NO170218B

NO170218B - SPHERICAL CATALYST CARRIER, CATALYST CONTAINING THE CARRIER AND MANUFACTURING THEREOF

Info

Publication number: NO170218B
Application number: NO870844A
Authority: NO
Inventors: Jean-Loup Lacombe; Michel Avaro; Claude Brun
Original assignee: Atochem
Priority date: 1986-03-27
Filing date: 1987-03-02
Publication date: 1992-06-15
Also published as: CN87102324A; NO870844D0; FR2596396B1; JPS62232405A; FI871337L; DE3767187D1; EP0239475B1; ES2011644A6; FI86643C; EP0239475A1; FI86643B; CA1295312C; FR2596396A1; NO170218C; NO870844L; JPH0832732B2; FI871337A0; CN1010021B; ATE59847T1

Abstract

Spherical catalyst support manufactured by reaction of an organic chlorine compound in the presence of an electron donor and of a mixture of an alkylmagnesium compound and of an organic aluminium compound, characterised in that the organic chlorine compound, in combination with an electron donor, is reacted with the preliminary mixture of alkylmagnesium compound, aluminoxane and/or aluminosiloxane and optionally of electron donor. This support, subjected to a second activation with a chlorine compound, is impregnated with a transition metal halide.

Description

Arklignende, vannsikker gjenstand. Sheet-like, waterproof item.

Nærværende oppfinnelse vedrorer nye for-formede arklignende gjenstander. De nye gjenstander etter oppfinnelsen er særlig anvendelige for påforing på betongoverflater og vil her bli beskrevet hovedsakelig med henvisning til slik anvendelse. Det skal imidlertid forstås at den samme beskrivelse finner anvendelse på mutatis mutandis, for tetning av andre overflater, særlig slike som forekommer ved bygninger og entre-penorarbeider. The present invention relates to new pre-formed sheet-like objects. The new objects according to the invention are particularly applicable for application to concrete surfaces and will be described here mainly with reference to such application. However, it should be understood that the same description applies mutatis mutandis, for sealing other surfaces, especially those that occur in buildings and construction work.

Det er kjent å tette overflater, særlig av bietong, ved å påfore dem en membran av en bituminos blanding eller lignende, It is known to seal surfaces, particularly of beetong, by applying a membrane of a bituminous mixture or similar,

Kfr. kl. 37C-5/02 Cf. at 37C-5/02

som i det vesentlige er ugjennomtrengelig for fuktighet og vanndamp. (Uttrykket "bituminos blanding" anvendes her som omfattende blandinger som inneholder asfalt, tjære og bek.). Det er også kjent at en slik blanding kan danne et klebemiddel for et lag av overtrekksmateriale,.'f .eks. fliser eller paneler av linoleum, polyvinylklorid, termoplastisk materiale, naturlig eller kunstig sten eller kork og treblokker eller parkett-stav\ Tidligere er slike membraner blitt dannet ved påforing in situ av varm, flytende bitumen,- tjære eller bek eller en kold" opplosning eller emulsjon av bitumen, tjære eller bek. Hvis onsket, kan membranen forsterkes med lateks, asbestfibre eller andre arter fyllstoffer. Det er også kjent å fremskaffe en vanntett membran ved bruk av filmer av polyetylen eller syntetisk eller naturlig gummi eller bituminos takfilt. which is essentially impermeable to moisture and water vapour. (The term "bituminous mixture" is used here to include mixtures containing asphalt, tar and pitch.). It is also known that such a mixture can form an adhesive for a layer of covering material, e.g. tiles or panels of linoleum, polyvinyl chloride, thermoplastic material, natural or artificial stone or cork and wooden blocks or parquet sticks \ In the past, such membranes have been formed by applying in situ hot, liquid bitumen, - tar or pitch or a cold" solution or emulsion of bitumen, tar or pitch. If desired, the membrane can be reinforced with latex, asbestos fibers or other types of fillers. It is also known to provide a waterproof membrane using films of polyethylene or synthetic or natural rubber or bituminous roofing felt.

