JPH0877950A - Integral implosion-protected cathode-ray tube - Google Patents
Integral implosion-protected cathode-ray tubeInfo
- Publication number
- JPH0877950A JPH0877950A JP21107594A JP21107594A JPH0877950A JP H0877950 A JPH0877950 A JP H0877950A JP 21107594 A JP21107594 A JP 21107594A JP 21107594 A JP21107594 A JP 21107594A JP H0877950 A JPH0877950 A JP H0877950A
- Authority
- JP
- Japan
- Prior art keywords
- glass panel
- resin sheet
- ray tube
- face plate
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、防爆補強を有する補強
型陰極線管に関し、そのうち特に補強型カラー陰極線管
の構造に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a reinforced cathode ray tube having explosion-proof reinforcement, and more particularly to a structure of a reinforced color cathode ray tube.
【０００２】[0002]
【従来の技術】テレビジョン受像機等の陰極線管におい
ては、陰極線管に外部から衝撃が与えられた場合に、そ
の衝撃を緩和し、爆縮時のガラス飛散を防止するため
に、様々な補強対策が施されている。この補強対策とし
ては、例えば、図４に示すように、ガラスパネル１０１
の側面外周部に補強用の金属環体１０２を配置し、この
金属環体１０２とガラスパネル１０１との間に金属環体
緩衝接着剤としての樹脂テープ１０３を介在させる方法
や、図５に示すように、フェイスプレート１０４の有効
画面を含み周縁わん曲部と接する近傍までを覆う範囲に
補強用のプラスチックシート１０５を感圧性接着剤を介
して貼着する方法がある（特開昭５２−８７３５３号公
報）。2. Description of the Related Art In a cathode ray tube of a television receiver or the like, when a shock is applied to the cathode ray tube from the outside, various reinforcements are provided in order to absorb the shock and prevent glass scattering at the time of implosion. Measures are taken. As a reinforcing measure, for example, as shown in FIG.
A method for arranging a reinforcing metal ring body 102 on the outer peripheral portion of the side surface and interposing a resin tape 103 as a metal ring body buffer adhesive between the metal ring body 102 and the glass panel 101, and FIG. As described above, there is a method in which the reinforcing plastic sheet 105 is attached to the area including the effective screen of the face plate 104 and covering the vicinity of the contact with the peripheral curved portion via a pressure sensitive adhesive (Japanese Patent Laid-Open No. 52-87353). Issue).
【０００３】[0003]
【発明が解決しようとする課題】しかし、上記のような
従来の構成では、フェイスプレートが球面もしくは円筒
型の場合にはその効果が大きいが、一様に平らなフェイ
スプレートを有するガラスパネルの場合には、そのフェ
イスプレートの形状から球面や円筒型の場合に比較して
バルブ自身にかかる真空ストレスが高くなってしまい、
その結果、外部からの衝撃に対して弱くなってしまう。
このように、一様に平らなフェイスプレートを有するガ
ラスパネルの場合、ガラスパネルの側面外周部に補強用
の金属環体を配置し、この金属環体とガラスパネルとの
間に樹脂テープを介在させるだけでは補強効果が小さ
く、その結果、爆縮時におけるガラス飛散を防止し、電
気用品取締法、ＵＬ、ＣＳＡ等の安全規格を満たすこと
は困難である。また、フェイスプレートの周縁わん曲部
と接する近傍までを覆う範囲にプラスチックシートを貼
着する方法では、補強効果が小さく、その結果、爆縮時
にプラスチックシートの周縁部からガラスパネルの破壊
が生じ、プラスチックごとバルブ内に吸い込まれるた
め、ガラス飛散を防止することはできない。However, in the conventional structure as described above, the effect is great when the face plate is spherical or cylindrical, but in the case of a glass panel having a uniformly flat face plate. , The face plate has a higher vacuum stress on the valve itself than the spherical or cylindrical type.
As a result, it becomes vulnerable to external impact.
