JPH0741744A - Polyester film for coating can body material and welded can body using the same - Google Patents
Polyester film for coating can body material and welded can body using the sameInfo
- Publication number
- JPH0741744A JPH0741744A JP19121993A JP19121993A JPH0741744A JP H0741744 A JPH0741744 A JP H0741744A JP 19121993 A JP19121993 A JP 19121993A JP 19121993 A JP19121993 A JP 19121993A JP H0741744 A JPH0741744 A JP H0741744A
- Authority
- JP
- Japan
- Prior art keywords
- polyester film
- layer
- resin
- body material
- metal plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【目的】缶外面側に形成される保護被覆層の画像に特殊
な色調を付与できる缶体材料被覆用ポリエステルフィル
ム及びこのポリエステルフィルムを用いる美粧性に優れ
た溶接缶体を提供する。
【構成】ポリエステルフィルム１の一方の面に顔料を含
む樹脂組成物からなる第１印刷層３ａ、金属粉末が分散
された樹脂組成物からなる第２印刷層３ｂ、熱硬化型樹
脂系接着剤層４を設ける。第２印刷層３ｂを形成する樹
脂組成物はアルミニウム粉末を１７〜２５重量％の範囲
で含む。ポリエステルフィルム１の他方の面に硬化オー
バーコート層５を設ける。缶体材料用金属板１１の缶外
面側に両側端縁部１１ａを除いてポリエステルフィルム
１を接着剤層４を介して加熱接着して保護被覆層１２を
形成する。溶接缶体は、金属板１１の両側端縁部１１ａ
を重ね合せて溶接接合して缶胴部１６を形成する。
(57) [Abstract] [Purpose] A polyester film for coating a can body material capable of imparting a special color tone to the image of the protective coating layer formed on the outer surface side of the can, and a welded can body excellent in aesthetics using the polyester film. provide. [Structure] A first printing layer 3a made of a resin composition containing a pigment on one surface of a polyester film 1, a second printing layer 3b made of a resin composition in which a metal powder is dispersed, and a thermosetting resin adhesive layer. 4 is provided. The resin composition forming the second printed layer 3b contains aluminum powder in the range of 17 to 25% by weight. A cured overcoat layer 5 is provided on the other surface of the polyester film 1. The polyester film 1 is heat-bonded via the adhesive layer 4 to the outer surface side of the can body material metal plate 11 excluding both side edge portions 11a to form the protective coating layer 12. The welding can is composed of both side edge portions 11a of the metal plate 11.
Are overlapped and welded to each other to form a can body 16.
Description
【０００１】[0001]
【産業上の利用分野】本発明は、缶体材料用金属板、例
えば溶接缶体の缶胴形成用表面処理鋼板等の金属板に熱
硬化型樹脂系接着剤を介して加熱接着されて保護被覆層
を形成するポリエステルフィルム及びそれを用いる溶接
缶体に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention protects a metal plate for a can body material, for example, a metal plate such as a surface-treated steel plate for forming a can body of a welded can body, by heat bonding with a thermosetting resin adhesive. The present invention relates to a polyester film forming a coating layer and a welding can body using the same.
【０００２】[0002]
【従来の技術】飲料物等の容器に使用される金属缶体と
して、缶胴形成用表面処理鋼板を短冊状に裁断した缶胴
ブランクの両側縁を溶接して接合することにより缶胴部
を形成し、この缶胴部の両端に別途製造された缶蓋を二
重巻締めされてなる溶接缶体が知られている。前記溶接
缶体では、基体金属である缶胴形成用表面処理鋼板と内
容物との接触により基体金属が腐食されたり溶出した金
属成分のために内容物のフレーバーが変化することを避
けるために缶内面側をエポキシ・フェノール樹脂等の塗
料を塗布して被覆する一方、缶外面側には所定の表示及
びデザイン等の画像を形成する塗装が施されて被覆され
ている。2. Description of the Related Art As a metal can body used for a container for beverages or the like, a can body part is formed by welding and joining both side edges of a can body blank obtained by cutting a can body forming surface-treated steel plate into a strip shape. There is known a welded can body that is formed by double-tightening a separately manufactured can lid on both ends of the can body. In the above-mentioned welded can body, in order to prevent the base metal from being corroded by the contact between the surface-treated steel sheet for forming a can body, which is the base metal, and the content of the contents being changed due to the eluted metal component, the can is used. The inner surface is coated with a coating material such as epoxy / phenolic resin, while the outer surface of the can is coated with a coating for forming an image such as a predetermined display and design.
【０００３】従来、前記溶接缶体の缶胴形成用表面処理
鋼板の内外面側に対する前記塗装は、前記塗料を塗布す
るごとに加熱オーブンで焼き付けをすることにより行な
われている。前記塗装をこのようにして行うときには、
加熱オーブンの熱と揮散する有機溶媒とにより作業環境
が害される傾向があり、特に多色印刷となる外面側で
は、２〜４色の塗装を施すごとに加熱オーブンによる焼
き付けを行なうため、前記傾向が強くなる。Conventionally, the coating of the inner and outer surfaces of the surface-treated steel plate for forming a can body of the welded can is performed by baking in a heating oven every time the coating material is applied. When performing the painting in this way,
The work environment tends to be impaired by the heat of the heating oven and the organic solvent that volatilizes, and in particular, on the outer surface side where multicolor printing is performed, baking is performed by the heating oven every time 2 to 4 colors are applied. Becomes stronger.
【０００４】そこで、缶胴形成用表面処理鋼板の缶内外
面側をポリエステルフィルムで被覆して保護被覆層を形
成することが検討されている。このようにして保護被覆
層を形成するときに、缶外面側を被覆するポリエステル
フィルムに予め印刷を施して所定の表示及びデザイン等
の画像を形成しておけば、前記ポリエステルフィルムか
らなる保護被覆層により缶外面側に塗装によらずに所定
の表示及びデザイン等の画像による美粧性を付与するこ
とができ、塗装及び焼き付けを行わずに溶接缶体が得ら
れるので、作業環境の向上が期待される。Therefore, it has been studied to form a protective coating layer by coating the inside and outside surfaces of the can of the surface-treated steel sheet for forming a can body with a polyester film. When the protective coating layer is formed in this way, if the polyester film coating the outer surface of the can is printed in advance to form an image such as a predetermined display and design, the protective coating layer made of the polyester film is formed. With this, it is possible to add beauty to the outer surface of the can with images such as predetermined display and design without painting, and a welded can can be obtained without painting and baking, so it is expected to improve the working environment. It
【０００５】前記缶外面側を被覆するポリエステルフィ
ルムとして、特開平５−９６６２７号公報に記載されて
いるもののように、その一方の面に熱硬化型樹脂系接着
剤層を設け、該ポリエステルフィルムと該熱硬化型樹脂
系接着剤層との間に顔料を含む樹脂組成物からなる印刷
層が設けられてなるポリエステルフィルムが知られてい
る。前記公報記載のポリエステルフィルムによれば、前
記熱硬化型樹脂系接着剤層を介して缶胴形成用表面処理
鋼板に熱接着することにより、高温で短時間の加熱によ
り缶胴形成用表面処理鋼板との間で優れた接着強度を得
ることができると共に、前記印刷層により所定の表示及
びデザイン等の画像を形成することができる。前記画像
は、缶胴形成用表面処理鋼板に美粧性を付与する点か
ら、特殊な色調を有することが望ましい。As the polyester film for coating the outer surface of the can, as described in JP-A-5-96627, a thermosetting resin adhesive layer is provided on one surface of the polyester film, A polyester film is known in which a printing layer made of a resin composition containing a pigment is provided between the thermosetting resin adhesive layer and the thermosetting resin adhesive layer. According to the polyester film described in the above publication, by heat-bonding to the surface-treated steel sheet for forming a can body through the thermosetting resin-based adhesive layer, the surface-treated steel sheet for forming a body can be heated at high temperature for a short time. It is possible to obtain excellent adhesive strength between the above and the above, and it is possible to form an image such as a predetermined display and design by the printing layer. It is desirable that the image has a special color tone from the viewpoint of imparting aesthetic appeal to the surface-treated steel sheet for forming a can body.
