KR101345839B1 - Flame resistance protective cushion and its fabricating method - Google Patents

Flame resistance protective cushion and its fabricating method Download PDF

Info

Publication number
KR101345839B1
KR101345839B1 KR1020130070282A KR20130070282A KR101345839B1 KR 101345839 B1 KR101345839 B1 KR 101345839B1 KR 1020130070282 A KR1020130070282 A KR 1020130070282A KR 20130070282 A KR20130070282 A KR 20130070282A KR 101345839 B1 KR101345839 B1 KR 101345839B1
Authority
KR
South Korea
Prior art keywords
flame retardant
flame
fabric
coating layer
artificial leather
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
KR1020130070282A
Other languages
Korean (ko)
Inventor
이영애
Original Assignee
이영애
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이영애 filed Critical 이영애
Priority to KR1020130070282A priority Critical patent/KR101345839B1/en
Application granted granted Critical
Publication of KR101345839B1 publication Critical patent/KR101345839B1/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

인조피혁재(100)를 준비하는 공정과, 베이스 패널(400) 상에 쿠션재(300)를 배치하는 공정과, 상기 인조피혁재(100)로 상기 쿠션재(300)를 감싼 후 상기 인조피혁재(100)를 상기 베이스 패널(400)에 고정하는 공정을 포함하는 보호 쿠션 제조방법이 개시된다. 이 방법에 있어서, 상기 인조피혁재를 준비하는 공정은, 직물(1)을 준비하는 단계와; 상기 직물(1)의 상면에만 국한하여 방염 코팅층(2)을 형성하는 단계와; 상기 방염 코팅층(2)을 덮는 표피(4)를 형성하는 단계와; 상기 표피(4)에 무늬를 형성하는 단계를 포함한다.The process of preparing the artificial leather 100, the process of arranging the cushioning material 300 on the base panel 400, and after wrapping the cushioning material 300 with the artificial leather 100, the artificial leather ( Disclosed is a method of manufacturing a protective cushion comprising a step of fixing 100 to the base panel 400. In this method, the process of preparing the artificial leather material comprises the steps of preparing a fabric (1); Forming a flame retardant coating layer (2) limited to only the top surface of the fabric (1); Forming an outer skin (4) covering said flame resistant coating layer (2); Forming a pattern on the epidermis (4).

Description

내염성 보호 쿠션 및 그 제조방법{FLAME RESISTANCE PROTECTIVE CUSHION AND ITS FABRICATING METHOD}Flame-resistant protective cushion and its manufacturing method {FLAME RESISTANCE PROTECTIVE CUSHION AND ITS FABRICATING METHOD}

본 발명은 실내공간의 벽에 부착 설치되거나 또는 실내 공간의 바닥에 배치되는 보호 쿠션에 관한 것으로서, 특히, 어린이, 노약자, 환자 등을 보호하기 위해, 어린이집, 유치원, 학원, 학교, 병원 등의 실내에 유용하게 적용될 수 있고, 화재 발생을 대비하여 우수한 방염 및 난연 특성을 갖는 보호 쿠션에 관한 것이다.The present invention relates to a protective cushion attached to the wall of the indoor space or disposed on the floor of the indoor space, in particular, in order to protect children, the elderly, patients, etc., indoors, such as a nursery, kindergarten, academy, school, hospital The present invention relates to a protective cushion that can be usefully applied to a fire and has excellent flame retardant and flame retardant properties against fire.

어린이집, 유치원, 학원, 학교, 병원 등의 실내 공간에 어린이, 노약자, 환자 등이 벽에 부딪히거나 넘어질 때 충격을 흡수하여 부상을 방지할 목적으로 보호 쿠션이 이용되고 있다. 이러한 보호 쿠션은 전술한 것과 같은 실내 공간의 내벽 또는 바닥에 고정 설치 또는 배치된다. Protective cushions are used for the purpose of preventing injuries by absorbing shocks when children, senior citizens, patients, etc. hit the walls or fall in indoor spaces such as daycare centers, kindergartens, academies, schools, and hospitals. This protective cushion is fixedly installed or arranged on the inner wall or floor of the indoor space as described above.

위와 같은 보호 쿠션은 충분한 충격 흡수 성능을 가져야 함과 동시에 내벽이나 바닥에 견고하게 유지될 수 있는 특성을 갖는 것이 좋다. 또한 보호 쿠션은 인테리어 기능을 가져야하므로 외관적으로도 미려함을 갖는 것이 좋다. 이를 위해, 벽에 대한 부착성 또는 바닥에 대한 견고한 유지 성능을 부여하기 위한 강성 베이스 패널 상에 쿠션 성능을 부여하기 위한 스폰지 등 쿠션재를 부착하고, 미려한 표면 특성을 갖는 인조피혁재로 쿠션재를 감싼 후 그 인조피혁재를 베이스 패널에 고정하여 마감한 보호 쿠션이 제안된 바 있다.The protective cushion as described above should have sufficient impact absorption performance and at the same time have a property that can be firmly maintained on the inner wall or floor. In addition, the protective cushion should have an interior function, so it is good to have aesthetic appearance. To this end, a cushioning material such as a sponge for imparting cushioning performance is attached on a rigid base panel to give adhesion to a wall or a solid holding performance to the floor, and the cushioning material is wrapped with an artificial leather having beautiful surface characteristics. A protective cushion has been proposed in which the artificial leather is fixed to the base panel.

또한 보호 쿠션은, 전술한 것과 같이 화재 대비가 특히 요구되는 시설물(예컨대, 어린이집, 유치원, 학교, 병원) 등에 적용되는 것임에도 불구하고, 전체적으로 불에 잘 타고, 불에 탈 때 유독 가스를 발생시키는, 화재에 취약한 재료들로 이루어져 이에 대한 개선이 시급한 상황이다. 특히, 실내에 설치된 보호 쿠션의 인조피혁재는, 화재 발생시 가장 먼저 불에 닿는 부분으로, 종래에는 쉽게 잘 타고 화염을 빠르게 전파하는 재료만으로 이루어져 그 문제가 심각하였다. 보다 구체적으로, 인조피혁재는 합성수지로 된 직물 기재와 그 직물 기재 상에 형성된 표피를 포함하는데, 직물 기재와 표피 모두 유기화합물과 같은 연소성 물질로 제조되므로, 화재시 불에 쉽게 타고 화염이 주변으로 잘 번지게 하며, 특히, 연소 과정에서 다이옥신 등을 포함하는 유해가스를 다량으로 배출한다. 또한, 종래의 보호 쿠션은 스폰지 등으로 이루어진 쿠션재는 화재시 많은 유독가스를 발생시킴과 동시에 화염을 빨리 전파한다는 점에서 이에 대한 대처가 시급한 상황이다. In addition, although the protective cushion is applied to a facility (e.g., a nursery, a kindergarten, a school, a hospital, etc.) where fire protection is particularly required as described above, it is well burned as a whole and generates toxic gas when burning. In addition, it is urgently needed to improve these materials because they are made of materials that are vulnerable to fire. In particular, the artificial leather of the protective cushion installed in the room, which is the first part that touches the fire when a fire occurs, the problem was serious only made of a material that easily rides quickly and propagates the flame in the prior art. More specifically, artificial leather includes a fabric base made of synthetic resin and a skin formed on the fabric base. Both fabric bases and skins are made of combustible materials such as organic compounds, so that in case of fire, the flame is easily burned. In particular, in the combustion process, a large amount of harmful gases including dioxins are emitted. In addition, the conventional protective cushion is a situation in which the cushion material made of a sponge or the like to generate a lot of toxic gas during the fire and at the same time to propagate the flame in an urgent situation to deal with this.

