JPH0748598A - Anti-scale tablets - Google Patents

Abstract

(57) [Summary] [Object] To provide a scale preventive tablet which does not show disintegration property due to swelling in water and in which sulfamic acid particles are uniformly hardened by a water-soluble organic binder. The tablet of the present invention is obtained by coating or binding 100 parts by weight of sulfamic acid particles having a particle size of 32 to 100 mesh with 20 to 200 parts by weight of a water-soluble organic binder having a melting point of 30 to 150 ° C. 10-60 mesh granules
Obtained by compression molding at 1000 kg / cm ² .

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a tablet used for preventing scale formation on the inner wall of a pipe or the like which is contacted with waste water, and a method for producing the tablet. In particular, the scale-preventing tablet of the present invention is useful for preventing the generation of scale caused by urine on the inner walls of toilet bowls, pipes, etc. that come into contact with urine.

[0002]

2. Description of the Related Art Scales caused by urine formed on the inner walls of toilets, pipes, etc. that come in contact with urine are composed of calcium-containing inorganic compounds and organic compounds, which are the main components based on the decomposition of urine alone or diluted with wash water. Including, it is usually called urinary stone. The scale called urine stone is easily generated from the vicinity of the outlet of the urinal of the men's toilet where the diameter of the drainage pipe is relatively small, to the vicinity of the inlet of the pipe, and when it is accumulated, it causes a bad odor and a blockage of the drainage passage. Therefore, the scale removing work is usually performed at intervals of about 1 to 2 years. However, this scale removal work is not only troublesome in itself,
In order to give the worker a feeling of unsanitary, instead of this, a urolith-preventing agent that does not generate the scale itself is used.

It is well known that sulfamic acid not only dissolves the produced scale well, but can also prevent scale formation by dissolving sulfamic acid in water containing a scale-forming component such as calcium ion. In addition, while sulfamic acid is a strong acid almost equivalent to hydrochloric acid, sulfuric acid, etc., its corrosiveness to metals is
It is also known that it is much lower than those, and therefore, there are many proposals for a scale removing agent, a scale formation preventing agent and the like containing sulfamic acid.

Japanese Examined Patent Publication No. 3-60359 discloses a so-called melting method in which a slurry of fine powder particles of sulfamic acid dispersed in molten paradichlorobenzene is poured into a mold and then cooled, which comprises paradichlorobenzene and sulfamic acid. A method of molding tablets is disclosed. JP-A-2-28110
No. 0 discloses a method for molding a tablet comprising paradichlorobenzene and sulfamic acid by a so-called tableting method in which a mixture of paradichlorobenzene and sulfamic acid having an adjusted particle size distribution is pressure-molded. .

[0005]

Since the sulfamic acid particles do not have a binding force, a molded product having sufficient strength cannot be obtained from the sulfamic acid powder alone. The above-mentioned tablet made of paradichlorobenzene and sulfamic acid utilizes the binding force of paradichlorobenzene. However, the molding by the above-mentioned tableting method requires a troublesome process for making the particle size distribution of the paradichlorobenzene to be used uniform.

Further, when molding by the above-mentioned melting method, during the time until the molten paradichlorobenzene solidifies in the mold,
Sulfamic acid particles settle down, and a tablet in which sulfamic acid particles are uniformly dispersed cannot be obtained. By adding a thickening agent and molding by a melting method, this non-uniformity of the obtained tablets is slightly eliminated, but it is difficult to improve it to a sufficient level. When a tablet in which sulfamic acid particles are not uniformly dispersed is used as a scale inhibitor, sulfamic acid is supplied at an unnecessarily high concentration during the initial drainage that comes into contact with the tablet, and sulfamic acid is used within a short period of time. The remaining tablets have no anti-scaling ability because they are consumed.

The present invention solves the above-mentioned problems of the prior art, and provides a method for efficiently and simply obtaining tablets used for preventing scale formation in which sulfamic acid particles are uniformly dispersed. It is the one we are trying to provide.

[0008]

The tablet of the present invention comprises 100 parts by weight of sulfamic acid particles having a particle size of 32 to 100 mesh and 10 to 200 parts by weight of a water-soluble organic bond having a melting point of 30 to 150 ° C. It is obtained by compression-molding granules having a particle size of 10 to 60 mesh, which are coated or bonded with an agent, at 100 to 1000 kg / cm ² .

