JPH0742097A - Coated paper for decorative laminate - Google Patents
Coated paper for decorative laminateInfo
- Publication number
- JPH0742097A JPH0742097A JP19244393A JP19244393A JPH0742097A JP H0742097 A JPH0742097 A JP H0742097A JP 19244393 A JP19244393 A JP 19244393A JP 19244393 A JP19244393 A JP 19244393A JP H0742097 A JPH0742097 A JP H0742097A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- coating
- binder
- base paper
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、後に印刷を施し、さら
に必要により表面保護剤を塗布して、合板などの基材に
貼着して建材などに利用するための化粧板用コート紙に
関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a coated paper for a decorative sheet which is used for a building material or the like after printing, coating a surface protective agent if necessary, and adhering it to a substrate such as plywood. .
【０００２】[0002]
【従来の技術】この種の化粧板用紙としては、古くは薄
葉紙が用いられてきたが、近年では、原紙に樹脂を内添
し、紙の坪量を30ｇ／m2に高めた原紙が用いることも知
られてる。さらに、印刷時における隠蔽性を高めるため
に、二酸化チタンを添加することも知られている。2. Description of the Related Art As a veneer paper of this type, thin paper has been used for a long time, but in recent years, a base paper in which a resin is internally added to increase the basis weight of the paper to 30 g / m 2 is used. It is also known. Furthermore, it is also known to add titanium dioxide in order to enhance the hiding property during printing.
【０００３】一方、特開昭63−190092号および同63−19
0094号公報には、同様に抄造または抄造後に樹脂液を含
浸することが開示されている。On the other hand, Japanese Patent Laid-Open Nos. 63-190092 and 63-19
[0094] In the same manner, Japanese Patent Laid-Open Publication No. 1994-242242 discloses that papermaking or impregnation with a resin liquid after papermaking is performed.
【０００４】従来の化粧板用原紙に印刷を施した場合、
平滑性、表面強度、隠蔽性および印刷光沢の何れもが充
分でなく、さらに良好なこれらの特性を満足するコート
紙の開発が急がれていた。When a conventional base paper for a decorative board is printed,
All of the smoothness, surface strength, hiding power and printing gloss are not sufficient, and there has been an urgent need to develop coated papers that satisfy these characteristics.
【０００５】そこで、本発明者は、これらの要請に対し
て特開平４−３１４５３８号として、JIS P 8129で規定
された表面強度が11〜25Ａ、JIS P 8119で規定された平
滑度が400 秒以上、透気度が30〜80秒である原紙に、填
料、バインダーを含む塗料を塗工してその塗料中の樹脂
成分を原紙に浸透させ、これをカレンダー処理したもの
を開示し、かつ、ここに、塗料が、填料100 重量部に対
して、ＳＢＲラテックス14〜20重量部、エステル化デン
プン５重量部以下を含み、塗工量が片面単位で８〜25ｇ
／m2であるのが望ましいものと教示した。In order to meet these demands, the inventor of the present invention has disclosed that the surface strength defined by JIS P 8129 is 11 to 25 A and the smoothness defined by JIS P 8119 is 400 seconds as disclosed in JP-A-4-314538. As described above, a base paper having an air permeability of 30 to 80 seconds is coated with a coating material containing a filler and a binder, the resin component in the coating material is allowed to penetrate into the base paper, and a calendering treatment is performed on the base paper. The coating composition contains 14 to 20 parts by weight of SBR latex and 5 parts by weight or less of esterified starch per 100 parts by weight of the filler, and the coating amount is 8 to 25 g per one side.
/ M 2 was taught to be desirable.
【０００６】[0006]
【発明が解決しようとする課題】しかしながら、建材、
特に高級家具などについては、いわゆるクロスカット後
のテープ剥離強度（紙間強度）としてより高いものが望
まれているが、前記の先行技術においては、未だ充分で
なかった。[Problems to be Solved by the Invention] However, building materials,
Particularly for high-end furniture and the like, a higher so-called tape peeling strength (paper-to-paper strength) after cross-cut is desired, but the above-mentioned prior art is not yet sufficient.
