MX2020004592A - Acero templado en prensa con propiedades personalizadas. - Google Patents

Acero templado en prensa con propiedades personalizadas.

Info

Publication number
MX2020004592A
MX2020004592A MX2020004592A MX2020004592A MX2020004592A MX 2020004592 A MX2020004592 A MX 2020004592A MX 2020004592 A MX2020004592 A MX 2020004592A MX 2020004592 A MX2020004592 A MX 2020004592A MX 2020004592 A MX2020004592 A MX 2020004592A
Authority
MX
Mexico
Prior art keywords
weight
hardened steel
press hardened
tailored properties
alloy
Prior art date
Application number
MX2020004592A
Other languages
English (en)
Inventor
Erik James Pavlina
Stephen Bryant Tate
Original Assignee
Ak Steel Properties Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ak Steel Properties Inc filed Critical Ak Steel Properties Inc
Publication of MX2020004592A publication Critical patent/MX2020004592A/es

Abstract

Una preforma soldada a la medida es hecha de dos aceros, un acero de la Aleación A y un acero de la Aleación B; la Aleación A comprende 0.10 - 0.50% en peso de C, 0.1 - 0.5% en peso de Si, 2.0 - 8.0% en peso de Mn, 0.0 - 6.0% en peso de Cr, 0.0 - 2.0% en peso 5 de Mo, 0.0 - 0.15% en peso de Ti y 0.0 - 0.005% en peso de B y en donde la Aleación B comprende 0.06 - 0.12% en peso de C, 0.1 - 0.25% en peso de Si, 1.65 - 2.42% en peso de Mn, 0.0 - 0.70% en peso de Cr, 0.08 - 0.40% en peso de Mo, 0.0 - 0.05% en peso de V y 0.01 - 0.05% en peso de Ti.
MX2020004592A 2017-11-02 2018-11-02 Acero templado en prensa con propiedades personalizadas. MX2020004592A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201762580591P 2017-11-02 2017-11-02
PCT/US2018/059002 WO2019090109A1 (en) 2017-11-02 2018-11-02 Press hardened steel with tailored properties

Publications (1)

Publication Number Publication Date
MX2020004592A true MX2020004592A (es) 2020-08-24

Family

ID=65041834

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2020004592A MX2020004592A (es) 2017-11-02 2018-11-02 Acero templado en prensa con propiedades personalizadas.

Country Status (6)

Country Link
US (1) US11491581B2 (es)
EP (1) EP3704281A1 (es)
CA (1) CA3076932C (es)
MX (1) MX2020004592A (es)
TW (1) TW201925495A (es)
WO (1) WO2019090109A1 (es)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115305412B (zh) * 2021-05-05 2024-02-06 通用汽车环球科技运作有限责任公司 具有优异耐腐蚀性和超高强度的组合的压制硬化钢
CN113996969A (zh) * 2021-11-10 2022-02-01 海隆管道工程技术服务有限公司 一种高硬度高耐磨管道内壁堆焊药芯焊丝