The tablet of the present invention preferably comprises the following steps (a) and (b): (a) 100 parts by weight of sulfamic acid particles having a particle size of 32 to 100 mesh, and 10 to 200 parts by weight of 30. The above water-soluble organic binder is mixed with a melt of a water-soluble organic binder having a melting point of ˜150 ° C. in a stirring granulator while stirring the mixture at a peripheral speed of 5-10 m / sec. By cooling to a temperature below the melting point of, to produce granules having a particle size of 10-60 mesh consisting of sulfamic acid particles coated or bound with the water-soluble organic binder, and (b)
The granules obtained in the step (a) are compression-molded at 100 to 1000 kg / cm ² , and the granules are produced.

The sulfamic acid used in the tablet of the present invention may be powdery, but the particle size is preferably about 32 to 100 mesh. Such a sulfamic acid powder can also be obtained as a commercially available industrial product. The water-soluble organic binder used in the tablet of the present invention is 30-150.
It is a substance having a melting point of ° C, preferably a melting point of 40 to 80 ° C, and shows a binding force necessary for tablets when the melt solidifies. Examples thereof include water-soluble polymer compounds such as polyethylene glycol, polyethylene oxide, and ethylene oxide / propylene oxide copolymers; ethylene oxide adducts of alkylphenols,
Nonionic surfactants such as alkyl sorbitan esters and glycerin monofatty acid esters; anionic surfactants such as sodium alkylbenzene sulfonate and sodium α-olefin sulfonate; positive ions such as alkyl trimethyl ammonium chloride and alkyl benzyl dimethyl ammonium chloride Examples thereof include ionic surfactants. In particular, a water-soluble polymer compound and a nonionic surfactant are preferable, and among them, a copolymer of 1 to 9 parts by weight of ethylene oxide and 1 part by weight of propylene oxide,
An alkyl sorbitan ester having an HLB value of 14 or less,
Nonionic surfactants such as glycerin monofatty acid ester are preferred.

The tablet of the present invention contains 100 parts by weight of the above sulfamic acid and 10 to 200 parts by weight, preferably 20 to 100 parts by weight of the above water-soluble organic binder. The tablets are then made from granules in which the sulfamic acid particles are coated or bound with the water-soluble organic binder. This granule is
It is obtained as solid particles cooled to a temperature below the melting point of this binder from a slurry which is a homogeneous mixture of a melt of the water-soluble organic binder and sulfamic acid in the above proportions. The granules can be produced by an extrusion granulation method, a fluidized bed granulation method, an agitation granulation method and the like, but the agitation granulation method is particularly preferable. The stirring granulator used in the stirring granulation method is capable of giving a peripheral velocity of 5 to 10 m / sec to the slurry when the slurry is stirred, and equipped with a jacket for heating and cooling. Is preferred. Such a stirring granulator can be obtained as a commercially available industrial product.

In the step (a) for producing granules preferably, for example, while stirring the cooling water having a temperature below the melting point of the water-soluble organic binder used in the jacket of the stirring granulator, the stirring granulation is carried out. Introduce the slurry into the stirring chamber of the granulator, while stirring the slurry at the peripheral speed, cooled to a temperature below the melting point of the water-soluble organic binder used,
It can be performed by converting into solid particles. This slurry can also be prepared in a stirring granulator. For example, while stirring the stirring granulator while circulating heated water having a temperature equal to or higher than the melting point of the water-soluble organic binder used in the stirring granulator jacket. It can be obtained by charging sulfamic acid and a water-soluble organic binder into the stirring chamber. After preparing this slurry in the stirring granulator, this slurry is converted into granules by cooling the slurry by circulating cooling water in its jacket while stirring the slurry at the above peripheral speed. Can be made.

The size of the granules is preferably about 10 to 60 mesh, and can be obtained as spherical particles by the stirring granulator as described above. The size of the granules changes depending on the change in the peripheral speed, and the larger the peripheral speed, the smaller the size of the granules. The tablet of the present invention is obtained by compression molding the above granules in step (b). For this molding,
An ordinary tableting machine is used, and it is preferable to adopt a pressure of about 100 to 1000 kg / cm ² . The tablet shape is spherical,
Any shape such as a disk shape, a conical shape, or a holed disk shape may be used.

The tablet of the present invention may contain optional components in addition to the sulfamic acid and the water-soluble organic binder as long as the object of the present invention is achieved. This optional component can be contained in the tablet by being contained in the slurry or by being mixed with the granules before the compression molding and then compression-molded. Examples of this optional component include a filler, a colorant, a dissolution rate modifier, a corrosion inhibitor, a bactericidal disinfectant, a lubricant, and a fragrance.