Disse kjente metoder lider av alvorlige ulemper. Således krever generelt de kjente fremgangsmåter dannelse av et lag av et tetningsmiddel in situ med ledsagende vanskeligheter i å sikre et ensartet lag og. arbeidsutgifter på stedet. Dessuten hvor overflaten er et betonggulv som er gjenstand for oppstigende fuktighet, må klebemidlet danne en vann- og alkali-motstandsdyktig membran, hvilket betyr at klebemidler på vannbasis ikke kan brukes. I praksis betyr dette at en bituminos blanding må påfores varm på gulvet, hvilket er meget uhensiktsmessig, eller en bituminos blanding på opplosningsbasis må anvendes, hvilket er dyrt og omfatter ildsfare. Vanligvis krever klebemiddel-blandinger som er i bruk for tiden, for å tillate fordampning av opplosningsmiddel eller vanninnholdet, å anbringes på plass noen tid for bekledningsmaterialet påfores hvis en tilfredsstillende binding skal oppnås, og dette er igjen uhensiktsmessig. These known methods suffer from serious disadvantages. Thus, in general, the known methods require the formation of a layer of a sealant in situ with accompanying difficulties in ensuring a uniform layer and. labor costs on site. Also, where the surface is a concrete floor subject to rising moisture, the adhesive must form a water- and alkali-resistant membrane, which means that water-based adhesives cannot be used. In practice, this means that a bituminous mixture must be applied hot to the floor, which is very inappropriate, or a solution-based bituminous mixture must be used, which is expensive and involves a fire hazard. Generally, adhesive compositions currently in use, to allow evaporation of the solvent or water content, require to be set in place for some time before the coating material is applied if a satisfactory bond is to be achieved, and this is again inconvenient.

Det er også kjent å utstyre baksiden av bekledningsmaterialet, særlig gulvfliser, med et lag av konfcaktklebemiddel dekket av et beskyttende ark som fjernes for overtrekksmaterialet brin-ges på plass. Imidlertid er det ikke mulig å fremskaffe-et tilfredsstillende vann- og alkali-motstandsdyktig, kontinuerlig overtrekk under bekledningsmaterialet med disse midler, It is also known to equip the back of the cladding material, particularly floor tiles, with a layer of concrete adhesive covered by a protective sheet which is removed before the covering material is put in place. However, it is not possible to provide a satisfactory water- and alkali-resistant, continuous covering under the cladding material with these means,

særlig på en typisk ruff, stovet betongoverflate. especially on a typical rough, stoked concrete surface.

Det er nå blitt funnet at vesentlige fordeler oppnås ved bruk av forformede membraner av vanntette, trykkfolsomme klebestoffer. Slike membraner kan fremstilles i stor målestokk i en fabrikk og deretter brukes på arbeidsstedet. Oppfinnelsen fremskaffer en gjenstand som er egnet for dannelse av et vannsikkert lag på en overflate, og gjenstanden består av et arklignende underlag, som er av en organisk polymer eller en metallfolie, og sammenhengende med dette en membran av et vannsikrende, trykkfolsomt klebemiddel og karakteristisk er at gjenstanden er minst 15 cm bred, membranen er minst 0,0 25 cm tykk, fortrinnsvis 0,063 - 0,4 cm tykk og særlig 0,23 - 0,33 cm tykk, og klebemidlet er et bitumen- og gummi-holdig klebemiddel, fortrinnsvis en blanding av naturlig eller syntetisk gummi og bitumen, idet forholdet mellom bitumen og gummi er fra 80:20 til 95:5. It has now been found that significant advantages are obtained by the use of preformed membranes of waterproof pressure sensitive adhesives. Such membranes can be produced on a large scale in a factory and then used at the workplace. The invention provides an object which is suitable for the formation of a waterproof layer on a surface, and the object consists of a sheet-like substrate, which is of an organic polymer or a metal foil, and connected to this a membrane of a waterproof, pressure-sensitive adhesive and characteristically is that the object is at least 15 cm wide, the membrane is at least 0.0 25 cm thick, preferably 0.063 - 0.4 cm thick and especially 0.23 - 0.33 cm thick, and the adhesive is a bitumen and rubber-containing adhesive, preferably a mixture of natural or synthetic rubber and bitumen, the ratio between bitumen and rubber being from 80:20 to 95:5.