실용신안등록 제20-0258727(등록일자: 2001년 12월 12일)Utility Model Registration No. 20-0258727 (Registration Date: December 12, 2001)

본 발명의 발명자는, 위와 같은 문제점을 해결하기 위하여 다양한 연구를 하였는바, 그 하나는 화재시 불이 처음 닿는 인조피혁재에 내염, 방염 및/또는 난연성을 부여하는 것이었다. 인조피혁재에 내염, 방염 및/또는 난연 특성을 부여하기 위해, 난연성 물질을 포함하는 합성수지를 이용하여 표피를 형성하거나 또는 난연사를 이용하여 직조한 직물을 인조 가죽으로 이용하는 방식이 고려되었다. 그러나, 위와 같은 방식들의 채용만으로 인조피혁재에 충분한 내염 특성을 부여하기 어려웠다. 또한 불연성 소재와 인조피혁재를 미리 일체화하여 이용하는 방법도 고려되었다. 그러나, 이는 인조피혁재의 유연성과 질감이 훼손되는 문제점이 있음을 알게 되었다. In order to solve the above problems, the inventor of the present invention has conducted various studies, one of which is to impart flame, flame and / or flame retardancy to an artificial leather which is first touched by fire. In order to impart flame resistant, flame retardant and / or flame retardant properties to artificial leather, a method of forming a skin using synthetic resin containing a flame retardant material or using a woven fabric using flame retardant yarn as an artificial leather has been considered. However, it was difficult to provide sufficient flame resistance characteristics to the artificial leather by only adopting the above methods. In addition, a method of using a non-combustible material and artificial leather in advance is also considered. However, it has been found that there is a problem that the flexibility and texture of artificial leather is damaged.

따라서 본 발명이 해결하고자 하는 하나의 과제는, 유연성과 질감을 그대로 유지하면서도 내염 특성이 탁월한 인조피혁재로 쿠션재를 감싸도록 하여, 혹시 있을 수 있는 화재에 충분하게 대비할 수 있는 개선된 구조의 보호 쿠션을 제공하는 것이다.Accordingly, one problem to be solved by the present invention is to protect the cushioning material with artificial leather having excellent flame resistance while maintaining flexibility and texture as it is, thereby providing a protective cushion of an improved structure that can be sufficiently prepared for any possible fire. To provide.

본 발명의 일 측면에 따라, 인조피혁재(100)를 준비하는 공정과, 베이스 패널(400) 상에 쿠션재(300)를 배치하는 공정과, 상기 인조피혁재(100)로 상기 쿠션재(300)를 감싼 후 상기 인조피혁재(100)를 상기 베이스 패널(400)에 고정하는 공정을 포함하는 보호 쿠션 제조방법이 제공되며, 상기 인조피혁재를 준비하는 공정은, 직물(1)을 준비하는 단계와; 상기 직물(1)의 상면에만 국한하여 방염 코팅층(2)을 형성하는 단계와; 상기 방염 코팅층(2)을 덮는 표피(4)를 형성하는 단계와; 상기 표피(4)에 무늬를 형성하는 단계를 포함한다.According to an aspect of the present invention, the process of preparing the artificial leather 100, the process of arranging the cushioning material 300 on the base panel 400, and the cushioning material 300 to the artificial leather 100 After wrapping the protective leather manufacturing method comprising the step of fixing the artificial leather 100 to the base panel 400 is provided, the process of preparing the artificial leather, the step of preparing the fabric (1) Wow; Forming a flame retardant coating layer (2) limited to only the top surface of the fabric (1); Forming an outer skin (4) covering said flame resistant coating layer (2); Forming a pattern on the epidermis (4).

본 발명의 다른 측면에 따라, 인조피혁재(100)를 준비하는 공정과, 베이스 패널(400) 상에 쿠션재(300)를 배치하는 공정과, 상기 인조피혁재(100)와 상기 인조피혁재(100) 안쪽에 위치하는 불연시트(200)로 상기 쿠션재(300)를 감싼 후 상기 인조피혁재(100)와 상기 불연시트(200)를 상기 베이스 패널(400)에 고정하는 공정을 포함하는 보호 쿠션 제조방법이 제공되며, 이 제조 방법에 있어서도, 상기 인조피혁재를 준비하는 공정은, 직물(1)을 준비하는 단계와; 상기 직물(1)의 상면에만 국한하여 방염 코팅층(2)을 형성하는 단계와; 상기 방염 코팅층(2)을 덮는 표피(4)를 형성하는 단계와; 상기 표피(4)에 무늬를 형성하는 단계를 포함한다.According to another aspect of the invention, the process of preparing the artificial leather 100, the process of disposing the cushioning material 300 on the base panel 400, and the artificial leather 100 and the artificial leather ( 100) a protective cushion including a step of fixing the artificial leather material 100 and the non-combustible sheet 200 to the base panel 400 after wrapping the cushioning material 300 with a non-combustible sheet 200 located inside. A manufacturing method is provided, and also in this manufacturing method, the process of preparing the artificial leather comprises the steps of: preparing a fabric (1); Forming a flame retardant coating layer (2) limited to only the top surface of the fabric (1); Forming an outer skin (4) covering said flame resistant coating layer (2); Forming a pattern on the epidermis (4).

일 실시예에 따라. 상기 표피(4)를 형성하는 단계 전에 상기 방염 코팅층(2) 상에 난연성 본딩층(3)을 형성하는 단계를 더 포함하고, 상기 표피(4)를 형성하는 단계는 상기 난연성 본딩층(3)에 난연성 폴리우레탄을 코팅하는 것을 포함한다.According to one embodiment. And forming a flame retardant bonding layer 3 on the flame retardant coating layer 2 prior to forming the skin 4, wherein forming the skin 4 is the flame retardant bonding layer 3. Coating the flame retardant polyurethane on the substrate.

본 발명의 또 다른 측면에 따라 전술한 방법으로 제조되는 내염성 보호 쿠션이 제공되며, 상기 내염성 보호 쿠션은, 베이스 패널(400)과; 상기 베이스 패널 상에 배치되는 쿠션재(300)와; 상기 쿠션재를 감싼 채 상기 베이스 패널에 고정되는 인조피혁재(100)를 포함하며, 상기 인조피혁재(100)는, 직물(1)과, 상기 직물(1)의 상면에만 국한하여 방염 코팅층(2)과, 상기 방염 코팅층(2)을 덮는 표피(4)를 포함한다.According to another aspect of the present invention there is provided a flameproof protective cushion manufactured by the above-described method, the flameproof protective cushion, the base panel 400; A cushion material disposed on the base panel; Including the artificial leather 100 is fixed to the base panel while wrapping the cushion material, the artificial leather 100, the fabric 1 and the flame retardant coating layer 2 limited to only the upper surface of the fabric (1) ) And the skin 4 covering the flame retardant coating layer 2.

