JPS6230089A - 光学的情報記録媒体 - Google Patents

光学的情報記録媒体

Info

Publication number
JPS6230089A
JPS6230089A JP60170036A JP17003685A JPS6230089A JP S6230089 A JPS6230089 A JP S6230089A JP 60170036 A JP60170036 A JP 60170036A JP 17003685 A JP17003685 A JP 17003685A JP S6230089 A JPS6230089 A JP S6230089A
Authority
JP
Japan
Prior art keywords
colorant
recording
layer
dye
reflectivity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP60170036A
Other languages
English (en)
Inventor
Toshiyuki Kanno
敏之 管野
Hitoshi Watanabe
均 渡辺
Kohei Hamanishi
浜西　広平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Olympus Corp
Original Assignee
Olympus Optical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Olympus Optical Co Ltd filed Critical Olympus Optical Co Ltd
Priority to JP60170036A priority Critical patent/JPS6230089A/ja
Publication of JPS6230089A publication Critical patent/JPS6230089A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、光学的情報記録媒体に関するものである。
〔従来技術及び問題点〕
従来回転しているディスク状の情報記録媒体にレーザー
光を照射して情報の記録再生を行う情報記録再生装置が
知られている。これら情報記録装置に用いられている情
報記録媒体としては基板、金属反射膜及び色素を含む半
透明着色層から構成されているものや、Ｔｏ、Ｂｌ、Ａ
ｓ等の金属の薄膜と基板から構成されているものが知ら
れている。
しかしながら、前者は金属反射膜ｆ：、真空蒸着法によ
り形成するためにコストが高くなるという欠点がある。
また、後者も真空蒸着法による薄膜の形成を行うために
コストが高くなり、かつ熱伝導率が高く比熱が大きいた
め記録感度が低く、更にそれ自身が毒性を有し廃棄する
場合に難を有するという欠点があった・ このようなことから、シアニン色素に代表される金属光
沢を有する有機色素ｑｉを記録層とする情報記録媒体が
提案されている、この記録媒体は、有機色素を用いてい
るため記録レーデ−波長に吸収極大を合せ易く、かつ反
射率も吸収極大付近においである一定以上の値を有する
友め、半導体レーデ−による記録再生が可能で、装置の
小型化、低コスト化が可能であるという利点を有する。
しかしながら、シアニン色素、メロシアニン色素は吸収
極大光付近において反射率が４０％を越えると、照射レ
ーザ光の吸収率が３０係以下になって感度が低下するた
め、記録時に記録速度を低くして感度低下を補なう等の
対処を会衆とする問題があった。
本発明は、上記事情に鑑みなされたもので、ある程度の
再生特性を有すると共に、感度の向上化を達成した光学
的情報記録媒体を提供しようとするものである。
〔問題点を解決する手段および作用〕
本発明者らは、記録感度及び再生特性に影響する記録層
の光反射率について鋭意研究を重ねた結果、有機色素を
