OA20362A - Method for selecting the composition of a building material comprising excavated clay soil, method and system for preparing such a building material. - Google Patents

Abstract

The invention relates to a method (100) for selecting the composition of a building material comprising excavated clayey soil, said building material composition being to comprise amounts of deflocculating agent and activating agent adapted to the excavated clayey soil, said method comprising a step of receiving (130) a measured value of at least one physicochemical property of an excavated clayey soil and a step of selecting (170) an amount of deflocculating agent and an amount of activating agent adapted to the excavated clayey soil. Furthermore, the invention also relates to a method (200) for calibrating a calculation algorithm for determining the composition of a site building material, to a building material formed from an excavated clayey soil and to a system (400) for preparing a building material comprising an excavated clayey soil.

Description

DESCRIPTION

TITLE: METHOD FOR SELECTING THE COMPOSITION OF A CONSTRUCTION MATERIAL COMPRISING EXCAVED CLAY EARTH, METHOD AND SYSTEM FOR PREPARING SUCH A CONSTRUCTION MATERIAL

The invention relates to the field of construction materials, and more particularly that of materials that can be used in construction such as construction binders or concretes. The invention relates to a method for selecting the composition of a construction material comprising excavated clay soil. The invention also relates to a method for calibrating a calculation algorithm for determining the composition of a site construction material comprising excavated clay soil, on a construction material formed from excavated clay soil and on a system for preparing a construction material comprising excavated clay soil.

[Prior art

Cement is the second most consumed resource in the world, with more than 4 billion tons of materials produced each year in the world and this consumption is constantly increasing driven by the growing demand for housing and infrastructure. Cement is a binder, usually hydraulic, which, when mixed with water, hardens and solidifies. After hardening, the cement retains its strength and stability even when exposed to water. There are a wide variety of cements used by the world. In addition, cement preparation processes are becoming increasingly sophisticated and automated systems have been developed for the preparation of various concretes (FR2751911, EP2296854).

However, all conventional cements contain a clinker at a percentage ranging from 5% for certain blast furnace cements to a minimum of 95% for Portland cement, which is the most used cement in the world today. Clinker results from the firing of a mixture composed of approximately 80% limestone and 20% aluminosilicates (such as clays). This cooking, the clinkering, is done at a temperature of more than 1200°C, such a cement preparation process therefore involves high energy consumption. Additionally, the chemical conversion of limestone to lime also releases carbon dioxide. As a result, the cement industry generates around 8% of global CO ₂ emissions. Faced with this challenge, the industry and researchers are studying the possibilities of reducing the impact of carbon dioxide emissions generated by the cement industry.

In addition to these carbon emissions is added in the context of major urban development projects the management of excavated soil. This excavated soil is generally stored or used for filling in quarries or developing parks, but this represents a potential use that is much lower than the available volumes. In addition, it has been proposed to use this excavated earth for the manufacture of building materials, however this application comes up against the problems of insufficient mechanical strength of raw earth constructions on the one hand and the non-optimal carbon footprint during from the use of metakaolin.

Indeed, the cements proposed based on raw earth, as described in the document FR3016376, have either physical properties, such as the improvement of the mechanical resistance, the reduction of the capillary absorption, or even the reduction of the liquid permeability, too low; or they require the addition of a portion of Portland cement to be able to present acceptable mechanical properties.

Concerning cements based on metakaolin, the mixture of lime or sodium hydroxide and metakaolin during the hydration of the cement will induce a pozzolanic reaction. This reaction improves the binding properties of metakaolin-based cements. Because of these properties, building materials based on metakaolin have been proposed, comprising in particular a flashed metakaolin combined with sodium hydroxide, as described in document FR3034094. Nevertheless, the formation of metakaolin requires a heat treatment of kaolinitic clays to lead to the dehydroxylation of the crystalline structure of kaolinite inducing an unfavorable carbon balance, especially when taking into account the transport of excavated soil to thermal units.

Thus, there is a need for new uses of excavated clay soil that can advantageously allow a reduction in greenhouse gas emissions and the preparation of construction material such as a construction binder or site concrete with a low carbon footprint. while having mechanical properties at least equivalent or even superior to the mechanical properties of cements commonly used in the field of construction.

[Technical problem]

The object of the invention is therefore to remedy the drawbacks of the prior art. In particular, the object of the invention is to propose a method for selecting the composition of a building material comprising an excavated clay soil, said method making it possible to form a building material, such as a building binder, making it possible to reduce the emission of greenhouse gases on the one hand, such as carbon dioxide, while conferring mechanical characteristics adapted to its use in the field of construction and on the other hand to propose a site concrete comprising such binding and able to improve the comfort of the inhabitants compared to a concrete formed from Portland cement.

The invention also aims to provide a construction material formed from an excavated clay soil with mechanical properties suitable for its use in the field of construction while constituting a way of recovering the excavated clay soil.

The invention also aims to provide a method and a system for preparing a construction material comprising an excavated clayey earth making it possible to reduce the emission of greenhouse gases compared to a conventional construction material of the Portland cement type. .

[Brief description of the invention]

To this end, the invention relates to a method for selecting the composition of a construction material comprising an excavated clay soil, said construction material composition having to comprise quantities of deflocculating agent and of activating agent adapted to the excavated clay soil, said method being implemented by a computer device comprising a calculation module, said method comprising:

A step of reception, by the calculation module, of a measured value of at least one physicochemical property of an excavated clay soil; and

A step of selection, by the calculation module, of a quantity of deflocculating agent and of a quantity of activating agent adapted to the clay soil excavated on the basis of a comparison of the value or values measured at reference values, said reference values comprising correlations between measured values of at least one physicochemical property of a clay soil and quantities of deflocculating agent and of activating agent suitable for said clay soil to form a building material.

Such a selection process has the advantage of being able to select at least some of the constituents of a construction material based on excavated clay soil so as to form a construction material, such as a construction binder or a site concrete, with mechanical properties equivalent to the mechanical properties of conventional building materials using clinkers. Indeed, with the methods of the prior art, the building materials obtained from excavated earth are generally not sufficiently efficient from a mechanical point of view to allow wide use.

In addition, the constituents selected via the selection process (i.e. excavated clay soil, deflocculating agent and activating agent) allow the formation of a construction material according to a less energy-consuming preparation process.

Finally, the construction material comprising an excavated clay soil having preferably not undergone a combustion stage, it retains advantageous hygrothermal properties making it possible to improve the comfort of the inhabitants compared to a concrete formed from Portland cement.

According to other optional characteristics of the selection process:

the at least one physicochemical property is selected from: the clay content in the excavated clay soil, the nature of the clays, the grain size, the impurity content, the content of non-clay mineralogical fractions, the pollution content, the analysis elemental, metal oxide content, salinity, pH, and total clay exchange capacity of the excavated clay soil. Preferably, the at least one physicochemical property is selected from: the clay content in the excavated clay soil, the nature of the clays, the grain size, the content of non-clay mineralogical fractions, the elemental analysis, the content of metal oxides , salinity, pH, and total clay exchange capacity of the excavated clay soil. More preferably, the at least one physicochemical property is selected from: the content of clays in the excavated clay soil, the nature of the clays, the grain size, the content of non-clay mineralogical fractions, the content of metal oxides, and the total clay exchange capacity of the excavated clay soil. Such physicochemical properties are the most likely to provide values of deflocculating agent and activating agents adapted to the excavated clay soil considered.

the at least one physicochemical property is measured on a pretreated excavated clay soil, said pretreatment being selected from: grinding, sorting, sieving and/or drying of the excavated clay soil. This advantageously makes it possible to minimize the error on the measurements carried out. Preferably, the pretreatment comprises at least one fractionation, for example by sieving or sedimentation, more preferably a fractionation at 50 μm and for example a fractionation at 20 μm.

It comprises beforehand the receipt of a desired mechanical property value of the construction material and the step of selecting the quantities of deflocculating agent and of activating agent further comprises an exclusion of the quantities of deflocculating agent and of activating agent that will not allow the building material to exhibit the desired mechanical property value. Thus, an operator can easily set an objective performance criterion for the construction material whose composition is expected. There is therefore a gain in time and performance in the process of recovering excavated soil for a construction application.

the step of selecting, by the calculation module, a quantity of deflocculating agent and a quantity of activating agent adapted to the excavated clay soil comprises the implementation of a previously calibrated calculation algorithm .

the previously calibrated calculation algorithm was obtained by implementing a statistical method of supervised learning.

According to another aspect, the invention further relates to a method for calibrating a calculation algorithm for determining the composition of a construction material, such as a construction binder or site concrete, for example put implemented by a digital device comprising a learning module, characterized in that it comprises:

A first step of receiving, by the learning module, a measured value of at least one physicochemical property of an excavated clay soil;

A second step of reception, by the learning module, of a quantity value of deflocculating agent and of a quantity value of activating agent which, once added to the excavated clay soil, make it possible to form a material of construction ;

A third step of reception, by the learning module, of a measured value of at least one mechanical property of the construction material formed from the excavated clayey earth, the value of at least one physicochemical property of which was received during from the first receiving step, and from the quantities of deflocculating agent and activating agent received during the second receiving step; and

A step of creating a correlation, by the learning module, between the measured values received in order to calibrate a calculation algorithm.

The combination of excavated clay soil, deflocculating agent and activating agent makes it possible to produce a building material with appreciable mechanical properties and the selection method according to the invention allows the selection of the appropriate quantity values. However, considering the complexity and the variability of the physicochemical properties of the excavated clay soils, the inventors have developed a method for calibrating a calculation algorithm making it possible to overcome this complexity. Such a calibration process makes it possible to propose values for the quantity of deflocculating agent and activating agent that are highly adapted to the excavated clay soil. Note that the order of reception does not matter and helps to clarify the description of the process.