Det er nodvendig, hvis en tilfredsstillende forsegling på en betongoverflate skal oppnås at den vannsikrende gjenstand skal være i stand til å strekke seg og trykke seg sammen med bevegelsen av betongen uten at forseglingen nedbrytes. Bevegelsen i betongen opptrer både når betongen krymper etter herdning og når det opptrer ved herdningen betongsprekker som åpner og lukker seg i avhengighet av temperaturen faller og stiger, hvilket uungålig opptrer i bygninger som utsettes for normale værbetingelser. Under slike bevegelser i betongen var der en tendens hos tidligere kjente gjenstander å glippe. Denne glipning er den ikke gjenvunne bevegelse av gjenstanden over betongen, hvilken etterlater et område udekket som tidligere var dekket. Denne glipning opptrer ikke hvis klebemidlet er minst 0,025 cm tykk. It is necessary, if a satisfactory seal on a concrete surface is to be achieved, that the waterproofing object should be able to stretch and compress with the movement of the concrete without the seal breaking down. The movement in the concrete occurs both when the concrete shrinks after curing and when concrete cracks occur during curing that open and close depending on the temperature falling and rising, which inevitably occurs in buildings exposed to normal weather conditions. During such movements in the concrete, there was a tendency for previously known objects to slip. This slip is the unrecovered movement of the object over the concrete, which leaves an area uncovered that was previously covered. This slippage does not occur if the adhesive is at least 0.025 cm thick.

Membranen kan være et lag av klebemiddel alene eller klebemidlet kan inneholde forsterkende materialer, særlig for å gi membranen mekanisk styrke. Hvis onsket, kan membranen inneholde flere lag av vanntette., trykkfolsomme klebestoffer (idet klebestoffet kan være det samme eller forskjellig i de for-skjellige lag), og lagene kan være adskilt av forsterkende materiale i form av et ark. The membrane can be a layer of adhesive alone or the adhesive can contain reinforcing materials, in particular to give the membrane mechanical strength. If desired, the membrane may contain several layers of waterproof, pressure-sensitive adhesives (the adhesive may be the same or different in the different layers), and the layers may be separated by reinforcing material in the form of a sheet.

Dan nye konstruksjon etter oppfinnelsen kan deles opp i to ge-nerelle typer- Den forste type er de som er utformet for å gi en sammenhengende, vannsikker membran heftende til en overflate og den ytre overflate av membranen har en ikke-klebende overflate i Den annen art er de som er utformet, for å gi på en. overflate et lag av et trykkfolsomt kontaktklebemiddel, enten over hele overflaten og således samtidig gi en kontinuerlig vannsikker membran, eller bare over utvalgte deler av overflaten. The new construction according to the invention can be divided into two general types - The first type are those designed to provide a continuous, waterproof membrane adhering to a surface and the outer surface of the membrane has a non-adhesive surface in the second species are those that are designed, to give on one. surface a layer of a pressure-sensitive contact adhesive, either over the entire surface and thus at the same time provide a continuous waterproof membrane, or only over selected parts of the surface.

