JPH11316547A - Film sheet with ink receiving layer surface and repeeling and sticking layer - Google Patents
Film sheet with ink receiving layer surface and repeeling and sticking layerInfo
- Publication number
- JPH11316547A JPH11316547A JP10122416A JP12241698A JPH11316547A JP H11316547 A JPH11316547 A JP H11316547A JP 10122416 A JP10122416 A JP 10122416A JP 12241698 A JP12241698 A JP 12241698A JP H11316547 A JPH11316547 A JP H11316547A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- film sheet
- ink
- sheet according
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、基材フイルムの一
方の表面に複写技術により高解像・高濃度の画像を形成
しうるインキ受理層を形成し、他方の表面に印刷法によ
り再剥離性貼着性を有する粘着層乃至粘弾性体層を形成
したフイルムシート、特に電子写真法などによりギラギ
ラした感じのない、ソフトであるが、解像度がよいカラ
ー画像を形成できる、個人が複写技術によって所望のカ
ラー画像を形成してマウスマットなどの製品を作ること
ができるフイルムシートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink receiving layer capable of forming a high-resolution and high-density image on one surface of a substrate film by a copying technique, and re-peeling on the other surface by a printing method. A film sheet on which an adhesive layer or a viscoelastic layer having an adhesive property is formed, especially a soft, high-resolution color image without a feeling of glaring by electrophotography, etc. The present invention relates to a film sheet capable of forming a desired color image to produce a product such as a mouse mat.
【０００２】[0002]
【従来技術】従来、フイルムシートに印刷性などの機能
を付与するために、フイルム表面に平均粒径が５μ未満
の白色顔料などを配合したコーティング層を形成するこ
とは知られているが、該コーティング層を形成したフイ
ルムシートは、従来からの高度な印刷法を用いれば実用
になり得る画像が形成できる程度のものである。また、
このようにして作られた画像は、ＰＯＰ、看板などの表
示用として使用するには、バックライトが設備されたガ
ラス面に貼付して使用しないと光の拡散性が十分でない
ために、バックライトの光源の形状が表示面に薄く見え
てしまう等の不都合があった。従って、従来のフイルム
シートは、多量の印刷物を作る印刷法により画像を形成
する材料としては、解像度、画像濃度などの特性をほぼ
満足させうるが、電子写真法などによりギラギラした感
じのない、ソフトであるが、解像度がよいカラー画像が
得られるフイルムシートとしては不十分であった。特に
表示用画像を形成するフイルムシートとしては光の拡散
性が良くないために適さないものであった。また、ディ
ナーシートやマウスマットとしての機能性を充分に併備
することもなかった。2. Description of the Related Art Conventionally, it has been known to form a coating layer containing a white pigment having an average particle size of less than 5 μm on a film surface in order to impart functions such as printability to a film sheet. The film sheet having the coating layer formed thereon is of such a size that an image which can be practically used by using a conventional advanced printing method can be formed. Also,
Images used in this manner are not suitable for use in displays such as POPs and signboards, because light diffusion is not sufficient unless they are used by sticking to the glass surface on which the backlight is installed. However, there is an inconvenience that the shape of the light source looks thin on the display surface. Therefore, a conventional film sheet can almost satisfy characteristics such as resolution and image density as a material for forming an image by a printing method for producing a large amount of printed matter, but is soft, without a feeling of glare by an electrophotographic method or the like. However, it was insufficient as a film sheet capable of obtaining a color image with good resolution. In particular, it is not suitable as a film sheet for forming a display image due to poor light diffusivity. Also, they did not have sufficient functions as a dinner sheet or a mouse mat.
【０００３】[0003]
【発明が解決しようとする課題】このような画像形成用
のフイルムシートの技術状況の下において、少量の、極
端な場合にはたった一枚の表示用の画像が得られれば良
いという場合がある。このような場合には、簡易な複写
技術によって表示などに使用できる品質の画像が形成で
きるフイルムシートが望まれてきた。例えば、通路など
に設けられる小量の広告看板、ＰＯＰ、電飾看板等が即
時に欲しい場合がある。このような場合、身近にある簡
易な複写機などの技術によって即座に必要な表示用画像
を作ることができるフイルムシートが望まれてきた。Under the technical situation of such an image forming film sheet, there is a case where it is sufficient to obtain a small amount of a display image in an extreme case. . In such a case, a film sheet capable of forming an image of a quality that can be used for display or the like by a simple copying technique has been desired. For example, a small amount of advertising signboard, POP, illuminated signboard, or the like provided in a passage or the like may be desired immediately. In such a case, there has been a demand for a film sheet capable of immediately producing a necessary display image by a technique such as a simple copier or the like.
【０００４】更に、この様な簡易な複写技術によって画
像が形成できるフイルムシートの開発の中で、いわゆる
パーソナルユーズの製品においても、差別化された画像
或いは模様を施した、特にカラーの画像或いは模様を施
したものを求めるようなってきた。例えば、ディナーシ
ート、マウスマットなどのパーソナルユーズの生活製品
を簡易な複写技術によって模様付けして作ることができ
るフイルムシートなどが望まれるようになってきた。こ
のような社会的ニーズに答えられる品質のフイルムシー
トを提供することが本発明の課題である。特に、マウス
マット、ディナーシートなどのパーソナルユーズの生活
製品を簡易な複写技術によって模様付けして作ることが
できるフイルムシートを提供することが本発明の課題で
ある。Further, in the development of a film sheet on which an image can be formed by such a simple copying technique, a so-called personal use product is provided with a differentiated image or pattern, especially a color image or pattern. I have been looking for something that has been subjected to. For example, there has been a growing demand for a film sheet or the like which can be made by patterning a personal use life product such as a dinner sheet or a mouse mat by a simple copying technique. It is an object of the present invention to provide a film sheet of a quality that can meet such social needs. In particular, it is an object of the present invention to provide a film sheet that can be made by patterning personal life products such as a mouse mat and a dinner sheet by a simple copying technique.
