MX376279B - Método para la fabricación de una lámina de acero galvanizada de alta resistencia. - Google Patents

Método para la fabricación de una lámina de acero galvanizada de alta resistencia.

Info

Publication number
MX376279B
MX376279B MX2016016705A MX2016016705A MX376279B MX 376279 B MX376279 B MX 376279B MX 2016016705 A MX2016016705 A MX 2016016705A MX 2016016705 A MX2016016705 A MX 2016016705A MX 376279 B MX376279 B MX 376279B
Authority
MX
Mexico
Prior art keywords
steel sheet
sup
sub
manufacturing
pickling
Prior art date
Application number
MX2016016705A
Other languages
English (en)
Other versions
MX2016016705A (es
Inventor
Hideyuki Kimura
Mai Aoyama
Yoshitsugu Suzuki
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2016016705A publication Critical patent/MX2016016705A/es
Publication of MX376279B publication Critical patent/MX376279B/es

Abstract

Se proporciona un método para la fabricación de una lámina de acero galvanizada de alta resistencia excelente en la adherencia de recubrimiento y el aspecto de superficie. Se llevaron a cabo las siguiente etapas: una primera etapa de calentamiento para mantener una lámina de acero que tiene una composición predeterminada en un intervalo de temperatura de 750 °C a 880 °C durante 20 s a 600 s en una atmósfera que tiene una concentración de H2 de 0.05% a 25.0% en volumen y un punto de rocío de -45 °C a - 10 °C, una etapa de enfriamiento, una etapa de laminación para laminar la lámina de acero con una reducción por laminación de 0.3% a 2.0%, una etapa de decapado para decapar la lámina de acero con una pérdida de peso por decapado de 0.02 gamos/m2 a 5 gramos/m2 en términos de Fe, una segunda etapa de calentamiento para mantener la lámina de acero en un intervalo de temperatura de 720 °C a 860 °C durante 20 seg a 300 seg en una atmósfera que tiene una concentración de H2 de 0.05% a 25.0% en volumen y un punto de rocío de -10 °C o inferior, y una etapa de galvanización para galvanizar la lámina de acero.
MX2016016705A 2014-07-02 2015-06-15 Método para la fabricación de una lámina de acero galvanizada de alta resistencia. MX376279B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014136461 2014-07-02
PCT/JP2015/002976 WO2016002141A1 (ja) 2014-07-02 2015-06-15 高強度溶融亜鉛めっき鋼板の製造方法

Publications (2)

Publication Number Publication Date
MX2016016705A MX2016016705A (es) 2017-04-25
MX376279B true MX376279B (es) 2025-03-07

Family

ID=55018722

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2016016705A MX376279B (es) 2014-07-02 2015-06-15 Método para la fabricación de una lámina de acero galvanizada de alta resistencia.

Country Status (7)

Country Link
US (1) US10570474B2 (es)
EP (1) EP3138931B1 (es)
JP (1) JP6086162B2 (es)
KR (1) KR101880086B1 (es)
CN (1) CN106661657B (es)
MX (1) MX376279B (es)
WO (1) WO2016002141A1 (es)

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10544477B2 (en) 2014-07-25 2020-01-28 Jfe Steel Corporation Method for manufacturing high-strength galvanized steel sheet
JP6249113B2 (ja) * 2016-01-27 2017-12-20 Ｊｆｅスチール株式会社 高降伏比型高強度亜鉛めっき鋼板及びその製造方法
KR102170060B1 (ko) 2016-01-27 2020-10-26 제이에프이 스틸 가부시키가이샤 고항복비형 고강도 아연 도금 강판 및 그의 제조 방법
WO2017131055A1 (ja) * 2016-01-27 2017-08-03 Ｊｆｅスチール株式会社 高降伏比型高強度亜鉛めっき鋼板及びその製造方法
WO2017169939A1 (ja) * 2016-03-31 2017-10-05 Ｊｆｅスチール株式会社 薄鋼板およびめっき鋼板、並びに、熱延鋼板の製造方法、冷延フルハード鋼板の製造方法、熱処理板の製造方法、薄鋼板の製造方法およびめっき鋼板の製造方法
JP6673290B2 (ja) 2017-05-19 2020-03-25 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
RU2675307C1 (ru) * 2017-12-14 2018-12-18 Публичное акционерное общество "Северсталь" (ПАО "Северсталь") Способ производства низколегированных рулонных полос с повышенной коррозионной стойкостью
US11530463B2 (en) 2018-03-30 2022-12-20 Jfe Steel Corporation High-strength galvanized steel sheet, high strength member, and method for manufacturing the same
US20210338860A1 (en) 2020-05-01 2021-11-04 Uv Innovators, Llc Ultraviolet (uv) light emission device employing visible light for operation guidance, and related methods of use, particularly suited for decontamination
CN113740142B (zh) * 2020-05-27 2024-07-12 宝山钢铁股份有限公司 一种镀锌板基体氢含量的获取方法
CN113969336B (zh) * 2020-07-23 2023-03-28 宝山钢铁股份有限公司 一种热镀锌钢板的制造方法、钢板及车用构件

