MA50898B1 - Procédé pour la fabrication d'une tôle d'acier revêtue de zinc résistant à la fragilisation par métal liquide - Google Patents

Procédé pour la fabrication d'une tôle d'acier revêtue de zinc résistant à la fragilisation par métal liquide

Info

Publication number
MA50898B1
MA50898B1 MA50898A MA50898A MA50898B1 MA 50898 B1 MA50898 B1 MA 50898B1 MA 50898 A MA50898 A MA 50898A MA 50898 A MA50898 A MA 50898A MA 50898 B1 MA50898 B1 MA 50898B1
Authority
MA
Morocco
Prior art keywords
steel sheet
coated steel
liquid metal
coating
producing zinc
Prior art date
Application number
MA50898A
Other languages
English (en)
Other versions
MA50898A (fr
Inventor
Christian Allely
Pascal BERTHO
Anirban Chakraborty
Hassan GHASSEMI-ARMAKI
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MA50898A publication Critical patent/MA50898A/fr
Publication of MA50898B1 publication Critical patent/MA50898B1/fr

Abstract

La présente invention concerne un procédé pour la fabrication d'une tôle d'acier revêtue, lequel procédé comprend les étapes successives suivantes : A. le revêtement de la tôle d'acier avec un premier revêtement composé de nickel et ayant une épaisseur entre 600 nm et 1400 nm, la tôle d'acier ayant la composition suivante en poids : 0,10 < C < 0,40%, 1,5 < Mn < 3,0%, 0,7 < Si < 3,0%, 0,05 < Al < 1,0%, 0,75 < (Si+Al) < 3,0 %, et, sur une base purement facultative, un ou plusieurs éléments tels que Nb ≤ 0,5 %, B ≤ 0,010%, Cr ≤ 1,0%, Mo ≤ 0,50%, Ni ≤ 1,0%, Ti ≤ 0,5%, le reste de la composition étant constitué par du fer et des impuretés inévitables résultant de l'élaboration ; B. le recuit de recristallisation à une température entre 820 et 1200° C ; C. le revêtement avec un second revêtement à base de zinc ne comprenant pas de nickel.
MA50898A 2017-11-17 2018-11-15 Procédé pour la fabrication d'une tôle d'acier revêtue de zinc résistant à la fragilisation par métal liquide MA50898B1 (fr)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
IB2017057196 2017-11-17
PCT/IB2018/058991 WO2019097440A1 (fr) 2017-11-17 2018-11-15 Procédé pour la fabrication d'une tôle d'acier revêtue de zinc résistant à la fragilisation par métal liquide
EP18808512.0A EP3710612B1 (fr) 2017-11-17 2018-11-15 Procédé pour la fabrication d'une tôle d'acier revêtue de zinc résistant à la fragilisation par métal liquide

Publications (2)

Publication Number Publication Date
MA50898A MA50898A (fr) 2021-04-07
MA50898B1 true MA50898B1 (fr) 2024-10-31

Family

ID=60629759

Family Applications (1)

Application Number Title Priority Date Filing Date
MA50898A MA50898B1 (fr) 2017-11-17 2018-11-15 Procédé pour la fabrication d'une tôle d'acier revêtue de zinc résistant à la fragilisation par métal liquide

Country Status (15)

Country Link
US (3) US11566310B2 (fr)
EP (1) EP3710612B1 (fr)
JP (2) JP2021503549A (fr)
KR (1) KR20200069328A (fr)
CN (1) CN111356783B (fr)
CA (1) CA3082357C (fr)
ES (1) ES3005182T3 (fr)
FI (1) FI3710612T3 (fr)
HU (1) HUE068927T2 (fr)
MA (1) MA50898B1 (fr)
MX (1) MX2020005026A (fr)
RU (1) RU2761927C1 (fr)
UA (1) UA125102C2 (fr)
WO (1) WO2019097440A1 (fr)
ZA (1) ZA202002400B (fr)

