JPS63189291A - 光情報記録媒体 - Google Patents

光情報記録媒体

Info

Publication number
JPS63189291A
JPS63189291A JP62020454A JP2045487A JPS63189291A JP S63189291 A JPS63189291 A JP S63189291A JP 62020454 A JP62020454 A JP 62020454A JP 2045487 A JP2045487 A JP 2045487A JP S63189291 A JPS63189291 A JP S63189291A
Authority
JP
Japan
Prior art keywords
recording medium
recording
layer
recording layer
information recording
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP62020454A
Other languages
English (en)
Inventor
Keiko Ichinose
一ノ瀬　恵子
Tsutomu Sato
勉 佐藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ricoh Co Ltd
Original Assignee
Ricoh Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ricoh Co Ltd filed Critical Ricoh Co Ltd
Priority to JP62020454A priority Critical patent/JPS63189291A/ja
Publication of JPS63189291A publication Critical patent/JPS63189291A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 〔技術分野〕 本発明はレーザ特に半導体レーザによる書込み記録に過
した光情報記録媒体さらに詳しくはポリメチン色Ｘを主
成分とする有機薄膜記録層の改良に関する。
〔従来技術〕
従来、回転しているディスク状の情報記録媒体にレーザ
光を照射して情報の記録再生を行なう情報記録再生装置
が知られている。そして、この種の情報記録装置に用い
られる情報記録媒体としては基板上に低融点金属または
低融点金属と誘電体とからなる記録層を設けたものなど
が提案されている。しかし、これらは保存性が悪い、分
解能が低い、記録密度が低い、製造条件が難しくコスト
高になるなどの欠点を有する。
そこで、最近になって記録層として金属薄膜に代えて有
機色素薄膜を使用することが提案されている。この有機
色素薄膜は融点、分解温度が低く、熱伝導率も低いので
高感度、高密度化の可能性があることまた膜形成がコー
ティングによシ可能なため量産性が高く、低コスト化が
期待できるなどの点で利点がある。
しかしながら、かかる有機色素＃膜を用いた記録媒体は
光および熱に対する安定性、記録後の再生光に対する保
存性などがまだ充分でないのが現状である。
〔目　的〕
本発明は上記問題に鑑みてなされたものであって、その
目的は光情報記録媒体の耐光性向上、再生劣化の防止お
よび低コスト化にある。
〔構　成〕
本発明はポリメチン色素の耐光性を改良するとともにア
ルコール系溶剤に可溶化し射出成形基板に直接塗布可能
な特定の化合物を見出したことにもとづいている。すな
わち、本発明の上記目的は記録層の主成分となるポリメ
チン色素に下記一般式の化合物を含有させることによつ
°ただし、Ｒ１、Ｒ２、Ｒ５およびＲ４はそれぞれ水素
または一８Ｏ２Ｎ（Ｒ５）　２を表わし、Ｒ５は８個ま
での炭素原子を有するアルキル基または水素を表わ・ すが、Ｒ１、Ｒ２、ＲｊおよびＲ４の少なくとも１つは
一８０２Ｎ（Ｒ５）２　ｋ示す。ＭはＣｕ５Ｖ％　ＶＯ
ｚ、Ｐｂ５Ｎｉ　、　５ｎＣ１２、血、ＺｎまたはＳｎ
　ｆ表わす。さらに、上記式中の芳香環上には一８Ｏ２
Ｎ（Ｒ５）２　　以外の置換基例えばへロゲン、アルキ
ルまたはアルコキシなどが存在していてもよい。
本発明の光情報記録媒体は基本的には基板上に上記一般
式の化合物およびポリメチン色素を含む記録層ｔ−設け
ることにより　ｈ！成されるが必要に応じて基板と記録
層との間に下引き層をあるいは記録層の上に保護層を設
けることができる。また、このようにして構成された一
対の記録媒体を記録層を内側にして他の基板と空間を介
して密封したエアーサンドインチ構造にしてもよくある
いは保護層を介して接着した密着サンドインチ（貼合せ
構造）にしてもよい。
本発明における上記一般式の化合物は記録層に添加する
と光情報記録媒体の耐光性の改良と再生劣化の防止にす
ぐれた効果を示すが、記録層のみならず他の層例えば下
引き層または保護層あるいは両方の層にも添加してその
効果を増強することができる。本発明の記録層における
ポリメチン色素と上記一般式の化合物との重量比は３０
ｉ７０ないし９９：１灯ましくは６０：４０ないし９５
：５である。
さらに本発明の光情報記録媒体を構成する材料および各
層の必要特性について具体的に説明する。
１）基板 基板の必要特性としては基板側よシ記録再生゛を行う場
合のみ使用レーザ光に対して透明でなければならず、記
録側から行う場合は透明である必要はない。基板材料と
しては例えばポリエステル、アクリル樹脂、ポリアミド
、ポリカーボネート、ポリオレフィン樹脂、フェノール
樹脂、エポキシ樹脂、ポリイミドなどのプラスチック、
ガラス、セラミックあるいは金属などを用いることがで
きる。
なお、基板の表面にはアドレス信号などのプレフォーマ
ットや案内溝のプレグルーブが形成されていてもよい。
また、射出成形によシ製作された基板を用いるのがコス
トの面で最も好ましい。
２）記録層 記録層はレーザ光の照射により何らかの光学的変化を生
じさせその変化によシ情報を記録できるもので、その主
成分がポリメチン色素からなっておシさらに本発明の上
記一般式の化合物が含有されている。
ポリメチン色素の代表例としてはシアニン色素、メロシ
