Abstract

PURPOSE: To obtain resin gloves having a glove skin formed by joining and integrating glove outer skin of resin skin layer of knitted fabric with glove inner skin and projections for non-slip on the surface of gloves and provide a method for producing the resin gloves. CONSTITUTION: A glove forming mold 5 providing the recessed part 6 for projection for non-slip applied onto the surface of gloves in recessed state on the surface and having required three-dimensional form of gloves is immersed into a resin solution 7 to pack the resin solution 7 in the recessed part 6 for projections and the resin solution 7 is attached to the surface of the forming mold 5 to form a resin skin layer 9 having uniform thickness and then, a knit glove body 10 of knitted fabric is covered around the forming mold 5 having the resin skin layer 9 and the resin skin layer 9 and knit glove body 10 are fused to integrate the resin skin layer 9 with the glove body 10 and the resin skin layer 9 is removed from the forming mold 5 the interior are reversed to the outside to provide the objective resin gloves 1 comprising a glove skin 11 using the resin skin layer 9 as glove outer skin 2 and using the knit glove body 10 as glove inner skin 3 and providing projections 4 for non-slip on the surface.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a resin glove and a method for manufacturing the glove.

[0002]

2. Description of the Related Art Some resin gloves have a knitted inner skin structure in which a knitted fabric is adhered to the inside of a resin glove outer skin to form a glove inner skin, and the outer skin and the inner skin are integrally formed into a glove skin. It is widely used for water work, cooking, etc. because it has excellent wearing feel, detachability on hands, and cold protection.

Since the resin glove of the knitted fabric inner structure needs to be formed as a glove skin in which the resin outer skin and the knitted fabric inner skin are integrated, the knitted glove formed in the required glove shape on the knitted fabric is beforehand formed. After making, and then spraying a resin on the knitted gloves, or immersing the knitted gloves in a resin solution, form a resin layer that is in close contact with the surface of the knitted gloves, and use the resin layer as the glove skin. The manufacturing method is adopted.

[0004]

Since the above-mentioned conventional knitted resin gloves having a knitted fabric inner structure cannot but rely on the above-mentioned manufacturing method, the surface of the resin outer coat, that is, the gloved surface has a "smooth" smooth surface. Since it is impossible to form "anti-slip" or "designed design" which is raised on the surface of the glove, the performance and design value of resin gloves are inferior.

The present invention provides a resin glove having a knitted inner skin structure and a method for manufacturing the same, which solves the above-mentioned problems of the prior art.

[0006]

[MEANS FOR SOLVING THE PROBLEMS] A resin glove and a method for producing the same according to the present invention for solving the above technical problems are described as follows: "A glove skin made of resin and a glove inner skin of a knitted fabric are integrally bonded, and , An integrated non-slip glove surface,
Or, a resin glove made of a "structure having a design",

"A glove forming die having a slip prevention or a design provided on the surface of the glove and having a desired glove three-dimensional shape is dipped in a resin solution to form a resin skin layer on the surface of the glove forming die. Then, the glove mold having the solidified resin skin layer is covered with a knitted knitted glove body having the required glove shape and encapsulated, and then the resin skin layer is removed from the glove mold. It is removed and turned inside-out, the resin skin layer is used as a glove skin to form the knitted fabric glove body as a glove inner skin, and the glove surface is formed into a resin glove in which the non-slip or design is raised ". It is a method of manufacturing resin gloves.

The above-mentioned non-slip is a "jagged protrusion" that functions as a non-slip when using resin gloves.
It means that optional items such as “dot projections” and “lattice projections” are provided at the required places on the gloves, and the design means an optional place for improving the aesthetics of the resin gloves and transmitting information to the user. "Pattern,""figure," and "character" to be applied to.

[0009]

The resin glove of the present invention and the resin glove according to the above-mentioned manufacturing method are resin gloves in which a resin outer skin and a knitted fabric inner skin are integrally formed into a glove skin, and the above-mentioned non-slip / design is raised on the glove surface. Therefore, the glove performance and the aesthetic value of the glove can be improved.

[0010]

EXAMPLE An example of the method for producing a resin glove of the present invention will be described in detail below with reference to FIG. That is, it is made of aluminum and has a three-dimensional shape of a resin glove to be formed, and at the required position on the surface of the resin glove, a projection concave portion 6 in which a non-slip projection to be raised is provided as it is. Using the glove forming mold 5 of No. 3, it is manufactured by the following procedure and method.

