PL232871B1 - Płyta wielowarstwowa - Google Patents

Płyta wielowarstwowa

Info

Publication number
PL232871B1
PL232871B1 PL413342A PL41334215A PL232871B1 PL 232871 B1 PL232871 B1 PL 232871B1 PL 413342 A PL413342 A PL 413342A PL 41334215 A PL41334215 A PL 41334215A PL 232871 B1 PL232871 B1 PL 232871B1
Authority
PL
Poland
Prior art keywords
layer
cork
layers
board according
multilayer board
Prior art date
Application number
PL413342A
Other languages
English (en)
Other versions
PL413342A1 (pl
Inventor
Sławomir Andrzej Gajdziński
Original Assignee
Gajdzinski Slawomir Andrzej
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Gajdzinski Slawomir Andrzej filed Critical Gajdzinski Slawomir Andrzej
Priority to PL413342A priority Critical patent/PL232871B1/pl
Priority to CN201680057109.6A priority patent/CN108139187A/zh
Priority to EP16830909.4A priority patent/EP3329206A4/en
Priority to PCT/PL2016/000085 priority patent/WO2017018898A1/en
Priority to JP2018525336A priority patent/JP2018523810A/ja
Priority to RU2018104094A priority patent/RU2018104094A/ru
Priority to US15/748,636 priority patent/US20190003806A1/en
Publication of PL413342A1 publication Critical patent/PL413342A1/pl
Priority to IL257257A priority patent/IL257257A/en
Publication of PL232871B1 publication Critical patent/PL232871B1/pl

