KR102755616B1 - Rubberized Asphalt-Based Integrated Waterproof Sheet and Construction methods Using Thereof - Google Patents

Rubberized Asphalt-Based Integrated Waterproof Sheet and Construction methods Using Thereof Download PDF

Info

Publication number
KR102755616B1
KR102755616B1 KR1020240095389A KR20240095389A KR102755616B1 KR 102755616 B1 KR102755616 B1 KR 102755616B1 KR 1020240095389 A KR1020240095389 A KR 1020240095389A KR 20240095389 A KR20240095389 A KR 20240095389A KR 102755616 B1 KR102755616 B1 KR 102755616B1
Authority
KR
South Korea
Prior art keywords
weight
parts
asphalt
rubberized
rubberized asphalt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
KR1020240095389A
Other languages
Korean (ko)
Inventor
이평원
Original Assignee
(주)대한하이텍건설
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)대한하이텍건설 filed Critical (주)대한하이텍건설
Priority to KR1020240095389A priority Critical patent/KR102755616B1/en
Application granted granted Critical
Publication of KR102755616B1 publication Critical patent/KR102755616B1/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Provided in the present invention is a rubberized asphalt-based integrally attached waterproof sheet comprising: a plastic film substrate layer; and a rubberized asphalt layer laminated on one side of the plastic film substrate layer, wherein a rubberized asphalt mixture comprising, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene-isoprene styrene, 1 to 30 parts by weight of polybutene, 1 to 10 parts by weight of calcium carbonate, 1 to 10 parts by weight of a tackifier, 1 to 5 parts by weight of a compatibilizer, 0.1 to 2 parts by weight of a flow inhibitor, 0.1 to 2 parts by weight of an anti-stripping agent, and 0.1 to 2 parts by weight of an antioxidant is included. According to the present invention, the rubberized asphalt-based integrally attached waterproof sheet is constructed on a concrete structure such as a floor, a wall surface, and the like of a concrete structure, a crack generation unit, a joint unit, and the like to perform waterproof construction to prevent leakage and flooding.

Description

고무화 아스팔트계 일체부착형 방수시트 및 이를 이용한 시공방법{Rubberized Asphalt-Based Integrated Waterproof Sheet and Construction methods Using Thereof}{Rubberized Asphalt-Based Integrated Waterproof Sheet and Construction Methods Using Thereof}

본 발명은 고무화 아스팔트계 일체부착형 방수시트 및 이를 이용한 시공방법에 관한 것으로서, 보다 상세하게는 콘크리트 구조물의 바닥, 벽면 등과 콘크리트 크랙 발생부 또는 조인트부 등의 콘크리트 구조체에 시공하여 누수 및 침수가 발생되지 않도록 방수 시공할 수 있도록 하는 고무화 아스팔트계 일체부착형 방수시트 및 이를 이용한 시공방법에 관한 것이다.The present invention relates to a rubberized asphalt-based integrally bonded waterproofing sheet and a construction method using the same, and more specifically, to a rubberized asphalt-based integrally bonded waterproofing sheet which can be constructed to waterproof concrete structures such as floors, walls, cracked areas or joints of concrete structures to prevent leakage and flooding, and a construction method using the same.

일반적으로, 실내, 옥상, 지붕, 지하실 등 각종 구조물 바닥, 교량, 도로 등의 노면 바닥, 각종 유체 저장탱크 등의 콘크리트 구조물에는 빗물 등이 스며들었을 경우, 일부가 내부로 침투하여 구조물의 내구성에 악영향을 주게 되므로 각종 방수재료를 사용하여 방수 시공하고 있다.In general, when rainwater, etc. seeps into concrete structures such as indoor, rooftop, rooftop, basement, etc. floors of various structures, road surfaces such as bridges and roads, and various fluid storage tanks, some of it seeps inside and adversely affects the durability of the structure, so various waterproofing materials are used for waterproofing construction.

상기한 방수 시공공법으로는 아스팔트, 콜타르피치, 우레탄, 에폭시 등 도막방수재를 도포하여 방수코팅층을 형성하는 방법, 아스팔트나 콜타르피치를 함침한 종이, 펠트, 천 등 방수시트로 시공면을 덮고, 그 위에 모르타르, 레미콘 등을 타설하는 방법 등이 있다.The above-mentioned waterproofing construction methods include a method of forming a waterproof coating layer by applying a waterproofing material such as asphalt, coal tar pitch, urethane, or epoxy; a method of covering the construction surface with a waterproofing sheet such as paper, felt, or cloth impregnated with asphalt or coal tar pitch, and then pouring mortar, ready-mixed concrete, etc. on top of it; etc.

상기와 같은 종래 방수공법으로서, 한국등록특허 10-0977160에는 바탕기재에 프라이머를 도포하는 단계와, 상기 바탕기재의 코너부에 부틸합성고무 밴드를 시공하는 단계와, 상기 프라이머에 무용제형 폴리우레탄 매스틱 방수재를 도포하는 단계와, 상기 방수재의 상부에 보호층을 시공하는 단계를 포함하여 이루어지며, 상기 무용제형 폴리우레탄 매스틱 방수재는 제1액과 제2액으로 이루어지며, 상기 제1액은 우레탄 경화제 15∼40중량%, 연화제 10∼40중량%, 무기질 필러 20∼70중량%, 점착부여제 2∼20중량%, 반응 촉매 0.1∼5중량%, 안료 1∼10중량% 및 기타 첨가제 0.1∼5중량%를 포함하여 이루어지고, 상기 제2액은 분자쇄에 2개 이상의 이소시아네이트 반응기를 가지는 우레탄 프리폴리머 또는 단량체로 이루어지며, 상기 부틸합성고무 밴드는 부틸합성고무 매스틱 조성물을 단면이 이등변 삼각형으로 되는 바형상의 부틸합성고무 밴드로 성형하되, 상기 이등변 삼각형은 등변의 길이가 2∼7cm이고, 꼭지각의 크기가 80∼150°이며, 상기 부틸합성고무 밴드의 하나 이상의 측면에는 이형층이 구비되고, 상기 부틸합성고무 매스틱 조성물은 부틸고무 10∼30중량%, 연화제 3∼20중량%, 무기질 필러 20∼70중량%, 점착부여제 8∼25중량%, 개질재 4∼15중량% 및 점도 조정제 4.8∼25중량%로 이루어지는 것을 특징으로 하는 무용제형 폴리우레탄 매스틱 방수재를 이용한 방수공법이 공지되어 있다.As a conventional waterproofing method as described above, Korean Patent No. 10-0977160 includes a step of applying a primer to a base substrate, a step of constructing a butyl synthetic rubber band to a corner of the base substrate, a step of applying a solvent-free polyurethane mastic waterproofing material to the primer, and a step of constructing a protective layer on top of the waterproofing material, wherein the solvent-free polyurethane mastic waterproofing material is composed of a first liquid and a second liquid, wherein the first liquid includes 15 to 40 wt% of a urethane hardener, 10 to 40 wt% of a softener, 20 to 70 wt% of an inorganic filler, 2 to 20 wt% of an adhesive, 0.1 to 5 wt% of a reaction catalyst, 1 to 10 wt% of a pigment, and 0.1 to 5 wt% of other additives, and the second liquid includes a urethane prepolymer or monomer having two or more isocyanate reactive groups in a molecular chain, and the A butyl synthetic rubber band is formed by forming a butyl synthetic rubber mastic composition into a bar-shaped butyl synthetic rubber band whose cross-section is an isosceles triangle, wherein the isosceles triangle has an equilateral length of 2 to 7 cm and a vertex angle of 80 to 150°, at least one side of the butyl synthetic rubber band has a release layer, and the butyl synthetic rubber mastic composition comprises 10 to 30 wt% of butyl rubber, 3 to 20 wt% of a softener, 20 to 70 wt% of an inorganic filler, 8 to 25 wt% of a tackifier, 4 to 15 wt% of a modifier, and 4.8 to 25 wt% of a viscosity modifier. A waterproofing method using a solvent-free polyurethane mastic waterproofing material is known.

또한, 한국등록특허 10-1573298에는 기초부재 표면에 프라이머를 도포하는 단계; 상기 프라이머 상부에 바탕조정제로서 폴리우레아를 도포하는 단계; 및 상기 바탕조정제 상부에 방수용으로서 폴리우레아를 코팅하는 단계;를 포함하고, 상기 바탕조정제는 폴리이소시아네이트를 함유하는 A액 및 폴리올, 폴리아민 및 폴리아스파틱 에스터를 함유하는 B액으로 이루어지며, 상기 A액은 NCO%가 8 내지 20중량%이고, 상기 B액은 폴리올이 5 내지 20중량%이고, 폴리아민이 20 내지 40중량%이고, 폴리아스파틱에스터(polyaspartic ester)가 20 내지 40 중량% 이며, 상기 A액과 B액의 부피비는 1:1이고, 상기 B액에는 실리콘계 소포제, 1.3-BG, 1.4-BD, 프로필렌 카보네이트(Propylene carbonate)가 첨가물로서 포함되는 것을 특징으로 하는 바탕조정제로 폴리우레아를 이용하는 방수공법이 개발된 바 있다.In addition, Korean Patent No. 10-1573298 discloses a step of applying a primer to the surface of a base member; a step of applying polyurea as a base conditioner on top of the primer; And a step of coating polyurea as a waterproofing agent on the upper part of the base conditioner; wherein the base conditioner is composed of Solution A containing polyisocyanate and Solution B containing polyol, polyamine, and polyaspartic ester, wherein Solution A has an NCO% of 8 to 20 wt%, Solution B has a polyol of 5 to 20 wt%, a polyamine of 20 to 40 wt%, and a polyaspartic ester of 20 to 40 wt%, and a volume ratio of Solutions A and B is 1:1, and Solution B contains a silicone-based defoaming agent, 1.3-BG, 1.4-BD, and propylene carbonate as additives. A waterproofing method using polyurea as a base conditioner has been developed.

또한, 한국등록특허 10-1469840에는 MMA수지를 포함하는 프라이머를 교면 바닥면에 도포하여 프라이머층을 형성하는 단계(S10); 상기 프라이머층 상부에 MMA수지를 포함하는 방수재를 도포하여 방수층을 형성하는 단계(S20); 상기 방수층의 상부로 택코팅을 실시하는 단계(S30);를 포함하는 교면 포장 방수공법에 있어서, 상기 S20 단계에서, 상기 방수재는 MMA수지와 골재를 포함하되, 상기 MMA수지는 MMA, PMMA, 우레탄(UR), 불포화 폴리에스테르(UP), 에폭시 아크릴레이트를 배합하여 고분자 물질화 된 수지이며, 상기 골재는 규사, 탄산칼슘, 자연사를 포함하는 것을 특징으로 하고, 상기 방수재는, MMA수지 100중량부에 대해 골재 100 내지 400중량부, 상기 골재보다 입경이 작은 충진분말 100 내지 300중량부, 경화제 2 내지 5중량부를 포함하면서, 증점제로는 메틸셀롤로오즈(MC)에 수용성 고분자를 도입한 것으로 타 조성들과 혼합 시 즉각적인 증점효과가 나타나지 않고 수용성 고분자가 용해된 이후에 메틸셀롤로오즈(MC)가 증점효과를 나타내도록 하는 히드록실프로필메틸셀룰로오즈계 점성분말 1 내지 3중량부와, 표면장력을 저하시킴으로써 미세균열로의 충진을 확보할 수 있도록 소디움 라우릴 설페이트 0.5 내지 1중량부가 더 배합되는 것을 특징으로 하는 교면 포장 방수공법이 공지된 바 있다.In addition, Korean Patent No. 10-1469840 includes a step (S10) of forming a primer layer by applying a primer containing an MMA resin to the bottom surface of a bridge; a step (S20) of forming a waterproof layer by applying a waterproofing material containing an MMA resin on top of the primer layer; In a waterproofing method for a bridge pavement, comprising a step (S30) of performing a tack coating on the upper part of the waterproofing layer; In the step S20, the waterproofing material comprises an MMA resin and an aggregate, wherein the MMA resin is a polymerized resin by mixing MMA, PMMA, urethane (UR), unsaturated polyester (UP), and epoxy acrylate, and the aggregate comprises silica, calcium carbonate, and natural sand, and the waterproofing material comprises 100 to 400 parts by weight of aggregate, 100 to 300 parts by weight of filler powder having a particle size smaller than that of the aggregate, and 2 to 5 parts by weight of a hardener, with respect to 100 parts by weight of the MMA resin, and a water-soluble polymer is introduced into methyl cellulose (MC) as a thickener, so that an immediate thickening effect does not appear when mixed with other compositions, and the methyl cellulose (MC) exhibits a thickening effect after the water-soluble polymer is dissolved. A waterproofing method for a bridge pavement is known, characterized in that 1 to 3 parts by weight of a hydroxylpropyl methyl cellulose-based viscous powder is further mixed with 0.5 to 1 part by weight of sodium lauryl sulfate to ensure filling of microcracks by lowering surface tension.

