PL174503B1 - Heat resisting cast steel

Info

Publication number: PL174503B1
Application number: PL95308382A
Authority: PL
Inventors: Andrzej Paluch; Andrzej Madej; Zygmunt Olbryt; Jerzy Gorażdża; Tadeusz Borek; Zofia Fleger; Zygmunt Gola; Mieczysław Jurkiewicz
Original assignee: Huta Malapanew Sa
Priority date: 1995-04-25
Filing date: 1995-04-25
Publication date: 1998-08-31

Abstract

The heat-resisting cast steel is designed to be used under a loading at the temperature up to 950 degrees C, in the oxidizing atmosphere. It contains carbon, manganese, silicon, phosphorus, sulphur, chromium and nickel. Characterized in that: It contains the following components by mass: 0.30 - 0.50 percent of carbon, the maximum amount of up to 1.50 percent of manganese, 1.00 - 2.50 percent of silicon, the maximum amount of up to 0.035 percent of phosphorus, the maximum amount of up to 0.035 percent of sulphur, 21.0 - 23.0 percent of chromium, 9.0 - 11.0 percent of nickel.

Description

Przedmiotem wynalazku jest staliwo żaroodporne przeznaczone na elementy urządzeń grzewczych, wysokoobciążone, pracujące w temperaturze do 950°C, w atmosferze utleniającej i posiadające strukturę austenityczną z wydzieleniami węglików.The subject of the invention is heat-resistant cast steel intended for elements of heating devices, highly loaded, working at temperatures up to 950 ° C, in an oxidizing atmosphere and having an austenitic structure with carbide precipitates.

Dotychczas stosowane staliwa żaroodporne, austenityczne, chromowoniklowe, znane z normy PN-90/H-83159, w zależności od zawartości chromu i niklu są przeznaczone do pracy pod obciążeniem w temperaturze od 800 do 1100°C, posiadają zawartość węgla max. 0,25%.The heat-resistant, austenitic, chromium-nickel cast steels used so far, known from the PN-90 / H-83159 standard, depending on the content of chromium and nickel, are designed to work under load at temperatures from 800 to 1100 ° C, have a carbon content of max. 0.25%.

Znane jest z polskiego opisu patentowego nr 148506 staliwo żaroodporne i żarowytrzymałe zawierające węgiel, mangan, fosfor, siarkę, chrom i nikiel, lecz o innym składzie wagowym zwłaszcza węgla, niklu i chromu.It is known from the Polish patent description No. 148506 heat-resistant and heat-resistant cast steel containing carbon, manganese, phosphorus, sulfur, chromium and nickel, but with a different weight composition, especially of carbon, nickel and chromium.

Znane są również staliwa stopowe z polskich opisów patentowych nr 151898 i 145093 o podobnym składzie, lecz zawierają inne ilości poszczególnych pierwiastków w szczególności zaś chromu i niklu.Also known are cast steel from Polish patents No. 151 898 and 145093 with a similar composition, but containing different amounts of individual elements, in particular chromium and nickel.

Celem wynalazkujest uzyskanie staliwa, które przy zachowaniu wysokiej żaroodpomości, będzie zdolne przenosić wyższe obciążenia i tym samym pozwoli na wzrost trwałości wykonanych z niego odlewów.The aim of the invention is to obtain cast steel which, while maintaining high heat resistance, will be able to withstand higher loads and thus allow for an increase in the durability of castings made of it.

Staliwo zawierające węgiel, mangan, krzem, fosfor, siarkę, chrom i nikiel, według wynalazku zawiera wagowo 0,30 - 0,50% węgla, maksymalnie do 1,50% manganu, 1,00 - 2,50% krzemu, maksymalnie do 0,035% fosforu, maksymalnie do 0,035% siarki, 21,00 - 23,00% chromu, 9,00 - 11,00% niklu.The cast steel containing carbon, manganese, silicon, phosphorus, sulfur, chromium and nickel, according to the invention, contains 0.30 - 0.50% by weight of carbon, up to 1.50% of manganese, 1.00 - 2.50% of silicon, up to a maximum of 0.035% phosphorus, up to 0.035% sulfur, 21.00 - 23.00% chromium, 9.00 - 11.00% nickel.

Otrzymane staliwo posiada strukturę austenityczną z wydzieleniami węglików i odznacza się dobrymi własnościami żaroodpornymi w warunkach wysokich obciążeń w atmosferze utleniającej.The obtained cast steel has an austenitic structure with carbide precipitates and is characterized by good heat-resistant properties under high loads in an oxidizing atmosphere.

Przykład I. Staliwo według wynalazku wytopione w piecu elektrycznym indukcyjnym o wyłożeniu kwaśnym zawiera wagowo: węgiel - 0,42%, mangan - 0,71%, krzem - 1,38%, fosfor - 0,029%, siarkę - 0,024%, chrom - 21,83%, nikiel - 9,40%.Example I. The cast steel according to the invention smelted in an induction electric furnace with acid lining contains by weight: carbon - 0.42%, manganese - 0.71%, silicon - 1.38%, phosphorus - 0.029%, sulfur - 0.024%, chromium - 21.83%, nickel - 9.40%.

Odlewy poddane obróbce cieplnej, polegającej na wyżarzaniu normalizującym w temp. 1050 do 11Ó0°C i chłodzeniu w wodzie lub na powietrzu, posiadają strukturę austenityczną z wydzieleniami węglików i odznaczają się twardością HB - 179.Castings subjected to heat treatment, consisting in normalizing annealing at the temperature of 1050 to 110 ° C and cooling in water or in air, have an austenitic structure with carbide precipitates and are characterized by a hardness of HB - 179.

Przykładem zastosowania tego staliwa jest odlew płyty chłodnika w cementowni.An example of the use of this cast steel is the casting of a cooler plate in a cement plant.

Przykład II. Staliwo według wynalazku wytopione w piecu elektrycznym łukowym o wyłożeniu zasadowym zawiera wagowo: węgiel - 0,38%, mangan - 1,10%, krzem - 1,31%, fosfor - 0,026, siarkę - 0,022%, chrom - 22,5%, nikiel - 9,78%.Example II. The cast steel according to the invention smelted in an electric arc furnace with basic lining contains by weight: carbon - 0.38%, manganese - 1.10%, silicon - 1.31%, phosphorus - 0.026, sulfur - 0.022%, chromium - 22.5% , nickel - 9.78%.

Odlewy poddane obróbce cieplnej, polegającej na wyżarzaniu normalizującym w temp. 1070°C i chłodzeniu na powietrzu, posiadają strukturę austenityczną z wydzieleniami węglików i odznaczają się twardością HB - 212.The castings subjected to heat treatment, consisting in normalizing annealing at 1070 ° C and cooling in air, have an austenitic structure with carbide precipitations and are characterized by a hardness of HB - 212.

Departament Wydawnictw UP RP. Nakład 90 egz.Publishing Department of the UP RP. Circulation of 90 copies

Cena 2,00 złPrice PLN 2.00

Claims

Patent claim

Heat-resistant cast steel, for work under load at temperatures up to 950 ° C in an oxidizing atmosphere containing carbon, manganese, silicon, phosphorus, sulfur, chromium and nickel, characterized in that it contains 0.30 - 0.50% by weight of carbon, up to a maximum of 1 , 50% manganese, 1.00 - 2.50% silicon, maximum 0.035% phosphorus, maximum 0.035% sulfur, 21.0 - 23.0% chromium, 9.0-11.0% nickel.