【０００５】[0005]
【課題を解決するための手段】前記本発明の課題を解決
するために、フイルムシートの表面を複写技術によって
前記所望の画質の像を形成し得るように改質するにはど
うすればよいかを鋭意検討を重ねた結果、基材フイルム
表面に、平均粒径が５μ〜４０μの球体であるビーズを
１５〜３５重量％インキベースに配合したインキを使用
し、印刷法、特にスクリーン印刷法により厚さ５μ〜１
００μの層を形成すれば前記課題の複写技術によって画
像が形成できるフイルムシートの得られることが分かっ
た。SUMMARY OF THE INVENTION In order to solve the above-mentioned problems of the present invention, the present inventors have intensively studied how to modify the surface of a film sheet by a copying technique so as to form an image having the desired image quality. As a result of repeated investigations, the ink was prepared by blending 15 to 35% by weight of an ink base with spherical beads having an average particle diameter of 5 to 40 μm on the surface of the base film, and the thickness was determined by a printing method, particularly a screen printing method. 5μ-1
It was found that a film sheet on which an image can be formed by the above-mentioned copying technique can be obtained by forming a layer having a thickness of 00 μ.
【０００６】また、このような検討の中で前記球体ビー
ズを受理層に配合することによって、特にウレタン樹脂
ビーズを配合することにより、インキ受理層に所望の画
像を電子写真などの複写技術によって形成した後におい
てもフイルムシートの表面は、マウスなどの動きが良
く、且つ耐摩耗性の特性を有する表面が得られ、かつ複
写技術によって再現性の良いカラー画像が形成できるフ
イルムシートが得られることが分かった。そして、前記
のような受理層を設けることにより光散乱性（拡散性）
が増しバックライトの形が見えなくなりより高品位な表
示用画像を得ることが可能なことが分かった。形状的に
は違いがないのに、ウレタン樹脂ビーズを使用した場合
に、光散乱性等の光学特性の改善の効果が著しいのは意
外であった。また、得られたカラー画像の耐光性、耐候
性も優れていた。[0006] In such studies, the desired image is formed on the ink receiving layer by a copying technique such as electrophotography by blending the spherical beads in the receiving layer, particularly by blending urethane resin beads. Even after this, the surface of the film sheet can be moved by a mouse or the like, and a surface having abrasion resistance can be obtained, and a film sheet capable of forming a color image with good reproducibility by a copying technique can be obtained. Do you get it. By providing the receiving layer as described above, light scattering (diffusion) can be achieved.
It was found that the shape of the backlight became invisible and a higher quality display image could be obtained. Although there was no difference in shape, it was surprising that the effect of improving optical characteristics such as light scattering was remarkable when urethane resin beads were used. The obtained color image was also excellent in light resistance and weather resistance.
【０００７】更に、前記ウレタン樹脂ビーズなどを配合
したインキのベースに電離放射線により固化する成分を
配合した印刷インキを用いることにより摩耗性がより改
善されたフイルムシートが得られ、該フイルムを所望の
製品の形状、例えばマウスマットの大きさに裁断して製
品とすれば、該製品の購入者は複写手段などにより所望
の画像または模様を施したマウスマット等とすることが
できる。Further, by using a printing ink containing a component which solidifies by ionizing radiation in the base of the ink containing the urethane resin beads and the like, a film sheet with further improved abrasion can be obtained, and the desired film can be obtained. If the product is cut into the shape of the product, for example, the size of a mouse mat, the purchaser of the product can obtain a mouse mat or the like on which a desired image or pattern is provided by a copying means or the like.
【０００８】特に、マウスマット等のよう製品として使
用する場合には、インキ受理層を施してない面に、印刷
法よってマウスマット等を机などの表面に剥離し得るよ
うに固定できる再剥離性貼着性を有する粘着層乃至粘弾
性体層を形成すれば、該シートを一時的に所望の表面に
固定することができるメリットがあり、マウスマット等
のフイルムシートの用途の機能を向上させる効果があ
る。In particular, when used as a product such as a mouse mat, the removability can be fixed so that the mouse mat can be peeled off to the surface of a desk or the like by a printing method on the surface not provided with the ink receiving layer. Forming an adhesive layer or a viscoelastic layer having an adhesive property has an advantage that the sheet can be temporarily fixed to a desired surface, and has an effect of improving the function of a film sheet such as a mouse mat. There is.
【０００９】従って、本願発明の要旨は、基材フイルム
の一方の表面に印刷法により平均粒径が５μ〜４０μの
球体であるビーズを１５〜３５重量％インキベースに配
合したインキを使用して厚さ５μ〜１００μの複写技術
により画像を形成し得るインキ受理層を形成し、基材フ
イルムの他方の表面に印刷法により再剥離性貼着性を有
する粘着層乃至粘弾性体層を形成したフイルムシートに
ある。Therefore, the gist of the present invention is to use an ink in which sphere beads having an average particle diameter of 5 to 40 μ are blended on one surface of a base film by a printing method in an ink base of 15 to 35% by weight. An ink-receiving layer capable of forming an image was formed by a copying technique having a thickness of 5 μ to 100 μ, and an adhesive layer or a viscoelastic layer having removable adhesive properties was formed on the other surface of the base film by a printing method. It is on the film sheet.
【００１０】本明細書において、「複写技術」とは、ト
ナー、静電トナーなどを使用して画像を形成する電子写
真、インクジェット記録、熱転写等を意味し、版を起こ
して印刷機を用いて印刷するグラビア印刷等と区別する
ものである。In this specification, the term "copying technology" means electrophotography, ink jet recording, thermal transfer, etc., which form an image using toner, electrostatic toner, or the like. It is distinguished from gravure printing or the like for printing.
【００１１】[0011]
【発明の実施の態様】本発明を図面を参照しながら説明
する。本発明において、基材フイルム２としては、ポリ
エステルフイルム、アクリルフイルム、ポリカーボネー
トフイルム、ポリオレフィンフイルム等の合成樹脂フイ
ルム、薄い金属フイルム等が使用できる。ポリエステル
フイルムは、機械的強度、寸法安定性、熱的安定性の点
で優れ、アクリルフイルムは透明性などの点で優れてい
る。従って、フイルムシートの使用用途との関連で使用
する基材フイルムを選択する必要がある。これらの基材
フイルムは、インキ受理層を形成する前に基材フイルム
表面をインキとの接着性を改善するための処理、例えば
コロナ放電処理などをしても良い。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described with reference to the drawings. In the present invention, as the base film 2, a synthetic resin film such as a polyester film, an acrylic film, a polycarbonate film, a polyolefin film, and a thin metal film can be used. Polyester films are excellent in mechanical strength, dimensional stability and thermal stability, and acrylic films are excellent in transparency and the like. Therefore, it is necessary to select a base film to be used in relation to the intended use of the film sheet. These base films may be subjected to a treatment for improving the adhesion of the base film to the ink, for example, a corona discharge treatment, before forming the ink receiving layer.
