LU83226A1 - INSULATION OF ELECTRIC CURRENT TRACKS - Google Patents
INSULATION OF ELECTRIC CURRENT TRACKS Download PDFInfo
- Publication number
- LU83226A1 LU83226A1 LU83226A LU83226A LU83226A1 LU 83226 A1 LU83226 A1 LU 83226A1 LU 83226 A LU83226 A LU 83226A LU 83226 A LU83226 A LU 83226A LU 83226 A1 LU83226 A1 LU 83226A1
- Authority
- LU
- Luxembourg
- Prior art keywords
- composition
- filler
- amount
- total weight
- epoxy resin
- Prior art date
Description
1 -2.5¾^1 -2.5¾ ^
> r ! U> r! U
τ -......... // / » Demande de brevet ^ de____/if - 0^· gd / ---- / / 3» / Désignation de i'inventeui/τ -......... // / "Patent application ^ de ____ / if - 0 ^ · gd / ---- / / 3" / Designation of the inventor /
0 Le soussigné .....\ 3r.*s.ï:X VtK ^00 KG0 The undersigned ..... \ 3r. * S.ï: X VtK ^ 00 KG
agissant en qualité de-déposant— de mandataire du dép/6sant — (2j ____________________A G O AT) WG- B>.V. /............................................acting as depositor— agent of the dep / 6sant - (2d ____________________ A G O AT) WG- B> .V. / ............................................
AV-, ArmsKerdat/v^euJeg / __ h%%0 UifViOörn / (3) de l'invention concernant: / ____________________________^sola-h'tjtt o'e rails co/d^ckeM^ de c.àor<zzv\+ ^.l-ecdrifue désigne comme inventeur (s) : / 1. Non, et prénoms WiHfa/-1 Da V,d PA-V'ES_____________________________.________AV-, ArmsKerdat / v ^ euJeg / __ h %% 0 UifViOörn / (3) of the invention relating to: / ____________________________ ^ sola-h'tjtt o'e rails co / d ^ ckeM ^ de c.àor <zzv \ + ^ .l-ecdrifue designates as inventor (s): / 1. No, and first names WiHfa / -1 Da V, d PA-V'ES _____________________________.________
Adresse Çbfi.j?ba.r<£ls, JWavj ^ ^ ôwér S-fa Ko ü ^ Sussec 2. Nom et prénoms.........................Z.......... ^.....................................ZIX * * ΗΤI Ç™àe -BiWafntfAddress Çbfi.j? Ba.r <£ ls, JWavj ^ ^ ôwér S-fa Ko ü ^ Sussec 2. Full name ...................... ... Z .......... ^ ................................... ..ZIX * * ΗΤI Ç ™ àe -BiWafntf
Adresse ......................................../ .....................................................................................................................................................................Address ......................................../ ........ .................................................. .................................................. .................................................. .......
3. Nom et prénoms_______________..Ll...._________________________________________________________________________-..............................................................................................................3. Name and first names _______________ .. Ll ...._________________________________________________________________________-.................................... .................................................. ........................
Adresse __________________________________________________________________________________________________________________________________________________________________________________________________________________________________Address __________________________________________________________________________________________________________________________________________________________________________________________________________________________________
Il affirme la Sincérité des indications susmentionnées et déclare en assumer l'entière responsabilité. /He asserts the Sincerity of the above indications and declares to assume full responsibility for them. /
_____Lvicqw bourg_____|e_____2½ . oi._______________uJJ_____Lvicqw bourg _____ | e _____ 2½. oi ._______________ uJJ
___N-^AiiWtZ___ N- ^ AiiWtZ
: (signature) A 68026___|___ (') Nom, prénoms, firme, adresse.: (signature) A 68026 ___ | ___ (') Last name, first names, company, address.
P) Nom. Drénoms et adresse du dénosanfP) Name. Name and address of the denosanf
JeI
Demande de brevet de.* 18 mars 198 1 Désignation de l'Inventeur 0 Le soussigné jean Waxweiler, 21-25 Allée S chef fer LUXEMBOURG agissant en qualité dexdsposoaic— de mandataire du déposant — 0 SIGMA... CQAT.ING...B _V................................................; ....................................._...........................................Patent application of. * March 18, 198 1 Designation of the Inventor 0 The undersigned jean Waxweiler, 21-25 Allée S chef fer LUXEMBOURG acting as dexdsposoaic— agent of the depositor - 0 SIGMA ... CQAT.ING ... B _V ................................................ ; ....................................._............ ...............................