As described above, in the case of a glass panel having a uniformly flat face plate, a metal ring for reinforcement is arranged on the outer periphery of the side surface of the glass panel, and a resin tape is interposed between the metal ring and the glass panel. Only by doing so, the reinforcing effect is small, and as a result, it is difficult to prevent glass scattering at the time of implosion and satisfy the safety standards such as the Electrical Appliance and Material Control Law, UL and CSA. Also, in the method of sticking the plastic sheet in the range covering up to the vicinity of the contact with the peripheral curved portion of the face plate, the reinforcing effect is small, and as a result, the glass panel is destroyed from the peripheral portion of the plastic sheet at the time of implosion, Since the plastic is sucked into the bulb, it is not possible to prevent the glass from scattering.
【０００４】本発明は、従来技術における前記課題を解
決するため、一様に平らなフェイスプレートを有するガ
ラスパネルにおける爆縮時のガラス飛散を防止し、か
つ、コストの低減をも図ることのできる補強型陰極線管
を提供することを目的とする。In order to solve the above-mentioned problems in the prior art, the present invention can prevent glass from scattering at the time of implosion in a glass panel having a uniformly flat face plate and can also reduce the cost. An object is to provide a reinforced cathode ray tube.
【０００５】[0005]
【課題を解決するための手段】前記目的を達成するた
め、本発明に係る補強型陰極線管の第１の構成は、一様
に平らなフェイスプレートを有するガラスパネルと、前
記ガラスパネルの後部に接続されたガラスファンネル
と、前記ガラスパネルの側面外周部に配置された補強用
金属環体とを備えた補強型陰極線管であって、前記フェ
イスプレートの表面及び前記補強用金属環体を覆うよう
に、樹脂シートを前記ガラスパネル及び前記に補強用金
属環体に貼着剤によって貼着したことを特徴とする。In order to achieve the above-mentioned object, a first structure of a reinforced cathode ray tube according to the present invention is a glass panel having a uniformly flat face plate, and a glass panel provided on the rear part of the glass panel. What is claimed is: 1. A reinforced cathode ray tube comprising a connected glass funnel and a reinforcing metal annulus arranged on an outer peripheral portion of a side surface of the glass panel, which covers the surface of the face plate and the reinforcing metal annulus. In addition, the resin sheet is attached to the glass panel and the reinforcing metal ring body with an adhesive.
【０００６】また、本発明に係る補強型陰極線管の第２
の構成は、一様に平らなフェイスプレートを有するガラ
スパネルと、前記ガラスパネルの後部に接続されたガラ
スファンネルと、前記ガラスパネルの側面外周部に配置
された補強用金属環体とを備えた補強型陰極線管であっ
て、前記フェイスプレートの表面及び前記ガラスパネル
の側面外周部を覆うように、樹脂シートを前記ガラスパ
ネルに貼着し、前記ガラスパネルの側面外周部における
樹脂シートの上から前記補強用金属環体を焼きはめした
ことを特徴とする。The second aspect of the reinforced cathode ray tube according to the present invention
The configuration of (1) comprises a glass panel having a uniformly flat face plate, a glass funnel connected to the rear portion of the glass panel, and a reinforcing metal ring disposed on the side surface outer peripheral portion of the glass panel. Reinforced cathode ray tube, so as to cover the surface of the face plate and the side surface outer peripheral portion of the glass panel, a resin sheet is attached to the glass panel, from above the resin sheet in the side surface outer peripheral portion of the glass panel. It is characterized in that the reinforcing metal ring is heat-shrinked.
【０００７】また、前記本発明の第１又は第２の構成に
おいては、樹脂シートとして、膜厚が５０μｍ以上３０
０μｍ以下のポリエチレンテレフタレートを用いるのが
好ましく、この場合にはさらに、ポリエチレンテレフタ
レートの表面に硬化膜を形成し、粘着剤として強粘性で
硬質な材料を付加したものであるのが好ましい。In the first or second structure of the present invention, the resin sheet has a film thickness of 50 μm or more and 30 or more.
It is preferable to use polyethylene terephthalate having a thickness of 0 μm or less. In this case, it is preferable that a cured film is further formed on the surface of polyethylene terephthalate, and a viscous and hard material is added as an adhesive.