【００１２】インキ組成物を作るためのベースに使用さ
れる樹脂は、基材フイルムとして使用される材料との関
係で選択することができる。例えば基材フイルムとして
ポリエステルフイルムを使用する場合にはインキベース
の樹脂としてポリエステル樹脂を、またアクリルフイル
ムを使用する場合には塩ビ−酢ビ共重合体を使用するこ
とによって、基材フイルムとインキ受理層とに強固な結
合が形成できる。また、インキベースとしては、複写技
術との関係で画像形成インキの受理性の良いもの、例え
ば、インクジェット記録技術では水性インキが使用され
ているから、水性インキの受理性の良いものを、また電
子写真では加熱定着性トナーが使用されるから、そのよ
うなトナーを加熱定着したときに該トナーの受理性の良
いものを選択することが重要である。[0012] The resin used as the base for making the ink composition can be selected in relation to the material used as the base film. For example, when a polyester film is used as a base film, a polyester resin is used as an ink-based resin, and when an acrylic film is used, a polyvinyl chloride-vinyl acetate copolymer is used. A strong bond can be formed with the layer. Also, as the ink base, one having good receptivity for image forming ink in relation to copying technology, for example, one having good receptivity for water-based ink, since water-based ink is used in ink jet recording technology, Since heat fixing toner is used in photography, it is important to select a toner having good receptivity when such toner is heated and fixed.
【００１３】またインキベースとして、電離放射線、例
えば電子線、及び活性光線、例えば紫外線、などで重
合、架橋などによって固化または硬化し得る成分を含有
するものを使用するようにすれば、前記インキ受理層の
形成を比較的容易にすることができる。このようなイン
キベースには、水溶性のモノマーを配合したもの、非水
溶性のモノマー乃至架橋し得る成分を溶液やエマルジョ
ンの形態で配合したものなどがあり、いずれも本願発明
のインキ受理層を形成したフイルムシートを得る際のイ
ンキ組成物を製造するのに使用できる。前記電離放射線
で固化乃至硬化する水溶性モノマーとしては、多価アル
コールの（メタ）アクリル酸エステル、Ｎ−アルキルア
ミノアルコールの（メタ）アクリル酸エステル、ポリエ
チレングリコール（メタ）アクリル酸エステル、Ｎ−ア
ルキル（メタ）アクリル酸アミド、多価アルコールのビ
ニルエーテル等を挙げることができる。また非水溶性の
モノマーとしては、１，６−ヘキサンジオールジアクリ
レート、トリプロピレングリコールジアクリレート、ネ
オペンチルグリコールジアクリレート、ビニルカプロラ
クタム、２−エチルヘキシルアクリレートなどがある。If the ink base contains a component which can be solidified or cured by ionizing radiation, for example, an electron beam, and actinic rays, for example, ultraviolet rays, by polymerization or crosslinking, etc. Layer formation can be relatively easy. Such ink bases include those containing a water-soluble monomer and those containing a water-insoluble monomer or a crosslinkable component in the form of a solution or an emulsion. It can be used to produce an ink composition for obtaining a formed film sheet. Examples of the water-soluble monomers which are solidified or cured by ionizing radiation include (meth) acrylates of polyhydric alcohols, (meth) acrylates of N-alkylamino alcohols, polyethylene glycol (meth) acrylates, and N-alkyls. (Meth) acrylic acid amide, vinyl ether of polyhydric alcohol and the like can be mentioned. Examples of the water-insoluble monomer include 1,6-hexanediol diacrylate, tripropylene glycol diacrylate, neopentyl glycol diacrylate, vinyl caprolactam, and 2-ethylhexyl acrylate.
【００１４】インキ受理層を形成するインキに配合され
るビーズとしては、球状で、粒径分布の狭いものが良
く、ガラスビーズ、及びシリコン樹脂、ウレタン樹脂、
尿素樹脂、ナイロン、ポリオレフィン、フッ素樹脂等か
らなる樹脂ビーズ等を使用することができる。ビーズの
配合によってインキ層表面の複写技術による画像形成特
性が改善されるが、ウレタン樹脂ビーズを使用してイン
キ受理層を形成したフイルムシートは、更にマウスの動
きが良く、マウスの使用時のマット表面の摩耗が小さ
く、及び表面傷付き発生がないという作用効果がもたら
され、更に他の材質のビーズを使用した場合より色再現
性の良い画像を形成することができる。As the beads to be mixed with the ink forming the ink receiving layer, those having a spherical shape and a narrow particle size distribution are preferable, and glass beads, silicone resin, urethane resin,
Resin beads made of urea resin, nylon, polyolefin, fluorine resin and the like can be used. The bead composition improves the image forming characteristics of the ink layer surface by copying technology.However, the film sheet with the ink receiving layer formed using urethane resin beads has a better mouse movement and a mat for mouse use. This has the effect of reducing surface wear and preventing scratches on the surface, and can form an image with better color reproducibility than when beads of another material are used.
【００１５】前記ビーズとしては、粒径が５μ〜４０
μ、好ましくは１０μ〜３０μ、更に好ましくは２０μ
〜３０μものが使用され、インキベースに対して１５〜
３５重量％配合して、該インキにより形成された層によ
り、複写技術により形成される画像の解像度、濃度及び
色の再現性などの画像形成特性を改善することがでる。
粒径が５μ未満では複写技術により形成される画像の画
質の向上が見られず、４０μより大きいと光拡散効果が
小さく、また、表面摩擦が大きく、表面に傷が発生し易
い。The beads have a particle size of 5 μm to 40 μm.
μ, preferably 10 μ to 30 μ, more preferably 20 μ
~ 30μ is used, and 15 ~
By blending at 35% by weight, the layer formed with the ink can improve image forming characteristics such as resolution, density and color reproducibility of the image formed by the copying technique.
If the particle size is less than 5 μm, the image quality of the image formed by the copying technique is not improved, and if it is larger than 40 μm, the light diffusion effect is small, the surface friction is large, and the surface is easily scratched.
