JPS5850516A - color display panel - Google Patents
color display panelInfo
- Publication number
- JPS5850516A JPS5850516A JP56149696A JP14969681A JPS5850516A JP S5850516 A JPS5850516 A JP S5850516A JP 56149696 A JP56149696 A JP 56149696A JP 14969681 A JP14969681 A JP 14969681A JP S5850516 A JPS5850516 A JP S5850516A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- resins
- display panel
- color
- transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】 本発明は光線の照射により発色する発色パネル。[Detailed description of the invention] The present invention is a coloring panel that develops color when irradiated with light.
更に詳述すれば、紫外線を吸収するプラスチック板の面
に付着された発色体が該プラスチック板を透過した光に
対しては発色せず、且つ該プラスチック板を透過しない
直接光に対しては発色する発色表示パネルに関す、る。More specifically, the coloring material attached to the surface of a plastic plate that absorbs ultraviolet rays does not develop color when exposed to light that passes through the plastic plate, and does not develop color when exposed to direct light that does not pass through the plastic plate. Regarding color display panels.
従来、発色表示パネルは螢光剤を塗料に混合し、金属板
や紙に塗付した看板や道路標識等に用いられている。Conventionally, color display panels have been used for signboards, road signs, etc., which are made by mixing fluorescent agents with paint and applying the mixture to metal plates or paper.
しかしながら、このような発色表示パネルは塗料が塗布
された面から光が照射された場合に、その面から螢光剤
の発色状態が観察できるに過ぎない。However, in such a color display panel, when light is irradiated from the surface coated with paint, the coloring state of the fluorescent agent can only be observed from that surface.
本発明は紫外線により発色する発色材料を透明、又は着
色透明基材に付着し、該基材を透過しない直接光に対し
ては発色し、その基材の両面から同一発色像を観察でき
るが、他方、基板を透過した光に対しては発色せず、発
色像の観察のできない発色表示パネルを提供する。すな
わち、本発明は紫外線を吸収する透明、又は着色透明の
プラスチック板の少なくとも一面に紫外線により発色す
る発色材料を付着した、該プラスチック板を透過する光
線に対しては該発色材料が発色しない発色表示パネルで
ある〇
本発明は該プラスチック板の両面に紫外線により発色す
る発色材料を付着することができる。この該プラスチッ
ク板の両面に該発色材料を付着することにより該プラス
チック板の一方の面から紫外線、又は紫外線を含む光線
（以下光と呼ぶ）を照射すると、顔面に付着した発色材
料の発色像のみがプラスチック板の両面から観察でき、
該プラスチック板の他方の面から光を照射すると、該他
方の面に付着した発色材料の発色像のみがプラスチック
板の両面から観察でき、該プラスチック板の両面から光
を照射すると、プラスチック板の両面に付着された発色
材料の発色像が観察できる。In the present invention, a coloring material that develops color when exposed to ultraviolet rays is attached to a transparent or colored transparent base material, and the color develops when exposed to direct light that does not pass through the base material, and the same colored image can be observed from both sides of the base material. On the other hand, the present invention provides a color display panel that does not develop color when exposed to light transmitted through a substrate, and in which a colored image cannot be observed. That is, the present invention provides a color display in which a coloring material that develops color when exposed to ultraviolet rays is attached to at least one surface of a transparent or colored transparent plastic plate that absorbs ultraviolet rays, and the coloring material does not color when exposed to light that passes through the plastic plate. In the present invention, which is a panel, a coloring material that develops color when exposed to ultraviolet rays can be attached to both sides of the plastic plate. By attaching the coloring material to both sides of the plastic plate, when ultraviolet rays or light rays containing ultraviolet light (hereinafter referred to as light) are irradiated from one side of the plastic plate, only the colored image of the coloring material attached to the face will appear. can be observed from both sides of the plastic plate,
When light is irradiated from the other side of the plastic plate, only the colored image of the coloring material attached to the other side can be observed from both sides of the plastic plate, and when light is irradiated from both sides of the plastic plate, both sides of the plastic plate can be observed. A colored image of the colored material attached to the surface can be observed.
