JPH086252B2 - 繊維処理油剤組成物 - Google Patents
繊維処理油剤組成物Info
- Publication number
- JPH086252B2 JPH086252B2 JP18944788A JP18944788A JPH086252B2 JP H086252 B2 JPH086252 B2 JP H086252B2 JP 18944788 A JP18944788 A JP 18944788A JP 18944788 A JP18944788 A JP 18944788A JP H086252 B2 JPH086252 B2 JP H086252B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- polyoxyethylene sorbitan
- parts
- squalene
- composition according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 ［産業上の利用分野］ 本発明は繊維処理用油剤、特に柔軟化剤の分野に使用
されるスクワランの組成物に関する。特に摩擦係数が低
く帯電防止性もあり、エマルジョンも微細で経時安定性
に優れ、油焼けや機械の腐食を起こさず、長期の保存に
耐え、エマルジョン化が容易であり、かつ冬季の使用に
耐えるための十分に低い凝固点を有するといった繊維処
理油剤に要求される基本的性能を十二分に満たす繊維処
理油剤、特に繊維用柔軟剤に関する。
されるスクワランの組成物に関する。特に摩擦係数が低
く帯電防止性もあり、エマルジョンも微細で経時安定性
に優れ、油焼けや機械の腐食を起こさず、長期の保存に
耐え、エマルジョン化が容易であり、かつ冬季の使用に
耐えるための十分に低い凝固点を有するといった繊維処
理油剤に要求される基本的性能を十二分に満たす繊維処
理油剤、特に繊維用柔軟剤に関する。
［従来の技術とその課題］ 一般に紡績工業では、天然の綿繊維、羊毛繊維または
化学繊維のいずれでも紡績時の繊維の摩擦係数の増大に
よる帯電や風合いむらまたは繊維の切断などを防止し、
円滑な紡績状態を維持するために紡績油または調合油と
いった繊維処理剤が使用されている。代表的な油剤とし
ては鉱油系の低粘度流動パラフインをベースに界面活性
剤や帯電防止剤を適宜に組み合わせたものが一般的であ
る。かかる鉱油系の場合、摩擦係数を十分に低減するほ
どの柔軟化効果が得られるとはいえず、また油焼けや機
械の腐食を防止するために水素精製を行うと粘度指数の
低下をきたしそのため低温時の流動性が失われる。また
実際の使用形態としてはエマルジョンの形態が最も一般
的であるがエマルジョンの長期安定性やエマルジョン化
の容易さなどの点でも必ずしも不十分であった。
化学繊維のいずれでも紡績時の繊維の摩擦係数の増大に
よる帯電や風合いむらまたは繊維の切断などを防止し、
円滑な紡績状態を維持するために紡績油または調合油と
いった繊維処理剤が使用されている。代表的な油剤とし
ては鉱油系の低粘度流動パラフインをベースに界面活性
剤や帯電防止剤を適宜に組み合わせたものが一般的であ
る。かかる鉱油系の場合、摩擦係数を十分に低減するほ
どの柔軟化効果が得られるとはいえず、また油焼けや機
械の腐食を防止するために水素精製を行うと粘度指数の
低下をきたしそのため低温時の流動性が失われる。また
実際の使用形態としてはエマルジョンの形態が最も一般
的であるがエマルジョンの長期安定性やエマルジョン化
の容易さなどの点でも必ずしも不十分であった。
そこで本発明の目的は、従来の繊維処理油剤の欠点を
克服した油剤、特に柔軟剤の提供にある。
克服した油剤、特に柔軟剤の提供にある。
［課題を解決するために手段］ すなわち本発明は、 （ａ） ヨー素価５以下のスクワレン水素添加物 100重
量部 （ｂ） ポリオキシエチレンソルビタンモノオレート、 ポリオキシエチレンソルビタンジオレート、 ポリオキシエチレンソルビタントリオレート、 および ポリオキシエチレンラウリルエーテルリン酸ナトリウム
塩 からなる群から選択された少なくとも一種の界面活性剤
15〜100重量部 から成る繊維処理油剤組成物 に関する。