이때, 상기 내염성 보호 쿠션은 상기 인조피혁재(100)와 상기 쿠션재(300) 사이에 개재된 불연시트(200)를 더 포함할 수 있다. 그리고, 상기 불연시트(200)는 유리섬유 시트, 탄소섬유 시트 또는 실리카 시트 중 적어도 하나를 포함하고, 상기 표피(4)는 난연성 폴리우레탄을 포함하고, 상기 방염 코팅층(2)은 상기 직물(1) 두께의 1/10 ~ 1/1000 의 두께로 형성되고, 상기 방염 코팅층(2)은 인계 난연재와 탄소계 화합물을 포함하는 난연재중 적어도 하나를 포함하고, 상기 인계 난연재는 ADPP(anilinodiphenyl phosphate), RDPP (resorcinol -bis[diphenol phosphate)를 포함하며, 상기 탄소계 화합물을 포함하는 난연재는 탄소계 화합물, 촉매, 불연성 기체 원료 및 방염용 필러를 포함하고, 상기 탄소계 화합물은 탄수화물, 단백질 또는 다가 알콜을 포함하고, 상기 촉매는 무기 산을 포함하며, 상기 방염용 필러는 알루미나 삼수화물, 규산염, 카올린, 석고 및 수화점토 중 적어도 하나를 포함한다.In this case, the flame resistant protective cushion may further include a non-flammable sheet 200 interposed between the artificial leather 100 and the cushion material 300. The non-flammable sheet 200 may include at least one of a glass fiber sheet, a carbon fiber sheet, or a silica sheet, the skin 4 may include a flame retardant polyurethane, and the flame retardant coating layer 2 may include the fabric 1 The flame retardant coating layer 2 includes at least one of a flame retardant containing a phosphorus-based flame retardant and a carbon-based compound, and the phosphorus-based flame retardant includes ADPP (anilinodiphenyl phosphate), A flame retardant comprising RDPP (resorcinol-bis [diphenol phosphate), wherein the flame retardant comprising the carbon-based compound includes a carbon-based compound, a catalyst, a non-flammable gas raw material, and a flame retardant filler, and the carbon-based compound is a carbohydrate, a protein, or a polyhydric alcohol. The catalyst includes an inorganic acid, and the flame retardant filler includes at least one of alumina trihydrate, silicate, kaolin, gypsum, and hydrated clay.

본 발명에 따른 보호 쿠션은, 예를 들면 화재 대비가 특히 요구되는 시설물(예컨대, 어린이집, 유치원, 학교, 병원) 등에서 실내 공간의 내벽 또는 바닥 설치재로 유용하게 적용될 수 있으며, 화재 발생시 가장 먼저 불에 닿는 부분인 인조피혁재가 효과적으로 화염의 전파를 억제 또는 지연하여, 화재시 화염 또는 유독가스로 인한 인명 손상을 최소화시키는데 크게 기여할 수 있다. The protective cushion according to the present invention can be usefully applied as an inner wall or floor mounting material of an indoor space, for example, in a facility (for example, a nursery, a kindergarten, a school, or a hospital) where fire protection is particularly required, Artificial leather, which is in contact with it, effectively suppresses or delays the propagation of the flame, which can greatly contribute to minimizing human injury caused by the flame or toxic gas in case of fire.

본 발명에 따르면, 보호 쿠션의 인조피혁재는 방염 코팅층이 난연성 직물 상면에 형성되며, 인조피혁재가 화염에 노출시 방염 코팅층이 화염을 차단하는 역할을 하는 한편 화염 노출시간 증가로 인하여 방염 코팅층이 형성된 직물에 화염구멍이 형성되더라도 방염 코팅층이 화염구멍 둘레에서 직물의 하부면 측으로 돌출하여 화염이 급속하게 번지는 것을 억제해준다. 또한, 인조피혁재와 쿠션재 아래에 불연성 재료를 추가로 더 둠으로써, 인조피혁재에 화염 구멍이 생기더라도 그 불연성 재료가 쿠션재로 화염이 전달되는 것을 완벽하게 차단하여 더 이상 화재가 번지는 것을 막아줄 수 있다. 본 발명의 다른 이점 내지 효과는 이하 실시예의 설명으로부터 당업자라면 충분히 이해할 수 있을 것이다. According to the present invention, the artificial leather of the protective cushion is a flame retardant coating layer is formed on the flame-retardant fabric upper surface, when the artificial leather material is exposed to the flame, the flame retardant coating layer serves to block the flame while the flame resistant coating layer is formed due to increased flame exposure time Even if a flame hole is formed in the flame retardant coating layer protrudes toward the lower surface of the fabric around the flame hole to suppress the spread of the flame rapidly. In addition, by adding an additional non-combustible material underneath the artificial leather and cushioning material, even if a fire hole is formed in the artificial leather material, the non-combustible material completely blocks the transmission of the flame to the cushioning material, preventing further fire spreading. Can give Other advantages and effects of the present invention will be fully understood by those skilled in the art from the following description of the examples.

도 1은 본 발명의 일 실시예에 따른 보호 쿠션을 도시한 부분 절개 사시도이다.
도 2는 도 1에 도시된 보호 쿠션을 부분 확대 단면도화 함께 도시한 단면도이다.
도 3는 도 1 및 도 2에 도시된 보호 쿠션의 인조피혁재를 설명하기 위한 사시도이다.
도 4의 (a), (b), (c), (d)는 도 1에 도시된 보호 쿠션 제조에 이용되는 재료들인 인조피혁재, 불연시트, 쿠션재 및 베이스 패널을 각각 도시한 단면도들이다.
도 5 내지 도 9는 보호 쿠션 제조 방법의 한 과정으로서, 도 4의 (a)에 도시된 인조피혁재를 준비(제조)하는 과정을 예시적으로 설명하기 위한 도면들이다.
도 10은 보호 쿠션 제조 방법의 또 다른 한 과정으로서, 4의 (a), (b), (c), (d)에 도시된 재료들을 적층 구조로 결합하는 과정을 설명하기 위한 도면이다.
도 11은 방염 코팅층이 형성된 직물에 화염을 직접 노출시킨 후 시간 흐름(10초, 15초, 1분, 1분 20초)에 따른 직물의 (방염 코팅층이 있는) 상부면 상태 변화를 보여주는 사진도들이고,
도 12 방염 코팅층이 형성된 직물의 상부면에 화염을 일정 시간(1분 20초) 가한 후 방염 코팅층이 없는 직물의 하부면 상태를 보여주는 사진도이다.1 is a partial cutaway perspective view showing a protective cushion according to an embodiment of the present invention.
2 is a cross-sectional view of the protective cushion shown in FIG.
3 is a perspective view for explaining the artificial leather of the protective cushion shown in FIG.
(A), (b), (c), and (d) of FIG. 4 are cross-sectional views showing artificial leather, non-combustible sheet, cushioning material, and base panel, respectively, which are materials used to manufacture the protective cushion shown in FIG.
5 to 9 are diagrams for explaining a process of preparing (manufacturing) the artificial leather shown in FIG.
FIG. 10 is a view for explaining a process of combining the materials shown in (a), (b), (c), and (d) of FIG. 4 as another process of the protective cushion manufacturing method.
11 is a photograph showing the change of the top surface of a fabric (with a flame retardant coating layer) according to the time flow (10 seconds, 15 seconds, 1 minute, 1 minute 20 seconds) after direct exposure of the flame to the fabric on which the flame resistant coating layer was formed. Entering,
12 is a photograph showing the state of the lower surface of the fabric without a flame resistant coating layer after applying a flame (1 minute 20 seconds) to the upper surface of the fabric on which the flame resistant coating layer is formed.

이하 첨부한 도면을 참조하여 본 발명의 실시예들을 상세히 설명하기로 한다. 다음에 소개되는 실시예들은 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위한 예로서 제공되는 것이다. 따라서 본 발명은 이하 설명되는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 그리고 도면에 있어서, 구성요소의 폭, 길이, 두께 등은 편의를 위해 과장되어 표현될 수 있다. Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. The following embodiments are provided as examples to sufficiently convey the spirit of the present invention to those skilled in the art. Therefore, the present invention is not limited to the embodiments described below and may be embodied in other forms. In the drawings, the width, length, thickness, and the like of the components may be exaggerated for convenience.