【０００６】しかしながら、前記ポリエステルフィルム
を缶胴形成用表面処理鋼板に熱接着する際に、金属下地
上に前記熱硬化型樹脂系接着剤層を介して接着すると、
前記印刷層の色調が前記金属下地の色調に支配され、前
記所定の表示及びデザインの画像に特殊な色調が得られ
ないとの不都合がある。However, when the polyester film is heat-bonded to the surface-treated steel sheet for forming a can body, if it is bonded to the metal substrate via the thermosetting resin adhesive layer,
There is an inconvenience that the color tone of the printed layer is dominated by the color tone of the metal base, and a special color tone cannot be obtained in the image of the predetermined display and design.
【０００７】[0007]
【発明が解決しようとする課題】そこで本発明は、上記
課題を解決するためになされたものであり、缶体材料用
金属板の缶外面側をポリエステルフィルムで被覆して保
護被覆層を形成する際に、前記所定の表示及びデザイン
の画像にメタリック感を有する特殊な色調を付与するこ
とができる缶体材料被覆用ポリエステルフィルム及びこ
のポリエステルフィルムを用いる美粧性に優れた溶接缶
体を提供することを目的とする。SUMMARY OF THE INVENTION Therefore, the present invention has been made to solve the above problems, and the outer surface side of a metal plate for a can body material is coated with a polyester film to form a protective coating layer. In this case, to provide a polyester film for coating a can body material capable of imparting a special color tone having a metallic feeling to the image of the predetermined display and design, and a welded can body using the polyester film and having excellent cosmetic properties. With the goal.
【０００８】[0008]
【課題を解決するための手段】前記目的を達成するため
に、本発明の缶体材料被覆用ポリエステルフィルムは、
缶体材料用金属板に熱硬化型樹脂系接着剤を介して加熱
接着されて保護被覆層を形成するポリエステルフィルム
であって、該ポリエステルフィルムの一方の面に顔料を
含む樹脂組成物からなる第１の印刷層が設けられ、該第
１印刷層上に金属粉末が分散された樹脂組成物からなる
第２の印刷層が設けられ、該第２の印刷層上に、熱硬化
型樹脂系接着剤層が設けられていることを特徴とする。In order to achieve the above object, the polyester film for coating a can body material of the present invention comprises:
A polyester film which is heat-bonded to a metal plate for a can body material via a thermosetting resin adhesive to form a protective coating layer, the polyester film comprising a resin composition containing a pigment on one surface of the polyester film. No. 1 printing layer is provided, a second printing layer made of a resin composition in which metal powder is dispersed is provided on the first printing layer, and a thermosetting resin-based adhesive is provided on the second printing layer. It is characterized in that an agent layer is provided.
【０００９】前記第１及び第２印刷層を形成する樹脂組
成物としては、エポキシブチラール系樹脂とポリイソシ
アネート系樹脂とからなる樹脂組成物、またはポリエス
テルポリウレタン樹脂とポリイソシアネート系樹脂とか
らなる樹脂組成物を用いることが好ましい。溶接缶体で
は、内容物を充填したのち、加熱殺菌処理（レトルト殺
菌処理）が行われるのが通常であるが、ポリエステルフ
ィルムと熱硬化型樹脂系接着剤層との間に顔料を含む樹
脂組成物からなる印刷層が設けられてなるポリエステル
フィルムにより保護被覆層を形成した缶体材料用金属板
から形成してなる溶接缶体に前記レトルト処理を施す
と、前記印刷層が白化し該印刷層により形成される所定
の表示及びデザイン等の画像が不明瞭になることがあ
る。しかし、前記第１及び第２印刷層が前記エポキシブ
チラール系樹脂とポリイソシアネート系樹脂とから、ま
たはポリエステルポリウレタン樹脂とポリイソシアネー
ト系樹脂とからなる樹脂組成物により形成されているこ
とにより、前記缶体材料被覆用ポリエステルフィルムに
より保護被覆層を形成した缶体材料用金属板から形成し
てなる溶接缶体に前記レトルト処理を施しても、前記印
刷層に白化を生じず、鮮明な画像が得られるので好まし
い。The resin composition forming the first and second printing layers is a resin composition comprising an epoxy butyral resin and a polyisocyanate resin, or a resin composition comprising a polyester polyurethane resin and a polyisocyanate resin. It is preferable to use a product. In the welding can, after the contents are filled, heat sterilization treatment (retort sterilization treatment) is usually performed, but a resin composition containing a pigment between the polyester film and the thermosetting resin adhesive layer. When the retort treatment is applied to a welding can body formed of a metal plate for a can body material having a protective coating layer formed of a polyester film having a printed layer made of a material, the print layer becomes white The image such as a predetermined display and design formed by may become unclear. However, since the first and second printing layers are formed of the epoxy butyral resin and the polyisocyanate resin or the resin composition of the polyester polyurethane resin and the polyisocyanate resin, the can body is formed. Even when the retort treatment is applied to a welding can body formed of a metal plate for a can body material in which a protective coating layer is formed with a polyester film for material coating, the printed layer does not whiten and a clear image is obtained. Therefore, it is preferable.
【００１０】前記第２印刷層を形成する樹脂組成物に分
散される金属粉末としては、アルミニウム、亜鉛、真
鍮、ステンレス等の粉末を挙げることができるが、優れ
たメタリック感を有する色調を付与するために平均粒径
１０〜１００μｍ、厚さ０．１〜２μｍの銀色の金属光
沢を有する鱗片状アルミニウム粉末が好ましい。Examples of the metal powder dispersed in the resin composition forming the second printing layer include powders of aluminum, zinc, brass, stainless steel and the like, which impart a color tone having an excellent metallic feeling. Therefore, a scaly aluminum powder having an average particle diameter of 10 to 100 μm and a thickness of 0.1 to 2 μm and having a silver metallic luster is preferable.
【００１１】前記第２印刷層を形成する樹脂組成物は前
記アルミニウム粉末が１７〜２５重量％の範囲で分散さ
れていることにより、前記ポリエステルフィルムが前記
缶体材料用金属板に加熱接着されてなる保護被覆層に形
成される所定の表示及びデザイン等の画像に特に優れた
メタリック感を有する色調を付与することができる。前
記樹脂組成物に分散されているアルミニウム粉末が１７
重量％未満のときには前記所定の表示及びデザイン等の
画像にメタリック感が得られないことがあり、２５重量
％を超えてもメタリック感を付与する効果はそれ以上に
は得られない。In the resin composition forming the second printing layer, the aluminum powder is dispersed in the range of 17 to 25% by weight, so that the polyester film is heat-bonded to the metal plate for can body material. It is possible to impart a color tone having a particularly excellent metallic feeling to an image such as a predetermined display and design formed on the protective coating layer. The aluminum powder dispersed in the resin composition is 17
When the amount is less than 25% by weight, metallic images may not be obtained in the image such as the predetermined display and design, and when the amount is more than 25% by weight, the effect of giving metallic feeling is not further obtained.