量部 （ｂ） ポリオキシエチレンソルビタンモノオレート、 ポリオキシエチレンソルビタンジオレート、 ポリオキシエチレンソルビタントリオレート、 および ポリオキシエチレンラウリルエーテルリン酸ナトリウム
塩 からなる群から選択された少なくとも一種の界面活性剤
15〜100重量部 から成る繊維処理油剤組成物 に関する。
以下に本発明をさらに詳しく説明する。
上記スクワレンの水素添加物は、常法によりスクワレ
ンを水素添加して製造する。スクワレンは鮫などの魚類
の肝油、オリーブなどの植物などの何れのものからのも
のも使用できる。また合成品も使用できる。本発明のス
クワレンの水素添加物のヨー素価は５以下、好ましくは
１以下のものである。５を超えるヨー素価の場合は、処
理された繊維の経時変化が悪くなり油焼けなどの弊害を
起こすので好ましくない。また上記スクワレンの水素添
加物は、良好な加脂効果を有し、特に動物性繊維に対し
て優れた浸透性を発揮する。そのため本発明の組成物で
繊維を処理すれば繊維は柔軟化される。
ンを水素添加して製造する。スクワレンは鮫などの魚類
の肝油、オリーブなどの植物などの何れのものからのも
のも使用できる。また合成品も使用できる。本発明のス
クワレンの水素添加物のヨー素価は５以下、好ましくは
１以下のものである。５を超えるヨー素価の場合は、処
理された繊維の経時変化が悪くなり油焼けなどの弊害を
起こすので好ましくない。また上記スクワレンの水素添
加物は、良好な加脂効果を有し、特に動物性繊維に対し
て優れた浸透性を発揮する。そのため本発明の組成物で
繊維を処理すれば繊維は柔軟化される。
上記スクワレンの水素添加物と併用する界面活性剤
は、ポリオキシエチレンソルビタンモノオレート、ポリ
オキシエチレンソルビタンジオレート、ポリオキシエチ
レンソルビタントリオレート、およびポリオキシエチレ
ンラウリルエーテルリン酸ナトリウム塩から成る群から
選択される少なくとも一種の界面活性剤である。これら
の界面活性剤は単独でも混合しても使用できる。該界面
活性剤は上記スクワレンの水素添加物の安定なエマルジ
ョンとなすために使用され、それ自身には特に繊維柔軟
効果は有しない。またこれらの界面活性剤は刺激性が低
く安全性が高い。
は、ポリオキシエチレンソルビタンモノオレート、ポリ
オキシエチレンソルビタンジオレート、ポリオキシエチ
レンソルビタントリオレート、およびポリオキシエチレ
ンラウリルエーテルリン酸ナトリウム塩から成る群から
選択される少なくとも一種の界面活性剤である。これら
の界面活性剤は単独でも混合しても使用できる。該界面
活性剤は上記スクワレンの水素添加物の安定なエマルジ
ョンとなすために使用され、それ自身には特に繊維柔軟
効果は有しない。またこれらの界面活性剤は刺激性が低
く安全性が高い。
これらは上記スクワレンの水素添加物の100重量部に
対して15〜100、好ましくは25〜50重量部使用する。該
範囲をはずれて界面活性剤を使用するといずれも安定な
乳化組成物が得られない。特に好ましくはポリオキシエ
チレンソルビタンモノオレート（その含有量をＡとす
る）とポリオキシエチレンソルビタントリオレート（そ
の含有量をＢとする）とを併用し、両者の重量比A/Bが
１以下であることが適当である。
対して15〜100、好ましくは25〜50重量部使用する。該
範囲をはずれて界面活性剤を使用するといずれも安定な
乳化組成物が得られない。特に好ましくはポリオキシエ
チレンソルビタンモノオレート（その含有量をＡとす
る）とポリオキシエチレンソルビタントリオレート（そ
の含有量をＢとする）とを併用し、両者の重量比A/Bが
１以下であることが適当である。
本発明では、水性エマルジョンの乳化安定性をさらに
増加させるために、C8以下の飽和有機モノまたはジカル
ボン酸を上記スクワレンの水素添加物の100重量部に対
して0.5〜５、好ましくは0.7〜1.0重量部を添加するの
が好ましい。炭素数C8以上のカルボン酸を使用した場合
や、上記使用量をはずれた場合では何れもエマルジョン
安定性を改良するというカルボン酸の添加効果が得られ
ない。
増加させるために、C8以下の飽和有機モノまたはジカル