Ved utforelsesformene for den forste type er substratet en arklignende bærer (f.eks. en film av en organisk polymer slik som polyetylen, som det forklares i detalj nedenfor), til hvilken membranen hefter (dvs. bæreren og membranen forblir ved-heftende til hverandre når konstruksjonen brukes), og overflaten på bæreren vendt bort fra membranen er ikke-klebende. Ved utformningen ifolge den annen type er substratet et beskyttende overtrekk (f.eks. silikonisert papir eller lignende materiale som det forklares i detalj nedenfor), som fysisk kan fjernes fra membranen uten vesentlig å skade denne. Det vil selvfølge-lig være klart at for lagringsformål må overflaten på membranen motsatt substratet ha et beskyttende overtrekk. De nye gjenstander etter oppfinnelsen fremstilt i fabrikken, lagret og bragt til bruksstedet, foreligger i form av laminater av det beskyttende overtrekk, membranen og enten en arklignende bærer (den forste type) eller et annet beskyttende overtrekk- (den annen type). Konstruksjonene er hensiktsmessige tilgjengelige i form av ruller. In embodiments of the first type, the substrate is a sheet-like support (eg, a film of an organic polymer such as polyethylene, as explained in detail below) to which the membrane adheres (ie, the support and the membrane remain adherent to each other when the construction is used), and the surface of the carrier facing away from the membrane is non-adhesive. In the design according to the second type, the substrate is a protective covering (e.g. siliconized paper or similar material as explained in detail below), which can be physically removed from the membrane without significantly damaging it. It will of course be clear that for storage purposes the surface of the membrane opposite the substrate must have a protective coating. The new objects according to the invention produced in the factory, stored and brought to the place of use, are in the form of laminates of the protective coating, the membrane and either a sheet-like carrier (the first type) or another protective coating (the second type). The constructions are conveniently available in the form of rolls.

De nye. gjenstander kan anvendes til å påfore en utsatt side av membranen til overflaten som skal tettes og/eller forsynes med et lag kontaktklebemiddel. I sistnevnte tilfelle fjernes det beskyttende overtrekk på et egnet trinn for å gjore den a/inen overflate av membranen ferdig for påforing av et bekledningsmateriale på denne. Hvis nodvendig oppnås dannelsen av en kontinuerlig, vannsikker tetning over hele overflaten ved ytterligere påfbringer, slik at hver membran overlapper sin nabo. The new. objects can be used to apply an exposed side of the membrane to the surface to be sealed and/or provided with a layer of contact adhesive. In the latter case, the protective covering is removed in a suitable step to make the a/in surface of the membrane ready for the application of a cladding material on it. If necessary, the formation of a continuous, waterproof seal over the entire surface is achieved by further application, so that each membrane overlaps its neighbor.

Breddene for de nye gjenstander vil variere sterkt, f.eks., fra 15 til 120 cm, og også mer, avhengig av den bruk de skal ha. Generelt vil de være 15 til 90 cm brede, og bredder i den ovre del av dette område, f.eks. 60 til 90 cm, er foretrukket hvor det hele av en overflate skal gjores vannsikkert. Tykkelsen av de nye gjenstander kan også variere sterkt, avhengig av den tilsiktede sluttanvendelse, men vil vanligvis være opp til 0,6 eller 0,9 cm. The widths of the new objects will vary greatly, for example, from 15 to 120 cm, and even more, depending on the use they will have. In general, they will be 15 to 90 cm wide, and widths in the upper part of this range, e.g. 60 to 90 cm, is preferred where the whole of a surface is to be made waterproof. The thickness of the new items can also vary greatly, depending on the intended end use, but will usually be up to 0.6 or 0.9 cm.

