MX2020009802A - Parte forjada de acero bainitico y un metodo de fabricacion del mismo. - Google Patents

Parte forjada de acero bainitico y un metodo de fabricacion del mismo.

Info

Publication number
MX2020009802A
MX2020009802A MX2020009802A MX2020009802A MX2020009802A MX 2020009802 A MX2020009802 A MX 2020009802A MX 2020009802 A MX2020009802 A MX 2020009802A MX 2020009802 A MX2020009802 A MX 2020009802A MX 2020009802 A MX2020009802 A MX 2020009802A
Authority
MX
Mexico
Prior art keywords
microstructure
steel
bainite
martensite
manufacturing
Prior art date
Application number
MX2020009802A
Other languages
English (en)
Inventor
Victor Bordereau
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MX2020009802A publication Critical patent/MX2020009802A/es

Abstract

Un acero para forjar partes mecánicas que comprende los siguientes elementos, expresados en porcentaje en peso: 0.15 % =C= 0.22 %; 1.6 % =Mn= 2.2 %; 0.6 % =Si= 1 %; 1 % =Cr= 1.5 %; 0.01 %=Ni= 1 %; 0 % =S= 0.06 %; 0 % =P= 0.02 %; 0 % =N= 0.013 %; y que tiene elementos opcionales 0 % =Al= 0.06 %; 0.03 % =Mo= 0.1 %; 0 % =Cu= 0.5 %; 0.01 % =Nb= 0.15%; 0.01% =Ti= 0.03%; 0% =V= 0.08 %; 0.0015 % =B= 0.004 %; el resto de la composición está formado de hierro e impurezas inevitables que resultan del procesamiento, la microestructura del acero tiene una microestructura por porcentaje de área que comprende una presencia acumulada de austenita residual y de islas de martensita-austenita entre 1 % y 20 %, el resto de la microestructura es bainita que tiene por lo menos 80%, en donde la fracción de los límites de grano de bainita con un ángulo de desorientación de 59.5° son por lo menos 7 % y con una presencia opcional de martensita entre 0 % y 10 %.
MX2020009802A 2018-03-23 2019-03-15 Parte forjada de acero bainitico y un metodo de fabricacion del mismo. MX2020009802A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2018/051970 WO2019180492A1 (en) 2018-03-23 2018-03-23 Forged part of bainitic steel and a method of manufacturing thereof
PCT/IB2019/052125 WO2019180563A1 (en) 2018-03-23 2019-03-15 Forged part of bainitic steel and a method of manufacturing thereof

Publications (1)

Publication Number Publication Date
MX2020009802A true MX2020009802A (es) 2020-10-14

Family

ID=61966033

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2020009802A MX2020009802A (es) 2018-03-23 2019-03-15 Parte forjada de acero bainitico y un metodo de fabricacion del mismo.

Country Status (16)

Country Link
US (1) US12203156B2 (es)
EP (1) EP3768868B8 (es)
JP (3) JP2021517609A (es)
KR (1) KR102476628B1 (es)
CN (1) CN111836908B (es)
CA (1) CA3092473C (es)
ES (1) ES2992076T3 (es)
FI (1) FI3768868T3 (es)
HU (1) HUE068050T2 (es)
MA (1) MA67583B1 (es)
MX (1) MX2020009802A (es)
PL (1) PL3768868T3 (es)
RU (1) RU2763027C1 (es)
UA (1) UA124913C2 (es)
WO (2) WO2019180492A1 (es)
ZA (1) ZA202005177B (es)