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
MX2020005026A (es) 2017-11-17 2020-08-13 Arcelormittal Un metodo para la fabricacion de hoja de acero recubierta con zinc resistente a la fragilizacion por metal liquido.
JP7269525B2 (ja) * 2020-05-13 2023-05-09 日本製鉄株式会社 ホットスタンプ用鋼板
EP4151767B1 (fr) * 2020-05-13 2024-05-01 Nippon Steel Corporation Tôle d'acier pour estampage à chaud
CN115298356B (zh) * 2020-05-13 2023-10-13 日本制铁株式会社 热压构件
WO2022071305A1 (fr) * 2020-09-30 2022-04-07 日本製鉄株式会社 Tôle d'acier
CN114686651B (zh) * 2020-12-31 2024-08-13 通用汽车环球科技运作有限责任公司 具有降低的液态金属致脆(lme)敏感性的锌涂覆的钢
KR20230094376A (ko) * 2021-12-21 2023-06-28 주식회사 포스코 점용접성이 우수한 고강도 고성형성 강판 및 그 제조방법
CN116200692B (zh) * 2023-02-24 2026-03-20 首钢集团有限公司 一种纯锌镀层钢的焊接方法
JP7773117B2 (ja) * 2023-10-13 2025-11-19 日本製鉄株式会社 溶融めっき鋼材
KR20250091877A (ko) * 2023-12-14 2025-06-23 주식회사 포스코 냉연강판 및 그 제조방법
EP4707411A1 (fr) 2024-09-06 2026-03-11 ThyssenKrupp Steel Europe AG Acier à allongement local et global excellé et ayant une sensibilité lme réduite et procédé de fabrication