【０００８】[0008]
【作用】前記本発明の第１の構成によれば、ガラスパネ
ルのフェイスプレートの表面及び側面外周部に配置され
た補強用金属環体を覆うように、樹脂シートを前記ガラ
スパネルに貼着したことにより、樹脂シートがガラスパ
ネルに強く貼着されるので、ガラスパネルの前面のフェ
イスプレート及び側面外周部は樹脂シートと補強用金属
環体とによって完全に補強される。従って、陰極線管に
外部から衝撃が加えられて爆縮が生じた場合において
も、ガラスがパネルの前面に飛散することはなく、その
結果、電気用品取締法、ＵＬ、ＣＳＡ等の安全規格を十
分に満足させることができる。また、樹脂シートの貼り
替えが可能であるので、樹脂シートを貼着した後に、フ
ェイスプレートの表面に傷等の不良が生じた場合には、
樹脂シートを剥すだけで容易に再生することができ、そ
の結果、コストの低減を図ることができる。According to the first structure of the present invention, the resin sheet is attached to the glass panel so as to cover the reinforcing metal ring disposed on the surface and the outer periphery of the side surface of the face plate of the glass panel. As a result, the resin sheet is strongly adhered to the glass panel, so that the face plate on the front surface and the outer peripheral portion of the side surface of the glass panel are completely reinforced by the resin sheet and the reinforcing metal ring. Therefore, even if an impact is applied to the cathode ray tube from the outside to cause implosion, the glass does not scatter on the front surface of the panel, and as a result, the safety standards such as the Electrical Appliance and Material Control Law, UL, CSA, etc. are sufficiently satisfied. Can be satisfied with. Also, since the resin sheet can be replaced, if defects such as scratches occur on the surface of the face plate after attaching the resin sheet,
The resin sheet can be easily recycled by peeling it off, and as a result, the cost can be reduced.
【０００９】また、前記本発明の第２の構成によれば、
ガラスパネルのフェイスプレートの表面及び側面外周部
を覆うように、樹脂シートを前記ガラスパネルに貼着
し、前記ガラスパネルの側面外周部における樹脂シート
の上から前記補強用金属環体を焼きはめしたことによ
り、補強用金属環体と樹脂シートとが熱によって強く接
着されるので、ガラスパネルの前面のフェイスプレート
及び側面外周部は樹脂シートと補強用金属環体とによっ
てさらに完全に補強される。従って、陰極線管に外部か
ら衝撃が加えられて爆縮が生じた場合においても、ガラ
スがパネルの前面に飛散することはなく、その結果、電
気用品取締法、ＵＬ、ＣＳＡ等の安全規格を十分に満足
させることができる。また、樹脂シートが補強用金属環
体とガラスパネルとの間に配置された形となるので、従
来補強用金属環体とガラスパネルとの間に介在させてい
た緩衝接着剤としての樹脂テープを使用する必要はな
く、その結果、コストの低減を図ることができる。According to the second aspect of the present invention,
A resin sheet was attached to the glass panel so as to cover the surface and the side surface outer periphery of the face plate of the glass panel, and the reinforcing metal ring was baked from above the resin sheet in the side surface outer periphery of the glass panel. As a result, the reinforcing metal ring and the resin sheet are strongly adhered to each other by heat, so that the face plate on the front surface and the outer peripheral portion of the side surface of the glass panel are further completely reinforced by the resin sheet and the reinforcing metal ring. Therefore, even if an external shock is applied to the cathode ray tube to cause implosion, the glass does not scatter on the front surface of the panel, and as a result, the safety standards such as the Electrical Appliance and Material Control Law, UL, CSA, etc. are sufficiently satisfied. Can be satisfied with. In addition, since the resin sheet is arranged between the reinforcing metal ring and the glass panel, the resin tape as the buffer adhesive that has been conventionally interposed between the reinforcing metal ring and the glass panel is used. It is not necessary to use it, and as a result, the cost can be reduced.