アニン色素、夛ロコニウム色素、ヒリリウム色素など含
アげることができる。
また、本発明による上記一般式の化合物の代表例全下記
の表に示すがこれらのみに制限されるものではない。
本発明による上記一般式の化合物は記録特性および安定
性向上のため２権以上組合せてもよく他の色素例えばフ
タロシアニン系、テトラヒドロコリン系、ジオキサジン
系、トリフエッチアジン系、フェナンスレン系、アント
ラキノン（インダンスレン）糸、キサンチン糸、トリフ
ェニルメタン系、トリフェニルアミン系、アズレン系な
どの色素または金属例えば工ｎ　Ｎ　Ｓｎ　％’ｒｅＳ
Ｂｉ、Ａ７．Ｓｅ５Ａｇ５Ｃｕ　　などまたは金属化合
物例えば’ｒｅｏ２　、ＳｎＯなどと混合分数しても積
層してもよい。また、記録層はその他に高分子材料、保
存安定剤（例えば、金、ｌ！１４ａ体、フェノール系化
合物など）、分散剤、難燃剤、滑剤、帯電防止剤、可塑
剤などを含有していてもよい。
記録層の形成は蒸着、スパッタリング、ＣｖＤまたは溶
液塗布などの通常の手段によって行なうことができる。
溶液塗布による場合には有機溶媒例えばアルコール類、
ケトン類、アミド類、エーテル類、スルホキシド類、エ
ステル類、脂肪族ハロゲン化炭化水素類、芳香族顔中に
ポリメチン色素場合によシ上記化合物を溶解してスプレ
ー、スピンナー、ディラグ、ブレード、ローラーなどの
慣用のコーティング法によって行なわれる。＆！録層の
膜厚は１００Ｘ〜１０μｍ好ましくは２００Ｘ〜２μｍ
である。
３）下引き層 下引き層は（ａ）　！！ｆ！増性の向上、（ｂ）水また
はガスなどのバリヤー、（ｃ）記録層の保存安定性の向
上および（ｄ）反射率の同上、（ｅ）溶剤からの基板の
保ａ、（ｆ）プレグルーブの形成などを目的として使用
される。（ａ）の目的に対しては高分子材料例えハアイ
オノマー樹脂、ポリアミド樹脂、ビニル系樹脂、天然高
分子、シリコーン、液状ゴムなどの種々の高分子物質お
よびシランカップリング剤などを用いることができ、（
ｂ）および（Ｃ）の目的に対しては上記高分子材料以外
に無機化合物例えば５ｔｏ２、ＭｇＦ２．５ｉＯ１Ｔｉ
０２　、ＺｎＯ、ＴｉＮ　。
ＳｉＮなど、金属または半金属例えばＺｎ　、　Ｃｕ　
％Ｓ、Ｎｉ、Ｃｒ５（）ｅ、Ｂｅ、％Ａｕ、Ａｇ５Ａｌ
　などを用いることができ、（ｄ）の目的に対しては金
属例えばＡｇ５Ａｌｓ金属光沢金有する色素例えばメチ
ン系色票、キサンチン系色素などを用いることができる
。上記（ｅ）および（ｆ）の目的に対しては紫外線硬化
樹脂、熱硬化性街脂、熱可塑性樹脂などを用いることが
できる。下引き層の膜厚は１１〜３０μｍＱましくは０
．２〜１０μｍが適当である。
４）保護層 保護層は記録層をキス、ホコリ、汚れなどから保護する
こと、記録層の保存安定性および反射率の向上を目的と
して設けられ、その材料としては下引き層と同じ材料を
使用することができる。保護層の膜厚はα０５μｍ以上
好ましくは５μｍ以下が適当である。
なお、下引き層と保護層中には安定剤、分散剤、難燃剤
、滑剤、帯電防止剤、界面活性剤、可塑剤などが含有さ
れていてもよい。
〔効　果〕
上述のようにして構成された本発明の光情報記録媒体に
よれば、熱および光に対する安定性が高く、保存性にす
ぐれかつ再生劣化の少い記録媒体が得られる。さらに長
波長レーザ（半導体レーザ）を用いても高感度に記録で
き、良好な形状でピットを形成することができしかも高
いＣ／　Ｎが得られる。射出成形基板上に直接塗布によ
シ記録層が形成でき大幅なコスト低減を達成できる。
〔実施例〕
以下に比較例と共に実施例？：あげて本発明をさらに説
明するが本発明はこれら実施例のみに限定されるもので
はな、い。
実施例　１ 厚さ１．２１ｍ、直径２００１１１１の射出成形された
ポリカーボネート基板上にピッチ１．６２ｍ１溝幅０．
３μｍ１深さ９５０Ｘのらせん状の案内溝を７オトボリ
マーによ多形成し、この上に下記式（１）の色素と前掲
例示化合物黒７とを混合比８０／２０で混合してメタノ
ール／１，２−ジクロルエタン（８／２　重量比）に溶
解した溶液上スピナー塗布し膜厚７００Ｘの記録層金膜
けた。
ＣＨ３ＣＨｓ 実施例　２ 実施例１において例示化金物屋７０代夛に前掲例示化合
物Ａ６’に用いそして色素と化合物の混合比’ｅ７５／
１５とした以外は実施例１と同様にして記録媒体を作製
した。
実施例　３ 実施例２において例示化合物＆７の代シに前掲例示化合
物Ａ１０を用いた以外には実施例２と同様にして記録媒
体全作製した。
実施例　４ 実施例１において例示化合物Ａ７０代シに前掲例示化合
物Ａｌｔ用いそして色素と化合物の混合比’！−７０／
３０とした以外には実施例１と同様にして記録媒体を作
表した。
”・　　実施例　５ 実施例２において式（１）の色素の代）に下記式（２）
の色素を用いた以外は実施例２と同様にして記録媒体を
作製した。
比較例　１ 実施例１において例示化金物屋７０代シに前掲一般式に
おいてＭ＝Ｃｕ　、　Ｒ１、Ｒ２、Ｒｓ　、Ｒ４＝Ｈの
化合物を用いた以外には実施例１と同様にして記録媒体
管作製した。
比較例　２ 実施例１において例示化合物黒７０代りに前掲一般式に
おいてＭ””Ｃｕ　ｓ　Ｒ１、Ｒ２、Ｒ５、Ｒ４””　
Ｆの化合物を用いた以外は実施例１と同様にして記録媒
体を作製した。
比較例　３ 実施例１において例示化合物ム７０代シに前掲一般式に
おいてＭ＝ＭｎＳＲ１、Ｒ２、Ｒ５、Ｒ４＝Ｈの化合物
を用いた以外は実施例１と同様にして記録媒体管作製し
た。
比較例　４ 実施例１において式（１）の色素のみを用いて記録層を
形成した。
比較例　５ 実施例５において式（２）の色素のみを用いて記録層を
形成した。
上記実施例および比較例で作表した各記録媒体に波長７
９０ｎｍの半導体レーザ光を用いて基板側より、記録周
波数α５　ＭＨ２％　ＫＭ速１．５ｍ／ｓｅｃで情報を
書込み再生し、その再生波形をスペクトル解析（スキャ
ニングフィルター、バンド幅！ｌ０ＫＨ２）してＣ／Ｎ
ｌ測定し良。さらに、同じ記録媒体に５４０００ルツク
スのタングステン光ｔ２０時間照射して再生劣化加速実
験を行なつた後の反射率およびＣ／Ｎｌ測定した。なお
、反射率は基板側よシ測定した。その結果を下記の表に
まとめて示す。なお、反射率は溝部ではなく平坦面での
値である。