Family Cites Families (45)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS589965A (ja) 1981-07-08 1983-01-20 Kawasaki Steel Corp 高耐食性表面処理鋼板
JPS60228693A (ja) 1984-04-25 1985-11-13 Kawasaki Steel Corp Ｚｎ−Ｎｉ合金めつき鋼板の製造方法
JP2561331B2 (ja) * 1988-11-07 1996-12-04 川崎製鉄株式会社 溶融ＺｎめっきＣｒ含有鋼帯の製造方法
US5234721A (en) 1989-05-26 1993-08-10 Rostoker, Inc. Method for forming carbide coating on various metals and their alloys
JPH0328358A (ja) 1989-06-23 1991-02-06 Kawasaki Steel Corp 溶融アルミニウムめっきクロム含有鋼板の製造方法
US5441628A (en) 1992-09-15 1995-08-15 Japan Energy Corporation Method for preparation for a Zn-Ni electroplating or hot-dip galvanizing bath using a Zn-Ni alloy, and method for producing a Zn-Ni alloy
US6465114B1 (en) 1999-05-24 2002-10-15 Nippon Steel Corporation -Zn coated steel material, ZN coated steel sheet and painted steel sheet excellent in corrosion resistance, and method of producing the same
JP4947565B2 (ja) * 2001-02-16 2012-06-06 新日本製鐵株式会社 めっき密着性およびプレス成形性に優れた高強度溶融亜鉛めっき鋼板の製造方法。
JP2004124187A (ja) 2002-10-03 2004-04-22 Sumitomo Metal Ind Ltd 密着性・溶接性に優れた高強度溶融亜鉛めっき鋼板
US8048285B2 (en) 2005-05-11 2011-11-01 The Boeing Company Low hydrogen embrittlement zinc/nickel plating for high strength steels
KR100705243B1 (ko) * 2005-07-20 2007-04-10 현대하이스코 주식회사 도금 부착성 및 성형성이 뛰어난 변태유기소성강의 용융아연 도금강판 및 그 제조방법
RU2418094C2 (ru) 2006-01-30 2011-05-10 Ниппон Стил Корпорейшн Высокопрочный горячеоцинкованный погружением стальной лист и высокопрочный отожженный после цинкования стальной лист с превосходными формуемостью и способностью к нанесению гальванопокрытия и способы изготовления и устройства для изготовления таких листов
JP2008144264A (ja) 2006-11-16 2008-06-26 Jfe Steel Kk 高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板の製造方法
RU2430185C2 (ru) 2007-04-11 2011-09-27 Ниппон Стил Корпорейшн Высокопрочная листовая сталь с покрытием, полученным горячим погружением, имеющая высокую ударную вязкость при низких температурах, для использования в штамповке и способ ее производства
JP5446499B2 (ja) 2009-06-19 2014-03-19 Ｊｆｅスチール株式会社 耐遅れ破壊特性に優れた鋼板およびその製造方法
EP2520686B1 (fr) 2009-12-29 2021-04-07 Posco Pièces embouties à chaud d'acier zingué et procédé de production de celle-ci
KR101322135B1 (ko) 2010-10-21 2013-10-25 주식회사 포스코 표면품질 및 내지연파괴성이 우수한 용융아연도금강판 및 그 제조방법
KR20120041544A (ko) 2010-10-21 2012-05-02 주식회사 포스코 도금성, 도금밀착성 및 스폿용접성이 우수한 용융아연도금강판 및 그 제조방법
KR101207767B1 (ko) 2010-12-27 2012-12-03 주식회사 포스코 도금성이 우수한 고망간 고알루미늄 용융아연도금강판 및 그 제조방법
KR101220708B1 (ko) 2010-12-27 2013-01-09 주식회사 포스코 내파우더링성이 우수한 고망간 고알루미늄 합금화 용융아연도금강판 및 그 제조방법
US9523139B2 (en) 2011-07-06 2016-12-20 Nippon Steel & Sumitomo Metal Corporation Cold-rolled steel sheet
CA2850045C (fr) * 2011-09-30 2016-04-12 Nippon Steel & Sumitomo Metal Corporation Feuille d'acier galvanisee et son procede de fabrication
KR101353701B1 (ko) * 2011-12-23 2014-01-21 주식회사 포스코 극저온 접합성이 우수한 용융아연도금강판 및 그 제조방법
US20140370330A1 (en) 2011-12-27 2014-12-18 Nippon Steel & Sumitomo Metal Corporation Hot-dip plated high-strength steel sheet for presswork excellent in low-temperature toughness and corrosion resistance and manufacturing method thereof
RU2587003C2 (ru) 2012-01-05 2016-06-10 Ниппон Стил Энд Сумитомо Метал Корпорейшн Горячекатаный стальной лист и способ его изготовления
CN104583437A (zh) 2012-08-15 2015-04-29 新日铁住金株式会社 热压用钢板、其制造方法以及热压钢板构件
CN104981346B (zh) 2013-02-12 2017-07-18 塔塔钢铁艾默伊登有限责任公司 适于热浸镀锌的涂覆钢基材
ES2705349T3 (es) 2013-05-01 2019-03-22 Nippon Steel & Sumitomo Metal Corp Chapa de acero galvanizado y método para producirla
MX376674B (es) 2013-05-20 2025-03-07 Nippon Steel Corp Star Lámina de acero galvanizada y recocida y método para fabricar la misma.
EP3040133B1 (fr) 2013-08-29 2017-03-01 JFE Steel Corporation Procédé de fabrication d'un élément pressé à chaud et élément pressé à chaud
RU2648104C2 (ru) 2013-09-18 2018-03-22 Ниппон Стил Энд Сумитомо Метал Корпорейшн Горячештампованная деталь и способ ее изготовления
KR101585721B1 (ko) * 2013-12-21 2016-01-14 주식회사 포스코 용접성이 우수한 아연도금강판 및 이의 제조 방법
KR101568543B1 (ko) 2013-12-25 2015-11-11 주식회사 포스코 액체금속취화에 의한 크랙 저항성이 우수한 용융아연도금강판
MX377269B (es) 2014-05-15 2025-03-07 Nippon Steel Corp Elemento placa de acero laminada en caliente.
JP2016089274A (ja) * 2014-11-04 2016-05-23 株式会社神戸製鋼所 ホットスタンプ用めっき鋼板
JP6536294B2 (ja) * 2015-08-31 2019-07-03 日本製鉄株式会社 溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板、およびそれらの製造方法
JP2017075394A (ja) * 2015-10-16 2017-04-20 株式会社神戸製鋼所 高強度溶融亜鉛めっき鋼板及び高強度溶融亜鉛めっき鋼板の製造方法
KR101758485B1 (ko) * 2015-12-15 2017-07-17 주식회사 포스코 표면품질 및 점 용접성이 우수한 고강도 용융아연도금강판 및 그 제조방법
WO2017109542A1 (fr) 2015-12-21 2017-06-29 Arcelormittal Procédé de fabrication d'une tôle d'acier à haute résistance présentant une ductilité et une formabilité améliorées et tôle d'acier obtenue par ce procédé
WO2018203097A1 (fr) * 2017-05-05 2018-11-08 Arcelormittal Procédé de fabrication d'une tôle d'acier recuite après galvanisation résistant à la fragilisation par métal liquide
US11466354B2 (en) 2017-10-24 2022-10-11 Arcelormittal Method for the manufacture of a coated steel sheet
US11680331B2 (en) 2017-10-24 2023-06-20 Arcelormittal Method for the manufacture of a coated steel sheet
US20200340124A1 (en) 2017-10-24 2020-10-29 Arcelormittal A method for the manufacture of a coated steel sheet
MX2020004313A (es) 2017-10-24 2020-08-13 Arcelormittal Un metodo para la fabricacion de una lamina de acero galvanizado.
MX2020005026A (es) 2017-11-17 2020-08-13 Arcelormittal Un metodo para la fabricacion de hoja de acero recubierta con zinc resistente a la fragilizacion por metal liquido.