【００１２】前記缶体材料被覆用ポリエステルフィルム
は、強度及び透明性等に優れているものであって、ジカ
ルボン酸成分とジオール成分との重縮合により得られる
ポリエステルであればどのようなものであってもよい
が、ナフタレンジカルボン酸、テレフタル酸、イソフタ
ル酸等の芳香族ジカルボン酸と、エチレングリコール、
プロピレングリコール、ブチレングリコール等のジオー
ル類との重縮合により得られるポリエステルであること
が好ましく、ナフタレンジカルボン酸とエチレングリコ
ールとの重縮合により得られるポリエステル（ポリエチ
レンナフタレート）またはテレフタル酸とエチレングリ
コールとの重縮合により得られるポリエステル（ポリエ
チレンテレフタレート）であることが特に好ましい。The polyester film for covering the can body material is excellent in strength and transparency, and may be any polyester as long as it is obtained by polycondensation of a dicarboxylic acid component and a diol component. However, aromatic dicarboxylic acids such as naphthalene dicarboxylic acid, terephthalic acid and isophthalic acid, ethylene glycol,
A polyester obtained by polycondensation with diols such as propylene glycol and butylene glycol is preferred, and a polyester obtained by polycondensation of naphthalene dicarboxylic acid and ethylene glycol (polyethylene naphthalate) or terephthalic acid and ethylene glycol A polyester (polyethylene terephthalate) obtained by polycondensation is particularly preferable.
【００１３】前記ポリエステルは、所望に応じて前記ジ
カルボン酸成分またはジオール成分に他のジカルボン酸
成分またはジオール成分を含んでいてもよい。ポリエチ
レンテレフタレートの他の前記好ましいポリエステルと
しては、特開昭５１─４２７８６号、特開昭６４─７０
３５２号、特開平２─２４２７３８号等の各公報に記載
されているポリエステルを挙げることができる。The polyester may contain other dicarboxylic acid component or diol component in the dicarboxylic acid component or diol component, if desired. Other preferable polyesters other than polyethylene terephthalate are JP-A-51-42786 and JP-A-64-70.
Examples thereof include polyesters described in JP-A No. 352, JP-A-2-242738 and the like.
【００１４】前記ポリエステルフィルムは、後述の熱硬
化型樹脂系接着剤による接着力を向上させるために、前
記接着剤層が形成される面に予めコロナ放電等の表面酸
化処理が施されていることが好ましい。In the polyester film, the surface on which the adhesive layer is formed is subjected to surface oxidation treatment such as corona discharge in advance in order to improve the adhesive force by the thermosetting resin adhesive described later. Is preferred.
【００１５】また、前記ポリエステルフィルムは５〜５
０μｍの範囲の厚さを有することが好ましい。前記ポリ
エステルフィルムの厚さが５μｍ以下であるときには、
該フィルムの保護被覆層が形成された缶体材料用金属板
を溶接缶体に加工するときに、該フィルムが傷付きやす
く、ピンホール等が発生して、缶体の腐食、金属の溶出
を防止する効果が十分に得られないことがある。また、
５０μｍ以上のときには残留応力が大きくなり、溶接缶
体に加工するときに缶胴部にネックイン加工等の絞り加
工を施すと、前記ポリエステルフィルムの前記缶体材料
用金属板に対する密着性が低下する傾向がある。The polyester film is 5 to 5
It preferably has a thickness in the range of 0 μm. When the thickness of the polyester film is 5 μm or less,
When a metal plate for a can body material on which a protective coating layer of the film is formed is processed into a welded can body, the film is easily scratched, pin holes are generated, and corrosion of the can body and elution of metal are prevented. The prevention effect may not be sufficiently obtained. Also,
When the thickness is 50 μm or more, the residual stress becomes large, and when the can body is subjected to a drawing process such as a neck-in process when it is processed into a welded can body, the adhesion of the polyester film to the metal plate for a can body material deteriorates. Tend.
【００１６】さらに、前記ポリエステルフィルムは、前
記第１及び第２印刷層を設けるための強度及び前記缶体
材料用金属板に接着される際の熱処理に対する寸法安定
性が要求されるので、ポリエチレンナフタレート等の耐
熱性ポリエステルフィルム、一軸または二軸延伸された
ポリエチレンテレフタレートフィルム等が好ましく、特
に、材料物性的には１５０℃に３０分保持したときの長
手方向の熱収縮率が１．２％以下、幅方向の熱収縮率が
０％の二軸延伸ポリエステルフィルムが好ましい。Further, the polyester film is required to have strength for providing the first and second printing layers and dimensional stability against heat treatment when it is adhered to the metal plate for a can body material. A heat-resistant polyester film such as phthalate, a uniaxially or biaxially stretched polyethylene terephthalate film, etc. are preferable, and in particular, the physical properties of the material have a heat shrinkage ratio of 1.2% or less in the longitudinal direction when kept at 150 ° C. for 30 minutes. A biaxially stretched polyester film having a heat shrinkage ratio of 0% in the width direction is preferable.
【００１７】前記ポリエステルフィルムは、前記寸法安
定性を確保するために、予め１６０℃で６秒間程度保持
する熱処理を施してもよいが、前記接着剤層が設けられ
ている面の反対側に熱硬化型樹脂からなる硬化オーバー
コート層が設けられていることが特に好ましい。前記硬
化オーバーコート層を設けることにより、前記ポリエス
テルフィルムの残留応力が緩和されると共にフィルムの
伸縮が規制され前記寸法安定性が確保されるとともに、
耐傷付性が向上される。また、前記硬化オーバーコート
層を設けることにより、前記缶体材料被覆用ポリエステ
ルフィルムにより保護被覆層を形成した缶体材料用金属
板から形成してなる溶接缶体に前記レトルト殺菌処理等
の加熱処理を施す際にポリエステルフィルム中の低重合
度成分（オリゴマー）が表面に析出することが防止され
る。また、滑り性がよくなる。The polyester film may be preliminarily heat-treated at 160 ° C. for about 6 seconds in order to secure the dimensional stability, but the polyester film may be heated on the side opposite to the surface on which the adhesive layer is provided. It is particularly preferable that a cured overcoat layer made of a curable resin is provided. By providing the cured overcoat layer, the residual stress of the polyester film is relaxed and the expansion and contraction of the film is regulated to secure the dimensional stability, and
Scratch resistance is improved. Further, by providing the cured overcoat layer, a heating treatment such as the retort sterilization treatment is performed on a welding can body formed of a metal plate for a can body material having a protective coating layer formed by the polyester film for coating the can body material. It is possible to prevent the low-polymerization degree component (oligomer) in the polyester film from being deposited on the surface during the treatment. Also, the slipperiness is improved.