従って、２種類の文字、模様、絵、及び図形等（以下文
字等と呼ぶ）を表示することができたり、また光の照射
方向を変えることにより異った文字等を表示したり、若
しくは文字等を表示しなかったりすることができる。Therefore, it is possible to display two types of characters, patterns, pictures, figures, etc. (hereinafter referred to as characters, etc.), or to display different characters, etc. by changing the direction of light irradiation. etc. may not be displayed.
また、本発明は、紫外線を吸収する透明、又は着色透明
のプラスチック板として、波長Ｊ ７０ ｙａｍより短
波長の紫外線を吸収するものを用いるのが好ましく、ポ
リカーボネート樹脂、アクリル樹脂。Further, in the present invention, as the transparent or colored transparent plastic plate that absorbs ultraviolet rays, it is preferable to use one that absorbs ultraviolet rays with a shorter wavelength than the wavelength J 70 yam, such as polycarbonate resin or acrylic resin.
塩化ビニル樹脂、ポリスチレン樹脂、ポリエステル樹脂
、及びセルロール樹脂の厚みが０．、！；ｍｍ 乃至／
Ｑｍｍ、好ましくは／、ｊ；ｍｍ乃至ｊｍｍのものが用
いられる。特にポリカーボネートは高い耐通抵抗を有し
ており、第１−に示す如く、厚さ２ｍｍのものは３７０
ｎｍより長波長の光線の透過率は高＜、３９０ｎｍ以下
の短波長の光線をＳＯ％以上吸収するので本発明の発色
表示パネルのプラスチック板として好適である。The thickness of vinyl chloride resin, polystyrene resin, polyester resin, and cellulose resin is 0. ,! ;mm to/
Qmm, preferably /, j; mm to jmm are used. In particular, polycarbonate has a high electrical resistance, and as shown in No. 1-1, a 2mm thick polycarbonate has a
It has a high transmittance for light rays with wavelengths longer than 390 nm, and absorbs light rays with short wavelengths of 390 nm or less by SO% or more, so it is suitable as a plastic plate for the color display panel of the present invention.
更にまた本発明は紫外線により発色する発色材料として
光を照射しないときは無色透明、あるいは無色で、光の
照射により青、緑、あるいは赤色を発色するスチルベン
系、オキサゾール系、トリアゾール系、クマリン系、及
びナフタルイミド系の螢光剤、並びにスピロピラン、ト
リアリールメタンロイコ体、及び多速芳香族化水素のフ
ォトクロミック物質が用いられる。Furthermore, the present invention uses stilbene-based, oxazole-based, triazole-based, coumarin-based, color-forming materials that are colorless and transparent when not irradiated with light, and develop blue, green, or red colors when irradiated with light, as color-forming materials that develop color with ultraviolet rays. and naphthalimide-based fluorescent agents, and photochromic substances such as spiropyran, triarylmethane leuco, and rapid hydrogen aromatization.
更にまた、本発明は前述の発色材料を透光性材料に分散
して、プラスチック板の面に塗付して付着したり、また
発色材料を分散した透明シートを透明、又は着色透明の
接着層を介してプラスチック板の面に接合できる。発色
材料をプラスチック板に塗付するのに用いられる透光性
材料として発色材料の発色機能を妨げず、且つプラスチ
ック板に接着するものが用いられ、ポリビニルピロリド
ン、ポリビニルアルコール、ポリエステル、ポリイソブ
チレン、ポリビニルブチラール、エチレン酢酸ビニル共
重合体、エチレンアクリル酸エステル共重合体、ポリ酢
酸ビニル、アクリル酸エステル、ポリウレタン、ポリア
ミド、エポキシ、光重合アクリル、及びシリコーン等が
あり、また接着層を介してプラスチック板に付着する発
色材料をその表面に分散した透明シートとじて発色材料
の発色機能を妨げないものが用いられ、ポリカーボネー
ト樹脂、アクリル樹脂、ポリエステル樹脂。Furthermore, the present invention can be applied by dispersing the above-mentioned color-forming material in a translucent material and applying it to the surface of a plastic plate, or by using a transparent sheet with the color-forming material dispersed therein as a transparent or colored transparent adhesive layer. It can be bonded to the surface of the plastic plate via. The translucent material used to apply the coloring material to the plastic plate is one that does not interfere with the coloring function of the coloring material and also adheres to the plastic plate, such as polyvinylpyrrolidone, polyvinyl alcohol, polyester, polyisobutylene, polyvinyl There are butyral, ethylene vinyl acetate copolymer, ethylene acrylic ester copolymer, polyvinyl acetate, acrylic ester, polyurethane, polyamide, epoxy, photopolymerized acrylic, and silicone. Polycarbonate resin, acrylic resin, and polyester resin are used as a transparent sheet that does not interfere with the coloring function of the coloring material as a transparent sheet with the attached coloring material dispersed on its surface.