En rekke bitumen- og gummi-holdige klebemidler kan anvendes med hell for membranen, men klebemidlet må være slik at membranen vil klebe til den foreliggende overflate uten bruk av varme eller ytterligere bindemidler. Således, for påforing til overflater av betong som er relativt ru og stovet, må klebelaget være minst 0,0 25 cm tykt, fortrinnsvis 0,063 til 0,5 cm. Jo tykkere klebemiddel!aget er jo bedre er den vannsikrende virkning, men generelt er et lag på 0,063 til 0,4 cm tilfredsstillendej og tykkelsene i den ovre del av dette område er foretrukket. Således for gjenstander av den forste type er en bærer med et enkelt lag klebemiddel på 0,23 til 0,33 cm's tykkelse foretrukket, og for gjenstander av den annen type er en lignende tykkelse foretrukket. Dette kan f.eks. oppnås ved to lag klebemiddel, hvert 0,1 til 0,18 cm tykt på hver side av et sentralt forsterkende materiale. A number of bitumen- and rubber-containing adhesives can be used successfully for the membrane, but the adhesive must be such that the membrane will stick to the existing surface without the use of heat or additional binders. Thus, for application to surfaces of concrete that are relatively rough and stony, the adhesive layer must be at least 0.0 25 cm thick, preferably 0.063 to 0.5 cm. The thicker the adhesive layer, the better the waterproofing effect, but generally a layer of 0.063 to 0.4 cm is satisfactoryj and the thicknesses in the upper part of this range are preferred. Thus, for articles of the first type, a carrier with a single layer of adhesive of 0.23 to 0.33 cm's thickness is preferred, and for articles of the second type, a similar thickness is preferred. This can e.g. achieved by two layers of adhesive, each 0.1 to 0.18 cm thick on either side of a central reinforcing material.

Det bitumen- og gummi-holdige klebemiddel kan tlannes av naturlig eller syntetisk gummi., opprinnelig eller regenerert, blan-det inn i bitumen for å gi en jevn" blanding. Vektsforholdet mellom bitumen og gummi er fortrinnsvis fra 80:20 til 95:5, særlig ca. 90:10. Vanligvis har egnede blandinger myknings-punkter (målt etter ring- og kule-metoden) på 60 til 110°C, The bitumen-rubber-containing adhesive may be prepared from natural or synthetic rubber, original or regenerated, mixed into bitumen to give a uniform mixture. The weight ratio of bitumen to rubber is preferably from 80:20 to 95:5 , especially about 90:10. Generally, suitable mixtures have softening points (measured by the ring and ball method) of 60 to 110°C,

og penetreringsverdier på 150 - 300 ved 25°C (100 g .5 sekunder, Institute of Petroleum metode). and penetration values of 150 - 300 at 25°C (100 g .5 seconds, Institute of Petroleum method).

En rekke materialer kan brukes for å fremskaffe beskyttende overtrekk i de nye gjenstander etter oppfinnelsen. Papir som "har et låsbart overtrekk, f.eks. silikonisert papir eller papir med et overtrekk av en vinylkloridpolymer, er tilfredsstillende. Andre materialer omfatter filmer av organiske po-lymere, særlig vinylkloridpolymere. A variety of materials can be used to provide protective coverings in the new articles according to the invention. Paper having a lockable coating, eg siliconized paper or paper with a coating of a vinyl chloride polymer, is satisfactory. Other materials include films of organic polymers, particularly vinyl chloride polymers.

En rekke materialer kan brukes som den arklignende bærer som danner en del av de nye gjenstander av den forste type angitt foran, og det er særlig fordel ved en slik gjenstand at de kan brukes til å gi en. vannsikker tetning over en flate som-for-ener egenskapene for membranen og bæreren. Det er vanligvis onskelig at bæreren skal være. i det vesentlige ugjennomtrengelig for vann. For mange formål er det onskelig at bæreren skal være slik at etter påforing på flaten har den evne til å strekke seg med bevegeligheten for betongen eller annet materiale, f.eks. som et resultat av krympning, og da under opprett-holdelse av en fuktighets- og fuktighetsdampsikker tetning. For dette er det onskelig at den kombinerte gjenstand av bæreren og membranen skal ha, ved 20°C, en forlengelse ved brudd på minst 300 %, en strekkstyrke på minst 1,5 kg/cm bredde og en Elmendorf-rivstyrke på minst 750 g. Imidlertid hvor strekkbarheten og fleksibiliteten er mindre viktig enn andre egenskaper kan bærere som ikke tilfredsstiller disse krav brukes. F.eks. er det onskelig for noen formål å anvende metallfolie, særlig av kobber eller aluminium, som bærer. A number of materials can be used as the sheet-like support which forms part of the new articles of the first type indicated above, and it is particularly advantageous for such an article that they can be used to provide a. waterproof seal over a surface that unites the properties of the membrane and the carrier. It is usually desirable for the carrier to be. substantially impermeable to water. For many purposes, it is desirable for the carrier to be such that, after being applied to the surface, it has the ability to stretch with the movement of the concrete or other material, e.g. as a result of shrinkage, and then while maintaining a moisture and moisture vapour-proof seal. For this, it is desirable that the combined article of the carrier and membrane should have, at 20°C, an elongation at break of at least 300%, a tensile strength of at least 1.5 kg/cm width and an Elmendorf tear strength of at least 750 g However, where stretchability and flexibility are less important than other properties, carriers which do not satisfy these requirements can be used. E.g. is it desirable for some purposes to use metal foil, especially of copper or aluminium, as a carrier.

