PL194360B1 - Kompozycja smarna zawierająca olej bazowy i zagęszczacz - Google Patents

Kompozycja smarna zawierająca olej bazowy i zagęszczacz

Info

Publication number
PL194360B1
PL194360B1 PL01363179A PL36317901A PL194360B1 PL 194360 B1 PL194360 B1 PL 194360B1 PL 01363179 A PL01363179 A PL 01363179A PL 36317901 A PL36317901 A PL 36317901A PL 194360 B1 PL194360 B1 PL 194360B1
Authority
PL
Poland
Prior art keywords
lubricant composition
benzotriazole
weight
hydroxy
additives
Prior art date
Application number
PL01363179A
Other languages
English (en)
Other versions
PL363179A1 (pl
Inventor
Takahiro Ozaki
Noriaki Shinoda
Kouichi Nakazawa
Original Assignee
Shell Int Research
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shell Int Research filed Critical Shell Int Research
Publication of PL363179A1 publication Critical patent/PL363179A1/pl
Publication of PL194360B1 publication Critical patent/PL194360B1/pl

Abstract

1. Kompozycja smarna zawierajaca olej bazowy i zageszczacz, znamienna tym, ze dodatkowo zawiera od 0,05% do 30% wag. tiosiarczanu sodu i co najmniej 0,1% wag. jednego lub wiecej z dodatków (A) wybranych z grupy obejmujacej salicylan wapnia, salicylan magnezu, fenolan wapnia i/lub sulfonian wapnia, w odniesieniu do calkowitej kompozycji smarnej, oraz ewentualnie zwiazek benzotriazolowy (B). PL PL PL PL

Description

Opis wynalazku
Niniejszy wynalazek dotyczy kompozycji smarnej zawierającej olej bazowy i zagęszczacz, która wykazuje właściwości polepszonego zapobiegania rdzewieniu i polepszonej odporności na ścieranie.
Smary stosowane w ekstremalnie wysokich ciśnieniach mają wiele zastosowań, ze względu na ich doskonałą odporność na ścieranie i ich zdolność do przenoszenia obciążeń, na przykład w łożyskach i przekładniach, w samochodach, przemyśle żelaza i stali, na kolei i wielu innych przemysłowych urządzeniach mechanicznych.
Typowe kompozycje smarów odpornych na wysokie ciśnienia generalnie są kompozycjami, które w różnych typach smarów zawierają dodatki, takie jak siarczki olefin, siarczki tłuszczów i olejów, środki oparte na siarce-fosforze, odporne na wysokie ciśnienia, disiarczek molibdenu, związki molibdenoorganiczne, związki ołowiu i ditiofosforan cynku.
Ostatnio ujawnione kompozycje smarowe, zawierające tiosiarczan sodu, wykazujące doskonałe właściwości odporności na wysokie ciśnienia to smary opisane w wyłożeniowych japońskich opisach patentowych 3-131690 i 11-35965 oraz opisie patentowym USA Nr 4 923 625.
Jednak odporność na ścieranie w tych publikacjach według stanu techniki jest niezadowalająca i istnieje dalsze niebezpieczeństwo, że zostanie wywołane rdzewienie, ponieważ tiosiarczan sodu ma właściwości absorpcji wilgoci. W szczególności, ponieważ łożyska i przekładnie wyposażenia ze stali i maszyn do przemysłu spożywczego są smarowane w warunkach, gdzie występuje duża ilość wody, sprzyja to powstawaniu rdzy i szybko powstają problemy związane ze smarowaniem.
Jest więc bardzo potrzebne, aby istniała możliwość dostarczenia kompozycji smarnych, zawierających tiosiarczan sodu, w których zachowane zostaną właściwości odporności na wysokie ciśnienia a także równoczesne zahamowanie powstawania rdzy i polepszenie odporności na ścieranie.
Niniejszy wynalazek dostarcza kompozycji smarnej zawierającej olej bazowy i zagęszczacz, która zawiera dodatkowo od 0,05% do 30% wag. tiosiarczanu sodu i co najmniej 0,1% wag. jednego lub więcej dodatków (A) wybranych z grupy obejmującej salicylan wapnia, salicylan magnezu, fenolan wapnia i/lub sulfonian wapnia, w odniesieniu do całkowitej kompozycji smarnej, oraz ewentualnie związek benzotriazolowy (B).