According to another aspect, the invention further relates to a method for preparing a building material from excavated clay soil, the method comprising:

A step for measuring at least the physicochemical property of the excavated clay soil;

A selection step according to a method for selecting the composition of a construction material comprising an excavated clay soil according to the invention; and

A step of mixing excavated clay soil, deflocculating agent and activating agent according to the selected composition.

Such a process, simple and fast, makes it possible to reduce the emission of greenhouse gases during its implementation compared to the implementation of a process for preparing a conventional construction material such as Portland cement.

According to other optional characteristics of the preparation process, it also comprises:

o a step of measuring the physico-chemical or mechanical property of the building material being formed, during the mixing step, o a step of comparing the measured values with predetermined values of the physico-chemical or mechanical property of the building material being formed, and o when the measured values differ from the predetermined physicochemical or mechanical property values of the construction material being formed, a step of adding at least one complementary ingredient.

Thus, the verification of the properties of the building material being formed makes it possible to carry out quality control online, that is to say preferably in real time, so as to ensure that the building material formed will present the best mechanical properties. as close as possible to the expected mechanical properties. Indeed, a deviation can be identified at the time of mixing and corrected before the construction material is finalized and a fortiori used.

According to another aspect, the invention relates to a computer program product configured to execute a selection method according to the invention.

According to another aspect, the invention relates to a computer program product configured to execute a calibration method according to the invention.

According to another aspect, the invention further relates to a building material formed from an excavated clay soil characterized in that it comprises a deflocculating agent and an excavated clay soil. Preferably, the invention further relates to a building material formed from an excavated clay soil characterized in that it comprises an excavated clay soil, an activating agent and a deflocculating agent, said deflocculating agent representing at least 0.1% by weight of the building material, preferably at least 0.25% by weight of the building material.

The activating agent is not systematically found in the construction binder or in the site concrete because it can react with constituents of the excavated clay soil and be transformed. Nevertheless, in certain cases, a construction material according to the invention, formed from an excavated clayey earth, may additionally comprise an activating agent.

Such a construction material ΪΟΓ111Θ 3 from υ’υΐΊΘ ΪΘΓΓΘ STynGuSe ΘΧ03νθθ ρΓθβθΓιΐθ υθ8 mechanical properties adapted to its use in the field of construction while constituting a way of recovering excavated clay soil.

According to other optional characteristics of the construction material according to the invention, it comprises a mixture of different types of clays.

Further, it may comprise at least 2% by weight silt particles, preferably at least 4% by weight, more preferably at least 6% by weight. The silt particles are in particular particles having a diameter of between 2 μm and 50 μm.

A building material according to the invention may comprise metal oxides at a content of at least 2% by weight of the building material.

A construction material in accordance with the invention may also comprise blast furnace slags.

A building material according to the invention may comprise from 30% to 80% by weight of excavated clay soil, from 0.1% to 10% by weight of deflocculating agent, and from 5 to 10% by weight of high-grade slags. stoves. In this case, the building material preferably corresponds to a building binder.

A construction material according to the invention may comprise:

between 5 and 20% by weight of raw clay from excavated clay soil;

between 0.1 and 3% by weight of deflocculating agent;

between 3 and 15% by weight of an activating agent;

between 25 and 45% by weight of sand; and between 35 and 55% by weight of aggregates;

said construction material then preferably corresponding to site concrete.

As presented in the examples, the building materials according to the invention have improved mechanical performance.

In addition, the excavated clay soil may advantageously have been pretreated, said pretreatment being selected from: grinding, sorting, sieving and/or drying of the excavated clay soil. The pre-processing can for example comprise a fractionation.

According to another aspect, the invention relates to a method for preparing a building material according to the invention from an excavated clay soil comprising:

a stage of excavation of clay soil;

optionally a step of sifting the excavated clay soil when the excavated clay soil contains stones retained by a 2 cm sift; and a mixing step 340 of excavated clay soil, preferably the fraction less than 50 μm, of deflocculating agent and of activating agent.

According to another aspect, the invention further relates to a system for preparing a building material comprising excavated clay soil, said system comprising:

At least one container comprising excavated clay soil;

At least one container comprising a deflocculating agent;

At least one container comprising an activating agent;

A mixing device, with automated means of transport between the containers and the mixing device;

A control module configured to generate output signals intended for automated means of transport in order to transport determined quantities of deflocculating agent and activating agent to the mixing device.

Advantageously, the system for preparing a construction material according to the invention comprises a means of communication configured to receive data on a quantity of deflocculating agent and a quantity of activating agent determined, adapted to the excavated clay soil. ; the control module being configured to generate output signals intended for the automated means of transport so as to transport the quantities of deflocculating agent and of activating agent determined towards the mixing device.

Preferably, the system for preparing a construction material according to the invention comprises: A means for measuring at least one physicochemical property of the excavated clay soil, A calculation means capable of implementing a computer program configured to perform: A step for obtaining a measured value of at least one physicochemical property of the excavated clay soil; and A step of determining a quantity of deflocculating agent and a quantity of activating agent suitable for the excavated clay soil on the basis of a comparison of the measured value(s) with reference values.

In particular, the invention further relates to a system for preparing a building material comprising excavated clay soil, said system comprising:

At least one container comprising excavated clay soil;

At least one container comprising a deflocculating agent;

At least one container comprising an activating agent;

A mixing device, with automated means of transport between the containers and the mixing device;

ιο

A means of measuring at least one physicochemical property of the excavated clay soil;

A means of calculation capable of implementing a computer program configured to carry out:

o A step for obtaining a measured value of at least one physicochemical property of the excavated clay soil, and o A step for determining a quantity of deflocculating agent and a quantity of suitable activating agent to the excavated clay soil based on a comparison of the measured value(s) to reference values; and

A control module configured to generate output signals intended for the automated means of transport in order to transport the quantities of deflocculating agent and activating agent determined towards the mixing device.

Such a system makes it possible in an automated way to form a construction binder or possibly a site concrete (with addition of fillers) from excavated clay soil, these construction materials having mechanical properties equivalent to the mechanical properties of conventional materials having an imprint much higher carbon.

Other advantages and characteristics of the invention will appear on reading the following description given by way of illustrative and non-limiting example, with reference to the appended Figures:

[Fig 1] represents the steps of a method for selecting the composition of a construction material comprising clay soil excavated according to an embodiment of the present invention. Dotted steps are optional.

[Fig 2] represents the steps of a calibration method of a calculation algorithm for determining the composition of a site construction material. Dotted steps are optional.

[Fig 3] represents the stages of a process for preparing a building material from excavated clay soil. Dotted steps are optional.

[Fig 4] shows a method for preparing a building material according to one embodiment of the invention.

[Fig 5] shows a method for preparing a building material according to one embodiment of the invention. Dotted steps are optional.

[Fig 6] represents a diagram showing a functional architecture of the system for preparing a building material comprising an excavated clay soil according to the invention. The solid line arrows represent means of transport and the dotted arrows transfers of data or instructions, in particular to said means of transport.

Aspects of the present invention are described with reference to flow charts and/or block diagrams of methods, apparatus (systems), and computer program products according to embodiments of the invention. In the figures, flowcharts and block diagrams illustrate the architecture, functionality, and operation of possible implementations of systems, methods, and computer program products according to various embodiments of the present invention.

In this regard, each block in the flowcharts or block diagrams may represent a system, device, module, or code, which includes one or more executable instructions to implement the specified logical function(s). In some implementations, the functions associated with the blocks may appear in a different order than that shown in the figures. For example, two blocks shown in succession may, in fact, be executed substantially simultaneously, or the blocks may sometimes be executed in reverse order, depending on the functionality involved. Each block in the block diagrams and/or flowchart, and combinations of blocks in the block diagrams and/or flowchart, can be implemented by special hardware systems that perform the specified functions or acts or perform combinations of special equipment and computer instructions.

[Description of the invention]

In the remainder of the description, the expression “clayey earth” should be understood as corresponding to earth originating from a soil comprising clays, or more generally from a fine-grained loose formation, and therefore comprising one or more rocky materials based on hydrated silicates or aluminosilicates with a lamellar structure. In particular, a clay soil may for example correspond to soils of the sandy-clay loam type, clay-loam soils, clay-sandy soils, clay soils. Preferably a clay soil comprises at least 25% by weight clay, preferably at least 30% by weight clay, more preferably at least 40% by weight clay. The content by weight of clay can be determined by standard methods of the prior art such as the granulometric method described in standard NF X31-107. In addition, preferably, a clay soil in the context of the invention comprises at most 95% by weight of clay, preferably at most 90% by weight of clay, more preferably at least 80% by weight of 'clay.

The expression “excavated clay soil” corresponds in the sense of the invention to clay soil obtained following a stage where the soil has been dug, for example during leveling and/or earthworks operations, with a view to building, build or fill. In particular, within the meaning of the invention, the excavated clay soil may or may not be moved outside the production site. Preferably and according to an advantage of the invention, the excavated earth is used on the production site or at a distance of less than 200 km. In addition, advantageously, the clayey earth excavated in the context of the invention is raw excavated clayey earth, that is to say that it has not undergone a calcination step. In particular, that is to say that it has not undergone any prior heat treatment. For example, this corresponds to a clay soil that has not undergone a temperature rise above 300°C, preferably above 200°C and more preferably a temperature above 150°C. Indeed, the raw clay soil can undergo a heating step requiring a rise in temperature generally of substantially equal to 150°C but no calcination step. Clay as conventionally used has a relatively constant grain size profile with sizes below 2 µm. Excavated clay soil can have different grain size profiles. In the context of the invention, an excavated clay soil may comprise particles of a size greater than 2 μm, preferably greater than 20 μm, preferably greater than 50 μm and for example greater than 75 μm as determined according to the ASTM standard. D422-63. Preferably, the excavated clay soil does not contain any aggregate larger than 2 cm as determined according to standard NF EN 933-1.