【００１８】前記硬化オーバーコート層を形成する熱硬
化型樹脂は、高温短時間で硬化フィルムを形成する樹脂
であることが好ましく、例えば、エポキシ樹脂とアミノ
プラスト樹脂とからなり短時間硬化触媒として有機酸ま
たはリン酸、ポリリン酸等の無機酸が添加されているも
のが適している。前記熱硬化型樹脂は、耐傷付性の向
上、滑り性向上のために、シリコン或はワックスが添加
されていることが好ましい。The thermosetting resin forming the cured overcoat layer is preferably a resin capable of forming a cured film at high temperature in a short time. For example, it is composed of an epoxy resin and an aminoplast resin and is used as an organic catalyst for a short time curing. Those to which an acid or an inorganic acid such as phosphoric acid or polyphosphoric acid is added are suitable. Silicon or wax is preferably added to the thermosetting resin in order to improve scratch resistance and slidability.
【００１９】前記缶体材料用金属板は、缶体用各種表面
処理鋼板、缶体用各種アルミニウム合金板などを用いる
ことができる。As the metal plate for a can body material, various surface-treated steel plates for a can body, various aluminum alloy plates for a can body can be used.
【００２０】前記熱硬化型樹脂系接着剤層は、数平均分
子量５０００〜２００００のエポキシ樹脂と酸無水物系
硬化剤とを７０／３０〜９９／１の重量比で含む樹脂ま
たはポリエステル樹脂とアミノプラスト樹脂とを７０／
３０〜９０／１０の重量比で含む樹脂からなるものを用
いることにより、高温で短時間の加熱で、前記缶体材料
被覆用ポリエステルフィルムと前記缶体材料用金属板と
の間で十分な接着強度を得ることができる。The thermosetting resin adhesive layer contains a resin or polyester resin containing an epoxy resin having a number average molecular weight of 5000 to 20000 and an acid anhydride curing agent in a weight ratio of 70/30 to 99/1, and an amino acid. 70 / with plast resin
By using a resin containing a weight ratio of 30 to 90/10, sufficient adhesion between the polyester film for coating the can body material and the metal plate for the can body material can be achieved by heating at high temperature for a short time. Strength can be obtained.
【００２１】前記接着剤層がエポキシ樹脂と酸無水物系
硬化剤とからなるときには、前記エポキシ樹脂は数平均
分子量が５０００未満のときには接着強度が不足し、２
００００を超えるときには高粘度となり塗布作業性が劣
るので、共に好ましくない。また、前記数平均分子量が
５０００未満であると、前記ポリエステルフィルムに予
め塗布乾燥して接着剤層を形成するときに、前記接着剤
層の粘着性が高くなり、タックフリー性が低下する。When the adhesive layer is composed of an epoxy resin and an acid anhydride-based curing agent, the epoxy resin has insufficient adhesive strength when the number average molecular weight is less than 5000, and
When it exceeds 0000, the viscosity is high and the coating workability is poor, so both are not preferable. Further, when the number average molecular weight is less than 5,000, when the polyester film is coated and dried in advance to form an adhesive layer, the adhesive layer has high tackiness and a low tack-free property.
【００２２】前記接着剤層において、前記エポキシ樹脂
と前記酸無水物系硬化剤との重量比が９９／１未満では
高温で加熱しても前記エポキシ樹脂の硬化に長時間を要
し、また７０／３０を超える割合としても前記エポキシ
樹脂の硬化を促進する効果はそれ以上には向上されな
い。In the adhesive layer, if the weight ratio of the epoxy resin to the acid anhydride type curing agent is less than 99/1, it takes a long time to cure the epoxy resin even if it is heated at a high temperature. Even if the ratio exceeds / 30, the effect of promoting the curing of the epoxy resin is not further improved.
【００２３】前記酸無水物系硬化剤としては、無水ピロ
メリット酸、ベンゾフェノンテトラカルボン酸無水物、
無水フタル酸、テトラヒドロ無水フタル酸、メチルシク
ロヘキサンジカルボン酸無水物、無水トリメリット酸及
びその誘導体等を挙げることができるが、硬化性、塗布
後の膜の耐ブロッキング性、タックフリー性等に優れて
いる点から無水トリメリット酸及びその誘導体からなる
無水トリメリット酸系硬化剤が適している。無水トリメ
リット酸の誘導体としては、例えば、グリセロールトリ
ストリメリテート無水物、無水トリメリット酸の二量
体、エチレングリコールビストリメリテート無水物等を
挙げることができる。Examples of the acid anhydride type curing agent include pyromellitic dianhydride, benzophenone tetracarboxylic acid anhydride,
Examples thereof include phthalic anhydride, tetrahydrophthalic anhydride, methylcyclohexanedicarboxylic acid anhydride, trimellitic acid anhydride and its derivatives, but they are excellent in curability, blocking resistance of the film after coating, tack-free property, etc. Therefore, trimellitic anhydride-based curing agents composed of trimellitic anhydride and its derivatives are suitable. Examples of the trimellitic anhydride derivative include glycerol tris trimellitate anhydride, trimeric anhydride dimer, and ethylene glycol bis trimellitate anhydride.
【００２４】前記接着剤層を形成するエポキシ樹脂は、
ビスフェノールとエピクロルヒドリンとの反応により得
られるビスフェノール型エポキシ樹脂であることが好ま
しく、前記酸無水物系硬化剤以外にさらにフェノール樹
脂などの他の硬化剤を含んでいてもよい。The epoxy resin forming the adhesive layer is
The bisphenol type epoxy resin obtained by the reaction of bisphenol and epichlorohydrin is preferable, and other curing agent such as phenol resin may be contained in addition to the acid anhydride curing agent.
【００２５】また、前記接着剤層がポリエステル樹脂と
アミノプラスト樹脂とからなるときには、その重量比が
９０／１０未満では高温で加熱しても該接着剤層の硬化
に長時間を要し、また７０／３０を超える割合とすると
硬化が進みすぎ、該接着剤層の加工性が低下するので好
ましくない。前記ポリエステル樹脂としては、公知のポ
リエステル樹脂を単独で用いてもよく、エポキシ樹脂等
で変性したエポキシ変性ポリエステル樹脂を用いてもよ
い。また、前記アミノプラスト樹脂としては、メラミン
樹脂、ベンゾグアナミン樹脂等を用いることができる。
また、前記接着剤層は、ポリエステル樹脂及びアミノプ
ラスト樹脂とともに、エポキシ樹脂を併用しても差し支
えない。When the adhesive layer is composed of polyester resin and aminoplast resin, if the weight ratio is less than 90/10, it takes a long time to cure the adhesive layer even if heated at high temperature. If the ratio exceeds 70/30, the curing will proceed excessively and the workability of the adhesive layer will be deteriorated, which is not preferable. As the polyester resin, a known polyester resin may be used alone, or an epoxy-modified polyester resin modified with an epoxy resin or the like may be used. As the aminoplast resin, melamine resin, benzoguanamine resin, or the like can be used.
Further, the adhesive layer may use an epoxy resin together with the polyester resin and the aminoplast resin.
【００２６】前記接着剤層を形成する樹脂組成物は、高
温で短時間の加熱で、前記缶体材料被覆用ポリエステル
フィルムと前記缶体材料用金属板との間で十分な接着強
度を得るために、前記第１及び第２印刷層を形成する樹
脂の種類に応じて選択的に使用されることが好ましい。
即ち、前記第１及び第２印刷層を形成する樹脂組成物
が、エポキシブチラール系樹脂とポリイソシアネート系
樹脂とからなり顔料を含みまたは前記金属粉末が分散さ
れた樹脂組成物であるときには、前記接着剤層は前記平
均分子量のエポキシ樹脂と酸無水物系硬化剤とを前記重
量比で含む樹脂または前記ポリエステル樹脂とアミノプ
ラスト樹脂とを前記重量比で含む樹脂からなることが適
している。また、前記第１及び第２印刷層を形成する樹
脂組成物が、ポリエステルポリウレタン樹脂とポリイソ
シアネート系樹脂とからなり顔料を含みまたは前記金属
粉末が分散された樹脂組成物であるときには、前記接着
剤層は前記ポリエステル樹脂とアミノプラスト樹脂とを
前記重量比で含む樹脂からなることが適している。In order to obtain sufficient adhesive strength between the polyester film for coating the can body material and the metal plate for the can body material, the resin composition forming the adhesive layer is heated at a high temperature for a short time. In addition, it is preferably used selectively depending on the type of resin forming the first and second printing layers.