【０００７】したがって、本発明の課題は、平滑性、隠
蔽性、印刷適性および印刷光沢度の何れにも優れ、特に
表面強度（紙間強度）が高い化粧板用コート紙を得るこ
とにある。Therefore, an object of the present invention is to obtain a coated paper for a decorative sheet which is excellent in smoothness, hiding power, printability and print gloss, and particularly has high surface strength (paper strength).
【０００８】[0008]
【課題を解決するための手段】上記課題は、JIS P 8129
で規定された表面強度が15Ａ〜32Ａ以下、JIS P 8119で
規定された平滑度が200 秒以上、透気度が30〜300 秒で
ある原紙に、填料、バインダーを含む塗料を塗工してそ
の塗料中の樹脂成分を原紙に浸透させ、これをカレンダ
ー処理したものであり、さらに前記このバインダーとし
てＳＢＲラテックスおよびポリビニルアルコールのうち
少なくともポリビニルアルコールを含み、これらの填料
100 重量部に対する重量割合が、図１の領域Ｘ内にあ
り、塗工量が片面単位で８〜25ｇ／m2であることが解決
できる。[Means for Solving the Problems] The above-mentioned problems are based on JIS P 8129.
A coating containing a filler and a binder is applied to a base paper having a surface strength of 15 A to 32 A or less, a smoothness of 200 seconds or more, and an air permeability of 30 to 300 seconds specified by JIS P 8119. The resin component in the paint is permeated into the base paper and calendered, and the binder further contains at least polyvinyl alcohol out of SBR latex and polyvinyl alcohol.
It can be solved that the weight ratio with respect to 100 parts by weight is within the region X in FIG. 1 and the coating amount is 8 to 25 g / m 2 per one side.
【０００９】[0009]
【作用】本発明では、塗料中のバインダーとして少なく
ともポリビニルアルコール（ＰＶＡという）を用いる。
また、ＳＢＲラテックスを併用することは有効である。In the present invention, at least polyvinyl alcohol (referred to as PVA) is used as the binder in the paint.
In addition, it is effective to use SBR latex together.
【００１０】これによって、高い原紙の表面強度と相俟
って、最終的に化粧板用コート紙を得た場合におけるク
ロスカット後のテープ剥離強度（紙間強度）を著しく高
めることができる。したがって、高級家具用途に適用し
た場合において、テープ剥離を確実に防止できるなどの
利点がもたらされる。また、バインダーとしてのＳＢＲ
ラテックスとＰＶＡとの配合割合が図１の領域Ｘ内にあ
るために、クロスカット後のテープ剥離強度のみなら
ず、塗工を円滑に行うことができる。With this, in combination with the high surface strength of the base paper, the tape peeling strength (paper-to-paper strength) after cross cutting in the case of finally obtaining the coated paper for decorative sheet can be significantly increased. Therefore, when applied to high-end furniture applications, there are advantages such as the ability to reliably prevent tape peeling. In addition, SBR as a binder
Since the mixing ratio of the latex and PVA is within the area X in FIG. 1, not only the tape peeling strength after cross cutting but also the coating can be smoothly performed.
【００１１】[0011]
【実施例】以下本発明をさらに詳説する。本発明者は、
所定の特性を有する原紙に、填料を含む塗料を塗工する
ことが、特に印刷適性に優れる。The present invention will be described in more detail below. The inventor
It is particularly excellent in printability to apply a paint containing a filler to a base paper having predetermined properties.
【００１２】さらに、この場合、原紙として要求される
のは、特に表面強度、平滑度および透気度である。Furthermore, in this case, the requirements for the base paper are, in particular, surface strength, smoothness and air permeability.