【００１０】また、前記本発明の第１又は第２の構成に
おいて、樹脂シートとして、膜厚が５０μｍ以上３００
μｍ以下のポリエチレンテレフタレートを用いるという
好ましい構成によれば、適度の硬度を有し、かつ、爆縮
時に破切されることがないと共に、折り曲げ貼りを容易
に行うことができる。この場合さらに、ポリエチレンテ
レフタレートの表面に硬化膜を形成し、粘着剤として強
粘性で硬質な材料を付加したものであるという好ましい
構成によれば、樹脂シートの硬度をさらに大きくするこ
とができると共に、樹脂シートを強力に接着させること
ができる。In the first or second structure of the present invention, the resin sheet has a thickness of 50 μm or more and 300 or more.
According to the preferable configuration in which polyethylene terephthalate having a thickness of μm or less is used, it has appropriate hardness, is not broken at the time of implosion, and can be easily bent and stuck. In this case, further, according to a preferable configuration in which a hardened film is formed on the surface of polyethylene terephthalate and a viscous and hard material is added as an adhesive, the hardness of the resin sheet can be further increased, and The resin sheet can be strongly bonded.
【００１１】[0011]
【実施例】以下、実施例を用いて本発明をさらに具体的
に説明する。 （実施例１）図１は本発明に係る補強型陰極線管の一実
施例を示す側面図である。図１に示すように、陰極線管
１の外形は、一様に平らなフェイスプレート２を有する
ガラスパネル３と、ガラスパネル３の後部に低膨張ガラ
ス５によって接続されたガラスファンネル４とにより構
成されている。ガラスパネル３の側面外周部８には、補
強用金属環体６が焼きはめされている。そして、ガラス
パネル３のフェイスプレート２の表面及び側面外周部８
に配置された補強用金属環体６を覆うように、樹脂シー
ト７がガラスパネル３及び補強用金属環体６に後述する
貼着剤によって貼着されている。EXAMPLES The present invention will be described in more detail below with reference to examples. (Embodiment 1) FIG. 1 is a side view showing an embodiment of a reinforced cathode ray tube according to the present invention. As shown in FIG. 1, the outer shape of the cathode ray tube 1 is composed of a glass panel 3 having a uniformly flat face plate 2 and a glass funnel 4 connected to the rear portion of the glass panel 3 by a low expansion glass 5. ing. The reinforcing metal ring body 6 is annealed to the side surface outer peripheral portion 8 of the glass panel 3. Then, the surface and side surface outer peripheral portion 8 of the face plate 2 of the glass panel 3
The resin sheet 7 is attached to the glass panel 3 and the reinforcing metal annular body 6 by an adhesive agent described below so as to cover the reinforcing metal annular body 6 arranged in.
【００１２】樹脂シート７は、膜厚が１００μｍで、フ
ェイスプレート２を囲み補強用金属環体６まで覆う大き
さを有しており、その展開形は図３に示すように長方形
の四隅の部分を切り取った十字形をしている。樹脂シー
ト７の材質はポリエチレンテレフタレートであり、表面
には例えばモノメチルポリシロキサンよりなる透明シリ
コンレンジ等の被膜を塗布することにより硬化処理が施
されている。また、粘着剤としては、例えばアクリル系
樹脂又はシリコーン系樹脂等による強粘着で硬質なもの
を使用する。以上のような構成を有する樹脂シート７に
対して１ｋｇの鉛筆引っかきテストを行ったところ、３
Ｈ以上の強度を確保することができた。The resin sheet 7 has a film thickness of 100 μm and has a size that surrounds the face plate 2 and covers the reinforcing metal ring 6, and its developed form is the four corners of the rectangle as shown in FIG. It has a cross shape that is cut out. The material of the resin sheet 7 is polyethylene terephthalate, and the surface of the resin sheet 7 is hardened by applying a coating such as a transparent silicon range made of monomethyl polysiloxane. Further, as the adhesive, for example, a strong and hard adhesive made of acrylic resin or silicone resin is used. When a 1 kg pencil scratch test was performed on the resin sheet 7 having the above-mentioned configuration, it was 3
It was possible to secure a strength of H or higher.