ポリスチレン樹脂、ポリ塩化ビニル樹脂、ポリエチレン
樹脂、エチレン酢酸ビニル共重合樹脂、エチレンアクリ
ル酸エステル樹脂、ポリアミド樹脂。Polystyrene resin, polyvinyl chloride resin, polyethylene resin, ethylene vinyl acetate copolymer resin, ethylene acrylate resin, polyamide resin.
及びセルロース樹脂等の厚さ／ ｍｍ以下のシートが用
いられる。これらの透明シートは適当な大きさの文字等
の形状に切り取られ接着層を介してプラスチック板に貼
付けられる。A sheet made of cellulose resin or the like with a thickness of 1 mm or less is used. These transparent sheets are cut into shapes such as letters of appropriate size and pasted onto a plastic plate via an adhesive layer.
また前記接着層として透明性、耐水性及び耐候性の優れ
た接着剤が用いられ、エチレン酢酸ビニル共重合樹脂、
エチレンアクリル酸エステル共重合樹脂、ポリエステル
樹脂、ポリイソブチレン樹脂。Further, as the adhesive layer, an adhesive having excellent transparency, water resistance and weather resistance is used, and an ethylene vinyl acetate copolymer resin,
Ethylene acrylate copolymer resin, polyester resin, polyisobutylene resin.
ポリビニルブチラール樹脂、酢酸ビニル樹脂、アクリル
酸エステル樹脂、ポリウレタン樹脂、ポリアミド樹脂の
如き熱可塑性樹脂、及びこれらに粘着付与剤を添加した
樹脂、並びにエポキシ樹脂光重合アクリル樹脂１．シリ
コーン樹脂、ポリウレタン樹脂の如き硬化型樹脂よりな
る透明、及び着色透明接着剤が好んで用いられる。Thermoplastic resins such as polyvinyl butyral resins, vinyl acetate resins, acrylic ester resins, polyurethane resins, and polyamide resins, resins obtained by adding tackifiers to these resins, and epoxy resins Photopolymerized acrylic resins1. Transparent and colored transparent adhesives made of curable resins such as silicone resins and polyurethane resins are preferably used.
以下に添付図面を用いて、本発明の実施例について詳述
する。Embodiments of the present invention will be described in detail below with reference to the accompanying drawings.
