JPH0741353A - Wall material having bactericidal action and method of using the same - Google Patents
Wall material having bactericidal action and method of using the sameInfo
- Publication number
- JPH0741353A JPH0741353A JP11002594A JP11002594A JPH0741353A JP H0741353 A JPH0741353 A JP H0741353A JP 11002594 A JP11002594 A JP 11002594A JP 11002594 A JP11002594 A JP 11002594A JP H0741353 A JPH0741353 A JP H0741353A
- Authority
- JP
- Japan
- Prior art keywords
- wall material
- bactericidal action
- ceramic powder
- wall
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【目的】本発明は、院内感染の主たる原因菌である緑膿
菌(Pseudomonous aeruginosa) とＭＲＳＡ(methicillin
resistant staphylococcus aereus) に対して効果的な
殺菌作用を有する壁材に関する。
【構成】殺菌作用を有する壁材を、モルタルに、アクリ
ル酸エステル共重合体を主成分とする複合ポリマーエマ
ルジョンとセラミック粉とを混入した生成している。か
かる壁材は、モルタル内に混入した複合ポリマーエマル
ジョン及びセラミック粉の保有する良好な抗菌力によっ
て、緑膿菌及びＭＲＳＡをともに著しく減少することが
でき、院内感染の防止に極めて有効である。
(57) [Summary] [Purpose] The present invention aims to provide Pseudomonous aeruginosa (Pseudomonas aeruginosa) and MRSA (methicillin), which are the main causes of nosocomial infections.
The present invention relates to a wall material having an effective bactericidal action against resistant staphylococcus aereus). [Structure] A wall material having a bactericidal action is produced by mixing a mortar with a composite polymer emulsion containing an acrylic ester copolymer as a main component and a ceramic powder. Such a wall material can significantly reduce both Pseudomonas aeruginosa and MRSA due to the good antibacterial activity of the composite polymer emulsion and ceramic powder mixed in the mortar, and is extremely effective in preventing nosocomial infections.
Description
【０００１】[0001]
【産業上の利用分野】本発明は、院内感染の主たる原因
菌である緑膿菌(Pseudomonous aeruginosa)とＭＲＳＡ
(methicillin resistant staphylococcus aereus) に対
して効果的な殺菌作用を有する壁材及びその使用方法に
関する。The present invention relates to Pseudomonous aeruginosa, which is the main causative agent of nosocomial infection, and MRSA.
The present invention relates to a wall material having an effective bactericidal action against (methicillin resistant staphylococcus aereus) and a method of using the same.
【０００２】[0002]
【従来の技術】上記した院内感染の発生メカニズムとし
ては、一般に、以下のものが考えられる。2. Description of the Related Art The following are generally considered as the mechanism of the occurrence of the above-mentioned nosocomial infection.
【０００３】感染に対して抵抗力の弱っている患者が
増加している。An increasing number of patients are less resistant to infection.
【０００４】感染に対して抵抗力を弱めるような治療
法や検査法が行われることがある。Treatments and tests that weaken the resistance to infection may be performed.
【０００５】正常な防御機構を障害するような医療な
どが行われる場合がある。There are cases where medical treatment is performed to impair the normal defense mechanism.
【０００６】化学療法剤、殊に広域抗生物質の濃厚長
期使用が考えられる。Concentrated long-term use of chemotherapeutic agents, especially broad spectrum antibiotics, is conceivable.
【０００７】病室の構造、特に壁面や床面が緑膿菌や
ＭＲＳＡの成育を助長している。The structure of the hospital room, particularly the wall surface and the floor surface, promote the growth of Pseudomonas aeruginosa and MRSA.
【０００８】ところで、上記した院内感染の発生メカニ
ズムの内のに着目した場合、従来の病院における壁材
は、主として、セメントによるモルタル層やペイント等
の美装材によって形成されている。[0008] By the way, when focusing on the above-mentioned mechanism of nosocomial infection, the wall material in the conventional hospital is mainly formed of a mortar layer made of cement or a beauty material such as paint.
【０００９】[0009]
【発明が解決しようとする課題】しかし、かかる壁材
は、院内感染に関して、以下の問題を有する。However, such wall materials have the following problems regarding nosocomial infections.
【００１０】即ち、壁材は専らモルタルからなるが、モ
ルタルは吸水性が大きく、その表面ないし裏面が、緑膿
菌やＭＲＳＡの恰好の成育場所になる。That is, although the wall material is composed exclusively of mortar, the mortar has a high water absorption property, and the front surface or the back surface thereof is a suitable growth place for Pseudomonas aeruginosa and MRSA.
【００１１】本発明は、上記問題点を解決することがで
きる殺菌作用を有する壁材を提供することを目的とす
る。An object of the present invention is to provide a wall material having a bactericidal action capable of solving the above problems.