主成分とする記録層において光反射率の上限を２０４に
規定することにより感度向上が図られ、かつ光反射率の
下限を８優にしてもある程度の再生特性全売すことを究
明し、ここに記録感度が高く、再生特性を有する光学的
情報記録媒体を児い出した。
即ち、本発明は基板上に有機色素を主成分とし、光反射
率が８〜２０俤の記録層を被覆したことを特像とする光
学的情報記録媒体である。
上記基板としては、例えばガラス、プラスチック、金属
等を用いることができる。特に、有機色素の記録層との
接着性全考慮した場合、グラスチック基板を用いること
が好ましい。
上記有機色素としては、例えばシアニン色素、メロシア
ニン色素、アントラキノン系色素、トリフェニルメタン
系色素、キサンチン系色素、フタロシアニン等を用いる
ことができる。こうした色［け、スピンナー法、ディッ
ピング法、ドクターブレード法等により薄膜（記録層）
として基板上に形成される。
上記有機色素を主成分とする記録層の光反射率を８〜２
０優にコントロールするには、以下に示す方法が挙げら
れる。
（１）　　有機色素に異なった波長域に反射率極大を与
える他の色素を添加する。
（１１）有機色素に反射性を持念ず、かつ吸収極大が一
致する別の色素を添加する。
（ｉ）　　有機色素にポリマーを添加する。
（ｉＶ）　　有機色素記録層を多層化し、レーデ−波長
における反射性の高い色素と反射性を有さない色素の層
を積層する方法。
特に（１１）の方法は記録感度が向上するという点にお
いて浸れている。また、（ｉｉｉ）の方法は感度を絣持
しつつポリマーによるバインダー効果で耐熱性を向上さ
せることができる点で優れている。
上記（１）の方法に用いられる他の色素としては前述し
たシアニン色素、メロシアニン色素、トリフェニルメタ
ン色素等がある。こうした他の色素の添加量は、反射率
極大の波長位置にも依るが、モル比で主成分色素に対し
て２％〜５０％好ましくは５％〜３０％である。
上記（１１）の方法に用いられる添加色素としては、下
式（Ｉ）に示すアミン系、下式（ｎ）に示す１．２−ジ
チオレート金属錯体、赤外線吸収剤を挙げることができ
る。
Ｎ（Ｒ）２Ｎ（Ｒ２） Ｒ；アルキル基 〔但し、式（ｎ）中のＲ１〜４はアルキル基又はフェニ
ル基、Ｘ、Ｙは水素、アルキル基、ハロダン基、ＭＨＮ
ｉ　、　Ｃｕ　、　Ｃｏ　、　Ｆｅ等の金属を示す〕こ
うした色素の添加量は主成分色素に対して、モル比で１
〜５０％好ましくは５〜３０俤である。
上記（山）の方法に用いられる。３ｆ　リマーとしては
、塩化ビニル樹脂、酢酸ビニル樹脂、アクリル樹脂、ポ
リエステル樹脂、ニトロセルロース、ポリエチレン樹脂
、ポリプロピレン樹脂、ポリカーボネート樹脂、ポリエ
チレンテレフタレート樹脂、エポキシ樹脂、ポリブチラ
ール樹脂の単体もしくは共重合体を挙げることができる
。これらのポリマーの添加量は色素に対して重量比でＯ
，１〜３０チ好ましくは１〜１０優である。
上記Ｑｖ）の方法においては、上記（１）　、　（ｉｉ
）の方法で用いた色素を用いることができる。この場合
先に基板上に形成した薄膜層を保護するために中間層を
設けてもよい。
なお、本発８Ａにおいては、有機色素記録層の他に、中
間層、保護層を設けてもよい。中間層は記録層の接着性
の向上、水、酸素、ガスの保護を目的として設けられる
。保護層は記録層のギズホコリからの保護及び水、酸素
、ガスによる酸化防止の目的で設けられる。これらの層
は、前記（ｉｉｉ）の方法に用いられるポリマーや酸化
防止剤から構成される。
次に、本発明の光学的情報記録媒体の構造を図面を参照
して説明する。
第１図は、光学的情報記録媒体の基本構成を示すもので
、基板１とこの基板１上に被覆され光反射ｒＡをコント
ロールした有機色素を主成分とする記録層２からなるも
のである。記録再生時の集束レーザー光３の照射は、基
板１側、記録層２９Ｑのいず九でもよい。
第２図ｉｄ、高反射性色素層と低反射性色素層の積層膜
からなる記録層を用いた例であり、同図ＧＡ）は基板ｌ