【００１６】前記インキによりフイルム表面に形成され
るインキ受理層の厚さは、５μ〜１００μ、好ましくは
１０μ〜８０μとするのが前記本願発明の課題を達成す
るのに必要である。そして、該層の厚さを調整すること
によって、光の透過性、拡散性、画像特性などが変化す
るので、どのような表示に使用するか、また使用用途に
よって前記範囲内で適宜調整することができる。It is necessary that the thickness of the ink receiving layer formed on the film surface by the ink be 5 μm to 100 μm, preferably 10 μm to 80 μm in order to achieve the object of the present invention. By adjusting the thickness of the layer, the light transmittance, diffusion, image characteristics, and the like are changed. Therefore, it is necessary to appropriately adjust the display within the above range depending on what display is to be used and the intended use. Can be.
【００１７】インキ受理層を形成するインキ組成物に
は、受理層の特性及び該層の形成性を落とすことなくイ
ンクジェットインキの受理性を改善する平均粒径が１〜
２０μｍ程度の天然繊維粉末やプロティンパウダーなど
を添加してもよいし、白色顔料や着色剤、レベリング剤
等従来からインキに添加されている成分を、インキ受理
層の複写技術により高解像・高濃度の画像を形成できる
特性を低下させない範囲で配合することができる。The ink composition for forming the ink receiving layer has an average particle size of 1 to improve the ink jet ink acceptability without deteriorating the properties of the receiving layer and the formability of the layer.
About 20 μm of natural fiber powder or protein powder may be added, or components conventionally added to the ink, such as white pigments, colorants, and leveling agents, may be added to the ink receiving layer using a high-resolution, high-resolution copying technique. The compound can be blended within a range that does not deteriorate the characteristics capable of forming an image having a density.
【００１８】平坦な表面に剥離し得るように固定するこ
とができる再剥離性貼着性を有する粘着層乃至粘弾性体
層は、例えばウレタン樹脂、エポキシ樹脂、シリコン樹
脂、塩化ビニル樹脂などのインキベースに、硬化剤、可
塑剤、溶剤その他の添加剤を配合して可撓性及び柔軟性
等の調整を行いインキ組成物を作り、このインキ組成物
を用い適宜の印刷手段、好ましくはスクリーン印刷法に
より形成することができる。好ましいインキ組成物とし
ては、紫外線等により硬化して再剥離貼着性を示す固体
層を形成する紫外線硬化型粘着剤組成物、例えば、平均
分子量が１０００〜１２０００程度であり、特に好まし
い平均分子量は３０００〜１００００程度のオリゴウレ
タン（ジ）アクリレート（この程度の分子量がインキ組
成物を作るのに好ましい範囲である。）、単官能モノマ
ー、例えばＨ2Ｃ＝ＣＨ−Ｃ（＝Ｏ）−Ｏ（Ｃ2Ｈ4−
Ｏ）n−ＰＨ−Ｒ1（ｎ＝１〜５、Ｒ1＝Ｃ1〜Ｃ15の炭化
水素残基、ＰＨ＝フェニレン基）及び紫外線などにより
重合反応、架橋反応、硬化反応を起こす活性種を生成す
る化合物（光開始剤）とから実質的になる液状インキ組
成物が、印刷法により基体シート表面に該組成物の層を
形成でき、該層の形成後紫外線などの照射により固体の
再剥離性貼着性を有する粘着層を形成することができる
点で好ましい。市販の前記のような特性を持つインキ組
成物としては、帝国インキ製造株式会社製のＵＶ ＱＶ
Ｎ−０００メジウム、ＵＶ ＱＶＮ−７０４２５特メジ
ウム、ＱＶＮ−０００メジウム等を挙げることができ
る。The adhesive layer or the viscoelastic layer having a removable adhesive property which can be fixed on a flat surface so as to be releasable is formed of, for example, an ink such as urethane resin, epoxy resin, silicone resin and vinyl chloride resin. A curing agent, a plasticizer, a solvent, and other additives are blended into a base to adjust flexibility and flexibility, etc., to prepare an ink composition, and an appropriate printing means, preferably screen printing, is performed using the ink composition. It can be formed by a method. As a preferred ink composition, an ultraviolet-curable pressure-sensitive adhesive composition that forms a solid layer exhibiting re-peeling adhesiveness by being cured by ultraviolet light or the like, for example, an average molecular weight of about 1,000 to 12,000, and a particularly preferred average molecular weight is Oligourethane (di) acrylate of about 3,000 to 10,000 (this molecular weight is a preferable range for preparing an ink composition), a monofunctional monomer, for example, H 2 CＣＨCH—C (＝ O) —O ( C 2 H 4 −
O) Active species that cause polymerization reaction, cross-linking reaction and curing reaction by n-PH-R 1 (n = 1 to 5, R 1 = C 1 to C 15 hydrocarbon residue, PH = phenylene group) and ultraviolet rays A liquid ink composition consisting essentially of a compound (photoinitiator) capable of forming a layer of the composition on the surface of the base sheet by a printing method, and after the formation of the layer, the solid is regenerated by irradiation with ultraviolet rays or the like. It is preferable in that a pressure-sensitive adhesive layer having a peelable adhesive property can be formed. Commercially available ink compositions having the above characteristics include UV QV manufactured by Teikoku Ink Mfg. Co., Ltd.
N-000 medium, UV QVN-70425 special medium, QVN-000 medium and the like can be mentioned.
【００１９】図１は、本発明の再剥離性貼着性の粘着層
乃至粘弾性層３及びインキ受理層１を有する基材フイル
ム２の実施例を示す平面図であり、複写用インキ４（ト
ナー）により画像が形成されている。第２図は、図１の
Ａ−Ａ切断線による断面図である。図３は、再剥離性貼
着性の粘着層乃至粘弾性層３（再剥離貼着層）を設けた
場合の本発明のフイルムシートの底面図であり、そして
図４及び５は剥離紙５を取り除いた再剥離貼着層の一印
刷態様を示すものである。該再剥離貼着層の印刷態様は
種々に変形することができる。FIG. 1 is a plan view showing an embodiment of a base film 2 of the present invention having a removable adhesive layer or a viscoelastic layer 3 and an ink-receiving layer 1, wherein a copying ink 4 ( (Toner) to form an image. FIG. 2 is a sectional view taken along line AA of FIG. FIG. 3 is a bottom view of the film sheet of the present invention provided with a removable adhesive layer or a viscoelastic layer 3 (removable adhesive layer), and FIGS. 1 shows one printing mode of the re-peelable adhesive layer from which is removed. The printing mode of the removable layer can be variously modified.