That is, when the resin composition forming the first and second printed layers is a resin composition containing an epoxy butyral-based resin and a polyisocyanate-based resin and containing a pigment or the metal powder is dispersed, Suitably, the agent layer is made of a resin containing the epoxy resin of the average molecular weight and an acid anhydride-based curing agent in the weight ratio, or a resin containing the polyester resin and the aminoplast resin in the weight ratio. Further, when the resin composition forming the first and second printing layers is a resin composition containing a polyester polyurethane resin and a polyisocyanate resin and containing a pigment, or the metal powder is dispersed, the adhesive agent is used. Suitably, the layer comprises a resin containing the polyester resin and aminoplast resin in the weight ratio.
【００２７】本発明の溶接缶体は、缶体材料用金属板の
缶胴部外面側に対し、その両側端縁部を除いた部分に、
前記缶体材料被覆用ポリエステルフィルムを前記接着剤
層を介して加熱接着して保護被覆層を形成し、該金属板
の両側端縁部を重ね合せて溶接接合することにより缶胴
部を形成してなることを特徴とする。The welded can body of the present invention is a metal plate for a can body material, on the outer surface side of the can body portion, excluding both side edge portions,
The polyester film for coating the can body material is heat-bonded via the adhesive layer to form a protective coating layer, and both end edges of the metal plate are overlapped and welded to form a can body. It is characterized by
【００２８】前記溶接缶体は、缶胴部内面側にもポリエ
ステルフィルムからなる保護被覆層が形成されていても
よい。缶胴部内面側に保護被覆層を形成するポリエステ
ルフィルムとしては、前記外面側に保護被覆層を形成す
るポリエステルフィルムと同様の熱硬化型樹脂系接着剤
層が一方の面に設けられているポリエステルフィルムが
挙げられる。尚、このようなポリエステルフィルムは、
無地でよく、印刷層を設ける必要がないので、前記外面
側に保護被覆層を形成するポリエステルフィルムのよう
な強度、寸法安定性などが厳格には要求されない。従っ
て、延伸されていないポリエステルフィルムであっても
よく、一軸または二軸延伸されたポリエステルフィルム
であってもよいが、缶体材料用金属板を被覆する工程へ
の適性、缶体となったときの缶品質の面からポリエチレ
ンテレフタレートフィルムが適している。The welded can may have a protective coating layer made of a polyester film on the inner surface of the can body. As the polyester film forming the protective coating layer on the inner surface side of the can body, a polyester having a thermosetting resin adhesive layer similar to the polyester film forming the protective coating layer on the outer surface side is provided on one surface. Examples include films. Incidentally, such a polyester film,
Since it may be plain and a printing layer need not be provided, the strength and dimensional stability of the polyester film for forming a protective coating layer on the outer surface side are not strictly required. Therefore, it may be an unstretched polyester film or a uniaxially or biaxially stretched polyester film, but it is suitable for the step of coating a metal plate for a can body material, when it becomes a can body. Polyethylene terephthalate film is suitable from the viewpoint of can quality.
【００２９】[0029]
【作用】本発明の缶体材料被覆用ポリエステルフィルム
は、その一方の面に設けられた前記接着剤層により缶体
材料用金属板に加熱接着されて保護被複層を形成すると
きに、該ポリエステルフィルムに設けられている第１及
び第２印刷層により前記缶胴形成用金属板の缶外面側に
塗装によらずに所定の表示及びデザインの画像が形成さ
れる。このとき、第１印刷層と前記缶体材料用金属板の
金属下地との間に金属粉末が分散された樹脂組成物から
なる第２印刷層が介在するので、第１及び第２印刷層の
印刷が前記金属下地の色調に支配されることなく、前記
第２印刷層により前記所定の表示及びデザインの画像に
優れたメタリック感を有する色調が付与される。また、
前記第１及び第２印刷層は、前記のようにポリエステル
フィルムと接着剤層との間に設けられるので、特に第１
印刷層が該ポリエステルフィルムにより遮蔽され外傷か
ら保護される。The polyester film for coating a can body material according to the present invention, when it is heat-bonded to the metal plate for a can body material by the adhesive layer provided on one surface thereof to form a protective multi-layer, The first and second printing layers provided on the polyester film form an image of a predetermined display and design on the outer surface side of the can body forming metal plate without coating. At this time, since the second printing layer made of the resin composition in which the metal powder is dispersed is interposed between the first printing layer and the metal base of the metal plate for a can body material, the first and second printing layers are The second printing layer imparts a color tone having an excellent metallic feeling to the image of the predetermined display and design without the printing being controlled by the color tone of the metal base. Also,
Since the first and second printing layers are provided between the polyester film and the adhesive layer as described above, the first and second printing layers are not particularly limited to the first and second printing layers.
The printed layer is shielded by the polyester film and protected from external damage.
【００３０】前記第２印刷層を形成する樹脂組成物は、
金属粉末としてアルミニウム粉末が１７〜２５重量％の
範囲で分散されていることにより、前記所定の表示及び
デザインの画像にさらに優れたメタリック感を有する色
調が付与される。The resin composition forming the second printing layer is
By dispersing the aluminum powder in the range of 17 to 25% by weight as the metal powder, a color tone having a more excellent metallic appearance is imparted to the image of the predetermined display and design.
【００３１】本発明の缶体材料被覆用ポリエステルフィ
ルムは、前記接着剤層が設けられている面の反対側に熱
硬化型樹脂からなる硬化オーバーコート層が設けられて
いることにより、缶体材料用金属板に前記接着剤層を介
して加熱接着される際に、前記ポリエステルフィルムの
残留応力が緩和されると共に伸縮が規制されるので熱処
理に対する寸法安定性が確保される。また、前記硬化オ
ーバーコート層により、前記ポリエステルフィルムを加
熱接着して前記保護被覆層を形成した缶体材料用金属板
から溶接缶体を形成したのち、前記レトルト殺菌処理等
の加熱処理を施す際に缶表面にポリエステルフィルム中
のオリゴマーの析出、フィルム表面の傷付きが防止さ
れ、缶表面の滑り性がよくなる。The polyester film for coating a can body material of the present invention has a cured overcoat layer made of a thermosetting resin on the side opposite to the surface on which the adhesive layer is provided. When the polyester film is heat-bonded to the metal plate via the adhesive layer, the residual stress of the polyester film is relaxed and the expansion and contraction thereof are restricted, so that the dimensional stability against heat treatment is secured. When the heat treatment such as the retort sterilization treatment is performed after the welding can body is formed from the metal plate for the can body material in which the polyester film is heat-bonded by the cured overcoat layer to form the protective coating layer. Further, the precipitation of oligomers in the polyester film on the can surface and the scratches on the film surface are prevented, and the slipperiness of the can surface is improved.