그러나 상기와 같은 도막방수재를 사용하여 방수코팅층을 시공하는 경우에는 시공도 쉽고 가격도 저렴하지만, 구조물에 균열이 발생하면 방수코팅층이 파괴되어 균열이 발생한 부분은 방수효과를 상실한다는 문제점이 있고, 도막방수재를 사용하여 도막을 형성할 경우에는 균일한 도막형성 또는 매끈한 도막을 형성하는데 어려움이 있을 뿐만 아니라 일정시간의 경화시간을 필요로 한다는 점에서 단점이 있고, 특히, 크랙발생부 또는 콘크리트 구조체를 연결하는 조인트부가 형성된 방수구조체의 경우에는 상기 크랙발생부 및/또는 조인트부에 의한 팽창 또는 균열에 의해 도막방수재에도 균열이 발생한다는 심각한 문제점이 있다.However, when constructing a waterproofing coating layer using the above-mentioned waterproofing film, although the construction is easy and the price is low, there is a problem that if a crack occurs in the structure, the waterproofing coating layer is destroyed and the cracked area loses the waterproofing effect, and when forming a coating using a waterproofing film, not only is it difficult to form a uniform or smooth coating film, but there is also a disadvantage in that a certain amount of curing time is required, and in particular, in the case of a waterproofing structure in which a crack-generating portion or a joint connecting a concrete structure is formed, there is a serious problem that cracks also occur in the waterproofing film due to expansion or cracking caused by the crack-generating portion and/or the joint.

한편, 상기 도막방수재의 문제점과 단점을 해소하기 위하여 방수시트를 이용한 공법으로서 한국공개특허 10-2010-0046369에는 골조바닥(10)에 소정의 폭(W)과 길이(L)를 가지는 아스팔트 방수시트(S)를 1개의 단위로 하여 독립적으로 시공하는 공법으로서, 상기 골조바닥(10) 전면에 아스팔트 프라이머을 도포하여 아스팔트 프라이머층(11)을 형성하는 프라이머층 형성단계(S1); 상기 아스팔트 프라이머층(11)의 상부에 고온으로 녹인 아스팔트를 길게 도포하여 제1아스팔트층(12)을 형성하는 제1아스팔트층 형성단계(S2); 상기 제1아스팔트층(12) 상에 아스팔트 방수시트(S)와 다른 아스팔트 방수시트(S')를 이격된 상태로 배치하여 압착시키는 아스팔트 방수시트 배치단계(S3); 상기 아스팔트 방수시트(S)와 다른 아스팔트 방수시트(S')의 가장자리 상부 및 이격된 부분으로 돌출되는 제1아스팔트층(12)의 상부를 덮도록 고온으로 녹인 아스팔트를 도포하여 제2아스팔트층(13)을 형성하는 제2아스팔트층 형성단계(S4); 및 상기 제2아스팔트층(13)의 상부면에 비닐(14)을 부착하는 비닐 부착단계(S5);를 포함하는 아스팔트 방수시트를 이용한 방수공법이 공지되어 있다.Meanwhile, in order to resolve the problems and shortcomings of the above-mentioned waterproofing film, a method using a waterproofing sheet is disclosed in Korean Patent Publication No. 10-2010-0046369, which comprises a method of independently constructing an asphalt waterproofing sheet (S) having a predetermined width (W) and length (L) as a single unit on a frame floor (10), comprising: a primer layer forming step (S1) of applying an asphalt primer to the entire frame floor (10) to form an asphalt primer layer (11); a first asphalt layer forming step (S2) of applying a long layer of asphalt melted at a high temperature on top of the asphalt primer layer (11) to form a first asphalt layer (12); an asphalt waterproofing sheet arranging step (S3) of arranging an asphalt waterproofing sheet (S) and another asphalt waterproofing sheet (S') on the first asphalt layer (12) in a spaced state and pressing them together; A waterproofing method using an asphalt waterproofing sheet is known, which includes a second asphalt layer forming step (S4) of forming a second asphalt layer (13) by applying high-temperature melted asphalt so as to cover the upper portion of a first asphalt layer (12) protruding from the upper edge and the spaced portion of another asphalt waterproofing sheet (S') than the above asphalt waterproofing sheet (S); and a vinyl attachment step (S5) of attaching vinyl (14) to the upper surface of the second asphalt layer (13).

그러나 상기와 같이 방수시트를 사용하여 방수시공하는 경우에는 상기 방수시트가 겹치는 부위에서 누수현상이 발생할 수 있고, 방수시트의 인장 변화에 따라 방수시트의 균열 또는 틈새가 발생하여 역시 누수현상이 발생할 수 있을 뿐만 아니라 누수현상이 발생할 경우 결함 부분의 발견과 보수가 어렵다는 문제점이 있다.However, in the case of waterproofing construction using a waterproof sheet as described above, there is a problem that leakage may occur in the area where the waterproof sheets overlap, and cracks or gaps in the waterproof sheet may occur depending on changes in the tensile strength of the waterproof sheet, which may also cause leakage. In addition, if leakage occurs, it is difficult to find and repair the defective area.

더욱이, 상기 방수시트를 사용하여 방수시공하는 경우에도 크랙발생부, 단면보수부 또는 콘크리트 구조체를 연결하는 조인트부가 형성된 구조물은 크랙발생부, 단면보수부 또는 조인트부에 의하여 크랙이 발생하는 경우, 상기 방수시트에도 크랙이 발생함으로써 방수성능이 저하되고, 또한, 별도의 도막방수재와 결합하여 2중 구조를 형성해야 한다는 시공의 복잡성이 있고, 일정시간의 경화시간을 필요로 한다는 점에서 단점이 있다.Furthermore, even when waterproofing is performed using the above waterproofing sheet, structures having crack-generating portions, cross-sectional repair portions, or joint portions connecting concrete structures have cracks in the crack-generating portions, cross-sectional repair portions, or joint portions, and thus cracks also occur in the waterproofing sheet, thereby reducing the waterproofing performance. In addition, there is the complexity of construction in that a double structure must be formed by combining with a separate waterproofing film, and there is a disadvantage in that a certain amount of curing time is required.

특허문헌 1. 국내등록특허 제10-0977160호Patent Document 1. Domestic Registration Patent No. 10-0977160 특허문헌 2. 국내등록특허 제10-1573298호Patent Document 2. Domestic Registration Patent No. 10-1573298 특허문헌 3. 국내등록특허 제10-1469840호Patent Document 3. Domestic Registration Patent No. 10-1469840

본 발명은 전술한 문제점을 극복하기 위해 창출된 것으로서, 콘크리트 크랙 발생부 또는 조인트부 등의 콘크리트 구조체 뿐만 아니라, 콘크리트 구조물의 바닥, 벽면 등에도 시공하여 누수 및 침수가 발생되지 않도록 방수시공 할 수 있는 고무화 아스팔트계 일체부착형 방수시트 및 이를 이용한 시공방법을 제공하고자 한다.The present invention has been created to overcome the aforementioned problems, and provides a rubberized asphalt-based integrally bonded waterproofing sheet that can be constructed to waterproof not only concrete structures such as concrete crack occurrence areas or joint areas, but also floors, walls, etc. of concrete structures to prevent leakage and flooding, and a construction method using the same.

본 발명은The present invention

플라스틱 필름 기재층; 및Plastic film substrate layer; and

상기 플라스틱 필름 기재층의 일측면에 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 30중량부, 폴리부텐 1 내지 30중량부, 탄산칼슘 1 내지 10중량부, 점착부여제 1 내지 10중량부, 상용화제 1 내지 5중량부, 흐름방지제 0.1 내지 2중량부 박리방지제 0.1 내지 2중량부, 및 산화방지제 0.1 내지 2중량부를 포함하는 고무화 아스팔트 혼합물을 적층한 고무화 아스팔트층을 포함하는 고무화 아스팔트계 일체부착형 방수시트를 제공한다.The present invention provides a rubberized asphalt-based integrally bonded waterproofing sheet including a rubberized asphalt layer laminated on one side of the plastic film substrate layer, the rubberized asphalt mixture including, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene isoprene styrene, 1 to 30 parts by weight of polybutene, 1 to 10 parts by weight of calcium carbonate, 1 to 10 parts by weight of a tackifier, 1 to 5 parts by weight of a compatibilizer, 0.1 to 2 parts by weight of an anti-flow agent, 0.1 to 2 parts by weight of an anti-stripping agent, and 0.1 to 2 parts by weight of an antioxidant.

또한, 본 발명은In addition, the present invention

시공할 대상면을 정리하는 정리단계;The preparation stage of organizing the surface to be constructed;

상기 정리단계가 종료된 시공면에 프라이머를 도포하는 프라이머 도포단계;Primer application step of applying a primer to the construction surface where the above organizing step has been completed;

상기 프라이머 도포단계가 종료된 시공면에 플라스틱 필름 기재층 및 상기 플라스틱 필름 기재층의 일측면에 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 30중량부, 폴리부텐 1 내지 30중량부, 탄산칼슘 1 내지 10중량부, 점착부여제 1 내지 10중량부, 상용화제 1 내지 5중량부, 흐름방지제 0.1 내지 2중량부 박리방지제 0.1 내지 2중량부, 및 산화방지제 0.1 내지 2중량부를 포함하는 고무화 아스팔트 혼합물을 적층한 고무화 아스팔트층을 포함하는 고무화 아스팔트계 일체부착형 방수시트를 부착하는 방수시트 부착단계: 및A waterproofing sheet attachment step for attaching a rubberized asphalt-based integrally bonded waterproofing sheet including a rubberized asphalt layer laminated with a rubberized asphalt mixture containing, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene isoprene styrene, 1 to 30 parts by weight of polybutene, 1 to 10 parts by weight of calcium carbonate, 1 to 10 parts by weight of a tackifier, 1 to 5 parts by weight of a compatibilizer, 0.1 to 2 parts by weight of a flow inhibitor, 0.1 to 2 parts by weight of an anti-stripping agent, and 0.1 to 2 parts by weight of an antioxidant, on a construction surface where the primer application step is completed, and

상기 방수시트 부착단계가 종료된 고무화 아스팔트계 일체부착형 방수시트 상면에 보호재를 부착하는 보호재 부착단계를 포함하는 고무화 아스팔트계 일체부착형 방수시트 시공방법을 제공한다.A method for constructing a rubberized asphalt-based integrally bonded waterproofing sheet is provided, which includes a protective material attachment step of attaching a protective material to the upper surface of a rubberized asphalt-based integrally bonded waterproofing sheet after the above waterproofing sheet attachment step has been completed.

본 발명에 따른 고무화 아스팔트계 일체부착형 방수시트는 콘크리트 구조물의 바닥, 벽면 등과 크랙 발생부 또는 조인트부 등의 콘크리트 구조체에 시공하여 누수 및 침수가 발생되지 않도록 방수시공 할 수 있는 효과가 있다.The rubberized asphalt-based integrally bonded waterproofing sheet according to the present invention can be constructed on concrete structures such as floors, walls, cracked areas, or joint areas to prevent leakage and flooding, thereby providing waterproofing.

도 1은 본 발명의 시공 과정으로, 정리단계가 종료된 시공면에 프라이머가 도포된 사진,
도 2는 프라이머 도포 후 본 발명에 따른 고무화 아스팔트계 일체부착형 방수시트가 부착된 사진,
도 3은 본 발명에 따른 고무화 아스팔트계 일체부착형 방수시트의 표면에 보호재가 부착된 사진. Figure 1 is a photograph showing the construction process of the present invention, in which a primer is applied to a construction surface after the cleaning step is completed.
Figure 2 is a photograph showing a rubberized asphalt-based integrally bonded waterproofing sheet according to the present invention attached after primer application.
Figure 3 is a photograph showing a protective material attached to the surface of a rubberized asphalt-based integrally bonded waterproofing sheet according to the present invention.

이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.

