JPS60232801A - 難削材の切削加工法 - Google Patents
難削材の切削加工法Info
- Publication number
- JPS60232801A JPS60232801A JP59085773A JP8577384A JPS60232801A JP S60232801 A JPS60232801 A JP S60232801A JP 59085773 A JP59085773 A JP 59085773A JP 8577384 A JP8577384 A JP 8577384A JP S60232801 A JPS60232801 A JP S60232801A
- Authority
- JP
- Japan
- Prior art keywords
- difficult
- cutting
- cut
- heating
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明ｌ；ｌｌ：難削材料すなわちチタンをはじめとす
る金属材料やアルミナ、ジルコニアなどの硬脆材セラミ
ックスなどを容易に切削する方法を提供するものである
。
る金属材料やアルミナ、ジルコニアなどの硬脆材セラミ
ックスなどを容易に切削する方法を提供するものである
。
一般に構造性にすぐｎた材料は、強靭、硬質その他の性
質を有し、ｆｉｔ：加工材として加工性が悪い。そのた
めその解決法としてまず刀ロエ技術の開発よび電侠刀ロ
エその他いろいろと開発が進められている。いま一つの
解決方法は材料仰からの改善で、難削材の材質自身をか
えて容易に加工できるようにすることでちる。
質を有し、ｆｉｔ：加工材として加工性が悪い。そのた
めその解決法としてまず刀ロエ技術の開発よび電侠刀ロ
エその他いろいろと開発が進められている。いま一つの
解決方法は材料仰からの改善で、難削材の材質自身をか
えて容易に加工できるようにすることでちる。
本発明は難切削材料全切削条件を選ぶことで容易に切削
を可能にしたものである。
を可能にしたものである。
本発明による切削那工方法は材料の変態超塑性を利用す
るもので、材料の変態温度まで刀口讐や冷却し変態点附
近で温度サイクルを与えながら切削すると、塑性変形が
容易な状態のため切削抵抗が減少し仕上面精度も向上す
るというものである。
るもので、材料の変態温度まで刀口讐や冷却し変態点附
近で温度サイクルを与えながら切削すると、塑性変形が
容易な状態のため切削抵抗が減少し仕上面精度も向上す
るというものである。
よく知ら几ている鉄鋼にはへ３＊Ａｌ変態があるので変
態温度区間において大きなＶＷひずみがあられする。ま
た脆性材料であるねずみ鋳鉄でもそのマトリックスがパ
ーライトであるのでＡｘＫ態超塑性を示す。この温度域
に材料を置き、切削すると切削抵抗が著しく低下し容易
に切削できることがわかった。
態温度区間において大きなＶＷひずみがあられする。ま
た脆性材料であるねずみ鋳鉄でもそのマトリックスがパ
ーライトであるのでＡｘＫ態超塑性を示す。この温度域
に材料を置き、切削すると切削抵抗が著しく低下し容易
に切削できることがわかった。
以上に述べた金属材料の低かにセラミックスにも変態超
塑性がちり、例えば石英には５８０℃附近にα→β変態
点があり超塑性現象の発現があるので、その延性により
セラミックは切削に際しボロボロ脱落せず切削可能であ
る。
塑性がちり、例えば石英には５８０℃附近にα→β変態
点があり超塑性現象の発現があるので、その延性により
セラミックは切削に際しボロボロ脱落せず切削可能であ
る。
以下に実施例に沿って説明する。
実施例１
チタン合金のＴｊ−６Ａｔ−４Ｖ合金製丸棒をＡｒガス
雰囲気中で低同波誘導７１０ＦＢを行い９００℃と８６
０℃の区間を往復刃口熱しながら超硬合金製バイトチッ
プで旋削加工した。
雰囲気中で低同波誘導７１０ＦＢを行い９００℃と８６
０℃の区間を往復刃口熱しながら超硬合金製バイトチッ
プで旋削加工した。
その際の切削抵抗は同材料の冷間の通常旋削にくらべて
１／３〜１１５に低下し、仕上面精度も良好であった。
１／３〜１１５に低下し、仕上面精度も良好であった。
実施例２
石英（ｓ ７ ｏ、 ）を５５０℃と５９０℃の温度に
繰返し加熱しなから超硬合金９μフライスカッタ゛−で
石英を切削した。
繰返し加熱しなから超硬合金９μフライスカッタ゛−で
石英を切削した。
、この温度域で変態超塑性ひずみがちられ牡、延性挙動
を示し、石英は比較的容易に切削が可能であった。
を示し、石英は比較的容易に切削が可能であった。
以上に述べたように、室温では脆性体のほとんどマイク
ロひずみの発生しない材料や、ニッケル基耐熱合金、チ
タン合金の工うな切削加工がむずかしい材料でも超塑性
状態の発現によって延性化し切削抵抗が小さくなり切削
カロエが可能になつ、た。すなわち難切削材の切削につ
いて、材料面からの快削化によらずにその材料の有する
相変態を利用して切削が容易に行えるようになった。
ロひずみの発生しない材料や、ニッケル基耐熱合金、チ
タン合金の工うな切削加工がむずかしい材料でも超塑性
状態の発現によって延性化し切削抵抗が小さくなり切削
カロエが可能になつ、た。すなわち難切削材の切削につ
いて、材料面からの快削化によらずにその材料の有する
相変態を利用して切削が容易に行えるようになった。
初切削材が切削可能になったことで、産業界の有用性を
極めて高い。 以上 出願人 セイコー電子工業株式会社
極めて高い。 以上 出願人 セイコー電子工業株式会社
Claims (3)
- （１）材料の相変態点附近で上下の温度サイクルを与え
ながら切削することを特徴とする難削材の切削刃ロ工法
。 - （２）材料が金属でちることを特徴とする特許請求の範
囲第１項記載の難削材の切削加工法。 - （３）材料がセラミックでちることｌ）徴とする特許請
求の範囲第１項記載の難削材の切削加工法。