도 1은 본 발명의 일 실시예에 따른 보호 쿠션을 도시한 부분 절개 사시도이고, 도 2는 도 1에 도시된 보호 쿠션을 부분 확대 단면도화 함께 도시한 단면도이고, 도 3는 도 1 및 도 2에 도시된 보호 쿠션의 인조피혁재를 설명하기 위한 사시도이고, 도 4의 (a), (b), (c), (d)는 도 1에 도시된 보호 쿠션 제조에 이용되는 재료들인 인조피혁재, 불연시트, 쿠션재 및 베이스 패널을 각각 도시한 단면도들이고, 도 5 내지 도 9는 보호 쿠션 제조 방법의 한 과정으로서, 도 4의 (a)에 도시된 인조피혁재를 준비(제조)하는 과정을 예시적으로 설명하기 위한 도면들이며, 도 10은 보호 쿠션 제조 방법의 또 다른 한 과정으로서, 4의 (a), (b), (c), (d)에 도시된 재료들을 적층 구조로 결합하는 과정을 설명하기 위한 도면이다. 도 11은 방염 코팅층이 형성된 직물에 화염을 직접 노출시킨 후 시간 흐름(10초, 15초, 1분, 1분 20초)에 따른 직물의 (방염 코팅층이 있는) 상부면 상태 변화를 보여주고, 도 12 방염 코팅층이 형성된 직물의 상부면에 화염을 일정 시간(1분 20초) 가한 후 방염 코팅층이 없는 직물의 하부면 상태를 보여준다.1 is a partial cutaway perspective view showing a protective cushion according to an embodiment of the present invention, Figure 2 is a cross-sectional view showing a partial enlarged cross-sectional view of the protective cushion shown in Figure 1, Figure 3 and Figures 1 and 2 Figure 4 is a perspective view for explaining the artificial leather of the protective cushion shown in Figure 4, (a), (b), (c), (d) is artificial leather which is a material used to manufacture the protective cushion shown in FIG. Ash, non-combustible sheet, cushioning material and the base panel are cross-sectional views respectively, Figures 5 to 9 is a process of manufacturing a protective cushion, the process of preparing (manufacturing) the artificial leather material shown in Figure 4 (a) 10 is a view illustrating an exemplary embodiment of the present invention, and FIG. 10 is another process of the method for manufacturing a protective cushion, wherein the materials shown in 4 (a), (b), (c) and (d) are combined into a laminated structure. It is a figure for demonstrating the process. FIG. 11 shows the change of state of the top surface of the fabric (with flame retardant coating layer) over time (10 seconds, 15 seconds, 1 minute, 1 minute 20 seconds) after direct exposure of the flame to the fabric on which the flame resistant coating layer was formed, Figure 12 shows the state of the bottom surface of the fabric without a flame resistant coating layer after applying a flame (1 minute 20 seconds) to the top surface of the fabric on which the flame resistant coating layer is formed.

도 1 내지 도 4를 참조하면, 보호 쿠션(1000)은 그것이 설치되는 면에서 강성을 부여하기 위해 제공되는 대략 직사각형 또는 정사각형의 베이스 패널(400)과, 충격 흡수를 위해 상기 베이스 패널(400)의 상면에 부착되는 쿠션재(300)와, 상기 쿠션재(300)를 감싸도록 제공되는 인조피혁재(100)를 포함한다. 부가적으로, 상기 보호 쿠션(1000)은 상기 인조피혁재(100)와 상기 쿠션재(300) 사이에서 제공되어 인조피혁재(100)에 불이 붙는 경우에도 상기 쿠션재(300)로 불이 번지는 것을 차단하기 위한 불연시트(200)을 더 포함할 수 있다. 상기 인조피혁재(100)는, 화재시 불이 최초로 닿는 부분으로서, 이하 자세히 설명되는 바와 같이 충분한 내염 특성을 갖도록 제작된다.1 to 4, the protective cushion 1000 is formed of a substantially rectangular or square base panel 400 provided to impart rigidity at the surface where it is installed, and the base panel 400 of the base panel 400 for shock absorption. And a cushioning material 300 attached to the upper surface, and an artificial leather material 100 provided to surround the cushioning material 300. In addition, the protective cushion 1000 is provided between the artificial leather 100 and the cushioning material 300 so that the fire is spread to the cushioning material 300 even when the artificial leather 100 is catching fire. It may further include a non-flammable sheet 200 to block the thing. The artificial leather 100 is, as the fire portion first touches during the fire, is manufactured to have sufficient flame resistance as described in detail below.

본 실시예에서, 상기 보호 쿠션(1000)은 베이스 패널(400) 상에 쿠션재(300) 착한 후, 미려한 표면 특성을 갖는 인조피혁재(100)로 상기 쿠션재(300)를 감싼 후, 예컨대, 스테이플과 같은 고정부재(600)로 상기 인조피혁재(100)를 상기 베이스 패널(400)에 고정하여 마감하는 방식으로 제작된다. 이때, 인조피혁재(100)로 마감하기 전에, 인조피혁재(100)의 고정 방식과 동일한 방식으로 상기 불연시트(200)로 상기 쿠션재(300)를 1차로 미리 감싸 고정할 수 있다.In the present embodiment, the protective cushion 1000 is attached to the cushioning material 300 on the base panel 400, and then wrapped the cushioning material 300 with artificial leather 100 having a beautiful surface characteristics, for example, staples The artificial leather 100 is fixed to the base panel 400 by a fixing member 600 such as to be manufactured in a manner of finishing. At this time, before finishing with the artificial leather 100, the cushion member 300 may be wrapped in the primary and preliminarily fixed in the same manner as the fixing method of the artificial leather 100.

상기 베이스 패널(400)는 충분한 강성을 가지면서도 경량성을 갖는 MDF(Medium Density Fiber board) 합판을 일정 크기 및 형상으로 재단하여 제작된 것이 이용하게 이용된다. 또한 상기 MDF 패널은 스테이플과 같은 고정부재(600)가 쉽게 박힐 수 있는 특성을 가지므로, 상기 고정부재(600)를 이용한 인조피혁재(100)의 고정 작업에 있어서 유리하다. 상기 베이스 패널(400)은 난연 특성을 확보하기 위해 표면에 난연 코팅층을 더 포함할 수 있다.The base panel 400 is used to be produced by cutting the MDF (Medium Density Fiber board) plywood having a sufficient rigidity and lightweight to a certain size and shape. In addition, the MDF panel has a property that the fixing member 600, such as staples, can be easily nailed, and is advantageous in the fixing operation of the artificial leather 100 using the fixing member 600. The base panel 400 may further include a flame retardant coating layer on the surface to ensure flame retardant properties.

상기 쿠션재(300)는 탄성 변형이 가능한 다양한 재료가 이용될 수 있으며, 예컨대, PU 스폰지 또는 PE 스폰지가 유용하게 이용될 수 있다. 도시된 것과 같이 상기 쿠션재(300)이 벌크형 스폰지로 이루어질 수 있지만, 다수의 스폰지(특히, PE 스폰지) 알갱이들이 모여 하나의 쿠션재(300)를 구성할 수도 있음에 유의한다. 다수의 알개이형 스폰지를 일정 형태로 봉지하는 봉지 재료가 요구될 것이다. 상기 쿠션재(300)는 일정 두께를 갖는 판 형태에서 압축 변형되어, 예컨대, 도시된 것과 같이 양 사이드에 곡부를 갖는 단면 형상을 가질 수 있다. 상기 쿠션재(300)로 나연성 스폰지를 이용하는 것도 고려될 수 있다.As the cushioning material 300, various materials capable of elastic deformation may be used. For example, a PU sponge or a PE sponge may be usefully used. As shown in the figure, the cushion member 300 may be made of a bulk sponge, but it is noted that a plurality of sponge (especially, PE sponge) grains may be gathered to constitute one cushion member 300. There will be a need for an encapsulation material that encapsulates a plurality of nested sponges in some form. The cushion member 300 is compressively deformed in the form of a plate having a predetermined thickness, for example, may have a cross-sectional shape having curved portions on both sides as shown. It may also be considered to use a flame retardant sponge as the cushion material 300.

