JPS60165292A - 光学記録媒体 - Google Patents
光学記録媒体Info
- Publication number
- JPS60165292A JPS60165292A JP59020181A JP2018184A JPS60165292A JP S60165292 A JPS60165292 A JP S60165292A JP 59020181 A JP59020181 A JP 59020181A JP 2018184 A JP2018184 A JP 2018184A JP S60165292 A JPS60165292 A JP S60165292A
- Authority
- JP
- Japan
- Prior art keywords
- thin film
- recording
- recording medium
- composition
- transparent base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
（イ）産業上の利用分野
本発明は光学的な記録媒体に関するものでろシレーザ光
等の光及び熱エネルギーを用いて情報を高密度に記録し
、且つ再生可能な記録媒体に関する。
等の光及び熱エネルギーを用いて情報を高密度に記録し
、且つ再生可能な記録媒体に関する。
（ロ）従来技術
レーザ光等のエネルギービームを照射して、基板上の金
属等の薄膜を溶隔あるいは蒸発させ、ビットを形成する
方式の記録材料としては感度が高く、基板上の記録層の
膜厚が均一で１化学、物理的にも安定で長期にわたって
記録再生ができなければならない。
属等の薄膜を溶隔あるいは蒸発させ、ビットを形成する
方式の記録材料としては感度が高く、基板上の記録層の
膜厚が均一で１化学、物理的にも安定で長期にわたって
記録再生ができなければならない。
例えば、日経エレクトロニクス１９８２年１月４日号第
８６頁以下、「画像ファイルに使われ出した光ディスク
・メモリ」なる記事等に開示されて−る如＜、現在この
方式の記録材料としてはテルル（Ｔｅ’）が一般的に用
いられている。Ｔｅは熱伝導率が低く、光吸収係数が大
きく、低融点であるので感度の良い記録膜が得られるが
、空気中の水分によって容易に酸化され、光学的に透明
な二酸化テルル（ＴｅＯ２）Ｋ変化するため信号が再生
できなくなり、長期間の情報の記録は非常に難しい。す
なわち記録寿命が短いという欠点を有している。
８６頁以下、「画像ファイルに使われ出した光ディスク
・メモリ」なる記事等に開示されて−る如＜、現在この
方式の記録材料としてはテルル（Ｔｅ’）が一般的に用
いられている。Ｔｅは熱伝導率が低く、光吸収係数が大
きく、低融点であるので感度の良い記録膜が得られるが
、空気中の水分によって容易に酸化され、光学的に透明
な二酸化テルル（ＴｅＯ２）Ｋ変化するため信号が再生
できなくなり、長期間の情報の記録は非常に難しい。す
なわち記録寿命が短いという欠点を有している。
又前掲の記事中には、チタニウム（Ｔｉ）単体を薄膜材
料として使用する例（第９８頁第１３図（ｂ）〕も挙げ
られている。しかし乍らＴｌ単体は感度が劣るだけでな
く大面積に亘って均一な組成のものを低コストで得るこ
とが困難でｂるという欠点を否めない。
料として使用する例（第９８頁第１３図（ｂ）〕も挙げ
られている。しかし乍らＴｌ単体は感度が劣るだけでな