De foretrukne bærere er filmer av naturlig gummi eller av en syntetisk, organisk polymer slik som polyetylen, som er foretrukket, f.eks. det i handelen tilgjengelige under varenavnet "POLYTHENE", polypropylen eller annet polyolefin, et polyamid, en polyester, f.eks. polyetylenterefthalat, et polyurethan, polyvinylklorid, en kopolymer av vinylklorid og vinylidenklo-rid, eller en syntetisk gummi slik som polykloropren eller butylgummi. The preferred supports are films of natural rubber or of a synthetic organic polymer such as polyethylene, which is preferred, e.g. the commercially available under the trade name "POLYTHENE", polypropylene or other polyolefin, a polyamide, a polyester, e.g. polyethylene terephthalate, a polyurethane, polyvinyl chloride, a copolymer of vinyl chloride and vinylidene chloride, or a synthetic rubber such as polychloroprene or butyl rubber.

Særlig for bruk ved veibygning er det onskelig at bæreren skal være slik at varm asfalt kan helles direkte på den uten skade-lig virkning på den vannsikrende tetning. For dette formål skal bæreren være i stand til å motstå en temperatur på minst 150°C. Especially for use in road construction, it is desirable for the carrier to be such that hot asphalt can be poured directly onto it without damaging the waterproof seal. For this purpose, the carrier must be able to withstand a temperature of at least 150°C.

Skjont cellulære filmer kan anvendes som bærere, er bærerene. vanligvis ikke komprimérbare og har en tykkelse på hoyst O,6 cm. Although cellular films can be used as carriers, the carriers are usually not compressible and have a thickness of at most 0.6 cm.

Andre arklignende bærere omfatter vevete og ikke-vevete stof-fer av naturlige eller syntetiske fibre, dvs. stabile fibre eller kontinuerlige filamenter, f.eks. et vevet glassduk, hes-s<*>ian, bomull eller annet fiberlerret eller bituminos takfilt. Other sheet-like supports include woven and non-woven fabrics of natural or synthetic fibers, i.e. stable fibers or continuous filaments, e.g. a woven glass cloth, hess<*>ian, cotton or other fiber canvas or bituminous roofing felt.

Hvis onsket, kan overflaten av bæreren som vender bort fra membranen, behandles for å beskytte den for skade og/eller slik at den gir en forbedret kontaktflate for andre materialer, f.eks. betong, som deretter påfores den. Således kan denne overflate på bæreren være profilert og/eller bære et lag av klebemiddel som fortrinnsvis er vannmotstandsdyktig og kan være det samme som eller forskjellig fra klebemidlet i membranen, til hvilket lag er vedheftet en avsetning av granulært eller pulverisert materiale, f.eks. finfordelt aggregat eller annet organisk eller uorganisk materiale, f.eks. sand- eller kork-granuler. If desired, the surface of the support facing away from the membrane can be treated to protect it from damage and/or to provide an improved contact surface for other materials, e.g. concrete, which is then applied to it. Thus, this surface of the carrier may be profiled and/or carry a layer of adhesive which is preferably water resistant and may be the same as or different from the adhesive in the membrane, to which layer is adhered a deposit of granular or powdered material, e.g. finely divided aggregate or other organic or inorganic material, e.g. sand or cork granules.

