KR20200060075A - 하이브리드 젤네일 폴리쉬 조성물 - Google Patents

하이브리드 젤네일 폴리쉬 조성물 Download PDF

Info

Publication number
KR20200060075A
KR20200060075A KR1020180145569A KR20180145569A KR20200060075A KR 20200060075 A KR20200060075 A KR 20200060075A KR 1020180145569 A KR1020180145569 A KR 1020180145569A KR 20180145569 A KR20180145569 A KR 20180145569A KR 20200060075 A KR20200060075 A KR 20200060075A
Authority
KR
South Korea
Prior art keywords
gel
polish
parts
weight
nail
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
KR1020180145569A
Other languages
English (en)
Inventor
송하경
Original Assignee
주식회사모나미
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사모나미 filed Critical 주식회사모나미
Priority to KR1020180145569A priority Critical patent/KR20200060075A/ko
Publication of KR20200060075A publication Critical patent/KR20200060075A/ko
Ceased legal-status Critical Current

Abstract

본 발명은 하이브리드 젤네일 폴리쉬 조성물에 관한 것으로, 보다 상세하게는 수성 베이스 코트 상에 UV 컬러젤 폴리쉬와 UV 탑젤 폴리쉬를 형성함으로써 손톱에 손상을 주지 않으며, 유지력 광택력, 지속성 및 워터 프루프 기능이 우수한 하이브리드 젤네일 폴리쉬 조성물에 관한 것이다.

Description

하이브리드 젤네일 폴리쉬 조성물{Hybrid gel nail polish composition}
본 발명은 하이브리드 젤네일 폴리쉬 조성물에 관한 것으로, 보다 상세하게는 수성 베이스 코트 상에 UV 컬러젤 폴리쉬와 UV 탑젤 폴리쉬가 형성된 하이브리드 젤네일 폴리쉬 조성물에 관한 것이다.
젤네일 폴리쉬는 시장에 나온지 얼마 되지 않았으나 단시간에 미용실의 네일아트 애호가들에게 큰 인기를 끌고 있다. 인기 있는 젤네일 폴리쉬 중 하나는 소프트 젤 폴리쉬(soft gel polish)로, 이들은 종종 쏙오프 젤 폴리쉬(soak off gel polish)로도 불린다. 최근 시중에 나와 있는 쏙오프 젤 폴리쉬 제품은 네일에 도포 후에 오래 지속되며 항상 새것처럼 보이는데, 이러한 쏙오프 젤 폴리쉬는 보통 2주 내지 3주 손상 없이 지속되면서도, 마치 방금 시술한 것처럼 보인다. 또한, 사용자는 쏙오프 젤 폴리쉬를 자연 손톱에 직접 용이하게 시술함으로써, 네일 익스텐션(nail extension)을 할 수 있고, 쏙오프 젤 네일 상에 전통적인 네일 폴리쉬를 직접 도포함으로써, 쏙오프 젤 네일의 색상도 용이하게 변경할 수 있도록 구성된다.
따라서, 사용자는 우선 그들의 네일 상에 쏙오프 기반 코팅을 첫번째 층으로 도포한 다음, 그 위에 적어도 한 층의 쏙오프 젤 네일 폴리쉬를 제2층 또는 제3층으로 도포할 필요가 있다. 따라서, 사용자는 최상단 네일 폴리쉬를 제3층 또는 제4층 상에 도포할 필요가 있다. 특히, 네일 상에 도포된 각 층의 건조를 위해서는, 네일을 LED 광이나 UV 광에 노출시켜야 한다. 즉, 네일 상의 각 층을 자연광(햇빛)으로 건조할 수 없기 때문에, 사용자는 LED 광이나 UV 광을 별도로 준비 및 구매해야 하고, 따라서 불편할 뿐더러 비용이 낭비되는 문제가 있다. 또한, 각 층의 건조 후, 일부 습하고 끈적한 콜로이드(colloid)가 층 상에 잔류하기 때문에, 사용자는 알콜을 사용하여 이러한 각 층 상에 잔류하는 이러한 콜로이드를 제거한 다음, 후속 층을 도포하고 각 층의 광택 작업을 수행하도록 구성되어야 한다. 따라서, 사용자는 쏙오프 젤네일 폴리쉬 도포 시간, 건조 시간 및 잔류물 제거 시간을 포함하여 적어도 60분을 소비하여야만 4개층으로 구성된 쏙오프 젤 폴리쉬 구조를 완성할 수 있다.