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3826693A (en) * 1973-01-29 1974-07-30 Bethlehem Steel Corp Atmosphere controlled annealing process
JP2587724B2 (ja) 1990-11-30 1997-03-05 新日本製鐵株式会社 めっき密着性の良好な高Ｓｉ含有高張力溶融亜鉛めっき鋼板の製造方法
JP3020846B2 (ja) * 1995-07-31 2000-03-15 川崎製鉄株式会社 高張力溶融亜鉛めっき鋼板の製造方法
JP3956550B2 (ja) * 1999-02-02 2007-08-08 Ｊｆｅスチール株式会社 強度延性バランスに優れた高強度溶融亜鉛メッキ鋼板の製造方法
JP2001140021A (ja) * 1999-11-18 2001-05-22 Kawasaki Steel Corp めっき密着性に優れた高強度溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法
US6797410B2 (en) * 2000-09-11 2004-09-28 Jfe Steel Corporation High tensile strength hot dip plated steel and method for production thereof
JP2002173714A (ja) * 2000-09-29 2002-06-21 Kawasaki Steel Corp 高張力溶融めっき鋼板およびその製造方法
CN100552076C (zh) 2003-02-10 2009-10-21 杰富意钢铁株式会社 镀层附着性优良的合金化热镀锌钢板及其制造方法
JP4729850B2 (ja) * 2003-02-10 2011-07-20 Ｊｆｅスチール株式会社 めっき密着性に優れた合金化溶融亜鉛めっき鋼板およびその製造方法
JP3997931B2 (ja) * 2003-03-04 2007-10-24 Ｊｆｅスチール株式会社 高張力溶融亜鉛めっき鋼板の製造方法
CN101155935B (zh) * 2005-03-30 2011-08-03 新日本制铁株式会社 热浸镀热轧钢板的制造方法
JP5949253B2 (ja) * 2012-07-18 2016-07-06 新日鐵住金株式会社 溶融亜鉛めっき鋼板とその製造方法

Also Published As

Publication number Publication date
EP3138931A4 (en) 2017-05-03
US20170159151A1 (en) 2017-06-08
KR101880086B1 (ko) 2018-07-19
EP3138931B1 (en) 2018-04-25
MX2016016705A (es) 2017-04-25
EP3138931A1 (en) 2017-03-08
JPWO2016002141A1 (ja) 2017-04-27
JP6086162B2 (ja) 2017-03-01
KR20170010859A (ko) 2017-02-01
CN106661657A (zh) 2017-05-10
WO2016002141A1 (ja) 2016-01-07
CN106661657B (zh) 2018-11-06
US10570474B2 (en) 2020-02-25

Similar Documents

Publication Publication Date Title
MX376279B (es) Método para la fabricación de una lámina de acero galvanizada de alta resistencia.
MX2018006419A (es) Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia, metodo para la fabricacion de lamina de acero laminada en caliente para laminas de acero galvanizadas de alta resistencia, metodo para la fabricacion de lamina de acero laminada en frio para laminas de acero galvanizadas de alta resistencia, y lamina de acero galvanizada de alta resistencia.
MX2017002974A (es) Metodo e instalacion para la produccion de laminas de acero galvanizadas de alta resistencia.
MX2016013771A (es) Metodo para la produccion de lamina de acero galvanizada de alta resistencia y lamina de acero galvano-recocida de alta resistencia.
MX377677B (es) Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de la misma.
MX2017001106A (es) Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia.
MX2019010190A (es) Metodo para producir una tira de acero con una capa de recubrimiento de aleacion de aluminio.
MX2016002449A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX382046B (es) Metodo para la produccion de lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de lamina de acero recocida despues de galvanizada de alta resistencia.
EP3144406A4 (en) High-strength cold rolled steel sheet having excellent ductility, hot-dip galvanized steel sheet and method for manufacturing same
SG10201707903VA (en) Hot-dip zinc alloy coated steel sheet excellent in coating adhesion, and method for producing the same
MX386346B (es) Método para la producción de láminas de acero recocidas después de galvanizadas de alta resistencia.
WO2014129106A8 (ja) 無方向性電磁鋼板製造用の熱延鋼板およびその製造方法
MX2019004000A (es) Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
MX387221B (es) Metodo para preparar y tratar un substrato de acero.
MX374164B (es) Procedimiento de fabricacion de un componente de acero provisto de un revestimiento metalico de proteccion contra la corrosion.
MX376280B (es) Método para la fabricación de una lámina de acero recocida después de galvanizada de alta resistencia.
MX380705B (es) Lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma.
WO2017001283A3 (de) Vorrichtung und verfahren zur herstellung eines verzinkten stahlbandes
MX2015015064A (es) Lamina de acero galvanizado y metodo para producir el mismo.
WO2014119263A8 (ja) 溶融Al－Zn系めっき鋼板とその製造方法
MX2018005073A (es) Metodo de produccion de lamina de acero galvanizada por inmersion en caliente.
MX2020004627A (es) Metodo de fabricacion de lamina de acero galvanizada-recocida.
PH12013502223A1 (en) Hot-dip zinc-aluminium alloy coated steel sheet having high corrosion resistance and formability and method for producing the same
ZA201807922B (en) Composition for reducing the removal of material by pickling in the pickling of metal surfaces that contain galvanized and/or ungalvanized steel

Legal Events

Date Code Title Description
FG Grant or registration