The expression "% by weight" in connection with the excavated clay soil, the composition, the binder or the site concrete must be understood as being a proportion in relation to the dry weight of the composition, the binder or the site concrete. The dry weight corresponds to the weight before the addition of water, for example, necessary for the formation of a building material.

The expression “construction material” within the meaning of the present invention corresponds to a construction binder or site concrete. The site concrete will in particular include fillers such as aggregates and/or sand.

The term "deflocculating agent" means any compound which, in aqueous suspension, will dissociate aggregates and colloids. Deflocculating agents have for example been used in the context of drilling or oil extraction to make the clay more fluid and facilitate extraction or drilling.

The term "activating agent" means any composition having the function of accelerating the dispersion of an aluminosilicate source, promoting the formation of stable hydrates with low solubility and the formation of a compact structure with these hydrates, increasing thus the mechanical strength of the materials incorporating such an activation composition.

The term "particle size" within the meaning of the invention corresponds to the distribution of the elements and particles of the clay soil according to the relative weight of the different classes of particles, identified by their size and constituting the mineral skeleton of the soil. Five particle size classes exist: - Clays (0 to 2 micrometers) - Fine silts (2 to 20 micrometers) - Coarse silts (20 to 50 micrometers) - Fine sands (50 to 200 micrometers) - Coarse sands (200 at 2000 micrometers).

The expression "nature of clays" corresponds in the sense of the invention to the chemical and/or mineralogical properties of clays. This corresponds in particular to the chemical composition of clays but also to their mineralogy and their physical characteristics (such as specific surface, porosity, morphology). For example, this may correspond to the identification of clay by its usual name (e.g. kaolinite, illite, Montmorillonite, Smectite, Bentonite, Chlorite and Vermiculite).

The expression "metallic trace elements" corresponds within the meaning of the invention to metallic chemical elements and in particular they correspond within the meaning of the invention to metals selected from: iron, lead, mercury, uranium, chromium, copper, cadmium, silver, gold, zinc, nickel or titanium.

The term “substantially equal” within the meaning of the invention corresponds to a value varying by less than 20% with respect to the compared value, preferably by less than 10%, even more preferably by less than 5%.

By “model” or “rule” or “calculation algorithm”, it is necessary to understand within the meaning of the invention a finite sequence of operations or instructions making it possible to select values of quantity of deflocculating agent and of agent of activation, that is to say for example to form previously defined groups Y associated with scores or categories according to correlation with quantities of deflocculating agent D and activating agent A on the one hand and one or more values of physicochemical properties of excavated clay soil E. The implementation of this finite series of operations makes it possible, for example, to assign a label Y _o to an observation described by a set of characteristics D _o . A _o , E _o , thanks for example to the implementation of a function f capable of reproducing Y having observed D, A and E.

Y = f (D,A,E) + e where e symbolizes the noise or measurement error.

Here Y can for example be the capacity (yes/no) to form a building material.

Advantageously, the calculation algorithm can establish previously defined groups, associate other values such as values of mechanical properties M of the construction material that can be formed from these quantities. Thus with the formula “M=f(D,A,E)+e” it is possible to select quantity values making it possible to form building materials having predetermined mechanical properties.

By “supervised learning method”, we mean within the meaning of the invention a process making it possible to define a function f from a base of n labeled observations (Xi n, Yi.n, Dv.n, , Ai „ _n , , Ev.n) where for example Y = f (D,A,E) + e or M = f (D,A,E) + e.

The term “process”, “calculate”, “determine”, “display”, “extract”, “compare” or more broadly “executable operation”, within the meaning of the invention, means an action performed by a device or a processor except if the context indicates otherwise. In this regard, operations refer to actions and/or processes of a data processing system, for example a computer system or an electronic computing device, which manipulates and transforms data represented as physical (electronic ) in computer system memories or other information storage, transmission or display devices. In particular, calculation operations are carried out by the processor of the device, the data produced is written in a corresponding field in a data memory and this or these fields can be returned to a user, for example through a Human Machine Interface adapted, such as by way of non-limiting examples a screen of a connected object, formatting such data. These operations can be based on applications or software.

The terms or expressions "application", "software", "program code", and "executable code" mean any expression, code or notation, of a set of instructions intended to cause data processing to perform a particular function directly or indirectly (e.g. after a conversion operation to another code). Sample program code may include, but is not limited to, a subroutine, function, executable application, source code, object code, library, and/or any other sequence of instructions designed for execution on a computer system.

The term "processor", within the meaning of the invention, means at least one hardware circuit configured to execute operations according to instructions contained in a code. The hardware circuit may be an integrated circuit. Examples of a processor include, but are not limited to, a central processing unit, a graphics processor, an application-specific integrated circuit ("ASIC" in English terminology), and a programmable logic circuit. A single processor or several other units can be used to implement the invention.

The term “coupled”, within the meaning of the invention, is understood to mean connected, directly or indirectly, with one or more intermediate elements. Two elements can be coupled mechanically, electrically or linked by a communication channel.

The expression "man-machine interface" within the meaning of the invention corresponds to any element allowing a human being to communicate with a particular computer and without this list being exhaustive, a keyboard and means allowing in response to the orders entered the keyboard to perform displays and possibly to select using the mouse or a touchpad elements displayed on the screen. Another example of embodiment is a touch screen making it possible to select directly on the screen the elements touched by the finger or an object and possibly with the possibility of displaying a virtual keyboard.

In the claims, the term comprising or comprising does not exclude other elements or other steps.

In the remainder of the description, the same references are used to designate the same elements. The reference signs cannot be understood as limiting the scope of the invention. In addition, the different characteristics presented and/or claimed can be advantageously combined. Their presence in the description or in different dependent claims does not exclude this possibility.

As mentioned, the current observation is that the excavated soil is numerous, often considered as waste and therefore constitutes, during site development, an additional burden for developers. This management, and in particular the pollution that may be generated by the transport of this excavated soil, is added to the pollution generated by the preparation of conventional cement (e.g. Portland).

Faced with this observation, the inventors have identified a process for selecting a composition for a construction material using excavated clay soil and making it possible to obtain a construction binder with mechanical properties similar to the mechanical properties of conventional cement (e.g. Portland ). From this process, they are capable, as will be presented in the examples, of generating a construction binder which could be advantageously, but not limitatively, used as a replacement for Portland cement, lime or CSA. Thus, the waste (i.e. excavated clay soil) combined in specific proportions with a deflocculating agent and an activating agent, can become a raw material in a construction process.

In addition, given its method of preparation on the one hand and the use of excavated clay soil, the construction material according to the invention has the advantage of having a carbon footprint at least twice lower than most materials. construction, or hydraulic binder, the most widely used in the world today (ie Portland cement). Indeed, a construction material according to the invention is mainly made up of a clayey earth and having a zero or lower clinker content than equivalent products and makes it possible, with equivalent mechanical properties, to reduce CO ₂ emissions and the costs of production. In addition, the clay soil has preferably not undergone a calcination step, an energy-intensive step which also generates the emission of greenhouse gases and more particularly of carbon dioxide.

Finally, advantageously, as will be presented in the examples, a building binder according to the invention allows the manufacture of building materials having mechanical properties at least equivalent to Portland cement and much higher than "low carbon" materials, such as those previously described.

Thus, according to a first aspect, the invention relates to a method 100 for selecting the composition of a building material comprising excavated clay soil. Given that the construction binder can then be used to form a site concrete, following the addition of a filler for example, the selection method 100 can alternatively correspond to a method 100 for selecting the composition of a site concrete.

In particular, for a preparation of a construction material from excavated clay soil to be possible, the composition of construction material must comprise quantities of deflocculating agent and of activating agent adapted to the clay soil. excavated.

For this, a method according to the invention, preferably implemented by a computer device comprising a calculation module can comprise a step of reception 130, by the calculation module, of a measured value of at least one physicochemical property of excavated clay soil; and a selection step 170, by the calculation module, of a quantity of deflocculating agent and of a quantity of activating agent adapted to the excavated clay soil.

In addition, a method according to the invention may comprise steps such as: preliminary treatments 110 of the excavated clay soil, measurements 120 of physicochemical properties of the excavated clay soil, reception 140 of the desired mechanical property value of the material of construction, the generation 150 of a plurality of combinations of deflocculating agent and activating agent quantity values, the determination 160 of a desired mechanical property value of the construction material, or the determination of at minus a physicochemical or mechanical property value of the building material being formed.

As illustrated in Figure 1, the selection method according to the invention may include a step 110 of prior treatment of the excavated clay soil. Thus, advantageously, the measurement value(s) are obtained from a sample of excavated clay soil having undergone a prior treatment step 110 of the excavated clay soil.

This prior treatment step may for example include or consist of fractionation, grinding, sorting (e.g. depending on the color), sieving and/or drying of the excavated clay soil.

In particular, given that, in the context of the present invention, the clayey earth is an excavated earth, it may comprise coarse elements or fractions of large dimensions which it would be advantageous to eliminate in the first stages of the process. Thus, in particular, the method according to the invention may comprise a deletion of the elements having at least one dimension greater than 1 cm (per centimeter), preferably a deletion of the elements having at least one dimension greater than 0.2 cm. Preferably, the method according to the invention can comprise a suppression of the elements having at least a size greater than 1 cm, preferably greater than 475 μm (for micrometer), more preferably greater than 75 μm as determined according to the ASTM D422-63 standard.