한 가지 관점에서, 본 발명은 플라스틱 필름 기재층; 및 상기 플라스틱 필름 기재층의 일측면에 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 30중량부, 폴리부텐 1 내지 30중량부, 탄산칼슘 1 내지 10중량부, 점착부여제 1 내지 10중량부, 상용화제 1 내지 5중량부, 흐름방지제 0.1 내지 2중량부 박리방지제 0.1 내지 2중량부, 및 산화방지제 0.1 내지 2중량부를 포함하는 고무화 아스팔트 혼합물을 적층한 고무화 아스팔트층을 포함하는 고무화 아스팔트계 일체부착형 방수시트를 제공한다.In one aspect, the present invention provides a rubberized asphalt-based integrally bonded waterproofing sheet comprising a plastic film substrate layer; and a rubberized asphalt layer laminated on one side of the plastic film substrate layer, the rubberized asphalt mixture comprising, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene isoprene styrene, 1 to 30 parts by weight of polybutene, 1 to 10 parts by weight of calcium carbonate, 1 to 10 parts by weight of a tackifier, 1 to 5 parts by weight of a compatibilizer, 0.1 to 2 parts by weight of an anti-flow agent, 0.1 to 2 parts by weight of an anti-stripping agent, and 0.1 to 2 parts by weight of an antioxidant.

다른 관점에서, 본 발명은 시공할 대상면을 정리하는 정리단계; 상기 정리단계가 종료된 시공면에 프라이머를 도포하는 프라이머 도포단계; 상기 프라이머 도포단계가 종료된 시공면에 플라스틱 필름 기재층 및 상기 플라스틱 필름 기재층의 일측면에 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 30중량부, 폴리부텐 1 내지 30중량부, 탄산칼슘 1 내지 10중량부, 점착부여제 1 내지 10중량부, 상용화제 1 내지 5중량부, 흐름방지제 0.1 내지 2중량부 박리방지제 0.1 내지 2중량부, 및 산화방지제 0.1 내지 2중량부를 포함하는 고무화 아스팔트 혼합물을 적층한 고무화 아스팔트층을 포함하는 고무화 아스팔트계 일체부착형 방수시트를 부착하는 방수시트 부착단계: 및 상기 방수시트 부착단계가 종료된 고무화 아스팔트계 일체부착형 방수시트 상면에 보호재를 부착하는 보호재 부착단계를 포함하는 고무화 아스팔트계 일체부착형 방수시트 시공방법을 제공한다.From another perspective, the present invention comprises: a cleaning step of cleaning a surface to be constructed; a primer application step of applying a primer to the construction surface after the cleaning step; The present invention relates to a rubberized asphalt-based integrally bonded waterproofing sheet, the waterproofing sheet attachment step comprising: attaching a rubberized asphalt layer comprising a plastic film substrate layer on a construction surface on which the primer application step has been completed; and a rubberized asphalt mixture comprising, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene isoprene styrene, 1 to 30 parts by weight of polybutene, 1 to 10 parts by weight of calcium carbonate, 1 to 10 parts by weight of an adhesive, 1 to 5 parts by weight of a compatibilizer, 0.1 to 2 parts by weight of an anti-flow agent, 0.1 to 2 parts by weight of an anti-stripping agent, and 0.1 to 2 parts by weight of an antioxidant, on one side of the plastic film substrate layer; and a method for constructing a rubberized asphalt-based integrally bonded waterproofing sheet, the method comprising: a waterproofing sheet attachment step of attaching a protective material to the upper surface of the rubberized asphalt-based integrally bonded waterproofing sheet on which the waterproofing sheet attachment step has been completed.

본 발명에 따른 방수시트, 특정적으로 고무화 아스팔트계 일체부착형 방수시트를 구성하는 플라스틱 필름 기재층은 당업계의 통상적인 플라스틱 필름으로 이루어진 것이라면 어떠한 것을 사용하여도 무방하지만, 추천하기로는 폴리에틸렌, 폴리프로필렌, 폴리에틸렌테레프탈레이트 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 포함하는 것이 좋다.The plastic film substrate layer constituting the waterproofing sheet according to the present invention, specifically the rubberized asphalt-based integrally bonded waterproofing sheet, may be any plastic film conventional in the art, but it is recommended to use one containing polyethylene, polypropylene, polyethylene terephthalate, or at least one mixture thereof.

본 발명에 따른 방수시트, 특정적으로 고무화 아스팔트계 일체부착형 방수시트를 구성하는 고무화 아스팔트층은 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 30중량부, 폴리부텐 1 내지 30중량부, 탄산칼슘 1 내지 10중량부, 점착부여제 1 내지 10중량부, 상용화제 1 내지 5중량부, 흐름방지제 0.1 내지 2중량부 박리방지제 0.1 내지 2중량부, 및 산화방지제 0.1 내지 2중량부를 포함한다.The rubberized asphalt layer constituting the waterproofing sheet according to the present invention, specifically the rubberized asphalt-based integrally bonded waterproofing sheet, contains, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene isoprene styrene, 1 to 30 parts by weight of polybutene, 1 to 10 parts by weight of calcium carbonate, 1 to 10 parts by weight of a tackifier, 1 to 5 parts by weight of a compatibilizer, 0.1 to 2 parts by weight of an anti-flow agent, 0.1 to 2 parts by weight of an anti-stripping agent, and 0.1 to 2 parts by weight of an antioxidant.

본 발명에 따른 고무화 아스팔트층을 구성하는 고무화 아스팔트 혼합물에 포함된 아스팔트는 당업계에서 통상적으로 사용되는 아스팔트라면 특별히 한정되지 않지만, 추천하기로는 석유계 아스팔트 또는 아스팔트 혼합물을 사용할 수 있다.The asphalt included in the rubberized asphalt mixture constituting the rubberized asphalt layer according to the present invention is not particularly limited as long as it is an asphalt commonly used in the art, but it is recommended to use petroleum-based asphalt or an asphalt mixture.

여기서, 상기 아스팔트 혼합물은 천연 아스팔트 혼합물을 사용하는 것을 추천한다.Here, it is recommended to use a natural asphalt mixture as the asphalt mixture.

상기 아스팔트 혼합물, 특정적으로 천연 아스팔트 혼합물은 당업계에서 통상적으로 사용되는 천연 아스팔트 혼합물이라면 특별히 한정되지 않지만, 바람직하게는 스트레이트(straight) 아스팔트, 트리니다드레이크(Trinidad lake) 아스팔트, 트리니다드에퓨레(Trinidad epure) 아스팔트 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋고, 보다 바람직하게는 침입도 20 내지 40의 스트레이트 아스팔트와 천연 아스팔트, 예를 들면 트리니다드레이크 아스팔트 및/또는 트리니다드에퓨레 아스팔트 혼합물을 사용하는 것이 좋고, 더욱 바람직하게는 침입도 20 내지 40의 스트레이트 아스팔트 70 내지 80중량% 및 트리니다드레이크 아스팔트 또는 트리니다드에퓨레 아스팔트로 이루어진 천연 아스팔트 20 내지 30중량%를 혼합한 것을 사용하는 것을 추천한다.The above asphalt mixture, specifically a natural asphalt mixture, is not particularly limited as long as it is a natural asphalt mixture commonly used in the art, but is preferably straight asphalt, Trinidad lake asphalt, Trinidad epure asphalt or at least one mixture selected from them, more preferably a mixture of straight asphalt having a penetration degree of 20 to 40 and natural asphalt, for example, Trinidad lake asphalt and/or Trinidad epure asphalt, is preferably used, and even more preferably a mixture of 70 to 80 wt% of straight asphalt having a penetration degree of 20 to 40 and 20 to 30 wt% of natural asphalt composed of Trinidad lake asphalt or Trinidad epure asphalt is recommended to be used.

여기서, 상기 스트레이트 아스팔트(straight asphalt)는 석유 아스팔트로 원료를 건류 또는 증류한 잔류물을 정제한 통상의 아스팔트로, 특히 침입도가 20 내지 40인 것이 도로에 시공 시 용이성이 있어 더욱 좋다.Here, the straight asphalt is a common asphalt refined from the residue obtained by drying or distilling the raw material from petroleum asphalt, and in particular, a penetration degree of 20 to 40 is preferable for ease of construction on roads.

상기 스트레이트 아스팔트는 아스팔트 혼합물에 70 내지 80중량%로 포함되는 것이 바람직하다. 그 함량이 70중량% 미만일 경우에는 아스팔트 포장 후 굳는데 오랜 시간이 소요될 수 있고, 연화점이 낮아질 수 있으며, 80중량%를 초과할 경우에는 유동성이 저하될 수 있다.The above straight asphalt is preferably included in the asphalt mixture at 70 to 80 wt%. If the content is less than 70 wt%, it may take a long time for the asphalt to harden after paving and the softening point may be lowered, and if it exceeds 80 wt%, the fluidity may be reduced.

또한, 상기 천연 아스팔트는 트리니다드레이크(trinidad lake) 아스팔트 및/또는 트리니다드에퓨레(Trinidadepure) 아스팔트 등을 사용할 수 있다.Additionally, the natural asphalt may be Trinidad lake asphalt and/or Trinidad Epure asphalt.

상기 천연 아스팔트는 아스팔트 혼합물에 20 내지 30중량%로 포함되는 것이 바람직하며, 그 함량이 20중량% 미만일 경우에는 유동성, 변형저항, 미끄럼저항 및 마찰저항의 개선효과가 미미하며, 30중량%를 초과할 경우에는 본 발명의 아스팔트가 연질화되고 연화점이 낮아질 수 있다.The above natural asphalt is preferably included in the asphalt mixture at 20 to 30 wt%. If the content is less than 20 wt%, the improvement effects in fluidity, deformation resistance, slip resistance, and friction resistance are minimal. If it exceeds 30 wt%, the asphalt of the present invention may become soft and the softening point may be lowered.

본 발명에 따른 방수시트, 특정적으로 고무화 아스팔트계 일체부착형 방수시트에 포함된 고무화 아스팔트층을 구성하는 고무화 아스팔트 혼합물의 아스팔트 외 나머지 성분의 함량은 아스팔트 100중량부 기준으로 한다.The content of the remaining components other than asphalt in the rubberized asphalt mixture constituting the rubberized asphalt layer included in the waterproofing sheet according to the present invention, specifically the rubberized asphalt-based integrally bonded waterproofing sheet, is based on 100 parts by weight of asphalt.

본 발명에 따른 스티렌이소프렌스티렌(stylene isoprene stylene; SIS)은 고무화 아스팔트계 일체부착형 방수시트의 시공시 균열 발생을 억제하고, 포트홀을 방지할 뿐 아니라, 점결력을 제공하는 동시에 전단강도 및 부착강도를 향상시킨다.The styrene isoprene stylene (SIS) according to the present invention suppresses the occurrence of cracks and prevents potholes during construction of a rubberized asphalt-based integrally bonded waterproofing sheet, while also providing cohesive strength and improving shear strength and bond strength.

바람직한 스티렌이소프렌스티렌은 신율이 320 내지 1,400%인 스티렌이소프렌스티렌을 사용하는 것이 좋고, 그 사용량은 아스팔트 100중량부 기준으로 1 내지 30중량부인 것을 추천한다.It is recommended to use styrene isoprene styrene having an elongation of 320 to 1,400%, and its usage amount is 1 to 30 parts by weight based on 100 parts by weight of asphalt.

본 발명에 따른 폴리부텐은 방수시트의 고무화 아스팔트층을 구성하는 고무화 아스팔트 혼합물을 구성하는 혼합물의 점성을 줄이고 소성을 증가시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 폴리부텐이라면 어떠한 것을 사용하여도 무방하다.The polybutene according to the present invention is intended to reduce the viscosity and increase the plasticity of a mixture constituting a rubberized asphalt mixture constituting a rubberized asphalt layer of a waterproofing sheet, and any polybutene conventional in the art having this purpose may be used.

특히, 본 발명에 따른 폴리부텐은 방수시트를 구성하는 고무화 아스팔트 혼합물에 포함됨으로써, 여름철에도 상온접착은 계속 유지되며, 겨울철의 낮은 온도에 유연성 유지할 수 있도록 한다.In particular, the polybutene according to the present invention is included in a rubberized asphalt mixture constituting a waterproof sheet, thereby maintaining room temperature adhesion even in the summer and maintaining flexibility at low temperatures in the winter.

바람직한 폴리부텐의 사용량은 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 아스팔트 100중량부 기준으로 1 내지 30중량부인 것이 좋다.The preferred amount of polybutene to be used can be varied at the user's discretion, but is recommended to be 1 to 30 parts by weight per 100 parts by weight of asphalt.