【００１３】表面強度および平滑度は、JIS P 8129およ
びJIS P 8119で規定されている。表面強度としては、15
A 〜32Ａとされ、より好ましくは23Ａ以上、特に好まし
くは25Ａ以上とされる。化粧板は、その表面に粘着テー
プを長時間貼着した後、そのテープを剥がすことがあ
り、主にこのために表面強度が高いことが望まれる。The surface strength and smoothness are specified in JIS P 8129 and JIS P 8119. The surface strength is 15
It is set to A to 32 A, more preferably 23 A or more, and particularly preferably 25 A or more. The decorative plate may be peeled off after sticking an adhesive tape on its surface for a long time, and it is mainly desired that the decorative plate has high surface strength.
【００１４】表面強度を高める手段として、フリーネス
を下げるだけでなく、適宜紙力増強剤などを添加するこ
とができる。As means for increasing the surface strength, not only lowering the freeness but also adding a paper strength enhancer or the like can be added appropriately.
【００１５】平滑度としては、200 秒以上とされる。本
発明に従って、原紙の平滑度が高いと、後に塗料をブレ
ード塗工したときに、平滑性が高くなり、印刷インキの
密着性が良好となる。逆に、平滑度が低いと、塗工後に
塗工ムラが大きくなる。The smoothness is set to 200 seconds or more. According to the present invention, when the smoothness of the base paper is high, the smoothness becomes high when the coating material is blade-coated later, and the adhesion of the printing ink becomes good. On the contrary, when the smoothness is low, coating unevenness becomes large after coating.
【００１６】原紙の透気度としては、30〜300 秒とされ
る。透気度が高いことは、原紙の緻密性が高いことを意
味し、これによりインキのビヒクルが原紙に浸透せず、
印刷が映えることになる。かかる透気度を高める手段と
しては、パルプの配合としてＬ材を80％以上とする他、
フリーネスを低くすることにより得られる。フリーネス
としては、30ｇ／m2の場合、180 〜300cc が、特に200
〜250cc が好ましい。The air permeability of the base paper is 30 to 300 seconds. High air permeability means that the base paper is highly dense, which prevents the ink vehicle from penetrating into the base paper.
The print will look good. As a means for increasing the air permeability, the L material is 80% or more in the pulp mixture,
Obtained by lowering the freeness. Freeness is 180-300cc, especially 200 at 30g / m 2.
~ 250cc is preferred.
【００１７】フリーネスが180 cc未満であると、抄紙上
の乾燥性が悪くなり、ドライヤー接着ムラによる光沢ム
ラなどを生じる。逆にフリーネスが300 ccを超えると、
目標の紙間強度が得難い。50ｇ／m2の場合、350cc ±50
ccが好ましい。When the freeness is less than 180 cc, the drying property on the paper is deteriorated, and uneven glossiness due to uneven adhesion of the dryer occurs. Conversely, when the freeness exceeds 300 cc,
It is difficult to obtain the target paper strength. In case of 50g / m 2 , 350cc ± 50
cc is preferred.