Family Cites Families (36)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6866942B1 (en) 1999-04-23 2005-03-15 Nippon Steel Corporation Press-forming tailored blank material excellent in formability and production method therefor
CN1145709C (zh) * 2000-02-29 2004-04-14 川崎制铁株式会社 应变时效硬化特性优良的高强度冷轧钢板及其制造方法
FR2809648B1 (fr) 2000-05-31 2002-08-30 Air Liquide Procede et installation de soudage hybride par laser et arc electrique, notamment de pieces automobiles ou de tubes
FR2840832B1 (fr) 2002-06-14 2004-07-23 Air Liquide Utilisation de melanges gazeux helium/azote en soudage laser de flancs raboutes
US6825442B2 (en) 2003-01-06 2004-11-30 General Motors Corporation Tailor welded blank for fluid forming operation
JP4351465B2 (ja) * 2003-04-15 2009-10-28 新日本製鐵株式会社 穴拡げ性に優れた溶融亜鉛めっき高強度鋼板およびその製造方法
DE10333165A1 (de) 2003-07-22 2005-02-24 Daimlerchrysler Ag Pressgehärtetes Bauteil und Verfahren zur Herstellung eines pressgehärteten Bauteils
US7011361B2 (en) 2004-03-12 2006-03-14 Ford Global Technologies, Llc Automotive vehicle body having tailor welded blanks
US7922067B2 (en) 2006-10-17 2011-04-12 GM Global Technology Operations LLC Tailor welded blank assembly and method
JP4952236B2 (ja) 2006-12-25 2012-06-13 Ｊｆｅスチール株式会社 高炭素熱延鋼板およびその製造方法
DE102007015963A1 (de) * 2007-04-03 2008-10-09 Thyssenkrupp Steel Ag Verfahren zum Herstellen von aus Stahlblechen bestehenden Flachprodukten, aus Stahlblechen zusammengesetztes Stahlflachprodukt und Strukturbauteil
DE102009003508B4 (de) 2009-02-19 2013-01-24 Thyssenkrupp Steel Europe Ag Verfahren zur Herstellung eines pressgehärteten Metallbauteils
JP5434960B2 (ja) * 2010-05-31 2014-03-05 Ｊｆｅスチール株式会社 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
FR2962674B1 (fr) 2010-07-13 2013-03-08 Air Liquide Procede de soudage hybride arc/laser de pieces en acier aluminise
ES2535420T3 (es) 2011-03-07 2015-05-11 Tata Steel Nederland Technology B.V. Proceso para producir acero conformable de alta resistencia y acero conformable de alta resistencia producido con el mismo
FI20115702L (fi) 2011-07-01 2013-01-02 Rautaruukki Oyj Menetelmä suurlujuuksisen rakenneteräksen valmistamiseksi ja suurlujuuksinen rakenneteräs
WO2013014481A1 (fr) * 2011-07-26 2013-01-31 Arcelormittal Investigación Y Desarrollo Sl Pièce d'acier soudée préalablement mise en forme à chaud à très haute résistance mécanique et procédé de fabrication
MX373607B (es) * 2012-01-13 2020-05-15 Nippon Steel Corp Artículo moldeado estampado en caliente y método para la producción del mismo.
JP5890710B2 (ja) 2012-03-15 2016-03-22 株式会社神戸製鋼所 熱間プレス成形品およびその製造方法
KR20130122493A (ko) 2012-04-30 2013-11-07 주식회사 신영 Ｔｂｐｈ 기술을 적용한 차체 부품 제조 방법
JP6034490B2 (ja) 2012-06-29 2016-11-30 シロー インダストリーズ インコーポレイテッド 溶接ブランクアセンブリおよび方法
DE102012111118B3 (de) 2012-11-19 2014-04-03 Wisco Tailored Blanks Gmbh Verfahren zum Laserschweißen eines oder mehrerer Werkstücke aus härtbarem Stahl im Stumpfstoß
KR101318060B1 (ko) 2013-05-09 2013-10-15 현대제철 주식회사 인성이 향상된 핫스탬핑 부품 및 그 제조 방법
CA2910012C (en) 2013-05-17 2020-02-18 Ak Steel Properties, Inc. High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath
DE102013008853A1 (de) 2013-05-23 2014-11-27 Linde Aktiengesellschaft Anlage und Verfahren zum Warmumformen von Platinen
JP5843830B2 (ja) 2013-09-18 2016-01-13 アイシン高丘株式会社 触媒ケース一体型排気マニホルド
MX2016006485A (es) 2013-11-25 2016-08-05 Magna Int Inc Componente estructural que incluye zona de transicion templada.
DE102014001979A1 (de) 2014-02-17 2015-08-20 Wisco Tailored Blanks Gmbh Verfahren zum Laserschweißen eines oder mehrerer Werkstücke aus härtbarem Stahl im Stumpfstoß
WO2015150848A1 (fr) 2014-03-31 2015-10-08 Arcelormittal Investigación Y Desarrollo Sl Procede de fabrication a haute productivite de pieces d'acier revêtues et durcies a la presse
WO2015162445A1 (fr) 2014-04-25 2015-10-29 Arcelormittal Investigación Y Desarrollo Sl Procede et dispositif de preparation de toles d'acier aluminiees destinees a etre soudees puis durcies sous presse; flan soude correspondant
MX385812B (es) * 2014-10-24 2025-03-11 Jfe Steel Corp Parte prensada en caliente de alta resistencia y método para la fabricación de la misma.
KR101714121B1 (ko) 2014-11-21 2017-03-09 현대자동차주식회사 테일러 웰디드 블랭크 제조방법
WO2017006144A1 (en) 2015-07-09 2017-01-12 Arcelormittal Steel for press hardening and press hardened part manufactured from such steel
US20170247774A1 (en) 2016-02-26 2017-08-31 GM Global Technology Operations LLC Continuous tailor heat-treated blanks
CN106350741B (zh) 2016-10-24 2017-12-19 大连理工大学 一种激光拼焊高强钢的温成形制备方法
CA3076934C (en) * 2017-11-02 2023-03-21 Ak Steel Properties, Inc. Press hardened steel with tailored properties after novel thermal treatment