W korzystnej postaci wykonania, kompozycja smarna według wynalazku zawiera dodatkowo co najmniej 0,1% wag. związku benzotriazolowego (B), w odniesieniu do całkowitej kompozycji smarnej.
W kompozycjach smarnych według wynalazku zagęszczaczem może być środek, taki jak związki mocznikowe, mydła litowe, kompleksowe mydła litowe i kompleksowe mydła glinowe, które mogą być stosowane pojedynczo lub w mieszaninie. Dodatkowo, obok związków zawierających wiązania mocznikowe, związki mogą naturalnie zawierać zarówno wiązania mocznikowe jak i wiązania uretanowe. Dogodnie można stosować zagęszczacz dimocznikowy, trimocznikowy i/lub tetramocznikowy. Jako zagęszczacz można stosować ponadto dogodnie związki mocznikowo-imidowe.
W korzystnej postaci wykonania wynalazku stosuje się 2 do 35% wag. zagęszczacza w odniesieniu do całkowitej kompozycji smarnej.
Oleje bazowe stosowane zgodnie z wynalazkiem mogą wykorzystywać także oleje roślinne, oleje mineralne i oleje syntetyczne, takie jak oleje estrowe, oleje eterowe i oleje węglowodorowe.
Tiosiarczan sodu stosowany zgodnie z wynalazkiem może stanowić tiosiarczan Na2S2O3 (bezwodny) lub Na2S2O3^5H2O (pentahydrat) lub ich mieszanina. Można stosować handlowe dodatki zawierające tiosiarczan sodu (na przykład, Desilube 88, Desilube Technology Incorporated, USA).
Ilość dodawanego tiosiarczanu sodu leży korzystnie w zakresie od 0,2% do 20% wag., bardziej korzystnie od 0,2% do 10% wag., jeszcze bardziej korzystnie w zakresie od 0,2% do 8% wag. a najbardziej korzystnie w zakresie od 0,5% do 6% wag. w odniesieniu do całkowitej kompozycji smarnej.
Korzystnie jeden lub więcej dodatków (A),wybranych z grupy obejmującej salicylan wapnia, salicylan magnezu, fenolan wapnia i/lub sulfonian wapnia, każdy zawarty jest w ilości w zakresie od 0,1% do 5% wag., bardziej korzystnie w zakresie od 0,2% do 3% wag., w odniesieniu do całkowitej kompozycji smarnej.
Związek benzotriazolowy (B) zawarty jest korzystnie w ilości w zakresie od 0,1% do 5% wag., bardziej korzystnie w zakresie od 0,2% do 3% wag. w odniesieniu do całkowitej kompozycji smarnej.
Przedmiotem wynalazku jest także zastosowanie kompozycji smarnej według wynalazku do polepszenia zapobiegania rdzewieniu oraz odporności na ścieranie.
PL 194 360 B1
Gdy zawartość wyżej wspomnianego związku (A) jest mniejsza niż 0,1% wag., to zabezpieczenie przed rdzewieniem jest niewystarczające, zaś gdy zawartość wyżej wspomnianego związku (B) jest mniejsza niż 0,1% wag., to odporność na ścieranie jest niewystarczająca.
Gdy zawartość każdego z dodatków jest większa niż 5% wag., to dalszy wzrost ich wpływów albo jest ograniczony albo go nie ma.
Przykłady wyżej wspomnianych benzotriazoli (B) obejmują: 1,2,3-benzotriazol, 2-(2'-hydroksy-5'-metylofenylo)benzotriazol, 2-[2'-hydroksy-3'-(3'',4,5,6-tetrahydroftalimido-metylo)-5'-metylofenylo]benzotriazol, 2-(2'-hydroksy-3',5'-di-t.-butylofenylo)benzotriazol, 2-(2'-hydroksy-5'-t.-oktylofenylo)benzotriazol, 2-(2'-hydroksy-3',5'-di-t.-amylofenylo)benzotriazol, 2-[2-hydroksy-3,5-bis(a,a-dimetylobenzylo)fenylo]-2H-benzotriazol i 2-(2'-hydroksy-3'-undecylo-5'-metylofenylo)benzotriazol.
