MX2020009042A - Recubrimiento de aleacion a base de zinc para acero y metodos. - Google Patents

Recubrimiento de aleacion a base de zinc para acero y metodos.

Info

Publication number
MX2020009042A
MX2020009042A MX2020009042A MX2020009042A MX2020009042A MX 2020009042 A MX2020009042 A MX 2020009042A MX 2020009042 A MX2020009042 A MX 2020009042A MX 2020009042 A MX2020009042 A MX 2020009042A MX 2020009042 A MX2020009042 A MX 2020009042A
Authority
MX
Mexico
Prior art keywords
zinc
based alloy
steel
alloy coating
methods
Prior art date
Application number
MX2020009042A
Other languages
English (en)
Inventor
Weiping Sun
Nan Gao
Yihui Liu
Original Assignee
Nucor Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nucor Corp filed Critical Nucor Corp
Publication of MX2020009042A publication Critical patent/MX2020009042A/es

Abstract

La presente descripción se refiere a un recubrimiento de aleación a base de zinc para tiras de acero a través de un proceso de galvanizado continuo. Este recubrimiento de aleación a base de zinc proporciona al acero una protección catódica antes y después de que el acero sea procesado por endurecimiento por presión a una temperatura de austenitización alta de hasta 950°C. El recubrimiento de aleación a base de zinc también reduce o elimina la susceptibilidad a la fragilización por metal líquido durante o después de la soldadura para diversos tipos de acero avanzado de resistencia ultra alta endurecidos sin presión. La aleación a base de zinc comprende al menos un elemento seleccionado de manganeso (Mb) y/o antimonio (Sb).
MX2020009042A 2018-03-01 2019-02-28 Recubrimiento de aleacion a base de zinc para acero y metodos. MX2020009042A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201862637102P 2018-03-01 2018-03-01
PCT/US2019/020154 WO2019169199A1 (en) 2018-03-01 2019-02-28 Zinc-based alloy coating for steel and methods

Publications (1)

Publication Number Publication Date
MX2020009042A true MX2020009042A (es) 2021-01-08

Family

ID=67805952

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2020009042A MX2020009042A (es) 2018-03-01 2019-02-28 Recubrimiento de aleacion a base de zinc para acero y metodos.

Country Status (5)

Country Link
US (1) US20210108301A1 (es)
EP (1) EP3758888A4 (es)
CA (1) CA3092822A1 (es)
MX (1) MX2020009042A (es)
WO (1) WO2019169199A1 (es)

Family Cites Families (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5952947B2 (ja) * 1980-01-29 1984-12-22 三菱マテリアル株式会社 溶融メツキ用亜鉛合金
JPS6055591B2 (ja) * 1980-10-09 1985-12-05 新日本製鐵株式会社 耐経時めつき剥離性に優れた溶融亜鉛合金めつき鋼板の製造法
US5266182A (en) 1988-03-16 1993-11-30 Kawasaki Steel Corporation Method for producing Zn-Ni alloy plated steel plate having superior press formability
US5597656A (en) * 1993-04-05 1997-01-28 The Louis Berkman Company Coated metal strip
KR960006049B1 (ko) * 1993-12-09 1996-05-08 포항종합제철주식회사 합금화 용융아연도금강판의 제조방법
JP3382697B2 (ja) * 1994-02-01 2003-03-04 川崎製鉄株式会社 合金化溶融亜鉛めっき鋼板の製造方法
KR19980013904A (ko) * 1996-08-05 1998-05-15 김종진 합금화 처리성이 우수한 합금화 용융아연 도금강판의 제조방법
DE60236447D1 (de) 2001-10-23 2010-07-01 Sumitomo Metal Ind Verfahren zur heisspressbearbeitung von einem plattierten stahlprodukt
KR100825975B1 (ko) 2003-07-29 2008-04-28 뵈스트알파인 스탈 게엠베하 경화 강판 부품의 제조 방법
WO2005068676A1 (ja) * 2004-01-14 2005-07-28 Nippon Steel Corporation めっき密着性および穴拡げ性に優れた溶融亜鉛めっき高強度鋼板とその製造方法
JP2007006378A (ja) 2005-06-27 2007-01-11 Toshiba Corp 移動無線端末装置
EP2209926B1 (en) * 2007-10-10 2019-08-07 Nucor Corporation Complex metallographic structured steel and method of manufacturing same
TWI396772B (zh) * 2009-02-03 2013-05-21 Nippon Steel & Sumitomo Metal Corp 合金化熔融鍍鋅鋼板及其製造方法
US20120018437A1 (en) 2009-03-10 2012-01-26 Savage Danielle Z Flexible package with slidable lock and method thereof
CA2850045C (en) * 2011-09-30 2016-04-12 Nippon Steel & Sumitomo Metal Corporation Galvanized steel sheet and method of manufacturing the same
PL2762585T3 (pl) * 2011-09-30 2020-01-31 Nippon Steel Corporation Blacha stalowa cienka o dużej wytrzymałości cynkowana zanurzeniowo na gorąco o doskonałych właściwościach skrawania mechanicznego, stopowa blacha stalowa cienka o dużej wytrzymałości cynkowana zanurzeniowo na gorąco oraz sposób wytwarzania wspomnianych blach cienkich
JP2013189671A (ja) * 2012-03-13 2013-09-26 Jfe Steel Corp 溶融Ａｌ−Ｚｎ系めっき鋼板
DE102012024616A1 (de) 2012-12-17 2014-06-18 GM Global Technology Operations LLC (n. d. Gesetzen des Staates Delaware) Stahlblech und Formteil daraus
WO2014184599A1 (fr) * 2013-05-13 2014-11-20 Arcelormittal Investigación Y Desarrollo Sl Assemblage d'une pièce à base d'aluminium et d'une pièce en acier munie d'un revêtement à base d'un alliage znaimg
KR20160007648A (ko) 2013-05-17 2016-01-20 에이케이 스틸 프로퍼티즈 인코포레이티드 프레스 경화 적용을 위한 아연-코팅된 스틸 및 그 생산 방법
DE102013015032A1 (de) * 2013-09-02 2015-03-05 Salzgitter Flachstahl Gmbh Zinkbasierte Korrosionsschutzbeschichtung für Stahlbleche zur Herstellung eines Bauteils bei erhöhter Temperatur durch Presshärten
KR101568543B1 (ko) * 2013-12-25 2015-11-11 주식회사 포스코 액체금속취화에 의한 크랙 저항성이 우수한 용융아연도금강판
CN104099550A (zh) * 2014-06-27 2014-10-15 陕西理工学院 一种热浸镀Zn-Al-Mn合金的制备方法及热浸镀工艺
EP3342893A4 (en) * 2015-08-24 2019-01-16 Nippon Steel & Sumitomo Metal Corporation ALLOY STEEL PLATE PLATED WITH ZINC MELT AND METHOD OF MANUFACTURE THEREOF
KR101819393B1 (ko) * 2016-12-22 2018-01-16 주식회사 포스코 용접성 및 프레스 가공성이 우수한 용융 아연계 도금강재 및 그 제조방법