【００２０】さらに、本発明のフイルムシートに、前記
再剥離貼着層を覆う剥離紙５を剥離自在に設けることが
できる。この場合、前記貼着層は剥離紙により覆われて
いるので貼着層の不用意な貼着が防止される。Further, a release paper 5 covering the re-peelable adhesive layer can be provided on the film sheet of the present invention in a releasable manner. In this case, since the sticking layer is covered with the release paper, careless sticking of the sticking layer is prevented.
【００２１】[0021]
【実施例及び比較例】参考例（インキ受理層の画像形成
特性及びマウスの操作性を示す） 基材（２）として１８８μの厚さを有するポリエステル
フイルムを使用する。該フイルムの一方の表面に、次の
成分を主成分とするインキ組成物を使用し、インキ受理
層１を形成する。 インキ組成 ビーズ：平均粒径２５μのウレタン樹脂ビーズ２５ｇ（インキ重量１００重量 ％中２５重量％） ケトン系溶剤 １０ｇ 炭化水素系溶剤 ２０ｇ ポリエステル系樹脂 ３０ｇ チタン顔料 ３５ｇ 補助剤（シリコン油等） ５ｇ インキ受理層の形成及びその特性 使用スクリーン １５０メッシュ インキ受理層の厚さ ３０μ 画像の形成 電子写真法によりカラー画像を形成 形成された画像の評価 目視により、光沢度（ぎらつき性）、画像のソフト感、
解像度、色の再現性をオリジナルと対比した。それぞれ
の特性を被験者（評価パネラー）が心理的に評価して、
良いを３点、普通を２点、悪いを１点として加算した。 ○：加算点が１１以上 △：加算点が１０〜８ ×：７以下 評価結果を表１に示す。EXAMPLES AND COMPARATIVE EXAMPLES Reference Example (showing image forming characteristics of ink receiving layer and operability of mouse) A polyester film having a thickness of 188 μm is used as the substrate (2). The ink receiving layer 1 is formed on one surface of the film using an ink composition containing the following components as main components. Ink composition Beads: 25 g of urethane resin beads having an average particle size of 25 μm (25% by weight in 100% by weight of ink) Ketone solvent 10 g Hydrocarbon solvent 20 g Polyester resin 30 g Titanium pigment 35 g Auxiliary agent (silicon oil, etc.) 5 g Ink receiving Layer formation and its properties Screen used 150 mesh Thickness of ink receiving layer 30μ Image formation Color image formed by electrophotography Evaluation of formed image Visually, gloss (glitter), softness of image,
Resolution and color reproducibility were compared with the original. The subject (evaluation panel) evaluates each characteristic psychologically,
Three points for good, two points for normal, and one point for bad were added. ：: Addition point is 11 or more Δ: Addition point is 10 to 8 ×: 7 or less Table 1 shows the evaluation results.
【００２２】実施例１ 参考例で使われた基材２のインキ受理層１が形成された
面とは反対の面に再剥離貼着層３を、下記の紫外線硬化
型の塗布インキ組成物を使用し、スクリーン印刷により
均一塗布した後、紫外線を照射して硬化することによっ
て形成した。Example 1 A removable adhesive layer 3 was applied to the surface of the substrate 2 used in the reference example opposite to the surface on which the ink receiving layer 1 was formed, and the following UV-curable coating ink composition was used. It was formed by using a uniform coating by screen printing, and then irradiating with ultraviolet rays to cure.
【００２３】 紫外線硬化型インキの組成。 オリゴウレタン系アクリレート・・・・・・・・・・・３０．０〜６０．０％ エポキシ系モノマー・・・・・・・・・・・・・・・・・８．０〜１５．８％ エステル系モノマー・・・・・・・・・・・・・・・・２５．０〜３０．０％ アセトフェノン系光開始剤・・・・・‥・・・・・・・・ ３．０〜８．０％ アシルホオスフィンオキサイド・・・・・・・・・・・・ ３．０〜８．０％ エラストマー ・・・・・・・・・・・・・・・・・・・ １．０〜１０．０％ アクリル系等に代表されるシリコンを含まない消泡剤・・ １．０〜３．０％ 重合禁止剤・・・・・・・・・・・・・・・・・・・ ０．１％ なお、前記塗布インキの塗布工程においては、前記基材
２に予めアンダーコート層を設け、このアンダーコート
層上に塗布インキを塗布して前記再剥離貼着層３を形成
しても良い。前記塗布インキが塗布されてなるフイルム
シート、例えばマウスマットの形状に裁断されたシート
の裏面には、粘弾性体からなる再剥離貼着層３が均一に
形成されるので、この貼着層の粘着力によって、マウス
マットを対象物に、つまり机に貼付した状態で固定する
ことができる。したがって、このマウスマットを、摩擦
抵抗が非常に小さく滑らかな机上に敷いた場合であって
も、従来のように、マウスを移動操作した際に、マウス
マットが滑って移動してしまうことはない。よって、マ
ウスの移動量を正確にパソコンに伝達することができ
る。貼着−剥離をガラス板表面に繰り返し、１万回以上
においても。貼着・剥離特性が良好であった。また、被
貼着面の汚れ（糊残り現象）も小さかった。Composition of UV-curable ink. Oligourethane acrylate 30.0 to 60.0% Epoxy monomer 8.0 to 15.8 % Ester-type monomer 25.0-30.0% Acetophenone-type photoinitiator 3.0 3.0 -8.0% acylphosphine oxide 3.0-8.0% Elastomer 1 0.0 to 10.0% Silicon-free defoamer represented by acrylics, etc. 1.0 to 3.0% Polymerization inhibitor ... .. 0.1% In the step of applying the coating ink, an undercoat layer is provided on the base material 2 in advance, and the coating ink is coated on the undercoat layer. Fabric to be formed the removable lamination adhesive layer 3. The re-peelable adhesive layer 3 made of a viscoelastic material is uniformly formed on the back surface of the film sheet coated with the coating ink, for example, a sheet cut into a shape of a mouse mat. By the adhesive force, the mouse mat can be fixed to the target object, that is, in a state of being attached to the desk. Therefore, even when the mouse mat is laid on a smooth desk with a very small frictional resistance, the mouse mat does not slide and move when the mouse is moved as in the related art. . Therefore, the movement amount of the mouse can be accurately transmitted to the personal computer. Adhesion-peeling is repeated on the surface of the glass plate, even at 10,000 times or more. The sticking / peeling properties were good. In addition, dirt (adhesive residue phenomenon) on the adhered surface was small.