여기서, 상기 폴리부텐의 사용량이 1중량부 미만이면 첨가효과가 거의 없고, 30중량부를 초과하면 고무화 아스팔트 혼합물의 접착성능과 인장강도와 같은 기계적 물성이 저하되는 경향이 있다.Here, if the amount of polybutene used is less than 1 part by weight, the addition effect is almost nonexistent, and if it exceeds 30 parts by weight, the mechanical properties such as adhesive performance and tensile strength of the rubberized asphalt mixture tend to deteriorate.

본 발명에 따른 탄산칼슘은 방수시트의 고무화 아스팔트층을 구성하는 고무화 아스팔트 혼합물의 치수 안정성 및 내마모성을 향상시키는 동시에 충진성을 제공하기 위한 것으로서, 이러한 목적을 갖는 탄산칼슘이라면 어떠한 것을 사용하여도 무방하며, 그 사용량은 아스팔트 100중량부 기준으로 1 내지 10중량부인 것이 좋다.The calcium carbonate according to the present invention is intended to improve the dimensional stability and wear resistance of a rubberized asphalt mixture constituting a rubberized asphalt layer of a waterproofing sheet while providing filling properties. Any calcium carbonate having this purpose may be used, and the amount used is preferably 1 to 10 parts by weight based on 100 parts by weight of asphalt.

본 발명에 따른 점착부여제는 방수시트의 고무화 아스팔트층을 구성하는 고무화 아스팔트 혼합물에 점착성을 제공하기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적인 점착부여제라면 어떠한 것을 사용하여도 무방하지만, 추천하기로는 석유수지, 로진, 로진에스테르, 타키피에르(takifier) 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.The tackifier according to the present invention is intended to provide tackiness to a rubberized asphalt mixture constituting a rubberized asphalt layer of a waterproofing sheet. For this purpose, any tackifier conventional in the art may be used, but it is recommended to use a petroleum resin, rosin, rosin ester, takifier, or at least one mixture selected from these.

여기서, 상기 석유수지로는 C9계, C5계, C9-C5계 공중합 수지, 수첨수지 등이 있으며 단독 또는 2종 이상으로 조합하여 사용할 수 있다. Here, the petroleum resins include C9 series, C5 series, C9-C5 series copolymer resins, hydrogenated resins, etc., and can be used alone or in combination of two or more types.

바람직한 점착부여제의 사용량은 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 아스팔트 100중량부 기준으로 1 내지 10중량부인 것이 좋다.The amount of desired tackifier to be used can be varied according to the user's preference, but it is recommended to use 1 to 10 parts by weight per 100 parts by weight of asphalt.

여기서, 상기 점착부여제의 사용량이 1중량부 미만이면 그 효과가 미미하고, 10중량부를 초과하면 제품의 가격이 상승하는 문제점이 있다. Here, if the amount of the adhesive used is less than 1 part by weight, the effect is minimal, and if it exceeds 10 parts by weight, there is a problem that the price of the product increases.

본 발명에 따른 상용화제는 고무화 아스팔트 혼합물의 구성성분들 간 상용성을 극대화하기 위한 것으로서, 이러한 목적을 위해 당업계의 통상적인 상용화제라면 어떠한 것을 사용하여도 무방하며, 그 사용량은 아스팔트 100중량부 기준으로 1 내지 5중량부인 것이 좋다. The compatibilizer according to the present invention is intended to maximize compatibility between components of a rubberized asphalt mixture. For this purpose, any conventional compatibilizer in the art may be used, and the amount used is preferably 1 to 5 parts by weight based on 100 parts by weight of asphalt.

바람직한 상용화제로는 아이소택틱 폴리프로필렌(Atactic Polypropylene; APP), 에틸렌 초산비닐(Ethylene-Vinyl Acetate; EVA), 스티렌부타디엔 고무(Styrene-Butadiene Rubber; SBR), 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋고, 추천하기로는 미국 허드슨 아스팔트사의 PT-423, PT- 743 등을 사용하는 것을 추천한다.Preferred compatibilizers include isotactic polypropylene (APP), ethylene-vinyl acetate (EVA), styrene-butadiene rubber (SBR), or a mixture of at least one selected from these, and PT-423 and PT-743 from Hudson Asphalt Co., USA are recommended.

본 발명에 따른 흐름방지제는 고무화 아스팔트 혼합물이 온도 상승시 흘러내리는 현상이 발생되는 것을 방지하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 흐름방지제라면 어떠한 것을 사용하여도 무방하지만, 추천하기로는 클레이, 톱밥, 셀룰로오스 또는 이들로부터 선택된 적어도 하나 이상의 혼합물이라면 어떠한 것을 사용하여도 무방하다.The anti-flow agent according to the present invention is intended to prevent a rubberized asphalt mixture from flowing down when the temperature rises. Any conventional anti-flow agent having this purpose in the art may be used, but it is recommended to use any mixture of at least one selected from clay, sawdust, cellulose, or these.

바람직한 흐름방지제의 사용량은 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 아스팔트 100중량부 기준으로 0.1 내지 2중량부인 것이 좋다.The amount of desired flow inhibitor to be used can be varied according to the user's preference, but it is recommended to use 0.1 to 2 parts by weight per 100 parts by weight of asphalt.

여기서, 상기 흐름방지제의 사용량이 0.1중량부 미만이면, 고온에서 고무화 아스팔트 혼합물이 흘러내리는 현상이 발생하고, 2중량부를 초과하면 점착부여제, 폴리부텐 등의 상용량이 상대적으로 낮아져 점착기능이 저하될 수 있고, 흡수력이 증가하여 폴리부텐 등을 흡수하여 고무화 아스팔트 혼합물이 딱딱해지는 문제점이 있다.Here, if the amount of the above-mentioned flow-preventing agent used is less than 0.1 parts by weight, the rubberized asphalt mixture may flow at high temperatures, and if it exceeds 2 parts by weight, the amount of the adhesive, polybutene, etc. used may be relatively low, which may result in a decrease in the adhesive function, and the absorption capacity may increase, which may absorb polybutene, etc., thereby causing the rubberized asphalt mixture to harden.

본 발명에 따른 박리방지제는 방수시트의 시공시 시공대상면으로부터 쉽게 박리되어 탈리되는 것을 방지하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 박리방지제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 폴리인산계, 아민계, 또는 인산 에스테르계 박리방지제를 사용하는 것이 좋고, 추천하기로는 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제; 산가가 10 ㎎KOH/g 이하이고, 총 아민가가 140 내지 400㎎HCl/g인 아민계 박리방지제인 것이 좋다.The anti-stripping agent according to the present invention is intended to prevent the waterproofing sheet from being easily peeled off and detached from the surface to be constructed during construction, and any conventional anti-stripping agent having this purpose in the art may be used, but it is preferably a polyphosphoric acid-based, amine-based, or phosphate ester-based anti-stripping agent, and it is recommended to use a polyphosphoric acid-based anti-stripping agent having a liquid form, a specific gravity of 1.0 or higher, and a viscosity at 60°C of 110 cPs; and an amine-based anti-stripping agent having an acid value of 10 mgKOH/g or lower, and a total amine value of 140 to 400 mgHCl/g.

바람직한 박리방지제의 사용량은 특별히 한정되지 않지만, 사용자의 선택에 따라 아스팔트 100중량부 기준으로 0.1 내지 2중량부인 것이 좋다.The amount of the preferred anti-stripping agent to be used is not particularly limited, but is preferably 0.1 to 2 parts by weight per 100 parts by weight of asphalt, depending on the user's choice.

본 발명에 따른 산화방지제는 방수시트를 구성하는 고무화 아스팔트층에 포함된 고무화 아스팔트 혼합물의 산화를 방지하기 위한 것이다.The antioxidant according to the present invention is for preventing oxidation of a rubberized asphalt mixture included in a rubberized asphalt layer constituting a waterproof sheet.

바람직한 산화방지제는 아민계, 비스페놀계, 모노페놀계 및 유황계 산화방지제가 사용될 수 있고, 그 사용량은 아스팔트 100중량부 기준으로 0.1 내지 2중량부인 것이 좋다.Preferred antioxidants include amine-based, bisphenol-based, monophenol-based and sulfur-based antioxidants, and the amount used is preferably 0.1 to 2 parts by weight based on 100 parts by weight of asphalt.

특정적으로, 본 발명에 따른 산화방지제는 고온에서 가공이 이루어질 경우 저분자형 고분자형 페놀계 산화방지제, 예를 들면 2.2-메틸렌비스(4-메틸-6-t-부틸페놀)[2 . 2 - M e t h y l e n e b i s ( 4 - m e t h y l - 6 - t - b u t y l p h e n o l )], 2.6-디-t-부틸-4-메틸페놀(2.6-di -t-Butyl-4-methylphenol) 또는 이들의 혼합물을 사용하는 것을 추천한다.Specifically, when the antioxidant according to the present invention is processed at high temperatures, it is recommended to use a low molecular weight high molecular weight phenol antioxidant, for example, 2.2-methylenebis(4-methyl-6-t-butylphenol)[2.2-M e t h y l e n e b i s ( 4- m e t h y l - 6 - t - b u t y l p h e n o l )], 2.6-di-t-butyl-4-methylphenol, or a mixture thereof.

이와 같은 구성을 갖는 본 발명에 따른 방수시트, 특정적으로 고무화 아스팔트계 일체부착형 방수시트를 구성하는 고무화 아스팔트층은 하기의 특정 양태로 실시되는 부가물을 1종 또는 1종 이상 더 포함할 수 있다.The waterproofing sheet according to the present invention having such a configuration, specifically the rubberized asphalt layer constituting the rubberized asphalt-based integrally bonded waterproofing sheet, may further include one or more types of additives implemented in the following specific manner.

특정 양태로서, 본 발명에 따른 방수시트, 특정적으로 고무화 아스팔트계 일체부착형 방수시트를 구성하는 고무화 아스팔트 혼합물은 혼합물의 강도, 자외선 저항성 및 재료 분리 저항성을 개선하기 위하여, 아스팔트 100중량부 기준으로 1 내지 3중량부의 티타늄옥사이드를 더 포함할 수 있다.In a specific embodiment, the rubberized asphalt mixture constituting the waterproofing sheet according to the present invention, specifically the rubberized asphalt-based integrally bonded waterproofing sheet, may further contain 1 to 3 parts by weight of titanium oxide based on 100 parts by weight of asphalt in order to improve the strength, ultraviolet resistance and material separation resistance of the mixture.