Also Published As

Publication number Publication date
CA3092822A1 (en) 2019-09-06
EP3758888A4 (en) 2021-12-22
US20210108301A1 (en) 2021-04-15
WO2019169199A1 (en) 2019-09-06
EP3758888A1 (en) 2021-01-06

Similar Documents

Publication Publication Date Title
Kartsonakis et al. A comparative study of corrosion inhibitors on hot-dip galvanized steel
JP6718656B2 (ja) プレス焼入れ用亜鉛めっき鋼材およびその製造方法
UA96468C2 (ru) Способ обработки металлической полосы и устройство для его осуществления
US20160215376A1 (en) Zinc-based anti-corrosion coating for steel sheets, for producing a component at an elevated temperature by hot forming die quenching
MX2019004000A (es) Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
MX2015013538A (es) Placa de acero chapada de alta resistencia para elemento estructural soldado, metodo para producir la misma.
US9938600B2 (en) Manufacturing a hardened formed part
WO2012085248A3 (de) Verfahren zum umformen und härten von beschichteten stahlblechen
UA100522C2 (ru) Композиция для предварительной обработки металлической основы и способ обработки металлической основы
RS56715B1 (sr) Čelični lim sa žrtvenom katodnom zaštitnom prevlakom i postupak za izradu proizvoda polazeći od tog čeličnog lima
MX378603B (es) Metodo para la produccion de lamina de acero galvanizada de alta resistencia y lamina de acero galvano-recocida de alta resistencia.
JP2016520162A5 (es)
UA119946C2 (uk) Спосіб виробництва надвисокоміцної листової сталі, підданої цинкуванню з відпалюванням, і одержана листова сталь, піддана цинкуванню з відпалюванням
JP2018524471A5 (es)
US20160102380A1 (en) Heat-treated steel material and method of manufacturing the same
KR102731359B1 (ko) 핫 스탬프용 강판 및 핫 스탬프 성형체
MX2022009801A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
CN100510141C (zh) 耐氢脆化特性优良的超高强度薄钢板
HUE060841T2 (hu) Eljárás vas- és acéltermékek galvanizálására, különösen tûzihorganyzására
MX2020009042A (es) Recubrimiento de aleacion a base de zinc para acero y metodos.
WO2016146581A1 (en) Steel for hot forming
JP2015199995A (ja) 自動車部材の製造方法
Bleck et al. Production and Properties of IF(Interstitial-Free) Steel
WO2016193268A8 (de) Umformgehärtetes bauteil aus verzinktem stahl, herstellverfahren hierzu und verfahren zur herstellung eines stahlbandes geeignet zur umformhärtung von bauteilen
MX2020009043A (es) Aceros endurecidos por presion recubiertos con aleacion de zinc y metodo de fabricacion de estos.