Also Published As

Publication number Publication date
EP3710612B1 (fr) 2024-10-02
US12139782B2 (en) 2024-11-12
KR20200069328A (ko) 2020-06-16
MA50898A (fr) 2021-04-07
UA125102C2 (uk) 2022-01-05
US20230137133A1 (en) 2023-05-04
CN111356783A (zh) 2020-06-30
MX2020005026A (es) 2020-08-13
HUE068927T2 (hu) 2025-02-28
ES3005182T3 (en) 2025-03-14
JP2021503549A (ja) 2021-02-12
JP7696862B2 (ja) 2025-06-23
US20250034688A1 (en) 2025-01-30
US11566310B2 (en) 2023-01-31
CA3082357A1 (fr) 2019-05-23
CN111356783B (zh) 2023-03-21
US20200263284A1 (en) 2020-08-20
WO2019097440A1 (fr) 2019-05-23
ZA202002400B (en) 2021-03-31
EP3710612A1 (fr) 2020-09-23
JP2022133281A (ja) 2022-09-13
BR112020007314A2 (pt) 2020-09-29
FI3710612T3 (fi) 2024-11-13
CA3082357C (fr) 2022-07-12
RU2761927C1 (ru) 2021-12-14

Similar Documents

Publication Publication Date Title
MA50898B1 (fr) Procédé pour la fabrication d&#39;une tôle d&#39;acier revêtue de zinc résistant à la fragilisation par métal liquide
US10196727B2 (en) High strength galvanized steel sheet having excellent bendability and weldability, and method of manufacturing the same
US9464345B2 (en) Hot dip Al coated steel sheet excellent in heat black discoloration resistance and method of production of same
TWI458840B (zh) 冷軋鋼板及其製造方法
JP6328247B2 (ja) 溶接性及び耐食性に優れた熱間プレス成形用めっき鋼板、成形部材、及びその製造方法
KR102630305B1 (ko) 향상된 연성을 갖는 고강도 강 부품들을 제조하기 위한 방법, 및 상기 방법에 의해 얻어진 부품들
EP2753725B1 (fr) Acier à haute résistance, à faible densité, et procédé de fabrication dudit acier
JP6897757B2 (ja) 表面処理鋼板
MX2009008194A (es) Tira de acero de alta resistencia laminada en frio y recocida en continuo, y metodo para producirla.
JP6288248B2 (ja) ホットスタンプ鋼材
WO2014024831A1 (fr) Feuille d&#39;acier laminée à froid, son procédé de fabrication et article moulé par estampage à chaud
JP2005113233A (ja) 熱間プレス用Ｚｎ系めっき鋼材
MA54523B1 (fr) Tôle d&#39;acier laminée à froid traitée thermiquement et son procédé de fabrication
WO2013121963A1 (fr) Feuille d&#39;acier, feuille d&#39;acier plaquée, procédé de fabrication d&#39;une feuille d&#39;acier et procédé de fabrication d&#39;une feuille d&#39;acier plaquée
US20230416888A1 (en) Al plated welded pipe for hardening use and al plated hollow member and method for producing same
TWI433961B (zh) 材質安定性和加工性優異之高強度熔融鍍鋅鋼板及其製造方法
JP2004270029A (ja) 耐亜鉛揮発性に優れた亜鉛系めっき鋼板
MA54486B1 (fr) Pièce durcie à la presse ayant une résistance élevée à la rupture différée et procédé de fabrication associé
JP2011195845A5 (fr)
JPWO2017131054A1 (ja) 高強度亜鉛めっき鋼板、高強度部材及び高強度亜鉛めっき鋼板の製造方法
TW201734228A (zh) 含有Ｔｉ之肥粒鐵系不銹鋼板及製造方法以及凸緣件
CN107406932B (zh) 高强度钢板及其制造方法
CN109371320A (zh) 镀锌钢板及其制造方法
TWI470093B (zh) 熱浸鍍鋅鋼板及其製造方法
JP3872426B2 (ja) 熱間プレス成形性に優れた亜鉛めっき鋼板および該鋼板を用いた熱間プレス成形部材の製法並びに高強度かつめっき外観に優れた熱間プレス成形部材