14, Amsterdamseweg14, Amsterdamseweg
1220 UITHOORN, PAYS-BAS1220 UITHOORN, THE NETHERLANDS
(') de l’invention concernant :(') of the invention relating to:
Isolation de rails conducteurs de courant électrique, désigne comme inventeur (s) :Insulation of electrically conductive rails, designated as inventor (s):
William David DAVIES _ _ ____William David DAVIES _ _ ____
Shepharas «ayShepharas "ay
Lower Station Road f®"1* L°a9e „ .Lower Station Road f® "1 * L ° a9e„.
Newtek East Sussec BN8 4HT Brandbury RoadNewtek East Sussec BN8 4HT Brandbury Road
Grande-Bretagne °xfoJa „ „ » Grande-BretagneGreat Britain ° xfoJa „„ »Great Britain
Mr. R.J. BEAUMONT SpinacresMr. R.J. BEAUMONT Spinacres
Cray Hills-Billericay ,Cray Hills-Billericay,
Essex ' 'Essex ''
Grande-Bretagne iGreat Britain i
Il affirme la sincérité des indications susmentionnées et déclare en assumer I entière responsabilité. La présente désignation de 1’inventeur se substitue à toute désignation de l’inventeur antérieure qu’elle annulle.He affirms the sincerity of the above-mentioned indications and declares to assume full responsibility for them. This designation of the inventor replaces any designation of the previous inventor that it cancels.
Luxembourg ............................., «e -22 3uil 1-et..................— 19....8..2..Luxembourg ............................., "e -22 3uil 1-et ........... .......— 19 .... 8..2 ..
r .......ifatoA..........r ....... ifatoA ..........
(slgnaturei ^ I * ____________________ i , ^ * MEMOIRE DESCRIPTIF déposé à l'appui d'une(slgnaturei ^ I * ____________________ i, ^ * DESCRIPTIVE MEMORY filed in support of a
DEMANDE DE BREVET D'INVENTIONPATENT INVENTION APPLICATION
formée par la Société dite : SIGMA COATINGS B.V.formed by the so-called Company: SIGMA COATINGS B.V.
pourfor
ISOLATION DE RAILS CONDUCTEURS DE COURANT ELECTRIQUEINSULATION OF ELECTRIC CURRENT TRACKS
La présente invention se rapporte à un procédé d'isolation de rails conducteurs de courant électrique, utilisés dans les voies de certains chemins de fer.The present invention relates to a method of insulating conductive rails of electric current, used in the tracks of certain railways.
Un système d'électrification de chemins de fer consiste à utiliser, entre les deux rails usuels, un troisième rail qui sert de con- \ . ducteur de courant électrique alimentant la machine de traction des rames de wagons. Ce système offre certains avantages par rapport au système * - 2 - d'électrification par caténaires.A railway electrification system consists in using, between the two usual rails, a third rail which serves as a connector. electric current driver supplying the wagon train traction machine. This system offers certain advantages compared to the catenary electrification system.
Il présente cependant un inconvénient : lors de l’entretien ou de la réfection des voies, des outils métalliques manipulés par les ouvriers peuvent venir accidentellement en contact avec le rail conducteur de courant électrique, dont le voltage dépasse 700 volts et peut mime atteindre 900 volts, d'où des accidents mortels.However, it has a drawback: during the maintenance or repair of the tracks, metal tools manipulated by workers can accidentally come into contact with the electric current conductor rail, whose voltage exceeds 700 volts and can even reach 900 volts , hence fatal accidents.
On voit donc qu'il est nécessaire de disposer d'une solution permettant de remédier ä cet inconvénient. La présente invention a pour objet de fournir cette solution, par isolation partielle du rail conducteur de courant électrique.It can therefore be seen that it is necessary to have a solution which makes it possible to remedy this drawback. The object of the present invention is to provide this solution, by partial insulation of the electric current conducting rail.