상기 불연시트(200)은 유리섬유 시트, 탄소섬유 시트 또는 실리카 시트로 이루어질 수 있다. 상기 불연시트(200)은 인조피혁재(100)에 화염 구멍이 형성되더라도 화염 구멍을 통과한 화염을 차단하므로 화염이 더 이상 확산되는 것을 막을 수 있다.The non-combustible sheet 200 may be made of a glass fiber sheet, a carbon fiber sheet or a silica sheet. The non-combustible sheet 200 may block the flame passing through the flame hole even if the flame hole is formed in the artificial leather 100, thereby preventing the flame from spreading further.

도 2 및 도 3에 잘 도시된 바와 같이, 상기 쿠션재(300)를 감싸는 인조피혁재(100)는 직물(1)과, 상기 직물(1)의 상면에만 국한적으로 형성된 방염 코팅층(2)과, 상기 방염 코팅층(2) 상에 형성된 난연성 본딩층(3)과, 상기 난연성 본딩층(3) 상에 코팅 형성된 난연성 표피(4)를 포함한다. 이때, 난연성 본딩층(3)을 생략하고 난연성 표피(4)가 방염 코팅층(2) 상에 직접 형성되는 것도 고려될 수 있다. 2 and 3, the artificial leather 100 surrounding the cushion member 300 is a fabric (1), and the flame-resistant coating layer (2) formed only on the upper surface of the fabric (1) and And a flame retardant bonding layer 3 formed on the flame retardant coating layer 2, and a flame retardant skin 4 coated on the flame retardant bonding layer 3. In this case, it is also possible to omit the flame retardant bonding layer 3 and to form the flame retardant skin 4 directly on the flame retardant coating layer 2.

상기 직물(1)은 예컨대 난연사(flame retardant fibers)를 횡사(11) 및 경사(12)로 하여 평직하거나 또는 니팅(knitting)하여 만들어질 수 있다. 난연사는 폴리에스테르 계열의 난연사일 수 있다. 하지만, 상기 난연사는 난연성 폴리에스테르, 모다크릴릭(modacrylic), 면, 레이온, PP, 나일론 중 하나 또는 이들 중 2개 이상을 브렌딩하여 만들어진 것일 수 있다.The fabric 1 can be made, for example, by weaving flame retardant fibers into the transverse yarns 11 and the warp yarns 12 or by knitting or knitting. Flame retardant yarn may be a polyester-based flame retardant yarn. However, the flame retardant yarn may be made by blending one or two or more of flame retardant polyester, modacrylic, cotton, rayon, PP, nylon.

상기 방염 코팅층(2)은 상기 직물(1)의 유연성을 저하시키지 않는 두께로 상기 직물(1)의 상면에만 제한적으로 형성된다. 상기 방염 코팅층(2)은 상기 직물(1) 두께의 1/10 ~ 1/1000 의 두께로 형성되는 것이 좋다. 방염 코팅층(2)은 나이프 코팅, 로울러 코팅, 스프레이 코팅, 캘린더 코팅, 전사 코팅 또는 스크린 날염과 같은 코팅 기술을 이용하여 형성될 수 있다.  The flame retardant coating layer 2 is formed only limited to the upper surface of the fabric 1 to a thickness that does not reduce the flexibility of the fabric (1). The flame retardant coating layer 2 is preferably formed to a thickness of 1/10 ~ 1/1000 of the thickness of the fabric (1). The flame retardant coating layer 2 can be formed using a coating technique such as knife coating, roller coating, spray coating, calender coating, transfer coating or screen printing.

방염 코팅층(2)은 인계 난연재로서 ADPP(anilinodiphenyl phosphate), RDPP (resorcinol -bis[diphenol phosphate)를 이용할 수 있다. 또한 방염 코팅층(2)은 탄소계 화합물을 포함하는 것이 이용될 수 있다. 후자의 경우, 방염 코팅층(2)은 탄소 원료(즉, 탄소계 화합물), 촉매 및 불연성 기체 원료를 포함할 수 있다. 이 경우, 탄소계 화합물로는 카제인 또는 전분과 같은 탄수화물, 단백질 또는 다가 알콜을 포함할 수 있다. 방염 코팅층(2)이 화염에 노출시 촉매는 탄소계 화합물을 발포시켜 화염의 진행을 차단하는 탄소 입자들을 만든다. 촉매로는 무기 산 또는 무기 산의 분해 형태인 화합물을 포함할 수 있다. 또한, 방염 코팅층(2) 형성을 위한 방염 약재는 알루미나 삼수화물, 규산염, 카올린, 석고 및 수화점토와 같은 방염용 필러가 추가될 수 있다. 이때, 상기 촉매에 포함될 수 있는 무기 산은 붕산, 인산 또는 황산일 수 있다.The flame retardant coating layer (2) may be used as a phosphorus-based flame retardant material (ADPP (anilinodiphenyl phosphate), RDPP (resorcinol -bis [diphenol phosphate)). In addition, the flame retardant coating layer 2 may include a carbon-based compound. In the latter case, the flame retardant coating layer 2 may comprise a carbon raw material (ie, a carbon-based compound), a catalyst and a non-combustible gas raw material. In this case, the carbon-based compound may include carbohydrates such as casein or starch, protein or polyhydric alcohol. When the flame retardant coating layer 2 is exposed to flame, the catalyst foams carbon-based compounds to produce carbon particles that block the progress of the flame. The catalyst may include an inorganic acid or a compound in the form of decomposition of the inorganic acid. In addition, the flame retardant medicine for forming the flame retardant coating layer 2 may be added flame retardant fillers such as alumina trihydrate, silicate, kaolin, gypsum and hydrated clay. In this case, the inorganic acid that may be included in the catalyst may be boric acid, phosphoric acid or sulfuric acid.

난연성 본딩층(3)은, 방염 코팅층(2)에 대한 난연성 표피(4)의 부착 특성을 좋게 하기 위해 부가적으로 제공되는 것으로서, 접착성분을 갖는 합성수지가 방염 코팅층(2) 상에 도포되어 형성된다. 상기 난연성 본딩층(3)은 까칠 까칠한 방염 코팅층(2)을 덮어 아래로 가림과 동시에 표피(4) 코팅을 위한 최적의 표면을 제공한다. 난연성 본딩층(3)은 표피(4)의 재료와 친화력을 갖는 재료로 선택되며, 예컨대, 표피(4)가 난연성 폴리우레탄 수지를 코팅하여 형성되는 경우, 난연성 본딩층(3)은 폴리우레탄 또는 그와 유사한 합성수지 재료로 이루어진다.The flame retardant bonding layer 3 is additionally provided to improve the adhesion property of the flame retardant skin 4 to the flame retardant coating layer 2, and is formed by applying a synthetic resin having an adhesive component on the flame retardant coating layer 2. do. The flame-retardant bonding layer 3 covers the rough, flame-retardant coating layer 2 and covers it down and at the same time provides an optimal surface for coating the epidermis 4. The flame retardant bonding layer 3 is selected as a material having affinity with the material of the skin 4, for example, when the skin 4 is formed by coating a flame retardant polyurethane resin, the flame retardant bonding layer 3 is made of polyurethane or Similar synthetic resin materials.