In addition, the method according to the invention may include a step 120 of measuring at least one physicochemical property of an excavated clay soil. This step is preferably carried out on a sample of excavated clay soil and can be carried out on site or in a specialized laboratory. Indeed, depending on the physicochemical property(ies) measured, it will be possible or not to have transportable instruments.

The measurement step 120 can for example comprise a measurement step of:

the clay content in the excavated clay soil, measured for example by a granulometric method such as that described in standard NF X31-107;

the nature of the clays, obtained for example by X-ray diffractometry;

the content of impurities and in particular metallic trace elements, obtained for example by elemental analysis using an ICP-MS device;

salinity using a conductivity meter measuring the conductivity of clay soil washing water;

the pH using a pH meter measuring the pH of clay soil washing water; and the total clay exchange capacity of the excavated clay soil measured for example by the so-called methylene blue method according to standard NF EN 933-9+A1.

The measurement step 120 can therefore include, for example, the use of a pH meter, an X-ray diffractometer, a conductivity meter, an electron microscope, a mercury porosimeter, a spectrofluorometer, an ICP-MS (Inductively Coupled Plasma Mass Spectrometry for inductively coupled plasma mass spectrometry), an HPLC-MS (liquid phase chromatography coupled to mass spectrometry), a GC-MS (gas chromatography coupled with mass spectrometry), measurement of the specific surface by the BET method (specific surface measurement, for Brunauer-Emmett-Teller), a particle sizer, or even an ATG rheometer (for thermogravimetric analysis).

The method according to the invention comprises a step 130 of receiving a measured value of at least one physicochemical property of an excavated clay soil. This step can in particular be implemented by the calculation module of the digital device.

The physicochemical property of the excavated soil, the measured value of which is received, can be selected from: the clay content in the excavated clay soil, the nature of the clays, the grain size, the impurity content, the presence of pollutants, the limit liquid content, plastic limit, metal oxide content, salinity, pH, and total clay exchange capacity of the excavated clay soil. For example, the physicochemical property of the excavated soil whose measured value is received can for example be selected from: the clay content in the excavated clay soil, the nature of the clays, the granulometry, the content of impurities, the content of oxides metals, salinity, pH, and total clay exchange capacity of the excavated clay soil. Preferably, the physicochemical property of the excavated earth whose measured value is received can for example be selected from: the clay content in the excavated clayey earth, the liquid limit, and the plasticity limit. More preferably, the physicochemical property of the excavated earth whose measured value is received includes the clay content in the excavated clayey earth.

In particular, the content of impurities can correspond to the content of metals and advantageously of metal oxides such as: iron oxide or aluminum oxide.

Preferably, measured values of at least two physicochemical properties of an excavated clay soil are received, more preferably at least three and even more preferably at least four. Indeed, depending on the number of physicochemical properties taken into account, the result of the selection process may be of better quality.

The physicochemical property or properties are the physicochemical properties of widely studied soils such as the pH, the granulometry, the clay content.

In particular, the method according to the invention comprises the reception 130 of a combination of measured values selected from:

the clay content in the excavated clay soil and the nature of the clays;

the clay content and total clay exchange capacity of the excavated clay soil;

The clay content and the amount of pollutants;

pH and clay content in the excavated clay soil; or the total clay exchange capacity of the excavated clay soil and the grain size.

Further, as shown in Figure 1, the method according to the invention may include receiving 140 a desired mechanical property value of a material of construction.

Indeed, beyond the selection of the composition of a building material, the method according to the invention can advantageously make it possible to select a composition of a building material allowing the preparation of a building material which will present mechanical property data. Thus, a user will be able, according to his needs, to select the most accurate quantities to obtain a building material that meets his needs.

The desired mechanical properties of the building material can for example be selected from: compressive strength, drying shrinkage, setting time, flexural strength, tensile strength, Young's modulus, Poisson's ratio .

For example, the method of the invention may include receiving a desired compressive strength value for the material of construction. This value can for example consist of a lower limit (e.g. 20 MPa, for MegaPascal, or 30 MPa) or even a fixed value (e.g. 40 MPa).

Preferably, when the method according to the invention comprises the reception 140 of a desired mechanical property value of the construction material, the step of selecting 170 of;

amounts of deflocculating agent and activating agent further includes an exclusion 171 of the amounts of deflocculating agent and activating agent that will not allow the material of construction to exhibit the desired mechanical property value. Thus, this can for example correspond to a selection via the calculation algorithm of all the values of A and D which make it possible, from a measured value of E, to obtain a value M = 40 MPa. Alternatively, in the absence of a calculation algorithm, this may include filtering all the values from a database for which the value of M is less than 30 MPa.

The step 130 of receiving a measured value of at least one physicochemical property of an excavated clay soil may be followed by a step of generating 150 a plurality of combinations of values of the quantity of deflocculating agent on the one hand and activating agent on the other hand. Following the generation of this plurality of values, the calculation module can set up a step 170 for selecting values as will be described below.

In addition, the method according to the invention may include a step 160 for determining at least one physicochemical property value or mechanical property value expected for the construction material. This step is for example implemented by a calculation module.

From the measured values of physicochemical properties of the excavated clay soil and from values of the quantity of deflocculating agent and of activating agent generated then it is possible to determine a mechanical property value of a building material formed from of the excavated soil and the quantities of deflocculating agent and activating agent considered.

The method according to the invention comprises a step 170 of selecting a quantity of deflocculating agent and a quantity of activating agent adapted to the excavated clay soil. This step can for example be implemented by a calculation module.

The amount of deflocculating agent and activating agent can correspond to a volume, a mass or even a proportion. Preferably, the quantity corresponds to a proportion relative to a quantity of excavated clay soil to be added to the construction material composition. Alternatively, if the quantity corresponds to a volume or a mass then it is associated with a quantity of excavated clay soil to be added to the construction material composition.

In addition, the selection 170 of an amount of deflocculating agent and an amount of activating agent may include determining the nature of the deflocculating agent and/or the activating agent to be added. For example, the nature of these agents may correspond to a family of chemical molecules or to a particular chemical molecule or even to a combination of molecules.

Indeed, the deflocculating agent can be a combination of molecules and the selection of a quantity of deflocculating agent can then correspond to the selection of quantity of each of the molecules composing the deflocculating agent. The same goes for the activating agent which may correspond to one molecule or to a plurality of molecules.

Advantageously, the selection is made on the basis of a comparison of the measured value or values of the physicochemical property of an excavated clay soil with reference values. In particular, the reference values comprise correlations between measured values of at least one physicochemical property of a clayey earth and quantities of deflocculating agent and of activating agent adapted to said clayey earth to form a material of construction.

Deflocculating agent

Many compounds can act as deflocculating agents and many are generally known to those skilled in the art.

In the context of the invention, the deflocculating agent is in particular a nonionic surfactant such as a polyoxyethylene ether. The polyoxyethylene ether can for example be selected from: a poly(oxyethylene) lauryl ether.

The deflocculating agent can also be an anionic agent such as an anionic surfactant. In particular, the anionic agent can be selected from: alkylaryl sulphonates, aminoalcohols, carbonates, silicates, fatty acids, humates (e.g. sodium humates), carboxylic acids, lignosulphonates (e.g. lignosulphonates of sodium), polyacrylates, phosphates or polyphosphates such as sodium hexametaphosphate, sodium tripolyphosphate, sodium orthophosphate, carboxymethylcelluloses and mixtures thereof.

The deflocculating agent can also be a polyacrylate. It can then be selected, for example, from sodium polyacrylate and ammonium polyacrylate.

The deflocculating agent can also be an amine selected, for example, from: 2-amino-2-methyl-1-propanol; mono-, di- or triethanolamine; isopropanolamines (1-Amino2-propanol, diisopropanolamine and triisopropanolamine) and N-alkylated ethanolamines.

The deflocculating agent can also be a silicate such as sodium silicate, sodium metasilicate or sodium trisilicate.

Alternatively, as presented previously, the deflocculating agent can be a mixture of compounds, such as a mixture comprising at least two compounds selected from: nonionic surfactant, anionic agent, polyacrylate, amine and organophosphorus compound.

In particular, the deflocculating agent can be a mixture of sodium silicate and sodium carbonate.

Preferably, the deflocculating agent is selected from: a lignosulphonate (e.g. sodium lignosulphonate), a polyacrylate, a humate and mixtures thereof.

The deflocculating agent is preferably in the form of a salt.

However, the invention cannot be limited to the deflocculating agents mentioned above, any type of deflocculating agent known to those skilled in the art can be used instead of said deflocculating agents mentioned above.

Activation agent

It is the activating agent, in conjunction with the excavated clay soil and the deflocculating agent, which will give the construction material its mechanical properties of interest.

Without being limited by theory, the activating agent can allow the constitution of a network between the clay sheets which will bring its mechanical properties to the construction material according to the invention.

In particular, the activating agent can include metal oxides and/or be an alkaline activating composition.

Preferably, the metal oxides are transition metal oxides. More preferably, the metal oxides are selected from: iron oxides such as FeO, Fe ₃ O ₄ , Fe ₂ O ₃ , Fe ₂ O ₃ , alumina Al ₂ O ₃ , manganese (II) oxide ) MnO, titanium(IV) oxide TiO ₂ and mixtures thereof.