Description

Opis wynalazku
Przedmiotem wynalazku jest płyta wielowarstwowa, przeznaczona do ochrony przed penetracją, zwłaszcza pocisków z broni palnej.
Znany jest szereg płyt wielowarstwowych, służących jako płyty pancerne, do ochrony przed penetracją pocisków broni palnej, różnego kalibru i rodzaju.
Z opisu patentowego PL172656 znany jest pancerz wielowarstwowy, zawierający płytę pancerną, do której przylega warstwa wychwytująca, wykonana z wielowarstwowej tkaniny, do której przymocowana jest warstwa amortyzująca, zbudowana z elastomeru, do której następnie przymocowana jest warstwa zabezpieczająca z wielowarstwowej tkaniny, trwale ze sobą zespolone. Rozwiązanie to jest dedykowane odzieży ochronnej i ma ograniczony zakres zastosowania, ze względu na dużą masę własną jednostkową oraz poziom zabezpieczenia przed przebiciem i służy do ochrony przed pociskami broni palnej krótkiej.
Ze zgłoszenia patentowego PL404286 znany jest pasywny, modułowy pancerz warstwowy, zawierający dwie warstwy stopu aluminium, warstwę stali pancernej, drugiej warstwy stali pancernej walcowanej, warstwy z lekkiego tworzywa sztucznego oraz cienkiej warstwy z blachy stopu aluminium. Drugi wariant tego rozwiązania nie zawiera warstwy z lekkiego tworzywa sztucznego. Rozwiązanie to jest dedykowane do ochrony przed pociskami kalibru do 14,5 mm i do zastosowania na obiektach stałych oraz pojazdach, jednak ze względu na dużą masę własną jednostkową jego zastosowanie jest ograniczone.
Ze zgłoszenia patentowego PL406578 znany jest pancerz elastyczny zawierający warstwę ceramiczną zbudowaną z elementów przestrzennych, przedniego stosu warstw, za którym umieszczona jest warstwa woreczków zawierających ciecz, której lepkość wzrasta wraz ze wzrostem szybkości ścinania oraz tylnego stosu warstw aramidowych i/lub polietylenowych. Rozwiązanie to jest dedykowane do ochrony przed pociskami kalibru do 14,5 mm, dodatkowo chroni przed przebiciem odłamkami i wybuchem. Nadaje się również do zastosowania jako wkład do kamizelek kuloodpornych, jednak ze względu na skomplikowany proces wytwarzania oraz ograniczone możliwości ochrony jak też ze względu na dużą masę własną jednostkową jego zastosowanie jest ograniczone.
Płyta wielowarstwowa według wynalazku zawiera warstwy zbrojenia zbudowane z metalu lub ceramiki lub szkła lub tworzyw sztucznych lub tkaniny aramidowej, aramidowo-szklanej, szklanej, polietylenowej o ultrawysokiej masie cząsteczkowej (PE-UHMW), lub zbudowane z kombinacji tych materiałów oraz warstw amortyzujących charakteryzuje się tym, że co najmniej jedna warstwa amortyzująca utworzona jest z korka i/lub co najmniej jedna warstwa amortyzująca utworzona jest z mieszaniny korka z innymi substancjami sprężystymi, przy czym warstwy zewnętrzne płyty stanowią warstwy zbrojenia a pomiędzy nimi znajdują się naprzemiennie warstwy amortyzujące i warstwy zbrojenia, trwale zespolone. Korzystnym wariantem rozwiązania jest utworzenie przynajmniej jednej warstwy amortyzującej z aglomeratu korkowego lub z ekspandowanego korka lub z mieszaniny korka z innymi substancjami sprężystymi. Szczególnie korzystnym wariantem rozwiązania jest utworzenie warstwy amortyzującej z mieszaniny korka z gumą lub z mieszaniny korka z poliuretanem lub z mieszaniny korka z gumą i poliuretanem. Płyta wielowarstwowa według wynalazku może składać się z warstwy amortyzującej, która zawiera wewnątrz dodatkowe przestrzenne warstwy amortyzujące, korzystnie w kształcie falistym, trapezowym, trójkątnym, lub sześciennym lub plastra miodu. Warstwa zbrojenia korzystnie jest zbudowana z aluminium lub duraluminium, tytanu lub stali pancernej - w zależności od zapotrzebowania. W płycie według wynalazku zespolenie warstw korzystnie jest dokonywane przez sklejenie lub łączenie termoplastyczne lub laminowanie lub prasowanie lub warstwy są zespolone korzystnie w procesie infuzji RTM (Resin Transfer Molding) lub infuzji LRTM (Light Resin Transfer Molding) lub w procesie CCBM (Closed Cavity Bag Moulding).
Płyta wielowarstwowa według wynalazku charakteryzuje się bardzo niską masą własną jednostkową, przy jednoczesnym zachowaniu wysokiej odporności na przebicie. Ponadto nadaje się do dowolnego kształtowania, może stanowić ochronę właściwą, lub wspomagać inne rodzaje opancerzenia. Możliwe jest zastosowanie płyty przy wytwarzaniu elementów konstrukcyjnych lub izolacyjnych w przemyśle motoryzacyjnym, budowlanym, transportowym. Przedmiot wynalazku pokazany jest na przykładach wykonania i na rysunku, gdzie fig. 1 przedstawia odpowiednio płytę w przekroju poprzecznym z zastosowaniem wielu warstw, fig. 2 przedstawia płytę w przekroju poprzecznym w wersji tytan - korek, fig. 3 przedstawia odpowiednio płytę w przekroju poprzecznym z dodatkową przestrzenną warstwą
PL 232 871 B1 amortyzującą, a fig. 4 przedstawia płytę w przekroju poprzecznym w wersji tytan - korek z zastosowaniem warstwy aramidu i ukształtowaną w formie zagiętej.
W pierwszym przykładzie wykonania płyty wielowarstwowej według wynalazku w kolejności od strony zewnętrznej ułożona jest warstwa zbrojenia wykonana ze szkła 1, do której przymocowana jest kolejna warstwa zbrojenia wykonana z tkaniny aramidowej 2, do której przymocowana jest warstwa amortyzująca wykonana z korka 3, do której następnie przymocowana jest kolejna warstwa zbrojenia wykonana z tytanu 4, do której następnie przymocowana jest kolejna warstwa korka 3, kolejna warstwa tytanu 4, a następnie ostatnia warstwa korka 3 i ostatnia warstwa tytanu 4. Płyta cechuje się wysoką odpornością na przebijanie. Wszystkie warstwy są połączone trwale za pomocą kleju.
W drugim przykładzie wykonania płyty wielowarstwowej według wynalazku w kolejności od strony zewnętrznej ułożona jest warstwa zbrojenia wykonana z tytanu 4, do której przyklejono warstwę amortyzującą wykonaną z korka 3. Zestawienie warstw zostało następnie trzykrotnie powtórzone, i ostatnią warstwę stanowi ponownie tytan 4. Taka płyta cechuje się bardzo niską masą własną jednostkową a jednocześnie zachowuje wysoką odporność na przebijanie, dla kalibru 7,62 włącznie. Wszystkie warstwy są połączone trwale za pomocą kleju.
W trzecim przykładzie wykonania płyty wielowarstwowej według wynalazku w kolejności od strony zewnętrznej ułożona jest warstwa zbrojenia wykonana ze szkła 1, do której przymocowana jest warstwa zbrojenia wykonana z tkaniny aramidowej 2, do której przymocowana jest kolejna warstwa zbrojenia wykonana z tytanu 4. Do tej warstwy przymocowana jest przestrzenna warstwa amortyzująca 6 wykonana z poliuretanu, której wolne przestrzenie są wypełnione z jednej strony warstwą amortyzującą 3 z korka, a z drugiej strony warstwą amortyzującą 5 z mieszaniny korka z gumą. Następnie dwukrotnie powtórzono zestawienie warstw tytan 4 - korek 3 i ostatnią warstwę stanowi ponownie tytan 4. Wszystkie warstwy są połączone trwale za pomocą kleju.
W czwartym przykładzie wykonania płyty wielowarstwowej według wynalazku w kolejności od strony zewnętrznej ułożona jest warstwa zbrojenia wykonana w wersji zaokrąglonej do osłony elementów wypukłych. Zewnętrzną warstwę zbrojenia stanowi warstwa tytanu 4 i tkaniny aramidowej 2, następnie trzykrotnie powtórzono zestawienie warstw korek 3 - tytan 4. Wszystkie warstwy są połączone trwale za pomocą infuzji. Można zastosować też proces laminowania.
W podanych przykładach wykonania wymienione przykładowo poszczególne warstwy zbrojenia - w zależności od miejsca zastosowania - można zastępować odpowiednio warstwami zbrojenia wykonanymi z ceramiki (kopalnie), tworzyw sztucznych (lotnictwo), tkaniny aramidowo-szklanej, tkaniny szklanej (ochrona pożarowa), polietylenowej PE-UHMW (ochrona osobista), aluminium, duraluminium (lotnictwo) lub stali pancernej (militaria).
Płyta skonstruowana jak w powyższych przykładach wykonania ma znacznie mniejszą masę jednostkową aniżeli wykonana ze stali. Płyta skonstruowana może być w ten sposób, że tytan można zastąpić aluminium lub duraluminium, korzystnie z dodatkiem tkaniny aramidowej.