다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 충진성 및 내구성을 향상시키기 위하여, 아스팔트 100중량부 기준으로 1 내지 3중량부의 암모늄 노니페놀 에테르설페이트(amaonium nonylphenol ether sulfate)를 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 3 parts by weight of ammonium nonylphenol ether sulfate based on 100 parts by weight of asphalt to improve the filling properties and durability of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 내투수 저항성이 탁월하여 우수 등이 침투하는 것을 최소화 할 수 있도록 하기 위하여, 테트라에틸오소실리케이트(tetraethyl orthosilicate; TEOS)를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further include 1 to 3 parts by weight of tetraethyl orthosilicate (TEOS) based on 100 parts by weight of asphalt to provide excellent water resistance and minimize penetration of rainwater and the like.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물에 우수한 신장율, 내균열성, 내한성 및 접합성 향상 등을 제공하기 위하여, 에틸렌비닐아세테이트를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain ethylene vinyl acetate in an amount of 1 to 3 parts by weight based on 100 parts by weight of asphalt in order to provide the mixture with excellent elongation, crack resistance, cold resistance, and improved bonding properties.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 시공성, 부착성 및 내구성 등을 향상시키기 위하여, 아스팔트 100중량부 기준으로 1 내지 3중량부의 퍼플루오로메톡시실란을 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 3 parts by weight of perfluoromethoxysilane based on 100 parts by weight of asphalt in order to improve the workability, adhesion, durability, etc. of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 점도조절 및 강도증진을 위하여, 테트라에틸렌펜타민(Tetraethylenepentamine; TEPA)을 아스팔트 100중량부 기준으로 1 내지 10중량부로 더 포함할 수 있는데, 테트라에틸렌펜타민이 1중량부 미만이면 그 효과가 미미하며, 10중량부를 초과하면 그 양이 과다하여 고무화 아스팔트 혼합물의 물성에 좋지 않은 영향을 줄 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 10 parts by weight of tetraethylenepentamine (TEPA) based on 100 parts by weight of asphalt to control the viscosity of the mixture and increase the strength. If the amount of TEPA is less than 1 part by weight, the effect is minimal, and if it exceeds 10 parts by weight, the amount is excessive and may have a negative effect on the properties of the rubberized asphalt mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 공극을 치밀하게 하고 누수를 방지하며 강도를 향상시키기 위하여, 나트륨벤토나이트를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 3 parts by weight of sodium bentonite based on 100 parts by weight of asphalt in order to compact the pores of the mixture, prevent leakage, and improve strength.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 초기작업 성능을 유지하고 강도를 향상시키기 위하여 피로인산칼슘을 더 포함할 수 있는데, 그 사용량은 아스팔트 100중량부 기준으로 0.1 내지 2중량부가 좋다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain calcium pyrophosphate to maintain the initial working performance of the mixture and improve strength, the amount of which is preferably 0.1 to 2 parts by weight based on 100 parts by weight of asphalt.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물과 유기물과의 경화를 방지함으로써 경화 반응성을 향상시키기 위하여, 아스팔트 100중량부 기준으로 1 내지 5중량부의 수산화리튬을 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 5 parts by weight of lithium hydroxide based on 100 parts by weight of asphalt to improve curing reactivity by preventing curing of the mixture with organic matter.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 이온화를 방지하기 위하여, 아스팔트 100중량부 기준으로 1 내지 10중량부의 소듐헥사메타포스페이트를 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 10 parts by weight of sodium hexametaphosphate based on 100 parts by weight of asphalt to prevent ionization of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 가소성 및 보수성을 향상시키고 균열방지와 강도증진을 위하여, 코코베타인을 아스팔트 100중량부 기준으로 1 내지 5중량부 더 포함할 수 있다. In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 5 parts by weight of cocobetaine based on 100 parts by weight of asphalt to improve the plasticity and water-retaining properties of the mixture and to prevent cracking and increase strength.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 접착력 및 내구성을 향상시키기 위하여, 아스팔트 100중량부 기준으로 1 내지 5중량부의 초산비닐-말레인산디에틸을 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 5 parts by weight of diethyl vinyl acetate-maleate based on 100 parts by weight of asphalt to improve the adhesion and durability of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 접착성 및 부착강도 향상을 위하여 옥틸트리에톡시실란을 더 포함할 수 있는데, 상기 옥틸트리에톡시실란은 단량체 형태로 사용가능하며, 상기 단량체의 분자량은 특별히 한정되는 것은 아니지만, 바람직하게는 150 내지 450Da인 것이 좋고, 그 사용량은 아스팔트 100중량부 기준으로 1 내지 3중량부인 것을 추천한다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further include octyltriethoxysilane to improve the adhesiveness and bonding strength of the mixture. The octyltriethoxysilane can be used in the form of a monomer, and the molecular weight of the monomer is not particularly limited, but is preferably 150 to 450 Da, and the amount used is recommended to be 1 to 3 parts by weight based on 100 parts by weight of asphalt.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 내염해성, 중성화 저항성, 내열성, 자기보수성 등을 개선하기 위하여 알루미늄과 마그네슘이 풍부하고 흡착성이 강한 천연점토의 일종인 스멕타이트(smectite)를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 0.1 to 3 parts by weight of smectite, a type of natural clay rich in aluminum and magnesium and having strong adsorptive properties, based on 100 parts by weight of asphalt, in order to improve the salt resistance, neutralization resistance, heat resistance, self-retention, etc. of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 내식성, 내약품성 및 내화학성을 개선시키고, 동결융해저항성, 내구성 등을 향상시키기 위하여, 황화코발트를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있는데, 상기 황화코발트는 염화코발트 6수화물(Cobalt(ll) chloride hexahydrate), 지방산, 제1 아민계 화합물 및 비극성 용매의 혼합용액을 준비하는 단계; 상기 혼합용액을 불활성 기체 상에서 100 내지 120℃의 온도로 열처리하여 혼합물을 제조하는 단계; 파우더 형태의 황(sulfur)을 제2 아민계 화합물에 분산한 용액을 상기 혼합물에 교반시켜 250 내지 300 ℃의 반응온도로 반응시키는 반응 단계; 및 상기 반응 단계를 거쳐 생성된 물질을 에탄올(ethanol)과 톨루엔(toluene)의 혼합 용액으로 원심분리하는 단계;를 포함하여 제조될 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 0.1 to 3 parts by weight of cobalt sulfide based on 100 parts by weight of asphalt in order to improve the corrosion resistance, chemical resistance, and freeze-thaw resistance, durability, etc. of the mixture. The cobalt sulfide may be prepared by including the steps of: preparing a mixed solution of cobalt(ll) chloride hexahydrate, a fatty acid, a first amine compound, and a nonpolar solvent; heat-treating the mixed solution at a temperature of 100 to 120° C. in an inert gas phase to prepare a mixture; a reaction step of stirring a solution in which powdered sulfur is dispersed in a second amine compound into the mixture and reacting the mixture at a reaction temperature of 250 to 300° C.; and a step of centrifuging a material produced through the reaction step into a mixed solution of ethanol and toluene.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 점도증진 및 부착력 강화를 위하여, 아스팔트 100중량부 기준으로 1 내지 10중량부의 알긴산 나트륨을 더 포함할 수 있는데, 그 함량이 1중량부 미만이면 소수성이 저하되고, 함량이 10중량부를 초과하면 과도하게 점도가 상승되어 좋지 않다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 10 parts by weight of sodium alginate based on 100 parts by weight of asphalt to increase the viscosity of the mixture and strengthen the adhesiveness. If the content is less than 1 part by weight, the hydrophobicity is reduced, and if the content exceeds 10 parts by weight, the viscosity is excessively increased, which is not good.

상기 알긴산 나트륨은 (C6H8O6)n으로 표시되는 다당류의 하나로서 카르복실기를 가지고 있으며, 다시마류를 소다회 처리하여 만들 수 있는데, 알긴산 나트륨 자체에 점성을 갖고 있어 이를 고무화 아스팔트 혼합물에 혼입되면 점도증진 및 부착력을 강화하게 된다.The above sodium alginate is a polysaccharide represented by (C 6 H 8 O 6 )n, has a carboxyl group, and can be made by treating kelp with soda ash. Since sodium alginate itself has viscosity, when it is mixed into a rubberized asphalt mixture, it increases viscosity and strengthens adhesiveness.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 반응성을 높여 조기강도를 발현하기 위하여, 알루민산스트론튬(strontium aluminate)를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 0.1 to 3 parts by weight of strontium aluminate based on 100 parts by weight of asphalt in order to increase the reactivity of the mixture and develop early strength.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 노화방지, 박리방지 및 균열 저항성 향상을 위하여, 아스팔트 100중량부 기준으로 1 내지 5중량부의 글루코노락톤(gluconolactone)을 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 5 parts by weight of gluconolactone based on 100 parts by weight of asphalt to improve anti-aging, anti-stripping, and crack resistance of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 분산성 향상 및 조성물의 혼합 후에도 다시 엉김현상이 발생하지 않도록 하기 위하여 로진산 나트륨을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 3 parts by weight of sodium rosinate based on 100 parts by weight of asphalt in order to improve the dispersibility of the mixture and prevent the re-occurrence of clumping after mixing the composition.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 빠른 경화특성을 제공하여 재료분리 억제 및 재료손실을 효과적으로 방지하고, 습윤경화성능, 균열억제성능, 및 수축 저항성능을 향상시키기 위하여, 아스팔트 100중량부 기준으로 0.1 내지 2중량부의 제올라이트 미분말을 더 포함할 수 있는데, 바람직한 제올라이트 미분말의 평균입도는 1 내지 5㎛ 이다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further include 0.1 to 2 parts by weight of zeolite fine powder based on 100 parts by weight of asphalt in order to provide rapid curing properties of the mixture, effectively prevent material separation and material loss, and improve wet curing performance, crack suppression performance, and shrinkage resistance performance. The average particle size of the zeolite fine powder is preferably 1 to 5 μm.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 접착 강도 특성과 내마모성, 내오염성, 내화학성, 내후성, 내염해성 등을 개선하기 위하여, 아스팔트 100중량부 기준으로 0.1 내지 2중량부의 하이드록시탄산마그네슘을 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 0.1 to 2 parts by weight of magnesium hydroxycarbonate based on 100 parts by weight of asphalt in order to improve the adhesive strength properties, wear resistance, contamination resistance, chemical resistance, weather resistance, salt resistance, etc. of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 속경성, 강도 및 내구성을 개선하기 위하여, 아스팔트 100중량부 기준으로 0.1 내지 2중량부의 탄산아파타이트를 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 0.1 to 2 parts by weight of carbonated apatite based on 100 parts by weight of asphalt to improve rapid hardening, strength and durability.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 자외선 저항성 및 재료 분리 저항성을 개선하기 위하여, 아스팔트 100중량부 기준으로 0.1 내지 2중량부의 징크옥사이드를 더 포함할 수 있는데, 그 함량이 아스팔트 100중량부 기준으로 2중량부를 초과하면 자외선 및 재료 분리 저항성을 개선되나 강도가 저하되어 좋지 않고, 0.1중량부 미만이면 그 효과가 미미하여 좋지 않다. In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 0.1 to 2 parts by weight of zinc oxide based on 100 parts by weight of asphalt in order to improve ultraviolet resistance and material separation resistance of the mixture. If the content exceeds 2 parts by weight based on 100 parts by weight of asphalt, ultraviolet and material separation resistance is improved, but strength is reduced, which is not good. If the content is less than 0.1 parts by weight, the effect is minimal, which is not good.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 압축강도 및 접착강도를 향상시키고, 균열저항성을 향상시키기 위하여, 사포나이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있는데, 상기 사포나이트는 몬모릴로나이트 계열의 층상실리케이트 점토로서, 우수한 압축강도와 접착강도를 갖고 있어 이를 조성물에 포함시키면 상기와 같은 효과를 발현하게 된다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 5 parts by weight of saponite based on 100 parts by weight of asphalt, in order to improve the compressive strength and adhesive strength of the mixture and to improve crack resistance. The saponite is a layered silicate clay of the montmorillonite series, which has excellent compressive strength and adhesive strength, and thus, when included in the composition, the above-described effects are exhibited.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 방수성, 내열성, 내염성 및 접착성 등을 향상시키기 위하여, 아스팔트 100중량부 기준으로 1 내지 10중량부의 아세틸레이티드라놀란을 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 10 parts by weight of acetylated dranolane based on 100 parts by weight of asphalt to improve waterproofing, heat resistance, salt resistance, and adhesion.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 강도, 내산성 등을 향상시키고, 중성화 방지 및 오염물질 분해효과 등을 증진시키기 위하여, 아스팔트 100중량부 기준으로 1 내지 5중량부의 맥반석 미분말을 더 포함할 수 있는데, 상기 맥반석은 화성암류 중 화강섬록반암에 속하는 것으로 녹색 바탕에 석영과 장석이 조밀하게 고루 섞여 있는 암석으로 미세한 다공질 구조이며, 무수규산, 산화알미늄을 주성분으로 하여 산화제2철, 칼슘, 마그네슘, 게르마늄, 세레늄 등을 함유하고 있고, 다공질의 특성으로 시공대상면의 오염물질, 유기물, 잡균 등을 흡착·분해하여 제거하고, 세균을 소멸하고 토질을 중성으로 조절해 주는 작용이 있는 것으로, 바람직한 평균입도는 1 내지 5㎛ 이다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 5 parts by weight of fine powder of sphagnum moss based on 100 parts by weight of asphalt in order to improve the strength, acid resistance, etc. of the mixture, and to enhance the effect of preventing neutralization and decomposing pollutants. The sphagnum moss belongs to granodiorite among igneous rocks and is a rock in which quartz and feldspar are densely mixed on a green background and has a fine porous structure, and contains anhydrous silicic acid and aluminum oxide as main components, and ferric oxide, calcium, magnesium, germanium, selenium, etc., and due to the porous characteristics, it has the effect of removing pollutants, organic matter, and germs from the surface to be constructed by adsorbing and decomposing them, and extinguishing germs and adjusting the soil to neutrality. The preferable average particle size is 1 to 5㎛.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 내마모성, 내화학성, 내열성 등을 개선하기 위하여, 아스팔트 100중량부 기준으로 1 내지 3중량부의 티탄산칼륨을 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 3 parts by weight of potassium titanate based on 100 parts by weight of asphalt in order to improve the wear resistance, chemical resistance, heat resistance, etc. of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 강도를 개선하고 표면오염을 방지하기 위하여 산화제일구리(Cu2O)를 아스팔트 100중량부 기준으로 0.1 내지 2중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 0.1 to 2 parts by weight of cuprous oxide (Cu 2 O) based on 100 parts by weight of asphalt to improve the strength of the mixture and prevent surface contamination.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 휨강도, 수밀성, 내식성, 염해 및 동결융해 저항성 등을 향상시키고, 수축방지효과를 제공하기 위하여 불화바륨을 아스팔트 100중량부 기준으로 1 내지 10중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 10 parts by weight of barium fluoride based on 100 parts by weight of asphalt in order to improve the flexural strength, water tightness, corrosion resistance, salt damage and freeze-thaw resistance of the mixture and to provide an anti-shrinkage effect.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 우수한 강도발현과 수밀성을 향상시키고, 수축방지효과를 제공하기 위하여, 페로니켈 슬레그를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further include 1 to 5 parts by weight of ferronickel slag based on 100 parts by weight of asphalt in order to improve excellent strength development and water-tightness of the mixture and provide an anti-shrinkage effect.