또한, 쏙오프 젤네일의 제거 공정은 매우 불편하고 까다롭다. 쏙오프 젤 폴리쉬의 구조(적어도 3개층 보유)는 단단하기 때문에, 네일 폴리쉬 세정제로 적신 수건, 천 또는 티슈를 사용하여 직접 소제할 수 없으므로, 사용자는 약솜(cotton balls)을 네일 폴리쉬 세정제에 흠뻑 적신 후, 솜이 네일 전체 표면에 닿을 때까지 이들을 각 네일 상에 배치한 다음, 알루미늄 포일을 사용하여 약솜이 네일 상에 견고히 부착할 때까지 손가락 끝 주위를 묶도록 구성된다. 각각의 쏙오프 젤 폴리쉬 층 생성에는 기본적으로, 5 내지 7분간의 대기가 필요하며, 그런 다음 사용자는 큐티클 푸셔(cuticle pusher)나 아이언 푸셔(iron pusher)를 사용하여 네일로부터 쏙오프 젤 폴리쉬 층을 제거할 수 있다. 또한, 쏙오프 젤 폴리쉬 층을 네일에서 각각 제거할 때 일부 잔류 젤이 네일 상에 남기 때문에, 사용자는 네일 파일(nail file)이나 네일 버퍼(nail buffer)를 사용하여 이러한 잔류물을 네일로부터 완전히 제거해야 한다. 이러한 제거 공정(네일로부터 쏙오프 젤 폴리쉬 층의 제거)을 위해, 사용자는 적어도 30분을 소비해야 하며, 이 외에도 네일 파일이나 네일 버퍼의 자주 사용에 의해 손톱이 손상되고, 손톱의 유수분발란스를 무너뜨려 이로인해 손톱의 두께 감소와 심각한 피해 등이 발생한다.
국내공개특허 제10-2017-0026283호
상기와 같은 종래기술의 문제점을 해결하고자, 본 발명은 손톱에 손상을 주지 않으며 건강한 손톱을 만들기 위해 베이스 코트는 수성 네일로 하고, 발색 및 표현방식과 광택력, 유지력, 지속성 및 워터 프루프 기능을 부여한 컬러 코트 및 탑 코트는 UV 젤 폴리쉬로 하는 하이브리드 젤네일 폴리쉬 조성물을 제공하는 것을 목적으로 한다.
또한 본 발명은 손톱에 수분 및 영양성분을 공급하여 유수분발란스 맞춘 건강한 손톱을 유지할 수 있는 하이브리드 젤네일 폴리쉬 조성물 및 하이브리드 젤네일 폴리쉬의 사용방법을 제공하는 것을 목적으로 한다.
또한 본 발명은 유독한 화학약품을 사용(soak off)하지 않고도 손으로 뜯어내는 방식(peel off) 으로 쉽고 간단하게 UV 젤을 제거할 수 있는 하이브리드 젤네일 폴리쉬 조성물 및 하이브리드 젤네일 폴리쉬의 사용방법을 제공하는 것을 목적으로 한다.
상기 목적을 달성하기 위하여, 본 발명은 아크릴레이트 코폴리머류, 폴리우레탄류 및 아크릴레이트/폴리우레탄 코폴리머 중 선택된 어느 하나 이상의 폴리머를 주성분으로 하는 수성 베이스 코트; 및 아크릴레이트 코폴리어, 우레탄/메타크릴레이트 코폴리머 및 우레탄 코폴리머 중 선택된 어느 하나 이상의 올리고머를 주성분으로 하는 UV 컬러젤/UV 탑젤 폴리쉬(UV color gel/UV top gel polich);를 포함하되, 상기 UV 컬러젤 폴리쉬 또는 UV 탑젤 폴리쉬에는 2종 이상의 광개시제 또는 가교촉진제가 포함되는 하이브리드 젤네일 폴리쉬 조성물을 제공한다.
또한 본 발명은 a)네일에 제1항 기재의 수성 베이스 코트를 도포하는 단계; b)상기 도포된 수성 베이스 코트를 공기 중에서 건조시키는 단계; c)상기 도포된 수성 베이스 코트 상에 UV 컬러젤 폴리쉬를 도포하는 단계; d)상기 도포된 UV 컬러젤 폴리쉬에 UV 조사함으로써 가교시켜 컬러젤 폴리쉬층을 형성하는 단계; e)상기 도포된 컬러젤 폴리쉬층 상에 UV 탑젤 폴리쉬를 도포하는 단계; f)상기 도포된 UV 탑젤 폴리쉬에 UV 조사함으로써 가교시켜 젤네일 폴리쉬층을 형성하는 단계; 및 g)상기 젤네일 폴리쉬층을 필 오프(peel off)하여 제거하는 단계;를 포함하는 하이브리드 젤네일 폴리쉬의 사용방법을 제공한다.
본 발명의 하이브리드 젤네일 폴리쉬 조성물은 손톱에 손상을 주지 않으며 건강한 손톱을 만들기 위해 베이스 코트는 수성 네일로 하고, 컬러 코트 및 탑 코트는 발색 및 표현방식과 광택력, 유지력, 지속성 및 워터 프루프 기능을 부여한 UV 젤 폴리쉬로 함으로써 손톱에 수분 및 영양성분을 공급하여 유수분발란스 맞춘 건강한 손톱을 유지할 수 있다.