Som angitt foran, anvendes de nye gjenstander som inneholder en arklignende bærer, til å. gi en vannsikker membran på en flate, særlig en betongflate, ved å påfore den utsatte side av membranen på overflaten, og en rekke overlappene elementer anvendes, hvis nodvendig, for å gi en kontinuerlig membran over hele flaten. Etter at gjenstanden er blitt påfort på denne måte er det vanlig å danne eller anbringe en annen overflate opp til den, f.eks. en annen masse av betong, en sand-eller sementmortel eller annen gulvfinish, et lag av asfalt eller et bekledningsmateriale. As indicated above, the novel articles containing a sheet-like support are used to provide a waterproof membrane on a surface, particularly a concrete surface, by applying the exposed side of the membrane to the surface, and a number of overlapping elements are used, if necessary, to provide a continuous membrane over the entire surface. After the object has been applied in this way, it is usual to form or place another surface up to it, e.g. another mass of concrete, a sand or cement mortar or other floor finish, a layer of asphalt or a cladding material.

Som angitt foran er de forformede membraner med et beskyttende overtrekk på begge sider særlig verdifulle for lett og hurtig å sikre bekledningsmaterialet til overflaten, særlig betong. Folgelig kan gjenstandene ifolge oppfinnelsen brukes for å sikre bekledningsmaterialet til en overflate ved (a) å fjerne det beskyttende overtrekk fra en side av den fordannede membran, (b) å påfore den således utsatte flate av membranen til overflaten, (c) fjerne det beskyttende overtrekk fra den andre overflate av membranen og (d) påfore bekledningsmaterialet på denne annen side av membranen. As indicated above, the preformed membranes with a protective coating on both sides are particularly valuable for easily and quickly securing the cladding material to the surface, especially concrete. Accordingly, the objects according to the invention can be used to secure the cladding material to a surface by (a) removing the protective coating from one side of the formed membrane, (b) applying the thus exposed surface of the membrane to the surface, (c) removing the protective overlay from the other surface of the membrane and (d) apply the cladding material to this other side of the membrane.

Skjont forannevnte fremgangsmåte er mest verdifull ved bekledning av gulv, er den like anvendelig for bekledning av vegger og tak. Bekledningsmaterialets natur er ikke kritisk, og et-hvert av de bekledningsmaterialer som er nevnt foran, og også takfliser, f.eks. av polystyren, kan anvendes. Although the aforementioned method is most valuable for covering floors, it is equally applicable for covering walls and ceilings. The nature of the cladding material is not critical, and each of the cladding materials mentioned above, and also roof tiles, e.g. of polystyrene, can be used.

De nye gjenstander etter oppfinnelsen kan fremstilles uten vanskelighet etter i og for seg kjente arbeidsmåter. Det er foretrukket å anvende klebemidler som ikke er basert på opplosningsmiddel og således påfores varmt. Således kan klebemidlet påfores varmt ved hjelp av en egnet anordning for å sikre ensartet lag på substratet. Hvis det er onsket å inn-arbeide et arklignende, forsterkende lag på membranen, kan dette f.eks. oppnås ved å presse et lerret inn i klebemiddel-laget. Et slikt forsterkende lag er vanligvis ikke nodvendig når en bærer anvendes, men det er ofte av hjelp hvor ingen bærer foreligger for å forebygge noen altfor stor ødeleggelse av membranen når de beskyttende overtrekk fj ernes. The new objects according to the invention can be produced without difficulty according to methods known per se. It is preferred to use adhesives that are not based on solvents and are thus applied hot. Thus, the adhesive can be applied hot using a suitable device to ensure a uniform layer on the substrate. If it is desired to incorporate a sheet-like, reinforcing layer on the membrane, this can e.g. achieved by pressing a canvas into the adhesive layer. Such a reinforcing layer is usually not necessary when a carrier is used, but it is often helpful where no carrier is present to prevent excessive destruction of the membrane when the protective coverings are removed.