The metal oxides can preferably come from a composition of blast furnace slags, for example formed during the production of cast iron from iron ore.

The metal oxides are present at a content of at least 2% by weight of the building material, preferably at least 5% by weight of the building material, more preferably at least 10% by weight of the building material of construction.

When the activating agent is an alkaline activating composition. The alkaline composition may preferably comprise a compound having a pKa greater than or equal to 10, more preferably greater than or equal to 12, even more preferably substantially equal to 14.

The alkaline composition may for example comprise an organophosphorus compound such as sodium tripolyphosphate designated by the acronym NaTPP.

In particular, the activating agent may comprise a mixture of sodium hydroxide and sodium silicate.

Advantageously, the activating agent can be an alkaline activating composition further comprising metal oxides. As will be shown in the examples, building binders prepared from such an activating agent exhibit good mechanical properties. Thus, preferably, the activating agent may comprise metal oxides and at least one compound having a pKa greater than or equal to 10.

In addition, the selection step 170 may include a determination 172 of a quantity of additive to be integrated into the construction material composition. Indeed, the selection process according to the invention can lead to a construction material composition comprising certain additives in determined concentrations. These additives make it possible to modify the chemical and/or mechanical properties of the final construction material.

The additive is for example selected from: a plasticizer, a synthetic or natural rheological maintaining agent, an anti-shrinkage agent, a water-retaining agent, an air-entraining agent, a synthetic resin, a pigment and mixtures thereof. .

The plasticizer can for example be a polyacrylate, a polynaphthalenesulphonate, a polycarboxylate, or a polyphosphonate.

In addition, the selection step 170 may include a determination 173 of a quantity of filler to be integrated into the formulation so as to form a site concrete. These fillers make it possible to modify the mechanical properties of the final construction material.

The filler can for example be selected from recycled or non-recycled aggregates, powders, sand, gravel, gravel, crushed concrete and/or fibers.

The fibers are, for example, selected from: plant fibers such as flax cotton, hemp, cellulose, bamboo, miscanthus fibers, synthetic fibers such as metal, glass, carbon, polypropylene and their mixtures. The presence of fibers can allow the formation of a building material with improved mechanical and insulating properties.

Advantageously and as previously discussed, the step of determining 170 a quantity of deflocculating agent and a quantity of activating agent suitable for the excavated clay soil includes the implementation of a previously calibrated calculation algorithm.

This calculation algorithm may have been built from different learning models, in particular partitioning, supervised or unsupervised.

An unsupervised statistical learning model can for example be selected from among an unsupervised Gaussian mixture model, an ascending hierarchical clustering (Hierarchical clustering Agglomerative in Anglo-Saxon terminology), a descending hierarchical classification (Hierarchical clustering divisive in Anglo-Saxon terminology ).

A statistical model of supervised learning can for example be selected from among the kernel methods (e.g. Vast Margin Separators - Support Vector Machines SVM, Kernel Ridge Regression) described for example in Burges, 1998 (Data Mining and Knowledge Discovery. A Tutorial on Support Vector Machines for Pattern Recognition), ensemble methods (e.g. Bagging, Boosting, decision trees, Random Forest) described for example in Brieman, 2001 (Machine Learning. Random Forests), or neural networks described for example in Rosenblatt, 1958 (The perceptron: a probabilistic model for information storage and organization in the brain).

Preferably, the previously calibrated calculation algorithm has been obtained by implementing a statistical method of supervised learning.

Thus, according to another aspect, the invention relates to a method 200 for calibrating a calculation algorithm. This calculation algorithm is particularly dedicated to determining the composition of a building material. A calibration method according to the invention can in particular be implemented by a digital device comprising a learning module.

As illustrated in FIG. 2, such a calibration method according to the invention comprises a step 230 for receiving a measured value of at least one physicochemical property of an excavated clay soil.

Preferably, several measured values are received 230 and in particular values of at least two physicochemical properties of an excavated clay soil, more preferably at least three and even more preferably at least minus four. Indeed, depending on the number of physicochemical properties taken into account, the calibration process will be of better quality. you

The calibration method according to the invention also comprises a step 240 of receiving a value for the quantity of deflocculating agent and a value for the quantity of activating agent. These values correspond to quantities of agents which, once added to the excavated clay soil, make it possible to form a construction material.

The amount of deflocculating agent and activating agent can correspond to a volume, a mass or even a proportion. Preferably, the quantity corresponds to a proportion relative to a quantity of excavated clay soil to be added to the construction material composition. Alternatively, if the quantity corresponds to a volume or a mass then it is associated with a quantity of excavated clay soil to be added to the construction material composition. In addition, the reception 240 of value of quantities of deflocculating agent and quantity of activating agent can comprise the reception of the nature of the deflocculating agent and/or of the activating agent. For example, the nature of these agents may correspond to a family of chemical molecules or to a particular chemical molecule or even to a combination of molecules.

These values may have been obtained through tests which will be described in the examples section. There is integration in the calibration process of only the quantities of agents allowing the formation of a building material.

Indeed, the calibration process can include a step 250 of forming a building material according to the values received. Alternatively, and preferably, a plurality of combinations of agent amount values have been tested on a plurality of excavated clay soils to form a database that can be used as input to the calibration process.

The method then includes a step 270 for creating a correlation between the measured values received so as to calibrate a calculation algorithm. This correlation step, based on measured values, makes it possible to build a calculation algorithm from a statistical learning model. Thus, the calculation algorithm can take the form of a function f in an equation of the type

Y=f(E,A,D)

Preferably, as shown in FIG. 2, prior to the creation step 270, the calibration method according to the invention may also comprise a step 260 for receiving a measured value of at least one property mechanics of the formed building material. Indeed, in addition to the use of the agent quantity values and the physicochemical property value(s) of the excavated clay soil, the calibration method according to the invention can use one or more measured values of the construction material obtained. Thus, the calculation algorithm could take the form of a function f in an equation of the type:

M=f(E,A,D)

Preferably, several measured values are received 260 and in particular values of at least two physicochemical properties of the construction material, more preferably at least three and even more preferably at least four. .

In addition, as illustrated in Figure 2, the calibration method according to the invention may include a step 210 of prior treatment of a sample of clay soil which may come before a step 220 of measuring at least one physicochemical property of clay soil. Moreover, once the correlation has been established, it can be saved 280 on a recording medium such as RAM or non-volatile memory.

Advantageously, a calibration method according to the invention may comprise a step 290 of updating the calculation algorithm by repeating the previous steps described previously and at a minimum: Reception 230 of a measured value of at least one physicochemical property of an excavated clay soil, Reception 240 of a quantity of deflocculating agent and a quantity of activating agent which once added to the excavated clay soil so as to form a construction material and Creation 270 a correlation between the measured values received so as to calibrate a calculation algorithm.

According to another aspect, the invention relates to a process 300 for preparing a construction material from excavated clay soil.

Such a process according to the invention, illustrated in FIG. 3, has the advantage of being a so-called low carbon process, that is to say in which the greenhouse gas emissions, such as in particular the carbon dioxide emissions of carbon, are reduced with regard to the greenhouse gas emissions of the known construction binder preparation processes. Such reductions in greenhouse gas emissions are linked in particular to the absence of a calcination step which is particularly energy-intensive.

In addition, the preparation of a construction binder according to the invention can allow the preparation of a site concrete made at least in part from raw material coming from the construction site. Such characteristics further contribute to reducing the environmental footprint of the concrete produced. Once there has been selection of a quantity of deflocculating agent and a quantity of activating agent adapted to the excavated clay soil, it is possible according to conventional methods to proceed with the preparation of a material construction from excavated clay soil.

The preparation method according to the invention may include a step 310 of measuring at least one physicochemical property of the excavated clay soil.

Such a step can be carried out well before the mixing step 340. This is for example the case if preliminary studies are carried out and it is not necessary to use the excavated earth quickly. Alternatively, the step 310 of measuring at least one physicochemical property of the excavated clay soil can be carried out just before the steps 100 of selecting the composition of a construction material, corresponding to a step for implementing the method 100 according to the invention, and mixing 340. This is for example the case in an automated method for preparing a building material from an excavated clay soil where the excavated clay soil is analyzed online with an apparatus transportable measuring device then continuously mixed with selected quantities of agents so as to form a building material in a very short time.

Preferably, several values are measured and in particular values of at least two physicochemical properties of the excavated clay soil, more preferably at least three and even more preferably at least four.

Furthermore, as illustrated in FIG. 3 and in FIG. 4, a method of preparation according to the invention may comprise a selection 100 of the composition of a building material comprising a clay soil excavated according to the invention.

In addition, it may include a step of mixing 340 excavated clay soil, deflocculating agent and activating agent according to the selected composition.

During the mixing step, the water can be added so that the ratio between the mass of water and the mass of construction material is less than 1 and for example between 0.4 and 0.8 . Additionally, water can advantageously be added after the excavated clay soil and deflocculating agent have been dry-mixed.

Thus, preferably, the method according to the invention may comprise a mixing step so as to obtain a suspension of dispersed or deflocculated excavated clay soil. When mixing, preferably, the deflocculating agent is added before the activating agent so that the activating agent is mixed with dispersed or deflocculated excavated clay soil.

This mixing step 340 of the clay suspension can advantageously but not limitatively be carried out in a device selected from: a mixer and a mixer truck or more generally within any device suitable for mixing clay soil.

Preferably, the preparation method may comprise a step of sifting 330 of the excavated clay soil. This screening step occurs before the mixing step 340 and before or after the measuring step 310. In particular, it is carried out in such a way as to eliminate the aggregates whose diameter is greater than 20 mm (per millimeter).