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1990431A1 (fr) * 2007-05-11 2008-11-12 ArcelorMittal France Procédé de fabrication de tôles d'acier laminées à froid et recuites à très haute résistance, et tôles ainsi produites
CN109972042B (zh) * 2019-04-17 2020-11-20 北京科技大学 一种屈服强度800MPa级耐低温耐腐蚀H型钢及其制备方法
CN110760752A (zh) * 2019-10-10 2020-02-07 邯郸钢铁集团有限责任公司 具有良好成型性能的nm300xt钢带及其生产方法
FR3103498B1 (fr) * 2019-11-22 2021-12-10 Electricite De France Pièce massive métallique et son procédé de fabrication
CN112593159A (zh) * 2020-12-10 2021-04-02 含山县朝霞铸造有限公司 一种汽车用钢铁材料及其制备方法
FR3123659A1 (fr) 2021-06-02 2022-12-09 Ascometal France Holding Sas Pièce en acier mise en forme à chaud et procédé de fabrication
CN116926412B (zh) * 2022-03-29 2026-01-16 宝山钢铁股份有限公司 一种贝氏体无缝钢管及其制造方法
EP4575006A1 (en) * 2023-12-19 2025-06-25 Politechnika Slaska Method of thermomechnical processing of low-carbon bainitic steel with retained austenite, application of the steel obtained by the method

Family Cites Families (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2744733B1 (fr) * 1996-02-08 1998-04-24 Ascometal Sa Acier pour la fabrication de piece forgee et procede de fabrication d'une piece forgee
JP3468031B2 (ja) * 1997-06-24 2003-11-17 住友金属工業株式会社 マルテンサイト・ベイナイト型熱間鍛造部品及びその製造方法
US6159312A (en) * 1997-12-19 2000-12-12 Exxonmobil Upstream Research Company Ultra-high strength triple phase steels with excellent cryogenic temperature toughness
WO2009102848A1 (en) 2008-02-15 2009-08-20 Dayton Progress Corporation Methods of thermo-mechanically processing tool steel and tools made from thermo-mechanically processed tool steels
SI2103704T1 (sl) * 2008-03-10 2012-11-30 Swiss Steel Ag Vroče valjani dolg proizvod in postopek za njegovo izdelavo
JP5483859B2 (ja) 2008-10-31 2014-05-07 臼井国際産業株式会社 焼入性に優れた高強度鋼製加工品及びその製造方法、並びに高強度かつ耐衝撃特性及び耐内圧疲労特性に優れたディーゼルエンジン用燃料噴射管及びコモンレールの製造方法
EP2520686B1 (en) 2009-12-29 2021-04-07 Posco Hot-pressed parts with zinc-plating and a production method for the same
FR2958660B1 (fr) 2010-04-07 2013-07-19 Ascometal Sa Acier pour pieces mecaniques a hautes caracteristiques et son procede de fabrication.
EP2683839B1 (en) * 2011-03-07 2015-04-01 Tata Steel Nederland Technology B.V. Process for producing high strength formable steel and high strength formable steel produced therewith
BR112014000086A2 (pt) 2011-07-06 2017-02-14 Nippon Steel & Sumitomo Metal Corp método para produção de folha de aço laminada a frio
US9523139B2 (en) * 2011-07-06 2016-12-20 Nippon Steel & Sumitomo Metal Corporation Cold-rolled steel sheet
US9809874B2 (en) * 2012-04-10 2017-11-07 Nippon Steel & Sumitomo Metal Corporation Steel sheet suitable for impact absorbing member and method for its manufacture
JP5728108B2 (ja) * 2013-09-27 2015-06-03 株式会社神戸製鋼所 加工性および低温靭性に優れた高強度鋼板、並びにその製造方法
EP3209806B1 (en) 2014-10-21 2020-11-25 Bharat Forge Limited An ultra-high strength thermo-mechanically processed steel
EP3272896B1 (en) 2015-03-16 2020-01-08 Nippon Steel Corporation Age-hardenable steel, and method for manufacturing components using age-hardenable steel
WO2016151345A1 (fr) * 2015-03-23 2016-09-29 Arcelormittal Pieces a structure bainitique a hautes proprietes de resistance et procede de fabrication
US10870901B2 (en) * 2015-09-22 2020-12-22 Tata Steel Ijmuiden B.V. Hot-rolled high-strength roll-formable steel sheet with excellent stretch-flange formability and a method of producing said steel