Kompozycja smarna według wynalazku może ponadto zawierać dodatkowe dodatki, na przykład przeciwutleniacze, takie jak aminy i fenole; dodatki polepszające odporność na ekstremalne ciśnienia (dodatki smarne typu EP), takie jak siarczki olefin i tłuszczów oraz siarczki olejów; środki uodparniające na działanie wysokich ciśnień/odporność na ścieranie, takie jak fosforyny i fosforany; zagęszczacze, takie jak polibuteny i polimetakrylany; stałe substancje smarne, takie jak azotek boru i disiarczek molibdenu oraz różne inne dodatki.
Kompozycje smarne według wynalazku mogą być wytwarzane albo przez wstępne zmieszanie tiosiarczanu sodu, jednego lub więcej dodatków (A) wybranych z grupy obejmującej salicylan wapnia, salicylan magnezu, fenolan wapnia i/lub sulfonian wapnia i dowolnego dalszego dodatku przeznaczonego do wprowadzenia do oleju bazowego i dodanie mieszaniny do bazy smaru, zawierającej olej bazowy i zagęszczacz albo przez wprowadzenie każdego z dodatków indywidualnie do bazy smaru. Można to uzyskać poprzez mieszanie na zimno lub na gorąco i następujące po tym ujednorodnianie, w celu zapewnienia jednorodnej dyspersji składników dodatkowych.
Kompozycja smarna według wynalazku może być dogodnie stosowana w łożyskach, przekładniach i połączeniach, takich jak złącza o stałej szybkości.
Wynalazek zostanie teraz opisany w odniesieniu do następujących przykładów, które nie są pomyślane jako ograniczające w jakikolwiek sposób zakres wynalazku.
Przykłady
Wytwarzanie kompozycji smarnej
Smary z przykładów i z przykładów porównawczych otrzymuje się zgodnie z recepturami podanymi w tabelach 1 do 9, przez dodawanie do smarów bazowych odpowiednio wyżej wspomnianych dodatków (A) i (B), albo innych dodatków, i ich obróbkę w młynie trójwalcowym. Kompozycje smarów bazowych podane są niżej.
I. Mocznikowy smar bazowy
Poddaje się reakcji 4,4'-diizocyjanian difenylometanu (295,2 g) i oktyloaminę (304,8 g) w oczysz2 czonym oleju mineralnym (lepkość kinematyczna około 15 mm2/s w temperaturze 100°C; 5400 g); otrzymany związek mocznikowy jednorodnie dysperguje się tak, że uzyskuje się mocznikowy smar bazowy o konsystencji 289 (w temperaturze 25°C, 60 W) i temperaturze kroplenia 263°C. Zawartość związku mocznikowego wynosi 10% wagowych.
II. Smar bazowy z mydłami litowymi
Smar bazowy z mydłami litowymi o konsystencji 268 (w temperaturze 25°C, 60 W) i temperaturze kropienia 199°C uzyskuje się przez jednorodne dyspergowanie 12-hydroksy-stearynianu litu (600 g), rozpuszczając go w oczyszczonym oleju mineralnym (lepkość kinematyczna około 15 mm2/s w temperaturze 100°C; 5400 g). Zawartość mydła litowego wynosi 10% wagowych.
III. Smar bazowy z kompleksowymi mydłami litowymi
Kwas 12-hydroksystearynowy (350 g) i wodorotlenek litu (50,5 g) poddaje się reakcji w oczysz2 czonym oleju mineralnym (lepkość kinematyczna około 11 mm2/s w temperaturze 100°C; 4165 g), po czym otrzymuje się kompozycję smaru bazowego ze związkiem kompleksowego mydła litowego o konsystencji 281 (w temperaturze 25°C, 60 W) i temperaturze kroplenia 259°C przez reakcję kwasu azelainowego (120,65 g)i wodorotlenku litu (59,0 g) i jednorodne zdyspergowanie. Zawartość kompleksowego mydła litowego wynosi 10,4% wagowych.