【００２４】また、前記塗布インキは、印刷技術を用い
て塗布されるので、正確な位置に面一に塗布された後、
定着されて面一な貼着層が形成される。このため、貼着
層が面一に形成されていない場合と比較して、机への密
着性を高めることができる。さらに、前記塗布インキは
スクリーン印刷により塗布されるので、他の印刷方法に
より塗布した場合と比較して、厚肉に塗布することがで
き、これにより前記貼着層を厚肉に形成することができ
る。この場合には、この貼着層を机上を押圧することに
より、前記貼着層の机への密着性を高めることができ
る。また、貼着層をマウスマット等の一部角部に形成し
ないようにすれば、貼着層の粘着力を高めても剥離する
ことができるので、マウスマット等の固定力を向上させ
ることができる。また、前記貼着層は、密着させること
により粘着力が生じるので、未使用時には、このマウス
マットをガラス等の壁面に張り付けておくこともでき
る。Further, since the coating ink is applied by using a printing technique, it is applied to an accurate position in a flush manner.
The adhesive layer is fixed to form a uniform adhesive layer. For this reason, the adhesion to the desk can be improved as compared with the case where the adhesive layer is not formed flush. Further, since the coating ink is applied by screen printing, it can be applied thicker than when applied by another printing method, thereby forming the adhesive layer thicker. it can. In this case, the adhesiveness of the adhesive layer to the desk can be enhanced by pressing the adhesive layer on the desk. Further, if the adhesive layer is not formed at a corner portion of the mouse mat or the like, the adhesive layer can be peeled even if the adhesive force of the adhesive layer is increased, so that the fixing force of the mouse mat or the like can be improved. it can. In addition, since the adhesive layer has an adhesive force when brought into close contact with each other, the mouse mat can be attached to a wall surface of glass or the like when not in use.
【００２５】他方、前記マウスマット等の製品に裁断し
たフイルムシートには、前記貼着層を覆う剥離紙が剥離
自在に設けられているので、例えば、このマウスマット
等をビニール袋に収容して出荷する際には、マウスマッ
ト等に設けられた貼着層の前記ビニール袋への不用意な
貼着を防止することができる。よって、出荷作業の効率
化を図ることができる。On the other hand, the film sheet cut into the product such as the mouse mat is provided with a release paper covering the adhesive layer in a releasable manner. For example, the mouse mat is stored in a plastic bag. At the time of shipment, it is possible to prevent the sticking layer provided on the mouse mat or the like from being carelessly stuck to the plastic bag. Therefore, the efficiency of the shipping operation can be improved.
【００２６】また、本実施の形態においては、前記塗布
インキをスクリーン印刷した場合について説明したが、
例えば、グラビア印刷やフレキソ印刷などの他の印刷方
法、あるいは、ロールコーターを用いた印刷方法によ
り、前記塗布インキを塗布しても良く、この場合には、
前記塗布インキに、エステル系モノマー又はエーテル系
モノマーを添加し、塗布インキの粘性率を０．１〜１０
％にする。これにより、基材２への塗布インキの塗布を
高速に行うことができるので、貼着層を形成したマウス
マット等を短時間にて大量に生産することができ、マウ
スマット等の製造コストの低減化を図ることができる。In this embodiment, the case where the coating ink is screen-printed has been described.
For example, the printing ink may be applied by another printing method such as gravure printing or flexographic printing, or by a printing method using a roll coater. In this case,
An ester monomer or an ether monomer is added to the coating ink, and the viscosity of the coating ink is 0.1 to 10
%. This makes it possible to apply the coating ink to the base material 2 at a high speed, so that a mouse mat or the like having the adhesive layer formed thereon can be mass-produced in a short period of time. Reduction can be achieved.
【００２７】実施例２ インキ受理層は参考例と同様にして形成した。帝国イン
キ製造株式会社製のＵＶ ＱＶＮ−７０４２５特メジウ
ムインキ組成物を用いて、繰り返し模様状の再剥離貼着
性の粘着層を形成した。得られたフイルムシートを、マ
ウスマット形状とし、これにカラー複写機で、好みの風
景のカラー画像を形成して、マウスマットを得た。画像
形成と形成された画像の評価は参考例と同様に行った。
評価結果を表１に示す。 マウスの転がり性：ポインターの位置決めのし易さ、マ
ウスの転がり感覚を評価パネラーが心理評価で評価し
た。 フイルムシート表面の傷つき性：３０００回マウスを転
がした時の表面の傷を目視で観察した。それぞれの評価
において、 ○：良い △：普通 ×：悪いを表す。 結果を表１に示す。貼着−剥離をガラス板表面に繰り返
し、１万回以上においても。貼着・剥離特性が良好であ
った。また、被貼着面の汚れ（糊残り現象）も小さかっ
た。Example 2 An ink receiving layer was formed in the same manner as in the Reference Example. Using a UV QVN-70425 special medium ink composition manufactured by Teikoku Ink Mfg. Co., Ltd., a re-peelable adhesive layer having a repetitive pattern was formed. The obtained film sheet was formed into a mouse mat shape, and a color image of a desired scene was formed thereon by a color copying machine to obtain a mouse mat. Image formation and evaluation of the formed image were performed in the same manner as in the Reference Example.
Table 1 shows the evaluation results. Rolling property of mouse: The ease of positioning the pointer and the rolling sensation of the mouse were evaluated by a panelist. Scratch property on the surface of the film sheet: Surface damage was observed visually when the mouse was rolled 3000 times. In each evaluation, ：: good Δ: normal ×: bad. Table 1 shows the results. Adhesion-peeling is repeated on the surface of the glass plate, even at 10,000 times or more. The sticking / peeling properties were good. In addition, dirt (adhesive residue phenomenon) on the adhered surface was small.
