PL3323907T3 - Blacha stalowa cienka, blacha stalowa cienka cynkowana zanurzeniowo na gorąco, blacha stalowa cienka cynkowana z przeżarzaniem i sposoby ich wytwarzania - Google Patents

Blacha stalowa cienka, blacha stalowa cienka cynkowana zanurzeniowo na gorąco, blacha stalowa cienka cynkowana z przeżarzaniem i sposoby ich wytwarzania

Info

Publication number
PL3323907T3
PL3323907T3 PL15898251T PL15898251T PL3323907T3 PL 3323907 T3 PL3323907 T3 PL 3323907T3 PL 15898251 T PL15898251 T PL 15898251T PL 15898251 T PL15898251 T PL 15898251T PL 3323907 T3 PL3323907 T3 PL 3323907T3
Authority
PL
Poland
Prior art keywords
steel sheet
galvanized steel
angling
production
methods
Prior art date
Application number
PL15898251T
Other languages
English (en)
Inventor
Yuri TODA
Masafumi Azuma
Akihiro Uenishi
Hiroyuki Kawata
Naoki Maruyama
Genichi Shigesato
Original Assignee
Nippon Steel Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corporation filed Critical Nippon Steel Corporation
Publication of PL3323907T3 publication Critical patent/PL3323907T3/pl

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/001—Heat treatment of ferrous alloys containing Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P10/00—Technologies related to metal processing
    • Y02P10/20—Recycling

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
PL15898251T 2015-07-13 2015-07-13 Blacha stalowa cienka, blacha stalowa cienka cynkowana zanurzeniowo na gorąco, blacha stalowa cienka cynkowana z przeżarzaniem i sposoby ich wytwarzania PL3323907T3 (pl)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/JP2015/070069 WO2017009938A1 (ja) 2015-07-13 2015-07-13 鋼板、溶融亜鉛めっき鋼板、及び合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
EP15898251.2A EP3323907B1 (en) 2015-07-13 2015-07-13 Steel sheet, hot-dip galvanized steel sheet, galvannealed steel sheet, and manufacturing methods therefor

Publications (1)

Publication Number Publication Date
PL3323907T3 true PL3323907T3 (pl) 2020-07-27

Family

ID=57757132

Family Applications (1)

Application Number Title Priority Date Filing Date
PL15898251T PL3323907T3 (pl) 2015-07-13 2015-07-13 Blacha stalowa cienka, blacha stalowa cienka cynkowana zanurzeniowo na gorąco, blacha stalowa cienka cynkowana z przeżarzaniem i sposoby ich wytwarzania

Country Status (10)

Country Link
US (1) US10822672B2 (pl)
EP (1) EP3323907B1 (pl)
JP (1) JP6460239B2 (pl)
KR (1) KR102057946B1 (pl)
CN (1) CN107849666B (pl)
BR (1) BR112018000090A2 (pl)
ES (1) ES2785410T3 (pl)
MX (1) MX2018000329A (pl)
PL (1) PL3323907T3 (pl)
WO (1) WO2017009938A1 (pl)

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102031445B1 (ko) * 2017-12-22 2019-10-11 주식회사 포스코 내충격특성이 우수한 고강도 강판 및 그 제조방법
EP3992314A4 (en) * 2019-06-28 2023-07-19 Nippon Steel Corporation GALVANISED STEEL
CN114729432B (zh) * 2020-03-16 2023-07-21 日本制铁株式会社 钢板
EP4182488A1 (en) * 2020-07-20 2023-05-24 ArcelorMittal Heat treated cold rolled steel sheet and a method of manufacturing thereof
CN113355602A (zh) * 2021-06-03 2021-09-07 全球能源互联网研究院有限公司 一种架空导线用芯线材料及其制备方法
DE102021121997A1 (de) 2021-08-25 2023-03-02 Thyssenkrupp Steel Europe Ag Kaltgewalztes Stahlflachprodukt und Verfahren zu seiner Herstellung
KR102747792B1 (ko) * 2022-05-31 2024-12-31 현대제철 주식회사 초고강도 냉연강판 및 그 제조방법