IV. Smar bazowy z kompleksowymi mydłami glinowymi 2
W oczyszczonym oleju mineralnym (lepkość kinematyczna około 11 mm2/s w temperaturze 100°C; 4272 g), rozpuszcza się kwas benzoesowy (158,22 g) i kwas stearynowy (334,8 g), po czym otrzymuje się kompozycję smaru ze związkiem mydła glinowego o konsystencji 279 (w temperaturze 25°C, 60 W) i temperaturze kroplenia 258°C przez przeprowadzenie reakcji, polegającej na dodawaniu handlowej
PL 194 360 B1 cieczy smarnej propylanu cyklicznego tlenku glinu (nazwa handlowa Arugoma (Algomer) wytwarzanej przez Sengen Fain Kemikaru (Sengen Fine Chemicals) K.K.) i wytworzone mydło dysperguje się jednorodnie. Zawartość kompleksowego mydła glinowego wynosi 11% wagowych. Stosunek molowy kwasu benzoesowego (BA) i kwasu stearynowego (FA) przyjęto jako 1,1 : 1, a stosunek molowy kwasu benzoesowego plus kwasu stearynowego do glinu przyjęto jako (BA+FA)/Al = 1,9 : 1.
Właściwości zapobiegania korozji, ekstremalnego ciśnienia i ścierne określano wykonując testy zapobiegania korozji (testy wilgotności) i testy czterokulkowe (testy ekstremalnego ciśnienia oraz odporności na ścieranie).
Badania wilgotności
Na całej powierzchni badanych kawałków próbnych nakładano jednorodnie próbki smaru w taki sposób, że ilość smaru nałożona na powierzchnię badanej próbki wynosiła 0,30 ±0,05 g, jak to zaleca się według normy badania wilgotności JIS (Japońska norma przemysłowa) K2220 5.17. Płytki stalowe, na których nałożony był smar, umieszcza się w komorze wilgotnościowej w temperaturze 49°C i przy wilgotności względnej przynajmniej 95% i ocenia stopień zardzewienia po 2 tygodniach według oceny zgodnej z normą JIS K2246.
Stopień % zardzewienia
stopień A 0
stopień B 1 do 10
stopień C 11 do 25
stopień D 26 do 50
stopień E 51 do 100
Badania odporności na ekstremalne ciśnienia
Mierzy się obciążenie rozszerzalności (N) w teście czterokulkowym według ASTM (Amerykańskie Towarzystwo Badania Materiałów) D2596.
Warunki badania:
szybkość obrotów: 1770 ± 60 obrotów na minutę temperatura: 27°C ± 8°C czas: 10 ± 0,2 s.
Test odporności na ścieranie
Mierzy się średnicę odcisków ze ścierania dla kulek stosowanych w teście czterokulkowym zgodnie z ASTM D2266.
Warunki badania:
szybkość obrotów: 1200 ± 50 obrotów na minutę temperatura: 75°C ± 1,7°C obciążenie: 40 ± 2 kG (392 ± 2 N) czas: 60 ± 1 minuta.
Dodatki
W tabelach poniżej symbole od *1 do *10 oznaczają:
Desilube 88, *1, jest nazwą handlową firmy Desilube Technology Incorporated, dla dodatku nieorganicznego S-P, zawierającego tiosiarczan sodu.
Produkty niżej odpowiadają wyżej wspomnianemu dodatkowi (A) według wynalazku.
SAP001, *2, jest nazwą handlową produktu firmy Infineum Limited, dla salicylanu wapnia. SAP007, *3, jest nazwą handlową produktu firmy Infineum Limited, dla salicylanu magnezu. OLOA219, *4, jest nazwą handlową produktu firmy Oronaito, Japonia (K.K.), dla fenolanu wapnia. NA-SUL 729, *5, jest nazwą handlową produktu firmy King Industries Incorporated, dla sulfonianu wapnia.
Produkty niżej odpowiadają wyżej wspomnianemu dodatkowi (B) według wynalazku.
BT-120, *6, jest nazwą handlową produktu firmy Shirokita Kagaku (Skirokita Chemicals), (K.K), dla 1,2,3-benzotriazolu.
Następnie podane są dodatki inne niż (A) i (B).
NA-SUL ZS, *7, jest nazwą handlową produktu firmy King Industries Incorporated, dla sulfonianu cynku.