【００２８】実施例３ 基材として１８８μのポリエステルフイルムを使用す
る。該フイルムの一方の表面に、次の成分を主成分とす
るインキ組成物を使用し、インキ受理層を形成する。 インキ組成 ビ−ズ：平均粒径２５μのウレタン樹脂ビ−ズ ２５ｇ ビニルカプロラクタム ２２．０ｇ トリプロピレングリコールジアクリレート ２２．０ｇ ２官能ウレタンオリゴマー ３０．０ｇ アセトフェノン系光開始剤 ８．０ｇ チタン顔料 ２０．０ｇ 補助剤（シリコン油等） ５．０ｇ インキ受理層の形成及びその特性 使用スクリーン １５０メッシュ インキ受理層の厚さ ３０μ ５００ｍＪ／ｃｍ2の紫外線光量で硬化した。さらに、
上記の基材のインキ受理層が形成された面とは反対の面
に帝国インキ製造株式会社製のＵＶ ＱＶＮ−７０４２
５特メジウムインキ組成物により、再剥離性貼着性の粘
着層を形成した。得られたフイルムシートを、マウスマ
ット形状とし、これにカラー複写機で、好みの風景のカ
ラー画像を形成して、マウスマット得た。画像の形成と
形成された画像の評価は参考例と同様に行った。評価結
果を表１に示す。 マウスの転がり性：ポインターの位置決めのし易さ、マ
ウスの転がり感覚を評価パネラーが心理評価で評価し
た。 フイルムシート表面の傷つき性：３０００回マウスを転
がした時の表面の傷を目視で観察した。それぞれの評価
において、 ○：良い △：普通 ×：悪いを表す。 結果を表１に示す。貼着−剥離をガラス板表面に繰り返
し、１万回以上においても。貼着・剥離特性が良好であ
った。また、被貼着面の汚れ（糊残り現象）も小さかっ
た。Example 3 A 188 μm polyester film is used as a substrate. An ink receiving layer is formed on one surface of the film using an ink composition containing the following components as main components. Ink composition bead: urethane resin bead having an average particle size of 25 μg 25 g vinyl caprolactam 22.0 g tripropylene glycol diacrylate 22.0 g bifunctional urethane oligomer 30.0 g acetophenone-based photoinitiator 8.0 g titanium pigment 20.0 g Auxiliary agent (silicone oil, etc.) 5.0 g Formation of ink receiving layer and its properties Screen used 150 mesh Thickness of ink receiving layer 30 μ Cured by ultraviolet light of 500 mJ / cm 2 . further,
UV QVN-7042 manufactured by Teikoku Ink Mfg. Co., Ltd. is provided on the surface of the base opposite to the surface on which the ink receiving layer is formed.
A removable adhesive layer was formed from the 5 special medium ink composition. The obtained film sheet was formed into a mouse mat shape, and a color image of a desired scene was formed thereon by a color copying machine to obtain a mouse mat. The formation of the image and the evaluation of the formed image were performed in the same manner as in the Reference Example. Table 1 shows the evaluation results. Rolling property of mouse: The ease of positioning the pointer and the rolling sensation of the mouse were evaluated by a panelist. Scratch property on the surface of the film sheet: Surface damage was observed visually when the mouse was rolled 3000 times. In each evaluation, ：: good Δ: normal ×: bad. Table 1 shows the results. Adhesion-peeling is repeated on the surface of the glass plate, even at 10,000 times or more. The sticking / peeling properties were good. In addition, dirt (adhesive residue phenomenon) on the adhered surface was small.
【００２９】実施例４ 再剥離貼着性の粘着性を形成するインキ組成物として下
記のものを使用した以外は、実施例３を繰り返した。 インキ組成物。 オリゴウレタンジアクリレート（平均分子量１００００）・・３５．０重量部 単官能モノマー Ｈ2Ｃ＝ＣＨ−Ｃ（＝Ｏ）−Ｏ（Ｃ2Ｈ4−Ｏ）n−ＰＨ−Ｒ1（ｎ＝２、Ｒ1＝Ｃ（ −ＣＨ3）2−Ｃ6Ｈ5、ＰＨ＝フェニレン基） ・・・・・５９．０重量部 アセトフェノン系光開始剤 ・・・・・・・５．０重量部 補助剤（シリコン油など） ・・・・・１．０重量部 １５μの膜厚で、単位面積当たり５０％をスクリーン印
刷。印刷後に紫外線照射。貼着−剥離をガラス板表面に
繰り返し、１万回以上においても。貼着・剥離特性が良
好であった。また、被貼着面の汚れ（糊残り現象）も小
さかった。Example 4 Example 3 was repeated, except that the following ink composition was used as the ink composition for forming a peelable adhesive layer. Ink composition. Oligourethane diacrylate (average molecular weight 10000) · 35.0 parts by weight of monofunctional monomer H 2 C = CH-C ( = O) -O (C 2 H 4 -O) n-PH-R 1 (n = 2 , R 1 = C (-CH 3 ) 2 -C 6 H 5, PH = phenylene) ----- 59.0 parts by weight of acetophenone photoinitiator ....... 5.0 parts by weight auxiliary Agent (silicone oil, etc.) 1.0 part by weight Screen printing of 50% per unit area with a film thickness of 15μ. UV irradiation after printing. Adhesion-peeling is repeated on the surface of the glass plate, even at 10,000 times or more. The sticking / peeling properties were good. In addition, dirt (adhesive residue phenomenon) on the adhered surface was small.
【００３０】比較例１、２ 参考例において配合するビーズの粒径を、５μより小さ
い２μとした場合（比較例１）、ビーズの径を４０μよ
り大きい６０μとした場合（比較例）以外は実施例１を
繰り返した。評価結果を表１に示す。Comparative Examples 1 and 2 The procedure was carried out except that the particle diameter of the beads to be blended in the reference example was 2 μ smaller than 5 μm (Comparative Example 1), and the diameter of the beads was 60 μm larger than 40 μm (Comparative Example). Example 1 was repeated. Table 1 shows the evaluation results.