Also Published As

Publication number Publication date
WO2019180492A1 (en) 2019-09-26
MA67583B1 (fr) 2024-10-31
JP2026032201A (ja) 2026-02-25
EP3768868A1 (en) 2021-01-27
RU2763027C1 (ru) 2021-12-24
CN111836908B (zh) 2022-12-13
KR20200122376A (ko) 2020-10-27
CN111836908A (zh) 2020-10-27
EP3768868B8 (en) 2024-09-18
WO2019180563A1 (en) 2019-09-26
UA124913C2 (uk) 2021-12-08
BR112020017332A2 (pt) 2020-12-15
CA3092473A1 (en) 2019-09-26
CA3092473C (en) 2022-11-29
US20210010117A1 (en) 2021-01-14
JP2023182697A (ja) 2023-12-26
HUE068050T2 (hu) 2024-12-28
JP2021517609A (ja) 2021-07-26
US12203156B2 (en) 2025-01-21
EP3768868B1 (en) 2024-08-07
ZA202005177B (en) 2021-07-28
KR102476628B1 (ko) 2022-12-09
FI3768868T3 (fi) 2024-10-10
ES2992076T3 (es) 2024-12-09
PL3768868T3 (pl) 2024-10-28

Similar Documents

Publication Publication Date Title
MX2020009802A (es) Parte forjada de acero bainitico y un metodo de fabricacion del mismo.
MX2017015841A (es) Acero de alta resistencia y metodo de fabricacion.
UA117865C2 (uk) Високоміцна багатофазна сталь, спосіб її одержання та застосування
PH12019501995A1 (en) High-mn steel and production method therefor
MA51296B1 (fr) Tôles d'acier laminées à froid et traitées thermiquement, joints soudés par points par résistance et leurs procédés de fabrication
MA39075B1 (fr) Acier à haute résistance et procédé de fabrication
MX2019007170A (es) Hoja de acero enrollada en frio, de alta resistencia con alta capacidad de formacion y un metodo para fabricar la misma.
MA47998B1 (fr) Acier pour une trempe à la presse et pièce trempée à la presse fabriquée à partir d'un tel acier
MA63900B1 (fr) Tôle d'acier trempée et revêtue présentant une excellente aptitude au formage et son procédé de fabrication
MX380449B (es) Lámina de acero galvanizada de alta resistencia y método para la fabricación de la misma.
MX376541B (es) Hoja de acero laminada en caliente y método de fabricación relacionado.
NZ614798A (en) High-strength, high-toughness, wear-resistant steel plate and manufacturing method thereof
WO2015162939A8 (ja) 厚鋼板及びその製造方法
MA39417A1 (fr) Tôle d'acier doublement recuite a hautes caracteristiques mecaniques de resistance et de ductilite, procede de fabrication et utilisation de telles tôles
MA54523B1 (fr) Tôle d'acier laminée à froid traitée thermiquement et son procédé de fabrication
MX2019008649A (es) Producto de acero plano laminado en caliente que consiste en un acero de fase compleja con una microestructura y un metodo predominantemente bainitico para la fabricacion de un producto de acero plano.
US20200157651A1 (en) High-strength, hot rolled abrasive wear resistant steel strip
MX389192B (es) Lámina de acero galvanizada por inmersión en caliente de alta resistencia y método para fabricar la misma.
MA53708B1 (fr) Tôle d'acier laminée à chaud et son procédé de fabrication
MX2019001258A (es) Metodo de fabricacion de parte de acero que incluye la adicion de metal fundido a una parte de soporte y parte obtenida de esta manera.
MA58835B1 (fr) Tôle d'acier laminée à froid à résistance élevée et recuite après galvanisation et son procédé de fabrication
MX2022007054A (es) Hoja de acero laminada en frio tratada termicamente y un metodo de fabricacion de la misma.
MX2021007122A (es) Acero laminado en caliente y un metodo de fabricacion del mismo.
ZA202401756B (en) High strength press hardened steel part and method of manufacturing the same
MX2022009801A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.