또한 본 발명의 하이브리드 젤네일 폴리쉬 조성물은 수성 베이스 코트 위에 UV 컬러 젤과 UV 탑 젤이 형성되어 있으므로 유독한 화학약품을 사용(soak off)하지 않고도 손으로 뜯어내는 방식(peel off) 으로 쉽고 간단하게 UV 젤을 제거할 수 있다.
도 1은 본 발명의 일실시예에 따라 제조한 하이브리드 젤네일 폴리쉬가 네일 상에 도포된 후 수분 및 영양성분의 공급을 나타낸 모식도(DDS 개념 포함, 물질전달 농도에 대한 확산, Frick's 2법칙)이다.
도 2는 본 발명의 일실시예에 따라 제조한 하이브리드 젤네일 폴리쉬를 사용하여 네일 상에 도포하고 제거하는 일련의 과정을 나타낸 공정도이다.
도 3은 UV 베이스 코트를 사용하는 통상의 UV 젤네일 폴리쉬를 사용하여 네일 상에 도포하고 제거하는 일련의 과정을 나타낸 공정도이다.
도 4는 본 발명의 일실시예에 따라 제조한 하이브리드 젤네일 폴리쉬와 통상의 UV 젤네일 폴리쉬를 도포하고, 도포 2주 후 젤네일 폴리쉬를 제거한 후의 네일 상태를 나타낸 도이다.
이하 본 발명을 상세히 설명한다.
본 발명은 아크릴레이트 코폴리머류, 폴리우레탄류 및 아크릴레이트/폴리우레탄 코폴리머 중 선택된 어느 하나 이상의 폴리머를 주성분으로 하는 수성 베이스 코트; 및 아크릴레이트 코폴리어, 우레탄/메타크릴레이트 코폴리머 및 우레탄 코폴리머 중 선택된 어느 하나 이상의 올리고머를 주성분으로 하는 UV 컬러젤/UV 탑젤 폴리쉬(UV color gel/UV top gel polich);를 포함하되, 상기 UV 컬러젤 폴리쉬 또는 UV 탑젤 폴리쉬에는 2종 이상의 광개시제 또는 가교촉진제가 포함되는 하이브리드 젤네일 폴리쉬 조성물을 제공한다.
본 발명의 수성 베이스 코트를 이루는 폴리머는 아크릴레이트폴리머, 스티렌/아크릴레이트코폴리머, 아크릴레이트/에틸헥실아크릴레이트코폴리머, 스티렌/아크릴레이트/암모니움메타크릴레이트코폴리머, 암모니움/아크릴레이트코폴리머 등의 아크릴레이트 코폴리머류, 폴리우레탄(PUD 포함)류, 아크릴레이트/폴리우레탄 코폴리머(AUD 포함) 등을 1종 이상 혼합하여 사용할 수 있다. 이때, 상기 폴리머는 수성 베이스 코트 총 100중량부에 대하여 60~90중량부로 포함될 수 있다.
또한 상기 수성 베이스 코트에는 점증제, 레벨링제, 광택제, 소포제, 워터 프루프 강화제, 속건제, 충진제 등을 더 포함할 수 있다.
상기 점증제로는 잔탄, 말토덱스트린, 구아검, 로커스트콩검, 카라기난, 알긴, 곤약검, 카제인산 나트륨 등과 아크릴레이트코폴리머, 아크릴릭 산, 카보머 등이 사용될 수 있으며, 수성 베이스 코트 총 100중량부에 대하여 0.2~3중량부로 포함될 수 있다.
상기 레벨링제로는 디프로필렌글리콜 메틸에테르, 디프로필렌글리콜 에틸에테르, 디프로필렌글리콜 부틸에테르, 디프로필렌글리콜 프로필에테르, 프로필렌글리콜 메틸에테르, 프로필렌글리콜 에틸에테르, 프로필렌글리콜 부틸에테르, 프로필렌글리콜 프로필에테르, 설포숙시네이트(sulfosuccianate), 스테비오사이드, 글루코실 스테비오사이드 등의 표면장력을 저하시킬 수 있는 것을 사용할 수 있으며, 수성 베이스 코트 총 100중량부에 대하여 0.5~7중량부로 포함될 수 있다.
상기 광택제로는 스테비오사이드 글루코실 스테비오사이드, 감초 추출물, 슈크로오즈, 디프로필렌글리콜 메틸에테르, 디프로필렌글리콜 부틸에테르 등이 사용될 수 있으며, 수성 베이스 코트 총 100중량부에 대하여 1~8중량부로 포함될 수 있다.