く大面積に亘って均一な組成のものを低コストで得るこ
とが困難でｂるという欠点を否めない。
（ハ） 目 的
本発明は、上記欠点を改善し、長期間にわたって情報の
記録、再生ができる記録媒体を提供することを目的とす
る。
記録、再生ができる記録媒体を提供することを目的とす
る。
に）構 成
本発明は、基板上にテルル（ｊｅ）とチタン（Ｔｉ）か
らなる’ｒｅ１ｏｏ−Ｘ−ＴＩ！（３≦Ｘ≦１５）の組
成の組成をもつ非晶質薄膜を形成したものでおる。
らなる’ｒｅ１ｏｏ−Ｘ−ＴＩ！（３≦Ｘ≦１５）の組
成の組成をもつ非晶質薄膜を形成したものでおる。
（ホ）実 施 例
第１図は本発明の光学記録媒体の要部断面斜視図を示す
ものでるる。この記録媒体は基本的に記録薄膜（１１を
内面に形成した透明基盤［２１と、保護基盤（３）及び
両者を一定の間隔を空けて一体に固定するスペーサ＋４
５（５）で構成巧れる。天部は記録、再生用のレーザ光
の方向を示す。
ものでるる。この記録媒体は基本的に記録薄膜（１１を
内面に形成した透明基盤［２１と、保護基盤（３）及び
両者を一定の間隔を空けて一体に固定するスペーサ＋４
５（５）で構成巧れる。天部は記録、再生用のレーザ光
の方向を示す。
前記透明基盤【２）は、ガラス、ポリメチルメタクリレ
ート樹脂、ポリカーボネート樹脂、ポリメチ明度の秀れ
た素材で成型される。
ート樹脂、ポリカーボネート樹脂、ポリメチ明度の秀れ
た素材で成型される。
前記記録薄膜としては、上述の長寿命化を計るという課
題の他、記録再生用のＬＤ（半導体レーザダイオード）
の出力、Ｓ／Ｎ（Ｃ／Ｎ）、感度、信頼性等の観点から
、種々の実験によシ、テルル（Ｔｅ ）とチタニウム（
Ｔｉ）を主成分とし、Ｔｏ（，１０Ｏ−ｘ）、−Ｔｉｘ
（ｘはモ／ｌ／％（但し３＜Ｘ＜１５））なる組成の非
晶質薄膜を採用した。
題の他、記録再生用のＬＤ（半導体レーザダイオード）
の出力、Ｓ／Ｎ（Ｃ／Ｎ）、感度、信頼性等の観点から
、種々の実験によシ、テルル（Ｔｅ ）とチタニウム（
Ｔｉ）を主成分とし、Ｔｏ（，１０Ｏ−ｘ）、−Ｔｉｘ
（ｘはモ／ｌ／％（但し３＜Ｘ＜１５））なる組成の非
晶質薄膜を採用した。
この非晶質薄膜は蒸着着しくけスパッタリング法により
て前記透明基盤（２）上に６００〜５００にの膜厚に形
成される。
て前記透明基盤（２）上に６００〜５００にの膜厚に形
成される。
一一゛
Ｔｉの含有量対Ｃ／Ｎ（ｄＢ）の関係を、ディスク半径
６０−、回転数７０Ｏｒｐｍ、記録周波数２ＭＨｚの条
件で実験した結果を表わす第２図を参照すれば、少くと
も０≦Ｘ≦１５の範囲でＣ／Ｎ ｄＢ≧４５のＣ／Ｎが
確保出来ることが確認される。また、ディスク半径対し
Ｄ出力（ディスク面上）の特性をＴＩの含有量をパラメ
ータとして測定した結果を示した第３図を参照すれば、
大径ディスクにおいても０≦Ｘ≦２０の範囲で読出出力
の影響を受けず、なお且つＬＤの出力上限の範囲で十分
な録再特性を確保し得ることが判る。
６０−、回転数７０Ｏｒｐｍ、記録周波数２ＭＨｚの条
件で実験した結果を表わす第２図を参照すれば、少くと
も０≦Ｘ≦１５の範囲でＣ／Ｎ ｄＢ≧４５のＣ／Ｎが
確保出来ることが確認される。また、ディスク半径対し
Ｄ出力（ディスク面上）の特性をＴＩの含有量をパラメ
ータとして測定した結果を示した第３図を参照すれば、
大径ディスクにおいても０≦Ｘ≦２０の範囲で読出出力
の影響を受けず、なお且つＬＤの出力上限の範囲で十分