【００１８】なお、原紙の地合が良好であることも望ま
れる。原紙の地合ムラがあると、コート時における塗工
ムラとなり、結果的に印刷ムラを招く。これは、透気度
と同様に、パルプの配合としてＬ材を80％以上とし、Ｎ
材を配合するとしても、20％以下とすることが好まし
い。原紙の抄紙に際して、原料パルプに対して、紙力増
強剤のほか、硫酸バンドなどのサイズ定着剤、ピッチ除
去剤、ロジンサイズ剤、カチオン化澱粉（プレスロール
およびワイヤーからの剥離促進剤、乾燥時における紙力
増強剤として機能する）、消泡剤などを添加することが
できる。この原紙に酸化チタンなどの填料を添加するこ
ともできる。抄紙は、通常の長網や丸網などの抄紙機に
より抄造できる。ここに用いる紙力増強剤としては、ポ
リアクリルアマイド樹脂、デンプン、ポリエピクロルヒ
ドリン樹脂、ポリエチレンイミン、内添用アクリルラテ
ックスなどを挙げることができる。紙力増強剤は乾燥重
量で30〜65kg／Ton 、特に50〜60kg／Ton が好ましい。It is also desired that the base paper has a good texture. If there is unevenness in the formation of the base paper, it will cause uneven coating during coating, resulting in uneven printing. This is the same as the air permeability, the pulp content is 80% or more of L material,
Even if the material is blended, it is preferably 20% or less. When making base paper, in addition to paper strength enhancer, size fixer such as sulfuric acid band, pitch remover, rosin sizing agent, cationized starch (release accelerator from press rolls and wires, during drying) Functioning as a paper-strengthening agent), an antifoaming agent, etc. can be added. A filler such as titanium oxide may be added to this base paper. Papermaking can be carried out by a normal paper machine such as a Fourdrinier or a round net. Examples of the paper strengthening agent used here include polyacrylic amide resin, starch, polyepichlorohydrin resin, polyethyleneimine, and acrylic latex for internal addition. The paper strength enhancer is preferably 30 to 65 kg / Ton in dry weight, and particularly preferably 50 to 60 kg / Ton.
【００１９】他方、前記原紙に対して、填料およびバイ
ンダーを含む塗料を塗工し、これをカレンダー処理する
ことにより化粧板用コート紙を得ることができる。填料
としては、クレー、軽炭酸カルシウム、重炭酸カルシウ
ム、酸化チタン、サチン白などを用いることができる。
バインダーとしては、クロスカット後のテープ剥離強度
（紙間強度）を高いものとするために、少なくともＰＶ
Ａを用いる。ＳＢＲラテックスと併用することも有効で
ある。この場合におけるバインダーの配合は、填料100
重量部に対してバインダーの総量の部数として10〜30重
量部、より望ましくは15〜30重量部であり、図１の領域
Ｘの範囲内とされる。特に好ましい範囲は、ＰＶＡを２
〜５重量部、ＳＢＲラテックスを８〜25重量部（特に望
ましくは14〜22重量部）である。On the other hand, a coated paper for a decorative sheet can be obtained by applying a paint containing a filler and a binder to the base paper and calendering it. As the filler, clay, calcium carbonate light, calcium bicarbonate, titanium oxide, satin white and the like can be used.
As the binder, at least PV is used in order to increase the tape peeling strength (paper strength) after cross-cutting.
A is used. It is also effective to use it in combination with SBR latex. In this case, the binder composition is 100% filler.
The total amount of the binder is 10 to 30 parts by weight, more preferably 15 to 30 parts by weight with respect to parts by weight, and is within the range of region X in FIG. A particularly preferred range is 2 PVA
.About.5 parts by weight, and 8 to 25 parts by weight of SBR latex (particularly preferably 14 to 22 parts by weight).
【００２０】また、エステル化デンプンおよびまたはカ
ゼインを５重量部以下、特に２〜５重量部を含有させる
ことが好適である。It is preferable that the esterified starch and / or casein is contained in an amount of 5 parts by weight or less, particularly 2 to 5 parts by weight.
【００２１】ＳＢＲラテックスとしては、硝化綿タイプ
のインキと塗工層との密着性の点から、アクリルニトリ
ルの配合比の多いものが、特にその配合量が１０重量部
以上のものが好ましい。As the SBR latex, from the viewpoint of the adhesion between the nitrified cotton type ink and the coating layer, those having a large compounding ratio of acrylonitrile, particularly those having a compounding amount of 10 parts by weight or more are preferable.
【００２２】アクリルニトリルは耐溶剤性があり、イン
キビヒクルが塗工層に浸透しても、ラテックスポリマー
が膨潤せず、インキ層が剥がれることを防止できる。Acrylonitrile has solvent resistance, and even if the ink vehicle penetrates into the coating layer, the latex polymer does not swell and the ink layer can be prevented from peeling off.
