PL2682495T3 - Blacha stalowa powlekana zanurzeniowo systemem na bazie Zn-Al-Mg i sposób jej wytwarzania - Google Patents

Blacha stalowa powlekana zanurzeniowo systemem na bazie Zn-Al-Mg i sposób jej wytwarzania

Info

Publication number
PL2682495T3
PL2682495T3 PL12752196T PL12752196T PL2682495T3 PL 2682495 T3 PL2682495 T3 PL 2682495T3 PL 12752196 T PL12752196 T PL 12752196T PL 12752196 T PL12752196 T PL 12752196T PL 2682495 T3 PL2682495 T3 PL 2682495T3
Authority
PL
Poland
Prior art keywords
coated
production
steel sheet
sheet dip
dip
Prior art date
Application number
PL12752196T
Other languages
English (en)
Inventor
Kentaro Hirata
Yukio Katagiri
Susumu Fujiwara
Kazuaki Hosomi
Masaaki URANAKA
Original Assignee
Nisshin Steel Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nisshin Steel Co., Ltd. filed Critical Nisshin Steel Co., Ltd.
Publication of PL2682495T3 publication Critical patent/PL2682495T3/pl

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B60—VEHICLES IN GENERAL
    • B60R—VEHICLES, VEHICLE FITTINGS, OR VEHICLE PARTS, NOT OTHERWISE PROVIDED FOR
    • B60R13/00—Elements for body-finishing, identifying, or decorating; Arrangements or adaptations for advertising purposes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C23/00—Alloys based on magnesium
    • C22C23/02—Alloys based on magnesium with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C23/00—Alloys based on magnesium
    • C22C23/04—Alloys based on magnesium with zinc or cadmium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P10/00—Technologies related to metal processing
    • Y02P10/20—Recycling
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
PL12752196T 2011-02-28 2012-02-28 Blacha stalowa powlekana zanurzeniowo systemem na bazie Zn-Al-Mg i sposób jej wytwarzania PL2682495T3 (pl)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2011043334 2011-02-28
EP12752196.1A EP2682495B1 (en) 2011-02-28 2012-02-28 STEEL SHEET HOT-DIP-COATED WITH Zn-Al-Mg-BASED SYSTEM, AND PROCESS OF MANUFACTURING SAME
PCT/JP2012/054926 WO2012118073A1 (ja) 2011-02-28 2012-02-28 溶融Ｚｎ－Ａｌ－Ｍｇ系めっき鋼板および製造方法

Publications (1)

Publication Number Publication Date
PL2682495T3 true PL2682495T3 (pl) 2019-06-28

Family

ID=46758004

Family Applications (1)

Application Number Title Priority Date Filing Date
PL12752196T PL2682495T3 (pl) 2011-02-28 2012-02-28 Blacha stalowa powlekana zanurzeniowo systemem na bazie Zn-Al-Mg i sposób jej wytwarzania

Country Status (12)

Country Link
US (1) US9592772B2 (pl)
EP (2) EP3470541A1 (pl)
JP (1) JP5936390B2 (pl)
KR (1) KR102099588B1 (pl)
CN (1) CN103415641B (pl)
AU (1) AU2012224032B2 (pl)
CA (1) CA2826225C (pl)
ES (1) ES2712631T3 (pl)
HU (1) HUE043883T2 (pl)
PL (1) PL2682495T3 (pl)
TR (1) TR201903572T4 (pl)
WO (1) WO2012118073A1 (pl)