De folgende eksempler illustrerer oppfinnelsen. The following examples illustrate the invention.

EKSEMPEL 1 EXAMPLE 1

En gjenstand ifolge oppfinnelsen ble fremstilt ved å overtrekke hver side av en polyetylenfilm ("POLYTHENE"), 30 cm bred og 0,013 cm tykk med et overtrekk av et bituminost klebemiddel inneholdende 7 vektsdeler naturlig gummi og 93 velctsdeler ok-sydert bitumen, 0,3 cm tykt, og avsette fintfordelt silisium-oksyd på et av overtrekkene. Strukturen ble anbragt på et betonggulv med den side som har silisiumoksydsanden avsatt på seg overst, og et betongavretningslag av sand og sement ble derpå påfort. En tetning motstandsdyktig mot fuktighet og fuktig damp mellom gulvbasen og avretningen ble således oppnådd. An article according to the invention was produced by coating each side of a polyethylene film ("POLYTHENE"), 30 cm wide and 0.013 cm thick with a coating of a bituminous adhesive containing 7 parts by weight of natural rubber and 93 parts by weight of ox-synthesized bitumen, 0.3 cm thick, and deposit finely divided silicon oxide on one of the coatings. The structure was placed on a concrete floor with the side that has the silicon oxide sand deposited on top, and a concrete leveling layer of sand and cement was then applied. A seal resistant to moisture and damp steam between the floor base and screed was thus achieved.

EKSEMPEL 2 EXAMPLE 2

En. annen gjenstand ble fremstilt ved å overtrekke en side av One. other object was produced by covering one side of

en polyetylenfilm som anvendt i eksempel 1 med et overtrekk 0,3 cm tykt av bituminost klebemiddel som anvendt i eksempel 1. a polyethylene film as used in example 1 with a coating 0.3 cm thick of bituminous adhesive as used in example 1.

En slik gj enstand ble ahbragt på en betonggulvbasis- med den klebemiddelovertrukne side opp mot betongen. En gulvavret-rfing. av sand og sement ble derpå påfort. På denne måte ble oppnådd en tetning mellom- gulvbasisen og avretningen som var motstandsdyktig mot fuktighet og fuktighetsdamp. Such a work was carried out on a concrete floor base - with the adhesive-coated side facing the concrete. A floor sweeper rfing. of sand and cement was then continued. In this way, a seal was achieved between the floor base and screed which was resistant to moisture and moisture vapour.

En annen slik gjenstand ble anbragt over et betongtak med den klebemiddelovertrukne side opp mot betongen. Jord ble derpå fyllt inn over taket. En tetning motstandsdyktig mot fuktighet og fuktighetsdamp mellom taket og jorden ble således oppnådd. Another such object was placed over a concrete roof with the adhesive-coated side facing the concrete. Soil was then filled in over the roof. A seal resistant to moisture and moisture vapor between the roof and the ground was thus achieved.

Claims

Sheet-like object suitable for forming a waterproof layer on a surface, which object comprises a sheet-like substrate which is an organic polymer or a metal foil and connected to this a membrane of a waterproof, pressure-sensitive adhesive, characterized in that the object is at least 15 cm wide , the membrane is at least 0.025 cm thick, preferably 0.063 to 0.4 cm thick, and especially 0.23 to 0.33 cm thick, and that the adhesive is a bitumen- and rubber-containing adhesive, preferably a mixture of natural or synthetic rubber and bitumen, and the weight ratio between bitumen and rubber is from 80:20 to 95:5.