。しかも、延伸加工はフ
ィルム強度の面から二軸延伸するのが好ましい。二軸延
伸方法としては、インフレーション二軸延伸法やテンタ
ー法等が好ましい。この様な方法によって得られたポリ
ブチレンテレフタレートフィルムは、透明性が良く、強
度が強く、しかも、高温時でのフィルムの腰も強くてエ
ポキシ樹脂組成物包装用フィルムとして適している。There is also a method of increasing the density by heat treatment. As the method, it is preferable that the quenched film is stretched and then heat-treated to impart dimensional stability and to increase the density. Moreover, the stretching is preferably biaxially stretched from the viewpoint of film strength. As a biaxial stretching method, an inflation biaxial stretching method, a tenter method or the like is preferable. The polybutylene terephthalate film obtained by such a method is suitable as an epoxy resin composition packaging film because it has good transparency and strength, and the film is strong at high temperature.
【００１１】[0011]
【実施例】以下、実施例及び比較例を示し、本発明の内
容をより具体的に説明する。尚、本発明は、実施例に記
載された事項によってのみ限定されるものでないことは
当然である。 〔実施例１〕固有粘度１．２のポリブチレンテレフタレ
ート樹脂を２６５℃でサーキュラーダイより押出しイン
フレーション法によりフィルム化させた後、エアーリン
グにより徐冷させて厚み６０μｍのエポキシ樹脂組成物
包装用フィルムを得た。得られたフィルムは、高温時で
のフィルムの腰が強く、しかも、容易にヒートシールす
ることができ、段ボール箱内袋用の角底袋を製袋するこ
とができた。又、得られた角底袋を段ボールの中に装着
し、該袋の中に、各種添加剤を混合した温度１７０℃の
電気製品注型用エポキシ樹脂組成物を流し込み、その
後、冷却固化させてエポキシ樹脂組成物の包装体を得
た。得られた包装体は、フィルム部に皺がなく、しか
も、エポキシ樹脂組成物とフィルムとの剥離性が良好で
あった。尚、該実施例１のフィルムの密度は１．３１ｇ
／ｃｍ3 であった。EXAMPLES Hereinafter, the contents of the present invention will be described more specifically by showing Examples and Comparative Examples. Of course, the present invention is not limited only by the matters described in the examples. [Example 1] A polybutylene terephthalate resin having an intrinsic viscosity of 1.2 was extruded from a circular die at 265 ° C to form a film by an inflation method, and then slowly cooled by an air ring to form a film for packaging an epoxy resin composition having a thickness of 60 µm. Obtained. The obtained film was strong at high temperature and could be easily heat-sealed to form a square bottom bag for a cardboard box inner bag. Further, the obtained square bottom bag is mounted in a corrugated cardboard, and the epoxy resin composition for electric product casting at a temperature of 170 ° C., which is mixed with various additives, is poured into the bag and then cooled and solidified. A package of the epoxy resin composition was obtained. The obtained package had no wrinkles in the film portion and had good peelability between the epoxy resin composition and the film. The density of the film of Example 1 was 1.31 g.
/ Cm 3 .
【００１２】〔実施例２〕固有粘度１．０のポリブチレ
ンテレフタレート樹脂を２７０℃で押出し、水冷方式に
よって急冷させてチューブ状未延伸シートを得た。得ら
れた該チューブ状未延伸シートをインフレーション方式
によって二軸延伸し、その後、２００℃の熱処理を行っ
て厚み５０μｍのエポキシ樹脂組成物包装用フィルムを
得た。得られたフィルムは、実施例１と同様、高温時で
のフィルムの腰が強く、しかも、容易にヒートシールす
ることができた。又、得られたフィルムを用いて、実施
例１と同様、角底袋を製袋し、エポキシ樹脂組成物の包
装体を得た。得られた包装体は、実施例１と同様、フィ
ルム部に皺がなく、しかも、エポキシ樹脂組成物とフィ
ルムとの剥離性が良好であった。尚、該実施例２のフィ
ルムの密度は１．３２ｇ／ｃｍ3 で、しかも、透明性に
優れていた。Example 2 A polybutylene terephthalate resin having an intrinsic viscosity of 1.0 was extruded at 270 ° C. and rapidly cooled by a water cooling method to obtain a tubular unstretched sheet. The obtained tubular unstretched sheet was biaxially stretched by an inflation method and then heat-treated at 200 ° C. to obtain a 50 μm-thick epoxy resin composition packaging film. Similar to Example 1, the obtained film had a strong elasticity at high temperature and could be easily heat-sealed. Further, using the obtained film, a square bottom bag was formed in the same manner as in Example 1 to obtain a package of the epoxy resin composition. Similar to Example 1, the obtained package had no wrinkles in the film portion and had good releasability between the epoxy resin composition and the film. The film of Example 2 had a density of 1.32 g / cm 3 and was excellent in transparency.