Families Citing this family (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5372217B2 (ja) * 2012-02-24 2013-12-18 日新製鋼株式会社 アーク溶接構造部材の製造法
JP6049516B2 (ja) * 2013-03-26 2016-12-21 日新製鋼株式会社 溶接構造部材用高強度めっき鋼板およびその製造法
JP6238474B2 (ja) * 2013-12-19 2017-11-29 日新製鋼株式会社 加工性に優れた溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板及びその製造方法
US20150231726A1 (en) * 2014-02-19 2015-08-20 Nisshin Steel Co., Ltd. METHOD FOR PRODUCING ARC-WELDED Zn-Al-Mg ALLOY COATED STEEL PLATE STRUCTURAL MEMBER
CN107223166A (zh) * 2014-12-24 2017-09-29 Posco公司 焊接性和加工部耐蚀性优异的镀锌合金钢材及其制造方法
KR101758529B1 (ko) * 2014-12-24 2017-07-17 주식회사 포스코 인산염 처리성과 스폿 용접성이 우수한 아연합금도금강판 및 그 제조방법
JP6209175B2 (ja) * 2015-03-03 2017-10-04 日新製鋼株式会社 めっき表面外観およびバーリング性に優れた溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板の製造方法
WO2016162982A1 (ja) 2015-04-08 2016-10-13 新日鐵住金株式会社 Ｚｎ－Ａｌ－Ｍｇ系めっき鋼板、及びＺｎ－Ａｌ－Ｍｇ系めっき鋼板の製造方法
JP6114785B2 (ja) * 2015-05-29 2017-04-12 日新製鋼株式会社 溶接部外観と溶接強度に優れた溶融Ｚｎ系めっき鋼板のアーク溶接方法、および溶接部材の製造方法
CN105256196A (zh) * 2015-10-23 2016-01-20 首钢总公司 一种铝锌镁镀层钢板及其制备方法
JP2017145441A (ja) * 2016-02-16 2017-08-24 日新製鋼株式会社 黒色表面被覆高強度鋼板およびその製造方法
KR101899674B1 (ko) * 2016-12-19 2018-09-17 주식회사 포스코 저온역 버링성이 우수한 고강도 강판 및 이의 제조방법
WO2018234839A1 (en) 2017-06-20 2018-12-27 Arcelormittal ZINC COATED STEEL SHEET HAVING HIGH STRENGTH POINTS WELDABILITY
KR102010079B1 (ko) 2017-09-13 2019-08-12 주식회사 포스코 도장 후 선영성이 우수한 강판 및 그 제조방법
KR102031465B1 (ko) * 2017-12-26 2019-10-11 주식회사 포스코 가공 후 내식성 우수한 아연합금도금강재 및 그 제조방법
KR102142766B1 (ko) 2018-08-31 2020-08-07 주식회사 포스코 내식성 및 가공성이 우수한 용융도금강판 및 이의 제조방법
KR102276742B1 (ko) 2018-11-28 2021-07-13 주식회사 포스코 도금 밀착성 및 내부식성이 우수한 아연도금강판 및 이의 제조방법
JP2021055135A (ja) * 2019-09-27 2021-04-08 日本製鉄株式会社 溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
MX2022009482A (es) * 2020-02-13 2022-08-22 Nippon Steel Corp Componente de union y metodo de fabricacion del mismo.
CN115053009B (zh) * 2020-03-03 2024-05-31 杰富意钢铁株式会社 热压部件及其制造方法以及热压用镀覆钢板
CN112575275A (zh) * 2020-12-03 2021-03-30 攀钢集团研究院有限公司 高成形性的热浸镀锌铝镁合金镀层钢板及其制备方法
US11441039B2 (en) * 2020-12-18 2022-09-13 GM Global Technology Operations LLC High temperature coatings to mitigate weld cracking in resistance welding
CN115074576A (zh) * 2022-06-13 2022-09-20 首钢集团有限公司 一种锌铝镁合金锭、镀层、镀层钢及其制备方法
CN117604222B (zh) * 2023-11-30 2025-11-25 马鞍山钢铁有限公司 一种全规格经济型光伏用钢的制备工艺及其制得的产品

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3392154B2 (ja) * 1991-03-29 2003-03-31 日新製鋼株式会社 耐火用高張力溶融Ｚｎ−Ａ１合金めっき鋼板の製造方法
JPH05263145A (ja) 1992-03-05 1993-10-12 Nippon Steel Corp バーリング性の優れた高強度合金化溶融亜鉛メッキ鋼板の製造方法
KR100257900B1 (ko) * 1995-03-23 2000-06-01 에모토 간지 인성이 우수한 저항복비 고강도 열연강판 및 그 제조방법
BR0107195B1 (pt) * 2000-09-12 2011-04-05 chapa de aço imersa a quente de alta resistência à tração e método para produzì-la.
WO2002036840A1 (fr) * 2000-10-31 2002-05-10 Nkk Corporation Tole d"acier laminee a chaud presentant une resistance elevee a la traction et procede de fabrication
JP3715220B2 (ja) * 2001-06-22 2005-11-09 日新製鋼株式会社 耐食性に優れたＺｎ−Ａｌ−Ｍｇ系溶融めっき鋼材
JP3821043B2 (ja) * 2002-04-30 2006-09-13 Ｊｆｅスチール株式会社 溶接性に優れた溶融亜鉛系めっき高張力熱延鋼板ならびにその製造方法および加工方法
AU2003284496A1 (en) * 2002-12-24 2004-07-22 Nippon Steel Corporation High strength steel sheet exhibiting good burring workability and excellent resistance to softening in heat-affected zone and method for production thereof
JP4635525B2 (ja) * 2003-09-26 2011-02-23 Ｊｆｅスチール株式会社 深絞り性に優れた高強度鋼板およびその製造方法
JP4721221B2 (ja) * 2004-09-01 2011-07-13 日新製鋼株式会社 耐溶融金属脆化割れ性に優れたＺｎ−Ａｌ−Ｍｇ合金めっき鋼板
JP4776951B2 (ja) * 2005-03-11 2011-09-21 新日本製鐵株式会社 溶接性に優れた溶接用亜鉛系合金めっき鋼材
AU2006277251B2 (en) * 2005-08-05 2009-11-19 Jfe Steel Corporation High Strength Steel Sheet and Method for Manufacturing the Same
JP5264235B2 (ja) * 2008-03-24 2013-08-14 日新製鋼株式会社 耐溶融金属脆化割れ性に優れた高降伏比型Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
BRPI0822700A2 (pt) * 2008-05-15 2015-07-07 Siemens Vai Metals Technologies S A S Sistema e método para orientação de um dispositivo de secagem de um produto de galvanização
US20110318606A1 (en) * 2009-03-10 2011-12-29 Nisshin Steel Co., Ltd. Zinc-based alloy-plated steel material excellent in resistance to molten-metal embrittlement cracking

