MX2017002580A - Lamina de acero galvanizada de alta resistencia excelente en conformabilidad de brida de estiramiento. estabilidad en el plano de la conformabilidad de brida de estiramiento, y plegabilidad y metodo para fabricar la misma. - Google Patents

Lamina de acero galvanizada de alta resistencia excelente en conformabilidad de brida de estiramiento. estabilidad en el plano de la conformabilidad de brida de estiramiento, y plegabilidad y metodo para fabricar la misma.

Info

Publication number
MX2017002580A
MX2017002580A MX2017002580A MX2017002580A MX2017002580A MX 2017002580 A MX2017002580 A MX 2017002580A MX 2017002580 A MX2017002580 A MX 2017002580A MX 2017002580 A MX2017002580 A MX 2017002580A MX 2017002580 A MX2017002580 A MX 2017002580A
Authority
MX
Mexico
Prior art keywords
flangeability
stretch
steel sheet
galvanized steel
dip galvanized
Prior art date
Application number
MX2017002580A
Other languages
English (en)
Inventor
Fujita Koichiro
Hasegawa Hiroshi
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2017002580A publication Critical patent/MX2017002580A/es

Abstract

Se proporciona una lámina de acero galvanizada de alta resistencia la cual es excelente en conformabilidad de brida de estiramiento, estabilidad en el plano de la conformabilidad de brida de estiramiento, y plegabilidad, así como un método para fabricar la misma. La lámina de acero galvanizada de alta resistencia contiene de 0.12% a 0.25% de C, de 0.01% a 1.00% de Si, de 1.5% a 4.0% de Mn, de 0.100% o menos de P, 0.02% o menos de S, de 0.01% a 0.10% de Al, de 0.001% a 0.010% de N, de 0.005% a 0.100% de Ti, y 0.0005% a 0.0050% de B, el resto siendo Fe e impurezas inevitables, Ti > 4N siendo satisfechas. La lámina de acero galvanizada de alta resistencia contiene 80% hasta 100% de martensita en términos de fracción de área, 5% o menos (incluyendo 0%) ferrita poligonal en términos de fracción de área, y menos de 3% (incluyendo 0%) austenita retenida en términos de fracción de área. La dureza promedio de martensita es 400 hasta 500 en términos de dureza de Vickers (Hv). El tamaño del grano promedio de martensita es 20 µm o menos. La desviación estándar del tamaño del grano de martensita es 7.0 µm o menos.
MX2017002580A 2014-08-28 2015-08-14 Lamina de acero galvanizada de alta resistencia excelente en conformabilidad de brida de estiramiento. estabilidad en el plano de la conformabilidad de brida de estiramiento, y plegabilidad y metodo para fabricar la misma. MX2017002580A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014174410 2014-08-28
PCT/JP2015/004049 WO2016031165A1 (ja) 2014-08-28 2015-08-14 伸びフランジ性、伸びフランジ性の面内安定性および曲げ性に優れた高強度溶融亜鉛めっき鋼板ならびにその製造方法

Publications (1)

Publication Number Publication Date
MX2017002580A true MX2017002580A (es) 2017-05-25

Family

ID=55399083

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2017002580A MX2017002580A (es) 2014-08-28 2015-08-14 Lamina de acero galvanizada de alta resistencia excelente en conformabilidad de brida de estiramiento. estabilidad en el plano de la conformabilidad de brida de estiramiento, y plegabilidad y metodo para fabricar la misma.

Country Status (6)

Country Link
US (1) US10422015B2 (es)
EP (1) EP3187607B1 (es)
JP (1) JP5971434B2 (es)
CN (1) CN106661698B (es)
MX (1) MX2017002580A (es)
WO (1) WO2016031165A1 (es)