상기 표피(4)는 난연성 폴리우레탄 재료로 형성되는 것이 바람직하다. 난연성 폴리우레탄 재료를 상기 난연성 본딩층(3) 상에 코팅하여 전술한 표피(4)를 얻을 수 있다. 난연성 폴리우레탄 재료는 폴리카보네이트디올과 폴리테트라메틸렌에테르글리콜이 중량비 1:1 ~ 2:1로 혼합된 폴리올 혼합물을 교반하여 약 60~80℃로 유지시킨 다음, 폴리올 혼합물에 메틸렌디페닐디이소시아네이트를 첨가하여 반응시킨 후 수세하여 고형의 프리폴리머를 얻고, 상기 프리폴리머에 디메틸포름아미드를 가하여 용해시키고 1,4-부탄디올과 인산 에스테르 디올의 혼합물을 사슬연장제로 투입하여 60 내지 80℃에서 일정시간 반응시켜 합성한 것이 이용될 수 있다. 대안적으로, 폴리우레탄 배합액의 배합시, 트리아릴포스페이트 등의 인계 난연제 또는 할로겐계 난연제를 일정량 첨가하여 만들어진 난연성 폴리우레탄 재료가 이용될 수도 있다. 상기 표피(4)는 일정 패턴의 무늬를 포함하되, 상기 무늬는 무늬 성형 필름 또는 무늬 성형 롤러를 이용한 가압에 의해 형성될 수 있다. 위와 같이 제조된 내염성 인조피혁재를 KSF 2271:2006에서 정한 바에 따라 가열시험, 표면시험, 가스유해성시험 및 부가시험을 하였으며 난연 1급의 조건들을 모두 만족시켰다. The skin 4 is preferably formed of a flame retardant polyurethane material. A flame retardant polyurethane material may be coated on the flame retardant bonding layer 3 to obtain the skin 4 described above. The flame-retardant polyurethane material is a polyol mixture containing polycarbonate diol and polytetramethylene ether glycol in a weight ratio of 1: 1 to 2: 1 by stirring to maintain a temperature of about 60 ~ 80 ℃, and then to the polyol mixture methylene diphenyl diisocyanate After reaction by addition, washing with water to obtain a solid prepolymer, dimethylformamide was added to the prepolymer to dissolve it, and a mixture of 1,4-butanediol and phosphate ester diol was added as a chain extender to react at a constant time at 60 to 80 ° C for synthesis. One can be used. Alternatively, a flame-retardant polyurethane material made by adding a certain amount of a phosphorus-based flame retardant such as triaryl phosphate or a halogen-based flame retardant may be used in the formulation of the polyurethane compound. The skin 4 may include a pattern of a predetermined pattern, which may be formed by pressing using a pattern forming film or a pattern forming roller. The flame-resistant artificial leather produced as described above was subjected to heating test, surface test, gas hazard test and additional test as defined in KSF 2271: 2006, and satisfied all the conditions of flame retardant class 1.

위와 같은 내염 인조피혁재는 직물의 상면에 형성된 방염 코팅층이 화염을 중간에서 차단하여 탁월한 내염/방염 특성을 갖는다. Flameproof artificial leather as described above has an excellent flameproof / flameproof property by the flame-resistant coating layer formed on the upper surface of the fabric blocking the flame in the middle.

도 11은 방염 코팅층이 형성된 직물에 화염을 직접 노출시킨 후 시간 흐름(10초, 15초, 1분, 1분 20초)에 따른 직물의 (방염 코팅층이 있는) 상부면 상태 변화를 보여주고, 도 12는 방염 코팅층이 형성된 직물의 상부면에 화염을 일정 시간(1분 20초) 가한 후 방염 코팅층이 없는 직물의 하부면 상태를 보여준다.FIG. 11 shows the change of state of the top surface of the fabric (with flame retardant coating layer) over time (10 seconds, 15 seconds, 1 minute, 1 minute 20 seconds) after direct exposure of the flame to the fabric on which the flame resistant coating layer was formed, Figure 12 shows the state of the bottom surface of the fabric without a flame resistant coating layer after applying a flame (1 minute 20 seconds) to the top surface of the fabric on which the flame resistant coating layer is formed.

직물 상부면의 방염 코팅층에 화염이 직접 가해지는 동안 유해 가스는 거의 발생하지 않았다. 15초까지는 방염 코팅층에 거의 변화를 발견하기 어려웠고, 다만 방염 코팅층의 입자화를 발견할 수 있었다. 일정 시간이 지나면서 방염 코팅층이 형성되어 있는 직물에 화염 구멍이 생겼으며 화염 구멍의 크기는 천천히 증가하였다. 화염 구멍이 커지는 동안에도 가스 생성은 거의 없었다. 특히, 도 12를 참조하면, 화염 구멍 둘레에 형성된 턱이 직물의 하부면으로 돌출되어 있고 그 턱에는 방염 코팅층이 여전히 존재하여 화염 구멍을 통과하는 불꽃이 직물 하부면, 즉, 방염 코팅층이 없는 면으로 번지는 것을 차단하고 있음을 확인할 수 있었다.During the direct application of flames to the flame retardant coating on the top surface of the fabric, little harmful gases were generated. Up to 15 seconds, it was hard to find almost any change in the flame retardant coating layer, but only the granulation of the flame retardant coating layer was found. After a certain time, a flame hole was formed in the fabric on which the flame resistant coating layer was formed, and the size of the flame hole slowly increased. There was little gas production while the flame openings were large. In particular, with reference to FIG. 12, a jaw formed around the flame hole protrudes into the lower surface of the fabric and the flame resistant coating layer is still present at the jaw so that the flame passing through the flame hole has a lower surface of the fabric, i.e., the surface without the flame resistant coating layer. You can see that it is blocking the spread.

이제, 4 내지 도 10을 참조하여, 전술한 보호 쿠션을 제조하는 방법에 대해 보다 구체적으로 설명한다.Now, with reference to 4-10, the method of manufacturing the above-mentioned protective cushion is demonstrated in more detail.

먼저, 보호 쿠션 제작을 위한 재료들로서, 도 4에 도시된 것과 같은 내염성 인조피혁재(100), 쿠션재(300), 베이스 패널(400)이 준비된다. 필요한 경우, 불연시트(200)이 추가로 준비된다. 이와 같은 재료들 중 내염성 인조피혁재(100)은 도 5 내지 도 9에 도시된 방법에 의해 제작되어 준비된다 . First, as materials for fabricating a protective cushion, a flame resistant artificial leather 100, a cushioning material 300, and a base panel 400 as shown in FIG. 4 are prepared. If necessary, the non-combustible sheet 200 is further prepared. Among such materials, the flameproof artificial leather 100 is manufactured and prepared by the method illustrated in FIGS. 5 to 9.

먼저, 도 5를 참조하면, 직물(1)이 준비된다. 직물(1)은 난연사(flame retardant fibers) 또는 일반 (합성 또는 천연) 섬유 실을 횡사(11) 및 경사(12)로 하여 평직하거나 또는 니팅(knitting)하여 만들어질 수 있다. 난연사를 이용하는 경우, 상기 난연사는 폴리에스테르 계열의 난연사인 것이 바람직하다. 하지만, 상기 난연사로 난연성 폴리에스테르, 모다크릴릭(modacrylic), 면, 레이온, PP, 나일론 중 하나 또는 이들 중 2개 이상을 브렌딩하여 만든 것을 이용할 수 있다.First, referring to FIG. 5, a fabric 1 is prepared. The fabric 1 can be made by plain weaving or knitting with flame retardant fibers or plain (synthetic or natural) fibrous yarns as cross threads 11 and warp 12. When using a flame retardant yarn, the flame retardant yarn is preferably a polyester-based flame retardant yarn. However, as the flame retardant yarn, one made of flame retardant polyester, modacrylic, cotton, rayon, PP, nylon or two or more thereof may be used.