【００１３】上記のように、ガラスパネル３のフェイス
プレート２の表面及び側面外周部８に配置された補強用
金属環体６を覆うように、樹脂シート７をガラスパネル
３に貼着したことにより、樹脂シート７がガラスパネル
３に強く貼着される。このため、ガラスパネル３の前面
のフェイスプレート２及び側面外周部８は樹脂シート７
と補強用金属環体６とによって完全に補強される。この
場合の粘着力は６００ｇｆ／１０ｍｍ、引張強度は１７
ｋｇｆ／１０ｍｍであった（試験法はＪＩＳ−Ｚ０２３
７による）。従って、陰極線管１に外部から衝撃が加え
られて爆縮が生じた場合においても、ガラスがパネルの
前面に飛散することはないので、ＵＬ、ＣＳＡ等の安全
規格を十分に満足させることができる。As described above, the resin sheet 7 is attached to the glass panel 3 so as to cover the surface of the face plate 2 of the glass panel 3 and the reinforcing metal ring 6 arranged on the side surface outer peripheral portion 8. , The resin sheet 7 is strongly adhered to the glass panel 3. For this reason, the face plate 2 on the front surface of the glass panel 3 and the side surface outer peripheral portion 8 are covered with the resin sheet 7
And is completely reinforced by the reinforcing metal ring 6. In this case, the adhesive strength is 600 gf / 10 mm and the tensile strength is 17
It was kgf / 10 mm (the test method is JIS-Z023.
7). Therefore, even if an external shock is applied to the cathode ray tube 1 to cause implosion, the glass does not scatter on the front surface of the panel, so that safety standards such as UL and CSA can be sufficiently satisfied. .
【００１４】尚、本実施例１においては、ポリエチレン
テレフタレートからなる樹脂シート７の膜厚を１００μ
ｍにしているが、必ずしもこの数値に限定されるもので
はなく、５０μｍ以上３００μｍ以下であればよい。５
０μｍ以上の膜厚であれば爆縮時に破切されることがな
く、３００μｍ以下の膜厚であれば折り曲げ貼りを容易
に行うことができる。また、樹脂シート７を貼り付けた
後に、フェイスプレート２の表面に傷等の不良が生じた
場合には、樹脂シート７を剥すだけで再生可能となるの
で、コストの低減を図ることができる。In the first embodiment, the resin sheet 7 made of polyethylene terephthalate has a thickness of 100 μm.
However, the value is not limited to this value, and may be 50 μm or more and 300 μm or less. 5
If the film thickness is 0 μm or more, the film is not broken at the time of implosion, and if the film thickness is 300 μm or less, bending and sticking can be easily performed. Further, after the resin sheet 7 is attached, if a defect such as a scratch occurs on the surface of the face plate 2, the resin sheet 7 can be regenerated simply by peeling it off, so that the cost can be reduced.
【００１５】（実施例２）図２は本発明に係る補強型陰
極線管の他の実施例を示す側面図である。図２に示すよ
うに、陰極線管９は、一様に平らなフェイスプレート１
０を有するガラスパネル１１と、ガラスパネル１１の後
部に低膨張ガラス１３によって接続されたガラスファン
ネル１２とにより構成されている。(Embodiment 2) FIG. 2 is a side view showing another embodiment of the reinforced cathode ray tube according to the present invention. As shown in FIG. 2, the cathode ray tube 9 has a uniformly flat face plate 1
It is composed of a glass panel 11 having 0 and a glass funnel 12 connected to the rear portion of the glass panel 11 by a low expansion glass 13.
【００１６】ガラスパネル１１のフェイスプレート１０
及び側面外周部１５は、樹脂シート１４によって覆われ
ている。樹脂シート１４は、膜厚が１００μｍで、その
展開形は図３に示すように長方形の四隅の部分を切り取
った十字形をしている。樹脂シート１４の材質はポリエ
チレンテレフタレートであり、表面には例えばモノメチ
ルポリシロキサンよりなる透明シリコンレンジ等の被膜
を塗布することにより硬化処理が施されている。また、
粘着剤としては、例えばアクリル系樹脂又はシリコーン
系樹脂等による強粘性で硬質なものを使用する。以上の
ような構成を有する樹脂シート１４に対して１ｋｇの鉛
筆引っかきテストを行ったところ、３Ｈ以上の強度を確
保することができた。Face plate 10 of glass panel 11
The side surface outer peripheral portion 15 is covered with the resin sheet 14. The resin sheet 14 has a film thickness of 100 μm, and its developed shape is a cross shape in which four corners are cut off as shown in FIG. The material of the resin sheet 14 is polyethylene terephthalate, and the surface thereof is subjected to a curing treatment by applying a coating film such as a transparent silicon range made of monomethylpolysiloxane. Also,
As the adhesive, for example, a highly viscous and hard one made of acrylic resin or silicone resin is used. When a 1 kg pencil scratch test was performed on the resin sheet 14 having the above-described structure, a strength of 3H or more could be secured.