More broadly, the preparation process may comprise a step of preparing the excavated clay soil, said preparation possibly comprising, for example: drying, grinding, sieving, storage.

Preferably, the pre-processing or screening step includes at least one fractionation such as sieving, more preferably one fractionation such as 50 µm sieving. Advantageously but not limitatively, the elements or particles thus screened, such as for example fractions of sand and/or aggregates, can be reused in the formulation of the construction material and in particular of the site concrete. The most interesting fraction for the preparation of the construction material being the fraction not retained by the sieve. Thus, a method 300 according to the invention for preparing a construction material from excavated clay soil will advantageously include a step 335 of splitting the excavated clay soil, possibly screened, said splitting preferably taking place at 50 μm .

Alternatively, the excavated clay soil may not be pre-treated and all of the clay soil is used to obtain construction material. In this case, the process makes it possible to obtain site concrete.

This advantageously makes it possible to recover all of the excavated clay soil, in particular in the case where the physico-chemical properties associated with said excavated clay soil are sufficient to obtain a construction material having the desired mechanical properties. Thus, the whole of the earth can be valued from the start without necessarily having to isolate the clay to treat it and formulate the material.

As illustrated in Figure 5, a method 300 according to the invention for preparing a building material from excavated clay soil will advantageously include:

a step 320 of excavation of clay soil;

- a step 330 of screening the excavated clay soil when the excavated clay soil includes stones retained by a 2 cm sift;

a mixing step 340 of excavated clay soil, preferably the fraction less than 50 μm, of deflocculating agent and of activating agent.

Furthermore, advantageously, the method of preparation may also comprise a stage of treatment of the pollutants. Such a pollutant treatment step can make it possible to reduce the concentration of pollution in the excavated clay soil such as traces of metallic elements, hydrocarbons (e.g. Polycyclic Aromatic Hydrocarbon and C10 to C40), PCB (PolyChloroBiphenyls), BTEX (benzene , toluene, ethylbenzene, xylenes), 15 TOC (total organic carbon).

In addition, conventionally, before, concomitantly or after the addition of the activation composition, a method according to the invention may comprise the addition of additives or fillers making it possible to modify the mechanical properties of the final construction material.

Advantageously, the preparation process may include a measurement 350 of one or more physico-chemical or mechanical property values of the construction material, during the mixing step (i.e. the construction material is being formed), a comparison 360 measured values at predetermined values of physicochemical or mechanical property of the building material being formed.

Thus, it is possible to carry out quality control of the building material being formed.

In addition, when the measured values differ from the predetermined physicochemical or mechanical property values of the building material being formed, the preparation method may include a step 370 of adding at least one complementary ingredient.

Here, the complementary ingredient can for example be selected from: deflocculating agent, activating agent and excavated clay soil so as to modify the predetermined composition. The complementary ingredient can also be selected from: additives or fillers as described above.

This ensures that the building material being formed will exhibit mechanical properties as close as possible to the expected mechanical properties. Indeed, a deviation can be identified at the time of mixing and corrected before the material is used.

In addition, as illustrated in Figure 4, the method is completed by a recovery step 380 of the construction material formed.

According to another aspect, the invention relates to a system 400 for preparing a building material comprising excavated clay soil. Alternatively, as mentioned, the invention relates to a system 400 for preparing site concrete comprising excavated clay soil.

Such a method according to the invention, illustrated in FIG. 5, can comprise containers 410, 420, 430 intended for the various constituents of the construction material. For example, it may comprise at least one container 410 intended for excavated clay soil, at least one container 420 intended for a deflocculating agent and at least one container 430 intended for an activating agent. In addition, it may include at least one container 440 intended for fillers and/or additives. In addition; the system may include a cleaning container for containing a cleaning solution.

In particular in the case of excavated clay soil, the container 410 may not be an object but only a place at which the excavated clay soil is stored. A container can also be selected from a tank, a container, a bin, a silo.

In addition, the system according to the invention comprises a mixing device 450. Such a device is in particular capable of homogenizing and/or mixing the precursor ingredients of the construction binder.

This mixing device 450 is in particular coupled to means of transport (represented respectively by an arrow between the containers 410, 420, 430, 440 and the mixing device 450) automated positioned between the containers 410, 420, 430 and the device 450 mix. These means of transport can for example be flexible pipes or not, belts, conveyors or endless screws. Furthermore, in combination with the means of transport, the system may include pumps, valves, solenoid valves and flow limiters. In particular, the flow limiters can be arranged in functional switching with each of the transport means to independently regulate the quantity of each of the ingredients distributed to the mixing device 450 .

In addition, the system according to the invention may include a means 460 for measuring at least the physicochemical property of the excavated clay soil. Such a measuring means 460 can for example be a pH meter, an X-ray diffractometer, a conductivity meter, an electron microscope, a mercury porosimeter, a spectrofluorometer, an ICP-MS, an HPLC-MS, a GC-MS, measurement of the specific surface by the BET method, a particle size analyzer, or even a rheometer.

In addition, the system according to the invention may comprise a calculation means 470 capable of, preferably configured to, implement a computer program configured to carry out:

A step for obtaining a measured value of at least one physicochemical property of the excavated clay soil; and

A step for determining a quantity of deflocculating agent and a quantity of activating agent suitable for the excavated clay soil on the basis of a comparison of the measured value(s) with reference values.

In addition, the system according to the invention comprises a control module 480 configured to generate output signals intended for automated means of transport. Such output signals will allow the system to transport the determined quantities of deflocculating agent and activating agent to the mixing device 450. In addition, they can allow a predetermined quantity of excavated clay soil to be transported to the mixing device 450.

Preferably, the system for preparing a construction material according to the invention may also comprise: a screener, preferably compact, an earth grinder, a planetary mixer.

More preferably, it may include a dirt grinder. Indeed, the earth grinder makes it possible in particular to eliminate the presence of agglomerates which could influence the quality of the construction binder or the site concrete. In addition, the clayey earth reduced to powder will make it possible to have a homogeneous appearance in the site concrete.

Even more preferably, the system for preparing a construction material according to the invention comprises a sifter making it possible to isolate pebbles with a diameter greater than 10 cm, preferably greater than 2 cm. The system for preparing a building material can also comprise a sorting means, for example of the sieve type, making it possible to isolate particles with a diameter of less than 50 μm, preferably particles with a diameter of less than 20 μm. Advantageously but not limitatively, the elements or particles thus separated, such as for example fractions of sand and/or aggregates, can be reused in the formulation of the construction material and in particular of the site concrete.

Alternatively, the excavated clay soil may not be pre-treated and all of the clay soil is used to obtain construction material. In this case, the process makes it possible to obtain site concrete.

In addition, it may include a depollution device making it possible to treat the excavated earth before it is used.

Thus, according to another aspect, the invention relates to a building material formed from excavated clay soil. In particular, this building material is capable of being prepared according to a preparation process according to the invention described above. For example, this construction material is directly prepared according to a preparation process according to the invention described above.

The construction material according to the present invention is characterized in that it comprises a deflocculating agent and an excavated clay soil. Note that the preparation of the construction material includes the addition of an activating agent. However, since this activating agent may react with the excavated clay soil, it is not systematically found in the construction material. Nevertheless, occasionally, the construction material according to the present invention may comprise a deflocculating agent, an activating agent and an excavated clay soil.

Given the possible addition of fillers, the invention also relates to a site concrete characterized in that it comprises a deflocculating agent and an excavated clay soil.

Alternatively, in the absence of the addition of fillers, the invention also relates to a construction binder characterized in that it comprises a deflocculating agent and an excavated clay soil.

Advantageously, the construction material according to the invention comprises a mixture of different types of clay. In particular, it may include a combination of clay selected from:

Illite and kaolinite,

Illite and kaolinite and bentonite,

Illite and Bentonite,

Kaolinite and bentonite,

Illite and Montmorillonite, or

A combination of Kaolinite, Illite, Smectite, Bentonite, Chlorite, Montmorillonite, Muscovite, Hallocyte, Sepiolite, Attapulgite, and Vermiculite.

J.L.

In addition, advantageously, the building material formed from an excavated clay soil, characterized in that it comprises at most 80% by weight of particles greater than 2 μm, preferably at most 60% by weight of particles greater than 2 p.m. The content of particles greater than 2 μm can for example be measured according to standard NF X31-107. Thus, the excavated earth has preferably undergone a pretreatment step resulting in a particle size centered on a fraction having a diameter of size less than or equal to 50 μm, preferably less than or equal to 20 μm.

Preferably, a building material according to the invention comprises at least 50% by weight of excavated clay soil, at least 60% by weight of excavated clay soil, at least 70% by weight of excavated clay soil, at least 80% by weight of excavated clay soil, more preferably at least 90% by weight of excavated clay soil. This is advantageously the case when the construction material is a construction binder.

Indeed, the selection of quantity of deflocculating agent and of activating agent has the advantage of being able to form a building binder comprising a high quantity of excavated clay soil without this altering the mechanical properties of the building materials. resulting therefrom. When the construction material is site concrete, it may include at least 10% by weight of excavated clay soil, at least 15% by weight of excavated clay soil, at least 20% by weight of excavated clay soil, at least 30% by weight of excavated clay soil, at least 40% by weight of excavated clay soil, at least 50% by weight of excavated clay soil.

The deflocculating agent can represent at least 0.1% by weight of the construction material, at least 0.20% by weight of the construction material, at least 0.25% by weight of the construction material, preferably at least 0.5% by weight of the building material, more preferably at least 1% by weight of the building material, even more preferably at least 1.5% by weight of the building material, and for example at least 2 % by weight of the construction material. This is advantageously the case when the construction material is site concrete.