【００３２】また、本発明の溶接缶体によれば、前記缶
体材料被覆用ポリエステルフィルムでその缶外面側が被
覆され、前記所定の表示及びデザインの画像に優れたメ
タリック感を有する色調が付与された缶体材料用金属板
から缶胴部が形成されるので、該画像によりその缶胴部
外面側に優れた美粧性が得られる。Further, according to the welded can of the present invention, the outer surface of the can is coated with the polyester film for covering the can body material, and a color tone having an excellent metallic feeling is imparted to the image of the predetermined display and design. Since the can body is formed from the metal plate for a can body material, the image provides excellent external appearance on the outer surface of the can body.
【００３３】[0033]
【実施例】次に、添付の図面を参照しながら本発明につ
いてさらに詳しく説明する。図１は本実施例の缶体材料
被覆用ポリエステルフィルムの構成を示す説明的断面図
であり、図２は図１示の缶体材料被覆用ポリエステルフ
ィルムの保護被覆層が形成された金属板の構成を示す説
明的断面図であり、図３は図２示の金属板から形成され
る溶接缶体の缶胴部を示す説明的部分断面図である。The present invention will now be described in more detail with reference to the accompanying drawings. FIG. 1 is an explanatory cross-sectional view showing the structure of a polyester film for covering a can body material of this example, and FIG. 2 shows a metal plate having a protective coating layer of the polyester film for covering a can body material shown in FIG. FIG. 3 is an explanatory cross-sectional view showing the configuration, and FIG. 3 is an explanatory partial cross-sectional view showing a can body of a welding can body formed from the metal plate shown in FIG.
【００３４】まず、本実施例の缶体材料被覆用ポリエス
テルフィルムについて説明する。First, the polyester film for covering a can body material of this embodiment will be described.
【００３５】ポリエステルフィルム１は、溶接缶体の缶
胴形成用ブリキ板の缶外面側に接着されるポリエステル
フィルムであって、図１示のように、厚さ１２μｍの二
軸延伸ポリエチレンテレフタレート（以下、ポリエチレ
ンテレフタレートをＰＥＴと略記する）フィルム２の一
方の面に、顔料を含む印刷インキによりグラビア印刷が
施された第１印刷層３ａ、アルミニウム粉末を含むシル
バーインキによりグラビア印刷が施された第２印刷層３
ｂ、熱硬化型樹脂系接着剤からなる接着剤層４が設けら
れ、反対側の面には熱硬化型樹脂により形成された透明
な硬化オーバーコート層５が設けられている。The polyester film 1 is a polyester film adhered to the outer surface side of the tin plate for forming the can body of the welded can body, and as shown in FIG. 1, it has a thickness of 12 μm and is biaxially oriented polyethylene terephthalate (hereinafter referred to as “polyethylene terephthalate”). Polyethylene terephthalate is abbreviated as PET) On one surface of the film 2, a first printing layer 3a which is gravure-printed with a printing ink containing a pigment, a second printing layer 3a which is gravure-printing with a silver ink containing aluminum powder Print layer 3
b, an adhesive layer 4 made of a thermosetting resin adhesive is provided, and a transparent cured overcoat layer 5 made of a thermosetting resin is provided on the opposite surface.
【００３６】第１印刷層３ａは、エポキシブチラール樹
脂とポリイソシアネート系樹脂とからなり顔料を含む印
刷インキから形成されている。第１印刷層３ａは、缶外
面側に所定の表示及びデザインの画像を形成するため
に、所要の各色の顔料を含む前記印刷インキが１色ごと
にグラビア印刷により積層されて、多色印刷されてい
る。また、第２印刷層３ｂは、エポキシブチラール樹脂
とポリイソシアネート系樹脂とからなり２０重量％のア
ルミニウム粉末が分散されているシルバーインキから形
成されており、第１印刷層３ａ及び第２印刷層３ｂの厚
さが、乾燥後に約１μｍになるようにされている。そし
て、第１印刷層３ａ及び第２印刷層３ｂにより所定の表
示及びデザインの画像が形成されている。The first printing layer 3a is made of a printing ink containing an epoxy butyral resin and a polyisocyanate resin and containing a pigment. The first printing layer 3a is multi-color printed by stacking the printing inks containing the pigments of the respective required colors by gravure printing in order to form an image of a predetermined display and design on the outer surface side of the can. ing. The second printing layer 3b is made of silver ink in which 20% by weight of aluminum powder is dispersed, which is made of epoxy butyral resin and polyisocyanate resin. The first printing layer 3a and the second printing layer 3b Has a thickness of about 1 μm after drying. An image of a predetermined display and design is formed by the first printing layer 3a and the second printing layer 3b.
【００３７】接着剤層４は、ビスフェノールとエピクロ
ルヒドリンとの反応により得られるビスフェノール型エ
ポキシ樹脂で数平均分子量１００００のエポキシ樹脂と
無水トリメリット酸系硬化剤としてグリセロールトリス
トリメリテート無水物とを９５／５の重量比で含む熱硬
化型樹脂系接着剤から形成されている。接着剤層４は、
例えば、前記エポキシ樹脂とグリセロールトリストリメ
リテート無水物とを前記重量比で有機溶剤に溶解した樹
脂溶液を塗布し、接着剤の硬化反応が進行しないように
１２０℃で１０秒間の乾燥を行って前記熱硬化型樹脂系
接着剤の塗布量が２．５ｇ／ｍ2 になるようにして形成
される。尚、ＰＥＴフィルム２の接着剤層４が形成され
る面には、予めコロナ放電処理が施されていることが好
ましい。The adhesive layer 4 is a bisphenol type epoxy resin obtained by the reaction of bisphenol and epichlorohydrin with an epoxy resin having a number average molecular weight of 10,000 and glycerol tris trimellitate anhydride 95 / trimellitic anhydride curing agent. It is formed from a thermosetting resin-based adhesive containing a weight ratio of 5. The adhesive layer 4 is
For example, a resin solution prepared by dissolving the epoxy resin and glycerol tris trimellitate anhydride in an organic solvent in the above weight ratio is applied, and dried at 120 ° C. for 10 seconds so that the curing reaction of the adhesive does not proceed. The thermosetting resin adhesive is formed so that the coating amount is 2.5 g / m 2 . The surface of the PET film 2 on which the adhesive layer 4 is formed is preferably subjected to corona discharge treatment in advance.
【００３８】硬化オーバーコート層５は、エポキシ樹脂
とアミノプラスト樹脂とからなりリン酸触媒を添加した
熱硬化型樹脂により形成されている。また、硬化オーバ
ーコート層５は、ポリエステルフィルム１により保護被
覆層が形成された溶接缶体において、ポリエステルフィ
ルム１の耐傷付性向上及び前記溶接缶体表面の滑り性向
上のために、シリコンまたはワックスが添加されている
ことが好ましい。The cured overcoat layer 5 is formed of a thermosetting resin composed of an epoxy resin and an aminoplast resin to which a phosphoric acid catalyst is added. Further, the cured overcoat layer 5 is made of silicone or wax to improve the scratch resistance of the polyester film 1 and the slipperiness of the surface of the welding can body in the welding can body in which the protective coating layer is formed by the polyester film 1. Is preferably added.
【００３９】次に、本実施例のポリエステルフィルム１
を用いる溶接缶体について説明する。Next, the polyester film 1 of this embodiment
A welding can body using is explained.