な録再特性を確保し得ることが判る。
次ｒＣＴｅ（１００−ｘ）−Ｔｉｘの組成比と記録寿命
との関係を確認するために、透明基盤（２）としてアク
リル樹脂製の円盤を用い、その内面にＴｅＣ１０Ｏ−ｘ
）、’ｒｔ＊ｏ組成（但１． Ｘ ｘ Ｑ 。
との関係を確認するために、透明基盤（２）としてアク
リル樹脂製の円盤を用い、その内面にＴｅＣ１０Ｏ−ｘ
）、’ｒｔ＊ｏ組成（但１． Ｘ ｘ Ｑ 。
２．４，７．１５・）の記録薄膜を３０ＯＡの膜厚に形
成した記録媒体のサンプルを用意し、温度６０℃、湿度
９０％の雰囲気中に放置して加速試験を行った。その結
果を第４図に表わす。
成した記録媒体のサンプルを用意し、温度６０℃、湿度
９０％の雰囲気中に放置して加速試験を行った。その結
果を第４図に表わす。
この加速試験の結果に依れば、従来のＴｏ単体の記録膜
が試験開始後相対的な透過率が試験開始後１日で２０＜
、１週間後に２００％以上にも上昇したのに比べて本発
明の’ ” １：０ｊＯ＝ｉ −４ｆ ２の組成の記録
媒体の場合少くとも５＜−１の範囲で記録安定性が大巾
に向上し記録寿命が著しく向上することが判る。特にｘ
−７即ち、Ｔｅ９３Ｔｉ７の場合には１ケ月経過後にも
相対透過率は殆んど変化しない。従ってＴｔの含有量Ｘ
モル嘴を３〈ｘ＜１５に選定し、Ｔｅ（１００−ｘ）−
Ｔｉｘの組成の記録薄膜によって記録媒体を形成すれば
本発明の目的に清う記録媒体を実現し得ることが判る。
が試験開始後相対的な透過率が試験開始後１日で２０＜
、１週間後に２００％以上にも上昇したのに比べて本発
明の’ ” １：０ｊＯ＝ｉ −４ｆ ２の組成の記録
媒体の場合少くとも５＜−１の範囲で記録安定性が大巾
に向上し記録寿命が著しく向上することが判る。特にｘ
−７即ち、Ｔｅ９３Ｔｉ７の場合には１ケ月経過後にも
相対透過率は殆んど変化しない。従ってＴｔの含有量Ｘ
モル嘴を３〈ｘ＜１５に選定し、Ｔｅ（１００−ｘ）−
Ｔｉｘの組成の記録薄膜によって記録媒体を形成すれば
本発明の目的に清う記録媒体を実現し得ることが判る。
（へ）発明の効果
本発明に依れば、長記録寿命で感度がよく低コストの光
学式記録媒体が実現出来る。
学式記録媒体が実現出来る。
図面はいずれも本発明に係り、第１図は要部断面斜視図
、第２図はＴｉの含有量とＣ／Ｎの関係を表わす図、第
６図はディスク半径とＬＤ出力との関係をＴｅ−Ｔｉ素
材の組成をパラメータとして表わす図、第４図は相対的
透過率の加速試験の結果を示す図である。 （１）・・・記録薄膜、（２）・・・透明基盤、（３）
・・・保護基盤、１４１ｔ５３・・・スペーサ。 出願人三洋電機株式会社 代理人弁理士 佐 野 靜 夫 第１図 第２図 第４図 係過５日数
、第２図はＴｉの含有量とＣ／Ｎの関係を表わす図、第
６図はディスク半径とＬＤ出力との関係をＴｅ−Ｔｉ素
材の組成をパラメータとして表わす図、第４図は相対的
透過率の加速試験の結果を示す図である。 （１）・・・記録薄膜、（２）・・・透明基盤、（３）
・・・保護基盤、１４１ｔ５３・・・スペーサ。 出願人三洋電機株式会社 代理人弁理士 佐 野 靜 夫 第１図 第２図 第４図 係過５日数
Claims (1)
- エネルギービームの照射によって情報を記録する方式の
光学記録媒体におｉて、基板上ｖｃＴｅ１ＱＱ−Ｘ、Ｔ
ＩＸ（但り、Ｘはモル鳴、６≦×≦１５〕なる組成をも
つ非晶質薄膜を形成したことを特徴とする光学記録媒体
。