【００１７】樹脂シート１４の上から補強用金属環体１
６を熱膨張させてガラスパネル１１の側面外周部１５に
焼きはめする。すると、補強用金属環体１６の熱によっ
て樹脂シート１４が補強用金属環体１６に強く接着され
る。このため、ガラスパネル１１の前面のフェイスプレ
ート１０及び側面外周部１５は樹脂シート１４と補強用
金属環体１６とによってさらに完全に補強される。従っ
て、陰極線管９に外部から衝撃が加えられて爆縮が生じ
た場合においても、ガラスがパネルの前面に飛散するこ
とはないので、電気用品取締法、ＵＬ、ＣＳＡ等の安全
規格を十分に満足させることができる。また、樹脂シー
ト１４が補強用金属環体１６とガラスパネル１１との間
に配置された形となるので、従来補強用金属環体とガラ
スパネルとの間に介在させていた緩衝接着剤としての樹
脂テープを使用する必要はなく、その結果、コストの低
減を図ることができる。From the top of the resin sheet 14, the reinforcing metal ring 1
6 is thermally expanded and heat-shrinked to the side surface outer peripheral portion 15 of the glass panel 11. Then, the resin sheet 14 is strongly adhered to the reinforcing metal ring body 16 by the heat of the reinforcing metal ring body 16. Therefore, the front face plate 10 and the side surface outer peripheral portion 15 of the glass panel 11 are further completely reinforced by the resin sheet 14 and the reinforcing metal ring body 16. Therefore, even if an impact is applied to the cathode ray tube 9 from the outside to cause implosion, the glass does not scatter on the front surface of the panel, and therefore the safety standards such as the Electrical Appliance and Material Control Law, UL, CSA, etc. are sufficiently satisfied. Can be satisfied. Further, since the resin sheet 14 is arranged between the reinforcing metal ring body 16 and the glass panel 11, the resin sheet 14 serves as a buffer adhesive which is conventionally interposed between the reinforcing metal ring body and the glass panel. It is not necessary to use a resin tape, and as a result, the cost can be reduced.
【００１８】[0018]
【発明の効果】以上説明したように、本発明に係る補強
型陰極線管の第１の構成によれば、ガラスパネルのフェ
イスプレートの表面及び側面外周部に配置された補強用
金属環体を覆うように、樹脂シートを前記ガラスパネル
及び前記補強用金属環体に貼着剤によって貼着したこと
により、樹脂シートがガラスパネルに強く貼着されるの
で、ガラスパネルの前面のフェイスプレート及び側面外
周部は樹脂シートと補強用金属環体とによって完全に補
強される。従って、陰極線管に外部から衝撃が加えられ
て爆縮が生じた場合においても、ガラスがパネルの前面
に飛散することはなく、その結果、電気用品取締法、Ｕ
Ｌ、ＣＳＡ等の安全規格を十分に満足させることができ
る。また、樹脂シートの貼り替えが可能であるので、樹
脂シートを貼着した後に、フェイスプレートの表面に傷
等の不良が生じた場合には、樹脂シートを剥すだけで容
易に再生することができ、その結果、コストの低減を図
ることができる。As described above, according to the first configuration of the reinforced cathode ray tube according to the present invention, the reinforcing metal ring bodies arranged on the outer surface and the outer surface of the face plate of the glass panel are covered. As described above, by attaching the resin sheet to the glass panel and the reinforcing metal ring body with the adhesive, the resin sheet is strongly attached to the glass panel. The part is completely reinforced by the resin sheet and the reinforcing metal ring. Therefore, even when an external shock is applied to the cathode ray tube to cause implosion, the glass does not scatter on the front surface of the panel. As a result, the Electrical Appliance and Material Control Law, U
It is possible to sufficiently satisfy safety standards such as L and CSA. Also, because the resin sheet can be replaced, if defects such as scratches occur on the surface of the face plate after attaching the resin sheet, it can be easily regenerated simply by removing the resin sheet. As a result, the cost can be reduced.