[0015]

The tablet of the present invention contains the sulfamic acid particles uniformly dispersed in the granules before compression molding.
By being a homogeneous mixture of these components in a form in which the sulfamic acid particles are coated or bound with a water-soluble organic binder. And the homogeneity of the granules, during the manufacturing process, while the slurry under stirring is cooled while maintaining its uniform mixed state, while changing to a solid through a highly viscous fluid,
It is considered that this fluid is torn off by the external force given from the stirrer and turned into fine particles.

The tablets of the present invention have been found to have high strength and non-disintegration properties in water. Even when the mixture of the solid particles of the water-soluble organic binder obtained by pulverization and the sulfamic acid particles is compression-molded, the obtained tablets are disintegrated in water, whereas the tablets of the present invention are not disintegrated in water. It is surprising to show sex. This unexpected effect probably exists between the particles of the granules in the compression molding of the granules, as the fusion of the water-soluble organic binder existing so as to wrap the particles around the sulfamic acid particles occurs. It is considered that the air is rapidly extruded, and as a result, a dense tablet without voids is formed, so that even if the tablet is immersed in water, water absorption due to the capillary phenomenon and swelling due to the water do not occur. .

The finer the sulfamic acid particles used, the more uniform the tablet can be obtained. However, if the particle size is too small, powdering tends to occur during the operation of producing the granules.
To maintain a good working environment, it is preferable to use sulfamic acid having a particle size of about 32 to 100 mesh. If the melting point of the water-soluble organic binder used is lower than the ambient temperature, the binder will melt on the surface of the tablet during storage during periods of high temperatures such as summer, resulting in the adherence of tablets to each other and to the packaging material. Occur. The use of a binder with a high melting point requires a large amount of heat when melting it. 40-80
It is preferable to use a binder having a melting point of about 0 ° C.

In a tablet containing 200 parts by weight or more of a water-soluble organic binder with respect to 100 parts by weight of sulfamic acid, the concentration of sulfamic acid in the tablet is lowered and the ability to prevent scale formation becomes poor. On the contrary, when 100 parts by weight of sulfamic acid and 10 parts by weight or less of the water-soluble organic binder were used, the obtained granules were not sufficiently covered with the water-soluble organic binder, and even when the granules were compression molded. Tablets with high hardness cannot be obtained.

When granules having a particle size smaller than 60 mesh are compression-molded, air tends to remain in the obtained tablets, and tablets having stability in water cannot be obtained. And, it is difficult to obtain a tablet having a constant weight by compression molding of granules larger than 10 mesh.

[0020]

Example A commercially available Henschel mixer (FM-10 / L type) was prepared as a stirring granulator, and a commercially available product having a particle size of 32 to 100 mesh was prepared as sulfamic acid (SMA). As the water-soluble organic binder, stearic acid monoglyceride (A) having a melting point of 60 ° C, sorbitan monopalmitate (B) having a melting point of 50 ° C, and ethylene oxide and propylene oxide having a melting point of 55 ° C of 7: 3 are used. A weight ratio copolymer (C) was prepared.

Example 1 A 1 kg slurry was prepared by heating 100 parts by weight of the sulfamic acid and 25 parts by weight of the binder (A) in a container while heating to 80 ° C. Then, cooling water at 20 ° C was circulated in the jacket of the Henschel mixer, and the stirring blade was rotated at a rotation speed of 1200 rpm (peripheral speed 7 m / s).
The whole amount of the above slurry was put into a stirring chamber which was stirred at, and stirring was continued for 20 minutes to prepare granules having a particle size of 10 to 60 mesh. The granules did not swell when placed in water and did not break.

The above-prepared granules were placed in a mold having a diameter of 35 mm,
By compression molding at a pressure of about 600 kg / cm ² , 40 g of a cylindrical tablet was obtained. The tablets were measured for hardness, stability in water and uniformity by the following test methods. Hardness: The hardness is measured with a Kiya type hardness meter, and those with a hardness of 30 kg or more are indicated by a circle, and hardness less than 30 kg is indicated by a cross.

Stability in water: The above tablets are put into 1 liter of tap water in a beaker, left for 30 minutes and then taken out to observe the appearance of the molded body. When there is no change in appearance, it is indicated by a circle, and when the tablet is swollen or disintegrated, it is indicated by a cross. Uniformity: The upper and lower parts of the tablet are scraped off, and the sulfamic acid content of each is measured. When the difference in sulfamic acid content between the upper part and the lower part is less than 5%, the mark ◯ is shown, and when the difference is 5% or more, the mark x is shown.