The deflocculating agent may represent at least 0.30% by weight of the construction material, at least 0.5% by weight of the construction material, preferably at least 1% by weight of the construction material, more preferably at least 1.5% by weight of the building material, even more preferably at least 2% by weight of the building material, and for example at least 2.5% by weight of the building material. case when the building material is a building binder.

Furthermore, the deflocculating agent can represent at most 20% by weight of the construction material, more preferably at most 15% by weight of the construction material, and more preferably at most 10% by weight of the construction material.

In particular, the deflocculating agent can represent between 0.25 and 10% by weight of the construction material, preferably between 0.5 and 10% by weight of the construction material, more preferably between 1 and 10% by weight of the building material, even more preferably between 2 and 8% by weight of the building binder and for example between 2 and 5% by weight of the building binder. Thus, the deflocculating agent may preferably represent between 0.1 and 5% by weight of the construction material.

In particular, the deflocculating agent represents at least 0.5% by weight of the excavated clay soil, preferably at least 1% by weight of the excavated clay soil, more preferably at least 2% by weight of the clay soil excavated, even more preferably at least 3% by weight by weight of the excavated clay soil, and for example at least 4% by weight by weight of the excavated clay soil. Indeed, with such concentrations of deflocculating agent, the binder formulation according to the invention can then be used in combination with an activating composition to form a material with advantageous mechanical properties. ·

In addition, the deflocculating agent represents at most 20% by weight of the excavated clay soil, preferably at most 10% by weight of the excavated clay soil. Indeed, too high a concentration is not necessary to form a material with advantageous mechanical properties.

In particular, the deflocculating agent represents between 0.5 and 20% by weight of the excavated clay soil, preferably between 1 and 10% by weight of the excavated clay soil, more preferably between 3 and 10% by weight of the excavated clay soil and even more preferably between 4 and 10% by weight of the excavated clay soil.

The activating agent is for example present at a content of at least 5% by weight of the building material, preferably at least 7% by weight of the building material, more preferably at least 8% by weight building material. This is advantageously the case when the construction material is site concrete.

The activating agent may be present at a level of at least 10% by weight of the construction material, preferably at least 15% by weight of the construction material, more preferably at least 20% by weight of the building material, even more preferably at least 25% by weight of the building binder, and for example at least 30% by weight of the building binder.

Furthermore, the activating agent may represent at most 50% by weight of the construction material, preferably at most 45% by weight of the construction material, and more preferably at most 40% by weight of the construction material. construction. This is advantageously the case when the construction material is a construction binder.

The activating agent may also represent at most 15% by weight of the construction material, preferably at most 12% by weight of the construction material, and more preferably at most 10% by weight of the construction material. This is advantageously the case when the construction material is site concrete.

In particular, the activating agent can represent between 3 and 12% by weight of the construction material, preferably between 4 and 10% by weight of the construction material, more preferably between 5 and 10% by weight of the construction material. This is advantageously the case when the building material is site concrete.

In particular, the activating agent can represent between 10 and 80% by weight of the building material, preferably between 15 and 80% by weight of the building material, more preferably between 20 and 80% by weight of the building material. even more preferably between 30 and 80% by weight of the building material and for example between 40 and 60% by weight of the building material. This is advantageously the case when the construction material is a construction binder.

In a particular embodiment, a construction material, preferably a construction binder in accordance with the invention, comprises:

30% to 80% by weight of excavated clay soil, 1% to 10% by weight of deflocculating agent, and 10% to 50% by weight of an activating agent.

Preferably, a construction material, preferably a construction binder, in accordance with the invention comprises:

50% to 75% by weight of excavated clay soil, 1% to 10% by weight of deflocculating agent, and 15% to 50% by weight of an activating agent.

More preferably, a construction material, preferably a construction binder in accordance with the invention, comprises:

50% to 70% by weight of excavated clay soil, 2% to 5% by weight of deflocculating agent, and 15% to 45% by weight of an activating agent.

More preferably, a construction material, preferably a construction binder, in accordance with the invention comprises:

50% to 60% by weight excavated clay soil, 2% to 5% by weight deflocculating agent, and 25% to 45% by weight metal oxides.

Even more preferably, a construction material, preferably a construction binder, in accordance with the invention comprises:

- from 30% to 80% by weight of excavated clay soil, from 1% to 10% by weight of deflocculating agent,

- from 10% to 40% by weight of metal oxides, and from 2% to 15% by weight of a strong base.

Even more preferably, a construction material, preferably a construction binder, in accordance with the invention comprises:

from 30% to 80% by weight of excavated clay soil,

- from 0.1% to 10% by weight of deflocculating agent, and

- from 15% to 50% by weight of blast furnace slag.

Even more preferably, a construction material, preferably a construction binder in accordance with the invention, comprises:

- from 30% to 80% by weight of excavated clay soil, from 0.1% to 10% by weight of deflocculating agent,

- from 10% to 45% by weight of blast furnace slag, and

- from 5% to 20% by weight of an alkaline composition such as triphosphate.

Preferably, a construction material in accordance with the invention is a site concrete comprising:

- between 5 and 45% by weight, preferably between 5 and 30% by weight, more preferably between 10 and 20% by weight of a construction binder according to the invention; between 25 and 45% by weight, preferably between 30 and 40% by weight of sand, for example from site soil, preferably from excavated clay soil;

- between 35 and 55% by weight, preferably between 40 and 50% by weight of aggregates, for example from site soil, preferably from excavated clay soil; and preferably between 2 and 10% by weight of water.

More preferably, a construction material in accordance with the invention is a site concrete comprising:

between 5 and 20% by weight of raw clay from the excavated clay soil, preferably between 5 and 15% by weight of raw clay from the excavated clay soil;

between 0.1 and 3% by weight of deflocculating agent;

between 3 and 15% by weight, preferably between 5 and 12% by weight of an activating agent; for example between 5% and 10% by weight of a blast furnace slag;

- between 25 and 45% by weight, preferably between 30 and 40% by weight of sand, for example from site soil, preferably from excavated clay soil;

- between 35 and 55% by weight, preferably between 40 and 50% by weight of aggregates, for example from site soil, preferably from excavated clay soil; and preferably between 2 and 10% by weight of water.

The sands and aggregates may come from quarries. In addition, the binder may include quarry clay in addition to the clay from the excavated clay soil.

In addition, the site concrete may include admixtures such as plasticizers, superplasticizers, rheological maintenance agents or air entrainers.

In addition, the water to dry matter ratio of the construction binder is advantageously controlled and is preferably less than 1, more preferably substantially equal to 0.6.

Moreover, according to another aspect, the invention relates to a building material formed from a building binder according to the invention.

Furthermore, the invention relates to a building material obtained from a preparation process according to the invention. The invention relates to a building material obtained from a preparation process according to the invention.

The invention allows in particular the manufacture of:

insulating construction material: from a construction binder according to the invention with the addition of light aggregates of the "vegetable or porous" type;

lightweight concrete: from a construction binder according to the invention to which a foaming agent of the aluminum powder type has been added. This will help trap air in the material and improve its insulating properties;

Prefabrication elements: manufacture of concrete blocks or slabs in the factory from the construction binder according to the invention; and Isolation Modules.

As illustrated by the examples below, the present invention provides a solution based on a mixture of raw clay matrix, deflocculating agent and activating composition to provide a construction material with mechanical properties similar to the standard while with a reduced carbon footprint.

EXAMPLES:

Methodology for measuring the physicochemical properties of clay soil:

The clay soil is sieved beforehand so as to remove all the elements or particles having a diameter greater than 20 μm. Such a pretreated clay soil is particularly suitable for the formation of a construction binder according to the invention.

The pH is measured from 20 g of pretreated clay soil mixed with 100 mL of distilled water. After stirring for 20 minutes at 150 rpm (for “revolutions per minute” according to Anglo-Saxon terminology), the suspension is filtered then the pH of the filtered solution is the filtered solution.

The clay content is measured conventionally by the particle size method described in standard NF X31-107.

The nature of clays is measured conventionally by X-ray diffractometry.

Generation of reference values

As presented previously, the values of comprise correlations between measured values of at least one physicochemical property of a clay soil and values of quantities of deflocculating agent and of activating agent.

These reference values are generated from a plurality of clay soil samples coupled with varying amounts of deflocculating agent and activating agent in a construction binder preparation process described below.

The generation of reference values can for example implement a design of experiment such as a simplex design, a screening design, a factorial design, a response surface design, a mixture design, a Taguchi design .

Table 1 below presents the physicochemical properties of different samples of excavated soil while Table 2 shows an example of an experimental plan to generate reference values.

[Table 1]

Earth Physicochemical property clayey pH Clay content Nature of clays Sample A 7 to 8 90% to 100% Smectite and Montmorillionite B-sample 4 to 6 90% to 100% Kaolinite

[Table 2]

Reference clay soil Deflocculating agent Activation agent Nature Concentration Nature Concentration MUP42 Sample HAS n / A 0% by weight of binder LHF + Alkaline solution 23% by weight of binder MUP5B Sample HAS n / A 0% by weight of binder LHF+ Triphosphate 43% by weight of binder MUP12 Sample HAS n / A 0% by weight of binder blast furnace slag 25% by weight of binder MUP11 Sample HAS Humates of 2.73% by weight of binder top slag 25% by weight of binder

sodium stoves MUP2 Sample HAS Sodium humates 2.96% by weight of binder Metal oxides 12% by weight of binder MUP5 Sample HAS Sodium humates 3.13% by weight of binder LHF + Triphosphate 42% by weight of binder MUP41 Sample HAS Sodium humates 3.39% by weight of binder LHF + Alkaline solution 22% by weight of binder MUP3 Sample HAS Sodium humates 3.97% by weight of binder Metal oxides 9% by weight of binder

Preparation of a construction binder:

The building binders, in particular during the generation of the reference values, are prepared according to an identical protocol, namely that a premix is carried out between a clayey earth and a deflocculating agent in the predetermined quantities following for example an experimental plan , then water is added and the suspension is mixed at low speed, that is to say substantially at six hundred revolutions per minute for thirty seconds. Next, an activating agent is added to the premix and then the premix is mixed at high speed, i.e. at approximately one thousand five hundred revolutions per minute for three minutes.