다음, 도 6을 참조하면, 직물(1)의 상면에만 국한하여 방염 코팅층(2)을 형성한다. 상기 방염 코팅층(2)은 나이프 코팅, 로울러 코팅, 스프레이 코팅, 캘린더 코팅, 전사 코팅 또는 스크린 날염과 같은 코팅 기술을 이용하여 상기 직물(1)의 유연성을 저하시키지 않는 두께로 상기 직물(1)의 상면에만 제한적으로 형성된다. 상기 방염 코팅층(2)은 상기 직물(1) 두께의 1/10 ~ 1/1000 의 두께로 형성되는 것이 좋다. 상기 방염 코팅층(2)을 형성하기 위한 방염 재료로는, 예컨대 ADPP(anilinodiphenyl phosphate), RDPP (resorcinol -bis[diphenol phosphate)와 같은 인계 난연재 또는 탄소계 화합물을 포함하는 재료가 이용될 수 있다. 탄소 화합물을 포함하는 방염 재료는 탄소계 화합물, 촉매 및 불연성 기체 원료를 포함할 수 있다. 이 경우, 탄소계 화합물로는 카제인 또는 전분과 같은 탄수화물, 단백질 또는 다가 알콜을 포함할 수 있다. 촉매로는 무기 산 또는 무기 산의 분해 형태인 화합물을 포함할 수 있다. 또한 상기 방염 재료에 삼수화물, 규산염, 카올린, 석고 및 수화점토와 같은 방염용 필러를 추가할 수 있다.Next, referring to Figure 6, to form only the top surface of the fabric (1) to form a flame retardant coating layer (2). The flame retardant coating layer 2 is formed of a coating material such as knife coating, roller coating, spray coating, calender coating, transfer coating or screen printing to a thickness that does not reduce the flexibility of the fabric 1. Limited to the upper surface is formed. The flame retardant coating layer 2 is preferably formed to a thickness of 1/10 ~ 1/1000 of the thickness of the fabric (1). As the flame retardant material for forming the flame retardant coating layer 2, for example, a material containing a phosphorus-based flame retardant such as anilinodiphenyl phosphate (ADPP) or RDPP (resorcinol-bis [diphenol phosphate) or a carbon-based compound may be used. The flame retardant material comprising a carbon compound may include a carbonaceous compound, a catalyst and a nonflammable gaseous raw material. In this case, the carbon-based compound may include carbohydrates such as casein or starch, protein or polyhydric alcohol. The catalyst may include an inorganic acid or a compound in the form of decomposition of the inorganic acid. In addition, flame retardant fillers such as trihydrate, silicate, kaolin, gypsum and hydrated clay may be added to the flame retardant material.

다음, 도 7을 참조하면, 상기 방염 코팅층(2) 상에 난연성 본딩층(3)을 도포하여 형성한다. 난연성 본딩층(3)은 접착성분을 갖는 합성수지 재료로 이루어지며, 까칠 까칠한 방염 코팅층(2)을 덮어 아래로 가림과 동시에 표피(4) 코팅을 위한 최적의 표면을 제공한다. 난연성 본딩층(3)은 폴리우레탄 계열 또는 그와 유사한 합성수지 계열 재료로 이루어진다. 이때, 난연성 본딩층(3)은 표피(4)의 접착 성능 향상을 위해 부가적으로 제공되는 것이 좋지만, 방염 코팅층(2)이 충분한 접착 특성을 갖는 경우 생략하는 것도 고려될 수 있다.Next, referring to FIG. 7, the flame retardant bonding layer 3 is formed on the flame retardant coating layer 2. The flame retardant bonding layer 3 is made of a synthetic resin material having an adhesive component and covers the rough and rough flameproof coating layer 2 to cover it down and at the same time provide an optimal surface for coating the epidermis 4. The flame retardant bonding layer 3 is made of polyurethane-based or similar synthetic resin-based material. In this case, the flame retardant bonding layer 3 may be additionally provided to improve the adhesion performance of the skin 4, but may be considered to be omitted if the flame retardant coating layer 2 has sufficient adhesive properties.

다음, 도 8을 참조하면, 상기 방염 코팅층(2)를 덮도록 상기 방염 코팅층(2) 상에 있는 난연성 본딩층(3) 상에 난연성 폴리우레탄 재료를 코팅하여 표피(4)를 형성한다. 난연성 본딩층(3)이 생략된 경우, 방염 코팅층(2) 상에 직접 표피(4)를 형성하여 방염 코팅층(2)을 덮을 수도 있다. Next, referring to FIG. 8, a flame retardant polyurethane material is coated on the flame retardant bonding layer 3 on the flame retardant coating layer 2 to cover the flame retardant coating layer 2 to form the skin 4. When the flame retardant bonding layer 3 is omitted, the flame retardant coating layer 2 may be formed by directly forming the skin 4 on the flame retardant coating layer 2.

난연성 폴리우레탄 재료는 폴리카보네이트디올과 폴리테트라메틸렌에테르글리콜이 중량비 1:1 ~ 2:1로 혼합된 폴리올 혼합물을 교반하여 약 60~80℃로 유지시킨 다음, 폴리올 혼합물에 메틸렌디페닐디이소시아네이트를 첨가하여 반응시킨 후 수세하여 고형의 프리폴리머를 얻고, 상기 프리폴리머에 디메틸포름아미드를 가하여 용해시키고 1,4-부탄디올과 인산 에스테르 디올의 혼합물을 사슬연장제로 투입하여 60 내지 80℃에서 일정시간 반응시켜 합성한 것이 이용될 수 있다. 대안적으로, 폴리우레탄 배합액의 배합시, 트리아릴포스페이트 등의 인계 난연제 또는 할로겐계 난연제를 일정량 첨가하여 만들어진 난연성 폴리우레탄 재료가 이용될 수도 있다. The flame-retardant polyurethane material is a polyol mixture containing polycarbonate diol and polytetramethylene ether glycol in a weight ratio of 1: 1 to 2: 1 by stirring to maintain a temperature of about 60 ~ 80 ℃, and then to the polyol mixture methylene diphenyl diisocyanate After reaction by addition, washing with water to obtain a solid prepolymer, dimethylformamide was added to the prepolymer to dissolve it, and a mixture of 1,4-butanediol and phosphate ester diol was added as a chain extender to react at a constant time at 60 to 80 ° C for synthesis. One can be used. Alternatively, a flame-retardant polyurethane material made by adding a certain amount of a phosphorus-based flame retardant such as triaryl phosphate or a halogen-based flame retardant may be used in the formulation of the polyurethane compound.

다음 도 9를 참조하면, 상기 표피(4)의 상부 표면에 일정 패턴의 무늬를 형성한다. 난연성 폴리우레탄 코팅에 의해 형성된 표피(4)에 무늬 성형 필름(M)의 무늬를 전사함으로써 일정 패턴의 무늬를 상기 표피(4)의 표면에 형성할 수 있다.Next, referring to FIG. 9, a pattern of a predetermined pattern is formed on the upper surface of the epidermis 4. A pattern of a certain pattern can be formed on the surface of the epidermis 4 by transferring the pattern of the pattern forming film M to the epidermis 4 formed by the flame-retardant polyurethane coating.