【００２３】塗料には、さらに耐水化剤、潤滑剤、消泡
剤、保水剤、pH調整剤、着色顔料などをさらに添加でき
る。塗工には、チップブレードやベントブレードなどの
ブレードによる塗工を行うのが好ましい。ロール塗工、
エアーナイフ塗工、ワイヤーバー塗工なども可能であ
る。塗工量は８〜25ｇ／m2が望ましい。８ｇ／m2未満で
あると、良質な面質を得ることができず、またスーパー
カレンダー後の白紙光沢が上がらず、その結果、印刷光
沢が低下し、紙間強度も低下する。塗工量が25ｇ／m2を
超えると、塗工乾燥性が悪くなる。一方、裏面側に、カ
ール防止用の酸化デンプン、防腐剤、耐水化剤などを塗
工することができる。A water resistance agent, a lubricant, a defoaming agent, a water retention agent, a pH adjuster, a coloring pigment and the like can be further added to the paint. For coating, it is preferable to perform coating with a blade such as a tip blade or a vent blade. Roll coating,
Air knife coating and wire bar coating are also possible. The coating amount is preferably 8 to 25 g / m 2 . If it is less than 8 g / m 2 , good surface quality cannot be obtained, and the white paper gloss after supercalendering does not increase, resulting in a decrease in printing gloss and a decrease in paper strength. When the coating amount exceeds 25 g / m 2 , the coating drying property becomes poor. On the other hand, the back side can be coated with an anti-curling oxidized starch, a preservative, a waterproofing agent and the like.
【００２４】塗工が終了すると、カレンダー処理、特に
スーパーカレンダー処理がなされる。このカレンダー処
理に際して、得ようとするコート紙の坪量との関係に若
干左右されるが、ニップ圧としては、145 〜250 kg／cm
2 が好ましく、ニップ段数としては、５段以上が望まし
い。ニップ圧が250 kg／cm2 を超えると、塗工層の構造
破壊を生じ、印刷適性が悪くなる危険性がある。When the coating is completed, calendering treatment, particularly super calendering treatment, is performed. In this calendering process, the nip pressure is 145 to 250 kg / cm, although it depends slightly on the relationship with the grammage of the coated paper to be obtained.
2 is preferable, and the number of nip steps is preferably 5 or more. If the nip pressure exceeds 250 kg / cm 2 , the structure of the coating layer may be destroyed and the printability may deteriorate.
【００２５】＜実施例＞以下実施例および比較例を示
し、本発明の効果を明らかにする。 （実施例１）填料として、クレー：炭酸カルシウム＝８
０：２０重量部とし、ＳＢＲラテックスとＰＶＡの配合
量を変化させて、各特性を調べたところ、表１に示す結
果を得た。なお、塗工量は１５ｇ／m2とした。評価の表
示において、◎はきわめて良好、○は良好、△はやや劣
る、×は劣るである。この評価の表示は、他の表におい
ても同様である。<Examples> The effects of the present invention will be clarified by showing Examples and Comparative Examples below. (Example 1) As a filler, clay: calcium carbonate = 8
When the amount of SBR latex and PVA was changed to 0:20 parts by weight and the respective properties were examined, the results shown in Table 1 were obtained. The coating amount was 15 g / m 2 . In the evaluation display, ⊚ is extremely good, ◯ is good, Δ is slightly inferior, and x is inferior. The display of this evaluation is the same in other tables.
【００２６】[0026]
【表１】 [Table 1]
【００２７】ここにクロスカット適性とは、合板への貼
着後に、カッターナイフで塗工面を碁盤の目が１００升
となるようにカットし、その表面にセロハンテープを貼
り、このセロハンテープを剥がしたとき、何升が剥がれ
たかで評価し、これを１〜４回繰り返した後の全体評価
とするものである。[0027] Here, the cross-cut suitability means that after sticking to a plywood, the coated surface is cut with a cutter knife so that the grid pattern is 100 squares, cellophane tape is stuck to the surface, and the cellophane tape is peeled off. The evaluation is based on how many boxes are peeled off, and this is repeated 1 to 4 times to give an overall evaluation.