実施例／
大きさ７０ｍｍＸ！ｒＯｍｍＸ、２ｍｍ のボｌＪカー
ｔｉ−ト樹脂のプラスチック板ｌの両面２，３に堰を設
け、該堰で囲まれる部分が面２においては文字Ａ。Example/ Size 70mmX! rOmm
面３においては文字Ｂとなるようにしたものを用意した
。一方、ポリビニルピロリドン八３ｇｒと市販の螢光増
白剤（Ｑ、■、 Ｆｌｕｏｒｅｅｃｅｎｔ Ｂｒｉｇ
ｈｔｅｎｅｒｊ２）（住友化学工業株式会社製 商品名
ＷｈｉｔｅＦ／ｕｏｒ Ｂ）→ｏ、ｏｓ ｇｒとをエタ
ノール３．２ ｇｒに溶かし粘着性のある紫外線により
発色する発色材料を用意した。そしてこの発色材料をプ
ラスチック板ｌの一面一の基間に流し込み、数時間乾燥
後、同様にプラスチック板ｌを他面３の基間に流し込み
数時間乾燥した。その後、堰を除去して、プラスチック
板／の両面コ、３に紫外線により発色する発色材＋、１
を付着した第一図乃至第１図に示す発色表示パネルを製
作した。この発色表示パネルは光を照射しないとき、発
色材＋、１が無色透明であり、キセノンランプの光をパ
ネルの面２に照射すると、青色のＡがパネルの両面から
みえ、パネルの面３に前記光を照射すると、青色のＢが
パネルの両面からみえ、更にパネルの両面に前記光を照
射するとパネルの両面からＡ、とＢとが重なってみえた
。For side 3, a letter B was prepared. On the other hand, 3 gr of polyvinylpyrrolidone and a commercially available fluorescent brightener (Q, ■, Fluorescent Brig
htenerj2) (manufactured by Sumitomo Chemical Co., Ltd., trade name WhiteF/uor B) → o, os gr was dissolved in 3.2 gr of ethanol to prepare a coloring material that develops color with adhesive ultraviolet light. Then, this color-forming material was poured into the base of one side of the plastic plate 1, and after drying for several hours, the plastic plate 1 was similarly poured into the base of the other side 3 and dried for several hours. After that, the weir is removed and both sides of the plastic plate are covered with a coloring material that develops color using ultraviolet rays.
A color display panel shown in FIGS. 1 and 1 was manufactured. When this color display panel is not irradiated with light, the coloring materials + and 1 are colorless and transparent, and when the light from the xenon lamp is irradiated onto side 2 of the panel, blue A is visible from both sides of the panel, and on side 3 of the panel. When the light was irradiated, blue B was visible from both sides of the panel, and when the light was irradiated on both sides of the panel, A and B appeared to overlap from both sides of the panel.
実施例２
実施例／と同様にポリカーボネート樹脂面ｌ−に文字Ａ
の発色材料／ダを付着した第Ｓ図に示す発色表示パネル
を製作した。この表示パネルは光を照射しないとき無色
透明であり、水銀ランプ又はキセノンランプの光を面／
、２に照射するとＡが青色に発色し、面／３に前記光を
照射した場合には無色透明のままであった。Example 2 Letter A on the polycarbonate resin surface l- as in Example/
A color-forming display panel shown in FIG. This display panel is colorless and transparent when not irradiated with light, and when exposed to light from a mercury lamp or xenon lamp,
, 2, A developed a blue color, and when surface/3 was irradiated with the light, it remained colorless and transparent.
実施例３
酢酸ビニル／ざ重量％を含有するエチレン酢酸ビニル共
重合体樹脂ｊＪ ｇｒと前述の螢光増白剤０、．０１１
ｇｒ とをトルエンに溶かした溶液をガラス板面に設
けた種間に流し込み、−晩装置して硬化引きはがし１．
Ｑ、ｆ ｍｍ厚の紫外線により発色する発色材料の透明
シートを作った。この透明シートを文字Ａ及びＢの形状
に切り取り、その一方の面にエチレン酢酸ビニルのエマ
ルジ目ン、２ｔ（住友化学工業株式会社 商品名 スミ
カフレックスｊ／のを塗り、厚さ２ ｍｍのポリカーボ
ネート板コ／の一面コ２に文字Ａの発色材料２１を貼付
け、更にポリカーボネート板、２／の他方の面２３に発
色材料、２よとしてＢを貼付けて、第６図に示す発色表
示パネルを製作した。またポリカーボネート板−／の面
２３に発色材料を付着してない外は前述の発色表示パネ
ルと同じである、第７図に示す発色パ□ネルを製作した
。Example 3 Ethylene-vinyl acetate copolymer resin jJ gr containing % vinyl acetate by weight and the aforementioned fluorescent brightener 0, . 011
A solution prepared by dissolving gr in toluene is poured into a seed gap provided on the glass plate surface, and left to stand overnight to harden and peel off.1.