ボン酸を上記スクワレンの水素添加物の100重量部に対
して0.5〜５、好ましくは0.7〜1.0重量部を添加するの
が好ましい。炭素数C8以上のカルボン酸を使用した場合
や、上記使用量をはずれた場合では何れもエマルジョン
安定性を改良するというカルボン酸の添加効果が得られ
ない。
C8以下の飽和有機モノまたはジカルボン酸としては酢
酸、プロピオン酸、酪酸、吉草酸、カプロン酸、エナン
ト酸、カプリル酸、しゆう酸、マロン酸、コハク酸、グ
ルタミン酸、アジピン酸、ピメリン酸、スベリン酸など
が挙げられる。特に好ましくは乳化安定性や安全性の観
点からコハク酸である。
酸、プロピオン酸、酪酸、吉草酸、カプロン酸、エナン
ト酸、カプリル酸、しゆう酸、マロン酸、コハク酸、グ
ルタミン酸、アジピン酸、ピメリン酸、スベリン酸など
が挙げられる。特に好ましくは乳化安定性や安全性の観
点からコハク酸である。
なお本発明の目的の範囲で従来公知の他の界面活性剤
または添加剤例えば酸化防止剤、乳化助剤艶だし剤とし
てのシリコーン系化合物などを適宜の量で混合ででき
る。
または添加剤例えば酸化防止剤、乳化助剤艶だし剤とし
てのシリコーン系化合物などを適宜の量で混合ででき
る。
本発明の組成物は通常はエマルジョンの形態で使用さ
れる。かかるエマルジョン組成物は従来公知の方法で製
造できるが、例えばスクワレン水素添加物に撹拌下に界
面活性剤を徐々に添加し、終了後次いでカルボン酸水溶
液を同じく徐々に添加する。最後に水を添加してエマル
ジョンとする。
れる。かかるエマルジョン組成物は従来公知の方法で製
造できるが、例えばスクワレン水素添加物に撹拌下に界
面活性剤を徐々に添加し、終了後次いでカルボン酸水溶
液を同じく徐々に添加する。最後に水を添加してエマル
ジョンとする。
エマルジョンとして繊維処理剤に使用するときは適宜
の固形分濃度のエマルジョンとし、浴比５〜30、好まし
くは10〜20で10〜30分間浸漬後、脱水乾燥すればよい。
の固形分濃度のエマルジョンとし、浴比５〜30、好まし
くは10〜20で10〜30分間浸漬後、脱水乾燥すればよい。
［実施例］ 以下、実施例により本発明を説明するが、本発明はこ
れらの実施例のみに制約されるものではない。
れらの実施例のみに制約されるものではない。
製造例 配合方法： スクワレンの水素添加物（ヨー素価0.2）200gを撹拌
した。これに同じく撹拌しながらポリオキシエチレンソ
ルビタンモノオレート40gを徐々に添加した。次いでポ
リオキシエチレンソルビタントリオレートの10gを徐々
に添加した。続いて10％コハク酸水溶液（60℃で調製し
た）をスクワレン100g重量部の対し0.25〜1.0重量部に
なるように５、10、15、20gをそれぞれ添加し各種コハ
ク酸濃度の液を調製した。最後に水を合成1000gになる
ように添加してスクワレンの水素添加物濃度20％のエマ
ルジョンを調製した。
した。これに同じく撹拌しながらポリオキシエチレンソ
ルビタンモノオレート40gを徐々に添加した。次いでポ
リオキシエチレンソルビタントリオレートの10gを徐々
に添加した。続いて10％コハク酸水溶液（60℃で調製し
た）をスクワレン100g重量部の対し0.25〜1.0重量部に
なるように５、10、15、20gをそれぞれ添加し各種コハ
ク酸濃度の液を調製した。最後に水を合成1000gになる
ように添加してスクワレンの水素添加物濃度20％のエマ
ルジョンを調製した。
上記調製組成物は、次に固形分１％の成るようにそれ
ぞれ水で希釈し、24時間放置後の乳価状態を目視で観察
した。結果を第１表に示した。
ぞれ水で希釈し、24時間放置後の乳価状態を目視で観察
した。結果を第１表に示した。
第１表 コハク酸濃度 エマルジョンの安定性 （重量部） 無添加 分離 0.25 分離 0.50 安定 0.75 安定 1.00 安定 実施例 製造例で得られたコハク酸濃度0.75重量部のスクワレ
ン水素添加物濃度20重量％のエマルジョンを水で希釈し
て固形分濃度３、５、７％の組成物を調製した。
ン水素添加物濃度20重量％のエマルジョンを水で希釈し
て固形分濃度３、５、７％の組成物を調製した。
比較のためにスクワレンの水素添加物（ヨー素価0.