Family Cites Families (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01230715A (ja) 1987-06-26 1989-09-14 Nippon Steel Corp プレス成形性の優れた高強度冷延鋼板の製造方法
JPH0733551B2 (ja) 1989-02-18 1995-04-12 新日本製鐵株式会社 優れた成形性を有する高強度鋼板の製造方法
JP2826058B2 (ja) 1993-12-29 1998-11-18 株式会社神戸製鋼所 水素脆化の発生しない超高強度薄鋼板及び製造方法
JP3406094B2 (ja) * 1994-11-10 2003-05-12 株式会社神戸製鋼所 耐水素脆化特性にすぐれる超高強度薄鋼板の製造方法
JP3435035B2 (ja) 1997-09-24 2003-08-11 新日本製鐵株式会社 加工性およびほうろう密着性に優れた連続鋳造ほうろう用鋼板およびその製造方法
JP3527092B2 (ja) 1998-03-27 2004-05-17 新日本製鐵株式会社 加工性の良い高強度合金化溶融亜鉛めっき鋼板とその製造方法
JPH11293383A (ja) 1998-04-09 1999-10-26 Nippon Steel Corp 水素性欠陥の少ない厚鋼板およびその製造方法
EP1431406A1 (en) 2002-12-20 2004-06-23 Sidmar N.V. A steel composition for the production of cold rolled multiphase steel products
CN101802238B (zh) * 2007-08-01 2012-05-23 株式会社神户制钢所 弯曲加工性和耐疲劳强度优异的高强度钢板
JP5365216B2 (ja) * 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
US8343288B2 (en) 2008-03-07 2013-01-01 Kobe Steel, Ltd. Cold rolled steel sheet
JP4712882B2 (ja) 2008-07-11 2011-06-29 株式会社神戸製鋼所 耐水素脆化特性および加工性に優れた高強度冷延鋼板
WO2010109702A1 (ja) 2009-03-27 2010-09-30 株式会社神戸製鋼所 冷延鋼板
US8128762B2 (en) 2008-08-12 2012-03-06 Kobe Steel, Ltd. High-strength steel sheet superior in formability
JP5359168B2 (ja) 2008-10-08 2013-12-04 Ｊｆｅスチール株式会社 延性に優れる超高強度冷延鋼板およびその製造方法
PL2436797T3 (pl) 2009-05-27 2017-06-30 Nippon Steel & Sumitomo Metal Corporation Blacha stalowa cienka o dużej wytrzymałości, blacha stalowa cienka cynkowana ogniowo i stopowa blacha stalowa cienka cynkowana ogniowo o doskonałych parametrach zmęczenia, wydłużenia i właściwościach przy zderzeniu oraz sposób wytwarzania wspomnianych blach stalowych cienkich
CN101928875A (zh) 2009-06-22 2010-12-29 鞍钢股份有限公司 具有良好成形性能的高强度冷轧钢板及其制备方法
ES2758553T3 (es) 2009-11-30 2020-05-05 Nippon Steel Corp Lámina de acero de alta resistencia con excelente resistencia a la fragilidad por hidrógeno y una resistencia a tensión máxima de 900 MPa o más, y método para su producción
US9410231B2 (en) 2010-01-29 2016-08-09 Nippon Steel & Sumitomo Metal Corporation Steel sheet and method of manufacturing steel sheet
JP4893844B2 (ja) * 2010-04-16 2012-03-07 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
EP2617849B1 (en) * 2010-09-16 2017-01-18 Nippon Steel & Sumitomo Metal Corporation High-strength cold-rolled steel sheet with excellent ductility and stretch flangeability, high-strength galvanized steel sheet, and method for producing both
JP5765116B2 (ja) * 2010-09-29 2015-08-19 Ｊｆｅスチール株式会社 深絞り性および伸びフランジ性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5299591B2 (ja) 2011-07-29 2013-09-25 新日鐵住金株式会社 形状凍結性に優れた高強度鋼板、高強度亜鉛めっき鋼板およびそれらの製造方法
CA2850462C (en) * 2011-09-30 2016-10-11 Nippon Steel & Sumitomo Metal Corporation High-strength hot-dip galvanized steel sheet having excellent delayed fracture resistance and manufacturing method thereof
WO2013047755A1 (ja) * 2011-09-30 2013-04-04 新日鐵住金株式会社 耐衝撃特性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法、並びに、高強度合金化溶融亜鉛めっき鋼板およびその製造方法
PL2762600T3 (pl) 2011-09-30 2019-09-30 Nippon Steel & Sumitomo Metal Corporation Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania
US8876987B2 (en) * 2011-10-04 2014-11-04 Jfe Steel Corporation High-strength steel sheet and method for manufacturing same
CN103290307B (zh) 2012-02-27 2016-09-21 株式会社神户制钢所 耐冲击性优越的高强度钢板及其制造方法
US20150203947A1 (en) * 2012-07-31 2015-07-23 Jfe Steel Corporation High-strength galvanized steel sheet with excellent formability and shape fixability and method for manufacturing the same
JP5632947B2 (ja) 2012-12-12 2014-11-26 株式会社神戸製鋼所 加工性と低温靭性に優れた高強度鋼板およびその製造方法