여기서, 상기 페로니켈 슬래그는 페로니켈 공장에서 페로니켈의 제조시 전기로의 용융환원과정에서 발생하는 슬래그를 의미하는 것으로, 우수한 강도 발현과 수밀성을 향상시키고, 수축 방지 효과를 제공하는 기능을 한다.Here, the above ferronickel slag refers to slag generated during the melting reduction process in an electric furnace during the manufacture of ferronickel in a ferronickel factory, and has the function of improving excellent strength expression and water-tightness and providing a shrinkage prevention effect.

한편, 상기 페로니켈 슬래그는 SiO2의 함량이 50 내지 70 중량%이고, MgO의 함량이 25 내지 45 중량%이고, CaO의 함량이 0.1 내지 3 중량%이고, Fe2O3의 함량이 1 내지 10 중량%이고, Al2O3의 함량이 0.1 내지 3 중량%이고, NiO의 함량이 0.1 내지 3 중량%이고, Cr2O3의 함량이 0.1 내지 3 중량%인 것을 사용하여 상기한 효과를 더욱 향상시킬 수 있을 뿐만 아니라, 우수한 균열제어 효과를 더욱 향상시킬 수 있는 효과가 있다.Meanwhile, the ferronickel slag having a SiO2 content of 50 to 70 wt%, a MgO content of 25 to 45 wt%, a CaO content of 0.1 to 3 wt%, a Fe2O3 content of 1 to 10 wt%, a Al2O3 content of 0.1 to 3 wt%, a NiO content of 0.1 to 3 wt%, and a Cr2O3 content of 0.1 to 3 wt% can further improve the above-mentioned effects, and has the effect of further improving the excellent crack control effect.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 균열저항성, 동결융해 저항성 등을 향상시키고 내구성능을 개선하기 위하여 탄산구리를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있는데, 상기 탄산구리는 결정형의 염기성 탄산구리인 것이 좋은데, 상기 결정형의 염기성 탄산구리는 55 내지 70 ℃로 유지되는 증류수에, 0.05 내지 0.5 M농도의 황산구리 수용액 및 0.01 내지 0.1 M농도의 소석회 수용액을 1: 1 부피비율로 동시 적하 및 반응시켜 염기성 탄산구리 수용액을 제조하는 단계; 상기 반응이 완료된 염기성 탄산구리 수용액을 여과 및 세척하여 염기성 탄산구리 슬러리를 제조하는 단계; 및 상기 염기성 탄산구리 슬러리를 80 내지 150 ℃의 온도로 건조하여, 결정형의 염기성 탄산구리를 제조하는 단계를 포함하는 방법으로 제조할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 0.1 to 3 parts by weight of copper carbonate based on 100 parts by weight of asphalt in order to improve the cracking resistance, freeze-thaw resistance, etc. of the mixture and to enhance durability. The copper carbonate is preferably crystalline basic copper carbonate. The crystalline basic copper carbonate may be prepared by a method including: a step of simultaneously adding and reacting a 0.05 to 0.5 M concentrated copper sulfate aqueous solution and a 0.01 to 0.1 M concentrated slaked lime aqueous solution in a volume ratio of 1:1 to distilled water maintained at 55 to 70°C; a step of filtering and washing the basic copper carbonate aqueous solution, in which the reaction is completed, to prepare a basic copper carbonate slurry; and a step of drying the basic copper carbonate slurry at a temperature of 80 to 150°C to prepare a crystalline basic copper carbonate.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 경화를 촉진시키고 크랙의 발생을 예방하기 위하여, 2-하이드록시에틸 아크릴레이트(2-hydroxyethyl acrylate)를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다In another specific embodiment, the rubberized asphalt mixture according to the present invention may further include 1 to 5 parts by weight of 2-hydroxyethyl acrylate based on 100 parts by weight of asphalt to promote hardening of the mixture and prevent occurrence of cracks.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 강도 발현, 내마모성 및 스케일링 저항성 개선 효과를 향상시키기 위하여, 두랄루민(Duralumin)을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 5 parts by weight of duralumin based on 100 parts by weight of asphalt in order to improve the strength development, wear resistance, and scaling resistance of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 부착성, 유연성 및 점도조절을 용이하게 하기 위하여, 디펜타에리트올 헥사아크릴레이트(DPHA)을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 5 parts by weight of dipentaerythritol hexaacrylate (DPHA) based on 100 parts by weight of asphalt to facilitate control of the adhesion, flexibility, and viscosity of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 노화를 방지하기 위하여, 2,2,4-트리메틸-1,2-디하이드로퀴논(Kumanox RD)을 아스팔트 100중량부 기준으로 0.1 내지 2중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 0.1 to 2 parts by weight of 2,2,4-trimethyl-1,2-dihydroquinone (Kumanox RD) based on 100 parts by weight of asphalt to prevent aging of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 저장안정성을 향상시키기 위하여 글리세린 모노스테아레이트(GMS: Glycerin Mono Stearate)를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain glycerin monostearate (GMS) in an amount of 1 to 3 parts by weight based on 100 parts by weight of asphalt to improve the storage stability of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물을 구성하는 아스팔트 등이 물에 분산되어 잘 혼합되도록 하기 위하여, 우지 알킬(Tallowalkyl) 화합물, 예를 들면 폴리에톡실레이티드 탈로우 아민(Polyethoxylated tallow amine) 또는 폴리옥시에틸렌 탈로우아민(Polyoxyethylene tallowamine, POE-tallowamine)을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain a tallowalkyl compound, for example, polyethoxylated tallow amine or polyoxyethylene tallowamine (POE-tallowamine), in an amount of 0.1 to 3 parts by weight based on 100 parts by weight of asphalt, in order to allow asphalt and the like constituting the mixture to be dispersed in water and mixed well.

여기서, 상기 우지 알킬 화합물의 사용량이 0.1중량부 미만이면 아스팔트 등과 물이 분리되어 유화작용이 풀리게 되고, 3중량부를 초과하면 점도가 높게 올라가 경제성이 감소하는 효과가 있다.Here, if the amount of the above-mentioned alkyl compound used is less than 0.1 parts by weight, asphalt, etc. and water are separated, and the emulsifying effect is broken, and if it exceeds 3 parts by weight, the viscosity increases significantly, which has the effect of reducing economic efficiency.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 경화속도를 향상시키기 위하여, 톨유 지방산을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 5 parts by weight of tall oil fatty acid based on 100 parts by weight of asphalt to improve the curing speed of the mixture.

여기서, 상기 톨유 지방산은 높은 지방산 함량 및 낮은 로진산과 불검화물을 가지고 있어 건조 특성이 우수하고, 상기 아스팔트입자 표면에 석유수지 코팅층을 용이하게 형성시킬 수 있어, 상기 고무화 아스팔트 혼합물의 경화 속도가 현저히 개선될 수 있다.Here, the tall oil fatty acid has a high fatty acid content and low rosin acid and unsaponifiable matter, so it has excellent drying properties and can easily form a petroleum resin coating layer on the surface of the asphalt particles, so that the curing speed of the rubberized asphalt mixture can be significantly improved.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 경화속도 및 내구성을 향상시키기 위하여, 스티렌-부타디엔 고무 라텍스를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain styrene-butadiene rubber latex in an amount of 1 to 3 parts by weight based on 100 parts by weight of asphalt to improve the curing speed and durability of the mixture.

여기서, 상기 스티렌-부타디엔 고무 라텍스는 25℃에서 점도가 1,000 내지 1,800cps인 것을 사용하는 것이 바람직하다.Here, it is preferable to use the styrene-butadiene rubber latex having a viscosity of 1,000 to 1,800 cps at 25°C.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 유동성 개선, 항균성, 산화방지효과, 내산성, 내염해성 및 동결융해 저항성 등을 향상시키기 위하여, 디포타슘글리시리제이트(Dipotassium Glycyrrhizate)를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 5 parts by weight of dipotassium glycyrrhizate based on 100 parts by weight of asphalt in order to improve the fluidity, antibacterial properties, antioxidant effects, acid resistance, salt resistance, and freeze-thaw resistance of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 균열 저항성 향상 및 외부 충격을 흡수하여 강도의 안정성을 향상시키기 위하여 붕소의 천연광물로 백색의 미세한 분말인 콜레마나이트를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 3 parts by weight of colemanite, a natural mineral of boron, which is a white, fine powder, based on 100 parts by weight of asphalt, in order to improve the crack resistance of the mixture and absorb external impacts to improve the stability of strength.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 염화물이온의 침투 저항성, 방청성, 내수성 및 내구성을 개선하기 위하여 티오아세트아미드를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 1 to 3 parts by weight of thioacetamide based on 100 parts by weight of asphalt to improve the chloride ion penetration resistance, rust prevention, water resistance and durability of the mixture.

또 다른 특정 양태로서, 본 발명에 따른 고무화 아스팔트 혼합물은 혼합물의 방청성 및 내약품성을 향상시키고, 산화방지기능 및 내구성을 개선하기 위하여, 테크라하이드로커큐민(THC)을 아스팔트 100중량부 기준으로 0.1 내지 2중량부로 더 포함할 수 있는데, 그 함량이 0.1중량부 미만이면 상기의 성능 개선 효과가 미미하며, 2중량부를 초과하면 작업성이 저하되어 좋지 않다.In another specific embodiment, the rubberized asphalt mixture according to the present invention may further contain 0.1 to 2 parts by weight of tetrahydrocurcumin (THC) based on 100 parts by weight of asphalt in order to improve the rust prevention and chemical resistance of the mixture and to improve the oxidation prevention function and durability. If the content is less than 0.1 parts by weight, the performance improvement effect is minimal, and if it exceeds 2 parts by weight, workability deteriorates, which is not good.

특정 양태로서, 본 발명에 따른 방수시트, 특정적으로 고무화 아스팔트계 일체부착형 방수시트는 상기 플라스틱 필름 기재층이 고무화 아스팔트층의 일측 및/또는 양측면에 적층되는 형태로 구성될 수도 있다.In a specific embodiment, the waterproofing sheet according to the present invention, specifically the rubberized asphalt-based integrally bonded waterproofing sheet, may be configured in a form in which the plastic film substrate layer is laminated on one side and/or both sides of the rubberized asphalt layer.

다른 특정 양태로서, 본 발명에 따른 방수시트, 특정적으로 고무화 아스팔트계 일체부착형 방수시트는 상기 플라스틱 필름 기재층이 고무화 아스팔트층의 일측에 적층되면 이에 대향되는 타측 일측에 이형층이 형성될 수도 있다.In another specific embodiment, the waterproofing sheet according to the present invention, specifically the rubberized asphalt-based integrally bonded waterproofing sheet, may have a release layer formed on one side of the opposite side of the plastic film substrate layer when the plastic film substrate layer is laminated on one side of the rubberized asphalt layer.

이러한 경우, 상기 이형층을 제거한 후 상기 방수시트가 시공 대상면에 일체로 접착될 수 있도록 한다.In this case, after removing the above-mentioned heterogeneous layer, the waterproof sheet can be integrally adhered to the surface to be constructed.

이와 같은 구성을 갖는 본 발명에 따른 방수시트, 특정적으로 고무화 아스팔트계 일체부착형 방수시트를 이용한 방수시트 시공방법을 설명하면 다음과 같다.The waterproofing sheet construction method using the waterproofing sheet according to the present invention having such a configuration, specifically the rubberized asphalt-based integrally bonded waterproofing sheet, is explained as follows.