상기 소포제는 폴리머류, 알코올류, 미네랄오일류, 시메티콘, 디메티콘 등이 사용될 수 있으며, 수성 베이스 코트 총 100중량부에 대하여 0.3~3중량부로 포함될 수 있다.
상기 워터 프루프 강화제는 디프로필렌글리콜디벤조에이트, 프로필렌글리콜디벤조에이트, 프로필렌글리콜벤조에이트 등이 사용될 수 있으며, 수성 베이스 코트 총 100중량부에 대하여 0.5~7중량부로 포함될 수 있다.
상기 속건제는 프로필렌글리콜 메틸에테르, 프로필렌글리콜 에틸에테르, 프로필렌글리콜 부틸에테르, 프로필렌글리콜 프로필에테르 등이 사용될 수 있으며, 수성 베이스 코트 총 100중량부에 대하여 1~6중량부로 포함될 수 있다.
상기 충진제로는 안티케이킹, 프리플로우, 겔링, 서스펜딩, 교반력, 틱소성, 점도상승 등의 용도로, 벤토나이트, 헥토라이트, 스테아랄코늄헥토라이트, 실리카, 실리카디메틸실리케이트, 리튬마그네슘소듐실리케이트, 테트라소듐피로포스페이트 등이 사용될 수 있으며, 수성 베이스 코트 총 100중량부에 대하여 0.1~5중량부로 포함될 수 있다.
상기와 같은 수성 베이스 코트는 수성 기반 네일 폴리쉬(water based nail polish)로, 네일에 바로 도포되어도 네일의 유수분발란스를 맞추어 주며, 네일에 손상을 주지 않으며 건강한 손톱을 유지할 수 있다.
또한 본 발명은 상기 수성 베이스 코트 상에 컬러 코트(color coat)와 탑 코트(top coat)를 UV 젤 폴리쉬(UV gel polish)로 하여 표현하고자 하는 이미지와 발색, 유지력 및 광택력을 높이고, 지속성과 워터 프루프 기능을 부여한다.
상기 UV 컬러젤/UV 탑젤 폴리쉬를 이루는 올리고머는 아크릴레이트 코폴리머, 우레탄/메타크릴레이트 코폴리머, 우레탄 코폴리머 등을 1종 이상 혼합하여 사용할 수 있다. 이때, 상기 올리고머는 UV 컬러젤/UV 탑젤 폴리쉬 총 100중량부에 대하여 45~70중량부로 포함될 수 있다.
또한 상기 UV 컬러젤/UV 탑젤 폴리쉬에는 2종 이상의 광개시제 및 가교촉진제를 포함한다. 이때, 상기 광개시제 또는 가교촉진제가 UV 컬러젤 폴리쉬에 포함된 경우에는 UV 탑젤 폴리쉬에는 선택하여 포함할 수 있다.
상기 광개시제는 유리기 중합(free radical polymerization)에 참여하는 개시제를 사용할 수 있으며, 구체적으로 α-하이드록시 케톤(alpha-hydroxy ketone)류, 페닐글리옥실레이트(phenylglyoxylate)류, α-아미노 케톤류(alpha-amino ketone)류, 벤질 디메틸 케탈(benzil dimethyl ketal)류, 포스핀 옥사이드(phosphine oxide)류 등이 사용될 수 있다. 그 함량은 UV 컬러젤/UV 탑젤 폴리쉬 총 100중량부에 대하여 2~7중량부로 포함될 수 있다.
상기 가교촉진제는 가교를 촉진시켜 가교 속도를 빠르게 해주는 것으로 가교 시 반응하는 순간의 열로 연속적 가교제의 반응을 연쇄반응이 일어나게 해준다. 그 종류로는 트리에틸아민, 트리에탄올아민, 아미노메틸 프로핀 등의 아민이 포함되어 있는 가교촉진제나, N,N-톨루이딘(N,N-toluidine)과 3-머캅토프로피오네이트(mercaptopropionate)가 작용하여 가교가 촉진되는 트리메틸올프로판 트리스(3-머캅토프로피오네이트)(TMMP, trimethylolpropane tris(3-mercaptopropionate)), 펜타에리트리톨 테트라키스(3-머캅토프로피오네이트)(PEMP, pentaerythritol tetrakis (3-mercaptopropionate)), 디펜타에리트리톨 헥사키스(3-머캅토프로피오네이트)(DPMP, d ipentaerythritol hexakis(3-mercaptopropionate)) 등이 사용될 수 있다. 상기 가교촉진제는 UV 컬러젤/UV 탑젤 폴리쉬 총 100중량부에 대하여 3~5중량부로 포함될 수 있다.
또한 상기 UV 컬러젤/UV 탑젤 폴리쉬에는 희석제, 평활제 및 소포제를 더 포함할 수 있다.
