TH149261B - Extruded shape of high strength aluminum alloy. Showing resistance to corrosion, tensile conditions And excellent hardenable condition And a method for producing that shape - Google Patents
Extruded shape of high strength aluminum alloy. Showing resistance to corrosion, tensile conditions And excellent hardenable condition And a method for producing that shapeInfo
- Publication number
- TH149261B TH149261B TH1401000855A TH1401000855A TH149261B TH 149261 B TH149261 B TH 149261B TH 1401000855 A TH1401000855 A TH 1401000855A TH 1401000855 A TH1401000855 A TH 1401000855A TH 149261 B TH149261 B TH 149261B
- Authority
- TH
- Thailand
- Prior art keywords
- mass
- shape
- percent
- aluminum alloy
- high strength
- Prior art date
Abstract
รูปร่างที่ได้รับการอัดรีดของโลหะผสมอะลูมินัมที่มีความเเข็งเเรงสูง ซึ่งได้เเสดงถึง ความต้านทานการคัดกร่อน สภาพดึงยืดได้ เเละสภาพชุบเเข็งได้ที่ยอดเยี่ยม โดยรูปร่างที่ได้รับการ อัดรีดของโลหะผสมอะลูมินัมที่ประกอบรวมด้วย 0.65 ถึง 0.90 เปอร์เซ็นต์โดยมวลของ Mg 0.60 ถึง 0.90 เปอร์เซ็นต์โดยมวลของ Si,0.20 ถึง 0.40 เปอร์เซ็นต์โดยมวลของ Cu, 0.20 ถึง 0.40 เปอร์เซ็นต์ โดยมวลของ Fe, 0.10 ถึง 0.20 เปอร์เซ็นต์โดยมวลของ Mn เเละ 0.005 ถึง 0.1 เปอร์เซ็นต์โดยมวล ของ Ti ที่มีความสมดุลที่เป็น Al เเละสารเจือปนที่ไม่สามารถหลีกเลี่ยงได้ โดยรูปร่างที่ได้่รับการอัด รีดของโลหะผสมอะลูมินัมที่มีปริมาณ Mg,Si ที่เป็นปริมาณสัมพันธ์ที่มีค่า 1.0 ถึง 1.3 เปอร์เซ็นต์โดย มวล ปริมาณ Si ส่วนเกินไปที่สัมพัทธ์กับ Mg Si ที่เป็นปริมาณสัมพัทธ์ที่มีค่า 0.10 ถึง 0.30 เปอร์เซ็นต์โดยมวล เเละปริมาณทั้งหมดของ Fe เเละ Mn ที่มีค่า 0.35 เปอร์เซ็นต์โดยมวลหรือมากกว่า Extruded shape of high strength aluminum alloy. Which illustrates Corrosion resistance Stretchable condition And excellent condition. By the shape that has been Extrusion of an aluminum alloy comprising 0.65 to 0.90 percent by mass of Mg, 0.60 to 0.90 percent by mass of Si, 0.20 to 0.40 percent by mass of Cu, 0.20 to 0.40 percent by mass of Fe, 0.10 to 0.20 percent by The mass of Mn is 0.005 to 0.1% by the Ti balanced mass of Al and inevitable impurities. By the shape that has been pressed Extrusion of aluminum alloys with relative quantities of Mg, Si is 1.0 to 1.3 percent by mass, relative excess Si content with relative Mg Si, 0.10 to 0.30 percent by mass. And the total quantity of Fe and Mn were 0.35 percent by mass or more.
Claims (1)