A transparent sheet of a color-forming material that is colored by ultraviolet rays and has a thickness of Q, f mm was made. This transparent sheet was cut into the shapes of letters A and B, one side of which was coated with ethylene vinyl acetate emulsion, 2T (Sumitomo Chemical Co., Ltd., product name Sumikaflex J/), and a 2 mm thick polycarbonate plate was coated. A color-forming material 21 with the letter A was pasted on one side of the 2/, and a color-forming material 21 with B was pasted on the other side 23 of the polycarbonate plate 2/ to produce the color display panel shown in Figure 6. In addition, a coloring panel shown in FIG. 7 was manufactured which was the same as the coloring display panel described above except that no coloring material was attached to the surface 23 of the polycarbonate plate.
第６図に示す発色表示パネルは実施例−と同様の発色を
示し、第７図の発色表示パネルは実施例１と同様の発色
を示した。The color display panel shown in FIG. 6 showed the same color development as in Example 1, and the color display panel shown in FIG. 7 showed the same color development as in Example 1.
図面は本発明の実施例を示すものであって、第１図はポ
リカーボネート板の紫外可視領域の透過率曲線、第２図
は本発明の発色表示パネルの断面図、第３図は正面図、
第１図は裏面図、第５図。
第６図及び第７図は夫々本発明の他の実施例を示す発色
表示パネルの断面図である。The drawings show embodiments of the present invention; FIG. 1 is a transmittance curve of a polycarbonate plate in the ultraviolet and visible region, FIG. 2 is a cross-sectional view of a color display panel of the present invention, and FIG. 3 is a front view.
Figure 1 is a back view, Figure 5. 6 and 7 are cross-sectional views of color display panels showing other embodiments of the present invention, respectively.
Claims (1)
ック板の少なくとも一面に紫外線により発色する発色材
料を付着した、該プラスチック板を透過する光線に対し
ては該発色材料が発色しない発色表示パネル。 （２）該プラスチック板の両面に該発色材料を付着した
、特許請求の範囲第１項に記載の発色表示パネル０ （３） 該プラスチック板がボッ刀−ボネート樹脂、
アクリル樹脂、塩化ビニル樹脂、ポリスチレン樹脂。 ポリエステル樹脂、及び七ルロール樹脂から選ばれた一
種の樹脂板である特許請求の範囲第１項又は第一項に記
載の兇色表示パネル。 （４，） 該発色材料がスチルベン系、オキサゾール
系。 トリアゾール系、タマリン系、及びす７タルイミド系か
ら選ばれる一種以上の螢光剤である特許請求の範囲第１
項乃至第３項のいずれかに記載の発色表示パネル。 （５ン 該発色材料がスピロピラン、トリアリールメ
タンロイコ体、及び縮合多環芳香族炭化水素から選ばれ
る一種以上のフォトク四ミック物質である特許請求の範
囲第１項乃至第３項に記載のいずれかの発色表示パネル
。 （６）該発色材料を分散した透光性材料を該プラスチッ
ク板に塗布して該発色材料を付着した特許請求の範囲第
１項乃至第５項に記載のいずれがの発色表示パネル。 （７） 該透光性材料にポリビニルピロリドン、ポリ
ビニルアルコール、ｇリエステル、ポリイソブチレン、
ポリビニルブチラール、エチレン酢酸ビニル共重合体、
エチレンアクリル醸エステル共重合体ポリ酢酸ビニル、
アクリル酸エステル、ポリウレタン、ボ、リアミド、工
・ボキシ、光重合アクリル。 及びシリコ“−ンの如き透明、又は着色透明の樹脂から
選ばれた一種以上の樹脂である特許請求の範囲第を項に
記載の発色表示パネル。 （８）該発色材料を表側に分散した透明シートを透明、
又は着色透明の接着層を介しそ該プラスチック板に接合
した特許請求の範囲第１項乃至第３項に記載のいずれか
の発色表示パネル。 （９） 該透明シートがポリカーボネート樹脂、アク
リル樹脂、ポリエステル樹脂、ポリスチレン樹脂。 ポリ塩化ビニル樹脂、ポリエチレン樹脂、エチレン酢酸
ビニル共重合樹脂、エチレンアクリル酸エステル樹脂、
ポリアミド樹脂、及びセルロース樹脂から選ばれた一種
以上のＱ、３ｍｍ未満の厚味を有する樹脂である特許請
求の範囲第ざ項に記載の発色表示パネル。 （１０）該接着層がエチレン酢酸ビニル共重合樹脂、エ
チレンアクリル酸エステル共重合樹脂、ポリエステル樹
脂、ポリイソブチレン樹脂、ポリビニルブチラール樹脂
、酢酸ビニル樹脂、アクリル酸エステル樹脂、ポリウレ
タン樹脂、ポリアミド樹脂の如き熱可塑性樹脂、及びこ
れらに粘着付与剤を添加した樹脂、並びにエポキシ樹脂
光重合アクリル樹脂、シリコーン樹脂、ポリウレタン樹
脂の如き硬化型樹脂よりなる透明及び着色透明な接着剤
から選ばれた一種以上の樹脂である特許請求の範囲第９