【００４０】本実施例の溶接缶体は、図２示の缶胴形成
用ブリキ板１１から形成される。缶胴形成用ブリキ板１
１は、その缶外面となる側の両側端縁部１１ａ，１１ａ
を除いた部分に図１示のポリエステルフィルム１が接着
剤層４を介して熱接着されて保護被覆層１２が形成され
ている。また、ブリキ板１１の缶内面となる側の両側端
縁部１１ａ，１１ａを除いた部分には、透明なＰＥＴフ
ィルム１３がポリエステルフィルム１と同様の熱硬化型
樹脂系接着剤層１４を介して熱接着されて内面保護被覆
層１５が形成されている。The welding can body of this embodiment is formed from the tin plate 11 for forming a can body shown in FIG. Tin plate for can body 1
Reference numeral 1 denotes both side edge portions 11a, 11a on the outer surface of the can.
The polyester film 1 shown in FIG. 1 is heat-bonded via the adhesive layer 4 to the portion except for forming the protective coating layer 12. In addition, a transparent PET film 13 is formed on the part of the tin plate 11 excluding both side edge parts 11a, 11a on the inner surface of the can via a thermosetting resin adhesive layer 14 similar to the polyester film 1. The inner surface protective coating layer 15 is formed by heat bonding.
【００４１】ブリキ板１１はポリエステルフィルム１に
よりその缶外面側が被覆されているので、保護被覆層１
２に形成されている前記所定の表示及びデザインの画像
に、第２印刷層３ｂにより優れたメタリック感が付与さ
れている。Since the tin plate 11 is covered with the polyester film 1 on the outer surface side of the can, the protective coating layer 1
The second printed layer 3b imparts an excellent metallic feeling to the image of the predetermined display and design formed in No. 2.
【００４２】保護被覆層１２及び内面保護被覆層１５が
形成されたブリキ板１１は図２に矢示するように丸めら
れ、図３示のように両側端縁部１１ａ，１１ａを重ね合
わせて溶接接合することにより缶胴部１６が形成され
る。缶胴部１６の保護被覆層１２及び内面保護被覆層１
５が形成されていない部分には、公知の被覆補正塗料１
７により、被覆補正がなされる。そして、缶胴部１６の
両端縁部をネックイン加工、フランジ加工したのち、別
途製造された缶蓋を二重巻締めすることにより、溶接缶
体が得られる。前記溶接缶体は、その缶外面側が印刷が
施されたポリエステルフィルム１で被覆されて保護被覆
層１２が形成されているブリキ板１１から缶胴部１６が
形成されるので、保護被覆層１２に形成されている前記
所定の表示及びデザインの画像により缶胴部１６の外面
側に優れた美粧性が得られ、食缶、飲料缶等に好適に用
いられる。The tin plate 11 on which the protective coating layer 12 and the inner protective coating layer 15 are formed is rolled as shown by the arrow in FIG. 2, and both side edge portions 11a, 11a are overlapped and welded as shown in FIG. The can body 16 is formed by joining. Protective coating layer 12 of can body 16 and internal protective coating layer 1
In the part where 5 is not formed, the known coating correction paint 1
7, the covering correction is performed. Then, both end edges of the can body portion 16 are subjected to neck-in processing and flange processing, and then a separately manufactured can lid is double-wound to obtain a welded can body. In the welded can body, the can body portion 16 is formed from the tin plate 11 in which the outer surface side of the welded can is covered with the printed polyester film 1 and the protective cover layer 12 is formed. Due to the formed image of the predetermined display and design, excellent external appearance can be obtained on the outer surface side of the can body portion 16, and it can be suitably used for food cans, beverage cans and the like.
【００４３】溶接缶体では、通常、内容物を充填したの
ち、レトルト殺菌処理が行われるが、前記溶接缶体では
保護被覆層１２を形成するポリエステルフィルム１の第
２印刷層３ｂにおいて、前記シルバーインキを形成する
樹脂組成物がエポキシブチラール樹脂とポリイソシアネ
ート系樹脂を用いると、前記レトルト殺菌処理を行って
も前記第１及び第２印刷層に白化が生じることがない。
従って、前記所定の表示及びデザインに鮮明な画像が得
られる。In the welding can body, the retort sterilization treatment is usually performed after filling the contents, but in the welding can body, in the second printing layer 3b of the polyester film 1 forming the protective coating layer 12, the silver is used. When the resin composition forming the ink uses an epoxy butyral resin and a polyisocyanate-based resin, whitening does not occur in the first and second printing layers even if the retort sterilization treatment is performed.
Therefore, a clear image can be obtained in the predetermined display and design.
【００４４】尚、本実施例では前記各印刷層を形成する
樹脂組成物にエポキシブチラール樹脂とポリイソシアネ
ート系樹脂とからなる樹脂組成物を用いているが、ポリ
エステルポリウレタン樹脂とポリイソシアネート系樹脂
とからなる樹脂組成物を用いてもよく、この場合にも前
記レトルト殺菌処理の際に前記各印刷層に白化が生じる
ことがなく、前記所定の表示及びデザインに鮮明な画像
が得られる。In this embodiment, a resin composition comprising an epoxy butyral resin and a polyisocyanate resin is used as the resin composition for forming each of the printing layers, but a polyester polyurethane resin and a polyisocyanate resin are used. The resin composition may be used, and in this case also, a white image does not occur in each of the printing layers during the retort sterilization treatment, and a clear image can be obtained in the predetermined display and design.
【００４５】また、本実施例では、接着剤層４に数平均
分子量１００００のエポキシ樹脂と無水トリメリット酸
系硬化剤としてグリセロールトリストリメリテート無水
物とを９５／５の重量比で含む熱硬化型樹脂系接着剤を
用いているが、エポキシ樹脂の数平均分子量は５０００
〜２００００の範囲で、またエポキシ樹脂と酸無水物系
硬化剤との重量比は７０／３０〜９９／１の範囲で適宜
選択することができる。また、接着剤層４はポリエステ
ル樹脂とアミノプラスト樹脂とを７０／３０〜９０／１
０の重量比で含む熱硬化型樹脂系接着剤であってもよ
い。Further, in the present embodiment, the adhesive layer 4 is heat-cured by containing an epoxy resin having a number average molecular weight of 10,000 and glycerol tris trimellitate anhydride as a trimellitic anhydride curing agent in a weight ratio of 95/5. Type resin adhesive is used, but the number average molecular weight of epoxy resin is 5000
The weight ratio of the epoxy resin and the acid anhydride curing agent can be appropriately selected within the range of 70/30 to 99/1. The adhesive layer 4 contains a polyester resin and an aminoplast resin in a ratio of 70/30 to 90/1.
It may be a thermosetting resin-based adhesive containing a weight ratio of 0.
【００４６】また、接着剤層４はホワイト顔料を含むも
のであってもよい。接着剤層４がホワイト顔料を含むこ
とにより、缶胴形成用ブリキ板１１に接着された際に金
属下地が確実に遮蔽され、さらに優れたメタリック感が
得られる。The adhesive layer 4 may contain a white pigment. When the adhesive layer 4 contains the white pigment, the metal base is surely shielded when it is adhered to the tin plate 11 for forming a can body, and a more excellent metallic feeling is obtained.