PL 194 360 B1
Dailube Z-500, *8, jest nazwą handlową produktu firmy Dainippon Inki Kagaku Kogyo (Dainippon Ink and Chemicals) (K.K.) dla naftenianu cynku rozcieńczonego w oleju mineralnym (5% metalicznego cynku).
NA-SUL SS, *9, jest nazwą handlową produktu firmy King Industries Incorporated, dla sulfonianu sodu.
NA-SUL 707, *10, jest nazwą handlową produktu firmy King Industries Incorporated, dla sulfonianu litu.
Tabela 1
Przykład 1 2 3 4 5 6 7 8 9 10
Baza Smar 95,0 95,0 95,0 95,0 95,0 95,0 95,0 95,0 95,0 95,0
smaru mocznikowy
Na2S2O3 3,0 3,0 3,0 3,0
Skład % wagowy Na2S2O3x5H2O 3,0 3,0 3,0 3,0
Dodatek Desilube 88 *1 3,0 3,0
SAP001 *2 2,0 2,0 2,0
SAP007 *3 2,0 2,0 2,0
OLOA219*4 2,0 2,0
NA-SUL 729 *5 2,0 2,0
BT-120 *6
Łącznie 100 100 100 100 100 100 100 100 100 100
Wyniki badań Test zapobiegania rdzewieniu Test wilgotnościowy A A A A A A A A A A
Test czterokulkowy Obciążenie 7845 7845 7845 7845 6080 6080 6080 6080 7845 7845
ekspansji, N Średnica śladu ścierania, mm 0,71 0,71 0,63 0,71 0,71 0,71 0,58 0,68 0,70 0,69
PL 194 360 B1
T a b e l a 2
Przykład 11 12 13 14 15 16 17 18 19 20
Baza Smar 95,0 95,0 93,0 93,0 94,5 94,5 94,5 92,5 93,0 93,0
smaru mocznikowy
Na2S2O3 3,0 3,0 3,0 2,0
Skład % wagowy Na2S2O3x5H2O 1,0 3,0 1,0 2,0
Dodatek Desilube 88 *1 3,0 3,0 2,0 3,0 1,0
SAP001 *2 2,0 2,0 2,0 2,0 1,0
SAP007 *3 2,0 1,0 1,0 1,0
OLOA219 *4 2,0 1,0 0,5 1,0
NA-SUL 729 *5 2,0 2,0 2,0
BT-120 *6 0,5 0,5 2,0 0,5 2,0 2,0
Łącznie 100 100 100 100 100 100 100 100 100 100
Wyniki badań Test zapobiegania rdzewieniu Test wilgotnościowy A A A A A A A A A A
Test czterokulkowy Obciążenie 7845 7845 7845 7845 7845 6080 7845 7845 7845 7845
ekspansji, N Średnica śladu ścierania, mm 0,55 0,68 0,69 0,67 0,46 0,43 0,45 0,39 0,39 0,45
T a b e l a 3
Przykład 21 22 23 24 25 26 27 28 29 30
Baza Smar z mydłem 95,0 95,0 93,0 93,0 94,5 93,0 93,0 93,0 93,0 93,0
smaru litowym
Na2S2O3 2,0 2,0 3,0 2,0 2,0
Skład % wagowy Na2S2O3x5H2O 1,0 2,0 1,0 1,0 2,0
Dodatek Desilube 88 *1 3,0 1,0 1,0 3,0 3,0 1,0
SAP001 *2 1,0 1,0
SAP007 *3 2,0 2,0 2,0 1,0
OLOA219 *4 2,0 2,0 2,0 0,5 1,0 1,0 1,0 2,0
NA-SUL 729 *5 2,0 2,0
BT-120 *6 2,0 2,0 2,0 2,0 2,0
Łącznie 100 100 100 100 100 100 100 100 100 100
Wyniki badań Test zapobiegania rdzewieniu Test wilgotnościowy A A A A A A A A A A
Test czterokulkowy Obciążenie 6080 6080 6080 6080 6080 6080 6080 6080 6080 6080
ekspansji, N Średnica śladu ścierania, mm 0,72 0,72 0,71 0,68 0,72 0,47 0,49 0,39 0,49 0,50
PL 194 360 B1
T a b e l a 4
Przykład 31 32 33 34 35 36 37 38 39 40
Baza Smar z 95,0 95,0 95,0 94,0 95,0 93,0 93,0 93,0 94,0 94,0