Le procédé de la présente invention consiste à appliquer sur la partie inférieure et sur les côtés du rail conducteur de courant électrique une composition isolante comprenant essentiellement une charge minérale, isolante, et un liant constitué par une résine époxyde.The method of the present invention consists in applying to the lower part and to the sides of the electric current conducting rail an insulating composition essentially comprising a mineral filler, an insulator, and a binder consisting of an epoxy resin.
La composition appliquée sur les parties du rail mentionnées ci-dessus doit répondre à certains critères pour qu'elle agisse de façon efficace. Elle doit non seulement avoir une action isolante, mais elle doit aussi posséder des proprités mécaniques suffisantes, notamment aux points de vue de la résistance aux chocs, à l'abrasion, aux huiles, graisses, ainsi qu'aux intempéries.The composition applied to the parts of the rail mentioned above must meet certain criteria for it to act effectively. It must not only have an insulating action, but it must also have sufficient mechanical properties, in particular from the points of view of impact resistance, abrasion, oils, greases, as well as weathering.
Le choix de la charge dépend non seulement des propriétés isolantes désirées, mais également d'autres facteurs, tels que prix et facilité d'approvisionnement. On peut notamment utiliser une charge minérale, pulvérulente, telle que sable, silicate, argile, kaolin, craie, > ardoise broyée, ou une charge fibreuse, comme la fibre de verre ou simi laire, ou un mélange de telles charges. La quantité de charge peut varier dans de larges limites, allant d'environ 60 % à environ 85 % en poids et même plus, basé sur le poids total de la composition. Plus généralement, - 3 · % le matériau de charge sera utilisé en une quantité variant entre environ 70 et 80 % du poids total de la composition. D'après un mode d'exécution de l'invention, ce matériau de charge est constitué de sable quartzique, dont la granulométrie est située avantageusement entre environ 0,1 et 0,3 mm.The choice of filler depends not only on the desired insulating properties, but also on other factors, such as price and ease of supply. It is possible in particular to use a mineral, pulverulent filler, such as sand, silicate, clay, kaolin, chalk,> crushed slate, or a fibrous filler, such as fiberglass or the like, or a mixture of such fillers. The amount of filler can vary within wide limits, ranging from about 60% to about 85% by weight and even more, based on the total weight of the composition. More generally, - 3% of the filler material will be used in an amount varying between approximately 70 and 80% of the total weight of the composition. According to one embodiment of the invention, this filler material consists of quartz sand, the particle size of which is advantageously between approximately 0.1 and 0.3 mm.
époxydeepoxy
Le liant consiste principalement en une résine durcisable. Par les termes "résines époxyde", on entend non seulement les résines obtenues à partir d'épichlorhydrine et de composé organique hydroxydrique, mais également des copolymères, dont par exemple les résines époxy-sili-cones, ainsi que les mélanges constitués d'une majeure partie de résine époxyde et d'une quantité moindre de polymère organique compatible avec les résines époxydes. On peut notamment utiliser, en tant que polymère organique compatible, des polyamides, des novolaques et similaires, qui s permettent d'améliorer certaines caractéristiques particulières du re vêtement appliqué sur le rail. La quantité de liant dans la composition peut être comprise entre environ 15 % et 40 % du poids total de la composition. On utilise le liant en une proportion qui est au moins de 15 %, basé sur le poids de charge. D'autre part,une proportion de liant dépassant 25 % du poids de la charge ne conduit pas à une amélioration sensible des qualités du revêtement isolant.The binder consists mainly of a hardenable resin. By the terms "epoxy resins" is meant not only the resins obtained from epichlorohydrin and an organic hydroxide compound, but also copolymers, including for example epoxy-silicone resins, as well as mixtures consisting of a most of epoxy resin and less organic polymer compatible with epoxy resins. Use may, in particular, be made, as compatible organic polymer, of polyamides, novolaks and the like, which make it possible to improve certain particular characteristics of the coating applied to the rail. The amount of binder in the composition can be between approximately 15% and 40% of the total weight of the composition. The binder is used in a proportion which is at least 15%, based on the load weight. On the other hand, a proportion of binder exceeding 25% of the weight of the filler does not lead to a significant improvement in the qualities of the insulating coating.