【００１９】また、本発明に係る補強型陰極線管の第２
の構成によれば、ガラスパネルのフェイスプレートの表
面及び側面外周部を覆うように、樹脂シートを前記ガラ
スパネルに貼着し、前記ガラスパネルの側面外周部にお
ける樹脂シートの上から前記補強用金属環体を焼きはめ
したことにより、補強用金属環体と樹脂シートとが熱に
よって強く接着されるので、ガラスパネルの前面のフェ
イスプレート及び側面外周部は樹脂シートと補強用金属
環体とによってさらに完全に補強される。従って、陰極
線管に外部から衝撃が加えられて爆縮が生じた場合にお
いても、ガラスがパネルの前面に飛散することはなく、
その結果、電気用品取締法、ＵＬ、ＣＳＡ等の安全規格
を十分に満足させることができる。また、樹脂シートが
補強用金属環体とガラスパネルとの間に配置された形と
なるので、従来補強用金属環体とガラスパネルとの間に
介在させていた緩衝接着剤としての樹脂テープを使用す
る必要はなく、その結果、コストの低減を図ることがで
きる。The second embodiment of the reinforced cathode ray tube according to the present invention
According to the configuration, the resin sheet is attached to the glass panel so as to cover the surface and the side surface outer peripheral portion of the face plate of the glass panel, and the reinforcing metal is applied from above the resin sheet in the side surface outer peripheral portion of the glass panel. Since the metal ring for reinforcement and the resin sheet are strongly bonded by heat by the annealing of the ring body, the face plate on the front face of the glass panel and the outer peripheral surface of the side face are further bonded by the resin sheet and the metal ring body for reinforcement. Fully reinforced. Therefore, even when an external shock is applied to the cathode ray tube to cause implosion, the glass does not scatter on the front surface of the panel,
As a result, safety standards such as the Electrical Appliance and Material Control Law, UL, and CSA can be sufficiently satisfied. In addition, since the resin sheet is arranged between the reinforcing metal ring and the glass panel, the resin tape as the buffer adhesive that has been conventionally interposed between the reinforcing metal ring and the glass panel is used. It is not necessary to use it, and as a result, the cost can be reduced.
【００２０】また、前記本発明の第１又は第２の構成に
おいて、樹脂シートとして、膜厚が５０μｍ以上３００
μｍ以下のポリエチレンテレフタレートを用いるという
好ましい構成によれば、適度の硬度を有し、かつ、爆縮
時に破切されることがないと共に、折り曲げ貼りを容易
に行うことができる。この場合さらに、ポリエチレンテ
レフタレートの表面に硬化膜を形成し、粘着剤として強
粘性で硬質な材料を付加したものであるという好ましい
構成によれば、樹脂シートの硬度をさらに大きくするこ
とができると共に、樹脂シートを強力に接着させること
ができる。In the first or second structure of the present invention, the resin sheet has a film thickness of 50 μm or more and 300 or more.
According to the preferable configuration in which polyethylene terephthalate having a thickness of μm or less is used, it has appropriate hardness, is not broken at the time of implosion, and can be easily bent and stuck. In this case, further, according to a preferable configuration in which a hardened film is formed on the surface of polyethylene terephthalate and a viscous and hard material is added as an adhesive, the hardness of the resin sheet can be further increased, and The resin sheet can be strongly bonded.
【図１】本発明に係る補強型陰極線管の一実施例を示す
側面図である。FIG. 1 is a side view showing an embodiment of a reinforced cathode ray tube according to the present invention.