The water to dry matter mass ratio of the composition (also called construction binder) is adjusted to a value of less than 1, more preferably substantially equal to 0.6.

The construction binder thus formed is then poured into a mold and left to mature at room temperature, i.e. approximately 20 degrees Celsius for twenty-eight days.

The mechanical properties of the construction binder are then evaluated.

Methodology for measuring the mechanical properties of construction binders:

After curing is complete, the building binder is removed from the mold and the mechanical strength is measured. Mechanical strength of a construction binder means its resistance to compression, such compression being measured according to standard NF EN 196-1.

The results of the measurements carried out on the experiments described in Table 2 are presented below in Table 3.

[Table 3]

Reference Mechanical resistance (in MPa) MUP42 (comparative example) 27 MUP5B (comparative example) 25 MUP12 (comparative example) 21 MUP11 41 MUP2 37 MUP5 45 MUP41 43 MUP3 37

These results show that depending on the amounts of activating agent and deflocculating agent used, the performance of the binder formed will be different and in particular its mechanical strength.

In addition, they show that the presence of a deflocculating agent makes it possible to obtain mechanical strengths greater than 30 MPa.

Selection of the composition of a construction binder:

Following the preparation of reference values and, if necessary, a calculation algorithm, it is possible to implement a process for selecting the quantities of deflocculating and activating agents suitable for a given excavated clay soil.

First, a sample of the excavated clay soil is sieved to remove all elements or particles with a diameter greater than 20 μm.

The physicochemical properties of the pretreated excavated clay soil sample are then analyzed as described above.

The values obtained are then transmitted to a computer device configured to implement the method according to the invention.

The latter then generates values for the quantity of deflocculating and activating agent which, once coupled with a predetermined quantity of excavated soil, will make it possible to form a building binder.

Formation of a building binder according to the invention

The excavated clay soil is then sieved so as to remove all elements or particles having a diameter greater than 2 cm and then a predetermined quantity of pretreated excavated clay soil is mixed simultaneously or sequentially with the values for the quantity of deflocculating agent and selected activations.

The construction binders or site concretes formed according to the invention have compressive strengths equivalent to the compressive strengths obtained with a concrete formed with Portland cement. Thus, the present invention makes it possible to select the appropriate composition which will make it possible to form a low-carbon construction binder, from excavated clay soil, having sufficient mechanical properties to make it a construction material meeting the majority of the needs of the sector. .

Claims (21)

1. Method (100) for selecting the composition of a building material comprising an excavated clay soil, said construction material composition having to comprise quantities of deflocculating agent and of activating agent adapted to the excavated clay soil , said method being implemented by a computing device comprising a calculation module, said method comprising: - A reception step (130), by the calculation module, of a measured value of at least one physicochemical property of an excavated clay soil; and - A selection step (170), by the calculation module, of a quantity of deflocculating agent and of a quantity of activating agent adapted to the excavated clay soil on the basis of a comparison of the measured values with reference values, said reference values comprising correlations between measured values of at least one physicochemical property of a clay soil and quantities of deflocculating agent and of activating agent adapted to said soil clay to form a building material. 2. Method according to claim 1, characterized in that the at least one physicochemical property is selected from: the content of clays in the excavated clay soil, the nature of the clays, the particle size, the content of impurities, the content of fractions non-clay mineralogical, pollution content, elemental analysis, metal oxide content, salinity, pH, and total clay exchange capacity of the excavated clay soil. 3. Method according to one of claims 1 or 2, characterized in that the at least one physicochemical property is measured on a pretreated excavated clay soil, said pretreatment being selected from: grinding, sorting, sieving and/or drying of the excavated clay soil. 4. Method according to any one of claims 1 to 3, characterized in that it comprises beforehand the reception (140) of a desired mechanical property value of the construction material and in that the step of selecting ( 170) amounts of deflocculating agent and activating agent further includes an exclusion (171) of amounts of deflocculating agent and activating agent that will not allow the building material to exhibit the property value desired mechanics. 5. Method according to any one of claims 1 to 4, characterized in that the step of selecting (170), by the calculation module, a quantity of deflocculating agent and a quantity of deflocculating agent. The activation adapted to the excavated clay soil includes the implementation of a previously calibrated calculation algorithm. 6. Method according to claim 5, characterized in that the previously calibrated calculation algorithm has been obtained by implementing a statistical method of supervised learning. 7. Method (200) for calibrating a calculation algorithm for determining the composition of a construction material implemented by a digital device comprising a learning module, said method being characterized in that it comprises: - A first step (230) of reception, by the learning module, of a measured value of at least one physicochemical property of an excavated clay soil; - A second step (240) of reception, by the learning module, of a quantity value of deflocculating agent and of a quantity value of activating agent which, once added to the excavated clay soil, allow to form a building material; - A third step (260) of reception, by the learning module, of a measured value of at least one mechanical property of the construction material formed from the excavated clay soil, the value of at least one property of which physicochemical was received during the first step (230) of reception, and from the quantities of deflocculating agent and of activating agent received during the second step (240) of reception; and - A step (270) of creation of a correlation, by the learning module, between the measured values received so as to calibrate a calculation algorithm. 8. Process (300) for preparing a building material from excavated clay soil, the process comprising: - A measurement step (310) of at least the physicochemical property of the excavated clay soil; - A selection step according to a method (100) for selecting the composition of a construction material comprising an excavated clay soil according to one of claims 1 to 6; and - A step of mixing (340) excavated clay soil, deflocculating agent and activating agent according to the selected composition. 9. Process of preparation according to claim 8 further comprising: - a measurement step (350) of physico-chemical or mechanical properties of the building material being formed, during the mixing step, - a comparison step (360) of the measured values with predetermined values of physicochemical or mechanical property of the building material being formed, and - when the measured values differ (360-n) from the predetermined physicochemical or mechanical property values of the building material being formed, a step of adding (370) at least one complementary ingredient. 10. Building material formed from an excavated clay soil characterized in that it comprises an excavated clay soil, an activating agent and a deflocculating agent, said deflocculating agent representing at least 0.1% by weight of the material building material, preferably at least 0.25% by weight of the building material. 11. Building material according to claim 10, characterized in that it comprises a mixture of different types of clays. 12. Building material according to one of claims 10 or 11, characterized in that it comprises metal oxides at a content of at least 2% by weight of the building material, said building material then preferably corresponding to a building binder. 13. Building material according to any one of claims 10 to 12, characterized in that i! includes blast furnace slag. 14. Building material according to claim 13, characterized in that it comprises: from 30% to 80% by weight of excavated clay soil, from 0.1% to 10% by weight of deflocculating agent, and from 5 to 10% by weight of blast furnace slag; preferably said construction material then corresponding to a construction binder. 15. Building material according to claim 13, characterized in that it comprises: between 5 and 20% by weight of raw clay from the excavated clay soil; between 0.1 and 3% by weight of deflocculating agent; between 3 and 15% by weight of an activating agent; between 25 and 45% by weight of sand; and between 35 and 55% by weight of aggregates; preferably said building material then corresponding to a site concrete. 16. Building material according to any one of claims 10 to 15, characterized in that it comprises at least 2% by weight of silt particles. 17. Building material according to any one of claims 10 to 16, characterized in that the excavated clay soil has been pretreated, said pretreatment being selected from: grinding, sorting, sieving and/or drying of the excavated clay soil. 18. Process (300) for preparing a building material according to one of claims 10 to 17 from an excavated clay soil comprising: a step 320 of excavation of clay soil; a step 330 of sifting the excavated clay soil when the excavated clay soil includes stones retained by a 2 cm sift; a mixing step 340 of excavated clay soil, deflocculating agent and activating agent. 19. System (400) for preparing a construction material comprising excavated clay soil, said system comprising: - At least one container (410) comprising excavated clay soil, - At least one container (420) comprising a deflocculating agent, - At least one container (430) comprising an activating agent, - A mixing device (450), with automated transport means between the containers (410, 420, 430) and the mixing device (450), - A control module (480) configured to generate output signals intended for the automated means of transport so as to transport determined quantities of deflocculating agent and activating agent to the mixing device (450). 20. System (400) for preparing a construction material according to claim 19, characterized in that it comprises a communication means configured to receive data on a quantity of deflocculating agent and a quantity of deflocculating agent. determined activation, adapted to the excavated clay soil; the control module (480) being configured to generate output signals intended for the automated means of transport so as to transport the quantities of deflocculating agent and of activating agent determined towards the mixing device (450). 21. System (400) for preparing a building material according to claim 19, characterized in that it comprises: - A means of measuring (460) at least one physicochemical property of the excavated clay soil, - A calculation means (470) capable of implementing a computer program configured to carry out: - A step for obtaining a measured value of at least one physicochemical property of the excavated clay soil; and - A step for determining a quantity of deflocculating agent and a quantity of activating agent suitable for the excavated clay soil on the basis of a comparison of the measured value(s) with reference values.