The results of these measurements are shown in Table 1. Table 1 Example No. Binder and parts by weight Molding method Hardness Stability in water Uniformity Example 1 (A) 25 Granule compression 〇 〇 〇 Example 2 (A) 100 Granule compression 〇 〇 〇 Example 3 (B) 25 Granules Compressed 〇 〇 〇 Example 4 (B) Compressed 100 granules 〇 〇 〇 Example 5 (C) 43 Compressed granules 〇 〇 〇 Comparative example 1 (A) 25 Compressed powder 〇 × 〇 Comparative example 2 (B) 100 Powder compression 〇 × 〇 Comparative example 3 (C) 43 Powder compression 〇 × 〇 Comparative example 4 (A) 100 Melt casting 〇 〇 × Comparative example 5 (B) 100 Melt casting 〇 〇 × Comparative Example 6 (C) 43 Casting of melt 〇 〇 × Examples 2-5 Except for changing the mixing ratio (parts by weight) of the binder and its sulfamic acid to 100 parts by weight as shown in Table 1, Granules were made, tablets were made and tested as in Example 1. The results are shown in Table 1.

Comparative Examples 1 to 3 Powders obtained by mixing the binders shown in Table 1 and the sulfamic acid at a ratio (parts by weight) shown in Table 1 to 100 parts by weight of sulfamic acid were prepared as in Example 1. Tablets were similarly pressed into tablets and tested. The results are shown in Table 1. Comparative Examples 4 to 6 The binders shown in Table 1 and the sulfamic acid were mixed at a ratio (parts by weight) shown in Table 1 to 100 parts by weight of sulfamic acid to prepare a molten slurry at 80 ° C. Tablets were made by casting the slurry in the same mold used in Example 1 and cooling and tested as in Example 1. The results are shown in Table 1.

As shown in Table 1, the tablet of the present invention is excellent in hardness, stability in water and uniformity.
The tablet of the comparative example obtained by compression molding the mixed powder of the binder powder and the sulfamic acid powder swells or disintegrates in water,
Not stable in water. Further, the tablets of the comparative examples obtained by casting a slurry, which is a mixture of the binder melt and the sulfamic acid powder, do not have uniformity.

[0027]

EFFECTS OF THE INVENTION The tablet of the present invention is prepared by first forming a granule containing these components from a water-soluble organic binder and a sulfamic acid powder by a usual stirring granulation method, and then compressing the granule by a usual tableting method. It can be easily made by locking. This tablet is a hard tablet that uniformly contains sulfamic acid, and gradually releases sulfamic acid into water over a long period of time without causing swelling or disintegration even when contacted with water.

When the wastewater containing the scale forming component such as calcium content passes through the pipe for a long period of time, the tablet of the present invention should be installed at the inlet of the wastewater so as to come into contact with the wastewater. Thereby, it is possible to prevent scale from being generated on the inner wall of the pipe. As an example that is preferably used, urine or its washing water can be obtained by installing this tablet in the urinal of the men's toilet, in the trap of the urinal of the men's toilet, in the high tank of the men's toilet, or in the washing water pipe. When the urine or its cleaning water is discharged by contacting with, it is possible to effectively prevent the scale called urine stone from adhering to the inner wall of the pipe through which urine or its cleaning water passes.

Claims (2)

[Claims] 1. 100 parts by weight of sulfamic acid particles having a particle size of 32 to 100 mesh are added to 10 to 200 parts by weight of 30 to 15 parts by weight.
Granules having a particle size of 10 to 60 mesh coated or bound with a water-soluble organic binder having a melting point of 0 ° C.
Anti-scale tablets that are compression molded at 1000 kg / cm ² . 2. The following steps (a) and (b): (a) 100 parts by weight of sulfamic acid particles having a particle size of 32 to 100 mesh and 10 to 200 parts by weight of water-soluble having a melting point of 30 to 150 ° C. The homogeneous mixture with the melt of the water-soluble organic binder is cooled to a temperature below the melting point of the water-soluble organic binder while stirring the mixture at a peripheral speed of 5 to 10 m / sec in a stirring granulator. Thereby producing granules having a particle size of 10 to 60 mesh consisting of sulfamic acid particles coated or bound with the water-soluble organic binder, and (b) 100 g of the granules obtained in this step (a). A method for producing a scale-preventing tablet, which comprises a step of compression molding at ~ 1000 kg / cm ² .