본 발명에 따른 시공방법, 특정적으로 방수시트 시공방법, 보다 특정적으로 고무화 아스팔트계 일체부착형 방수시트 시공방법은 The construction method according to the present invention, specifically the waterproofing sheet construction method, and more specifically the rubberized asphalt-based integrally bonded waterproofing sheet construction method

시공할 대상면을 정리하는 정리단계;The preparation stage of organizing the surface to be constructed;

상기 정리단계가 종료된 시공면에 프라이머를 도포하는 프라이머 도포단계;Primer application step of applying a primer to the construction surface where the above organizing step has been completed;

상기 프라이머 도포단계가 종료된 시공면에 플라스틱 필름 기재층 및 상기 플라스틱 필름 기재층의 일측면에 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 30중량부, 폴리부텐 1 내지 30중량부, 탄산칼슘 1 내지 10중량부, 점착부여제 1 내지 10중량부, 상용화제 1 내지 5중량부, 흐름방지제 0.1 내지 2중량부 박리방지제 0.1 내지 2중량부, 및 산화방지제 0.1 내지 2중량부를 포함하는 고무화 아스팔트 혼합물을 적층한 고무화 아스팔트층을 포함하는 고무화 아스팔트계 일체부착형 방수시트를 부착하는 방수시트 부착단계: 및A waterproofing sheet attachment step for attaching a rubberized asphalt-based integrally bonded waterproofing sheet including a rubberized asphalt layer laminated with a rubberized asphalt mixture containing, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene isoprene styrene, 1 to 30 parts by weight of polybutene, 1 to 10 parts by weight of calcium carbonate, 1 to 10 parts by weight of a tackifier, 1 to 5 parts by weight of a compatibilizer, 0.1 to 2 parts by weight of a flow inhibitor, 0.1 to 2 parts by weight of an anti-stripping agent, and 0.1 to 2 parts by weight of an antioxidant, on a construction surface where the primer application step is completed, and

상기 방수시트 부착단계가 종료된 고무화 아스팔트계 일체부착형 방수시트 상면에 보호재를 부착하는 보호재 부착단계를 포함한다.It includes a protective material attachment step of attaching a protective material to the upper surface of the rubberized asphalt-based integrally bonded waterproofing sheet after the above waterproofing sheet attachment step is completed.

여기서, 상기 프라이머 도포단계의 프라이머는 당업계에서 통상적으로 사용하는 프라이머라면 어떠한 것을 사용하여도 무방하며, 보호재 부착단계의 보호재는 방수시트를 보호하기 위한 것으로 당업계에서 통상적으로 사용하는 보호재라면 어떠한 것이라도 무방하며, 이러한 보호재의 일례로 발포품, 몰탈 등을 들 수 있다.Here, the primer in the primer application step may be any primer commonly used in the industry, and the protective material in the protective material attachment step may be any protective material commonly used in the industry to protect the waterproofing sheet. Examples of such protective materials include foam products and mortar.

이하에서 실시 예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.Hereinafter, the present invention will be specifically described through examples. However, the following examples are only intended to specifically describe the present invention and the scope of the present invention is not limited by these examples.

[실시예 1][Example 1]

폴리프로필렌으로 이루어진 플라스틱 필름상에On a plastic film made of polypropylene

침입도 30의 스트레이트 아스팔트 75g 및 트리니다드레이크 아스팔트로 이루어진 천연 아스팔트 25g의 혼합물로 이루어진 아스팔트 혼합물 100g, 신율이 약 850%인 스티렌이소프렌스티렌 15g, 폴리부텐 15g, 탄산칼슘 5g, 로진에스테르 5g, 아이소택틱 폴리프로필렌 3g, 클레이 1g, 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제 1g, 및 2.2-메틸렌비스(4-메틸-6-t-부틸페놀) 1g을 혼합한 고무화 아스팔트 혼합물을 적층하여 방수시트를 제조하였다.A waterproof sheet was manufactured by laminating a rubberized asphalt mixture comprising 100 g of an asphalt mixture consisting of 75 g of straight asphalt having a penetration degree of 30 and 25 g of natural asphalt consisting of Trinidad lake asphalt, 15 g of styrene isoprene styrene having an elongation of about 850%, 15 g of polybutene, 5 g of calcium carbonate, 5 g of rosin ester, 3 g of isotactic polypropylene, 1 g of clay, 1 g of a polyphosphoric acid-based anti-stripping agent in liquid form having a specific gravity of 1.0 or higher and a viscosity at 60°C of 110 cPs, and 1 g of 2.2-methylenebis(4-methyl-6-t-butylphenol).

[실시예 2][Example 2]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 티타늄옥사이드 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of titanium oxide was additionally added to the rubberized asphalt mixture.

[실시예 3][Example 3]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 암모늄 노니페놀 에테르설페이트 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of ammonium noniphenol ether sulfate was additionally added to the rubberized asphalt mixture.

[실시예 4][Example 4]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 테트라에틸오소실리케이트 2g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 2 g of tetraethyl orthosilicate was additionally added to the rubberized asphalt mixture.

[실시예 5][Example 5]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 에틸렌비닐아세테이트 2g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 2 g of ethylene vinyl acetate was additionally added to the rubberized asphalt mixture.

[실시예 6][Example 6]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 퍼플루오로메톡시실란 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of perfluoromethoxysilane was additionally added to the rubberized asphalt mixture.

[실시예 7][Example 7]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 테트라에틸렌펜타민 5g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 5 g of tetraethylene pentamine was additionally added to the rubberized asphalt mixture.

[실시예 8][Example 8]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 나트륨벤토나이트 2g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 2 g of sodium bentonite was additionally added to the rubberized asphalt mixture.

[실시예 9][Example 9]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 피로인산칼슘 1g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 1 g of calcium pyrophosphate was additionally added to the rubberized asphalt mixture.

[실시예 10][Example 10]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 수산화리튬 2g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 2 g of lithium hydroxide was additionally added to the rubberized asphalt mixture.

[실시예 11][Example 11]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 소듐헥사메타포스페이트 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of sodium hexametaphosphate was additionally added to the rubberized asphalt mixture.

[실시예 12][Example 12]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 코코베타인 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of cocobetaine was additionally added to the rubberized asphalt mixture.

[실시예 13][Example 13]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 초산비닐-말레인산디에틸 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of diethyl vinyl acetate-maleate was additionally added to the rubberized asphalt mixture.

[실시예 14][Example 14]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 평균분자량이 약 200Da인 옥틸트리에톡시실란 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of octyltriethoxysilane having an average molecular weight of about 200 Da was additionally added to the rubberized asphalt mixture.

[실시예 15][Example 15]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 스멕타이트 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of smectite was additionally added to the rubberized asphalt mixture.

[실시예 16][Example 16]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 황화코발트 2g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 2 g of cobalt sulfide was additionally added to the rubberized asphalt mixture.

[실시예 17][Example 17]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 알긴산 나트륨 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of sodium alginate was additionally added to the rubberized asphalt mixture.

[실시예 18][Example 18]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 알루민산스트론튬 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of strontium aluminate was additionally added to the rubberized asphalt mixture.

[실시예 19][Example 19]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 글루코노락톤 2g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 2 g of gluconolactone was added to the rubberized asphalt mixture.

[실시예 20][Example 20]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 로진산 나트륨 2g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 2 g of sodium rosinate was additionally added to the rubberized asphalt mixture.

[실시예 21][Example 21]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 평균입도가 3㎛인 제올라이트 미분말 1g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 1 g of zeolite fine powder having an average particle size of 3 μm was additionally added to the rubberized asphalt mixture.

[실시예 22][Example 22]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 하이드록시탄산마그네슘 1g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 1 g of magnesium hydroxycarbonate was additionally added to the rubberized asphalt mixture.

[실시예 23][Example 23]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 탄산아파타이트 1g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 1 g of carbonated apatite was additionally added to the rubberized asphalt mixture.

[실시예 24][Example 24]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 징크옥사이드 1g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 1 g of zinc oxide was additionally added to the rubberized asphalt mixture.

[실시예 25][Example 25]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 사포나이트 3g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 3 g of saponite was additionally added to the rubberized asphalt mixture.

[실시예 26][Example 26]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 아세틸레이티드라놀란 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of acetylated dranolane was additionally added to the rubberized asphalt mixture.

[실시예 27][Example 27]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 평균입도가 3㎛인 맥반석 미분말 3g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 3 g of fine powdered slate having an average particle size of 3 μm was additionally added to the rubberized asphalt mixture.

[실시예 28][Example 28]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 티탄산칼륨 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of potassium titanate was additionally added to the rubberized asphalt mixture.

[실시예 29][Example 29]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 산화제일구리 1g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 1 g of cupric oxide was additionally added to the rubberized asphalt mixture.

[실시예 30][Example 30]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 불화바륨 5g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 5 g of barium fluoride was additionally added to the rubberized asphalt mixture.

[실시예 31][Example 31]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 페로니켈 슬래그 4g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 4 g of ferronickel slag was additionally added to the rubberized asphalt mixture.

[실시예 32][Example 32]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 염기성 탄산구리 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of basic copper carbonate was additionally added to the rubberized asphalt mixture.

[실시예 33][Example 33]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 2-하이드록시에틸 아크릴레이트 3g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 3 g of 2-hydroxyethyl acrylate was additionally added to the rubberized asphalt mixture.

[실시예 34][Example 34]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 두랄루민 3g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 3 g of duralumin was added to the rubberized asphalt mixture.

[실시예 35][Example 35]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 디펜타에리트올 헥사아크릴레이트 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of dipentaerythritol hexaacrylate was additionally added to the rubberized asphalt mixture.

[실시예 36][Example 36]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 2,2,4-트리메틸-1,2-디하이드로퀴논 1g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 1 g of 2,2,4-trimethyl-1,2-dihydroquinone was additionally added to the rubberized asphalt mixture.

[실시예 37][Example 37]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 글리세린 모노스테아레이트 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of glycerin monostearate was additionally added to the rubberized asphalt mixture.

[실시예 38][Example 38]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 폴리에톡실레이티드 탈로우아민 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of polyethoxylated tallowamine was additionally added to the rubberized asphalt mixture.

[실시예 39][Example 39]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 톨유 지방산 3g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 3 g of tall oil fatty acid was additionally added to the rubberized asphalt mixture.

[실시예 40][Example 40]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 25℃에서 점도가 약 1,400cps인 스티렌-부타디엔 고무 라텍스 2g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 2 g of styrene-butadiene rubber latex having a viscosity of about 1,400 cps at 25°C was additionally added to the rubberized asphalt mixture.

[실시예 41][Example 41]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 디포타슘글리시리제이트 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of dipotassium glycyrrhizate was additionally added to the rubberized asphalt mixture.

[실시예 42][Example 42]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 콜레마나이트 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of colemanite was additionally added to the rubberized asphalt mixture.

[실시예 43][Example 43]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 티오아세트아미드 2g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 2 g of thioacetamide was additionally added to the rubberized asphalt mixture.

[실시예 44][Example 44]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 테크라하이드로커큐민 1g을 더 부가하여 실시하였다.The same method as Example 1 was performed, but 1 g of tetrahydrocurcumin was additionally added to the rubberized asphalt mixture.

[실시예 45][Example 45]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 규불화마그네슘 2g을 더 부가하여 실시하였다.The same method as Example 1 was used, but 2 g of magnesium silicofluoride was additionally added to the rubberized asphalt mixture.

[실시예 46][Example 46]

실시예 1과 동일한 방법으로 실시하되, 고무화 아스팔트 혼합물에 실시예 2 내지 실시예 45에 따라 부가된 부가물을 모두 더 부가하여 실시하였다.The same method as Example 1 was performed, but all additives added according to Examples 2 to 45 were further added to the rubberized asphalt mixture.

[실 험][Experiment]

실시예에 따라 제조된 고무화 아스팔트계 일체부착형 방수시트를 7일 동안 상온에서 대기 방치 후, 방수성, KSF 2561 부착강도시험, KS F 2429 마모저항시험, KS F 2221 내충격성시험방법 등에 따라 시험하고, 그 측정결과를 표 1로 나타냈다.The rubberized asphalt-based integrally bonded waterproofing sheet manufactured according to the example was left at room temperature for 7 days, and then tested for waterproofness, KSF 2561 bond strength test, KS F 2429 abrasion resistance test, and KS F 2221 impact resistance test methods, and the measurement results are shown in Table 1.

