SE437852B - Sett vid framstellning av stalplat - Google Patents

Sett vid framstellning av stalplat

Info

Publication number
SE437852B
SE437852B SE8008717A SE8008717A SE437852B SE 437852 B SE437852 B SE 437852B SE 8008717 A SE8008717 A SE 8008717A SE 8008717 A SE8008717 A SE 8008717A SE 437852 B SE437852 B SE 437852B
Authority
SE
Sweden
Prior art keywords
steel
temperature
phase
cooling
range
Prior art date
Application number
SE8008717A
Other languages
English (en)
Swedish (sv)
Other versions
SE8008717L (sv
Inventor
T Furukawa
K Koyama
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of SE8008717L publication Critical patent/SE8008717L/
Publication of SE437852B publication Critical patent/SE437852B/sv

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0447—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the heat treatment
    • C21D8/0473—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C21D1/19—Hardening; Quenching with or without subsequent tempering by interrupted quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0421—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the working steps
    • C21D8/0426—Hot rolling

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
SE8008717A 1979-12-15 1980-12-11 Sett vid framstellning av stalplat SE437852B (sv)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP54163277A JPS5850300B2 (ja) 1979-12-15 1979-12-15 加工性に優れ且つ加工後人工時効硬化性の高い高強度低降伏比高延性複合組織鋼板の製造方法

Publications (2)

Publication Number Publication Date
SE8008717L SE8008717L (sv) 1981-06-16
SE437852B true SE437852B (sv) 1985-03-18

Family

ID=15770742

Family Applications (1)

Application Number Title Priority Date Filing Date
SE8008717A SE437852B (sv) 1979-12-15 1980-12-11 Sett vid framstellning av stalplat

Country Status (11)

Country Link
US (1) US4394186A (fr)
JP (1) JPS5850300B2 (fr)
BE (1) BE886583A (fr)
BR (1) BR8008153A (fr)
CA (1) CA1139644A (fr)
DE (1) DE3046941C2 (fr)
FR (1) FR2472022B1 (fr)
GB (1) GB2070058B (fr)
IT (1) IT1129435B (fr)
NL (1) NL184480C (fr)
SE (1) SE437852B (fr)

Families Citing this family (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62139848A (ja) * 1985-12-11 1987-06-23 Kobe Steel Ltd 自動車補強部材用高強度高延性冷延鋼板
US4793869A (en) * 1987-04-10 1988-12-27 Signode Corporation Continuous treatment of cold-rolled carbon manganese steel
MX165036B (es) * 1987-04-10 1992-10-16 Signode Corp Tratamiento continuo de acero de manganeso de carbono laminado en frio
US4793870A (en) * 1987-04-10 1988-12-27 Signode Corporation Continuous treatment of cold-rolled carbon high manganese steel
US5328531A (en) * 1989-07-07 1994-07-12 Jacques Gautier Process for the manufacture of components in treated steel
EP0559225B1 (fr) * 1992-03-06 1999-02-10 Kawasaki Steel Corporation Fabrication d'une tÔle d'acier résistant à la traction et ayant une déformabilité de bordage par étirage excellente
DE19936151A1 (de) * 1999-07-31 2001-02-08 Thyssenkrupp Stahl Ag Höherfestes Stahlband oder -blech und Verfahren zu seiner Herstellung
US6641931B2 (en) 1999-12-10 2003-11-04 Sidmar N.V. Method of production of cold-rolled metal coated steel products, and the products obtained, having a low yield ratio
DE10161465C1 (de) * 2001-12-13 2003-02-13 Thyssenkrupp Stahl Ag Verfahren zum Herstellen von Warmband
US20050247382A1 (en) * 2004-05-06 2005-11-10 Sippola Pertti J Process for producing a new high-strength dual-phase steel product from lightly alloyed steel
DE102004054444B3 (de) * 2004-08-10 2006-01-19 Daimlerchrysler Ag Verfahren zur Herstellung von Stahlbauteilen mit höchster Festigkeit und Plastizität
US7442268B2 (en) * 2004-11-24 2008-10-28 Nucor Corporation Method of manufacturing cold rolled dual-phase steel sheet
US8337643B2 (en) 2004-11-24 2012-12-25 Nucor Corporation Hot rolled dual phase steel sheet
US7959747B2 (en) * 2004-11-24 2011-06-14 Nucor Corporation Method of making cold rolled dual phase steel sheet
US11155902B2 (en) 2006-09-27 2021-10-26 Nucor Corporation High strength, hot dip coated, dual phase, steel sheet and method of manufacturing same
US7608155B2 (en) * 2006-09-27 2009-10-27 Nucor Corporation High strength, hot dip coated, dual phase, steel sheet and method of manufacturing same
MX2010003835A (es) * 2007-10-10 2010-05-13 Nucor Corp Acero estructurado metalografico complejo y metodo para manufacturarlo.
DE102008005158A1 (de) 2008-01-18 2009-07-23 Robert Bosch Gmbh Bauelement, insbesondere eine Kraftfahrzeugkomponente, aus einem höherfesten austenitischen Stahl mit TRIP-, TWIP- und/oder SIP-Effekt
ES2614465T3 (es) * 2012-07-10 2017-05-31 Thyssenkrupp Steel Europe Ag Producto plano de acero laminado en frío y procedimiento para su fabricación
CN104328346A (zh) * 2014-11-08 2015-02-04 江苏天舜金属材料集团有限公司 一种耐磨抗冲击型桩基钢护筒的加工工艺
CN108051549B (zh) * 2017-12-15 2024-03-15 中国科学院南京地理与湖泊研究所 一种测定水生植物能承受的水流临界流速的装置与方法
CN116497274B (zh) * 2023-04-19 2024-12-06 邯郸钢铁集团有限责任公司 一种低成本易轧制600MPa级热轧双相钢及制备方法
CN118064692B (zh) * 2024-03-27 2026-03-20 首钢集团有限公司 一种热轧镀锌双相钢及其制备方法