상기 희석제는 모노머 및 용매로 이루어진다.
상기 모노머로는 부틸메타크릴레이트(butyl (meth)acrylate, B(M)A), 2-에틸헥실메타크릴레이트(2-ethylhexyl (meth)acrylate, 2EH(M)A), 옥틸/데실메타크릴레이트(octyl/decyl (meth)acrylate, OD(M)A), 하이드록시알킬메타크릴레이트(hydroxyalkyl (meth)acrylates, 2HE(M)A. 2HP(M)A), 노닐페놀에톡실레이트(nonylphenolethoxylate), β-카르복실에틸메타크릴레이트(ㅯ-carboxylethyl (meth)acrylate, ㅯ-CE(M)A), 모노메타크릴레이트(mono (meth)acrylate, MNPEO(M)A), 이소보닐메타크릴레이트(isobornyl (meth)acrylate, IBO(M)A). 테트라하이드로퍼푸릴메타크릴레이트(tetrahydrofurfuryl (meth)acrylate, THFF(M)A), 시클로헥실메타크릴레이트(cyclohexyl (meth)acrylate, CH(M)A), 디시클로펜테닐메타크릴레이트(dicyclopentenyl (meth)acrylate, DCP(M)A), 디시클로펜테닐옥시에틸메타크릴레이트(dicyclopentenyloxyethyl (meth)acrylate, DCPEO(M)A), 프로필렌글리콜 모노메타크릴레이트(propylene glycol mono(meth)acrylate, MPPG(M)A), 2-(2에톡시에톡시)에틸메타크릴레이트(2-(2-ethoxyethoxy ethyl(meth)acrylate, EOEOEA), 에톡실레이티드 모노메타크릴레이트(ethoxylated mono(meth)acry!ale, EOM(M)A) 등의 1관능기; 부탄디올디메타크릴레이트(butanedioldi(meth)acrylate, BDD(M)A), 1,3-부틸렌글리콜디메타크릴레이트(1.3-butylene glycol dimethacrylate, BGDMA), 1,6-헥산디올 디메타크릴레이트(1.6-hexanediol di(meth)acrylate, HDD(M)A), 디메타크릴레이트(dimethacrylate, HDDMA), 네오페닐 글리콜디메타크릴레이트(neopenthyl glycoldi(meth)acrylate, NPGD(M)A). 에틸렌글리콜 디메타크릴레이트(ethylene glycol dimethacry!ale, EGDMA), 디에틸렌글리콜디메타크릴레이트(diethylene glycol di(meth)acrylate, DEGD(M)A), 트리에틸렌글리콜디메타크릴레이트(triethylene glycol di(meth)acrylate, TEGD(M)A), 테트라에틸렌글리콜 디메타크릴레이트(tetraethylene glycol di(meth)acrylate, TTEGD(M)A), 폴리에틸렌글리콜 디메타크릴레이트(polyethylene glycol di(meth)acrylate, PEGD(M)A), 디프로필렌글리콜 디메타크릴레이트(dipropyleneglycol di(meth)acrylate, DPGD(M)A), 트리프로필렌글리콜 디메타크릴레이트(tripropylene glycol di(meth)acrylate, TPGD(M)A). 디아놀 디메타크릴레이트(dianol di(meth)acrylate, DD(M)A) 등의 2관능기; 트리메틸올프로판 트리메타크릴레이트(trimethylolpropane tri(meth)acrylate, TMPTMA), 펜타에리트리올트리아크릴레이트(pentaerythriloltriacrylate, PETA). 글리세릴프로옥실레이티드아크릴레이트(glycerylpropoxylatedtriacrylate, GPTA) 등의 3관능기; 페닐에리트리올테트라아크릴레이트(penylaerythritoltetraacrylate, TETTA), 디벤타에리트리올펜타아크릴레이트(dipentaerythritolpentaacrylate, DPEPA), 디트리메틸올프로판테트라아크릴레이트(ditrimethylolpropanetetraacrylate, DTMPTTA) 등의 4이상 다관능기 등을 1종 이상 선택하여 사용할 수 있다. 이때, 상기 모노머는 UV 컬러젤/UV 탑젤 폴리쉬 총 100중량부에 대하여 15~45중량부로 포함될 수 있다.
상기 용매로는 알킬아세테이트류, 알코올류, 케톤류 등이 사용될 수 있으며, UV 컬러젤/UV 탑젤 폴리쉬 총 100중량부에 대하여 0.1~10중량부로 포함될 수 있다.
상기 평활제로는 셀룰로오스 아세테이트 부틸레이트, 수크로오스 아세테이트 이소부틸레이트 등이 사용될 수 있으며, UV 컬러젤/UV 탑젤 폴리쉬 총 100중량부에 대하여 1~5중량부로 포함될 수 있다.