【００３１】[0031]
【表１】 [Table 1]
【００３２】[0032]
【発明の効果】以上説明したように、本発明のインキ受
理層及び再剥離性貼着性能を有する粘着層乃至粘弾性体
層を形成したフイルムシートは、複写技術による画像形
成特性が改善されているので、複写技術によって随時所
望のカラー模様などを形成でき、かつ、フイルムシート
の裏面には、粘着層乃至粘弾性体からなる貼着部が形成
されているので、このフイルムシート等を、前記貼着部
の粘着力によって対象物に貼付した状態で固定すること
ができる。したがって、このフイルムシート等を、摩擦
抵抗が非常に小さく滑らかな机上に敷いた場合であって
も、フイルムシート等が机上に貼着した状態で固定され
ることから、例えばマウスを移動操作した際に、マウス
マットが滑り移動してしまうことはない。よって、マウ
スの移動量を正確にパソコンに伝達することができる。
また、前記貼着層は、粘着層乃至粘弾性体からなるた
め、机上からのマウスマットの剥離を容易に行うことが
できるとともに、貼着・剥離を繰り返し行うことができ
る。As described above, the film sheet formed with the ink receiving layer and the adhesive layer or the viscoelastic layer having the removable adhesive property of the present invention has improved image forming characteristics by the copying technique. Therefore, a desired color pattern or the like can be formed at any time by a copying technique, and an adhesive portion made of an adhesive layer or a viscoelastic body is formed on the back surface of the film sheet. It can be fixed in a state of being stuck to the object by the adhesive force of the stuck portion. Therefore, even when this film sheet or the like is laid on a smooth desk with a very small frictional resistance, the film sheet or the like is fixed in a state of being stuck on the desk. In addition, the mouse mat does not slide. Therefore, the movement amount of the mouse can be accurately transmitted to the personal computer.
Moreover, since the sticking layer is made of an adhesive layer or a viscoelastic material, the mouse mat can be easily peeled off from the desk, and sticking and peeling can be repeatedly performed.
【図１】本発明の一実施態様のフイルムシートの平面図FIG. 1 is a plan view of a film sheet according to an embodiment of the present invention.
【図２】本発明の一実施態様の図１のフイルムシートの
Ａ−Ａ断面図FIG. 2 is a cross-sectional view of the film sheet of FIG.
【図３】本発明の一実施態様のフイルムシートの底面図FIG. 3 is a bottom view of the film sheet according to the embodiment of the present invention.
【図４】剥離紙を取り除いたフイルムシートの断面図FIG. 4 is a cross-sectional view of a film sheet from which release paper has been removed.
【図５】基材フイルムの全表面に形成された規則的模様
形状再剥離貼着層FIG. 5 is a regular pattern-shaped re-peelable adhesive layer formed on the entire surface of a base film.
１ インキ受理層 ２ 基材フイルム ３ 再剥離貼着層（再剥離性貼着性を有する粘着層乃至
粘弾性層） ４ 複写インキ ５ 剥離紙REFERENCE SIGNS LIST 1 Ink receiving layer 2 Base film 3 Removable adhesive layer (adhesive layer or viscoelastic layer having removable adhesive properties) 4 Copying ink 5 Release paper
Claims (12)
平均粒径が５μ〜４０μの球体であるビーズ１５〜３５
重量％をインキベースに配合したインキを使用して厚さ
５μ〜１００μの複写技術により画像を形成し得るイン
キ受理層を形成し、他方の表面に印刷法により再剥離性
貼着性を有する粘着層乃至粘弾性体層を形成したことを
特徴とするフイルムシート。1. Beads 15 to 35 which are spheres having an average particle size of 5 to 40 .mu.m on one surface of a base film by a printing method.
An ink receiving layer capable of forming an image by a copying technique having a thickness of 5 to 100 μ is formed by using an ink in which the weight% is mixed with an ink base, and a releasable sticking adhesive is formed on the other surface by a printing method. A film sheet comprising a layer and a viscoelastic layer.
れた層であることを特徴とする請求項１記載のフイルム
シート。2. The film sheet according to claim 1, wherein the adhesive layer or the viscoelastic layer is a layer printed on the entire surface.
れた層であることを特徴とする請求項１記載のフイルム
シート。3. The film sheet according to claim 1, wherein the adhesive layer or the viscoelastic layer is a partially printed layer.
された規則的模様形状であることを特徴とする請求項３
に記載のフイルムシート。4. The method according to claim 3, wherein the partial printing is a regular pattern formed on the entire surface of the base film.
The film sheet according to 1.
特徴とする請求項１乃至４のいずれかに記載のフイルム
シート。5. The film sheet according to claim 1, wherein the beads are urethane resin beads.
より固化する成分を配合したものであることを特徴とす
る請求項１乃至５のいずれかに記載のフイルムシート。6. The film sheet according to claim 1, wherein the ink base contains a component which is solidified by ionizing radiation and actinic rays.
離性貼着性を有する粘着層乃至粘弾性体層を形成ること
を特徴とする請求項１乃至６のいずれかに記載のフイル
ムシート。7. The film sheet according to claim 1, wherein an adhesive layer or a viscoelastic layer having removable adhesive properties is formed by using a screen printing method as a printing method.
されたものであることを特徴とする請求項１乃至７のい
ずれかに記載のフイルムシート。8. The film sheet according to claim 1, wherein the film sheet is cut into a shape for a predetermined use.
徴とする請求項８に記載のフイルムシート。9. The film sheet according to claim 8, wherein the predetermined use is a mouse mat.
離自在に設けたことを特徴とする請求項１乃至９のいず
れかに記載のフイルムシート。10. The film sheet according to claim 1, wherein a release paper covering the adhesive layer or the viscoelastic material layer is provided in a releasable manner.
性体層は、紫外線硬化により粘着固体層を形成する液状
インク組成物によって形成されたものであることを特徴
とする請求項１乃至１０のいずれかに記載のフイルムシ
ート。11. The adhesive layer or the viscoelastic layer having removable adhesive properties is formed of a liquid ink composition that forms an adhesive solid layer by ultraviolet curing. A film sheet according to any one of claims 1 to 10.
液状インキ組成物が単官能モノマー、オリゴウレタンジ
アクリレート、紫外線開始剤を主成分とするものである
請求項１１に記載のフイルムシート。12. The film sheet according to claim 11, wherein the liquid ink composition for forming an adhesive solid layer by ultraviolet curing contains a monofunctional monomer, oligourethane diacrylate and an ultraviolet initiator as main components.