【００１２】[0012]
【課題を解決するための手段】本発明は、モルタルに、
アクリル酸エステル共重合体を主成分とする複合ポリマ
ーエマルジョンとセラミック粉とを混入したことを特徴
とする殺菌作用を有する壁材に係るものである。The present invention relates to a mortar,
The present invention relates to a wall material having a bactericidal action, which is obtained by mixing a composite polymer emulsion containing an acrylic acid ester copolymer as a main component and ceramic powder.
【００１３】上記構成において、モルタルとしては、白
色セメント又はポルトランドセメントに、珪砂、鉄粉、
亜鉛華、その他を混合したものを用いるのが好ましい。In the above structure, as the mortar, white cement or Portland cement, silica sand, iron powder,
It is preferable to use a mixture of zinc white and others.
【００１４】複合ポリマーエマルジョンは緑膿菌とＭＲ
ＳＡに対して殺菌機能を有するものであり、固形分とし
て25〜50％含むアクリル酸エステル共重合体水溶液を用
いるのが好ましい。The complex polymer emulsion is Pseudomonas aeruginosa and MR
It is preferable to use an aqueous solution of an acrylic acid ester copolymer which has a sterilizing function against SA and contains 25 to 50% as a solid content.
【００１５】セラミック粉も、緑膿菌とＭＲＳＡに対し
て殺菌機能を有するものであり、珪砂を焼結した後、粉
状としたセラミック粉を好適に用いる。The ceramic powder also has a bactericidal function against Pseudomonas aeruginosa and MRSA, and it is preferable to use ceramic powder which has been powdered after sintering silica sand.
【００１６】また、複合ポリマーエマルジョンと、セラ
ミック粉を含めたモルタルとの混合比は、1:1 〜1:6.5
とするのが好ましい。The mixing ratio of the composite polymer emulsion and the mortar containing the ceramic powder is 1: 1 to 1: 6.5.
Is preferred.
【００１７】さらに、本発明は、上記した殺菌作用を有
する壁材の好適な使用方法に係るものである。具体的に
は、以下の通りである。Furthermore, the present invention relates to a preferred method of using the above-mentioned wall material having a bactericidal action. Specifically, it is as follows.
【００１８】上記した壁材を建築物の壁体として用い
る。The above wall material is used as a wall of a building.
【００１９】上記した壁材を、不織布や、ガラスクロ
スや、織布等の表面に、スプレーガン等を用いて吹付塗
布し、乾燥後に、ロール状に巻取り、必要な寸法に裁断
して使用する。The above wall material is spray-coated on the surface of a non-woven fabric, glass cloth, woven fabric or the like with a spray gun, dried, wound into a roll and cut to a required size for use. To do.
【００２０】上記した壁材を、天井ボードに塗布す
る。The above wall material is applied to a ceiling board.
【００２１】上記した壁材を、新築・既存の構造物の
垂直壁面や床面に、直接、吹付塗布する。The above wall material is directly spray-coated on the vertical wall surface or floor surface of a new / existing structure.
【００２２】[0022]
【実施例】以下、本発明に係る殺菌作用を有する壁材の
製造方法について説明する。EXAMPLES A method for producing a wall material having a bactericidal action according to the present invention will be described below.
【００２３】まず、複合ポリマーエマルジョンとして、
以下の配合のものを用いた。First, as a composite polymer emulsion,
The following formulation was used.
【００２４】例１) しかし、以下の成分構成も好適に用いることができる。Example 1) However, the following component configurations can also be preferably used.
【００２５】例２) また、上記複合ポリマーエマルジョンに混合するモルタ
ルは、セラミック粉を含有した状態で、以下の成分構成
とした。Example 2) Further, the mortar mixed with the above-mentioned composite polymer emulsion had the following component constitution while containing the ceramic powder.
【００２６】 なお、上記白色セメントの成分重量比は、以下の通りで
あった。[0026] The component weight ratio of the white cement was as follows.
【００２７】 なお、この白色セメントに代えて、ポルトランドセメン
トを用いることもできる。[0027] Portland cement may be used instead of the white cement.
【００２８】上記したセラミック粉として、以下の組成
のものを用いた。このセラミック粉は、廃材としての使
用済碍子を磨砕して得たものであり、粒径は74μm 〜14
9 μm であった。As the above-mentioned ceramic powder, the one having the following composition was used. This ceramic powder was obtained by grinding used insulators as waste material and has a particle size of 74 μm ~ 14 μm.
It was 9 μm.
【００２９】 また、上記した組成では、顔料は、複合ポリマーエマル
ジョンのみに混入したが、モルタルのみ、或いは、両方
に、顔料、水性ペイント、或いは、その両方に添加する
ことにより、任意の色に着色することができる。[0029] Further, in the above composition, the pigment is mixed only in the composite polymer emulsion, but it can be colored in any color by adding it to the pigment, the water-based paint, or both to the mortar alone or both. it can.