상기 소포제로는 폴리머류, 알코올류, 미네랄 오일류, 시메티콘, 디메티콘 등이 사용될 수 있으며, UV 컬러젤/UV 탑젤 폴리쉬 총 100중량부에 대하여 0.3~3중량부로 포함될 수 있다.
또한, 상기 UV 컬러젤 폴리쉬에는 칼라 연출을 위해서 색소, 분산제 및 침강방지제를 더 포함할 수 있다.
상기 색소는 통상 젤 네일에 사용하는 모든 색소가 사용 가능하며, 예를 들어 CI Number 로는 CI 11680, CI 15850, CI 15850:1, CI 19140, CI 45410, CI 47000, CI 49410, CI 77007, CI 77491, CI 77492, CI 77499, CI 77510, 티타늄 디옥사이드(titanium dioxide) 등이 사용될 수 있다. 그 함량은 UV 컬러젤 폴리쉬 총 100중량부에 대하여 0.1~20중량부로 포함될 수 있다.
상기 분산제로는 비수계와 수계가 있으며, UV 컬러젤 폴리쉬에는 비수계의 습윤분산제를 사용하는 것이 좋다. 비수계의 습윤분산제로는 소듐메틸 2-설포라우레이트, 지방족 카르분산 및 염류, 고급알콜 황산에스테르류, 알킨술폰산염류, 알킨인산에스테르류, 폴리에스테르-에스테르카르본산염, 고분자 폴리에스테르 카르분산의 폴리아민 및 지방족 이민염류, 제4급 암모늄염, 긴사슬의 폴리아미노아마이드 및 그 인산염, 긴사슬의 폴리아미노아마이드와 고분자 폴리에스테르산의 중성염 등이 있다. 그 함량은 UV 컬러젤 폴리쉬 총 100중량부에 대하여 0.5~3중량부로 포함될 수 있다.
상기 침강방지제로는 안티케이킹, 프리플로우, 겔링, 서스펜딩, 교반력, 틱소성, 점도상승 등의 용도로 벤토나이트, 헥토라이트, 스테아랄코늄헥토라이트, 실리카, 실리카디메틸실리케이트, 리튬마그네슘소듐실리케이트, 테트라소듐피로포스페이트, 프로필렌카보네이트등이 사용될 수 있다. 그 함량은 UV 컬러젤 폴리쉬 총 100중량부에 대하여 0.1~5중량부로 포함될 수 있다.
또한 본 발명은 상기와 같은 하이브리드 젤네일 폴리쉬의 사용방법을 제공하는 바, 그 방법은 다음과 같다.
a)네일에 상기의 수성 베이스 코트를 도포하는 단계; b)상기 도포된 수성 베이스 코트를 공기 중에서 건조시키는 단계; c)상기 도포된 수성 베이스 코트 상에 UV 컬러젤 폴리쉬를 도포하는 단계; d)상기 도포된 UV 컬러젤 폴리쉬에 UV 조사함으로써 가교시켜 컬러젤 폴리쉬층을 형성하는 단계; e)상기 도포된 컬러젤 폴리쉬층 상에 UV 탑젤 폴리쉬를 도포하는 단계; f)상기 도포된 UV 탑젤 폴리쉬에 UV 조사함으로써 가교시켜 젤네일 폴리쉬층을 형성하는 단계; 및 g)상기 젤네일 폴리쉬층을 필 오프(peel off)하여 제거하는 단계;를 포함한다.
상기 단계 b)의 건조는 공기 중에서 3~5분간 수행되며, 상기 단계 d) 또는 f)의 가교는 UV램프에 2~5분 또는 LED램프에서 15~60초 정도 큐어링하여 수행된다.
전술한 바와 같이 본 발명의 하이브리드 젤네일 폴리쉬는 네일에 바로 도포되는 베이스 코트를 수성 기반 네일 폴리쉬(water based nail polish)로 하여 손톱의 유수분발란스, 수분과 케라틴, 비타민A, 비타민 E 및 그 유도체 등의 영양을 공급(도 1의 모식도 참고)하여 네일에 손상을 주지 않으며 건강한 네일을 유지할 수 있으며, 상기 베이스 코트 상부에는 컬러 코트와 탑 코트를 UV 젤 폴리쉬로 형성함으로써 표현이미지의 구현와 발색, 유지력, 광택력, 지속성, 워터 프루프 기능이 우수하다. 또한 본 발명의 UV 젤 폴리쉬는 완전 가교되어 미경화된 탑젤을 닦을 필요가 없어 화학물질의 사용을 최소화할 수 있고, 수성 베이스 코트를 사용함으로써 유독한 화학약품을 사용(soak off)하지 않고도 손으로 뜯어내는 방식(peel off) 으로 쉽고 간단하게 UV 젤을 제거할 수 있어 네일의 손상을 최소화할 수 있다.