도 10을 통해 전술한 보호 쿠션의 재료(100, 200, 300, 400)들이 적층 구조로 결합되는 과정을 볼 수 있다. 도 10을 참조하면, 특정 형상의 오목부를 갖는 삽입틀(F) 및 그와 대향되게 배치된 가압유닛(P)을 포함하는 보호 쿠션 포장기기가 준비된다. 삽입틀(F)의 오목부에 먼저 인조피혁재(100) 및/또는 불연시트(200)를 포함하는 쿠션 포장재료를 깔되 그 포장재료의 가장자리 부분은 상기 오목부 밖으로 나오도록 해준다. 그리고, 포장재료가 깔린 오목부에 베이스 패널(400)이 부착되어 있는 쿠션재(300)을 거꾸로 삽입한다. 그리고, 가압유닛(P)은 구동 실린더(D)를 하강 작동시켜 그와 연결되어 가압판(C)으로 베이스 패널(400)의 이면을 강하게 눌러 상기 쿠션재(300)를 상기 오목부에 대응되는 형상으로 탄성 압축 변형시킨다. 이 상태에서, 상기 오목부 밖으로 나와 있는 포장재료, 즉, 인조피혁재(100) 및/또는 불연시트(200)의 가장자리를 베이스 패널(400)의 이면에 접하도록 한 후, 스테이플 등과 같은 고정부재를 타정하여, 상기 쿠션재(300)를 포장한다. 이때, 삽입틀(F)과 상기 가압판(C)을 회전시키면서 포장 작업을 수행함으로써 보다 더 작업성을 향상시킬 수 있다.Referring to FIG. 10, a process of combining the materials 100, 200, 300, and 400 of the above-described protective cushion in a laminated structure can be seen. Referring to FIG. 10, a protective cushion packaging machine including an insertion frame F having a recess of a specific shape and a pressing unit P disposed opposite thereto is prepared. The recessed portion of the insert frame F is first laid with a cushioning packaging material comprising the artificial leather 100 and / or non-combustible sheet 200, with the edge of the packaging material coming out of the recess. Then, the cushioning material 300, to which the base panel 400 is attached, is inserted upside down in the recess in which the packaging material is laid. Then, the pressure unit (P) is operated by lowering the driving cylinder (D) is connected to it and by pressing the back surface of the base panel 400 with a pressure plate (C) to the shape corresponding to the recessed portion Elastic compressive deformation. In this state, the packaging material that comes out of the recess, that is, the edges of the artificial leather 100 and / or non-combustible sheet 200 is in contact with the back surface of the base panel 400, and then a fixing member such as a staple Tableting, the cushioning material 300 is packed. At this time, the workability can be further improved by performing the packaging operation while rotating the insertion frame (F) and the pressure plate (C).

위에서는 일정 두께의 일자형 단면을 갖는 직사각형 또는 정사각형의 베이스 패널을 기본으로 하는 보호 쿠션에 대해 설명되었는 바, 이러한 보호 쿠션은 내벽 모서리로부터 이격된 내벽면 또는 바닥면에 유용하다. 그러나, 본 발명은 이에 제한되지 않고, 다양한 단면을 갖는 베이스 패널을 기본으로 하여 제작된 보호 쿠션을 포함할 수 있는 바, 내벽면의 모서리 코너에 적합한 보호 쿠션으로서, "ㄴ" 단면의 베이스 패널을 기본으로 하여 제작되어 대략 "ㄴ"형 단면의 보호 쿠션이 있을 수 있다.Above, a protective cushion based on a rectangular or square base panel having a flat cross section of a certain thickness has been described, which is useful for inner walls or floors spaced from inner wall edges. However, the present invention is not limited thereto, and may include a protective cushion fabricated based on a base panel having various cross sections, and a base cushion having a “b” cross section as a protective cushion suitable for a corner corner of an inner wall surface. There may be a protective cushion of roughly " b " shaped cross-section, fabricated as a basis.

1: 직물 2: 방염 코팅층
3: 난연성 본딩층 4: 표피
100: 인조피혁재 200: 불연시트
300: 쿠션재 400: 베이스 패널 1: fabric 2: flame retardant coating layer
3: flame retardant bonding layer 4: skin
100: artificial leather 200: non-combustible sheet
300: cushioning material 400: base panel

Claims (5)

삭제delete 삭제delete 삭제delete 베이스 패널(400);
상기 베이스 패널 상에 배치되는 쿠션재(300); 및
상기 쿠션재(300)를 감싼 채 상기 베이스 패널에 고정되는 인조피혁재(100)를 포함하며,
상기 인조피혁재(100)는, 직물(1)과, 상기 직물(1)의 상측에 형성된 표피(4)와, 상기 직물(1)의 상면에만 국한하여 형성되어 상기 직물(1)과 상기 표피(4) 사이에 위치하는 방염 코팅층(3)을 포함하며,
상기 인조피혁재(100)와 상기 쿠션재(300) 사이에 개재된 불연시트(200)를 더 포함하며, 상기 불연시트(200)는 유리섬유 시트, 탄소섬유 시트 또는 실리카 시트 중 적어도 하나를 포함하고, 상기 표피(4)는 난연성 폴리우레탄을 포함하고, 상기 방염 코팅층(2)은 상기 직물(1) 두께의 1/10 ~ 1/1000 의 두께로 형성되고, 상기 방염 코팅층(2)은 인계 난연재와 탄소계 화합물을 포함하는 난연재중 적어도 하나를 포함하고, 상기 인계 난연재는 ADPP(anilinodiphenyl phosphate), RDPP (resorcinol -bis[diphenol phosphate)를 포함하며, 상기 탄소계 화합물을 포함하는 난연재는 탄소계 화합물, 촉매, 불연성 기체 원료 및 방염용 필러를 포함하고, 상기 탄소계 화합물은 탄수화물, 단백질 또는 다가 알콜을 포함하고, 상기 촉매는 무기 산을 포함하며, 상기 방염용 필러는 알루미나 삼수화물, 규산염, 카올린, 석고 및 수화점토 중 적어도 하나를 포함하는 것을 특징으로 하는 내염성 보호쿠션.A base panel 400;
A cushion material disposed on the base panel; And
Including the artificial leather 100 is fixed to the base panel while wrapping the cushion member 300,
The artificial leather 100, the fabric (1), the skin (4) formed on the upper side of the fabric (1), and formed only on the upper surface of the fabric (1), the fabric (1) and the skin (4) a flame retardant coating layer (3) located between,
It further comprises a non-flammable sheet 200 interposed between the artificial leather 100 and the cushion member 300, the non-combustible sheet 200 includes at least one of a glass fiber sheet, a carbon fiber sheet or a silica sheet , The skin (4) comprises a flame-retardant polyurethane, the flame retardant coating layer (2) is formed to a thickness of 1/10 ~ 1/1000 of the thickness of the fabric (1), the flame retardant coating layer (2) is a phosphorous flame retardant And a flame retardant comprising a carbon-based compound, wherein the phosphorus-based flame retardant includes ADPP (anilinodiphenyl phosphate) and RDPP (resorcinol-bis [diphenol phosphate), and the flame retardant including the carbon-based compound is a carbon-based compound. And a catalyst, a non-combustible gas raw material, and a flame retardant filler, wherein the carbonaceous compound includes a carbohydrate, a protein or a polyhydric alcohol, the catalyst includes an inorganic acid, and the flame retardant filler includes alumina trihydrate, silica Salt, kaolin, gypsum and salt tolerance protective cushion, characterized in that it comprises at least one of a hydrated clay. 삭제delete
KR1020130070282A 2013-06-19 2013-06-19 Flame resistance protective cushion and its fabricating method Expired - Fee Related KR101345839B1 (en)