【図２】本発明に係る補強型陰極線管の他の実施例を示
す側面図である。FIG. 2 is a side view showing another embodiment of the reinforced cathode ray tube according to the present invention.
【図３】本発明における樹脂シートの展開図である。FIG. 3 is a development view of a resin sheet according to the present invention.
【図４】従来技術における補強型陰極線管の側面図であ
る。FIG. 4 is a side view of a conventional reinforced cathode ray tube.
【図５】従来技術における補強型陰極線管の側面図であ
る。FIG. 5 is a side view of a reinforced cathode ray tube in the prior art.
１ 陰極線管 ２ フェイスプレート ３ ガラスパネル ４ ガラスファンネル ５ 低膨張ガラス ６ 補強用金属環体 ７ 樹脂シート ８ 側面外周部 ９ 陰極線管 １０ フェイスプレート １１ ガラスパネル １２ ガラスファンネル １３ 低膨張ガラス １４ 樹脂シート １５ 側面部 １６ 補強用金属環体 １０１ ガラスパネル １０２ 金属環体 １０３ 樹脂テープ １０４ フェイスプレート １０５ 補強用プラスッチクシート DESCRIPTION OF SYMBOLS 1 Cathode ray tube 2 Face plate 3 Glass panel 4 Glass funnel 5 Low expansion glass 6 Metal ring 7 for reinforcement 7 Resin sheet 8 Side peripheral part 9 Cathode ray tube 10 Face plate 11 Glass panel 12 Glass funnel 13 Low expansion glass 14 Resin sheet 15 Side surface Part 16 Metal ring 101 for reinforcement 101 Glass panel 102 Metal ring 103 Resin tape 104 Face plate 105 Plastic sheet for reinforcement
Claims (4)
ガラスパネルと、前記ガラスパネルの後部に接続された
ガラスファンネルと、前記ガラスパネルの側面外周部に
配置された補強用金属環体とを備えた補強型陰極線管で
あって、前記フェイスプレートの表面及び前記補強用金
属環体を覆うように、樹脂シートを前記ガラスパネル及
び前記補強用金属環体に粘着剤によって貼着したことを
特徴とする補強型陰極線管。1. A glass panel having a uniformly flat face plate, a glass funnel connected to a rear portion of the glass panel, and a reinforcing metal ring disposed on an outer periphery of a side surface of the glass panel. A reinforcing type cathode ray tube, characterized in that a resin sheet is attached to the glass panel and the reinforcing metal ring body with an adhesive so as to cover the surface of the face plate and the reinforcing metal ring body. Reinforced cathode ray tube.
ガラスパネルと、前記ガラスパネルの後部に接続された
ガラスファンネルと、前記ガラスパネルの側面外周部に
配置された補強用金属環体とを備えた補強型陰極線管で
あって、前記フェイスプレートの表面及び前記ガラスパ
ネルの側面外周部を覆うように、樹脂シートを前記ガラ
スパネルに貼着し、前記ガラスパネルの側面外周部にお
ける樹脂シートの上から前記補強用金属環体を焼きはめ
したことを特徴とする補強型陰極線管。2. A glass panel having a uniformly flat face plate, a glass funnel connected to a rear portion of the glass panel, and a reinforcing metal ring disposed on an outer peripheral portion of a side surface of the glass panel. A reinforcing type cathode ray tube, wherein a resin sheet is attached to the glass panel so as to cover the surface of the face plate and the side surface outer peripheral portion of the glass panel, and the resin sheet is provided on the side surface outer peripheral portion of the glass panel. A reinforced cathode ray tube characterized in that the reinforcing metal ring is heat-shrinked.
３００μｍ以下のポリエチレンテレフタレートを用いる
請求項１又は２に記載の補強型陰極線管。3. The reinforced cathode ray tube according to claim 1, wherein polyethylene terephthalate having a film thickness of 50 μm or more and 300 μm or less is used as the resin sheet.
化膜を形成し、粘着剤として強粘性で硬質な材料を付加
した請求項３に記載の補強型陰極線管。4. The reinforced cathode ray tube according to claim 3, wherein a cured film is formed on the surface of polyethylene terephthalate, and a viscous and hard material is added as an adhesive.