【００２８】この結果によれば、ＳＢＲラテックスの配
合量が多く、かつＰＶＡを併用した塗工層が、耐セロハ
ンテープ強度およびクロスカット適性が共に良好である
ことが判明した。また、図１に評価を併示した。From these results, it was found that the coating layer containing a large amount of SBR latex and combined with PVA had good cellophane tape strength and cross-cut suitability. The evaluation is also shown in FIG.
【００２９】（実施例２）実施例１において、ＳＢＲラ
テックスとＰＶＡの配合量を２０：５部とし、塗工量
と、光沢度および耐セロハンテープ強度との関係を調べ
たところ、表２に示す結果を得た。この結果から、塗工
量が８ｇ／m2未満であると、原紙を均一にカバーリング
できず、また原紙へのバインダーの浸透量も少ないた
め、耐セロハンテープ強度が弱く、紙間剥離する。Example 2 In Example 1, the blending amount of SBR latex and PVA was set to 20: 5 parts, and the relationship between the coating amount, the glossiness and the cellophane resistant tape was examined. The results shown were obtained. From this result, when the coating amount is less than 8 g / m 2 , the base paper cannot be uniformly covered and the amount of the binder permeating into the base paper is small, so that the strength of the cellophane tape is weak and peeling occurs between the paper.
【００３０】[0030]
【表２】 [Table 2]
【００３１】（実施例３）実施例２の条件の下で、塗工
量および表面強度を変えて、耐セロハンテープ強度との
関係を調べたところ、表３に示す結果を得た。(Example 3) Under the conditions of Example 2, the coating amount and the surface strength were changed and the relationship with the strength of the cellophane tape resistance was examined. The results shown in Table 3 were obtained.
【００３２】[0032]
【表３】 [Table 3]
【００３３】（実施例４）原紙の平滑度および透気度
と、耐セロハンテープ強度および画質との関係を調べた
ところ、表４に示す結果を得た。Example 4 The results shown in Table 4 were obtained by examining the relationship between the smoothness and air permeability of the base paper, and the strength of the cellophane tape and the image quality.
【００３４】[0034]
【表４】 [Table 4]
【００３５】[0035]
【発明の効果】以上の通り、本発明によれば、平滑性、
表面強度、隠蔽性および印刷光沢の何れにも優れ、印刷
適性にも優れたものとなる。As described above, according to the present invention, smoothness,
It has excellent surface strength, hiding power, and printing gloss, and also has excellent printability.
【図１】本発明に係るバインダーの配合割合の好適範囲
を示す説明図である。FIG. 1 is an explanatory diagram showing a preferable range of a blending ratio of a binder according to the present invention.
Claims (1)
32Ａ、JIS P 8119で規定された平滑度が200 秒以上、透
気度が30〜300 秒である原紙に、填料、バインダーを含
む塗料を塗工してその塗料中の樹脂成分を原紙に浸透さ
せ、これをカレンダー処理したものであり、 さらに前記このバインダーとしてＳＢＲラテックスおよ
びポリビニルアルコールのうち少なくともポリビニルア
ルコールを含み、これらの填料100 重量部に対する重量
割合が、図１の領域Ｘ内にあり、塗工量が片面単位で８
〜25ｇ／m2であることを特徴とする化粧板用コート紙。1. The surface strength specified by JIS P 8129 is 15A to
32A, JIS P 8119 has a smoothness of 200 seconds or more and an air permeability of 30 to 300 seconds, coated with a paint containing a filler and a binder, and the resin component in the paint penetrates into the raw paper. The binder is calendered and further contains at least polyvinyl alcohol among SBR latex and polyvinyl alcohol as the binder, and the weight ratio of these to 100 parts by weight of the filler is within the region X in FIG. Effort is 8 per single side
-25 g / m 2 coated paper for decorative boards.