Description

Przedmiotem wynalazku jest sposób wytwarzania surowca do produkcji wegla aktywnego z materialów gumowych, zwlaszcza ze zuzytych tasm przesuwników transportowych, opon samochodowych oraz innych odpadów gumowych.The subject of the invention is a method of producing a raw material for the production of activated carbon from materials rubber, especially from used belts of transport shifter, car tires and others rubber waste.

Dotychczas znane sposoby wytwarzania wegla aktywnego polegaja na tym, ze jako surowca wyjsciowego uzywa sie przede wszystkim drewna i produktów drewno podobnych, lub lignitów z wegla brunatnego.The so far known methods of producing activated carbon consist in the fact that it is the starting material Primarily wood and similar wood products or lignites made of lignite are used.

W pierwszym przypadku stosuje sie surowiec deficytowy stwarzajacy trudnosci w jego nabyciu. Ponadto, w obydwóch przypadkach technologia wytwarzania wegla aktywnego z tych surowców jest skomplikowana, droga i wymagajaca zastosowania specjalnej do tego celu, kosztownej aparatury.In the first case, scarce resource is used, which causes difficulties in its purchase. Also, in both cases, the technology of producing activated carbon from these raw materials is complicated, expensive and requiring the use of special, expensive equipment.

Celem wynalazku jest stworzenie nowej technologii wytwarzania surowca do produkcji wegla aktywnego z materialów tanich, odpadowych, latwo dostepnych i przy zastosowaniu nieskomplikowanego procesu.The aim of the invention is to create a new technology for the production of raw material for the production of activated carbon from cheap, waste, easily available materials and with the use of an uncomplicated process.

Postawiony cel zostal osiagniety dzieki zastosowaniu sposobu wedlug niniejszego wynalazku. Sposób ten polega na tym, ze jako surowiec wyjsciowy do produkcji wegla aktywnego stosuje sie odpadowe materialy gumowe, zwlaszcza tasmy przesuwników transportowych i zuzyte opony samochodowe, które najpierw rozdrab¬ nia sie do wielkosci od 20 do 200 mm, nastepnie poddaje termicznemu procesowi odgazowania w temperaturze od 600 do 900°C, najkorzystniej w temperaturze 750°C. Proces prowadzi sie tak dlugo, az caly wsad zostanie odgazowany. Uzyskany pólprodukt koksowy poddaje sie aktywacji, przy czym produkty lotne z odgazowania sie kierowane do dalszego przerobu na paliwa ciekle i gazowe. Okazalo sie niespodziewanie, ze mozna uzyskac w sposób tani i prosty surowiec do produkcji wegla aktywnego z gumowych materialów odpadowych, na przyklad z tasm gumowych i ze zuzytych opon samochodowych, o ile zastosuje sie proces zgazowania w parametrach temperaturowych wyzej okreslonych i przy rozdrobnieniu materialu odpadowego do wielkosci wiekszej jak 20 mm.The object set was achieved by using the method according to the present invention. This way waste material is used as a raw material for the production of activated carbon rubber, in particular conveyor belts, and used car tires, which are first shredded It is sized from 20 to 200 mm, then subjected to a thermal degassing process at temperature from 600 to 900 ° C, most preferably at a temperature of 750 ° C. The process is carried out until the entire batch is left degassed. The obtained coke intermediate is subjected to activation, and volatile products from degassing they are directed to further processing into liquid and gaseous fuels. It turned out unexpectedly that you can get in a cheap and simple manner, raw material for the production of activated carbon from rubber waste materials, na example from rubber bands and from used car tires, if the gasification process is used w temperature parameters specified above and at the fragmentation of the waste material to the size greater than 20 mm.

Przyklad .1 tone zuzytych tasm przenosników transportowych rozdrabnia sie do wielkosci 20 mm i umieszcza w zamknietej komorze piecowej ogrzewanej przeponowo. Stopniowo podnosi sie temperature wsadu do 750°C az do uzyskania pelnego odgazowania, co potwierdza pojawienie sie bezdymnego plomienia. Goracy2 90 460 pólprodukt koksowy poddaje sie aktywacji na przyklad para wodna. W wyniku procesu, otrzymuje sie okolo 420 kg surowca do produkcji wegla aktywnego, wielokrotnie tanszego od dotychczas znanego, ze wzgledu na to, ze bazuje sie na odpadowym materiale jakimi sa uciazliwe odpady w postaci zuzytych tasm przenosników transportowych. Oprócz surowca do produkcji wegla aktywnego z 1 tony wsadu, otrzymuje sie okolo 320 kg wysokowartosciowego oleju opalowego oraz okolo 300 nm3 gazu do przemyslowego wykorzystania.Example: 1 ton of used conveyor belts is crushed to a size of 20 mm and placed in a closed, membrane-heated furnace. The temperature of the load increases gradually to 750 ° C until complete degassing is achieved, which is confirmed by the appearance of a smokeless flame. Goracy2 90 460 The coke intermediate is activated by, for example, water vapor. As a result of the process, you get about 420 kg of raw material for the production of activated carbon, many times cheaper than the previously known, due to the fact that that it is based on waste material such as troublesome waste in the form of used conveyor belts transport. Apart from the raw material for the production of activated carbon from 1 ton of charge, about 320 kg are obtained high-quality heating oil and about 300 nm3 of gas for industrial use.

Claims

1. Patent claim A method of producing the raw material for the production of activated carbon, characterized in that waste rubber materials are used as the raw material, especially conveyor belts, used car tires, which are first crushed to a size of 20 to 200 mm, and then thermally thermally a degassing process at a temperature of 600 to 900 ° C, most preferably at a temperature of 750 ° C, as long as the entire charge is degassed, the volatile products from the degassing are routed for further processing into liquid and gaseous fuels. Wash. Typographer. UP PRL, circulation 120 + 18 Price PLN 45