Also Published As

Publication number Publication date
TW201925495A (zh) 2019-07-01
US11491581B2 (en) 2022-11-08
WO2019090109A1 (en) 2019-05-09
CA3076932C (en) 2023-08-15
EP3704281A1 (en) 2020-09-09
CA3076932A1 (en) 2019-05-09
US20190126400A1 (en) 2019-05-02

Similar Documents

Publication Publication Date Title
MX2017001374A (es) Procedimiento para la fabricacion de laminas de acero para el endurecimiento por presion y piezas obtenidas por este procedimiento.
MX2018009735A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
CL2013002758A1 (es) Lámina de acero resistente a la abrasión resistente al agrietamiento por corrosión con una microestructura que tiene una fase base de martensita templada que comprende c, si, mn, b, p, 0,005 s, al y n, uno o mas de cr, mo y w, uno o mas de nb y ti, uno o mas de cu, ni y v, y uno o mas de rem, ca y mg; método de fabricación
BR112017023444A2 (pt) peça de aço endurecida sob pressão, peça de aço soldada a laser endurecida sob pressão, processo de fabricação de peças de aço e uso de peça
MX2018008561A (es) Lamina de acero de alta resistencia que tiene excelente conformabilidad y un metodo de fabricacion de la misma.
MX2009011927A (es) Metodo para la fabricacion de chapas de acero laminadas en frio y recocidas de muy alta resistencia, y chapas asi producidas.
PE20151042A1 (es) Aleacion de acero para un acero de alta resistencia, de baja aleacion
AR108269A1 (es) Tecnología de soldadura circunferencial en campo para tuberías para lodos de acero con alto contenido de manganeso
MX388381B (es) Acero de elevada resistencia y procedimiento de fabricacion.
MX2019007165A (es) Lamina de acero templada y recubierta que tiene excelente conformabilidad y metodo para fabricar la misma.
MX2018012954A (es) Un metodo de endurecimiento de prensa.
MY176531A (en) Austenitic stainless clad steel plate and method for producing thereof
MX2019014873A (es) Alambre laminado para acero de resorte.
MX387576B (es) Acero martensítico con resistencia a fractura retardada y método de fabricación.
AR108268A1 (es) Tecnología de soldadura de metales distintos en campo para acero con alto contenido de manganeso resistente al desgaste mejorado
MX2021003458A (es) Hoja de acero laminada en caliente y un metodo de fabricacion de la misma.
MX387461B (es) Producto plano de acero y procedimiento para su fabricación.
MX2018014000A (es) "tubo de acero sin costura y metodo para producir el tubo de acero sin costura".
BR112016015645A8 (pt) tira de aço inoxidável para válvulas de charneira
MX2019011366A (es) Lamina de acero inoxidable a base de ferrita que tiene baja gravedad especifica y metodo de produccion para la misma.
SA521422138B1 (ar) أنبوب غير ملحوم من فولاذ مقاوم للصدأ مزدوج وطريقة تصنيعه
MX2019010378A (es) Acero endurecido por prensado con fuerza extremadamente alta y metodo para su produccion.
MX2019011367A (es) Tubo de acero inoxidable ferritico que tiene excelente tolerancia a la sal en separacion, estructura engrosada en el extremo de tubo, junta de soldadura, y estructura soldada.
MX393854B (es) Lámina de acero de alta formabilidad para la fabricación de partes estructurales ligeras y proceso de fabricación.
MX379119B (es) Material de acero tratado con calor y método para la fabricación del mismo.