【００１３】〔比較例１〕実施例１で用いたポリブチレ
ンテレフタレート樹脂を２６５℃でＴダイより押出して
フィルム化させた後、チルロールにより急冷させて厚さ
５０μｍのエポキシ樹脂組成物包装用フィルムを得た。
得られたフィルムは、ヒートシール性を有していたが、
高温時でのフィルムの腰が弱かった。又、得られたフィ
ルムを用いて、実施例１と同様、角底袋を製袋し、エポ
キシ樹脂組成物の包装体を得た。しかし、得られた包装
体は、高温のエポキシ樹脂組成物を充填させる時にフィ
ルム部に皺が生じ、しかも、エポキシ樹脂組成物とフィ
ルムとの剥離性が悪く、内容物のエポキシ樹脂組成物の
取り出しができなかった。尚、該実施例１のフィルムの
密度は１．２８ｇ／ｃｍ3 であった。Comparative Example 1 The polybutylene terephthalate resin used in Example 1 was extruded from a T die at 265 ° C. to form a film, which was then rapidly cooled by a chill roll to form a 50 μm thick epoxy resin composition packaging film. Obtained.
The obtained film had heat sealability,
The stiffness of the film was weak at high temperatures. Further, using the obtained film, a square bottom bag was formed in the same manner as in Example 1 to obtain a package of the epoxy resin composition. However, the obtained package has wrinkles in the film portion when it is filled with the high temperature epoxy resin composition, and further, the peeling property between the epoxy resin composition and the film is poor, and the removal of the epoxy resin composition of the contents is taken out. I couldn't. The density of the film of Example 1 was 1.28 g / cm 3 .
【００１４】[0014]
【効果】本発明のエポキシ樹脂組成物包装用フィルム
は、ヒートシール性が良好であるので、段ボール箱の内
袋用角底袋を容易に製袋させることができ、従来のポリ
エチレンテレフタレートフィルムを用いる際のように、
段ボール箱の内面に貼り合わせる必要がないので、包装
コストが少なくて済む。又、本発明のエポキシ樹脂組成
物包装用フィルムからなる角底袋は、高温でもフィルム
の腰が強いので、各種添加剤を混合した高温のエポキシ
樹脂組成物の充填にも充分に耐える。更に、本発明のエ
ポキシ樹脂組成物包装用フィルムは、該エポキシ樹脂組
成物との剥離性が良好であるので、フィルム表面に離型
剤等を塗布することなく容易に該樹脂を取り出すことが
できる。しかも、離型剤を塗布する必要がないので、該
成分等がエポキシ樹脂組成物に移行することもない。[Effect] The epoxy resin composition packaging film of the present invention has a good heat-sealing property, so that a square bottom bag for an inner bag of a corrugated cardboard box can be easily manufactured, and a conventional polyethylene terephthalate film is used. Just like
Since it is not necessary to attach it to the inner surface of the cardboard box, the packaging cost is low. Further, since the square bottom bag made of the epoxy resin composition packaging film of the present invention has a strong film rigidity even at high temperatures, it can sufficiently withstand the filling of the high temperature epoxy resin composition mixed with various additives. Furthermore, since the epoxy resin composition packaging film of the present invention has good releasability from the epoxy resin composition, the resin can be easily taken out without applying a release agent or the like to the film surface. . Moreover, since it is not necessary to apply a release agent, the components and the like do not migrate to the epoxy resin composition.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 // Ｂ２９Ｋ 67:00 Ｂ２９Ｌ 7:00 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 6 Identification number Office reference number FI technical display location // B29K 67:00 B29L 7:00
Claims (3)
ポリブチレンテレフタレートフィルムからなるエポキシ
樹脂組成物包装用フィルム。1. An epoxy resin composition packaging film comprising a polybutylene terephthalate film having a density of 1.30 g / cm 3 or more.
レンテレフタレートフィルムが、インフレーション法に
より得られていることを特徴とする請求項１記載のエポ
キシ樹脂組成物包装用フィルム。2. A film for packaging an epoxy resin composition according to claim 1, wherein the polybutylene terephthalate film having a density of 1.30 g / cm 3 or more is obtained by an inflation method.
レンテレフタレートフィルムが、二軸延伸法により製膜
された後に熱処理されていることを特徴とする請求項１
記載のエポキシ樹脂組成物包装用フィルム。 3. A polybutylene terephthalate film having a density of 1.30 g / cm 3 or more is heat-treated after being formed by a biaxial stretching method.
The epoxy resin composition packaging film described.