Families Citing this family (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018011978A1 (ja) 2016-07-15 2018-01-18 新日鐵住金株式会社 溶融亜鉛めっき鋼板
KR102209592B1 (ko) * 2016-12-23 2021-01-29 주식회사 포스코 굽힘가공성이 우수한 초고강도 열연강판 및 그 제조방법
MX391277B (es) 2016-12-27 2025-03-21 Jfe Steel Corp Lámina de acero galvanizado de alta resistencia y método para producir la misma.
KR102312464B1 (ko) * 2017-02-10 2021-10-13 제이에프이 스틸 가부시키가이샤 고강도 아연 도금 강판 및 그 제조 방법
MX394104B (es) * 2017-04-21 2025-03-24 Nippon Steel Corp Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo de produccion de la misma.
CN108130481A (zh) * 2017-12-07 2018-06-08 安徽科汇钢结构工程有限公司 一种拉伸凸缘性优的冷轧钢板
WO2019151017A1 (ja) * 2018-01-31 2019-08-08 Ｊｆｅスチール株式会社 高強度冷延鋼板、高強度めっき鋼板及びそれらの製造方法
CN111936651A (zh) 2018-03-30 2020-11-13 杰富意钢铁株式会社 高强度镀锌钢板、高强度部件及它们的制造方法
EP3954790B1 (en) 2019-04-11 2025-06-04 Nippon Steel Corporation Steel sheet and method for manufacturing same
JP7136061B2 (ja) * 2019-10-11 2022-09-13 Ｊｆｅスチール株式会社 高強度熱延鋼板及びその製造方法
US11149832B2 (en) * 2019-12-13 2021-10-19 Aichi Steel Corporation Differential hypoid gear, pinion gear, and paired hypoid gears formed by combination thereof
JP7277837B2 (ja) * 2020-01-16 2023-05-19 日本製鉄株式会社 ホットスタンプ成形体
WO2021200578A1 (ja) 2020-03-31 2021-10-07 Ｊｆｅスチール株式会社 鋼板、部材及びそれらの製造方法
KR102498141B1 (ko) * 2020-12-18 2023-02-08 주식회사 포스코 저온 충격인성이 우수한 고경도 방탄강 및 이의 제조방법
KR102498144B1 (ko) * 2020-12-18 2023-02-08 주식회사 포스코 저온 충격인성이 우수한 고경도 방탄강 및 이의 제조방법
KR102498142B1 (ko) * 2020-12-18 2023-02-08 주식회사 포스코 저온 충격인성이 우수한 고경도 방탄강 및 이의 제조방법
KR20230044048A (ko) * 2021-09-24 2023-04-03 주식회사 포스코 표면 품질이 우수하고 재질 편차가 적은 고강도 냉연강판 및 이의 제조 방법
WO2023162205A1 (ja) * 2022-02-28 2023-08-31 Ｊｆｅスチール株式会社 鋼板、部材およびそれらの製造方法
KR20250140115A (ko) * 2023-03-13 2025-09-24 닛폰세이테츠 가부시키가이샤 강판 및 그 제조 방법
JP7836013B2 (ja) * 2023-03-13 2026-03-26 日本製鉄株式会社 鋼板

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4959161B2 (ja) 2005-09-05 2012-06-20 新日本製鐵株式会社 耐食性と伸びと穴拡げ性に優れた溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板
US7608155B2 (en) * 2006-09-27 2009-10-27 Nucor Corporation High strength, hot dip coated, dual phase, steel sheet and method of manufacturing same
JP5194841B2 (ja) 2008-01-31 2013-05-08 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
WO2009119751A1 (ja) 2008-03-27 2009-10-01 新日本製鐵株式会社 成形性と溶接性に優れた高強度冷延鋼板、高強度亜鉛めっき鋼板、高強度合金化溶融亜鉛めっき鋼板、及びそれらの製造方法
JP5418168B2 (ja) 2008-11-28 2014-02-19 Ｊｆｅスチール株式会社 成形性に優れた高強度冷延鋼板、高強度溶融亜鉛めっき鋼板およびそれらの製造方法
JP4924730B2 (ja) 2009-04-28 2012-04-25 Ｊｆｅスチール株式会社 加工性、溶接性および疲労特性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
JP5703608B2 (ja) * 2009-07-30 2015-04-22 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5504737B2 (ja) 2009-08-04 2014-05-28 Ｊｆｅスチール株式会社 鋼帯内における材質のバラツキが小さい成形性に優れた高強度溶融亜鉛めっき鋼帯およびその製造方法
JP5327106B2 (ja) * 2010-03-09 2013-10-30 Ｊｆｅスチール株式会社 プレス部材およびその製造方法
JP5434960B2 (ja) 2010-05-31 2014-03-05 Ｊｆｅスチール株式会社 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
JP5136609B2 (ja) * 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5862051B2 (ja) 2011-05-12 2016-02-16 Ｊｆｅスチール株式会社 加工性に優れる高強度冷延鋼板ならびにその製造方法
US9896751B2 (en) * 2011-07-29 2018-02-20 Nippon Steel & Sumitomo Metal Corporation High strength steel sheet and high strength galvanized steel sheet excellent in shapeability and methods of production of same
JP5870861B2 (ja) 2012-06-26 2016-03-01 Ｊｆｅスチール株式会社 疲労特性と延性に優れ、且つ延性の面内異方性の小さい高強度溶融亜鉛めっき鋼板およびその製造方法
KR20150029736A (ko) 2012-07-31 2015-03-18 제이에프이 스틸 가부시키가이샤 성형성 및 형상 동결성이 우수한 고강도 용융 아연 도금 강판, 그리고 그의 제조 방법