【００４７】尚、本実施例では、ポリエステルフィルム
１による保護被覆層１２が形成されたブリキ板１１によ
り溶接缶体を形成しているが、ブリキ板１１は缶詰の
蓋、エアゾール缶の底蓋或はドーム状部等を形成するた
めに使用することもできる。In this embodiment, the welding can body is formed of the tin plate 11 on which the protective coating layer 12 of the polyester film 1 is formed, but the tin plate 11 is a can lid, a bottom lid of an aerosol can, or a tin lid. Can also be used to form domes and the like.
【００４８】[0048]
【発明の効果】以上のことから明らかなように、本発明
の缶体材料被覆用ポリエステルフィルムによれば、缶胴
材料用金属板に加熱接着されて保護被覆層を形成したと
きに、前記金属粉末が分散された樹脂組成物からなる第
２印刷層により金属下地の色調に支配されることなく、
所定の表示及びデザインに優れたメタリック感を有する
色調を付与することができる。As is apparent from the above, according to the polyester film for coating a can body material of the present invention, when the protective coating layer is formed by heat bonding to the metal plate for a can body material, the metal The second printing layer composed of the resin composition in which the powder is dispersed is not controlled by the color tone of the metal base,
It is possible to impart a color tone having an excellent metallic appearance to a predetermined display and design.
【００４９】また、前記第２印刷層がアルミニウム粉末
を１７〜２５重量％の範囲で含むことにより、さらに優
れたメタリック感を有する色調を付与することができ
る。When the second printing layer contains the aluminum powder in the range of 17 to 25% by weight, it is possible to impart a color tone having a more excellent metallic feeling.
【００５０】また、本発明の缶体材料被覆用ポリエステ
ルフィルムは、前記接着剤層が設けられている面の反対
側に熱硬化型樹脂からなる硬化オーバーコート層が設け
られているので、前記加熱接着の際の熱処理に対して寸
法安定性に優れているとともに、缶体を形成したときに
レトルト殺菌処理等の熱処理によるオリゴマーの析出を
防止することができ、さらに耐傷付性及び缶材、缶体の
滑り性を向上させることができる。In the polyester film for coating a can body material of the present invention, since a cured overcoat layer made of a thermosetting resin is provided on the side opposite to the surface provided with the adhesive layer, the above heating It has excellent dimensional stability against heat treatment during bonding, and can prevent precipitation of oligomers due to heat treatment such as retort sterilization treatment when forming a can body, and also has scratch resistance and can material, can. The slipperiness of the body can be improved.
【００５１】本発明の溶接缶体によれば、前記缶体材料
被覆用ポリエステルフィルムでその缶外面側が被覆さ
れ、前記所定の表示及びデザインの画像に優れたメタリ
ック感を有する色調が付与された缶体材料用金属板から
缶胴部が形成されるので、該画像によりその缶胴部外面
側に優れたた美粧性を得ることができる。According to the welded can body of the present invention, the can outer surface side is coated with the polyester film for coating the can body material, and the can having a color tone having an excellent metallic appearance on the image of the predetermined display and design is imparted. Since the body of the can is formed from the metal plate for body material, it is possible to obtain excellent aesthetic appearance on the outer surface side of the body of the can based on the image.
【図１】本発明に係わる缶体材料被覆用ポリエステルフ
ィルムの一構成例を示す説明的断面図。FIG. 1 is an explanatory cross-sectional view showing one structural example of a polyester film for covering a can body material according to the present invention.
【図２】図１示の缶体材料被覆用ポリエステルフィルム
の保護被覆層が形成された缶体材料用金属板の構成を示
す説明的断面図。2 is an explanatory cross-sectional view showing the structure of a metal plate for a can body material, on which a protective coating layer of the polyester film for a can body material shown in FIG. 1 is formed.
【図３】図２示の金属板から形成される溶接缶体の缶胴
部を示す説明的部分断面図。3 is an explanatory partial cross-sectional view showing a can body of a welding can body formed from the metal plate shown in FIG.
１…缶体材料被覆用ポリエステルフィルム、 ３ａ…第
１印刷層、３ｂ…第２印刷層、 ４…熱硬化型樹脂系接
着剤層、５…硬化オ−バーコート層、 １１…缶体材料
用金属板、１１ａ…側端縁部、 １２…保護被覆層、
１６…缶胴部。DESCRIPTION OF SYMBOLS 1 ... Polyester film for coating can body material, 3a ... 1st printing layer, 3b ... 2nd printing layer, 4 ... Thermosetting type resin adhesive layer, 5 ... Curing overcoat layer, 11 ... For can body material Metal plate, 11a ... Side edge portion, 12 ... Protective coating layer,
16 ... Can body.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ３２Ｂ 15/08 １０４ Ａ 7148−4Ｆ Ｂ６５Ｄ 8/22 Ｂ 9339−3Ｅ 25/36 7403−3Ｅ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display location B32B 15/08 104 A 7148-4F B65D 8/22 B 9339-3E 25/36 7403-3E
Claims (4)
を介して加熱接着されて保護被覆層を形成するポリエス
テルフィルムであって、該ポリエステルフィルムの一方
の面に顔料を含む樹脂組成物からなる第１の印刷層が設
けられ、該第１印刷層上に金属粉末が分散された樹脂組
成物からなる第２の印刷層が設けられ、該第２の印刷層
上に、熱硬化型樹脂系接着剤層が設けられていることを
特徴とする缶体材料被覆用ポリエステルフィルム。1. A polyester film which is heat-bonded to a metal plate for a can body material through a thermosetting resin adhesive to form a protective coating layer, and a resin containing a pigment on one surface of the polyester film. A first printing layer made of a composition is provided, a second printing layer made of a resin composition in which a metal powder is dispersed is provided on the first printing layer, and a heat A polyester film for coating a can body material, which is provided with a curable resin adhesive layer.
アルミニウム粉末が１７〜２５重量％の範囲で分散され
ていることを特徴とする請求項１記載の缶体材料被覆用
ポリエステルフィルム。2. A polyester film for coating a can body material according to claim 1, wherein aluminum powder is dispersed in the resin composition forming the second printing layer in a range of 17 to 25% by weight. .
が設けられている面の反対側に熱硬化型樹脂からなる硬
化オーバーコート層が設けられていることを特徴とする
請求項１記載の缶体材料被覆用ポリエステルフィルム。3. A can body according to claim 1, wherein a cured overcoat layer made of a thermosetting resin is provided on the side of the polyester film opposite to the surface provided with the adhesive layer. Polyester film for material coating.
その両側端縁部を除いた部分に、一方の面に顔料を含む
樹脂組成物からなる第１の印刷層が設けられ、該第１印
刷層上に金属粉末が分散された樹脂組成物からなる第２
の印刷層が設けられ、該第２の印刷層上に、熱硬化型樹
脂系接着剤層が設けられている缶体材料被覆用ポリエス
テルフィルムを該接着剤層を介して加熱接着して保護被
覆層を形成し、該金属板の両側端縁部を重ね合せて溶接
接合することにより缶胴部を形成してなることを特徴と
する溶接缶体。4. The outer surface side of the can body of the metal plate for can body material,
A first printing layer made of a resin composition containing a pigment is provided on one surface except the edge portions on both sides, and a resin composition in which a metal powder is dispersed on the first printing layer. Second
Is provided, and a thermosetting resin-based adhesive layer is provided on the second printed layer, and a polyester film for can body material coating is heat-bonded through the adhesive layer for protective coating. A welded can body, characterized in that a can body is formed by forming a layer and overlapping and welding both side edge portions of the metal plate.