Also Published As

Publication number Publication date
AU2012224032A1 (en) 2013-09-12
US20130337287A1 (en) 2013-12-19
JP2012193452A (ja) 2012-10-11
EP3470541A1 (en) 2019-04-17
ES2712631T3 (es) 2019-05-14
WO2012118073A1 (ja) 2012-09-07
EP2682495A4 (en) 2016-03-16
CA2826225A1 (en) 2012-09-07
CN103415641B (zh) 2016-01-06
KR102099588B1 (ko) 2020-04-10
TR201903572T4 (tr) 2019-04-22
CA2826225C (en) 2020-07-21
EP2682495B1 (en) 2019-01-02
US9592772B2 (en) 2017-03-14
HUE043883T2 (hu) 2019-09-30
JP5936390B2 (ja) 2016-06-22
AU2012224032B2 (en) 2017-03-16
CN103415641A (zh) 2013-11-27
EP2682495A1 (en) 2014-01-08
KR20140002740A (ko) 2014-01-08

Similar Documents

Publication Publication Date Title
PL2682495T3 (pl) Blacha stalowa powlekana zanurzeniowo systemem na bazie Zn-Al-Mg i sposób jej wytwarzania
PL2762590T3 (pl) Blacha stalowa ocynkowana i sposób jej wytwarzania
PL2578711T3 (pl) Blacha stalowa i sposób jej wytwarzania
PL2716782T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
HUE036408T2 (hu) A leukotrién-termelés benzodioxán inhibitorai
LT2771307T (lt) Akrilatų gamybos būdas iš epoksidų
PL2697060T3 (pl) Sposób wytwarzania panelu budowlanego
EP2724258A4 (en) DYNAMIC UPDATE OF A PAGE IN PROGRESS
FI20110375A0 (fi) Menetelmä ferriittis-austeniittisen ruostumattoman teräksen valmistamiseksi ja hyödyntämiseksi
PT2791176T (pt) Um método de purificação de anticorpos
PL3346447T3 (pl) Sposób uzyskiwania trybu predykcji wewnątrzobrazowej
HUE054867T2 (hu) Edzett szerkezeti elemek elõállításának módszere
GB2502937B (en) Running a plurality of instances of an application
CO7020903A2 (es) Construcción de un panel de vidrio
EP2554366A4 (en) COATING AND MANUFACTURING METHOD THEREFOR
IL227413A0 (en) Coating and its manufacturing process
BR112014008911A2 (pt) processo para a produção de 5-hidroximetilfurfural
PL2707515T3 (pl) Sposób produkcji blach ze stali martenzytycznej o bardzo wysokiej granicy plastyczności oraz wytworzone blachy stalowe
GB201109361D0 (en) Method of constructing a building
ZA201308673B (en) Method of predicting the energy consumption of a building
PL2627656T3 (pl) Sposób wytwarzania dihydropterydynonów i ich produktów pośrednich
PL2444227T3 (pl) Sposób ciągłego wytwarzania taśmy LED
ZA201402558B (en) Method of producing a plate-like construction with a double-wall structure
FR2978809B1 (fr) Ferrure et procede et outillage pour sa production
FR2977826B1 (fr) Procede de realisation d'un panneau avec une double courbure