smaru kompleksowym mydłem litowym
Na2S2O3 3,0 3,0
Skład % wagowy Na2S2O3x5H2O 3,0 3,0 1,0 3,0 3,0 1,0
Dodatek Desilube 88 *1 3,0 2,0 3,0 2,0
SAP001 *2 2,0 2,0 1,0
SAP007 *3 2,0 2,0
OLOA219 *4 2,0 1,0 1,0 2,0 1,0 1,0
NA-SUL 729 *5 2,0 1,0
BT-120 *6 2,0 2,0 2,0 2,0 1,0
Łącznie 100 100 100 100 100 100 100 100 100 100
Wyniki badań Test zapobiegania rdzewieniu Test wilgotnościowy A A A A A A A A A A
Test czterokulkowy Obciążenie 6080 4903 6080 4903 6080 6080 4903 6080 4903 6080
ekspansji, N Średnica śladu ścierania, mm 0,60 0,79 0,78 0,78 0,77 0,47 0,48 0,54 0,56 0,51
T a b e l a 5
Przykład 41 42 43 44 45 46 47 48 49 50
Baza Smar z 93,0 93,0 93,0 93,0 93,0 93,0 93,0 93,0 93,0 93,0
smaru kompleksowym mydłem glinowym
Na2S2O3 3,0 3,0 1,0 2,0
Skład % wagowy Na2S2O3x5H2O 3,0 3,0 3,0 2,0
Dodatek Desilube 88 *1 3,0 3,0 2,0 1,0 1,0
SAP001 *2 2,0 2,0 1,0
SAP007 *3 2,0 1,0 2,0 1,0
OLOA219 *4 2,0 1,0 1,0 1,0
NA-SUL 729 *5 2,0 1,0 1,0
BT-120 *6 2,0 2,0 2,0 2,0 2,0 2,0 2,0 2,0 2,0 2,0
Łącznie 100 100 100 100 100 100 100 100 100 100
Wyniki badań Test zapobiegania rdzewieniu Test wilgotnościowy A A A A A A A A A A
Test czterokulkowy Obciążenie 3922 3922 3089 3089 3922 3922 3089 3922 3922 3922
ekspansji, N Średnica śladu ścierania, mm 0,73 0,71 0,72 0,68 0,70 0,73 0,70 0,67 0,72 0,71
PL 194 360 B1
T a b e l a 6
Przykład porównawczy 1 2 3 4 5 6 7 8 9 10
Baza Smar 100,0 97,0 97,0 97,0 93,0 93,0 93,0 93,0 93,0 93,0
smaru mocznikowy
Na2S2O3 3,0 3,0 2,0 3,0
Skład % wagowy Na2S2O3x5H2O 3,0 1,0 3,0 2,0
Dodatek Desilube 88 *1 3,0 3,0 1,0
NA-SUL ZS *7 4,0
Dailube Z-500 *8 4,0 2,0
NA-SUL SS *9 4,0 2,0 2,0
NA-SUL 707 *10 4,0 2,0
Łącznie 100 100 100 100 100 100 100 100 100 100
Wyniki badań Test zapobiegania rdzewieniu Test wilgotnościowy A E E E E E E E E E
Test czterokulkowy Obciążenie 1570 7845 6080 7845 7845 7845 7845 6080 7845 7845
ekspansji, N Średnica śladu ścierania, mm 0,88 0,68 0,72 0,68 0,72 0,78 0,89 0,84 0,81 0,87
T a b e l a 7
Przykład porównawczy 11 12 13 14 15 16 17 18 19 20
Baza Smar z 100,0 97,0 97,0 97,0 93,0 93,0 93,0 93,0 93,0 93,0
smaru mydłem litowym
Skład % wagowy Na2S2O3 3,0 3,0 2,0 3,0
Na2S2O3x5H2O 3,0 1,0 3,0 2,0
Dodatek Desilube 88 *1 3,0 3,0 1,0
NA-SUL ZS *7 4,0
Dailube Z-500 *8 4,0 2,0
NA-SUL SS *9 4,0 2,0 2,0
NA-SUL 707 *10 4,0 2,0
Łącznie 100 100 100 100 100 100 100 100 100 100
Wyniki badań Test zapobiegania rdzewieniu Test wilgotnościowy A E E E E E E E E E
Test czterokulkowy Obciążenie 1236 6080 4903 6080 6080 6080 6080 4903 6080 6080
ekspansji, N Średnica śladu ścierania, mm 0,93 0,74 0,72 0,69 0,71 0,70 0,69 0,68 0,74 0,66