Claims (1)

  1. 【特許請求の範囲】 　基板上に直接または下引き層を介してポリメチン色素
    を主成分とする記録層を設けさらにその上に必要に応じ
    て保護層を設けてなる記録媒体において、前記記録層中
    に一般式 ▲数式、化学式、表等があります▼ 〔式中、Ｒ＿１、Ｒ＿２、Ｒ＿３およびＲ＿４はそれぞ
    れ水素または−ＳＯ＿２Ｎ（Ｒ＿５）＿２（Ｒ＿５は８
    個までの炭素原子を有するアルキル基または水素を表わ
    す）を表わすが、Ｒ＿１、Ｒ＿２、Ｒ＿３およびＲ＿４
    の少なくとも１つは−ＳＯ＿２Ｎ（Ｒ＿５）＿２を示し
    そしてＭはＣｕ、Ｖ、ＶＯ＿２、Ｐｂ、Ｎｉ、ＳｎＣｌ
    ＿２、Ｍｎ、ＺｎまたはＳｎを表わし、さらに上記式中
    の芳香環上にはＲ＿５以外の置換基が存在していてもよ
    い〕 で表わされる化合物を含有させることを特徴とする光情
    報記録媒体。
JP62020454A 1987-02-02 1987-02-02 光情報記録媒体 Pending JPS63189291A (ja)