【００３０】具体的には、無機顔料としては、酸化チタ
ン (白) 、カーボンブラック (黒)、ベンガラ (赤) 、
チタンイエロー (黄) 、酸化第２クロム (緑) 、コンジ
ョウ(青) を用いることができる。また、有機顔料とし
ては、パーマネントレッド(赤) 、ハンサイエロー (黄)
、フタロシアニングリーン (緑) 、フタロシアニンブ
ルー (青) 、ジオキサジンバイオレット (紫) 等を用い
ることができる。Specifically, the inorganic pigments include titanium oxide (white), carbon black (black), red iron oxide (red),
Titanium yellow (yellow), chromic oxide (green), and konjac (blue) can be used. Also, as organic pigments, permanent red (red), Hansa yellow (yellow)
, Phthalocyanine green (green), phthalocyanine blue (blue), dioxazine violet (purple) and the like can be used.
【００３１】上記した複合ポリマーエマルジョン１に対
して、重量比で、モルタルを、1.0〜６.5の割合で掻き
混ぜて、殺菌作用を有する壁材を製造する。Mortar is stirred into the composite polymer emulsion 1 described above in a weight ratio of 1.0 to 6.5 to produce a wall material having a bactericidal action.
【００３２】次に、上記した工程で製造した本発明に係
る殺菌作用を有する壁材の殺菌効果を試験したので、そ
の条件及び結果を以下に示す。Next, the sterilizing effect of the wall material having the bactericidal action according to the present invention produced in the above steps was tested, and the conditions and results are shown below.
【００３３】〔目 的〕 殺菌作用を有する壁剤の効
力をin vitroで検討した。[Objective] The efficacy of the wall agent having a bactericidal action was examined in vitro.
【００３４】〔実施機関〕 株式会社 シー・アール・
シー 細菌検査室 〔試 料〕 壁剤 茶色 30mm×30mm 菌株 緑膿菌(Pseudomonas aeruginosa ATCC 27853) 菌株 MRSA(methicillin resistant staphylococcus
aereus) 〔試験方法〕 1) 壁剤の準備 壁剤を30mmの正方形に裁断し、オートクレーブで121
℃15分間滅菌した。[Executing Agency] C.R.
Sea Bacteria Laboratory (Sample) Wall Agent Brown 30 mm × 30 mm Strain Pseudomonas aeruginosa ATCC 27853 Strain MRSA (methicillin resistant staphylococcus)
aereus) [Test method] 1) Preparation of wall material The wall material is cut into 30 mm squares and 121
Sterilized at 15 ° C for 15 minutes.
【００３５】2) 菌株の準備 緑膿菌(ATCC 27853)及びMRSA( 臨床分離株) をH I brot
h を用いて35℃、24時間培養した。2) Preparation of strain Pseudomonas aeruginosa (ATCC 27853) and MRSA (clinical isolate) were HI brot.
The cells were cultured for 24 hours at 35 ° C. using h.
【００３６】3) 菌液調整・測定 H I broth を用いて35℃、24時間培養した菌液から200
μl づつ800 μl のH I broth に接種し原液とした。測
定は、H I broth900 μl に100 μl づつ滴下した希釈
系列を作製し、20μl を標準寒天培地に滴下し、コンラ
ージ棒で拡散し35℃、24時間培養後菌数を測定した。対
照としてキムセル・ワイパー布30mm×30mmを用いた。3) Preparation / Measurement of Bacterial Solution 200 from bacterial solution cultured at 35 ° C. for 24 hours using HI broth
800 μl of HI broth was inoculated into each well to prepare a stock solution. For the measurement, a dilution series was prepared by dropping 100 μl of each to 900 μl of HI broth, 20 μl was added dropwise to a standard agar medium, diffused with a conradi rod and cultured at 35 ° C. for 24 hours, and the number of bacteria was measured. As a control, a 30 mm × 30 mm Kimsel wiper cloth was used.
【００３７】4) 結果4) Results
【００３８】[0038]
【表１】 [Table 1]
【００３９】5) まとめ 上記表から明らかなように、本発明に係る殺菌作用を有
する壁材に混入した複合ポリマーエマルジョン及びセラ
ミック粉(SiO2)による抗菌力によって、緑膿菌では、10
10/ml 以下に減少でき、ＭＲＳＡでは、1010/ml から10
6 に半減しており、良好な抗菌力を示した。5) Summary As is clear from the above table, due to the antibacterial activity of the composite polymer emulsion and the ceramic powder (SiO 2 ) mixed in the wall material having a bactericidal action according to the present invention, 10
It can be reduced to less than 10 / ml, and in MRSA, from 10 10 / ml to 10
It was halved to 6 , showing good antibacterial activity.