La composition de l'invention comprend avantageusement un agent thixotropique. Grâce à l'addition d'un tel agent, la composition se présente sous la forme d'un produit stable, homogène, ayant une viscosité telle qu'il puisse être appliqué facilement, par tout moyen approprié,The composition of the invention advantageously comprises a thixotropic agent. Thanks to the addition of such an agent, the composition is in the form of a stable, homogeneous product having a viscosity such that it can be applied easily, by any suitable means,
VV
y compris par pulvérisation. De plus, après application sur le rail, la composition forme un revêtement qui n'a aucune tendance à s'écouler du support. Parmi les agents thixotropiques utilisés dans la composition de l'invention, on peut citer les silices colloïdales, en particulier les i - 4 t gels de silice, ainsi que les bentenîtes modifiées par des amines, des n sels alcalins ou alcalino-terreux d'acides gras supérieurs, etc... .including spraying. In addition, after application to the rail, the composition forms a coating which has no tendency to flow from the support. Among the thixotropic agents used in the composition of the invention, there may be mentioned colloidal silicas, in particular i - 4 t silica gels, as well as bentenites modified with amines, n alkali or alkaline earth salts of higher fatty acids, etc ....
La quantité d’agent thixotropique éventuellement ajouté à la composition de l’invention ne dépasse généralement pas 5 % du poids total de liant et de charge minérale et elle se situe le plus souvent entre environ 1 % et 2 % en poids.The amount of thixotropic agent possibly added to the composition of the invention generally does not exceed 5% of the total weight of binder and mineral filler and it is most often between approximately 1% and 2% by weight.
La composition de l’invention peut aussi contenir des pigments et autres additifs, tels que des diluants liquides. Certains de ces diluants, tels que les esters glycidyliques d’acides versatiques, sont réactifs. Ces différents additifs»lorsqu’ils sont incorporés dans * la composition de l'invention, sont utilisés en quantité qui ne dépasse généralement pas 5 % du poids total de la composition.The composition of the invention may also contain pigments and other additives, such as liquid diluents. Some of these diluents, such as glycidyl esters of versatic acids, are reactive. These various additives "when incorporated into * the composition of the invention, are used in an amount which generally does not exceed 5% of the total weight of the composition.
On applique la composition de l’invention sur la partie inférieure et sur les cotés du rail qui à été préalablement nettoyé, par exemple par jet de sable, et qui peut aussi avoir été traité préalablement, à titre préventif, par une couche de produit protecteur. En vue de son application, la composition est préalablement mélangée avec un agent durcisseur usuel pour résines époxydes. La quantité nécessaire d'agent durcisseur varie en fonction du type de liant époxyde utilisé et de la nature (acide ou basique) de cet agent. Dans le cas des compositions de l'invention, cette quantité peut être comprise entre environ 2 et 10 % - . , basée sur le poids total de composition.The composition of the invention is applied to the lower part and to the sides of the rail which has been previously cleaned, for example by sand blasting, and which may also have been treated beforehand, as a preventive measure, with a layer of protective product. . In view of its application, the composition is mixed beforehand with a usual hardening agent for epoxy resins. The necessary quantity of hardening agent varies according to the type of epoxy binder used and the nature (acid or basic) of this agent. In the case of the compositions of the invention, this amount can be between approximately 2 and 10% -. , based on the total composition weight.
A titre d’exemple, on peut utiliser un durcisseur basique en une quantité d'environ 4 à 6 %, calculée sur le poids total de composition.As an example, a basic hardener can be used in an amount of about 4 to 6%, calculated on the total weight of the composition.
% - Exemple% - Example
Dans un mélangeur muni d'un agitateur, on prépare une composition à partir de : - résine époxyde (produit de réaction d'épichlorhydrine et de bisphénol-A) 15,5 % en poidsIn a mixer fitted with an agitator, a composition is prepared from: - epoxy resin (reaction product of epichlorohydrin and bisphenol-A) 15.5% by weight
Claims (10)