PL 194 360 B1
T a b e l a 8
Przykład porównawczy 21 22 23 24 25 26 27 28 29 30
Baza Smar z 100,0 97,0 97,0 97,0 93,0 93,0 93,0 93,0 93,0 93,0
smaru kompleksowym mydłem litowym
Skład % wagowy Na2S2O3 3,0 3,0 2,0 3,0
Na2S2O3x5H2O 3,0 1,0 3,0 2,0
Dodatek Desilube 88 *1 3,0 3,0 1,0
NA-SUL ZS *7 4,0
Dailube Z-500 *8 4,0 2,0
NA-SUL SS *9 4,0 2,0 2,0
NA-SUL 707 *10 4,0 2,0
Łącznie 100 100 100 100 100 100 100 100 100 100
Wyniki badań Test zapobiegania rdzewieniu Test wilgotnościowy A E E E E E E E E E
Test czterokulkowy Obciążenie 1570 6080 6080 6080 6080 6080 6080 6080 6080 6080
ekspansji, N Średnica śladu ścierania, mm 0,79 0,78 0,77 0,76 0,78 0,76 0,65 0,79 0,71 0,69
T a b e l a 9
Przykład porównawczy 31 32 33 34 35 36 37 38 39 40
Baza Smar z 100,0 97,0 97,0 97,0 93,0 93,0 93,0 93,0 93,0 93,0
smaru kompleksowym mydłem glinowym
Skład % wagowy Na2S2O3 3,0 3,0 2,0 3,0
Na2S2O3x5H2O 3,0 1,0 3,0 2,0
Dodatek Desilube 88 *1 3,0 3,0 1,0
NA-SUL ZS *7 4,0
Dailube Z-500 *8 4,0 2,0
NA-SUL SS *9 4,0 2,0 2,0
NA-SUL 707 *10 4,0 2,0
Łącznie 100 100 100 100 100 100 100 100 100 100
Wyniki badań Test zapobiegania rdzewieniu Test wilgotnościowy A E E E E E E E E E
Test czterokulkowy Obciążenie 1570 3089 3089 3922 3922 3922 3922 3089 3922 3922
ekspansji, N Średnica śladu ścierania, mm 0,98 0,71 0,70 0,69 0,72 0,72 0,76 0,81 0,70 0,84
PL 194 360 B1
Wyniki według wynalazku
Jak to jest wyraźnie widoczne z przykładów w tabelach 1 do 5 i przykładów porównawczych w tabelach 6 do 9, kompozycje smarne według wynalazku, w których do kompozycji smarnej, zawierającej tiosiarczan sodu, zostały dodane wyżej wspomniane dodatki (A), wykazywały doskonałe właściwości odporności na wysokie ciśnienia, a ich zdolność do zabezpieczenia przed rdzewieniem została znacznie zwiększona. Kompozycje smarne, w których wyżej wspomniane dodatki (A) i wyżej wspomniane związki benzotriazolowe (B) dodane zostały do kompozycji smarnej, zawierającej tiosiarczan sodu, wykazywały doskonałe właściwości odporności na wysokie ciśnienia i zdolność do zabezpieczenia przed rdzewieniem oraz dodatkowo miały doskonałą odporność na ścieranie. Zwiększenie odporności na ścieranie jest szczególnie duże w smarach mocznikowych, smarach z mydłami litowymi i smarach z kompleksowymi mydłami litowymi. Tiosiarczan sodu jest od dawna uznanym dodatkiem do żywności, a ponieważ wiadomo także, że jest środkiem odtruwającym, jest on dodatkiem nie tylko łagodnym dla organizmu ludzkiego, lecz także i dla całego środowiska. Kompozycje według wynalazku są więc doskonałymi smarami zgodnymi ze środowiskiem.