이러한 본 발명의 하이브리드 젤네일 폴리쉬 조성물은 수성 베이스를 사용하여 네일에 수분을 이용하여 접착시키기 때문에 DDS(dug dilivery system)의 개념을 넣는다면 네일 분야의 새로운 트랜드로 나갈뿐만 아니라 손발톱 무좀 및 손발톱이 약한 사람들의 손발톱을 건강하게 유지함과 동시에 아름다움과 개성을 표현할 수 있는 좋은 제품을 개발할 수 있을 것으로 기대된다.
이하에서는 실시예를 들어 본 발명에 관하여 더욱 상세하게 설명할 것이나. 이들 실시예는 단지 설명의 목적을 위한 것으로 본 발명의 보호 범위를 제한하고자 하는 것은 아니다.
실시예 1
하기 표 1에 나타낸 바와 같은 조성으로 실시예 1 및 2와 비교예 1의 젤네일 폴리쉬를 제조하였다.
하기 표 1의 단위는 중량부이다.
실시예 1 실시예 2 실시예 3
수성 베이스 코트 스티렌/아크릴레이트 폴리머 30 25 25
폴리우레탄 20 25 20
아크릴레이트/폴리우레탄 코폴리머 30 30 35
카보머 2 2 2
디프로필렌글리콜 메틸에티르 5.5 5.5 5.5
스테비오사이드글로코실스테비오사이드 5 5 5
시메티콘 1.5 1.5 1.5
프로필렌글리콜벤조에이트 5.5 5.5 5.5
프로필렌글리콜메틸에테르 3 3 3
테트라소듐피로포스페이트 2.5 2.5 2.5
UV 컬러젤 폴리쉬 아크릴레이트 코폴리머 22 27 25
우레탄/메타크릴레이트 코폴리머 20 23 22
우레탄 폴리머 25 24 20
포스파인 옥사이드 5 5 5
α-하이드록시 케톤 2 2 2
트리에틸아민 5 5 5
부틸메타크릴레이트 15 15 15
알킬아세테이트 5 5 5
셀룰로오스 아세테이트 부틸레이트 2 2 2
시메티콘 1 1 1
CI 11680 8 8 8
소듐메틸 2-설포라우레이트 1 1 1
안티케이킹 2 2 2
UV 탑젤 폴리쉬 메타크릴레이트 코폴리어 22 27 25
우레탄/메타크릴레이트 코폴리머 20 23 22
우레탄 폴리머 25 24 20
포스파인 옥사이드 5 5 5
α-하이드록시 케톤 2 2 2
트리에틸아민 - 5 5
부틸메타크릴레이트 15 15 15
알킬아세테이트 5 5 5
셀룰로오스 아세테이트 부틸레이트 2 2 2
시메티콘 1 1 1
비교예 1
우레탄 올리고머 55중량부, 2-하이드옥시에틸에틸렌우레아 모노머 30중량부, 2-하이드록시-2-메틸-1-페닐-1-프로판온 10중량부, 실리콘 5중량부, 안료 10중량부를 혼합하여 UV 베이스 젤을 사용하는 통상의 젤네일 폴리쉬를 제조하였다.
실험예 1
상기 실시예 3 및 비교예 1의 젤네일 폴리쉬를 네일상에 도포 및 제거과정을 각각 도 2 및 도 3에 나타내었으며, 실시예 3 및 비교예 1의 젤네일 폴리쉬를 사용하기 전 후(2주간)의 네일 상태를 관찰하여 도 4에 나타내었다.
도 4에 나타낸 바와 같이, 본 발명에 따른 실시예 3의 하이브리드 젤네일 폴리쉬를 도포한 실험군은 2주간의 사용 전과 2주 후 젤네일 폴리쉬를 제거한 후를 비교하여도 네일의 갈라짐이나 긁힘, 건조함, 두께감의 감소 등이 없이 사용 전의 네일과 거의 유사한 정도의 상태였으나, UV 베이스 젤을 사용하는 비교예 1을 도포한 대조군에서는 쏙오프 방식으로 젤네일을 제거한 후 네일 표면의 갈라짐과 긁힘이 심하게 확인되었으며, 손톱의 두께감 또한 사용 전과 대비하여 확연히 감소되었음을 확인할 수 있었다. 또한 젤네일의 유지력, 광택력, 지속력, 워터 프루프 기능 또한 본 발명의 하이브리드 젤네일 폴리쉬가 비교예 1의 기존 UV 젤네일 폴리쉬와 비교하여 더욱 우수한 성능을 나타냄을 확인할 수 있었다.