First, the glove mold 5 is heated for a while,
The resin liquid 7 in the resin liquid tank 8 is filled in the concave portion 6 for protrusion existing on the mold surface by dipping in the resin liquid tank 8 of vinyl chloride, and the resin liquid 7 is attached to the peripheral surface of the molding die 5. Then, the glove forming mold 5 is solidified to have a uniform film thickness, and a resin skin layer 9 having a smooth surface is formed.

A glove forming mold 5 having a resin skin layer 9 is formed.
The knitted knitted glove body 10 having a shape capable of being brought into close contact and encapsulation is separately encased, and an appropriate adhesive (the adhesive of this example is manufactured by Sanken Kako Co., Ltd. Using diptyl phthalate), the two are fused and integrated into one body. The resin skin layer 9 becomes the glove skin 2, the knitted glove body 10 becomes the glove inner skin 3, and the glove inner skin 3 and the glove outer skin 2 become a united and integrated glove skin 11, and the knitted glove body 10 Forming the inside-out glove body 12 in a state of being fitted to the glove forming mold 5 with the outer side being the outer side.

Finally, the inside out glove body 12 is removed from the molding die 5, and unnecessary portions of the wrist portion are cut and removed to reverse the inside and outside, and the glove inner skin 3 is placed inside the resin glove 1.
Is formed. Thus, at a predetermined position of the resin glove 1, the resin liquid 7 filled in the concave portion 6 for the projection of the glove forming die 5 is filled.
Is solidified, and a convex anti-slip projection 4 is formed on the surface of the glove.

Between the above-mentioned treatment steps, for example, the mold 5 is heated for some time in order to uniformly adhere the resin liquid 7 to the glove mold 5, and after the resin liquid 7 is pulled up, the adhered resin is cured. Heat treatment and quenching treatment of
After fitting the knitted fabric glove body 10 to the glove forming mold 5 with a resin layer, a heating / cooling process or the like for fusing the resin skin layer 9 and the knitted fabric glove body 10 is performed as necessary.

According to the manufacturing method of the above embodiment, the glove surface has the anti-slip projections 4 and the knitted inner fabric 2
It is possible to mass-produce the resin glove 1 including the glove skin 11 in which the resin outer skin 3 and the resin outer skin 3 are integrated together with high productivity.

The method of manufacturing the resin glove of the present invention is not limited to the above-mentioned embodiment, and any protrusions / patterns other than the above-mentioned anti-slip protrusions 4 are raised at arbitrary positions on the surface of the glove. is there.

[0017]

Industrial Applicability As described above, the resin glove of the present invention and the method for producing the same provide a high-quality knitted fabric endothelium resin glove excellent in anti-slip function and design value, and widely used in general resin gloves. This has the effect of improving the convenience of persons.

[Brief description of drawings]

FIG. 1 is an explanatory view of an embodiment of a method for producing a resin glove of the present invention.

[Explanation of symbols]

 DESCRIPTION OF SYMBOLS 1 Resin gloves 2 Glove outer skin 3 Globe inner skin 4 Non-slip protrusions 5 Glove mold 6 Recesses for protrusions 7 Resin liquid 8 Resin liquid tank 9 Resin skin layer 10 Knitted fabric glove body 11 Glove skin 12 Inside-out glove body

Claims (2)

[Claims] 1. A structure comprising an integral glove skin in which a resin glove skin and a knitted fabric glove inner skin are united and adhered, and having a non-slip or a design that is integrally raised on the glove surface. Resin gloves. 2. A glove forming die having a non-slip or design provided on the surface of the glove and having a desired glove three-dimensional shape is dipped in a resin solution to form a resin on the surface of the glove forming die. A skin layer is adhered and formed, and then a glove mold having the solidified resin skin layer is covered and adhered by covering a knitted fabric glove body having a required glove shape, and then the resin skin layer is formed in the glove mold. Characterized in that the resin skin layer is formed into a glove skin, the knitted glove body is made into a glove inner skin, and the glove surface is formed into a resin glove in which the non-slip or design is raised. Method for manufacturing resin gloves.