2）200gを加えずに界面活性剤とコハク酸のみから成る
固形分濃度５％のものも同様に製造した。
2）200gを加えずに界面活性剤とコハク酸のみから成る
固形分濃度５％のものも同様に製造した。
繊維の柔軟化試験は次のように行った。
市販の絹、綿、麻および羊毛の４種類について面積が
10cm×4cmとなるように切断し、これを上記各濃度のエ
マルジョンに浴比10、温度は室温で20分間浸漬した。
10cm×4cmとなるように切断し、これを上記各濃度のエ
マルジョンに浴比10、温度は室温で20分間浸漬した。
その後、マングローラー（辻井染機製）を使用し5kg
の荷重で加圧脱水し、その後ジェット乾燥機（辻井染機
製）により100℃、３分間乾燥した。
の荷重で加圧脱水し、その後ジェット乾燥機（辻井染機
製）により100℃、３分間乾燥した。
乾燥試験片を、５名のパネラーが柔軟剤未使用の原試
験片と比較しその柔軟化度を以下の基準で評価した。
験片と比較しその柔軟化度を以下の基準で評価した。
１点 悪くなった ２点 やや悪くなった ３点 変わらない ４点 やや良くなった ５点 良くなった 結果を第２表に示した。
［発明の効果］ 本発明のスクワレンの水素添加物は、鮫肝油から得ら
れたスクワレンの還元生成物であって繊維に対する加脂
効果を有し、特に動物繊維に対して良好な浸透性を発揮
する。さらに、好ましくは本発明の組成物はカルボン酸
を添加することより、特に低濃度のスクワレンまたはス
クワランエマルジョン組成物においても容易に乳化分散
すると共に入荷分散状態が長期に亘り維持さる。
れたスクワレンの還元生成物であって繊維に対する加脂
効果を有し、特に動物繊維に対して良好な浸透性を発揮
する。さらに、好ましくは本発明の組成物はカルボン酸
を添加することより、特に低濃度のスクワレンまたはス
クワランエマルジョン組成物においても容易に乳化分散
すると共に入荷分散状態が長期に亘り維持さる。
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ０６Ｍ 13/295 Ｄ０６Ｍ 13/32 13/20
Claims (6)
- 【請求項１】（ａ） ヨー素価５以下のスクワレン水素
添加物 100重量部 （ｂ） ポリオキシエチレンソルビタンモノオレート、 ポリオキシエチレンソルビタンジオレート、 ポリオキシエチレンソルビタントリオレート、 および ポリオキシエチレンラウリルエーテルリン酸ナトリウム
塩 から成る群から選択された少なくとも一種の界面活性剤
15〜100重量部 から成る繊維処理油剤組成物。 - 【請求項２】前記水素添加物のヨー素価が１以下である
特許請求の範囲第１項記載の組成物。 - 【請求項３】C8以下の飽和有機モノまたはジカルボン酸
を水素添加物100重量部に対して0.5〜５重量部含む特許
請求の範囲第１項記載の組成物。 - 【請求項４】C8以下の飽和有機モノまたはジカルボン酸
がコハク酸である特許請求の範囲第３項記載の組成物。 - 【請求項５】前記界面活性剤としてポリオキシエチレン
ソルビタンモノオレートとポリオキシエチレンソルビタ
ントリオレートとを用いる特許請求の範囲第１項記載の
組成物。 - 【請求項６】前記組成物が水性エマルジョンである特許
請求の範囲第１項記載の組成物。