Claims (11)

  1. Zastrzeżenia patentowe
    1. Płyta wielowarstwowa zawierająca warstwy zbrojenia zbudowane z metalu lub ceramiki lub szkła lub tworzyw sztucznych lub tkaniny aramidowej, aramidowo-szklanej, szklanej, polietylenowej o ultrawysokiej masie cząsteczkowej (PE-UHMW), i/lub zbudowane z kombinacji tych materiałów oraz warstw amortyzujących, znamienna tym, że co najmniej jedna warstwa amortyzująca utworzona jest z korka lub co najmniej jedna warstwa amortyzująca utworzona jest z mieszaniny korka z innymi substancjami sprężystymi, przy czym warstwy zewnętrzne płyty stanowią warstwy zbrojenia a pomiędzy nimi znajdują się naprzemiennie warstwy amortyzujące i warstwy zbrojenia trwale zespolone.
  2. 2. Płyta wielowarstwowa, według zastrz. 1, znamienna tym, że warstwa amortyzująca utworzona jest korzystnie z aglomeratu korkowego.
  3. 3. Płyta wielowarstwowa, według zastrz. 1, znamienna tym, że warstwa amortyzująca utworzona jest korzystnie z ekspandowanego korka.
  4. 4. Płyta wielowarstwowa, według zastrz. 1 , znamienna tym, że warstwa amortyzująca utworzona jest korzystnie z mieszaniny korka z gumą.
  5. 5. Płyta wielowarstwowa, według zastrz. 1, znamienna tym, że warstwa amortyzująca utworzona jest korzystnie z mieszaniny korka z poliuretanem.
    PL 232 871 B1
  6. 6. Płyta wielowarstwowa, według zastrz. 1, znamienna tym, że warstwa amortyzująca utworzona jest korzystnie z mieszaniny korka z gumą i poliuretanem.
  7. 7. Płyta wielowarstwowa, według zastrz. 1, znamienna tym, że warstwa amortyzująca zawiera wewnątrz dodatkowe przestrzenne warstwy amortyzujące, korzystnie w kształcie falistym, trapezowym, trójkątnym, lub sześciennym lub plastra miodu.
  8. 8. Płyta wielowarstwowa, według zastrz. 1, znamienna tym, że warstwa zbrojenia korzystnie jest zbudowana z aluminium.
  9. 9. Płyta wielowarstwowa, według zastrz. 1, znamienna tym, że warstwa zbrojenia korzystnie jest zbudowana z duraluminium.
  10. 10. Płyta wielowarstwowa, według zastrz. 1, znamienna tym, że warstwa zbrojenia korzystnie jest zbudowana z tytanu.
  11. 11. Płyta wielowarstwowa, według zastrz. 1, znamienna tym, że warstwa zbrojenia korzystnie jest zbudowana ze stali pancernej.
PL413342A 2015-07-30 2015-07-30 Płyta wielowarstwowa PL232871B1 (pl)