Also Published As

Publication number Publication date
US10422015B2 (en) 2019-09-24
JP5971434B2 (ja) 2016-08-17
US20170275726A1 (en) 2017-09-28
EP3187607A4 (en) 2017-11-22
CN106661698A (zh) 2017-05-10
JPWO2016031165A1 (ja) 2017-04-27
CN106661698B (zh) 2018-09-04
EP3187607A1 (en) 2017-07-05
EP3187607B1 (en) 2019-03-06
WO2016031165A1 (ja) 2016-03-03

Similar Documents

Publication Publication Date Title
MX387461B (es) Producto plano de acero y procedimiento para su fabricación.
WO2016098964A8 (ko) 재질 불균일이 작고 성형성이 우수한 고강도 냉연강판, 용융아연도금강판, 및 그 제조 방법
MX395053B (es) Lámina de acero galvanizada de alta resistencia y método para la fabricación de la misma.
MX366776B (es) Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma.
MX395449B (es) Lámina de acero galvanizada de alta resistencia y método para producir la misma.
WO2016067624A8 (ja) 高強度鋼板、高強度溶融亜鉛めっき鋼板、高強度溶融アルミニウムめっき鋼板および高強度電気亜鉛めっき鋼板、ならびに、それらの製造方法
MX389192B (es) Lámina de acero galvanizada por inmersión en caliente de alta resistencia y método para fabricar la misma.
MX380137B (es) Lamina de acero galvanizada de alta resistencia y metodo para producir la misma.
PH12019500350A1 (en) H section and method for manufacturing same
MX2013012116A (es) Placa de acero laminada en frio de alta resistencia que tiene excelente alargamiento por tension uniforme y capacidad de expansion de agujeros y metodo de fabricacion de la misma.
MY186913A (en) Aluminium-zinc-hot-dipped and colour-coated steel plate having a 500 mpa yield strength grade and a high elongation and a manufacturing method thereof
MY186509A (en) Aluminium-zinc-hot-dipped and colour-coated steel plate having a 600 mpa yield strength grade and a high elongation and manufacturing method thereof
MX2018014261A (es) Lamina de acero recubierta o chapada y metodo para producir la misma.
WO2015162939A8 (ja) 厚鋼板及びその製造方法
MX2014002021A (es) Lamina de acero laminada en caliente para lamina de acero laminada en frio, lamina de acero laminada en caliente para lamina de acero galvanizada, y metodo para la fabricacion de las mismas.
WO2016105064A8 (ko) 취성균열전파 저항성이 우수한 고강도 강재 및 그 제조방법
UA113404C2 (xx) Гарячекатаний сталевий лист та спосіб його виготовлення
MX2017011825A (es) Lamina de acero laminada en frio de alta resistencia y metodo para producir la misma.
MX2016012708A (es) Chapa de acero laminada en frio de alta resistencia, chapa de acero galvanizada en inmersion en caliente de alta resistencia y chapa de acero galvanfusionado en inmersion en caliente de alta resistencia que tiene excelente ductilidad, abocardabilidad por estiramiento y soldabilidad.
WO2016105059A8 (ko) 취성균열전파 저항성이 우수한 고강도 강재 및 그 제조방법
PH12017500557A1 (en) Steel sheet for cans and method for manufacturing steel sheet for cans
MX2017008296A (es) Laminas de acero galvanizado de alta resistencia y metodos para fabricar las mismas.
MX2016012797A (es) Chapa de acero laminada en frio de alta resistencia, chapa de acero galvanizada en baño caliente de alta resistencia y chapa de acero galvanofusionado en baño caliente de alta resistencia que tiene excelente ductilidad, abocardabilidad por estiramiento y soldabilidad.
WO2016105062A8 (ko) 취성균열전파 저항성이 우수한 고강도 강재 및 그 제조방법
RU2016151759A (ru) Способ изготовления высокопрочного стального листа, обладающего улучшенными прочностью, формуемостью, и полученный лист