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5215046B2 (fr) 1972-06-22 1977-04-26
JPS5619380B2 (fr) * 1973-08-11 1981-05-07
US4113517A (en) * 1974-04-26 1978-09-12 Nippon Kokan Kabushiki Kaisha Method of making cold-reduced al-killed steel strip for press-forming by continuous casting and continuous annealing process
JPS5178730A (en) * 1974-12-30 1976-07-08 Nippon Steel Corp Fueraitosoto kyureihentaisoyorinaru fukugososhikikohanno seizohoho
US4033789A (en) * 1976-03-19 1977-07-05 Jones & Laughlin Steel Corporation Method of producing a high strength steel having uniform elongation
BE846024A (fr) * 1976-09-09 1977-03-09 Procede pour le traitement thermique continu des toles
BE846022A (fr) * 1976-09-09 1977-03-09 Procede de fabrication de toles pour emboutissage
JPS54163719A (en) * 1978-06-16 1979-12-26 Nippon Steel Corp Production of high tensile strength * low yield ratio and high extensibility composite textured steel panel with excellent workability
US4159218A (en) * 1978-08-07 1979-06-26 National Steel Corporation Method for producing a dual-phase ferrite-martensite steel strip

Also Published As

Publication number Publication date
FR2472022A1 (fr) 1981-06-26
DE3046941C2 (de) 1984-04-26
SE8008717L (sv) 1981-06-16
NL184480B (nl) 1989-03-01
GB2070058B (en) 1983-06-02
CA1139644A (fr) 1983-01-18
GB2070058A (en) 1981-09-03
NL8006798A (nl) 1981-07-16
BE886583A (fr) 1981-04-01
FR2472022B1 (fr) 1987-04-10
DE3046941A1 (de) 1981-10-01
IT8068908A0 (it) 1980-12-15
IT1129435B (it) 1986-06-04
NL184480C (nl) 1989-08-01
JPS5850300B2 (ja) 1983-11-09
JPS5687626A (en) 1981-07-16
BR8008153A (pt) 1981-06-30
US4394186A (en) 1983-07-19

Similar Documents

Publication Publication Date Title
SE437852B (sv) Sett vid framstellning av stalplat
KR100638543B1 (ko) 연성이 우수한 고장력 용융아연도금강판 및 그 제조방법
CN101545071B (zh) 钢板、其制造方法，部件以及制造所述部件的方法
JP5834717B2 (ja) 高降伏比を有する溶融亜鉛めっき鋼板およびその製造方法
CN104040009B (zh) 热轧钢板及其制造方法
JP7636353B2 (ja) 冷間圧延鋼ストリップを熱処理する方法
JP6719486B2 (ja) 耐剥離性に優れたｈｐｆ成形部材及びその製造方法
US20080075971A1 (en) High strength, hot dip coated, dual phase, steel sheet and method of manufacturing same
JPWO2018105003A1 (ja) 高強度鋼板
KR20020073564A (ko) 복합조직형 고장력 강판, 복합조직형 고장력 도금강판 및이들의 제조방법
KR20160039304A (ko) 열간-압연 ｔｗｉｐ-강의 제조 방법 및 이에 의해 제조된 ｔｗｉｐ-강 제품
CZ290944B6 (cs) Způsob výroby pásové oceli s vysokou pevností a dobrou tvárností
US20110223441A1 (en) Very high mechanical strength steel and method for producing a sheet of this steel coated with zinc or zinc alloy
US20190112681A1 (en) Steel sheet, plated steel sheet, method for producing hot-rolled steel sheet, method for producing cold-rolled full hard steel sheet, method for producing steel sheet, and method for producing plated steel sheet
JP3820868B2 (ja) 延性に優れる高張力溶融亜鉛めっき鋼板の製造方法
JP3587126B2 (ja) 延性に優れる高張力溶融亜鉛めっき鋼板およびその製造方法
US11060157B2 (en) Steel sheet, coated steel sheet, method for producing hot-rolled steel sheet, method for producing full hard cold-rolled steel sheet, method for producing steel sheet, and method for producing coated steel sheet
JP5835624B2 (ja) 熱間プレス用鋼板および表面処理鋼板とそれらの製造方法
JP2013185240A (ja) 高張力冷延鋼板および高張力めっき鋼板ならびにそれらの製造方法
JP3972551B2 (ja) 高張力溶融亜鉛めっき鋼板およびその製造方法
US6143100A (en) Bake-hardenable cold rolled steel sheet and method of producing same
JP5686028B2 (ja) 合金化溶融亜鉛めっき鋼板およびその製造方法
US11655517B2 (en) Ultrahigh-strength and high-ductility steel sheet having excellent cold formability
US5156690A (en) Building low yield ratio hot-dip galvanized cold rolled steel sheet having improved refractory property
JP2001303178A (ja) 成形性に優れた高張力溶融亜鉛系めっき鋼板およびその製造方法

Legal Events

Date Code Title Description
NAL Patent in force

Ref document number: 8008717-4

Format of ref document f/p: F