방수성(%)Waterproofness (%) 부착강도(N/mm2)Bond strength (N/mm 2 ) 내충격성Impact resistance 내마모성(mg/mm2)Wear resistance (mg/mm 2 ) 실시예 1Example 1 100100 1.851.85 벗겨짐 없음No peeling 0.130.13 실시예 2Example 2 100100 1.831.83 벗겨짐 없음No peeling 0.110.11 실시예 3Example 3 100100 1.851.85 벗겨짐 없음No peeling 0.150.15 실시예 4Example 4 100100 1.861.86 벗겨짐 없음No peeling 0.140.14 실시예 5Example 5 100100 1.861.86 벗겨짐 없음No peeling 0.120.12 실시예 6Example 6 100100 1.911.91 벗겨짐 없음No peeling 0.150.15 실시예 7Example 7 100100 1.851.85 벗겨짐 없음No peeling 0.120.12 실시예 8Example 8 100100 1.831.83 벗겨짐 없음No peeling 0.140.14 실시예 9Example 9 100100 1.891.89 벗겨짐 없음No peeling 0.130.13 실시예 10Example 10 100100 1.901.90 벗겨짐 없음No peeling 0.140.14 실시예 11Example 11 100100 1.891.89 벗겨짐 없음No peeling 0.120.12 실시예 12Example 12 100100 1.871.87 벗겨짐 없음No peeling 0.160.16 실시예 13Example 13 100100 1.881.88 벗겨짐 없음No peeling 0.130.13 실시예 14Example 14 100100 1.851.85 벗겨짐 없음No peeling 0.120.12 실시예 15Example 15 100100 1.891.89 벗겨짐 없음No peeling 0.130.13 실시예 16Example 16 100100 1.871.87 벗겨짐 없음No peeling 0.110.11 실시예 17Example 17 100100 1.841.84 벗겨짐 없음No peeling 0.160.16 실시예 18Example 18 100100 1.831.83 벗겨짐 없음No peeling 0.140.14 실시예 19Example 19 100100 1.951.95 벗겨짐 없음No peeling 0.130.13 실시예 20Example 20 100100 1.891.89 벗겨짐 없음No peeling 0.140.14 실시예 21Example 21 100100 1.911.91 벗겨짐 없음No peeling 0.110.11 실시예 22Example 22 100100 1.871.87 벗겨짐 없음No peeling 0.130.13 실시예 23Example 23 100100 1.881.88 벗겨짐 없음No peeling 0.190.19 실시예 24Example 24 100100 1.851.85 벗겨짐 없음No peeling 0.150.15 실시예 25Example 25 100100 1.861.86 벗겨짐 없음No peeling 0.160.16 실시예 26Example 26 100100 1.841.84 벗겨짐 없음No peeling 0.140.14 실시예 27Example 27 100100 1.861.86 벗겨짐 없음No peeling 0.170.17 실시예 28Example 28 100100 1.891.89 벗겨짐 없음No peeling 0.150.15 실시예 29Example 29 100100 1.861.86 벗겨짐 없음No peeling 0.120.12 실시예 30Example 30 100100 1.881.88 벗겨짐 없음No peeling 0.130.13 실시예 31Example 31 100100 1.851.85 벗겨짐 없음No peeling 0.120.12 실시예 32Example 32 100100 1.891.89 벗겨짐 없음No peeling 0.110.11 실시예 33Example 33 100100 1.941.94 벗겨짐 없음No peeling 0.150.15 실시예 34Example 34 100100 1.871.87 벗겨짐 없음No peeling 0.160.16 실시예 35Example 35 100100 1.871.87 벗겨짐 없음No peeling 0.160.16 실시예 36Example 36 100100 1.851.85 벗겨짐 없음No peeling 0.180.18 실시예 37Example 37 100100 1.881.88 벗겨짐 없음No peeling 0.140.14 실시예 38Example 38 100100 1.861.86 벗겨짐 없음No peeling 0.130.13 실시예 39Example 39 100100 1.871.87 벗겨짐 없음No peeling 0.120.12 실시예 40Example 40 100100 1.881.88 벗겨짐 없음No peeling 0.130.13 실시예 41Example 41 100100 1.901.90 벗겨짐 없음No peeling 0.150.15 실시예 42Example 42 100100 1.911.91 벗겨짐 없음No peeling 0.140.14 실시예 43Example 43 100100 1.851.85 벗겨짐 없음No peeling 0.150.15 실시예 44Example 44 100100 1.851.85 벗겨짐 없음No peeling 0.150.15 실시예 45Example 45 100100 1.871.87 벗겨짐 없음No peeling 0.160.16 실시예 46Example 46 100100 1.861.86 벗겨짐 없음No peeling 0.170.17

표 1에 나타낸 바와 같이, 본 발명에 따른 실시예들에 따라 제조한 고무화 아스팔트계 일체부착형 방수시트는 방수성이 좋고, 부착강도, 내충격성 및 내마모성이 좋은 것으로 나타났다.As shown in Table 1, the rubberized asphalt-based integrally bonded waterproofing sheet manufactured according to the examples of the present invention was found to have good waterproofing properties, bonding strength, impact resistance, and wear resistance.

이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.As described above, those skilled in the art will understand that the present invention can be implemented in other specific forms without changing the technical idea or essential characteristics thereof. Therefore, it should be understood that the embodiments described above are all exemplary and not restrictive. The scope of the present invention should be interpreted that all changes or modifications derived from the meaning and scope of the claims described below and their equivalent concepts, rather than the detailed description above, are included in the scope of the present invention.

Claims (5)

플라스틱 필름 기재층; 및
상기 플라스틱 필름 기재층의 일측면에 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 30중량부, 폴리부텐 1 내지 30중량부, 탄산칼슘 1 내지 10중량부, 점착부여제 1 내지 10중량부, 상용화제 1 내지 5중량부, 흐름방지제 0.1 내지 2중량부 박리방지제 0.1 내지 2중량부, 및 산화방지제 0.1 내지 2중량부를 포함하는 고무화 아스팔트 혼합물에, 티타늄옥사이드를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하고, 테트라에틸오소실리케이트를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하며, 퍼플루오로메톡시실란을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하고, 수산화리튬을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 소듐헥사메타포스페이트를 아스팔트 100중량부 기준으로 1 내지 10중량부로 더 포함하고, 코코베타인을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 스멕타이트를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하고, 글루코노락톤을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 로진산 나트륨을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하고, 산화제일구리를 아스팔트 100중량부 기준으로 0.1 내지 2중량부로 더 포함하며, 2-하이드록시에틸 아크릴레이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 두랄루민을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하는 고무화 아스팔트 혼합물을 적층한 고무화 아스팔트층을 포함하는 고무화 아스팔트계 일체부착형 방수시트.
Plastic film substrate layer; and
A rubberized asphalt mixture comprising, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene isoprene styrene, 1 to 30 parts by weight of polybutene, 1 to 10 parts by weight of calcium carbonate, 1 to 10 parts by weight of an adhesive, 1 to 5 parts by weight of a compatibilizer, 0.1 to 2 parts by weight of an anti-flow agent, 0.1 to 2 parts by weight of an anti-stripping agent, and 0.1 to 2 parts by weight of an antioxidant on one side of the plastic film substrate layer, further comprising 1 to 3 parts by weight of titanium oxide based on 100 parts by weight of asphalt, 1 to 3 parts by weight of tetraethyl orthosilicate based on 100 parts by weight of asphalt, 1 to 3 parts by weight of perfluoromethoxysilane based on 100 parts by weight of asphalt, 1 to 5 parts by weight of lithium hydroxide based on 100 parts by weight of asphalt, and sodium hexametaphosphate. A rubberized asphalt-based integrally bonded waterproofing sheet comprising a rubberized asphalt layer laminated with a rubberized asphalt mixture, further comprising 1 to 10 parts by weight of asphalt, further comprising cocobetaine in an amount of 1 to 5 parts by weight based on 100 parts by weight of asphalt, further comprising smectite in an amount of 0.1 to 3 parts by weight based on 100 parts by weight of asphalt, further comprising gluconolactone in an amount of 1 to 5 parts by weight based on 100 parts by weight of asphalt, further comprising sodium rosinate in an amount of 1 to 3 parts by weight based on 100 parts by weight of asphalt, further comprising cuprous oxide in an amount of 0.1 to 2 parts by weight based on 100 parts by weight of asphalt, further comprising 2-hydroxyethyl acrylate in an amount of 1 to 5 parts by weight based on 100 parts by weight of asphalt, and further comprising duralumin in an amount of 1 to 5 parts by weight based on 100 parts by weight of asphalt.
 삭제delete 삭제delete 삭제delete 시공할 대상면을 정리하는 정리단계;
상기 정리단계가 종료된 시공면에 프라이머를 도포하는 프라이머 도포단계;
상기 프라이머 도포단계가 종료된 시공면에 플라스틱 필름 기재층 및 상기 플라스틱 필름 기재층의 일측면에 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 30중량부, 폴리부텐 1 내지 30중량부, 탄산칼슘 1 내지 10중량부, 점착부여제 1 내지 10중량부, 상용화제 1 내지 5중량부, 흐름방지제 0.1 내지 2중량부 박리방지제 0.1 내지 2중량부, 및 산화방지제 0.1 내지 2중량부를 포함하는 고무화 아스팔트 혼합물에, 티타늄옥사이드를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하고, 테트라에틸오소실리케이트를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하며, 퍼플루오로메톡시실란을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하고, 수산화리튬을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 소듐헥사메타포스페이트를 아스팔트 100중량부 기준으로 1 내지 10중량부로 더 포함하고, 코코베타인을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 스멕타이트를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하고, 글루코노락톤을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 로진산 나트륨을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하고, 산화제일구리를 아스팔트 100중량부 기준으로 0.1 내지 2중량부로 더 포함하며, 2-하이드록시에틸 아크릴레이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 두랄루민을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하는 고무화 아스팔트 혼합물을 적층한 고무화 아스팔트층을 포함하는 고무화 아스팔트계 일체부착형 방수시트를 부착하는 방수시트 부착단계: 및
상기 방수시트 부착단계가 종료된 고무화 아스팔트계 일체부착형 방수시트 상면에 보호재를 부착하는 보호재 부착단계를 포함하는 고무화 아스팔트계 일체부착형 방수시트 시공방법.The preparation stage of organizing the surface to be constructed;
Primer application step of applying a primer to the construction surface where the above organizing step has been completed;
A rubberized asphalt mixture comprising, on a construction surface where the primer coating step is completed, a plastic film substrate layer and, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene isoprene styrene, 1 to 30 parts by weight of polybutene, 1 to 10 parts by weight of calcium carbonate, 1 to 10 parts by weight of an adhesive, 1 to 5 parts by weight of a compatibilizer, 0.1 to 2 parts by weight of an anti-flow agent, 0.1 to 2 parts by weight of an anti-stripping agent, and 0.1 to 2 parts by weight of an antioxidant, further comprising 1 to 3 parts by weight of titanium oxide based on 100 parts by weight of asphalt, 1 to 3 parts by weight of tetraethyl orthosilicate based on 100 parts by weight of asphalt, 1 to 3 parts by weight of perfluoromethoxysilane based on 100 parts by weight of asphalt, and 1 to 2 parts by weight of lithium hydroxide based on 100 parts by weight of asphalt, A waterproofing sheet for attaching a rubberized asphalt-based integrally bonded waterproofing sheet including a rubberized asphalt layer laminated with a rubberized asphalt mixture, wherein the rubberized asphalt mixture further comprises 5 parts by weight of sodium hexametaphosphate, 1 to 10 parts by weight based on 100 parts by weight of asphalt, 1 to 5 parts by weight of cocobetaine based on 100 parts by weight of asphalt, 0.1 to 3 parts by weight of smectite based on 100 parts by weight of asphalt, 1 to 5 parts by weight of gluconolactone based on 100 parts by weight of asphalt, 1 to 3 parts by weight of sodium rosinate based on 100 parts by weight of asphalt, 0.1 to 2 parts by weight of cuprous oxide based on 100 parts by weight of asphalt, 1 to 5 parts by weight of 2-hydroxyethyl acrylate based on 100 parts by weight of asphalt, and 1 to 5 parts by weight of duralumin based on 100 parts by weight of asphalt. Attachment Step: And
A method for constructing a rubberized asphalt-based integrally bonded waterproofing sheet, comprising a step of attaching a protective material to the upper surface of a rubberized asphalt-based integrally bonded waterproofing sheet after the above waterproofing sheet attachment step has been completed.
KR1020240095389A 2024-07-19 2024-07-19 Rubberized Asphalt-Based Integrated Waterproof Sheet and Construction methods Using Thereof Active KR102755616B1 (en)