Also Published As

Publication number Publication date
KR20180016549A (ko) 2018-02-14
ES2785410T3 (es) 2020-10-06
BR112018000090A2 (pt) 2018-08-28
JP6460239B2 (ja) 2019-01-30
EP3323907B1 (en) 2020-03-04
EP3323907A1 (en) 2018-05-23
KR102057946B1 (ko) 2019-12-20
MX2018000329A (es) 2018-03-14
JPWO2017009938A1 (ja) 2018-03-29
WO2017009938A1 (ja) 2017-01-19
EP3323907A4 (en) 2018-12-12
US10822672B2 (en) 2020-11-03
CN107849666B (zh) 2020-05-12
CN107849666A (zh) 2018-03-27
US20180209006A1 (en) 2018-07-26

Similar Documents

Publication Publication Date Title
PL3276030T3 (pl) Blacha stalowa cienka walcowana na gorąco i sposób jej wytwarzania oraz sposób wytwarzania blachy stalowej cienkiej walcowanej na zimno
EP3341681A4 (en) AUTOMATED EXACT DETERMINATION OF THE RUNNING SOLAR AREA
PL3653738T3 (pl) Sposób wytwarzania jakiejś powlekanej blachy stalowej o wysokiej wytrzymałości o ulepszonej ciągliwości i odkształcalności oraz wytworzona powlekana blacha stalowa
PL3216887T3 (pl) Blacha stalowa cienka cynkowana zanurzeniowo na gorąco
SG11201706948RA (en) HOT-DIP Al-Zn-Mg-Si COATED STEEL SHEET AND METHOD OF PRODUCING THE SAME
HUE044866T2 (hu) Hidegen hengerelt, tûzi bevonatolt acéllemez, gyártási eljárás és alkalmazás
PL2993248T3 (pl) Płaski wyrób stalowy z powłoką al, sposób jego wytwarzania, oraz sposób wytwarzania elementu konstrukcyjnego kształtowanego na gorąco
HUE059116T2 (hu) Eljárás alkálifém-szulfátsó elõállítására
PL3216891T3 (pl) Blacha stalowa cienka cynkowana zanurzeniowo na gorąco
DK3411510T3 (da) Varmgalvaniseringsanlæg og varmgalvaniseringsproces
PL3656552T3 (pl) Walcowana na gorąco i powlekana blacha stalowa do tłoczenia na gorąco, powlekana część stalowa tłoczona na gorąco i sposoby jej wytwarzania
EP3374492A4 (en) MICROBIAL PRODUCTION OF NICOTINAMIDE RIBOSIDE
HUE069896T2 (hu) Eljárás fémfelületek nikkelmentes foszfátozására
EP3683006A4 (en) PROCESS FOR MANUFACTURING A MODULAR METAL CONSTRUCTION
PL3167091T3 (pl) Blacha stalowa walcowana na gorąco i powiązany sposób wytwarzania
EP3683007A4 (en) METHOD OF FORMING PROFILED METAL CONSTRUCTION
PL3018230T4 (pl) Blacha stalowa cienka walcowana na zimno, ocynkowana blacha stalowa cienka walcowana na zimno oraz sposób ich wytwarzania
HUE049238T2 (hu) Eljárás horganyzott-lágyított acéllemez gyártására, valamint az így nyert horganyzott-lágyított acéllemez
HUE049059T2 (hu) Eljárás ultranagy szilárdságú horganyzott-lágyított acéllemez gyártására, valamint az így nyert horganyzott-lágyított acéllemez
PL3728668T3 (pl) Walcowana na zimno i powlekana blacha stalowa oraz sposób jej wytwarzania
ZA201707294B (en) High strength hot dip galvanized steel strip
HUE046693T2 (hu) Berendezés tûzihorganyzáshoz, és tûzihorganyzási eljárás tömeggyártáshoz
EP3323166A4 (en) AUTOMATED MANUFACTURE OF A BIONANO CATALYST
KR20180084987A (ko) 비금속성 또는 금속성 물품의 열전달 방법
PL3164519T3 (pl) Sposób wytwarzania powlekanej blachy stalowej o wysokiej wytrzymałości mającej ulepszoną wytrzymałość, odkształcalność