Claims (10)

  1. Zastrzeżenia patentowe
    1. Kompozycja smarna zawierająca olej bazowy i zagęszczacz, znamienna tym, że dodatkowo zawiera od 0,05% do 30% wag. tiosiarczanu sodu i co najmniej 0,1% wag. jednego lub więcej z dodatków (A) wybranych z grupy obejmującej salicylan wapnia, salicylan magnezu, fenolan wapnia i/lub sulfonian wapnia, w odniesieniu do całkowitej kompozycji smarnej, oraz ewentualnie związek benzotriazolowy (B).
  2. 2. Kompozycja smarna według zastrz. 1, znamienna tym, że każdy spośród wspomnianego jednego lub więcej dodatków (A) jest zawarty w ilości w zakresie od 0,1% do 5% wag. w odniesieniu do całkowitej kompozycji smarnej.
  3. 3. Kompozycja smarna według zastrz. 1 albo 2, znamienna tym, że każdy spośród wspomnianego jednego lub więcej dodatków (A) jest zawarty w ilości w zakresie od 0,2% do 3% wagowych w odniesieniu do całkowitej kompozycji smarnej.
  4. 4. Kompozycja smarna według zastrz. 1 albo 3, znamienna tym, że kompozycja zawiera co najmniej 0,1% wag. związku benzotriazolowego (B) w odniesieniu do całkowitej kompozycji smarnej.
  5. 5. Kompozycja smarna według zastrz. 4, znamienna tym, że związek benzotriazolowy (B) zawarty jest w ilości w zakresie od 0,1% do 5% wag. w odniesieniu do całkowitej kompozycji smarnej.
  6. 6. Kompozycja smarna według zastrz. 4, znamienna tym, że związek benzotriazolowy (B) zawarty jest w ilości w zakresie od 0,2% do 3% wag. w odniesieniu do całkowitej kompozycji smarnej.
  7. 7. Kompozycja smarna według zastrz. 4, znamienna tym, że związek benzotriazolowy (B) wybrany jest spośród 1,2,3-benzotriazolu, 2-(2'-hydroksy-5'-metylofenylo)benzotriazolu, 2-[2'-hydroksy-3'-(3,4,5,6-tetrahydroftalimidometylo)-5'-metylofenylo]benzotriazolu, 2-(2'-hydroksy-3',5'-di-t.-butylofenylo)benzotriazolu, 2-(2'-hydroksy-3',5'-di-t.-oktylofenylo)benzotriazolu, 2-(2'-hydroksy-5'-t.-amylofenylo)benzotriazolu, 2-[2-hydroksy-3,5-bis(a,a-dimetylobenzylo)fenylo]-2H-benzotriazolu i 2-(2'-hydroksy-3'-undecylo-5'-metylofenylo)benzotriazolu.
  8. 8. Kompozycja smarna według zastrz. 1 albo 2, albo 5, znamienna tym, że zagęszczaczem jest jeden lub więcej związek mocznikowy, jedno lub więcej mydła litowe i/lub kompleksowe mydła litowe lub jedno lub więcej kompleksowe mydła glinowe.
  9. 9. Zastosowanie kompozycji smarnej określonejjakwzastrz. 1 albo2 do polepszenia zapobiegania rdzewieniu oraz odporności na ścieranie.
  10. 10. Sposób wytwarzania kompozycji smarnej określonej jak w zastrz. 1 albo 2, znamienny tym, że miesza się wstępnie tiosiarczan sodu i jeden lub więcej dodatków (A) wybranych z grupy obejmującej salicylan wapnia, salicylan magnezu, fenolan wapnia i/lub sulfonian wapnia, i mieszaninę dodaje się do bazy smaru zawierającej olej bazowy i zagęszczacz, albo tiosiarczan sodu i wspomniany jeden lub więcej dodatków (A)wprowadzasięosobnodowspomnianejbazysmaru.
PL01363179A 2000-08-10 2001-08-10 Kompozycja smarna zawierająca olej bazowy i zagęszczacz PL194360B1 (pl)