上に高反射性色素層２ａ、低反射性色素層２ｂを順次積
層した構造、同図（Ｂ）は基板ｌ上に低反射性色素層２
ｂ、高反射性色素層を順次積層した構造、を夫々示す。
こうした記録媒体では、レーデ−光を低反射性色素層２
ｂ側から入射するよ５にする。
第３図は、基板１と記録層２の間に中間層４を、記録層
２上に保護層５を夫々設けた構成の記録媒体を示す。こ
の場合、中間層４、保護層５のいずれ７５１一方を省い
てもよい。
第４図は、同一構成の２枚の記録媒体を記録層２側が更
に対向するようにスペーサ６を介して配置したものであ
る。なお、第３図中の７はエアー卒ヤツデ、８はスピン
ドル穴を夫々示す。
このような構成では、記録再生を基板１側から集束レー
デ−光３を照射しで行なうため、汚れやゴムによる影響
を抑制できる。
〔発明の実施例〕
以下、本発明の詳細な説明する。
実施例１ 下記（＠式に示す金属光沢を有するシアニン色素に対し
て下記（財）式に示す赤外吸収剤（日本化某社製商品名
：　ＩＲＧＯＯ２）を重量比で４０チ添加し、これを溶
剤に溶解した後スピンナー法で厚さ１，２Ｍのアクリル
樹脂基板上に塗布、乾燥して厚さ５０　ｎｍの色素記録
層を形成し、記録媒体を製造した。
しかして、得られた記録媒体における記録層の基板側か
らの反射率、吸収率を分光光度計で測定し九ところ、波
長８３０　ｎｍにおいて夫々１３係、７６憾であった。
また、記録媒体について半導体レーザー光（波長８３０
　ｎｍ　）を直径１．２μｍのスポットに集束し、線径
３ｗ−１書き込み時間１μ■の条件下で基板側から照射
し、記録再生を行なったところ、記録エネルギー閾値２
，４ｎ　Ｊ、／スポット、再生Ｃβ比４９　ｄＢを得た
。
比較例１ 実施例１に用いた式（ＩＩ）のシアニン色素ヲスビンナ
ー法で厚さ１．２ｍのガラス基板上に膜厚４７　ｎｍの
記録層を形成し、記録媒体を製造した。
この記録層の波長８３０　ｎｍにおける反射率、吸収率
はそれぞれ４５俤、４１チであった。また。
実施例１と同様に記録再生を行ったところ記録エネルギ
ー閾値３．８　ｎＪ／スポット　ＣＡ比４６ｄＢという
値を得た。
実施例２ 下記（至）式に示されるシアニン色素にポリエスチル樹
脂（バイロン２００）を重量比で９＝１の割合にて添加
し、溶媒で溶解した後、スピンナー法で厚さ１．２μｍ
のアクリル樹脂基板上に塗布、乾燥して厚さ７０　ｎｒ
ｎの記録層を形成し、記録媒体を段進した。
得られた記録媒体の記録層の基板側からの反射率、吸収
率は波長１３３０　ｎｍにおいて夫々１４壬、７０係で
あり念、ま九、記鋤媒体について実施例１と同様に記録
再生を行なったところ、記録エネルギー閾値２．８ｎＪ
／スポツト、再生ｃ２へ比４６　ｄＢ　ｆ：得た。
比較例２ 式（７）に示した色素を単体で実施例２と同様に１、２
　ｍのアクリル樹脂基板上に６８　ｎｍの厚さに塗布し
て記録層を形成し記録媒体を装造した。
得られた記録媒体の記録層の反射率、吸収率は、波長８
３０　ｎｍにおいてそれぞれ４４％と５０係であった。
記録媒体について実施例１と同様に省き込み再生を行っ
たところ、記録エネルギー閾値３．２　ｎＪ／スポット
、再生Ｃ／Ｎ比４７　ｄＢ　’、得た。
〔発明の効果〕
以上詳述した如く、本発明によれば記録感度が高く、良
好な再生特性を有す光学的情報記録媒体を提供できる。
【図面の簡単な説明】
第１図〜第４図は、夫々本発明の光学的情報記録媒体を
示す概略図である。 １・・・基板、２・・・記録層、２ｍ・・・高反射性色
素層、２ｂ・・・低反射性色素層、３・・・レーザー光
、４・・・中間層、５・・・保護層。 出願人代理人　　弁理士　坪　井、″マ゛淳第１図 第２図 第３図 第４図

Claims (1)

    【特許請求の範囲】
  1. 基板上に有機色素を主成分とし、光反射率が８〜２０％
    の記録層を被覆したことを特徴とする光学的情報記録媒
    体。
JP60170036A 1985-08-01 1985-08-01 光学的情報記録媒体 Pending JPS6230089A (ja)