【００４０】また、本発明に係る壁材は、建築構造物の
壁体そのものとして利用することもできるが、好ましく
は、図１又は図２に示す態様で用いるのが好ましい。The wall material according to the present invention can be used as the wall itself of a building structure, but it is preferably used in the mode shown in FIG. 1 or 2.
【００４１】即ち、図１では、不織布や、ガラスクロス
や、織布等10の表面に、上記した組成を有する壁材11を
スプレーガン12を用いて吹付塗布し (図１(a))、温風乾
燥後に (図１(a))、ロール状に巻取り (図１(a))、必要
な寸法に裁断して使用するものである。That is, in FIG. 1, a wall material 11 having the above-mentioned composition is spray-coated on the surface of a non-woven fabric, glass cloth, woven fabric or the like 10 by using a spray gun 12 (FIG. 1 (a)). After drying with warm air (Fig. 1 (a)), it is wound into a roll (Fig. 1 (a)) and cut into the required size before use.
【００４２】また、図２では、天井ボード13に同様に壁
材11を塗布した形態で用いている。Further, in FIG. 2, the ceiling board 13 is similarly applied with the wall material 11.
【００４３】また、新築・既存の構造物の垂直壁面や床
面に直接壁材11を吹付塗布するようにすることもでき
る。Alternatively, the wall material 11 can be directly spray-applied to the vertical wall surface or floor surface of a new or existing structure.
【００４４】[0044]
【効果】本発明に係る殺菌作用を有する壁材は、モルタ
ルに、アクリル酸エステル共重合体を主成分とする複合
ポリマーエマルジョンとセラミック粉とを混入したこと
を特徴とする。[Effect] The wall material having a bactericidal action according to the present invention is characterized in that a composite polymer emulsion containing an acrylic ester copolymer as a main component and ceramic powder are mixed in mortar.
【００４５】かかる壁材は、モルタル内に混入した複合
ポリマーエマルジョン及びセラミック粉の保有する良好
な抗菌力によって緑膿菌及びＭＲＳＡをともに著しく減
少することができ、院内感染の防止に極めて有効であ
る。Such a wall material can significantly reduce both Pseudomonas aeruginosa and MRSA due to the good antibacterial activity of the composite polymer emulsion and ceramic powder mixed in the mortar, and is extremely effective in preventing nosocomial infections. .
【図１】殺菌作用を有する壁材の使用状態を示す説明図
である。FIG. 1 is an explanatory view showing a usage state of a wall material having a bactericidal action.
【図２】殺菌作用を有する壁材の他の使用状態を示す説
明図である。FIG. 2 is an explanatory diagram showing another usage state of the wall material having a sterilizing action.
10 不織布・ガラスクロス・織布等 11 壁材 12 スプレーガン 13 天井ボード 10 Nonwoven fabric, glass cloth, woven fabric, etc. 11 Wall material 12 Spray gun 13 Ceiling board
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｅ０４Ｆ 13/08 Ａ 9127−2Ｅ // Ｅ０４Ｈ 3/08 Ｃ (Ｃ０４Ｂ 28/04 24:26 Ｆ 18:16） ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display area E04F 13/08 A 9127-2E // E04H 3/08 C (C04B 28/04 24:26 F 18 : 16)
Claims (5)
を主成分とする複合ポリマーエマルジョンとセラミック
粉とを混入して生成したことを特徴とする殺菌作用を有
する壁材。1. A wall material having a bactericidal action, which is produced by mixing mortar with a composite polymer emulsion containing an acrylic ester copolymer as a main component and ceramic powder.
用いることを特徴とする殺菌作用をジョンとセラミック
粉とを混入して生成したことを特徴とする殺菌作用を有
する壁材の使用方法。2. A wall material having a bactericidal action, characterized by using the wall material according to claim 1 as a wall of a building, which is produced by mixing John and ceramic powder. How to use.
クロスや、織布等の表面に、吹付塗布し、乾燥後に、ロ
ール状に巻取り、必要な寸法に裁断して使用することを
特徴とする殺菌作用を有する壁材の使用方法。3. The wall material according to claim 1 is spray-coated on the surface of a non-woven fabric, a glass cloth, a woven fabric, etc., dried, wound into a roll, and cut into a required size for use. A method of using a wall material having a bactericidal action, which is characterized by the following.
することを特徴とする殺菌作用を有する壁材の使用方
法。4. A method of using a wall material having a bactericidal action, which comprises applying the wall material according to claim 1 to a ceiling board 13.
の垂直壁面や床面に直接吹付塗布することを特徴とする
請求項１記載の殺菌作用を有する壁材の使用方法。5. The method of using a wall material having a bactericidal action according to claim 1, wherein the wall material according to claim 1 is directly spray-coated on the vertical wall surface or floor surface of a newly constructed / existing structure.