이러한 결과로부터 본 발명의 수성 기반 네일 폴리쉬(water based nail polish) 기반의 베이스 코트에 UV 컬러젤/탑젤 폴리쉬를 사용한 하이브리드 젤네일 폴리쉬는 기존 UV 젤네일 폴리쉬와 대비하여 네일의 유수분발란스를 맞춰주고, 수분과 케라틴, 비타민A, 비타민 E 및 그 유도체 등의 영양을 공급하여 네일에 손상을 주지 않으며 건강한 네일을 유지할 수 있음을 확인할 수 있었다. 젤네일의 유지력, 광택력, 지속성, 워터 프루프 기능이 우수함을 확인할 수 있었다.
비록 본 발명이 상기에 언급된 바람직한 실시예로서 설명되었으나, 발명의 요지와 범위로부터 벗어남이 없이 다양한 수정이나 변형을 하는 것이 가능하다. 또한 첨부된 청구 범위는 본 발명의 요지에 속하는 이러한 수정이나 변형을 포함한다.

Claims (7)

  1. 아크릴레이트 코폴리머류, 폴리우레탄류 및 아크릴레이트/폴리우레탄 코폴리머 중 선택된 어느 하나 이상의 폴리머를 주성분으로 하는 수성 베이스 코트; 및
    아크릴레이트 코폴리어, 우레탄/메타크릴레이트 코폴리머 및 우레탄 코폴리머 중 선택된 어느 하나 이상의 올리고머를 주성분으로 하는 UV 컬러젤/UV 탑젤 폴리쉬(UV color gel/UV top gel polich);를 포함하되,
    상기 UV 컬러젤 폴리쉬 또는 UV 탑젤 폴리쉬에는 2종 이상의 광개시제 또는 가교촉진제가 포함되는 하이브리드 젤네일 폴리쉬 조성물.
  2. 제1항에 있어서,
    상기 수성 베이스 코트는 아크릴레이트 코폴리머류, 폴리우레탄류 및 아크릴레이트/폴리우레탄 코폴리머 중 선택된 어느 하나 이상의 폴리머 60~90중량부, 점증제 0.2~3중량부, 레벨링제 0.5~7중량부, 광택제 1~8중량부, 소포제 0.3~3중량부, 워터 프루프 강화제 0.5~7중량부, 속건제 1~6중량부 및 충진제 0.1~5중량부를 포함하는 것을 특징으로 하는 하이브리드 젤네일 폴리쉬 조성물.
  3. 제1항에 있어서,
    상기 UV 컬러젤/UV 탑젤 폴리쉬는 아크릴레이트 코폴리어, 우레탄/메타크릴레이트 코폴리머 및 우레탄 코폴리머 중 선택된 어느 하나 이상의 올리고머 45~70중량부, 희석제로 모노머 15~45중량부 및 솔벤트 0.1~10중량부, 평활제 1~5중량부, 소포제 0.3~3중량부, 가교제 2~7중량부 및 가교촉진제 3~7중량부를 포함하는 것을 특징으로 하는 하이브리드 젤네일 폴리쉬 조성물.
  4. 제3항에 있어서,
    상기 UV 컬러젤 폴리쉬는 색소 0.1~20중량부, 분산제 0.5~3중량부 및 침강방지제 0.1~5중량부를 더 포함하는 것을 특징으로 하는 하이브리드 젤네일 폴리쉬 조성물.
  5. a)네일에 제1항 기재의 수성 베이스 코트를 도포하는 단계;
    b)상기 도포된 수성 베이스 코트를 공기 중에서 건조시키는 단계;
    c)상기 도포된 수성 베이스 코트 상에 UV 컬러젤 폴리쉬를 도포하는 단계;
    d)상기 도포된 UV 컬러젤 폴리쉬에 UV 조사함으로써 가교시켜 컬러젤 폴리쉬층을 형성하는 단계;
    e)상기 도포된 컬러젤 폴리쉬층 상에 UV 탑젤 폴리쉬를 도포하는 단계;
    f)상기 도포된 UV 탑젤 폴리쉬에 UV 조사함으로써 가교시켜 젤네일 폴리쉬층을 형성하는 단계; 및
    g)상기 젤네일 폴리쉬층을 필 오프(peel off)하여 제거하는 단계;
    를 포함하는 하이브리드 젤네일 폴리쉬의 사용방법.
  6. 제5항에 있어서,
    상기 단계 b)의 건조는 공기 중에서 3~5분간 수행되는 것을 특징으로 하는 하이브리드 젤네일 폴리쉬의 사용방법.
  7. 제5항에 있어서,
    상기 단계 d) 또는 f)의 가교는 UV램프에 2~5분 또는 LED램프에서 15~60초 정도 큐어링하여 수행되는 것을 특징으로 하는 하이브리드 젤네일 폴리쉬의 사용방법.
KR1020180145569A 2018-11-22 2018-11-22 하이브리드 젤네일 폴리쉬 조성물 Ceased KR20200060075A (ko)