項又は第１Ｏ項記載の発色表示パネル表[Scope of Claims] (1) At least one surface of a transparent or colored transparent plastic plate that absorbs ultraviolet rays is attached with a coloring material that develops color when exposed to ultraviolet rays, and the coloring material is resistant to light that passes through the plastic plate. A color display panel that does not produce color. (2) The coloring display panel 0 according to claim 1, wherein the coloring material is adhered to both sides of the plastic plate. (3) The plastic plate is made of Botto-bonate resin,
Acrylic resin, vinyl chloride resin, polystyrene resin. The multi-colored display panel according to claim 1 or 1, which is a type of resin plate selected from polyester resin and heptadylol resin. (4,) The coloring material is stilbene type or oxazole type. Claim 1 is one or more fluorescent agents selected from triazole type, tamarin type, and 7-talimide type.
The color display panel according to any one of items 1 to 3. (5) Any one of claims 1 to 3, wherein the color-forming material is one or more photochromic substances selected from spiropyran, triarylmethane leuco, and fused polycyclic aromatic hydrocarbons. (6) The color-forming display panel according to any one of claims 1 to 5, wherein the color-forming material is attached by coating the plastic plate with a light-transmitting material in which the color-forming material is dispersed. Color display panel. (7) The light-transmitting material includes polyvinylpyrrolidone, polyvinyl alcohol, glycester, polyisobutylene,
Polyvinyl butyral, ethylene vinyl acetate copolymer,
Ethylene acrylic ester copolymer polyvinyl acetate,
Acrylic acid ester, polyurethane, polyurethane, lyamide, polyester/boxy, photopolymerized acrylic. The color display panel according to claim 1, which is one or more resins selected from transparent or colored transparent resins such as silicone and silicone. transparent sheet,
Alternatively, the color display panel according to any one of claims 1 to 3, which is bonded to the plastic plate via a colored and transparent adhesive layer. (9) The transparent sheet is made of polycarbonate resin, acrylic resin, polyester resin, or polystyrene resin. Polyvinyl chloride resin, polyethylene resin, ethylene vinyl acetate copolymer resin, ethylene acrylate resin,
The color display panel according to claim 1, which is one or more Q selected from polyamide resins and cellulose resins, and a resin having a thickness of less than 3 mm. (10) The adhesive layer is made of ethylene vinyl acetate copolymer resin, ethylene acrylic ester copolymer resin, polyester resin, polyisobutylene resin, polyvinyl butyral resin, vinyl acetate resin, acrylic ester resin, polyurethane resin, polyamide resin, etc. One or more resins selected from transparent and colored transparent adhesives made of plastic resins, resins in which tackifiers are added, and curable resins such as epoxy resins, photopolymerized acrylic resins, silicone resins, and polyurethane resins. Claim No. 9
Color display panel table as described in Section 1 or Section 1O